CN114031333A - 一种环保彩泥沙及其制备方法 - Google Patents
一种环保彩泥沙及其制备方法 Download PDFInfo
- Publication number
- CN114031333A CN114031333A CN202111415130.8A CN202111415130A CN114031333A CN 114031333 A CN114031333 A CN 114031333A CN 202111415130 A CN202111415130 A CN 202111415130A CN 114031333 A CN114031333 A CN 114031333A
- Authority
- CN
- China
- Prior art keywords
- parts
- color
- environment
- sand
- sediment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保彩泥沙及其制备方法，包括以下按照重量份数计的原材料组成：面粉20‑30份，沙子48‑55份，盐3‑4份，油3‑4份，色粉0.5‑2份，水20‑30份，氯化钙8.3‑9.3份，按照设定比例，先将面粉、盐、色粉、防腐剂搅拌混合均匀，制备得到彩泥，然后往彩泥中加入沙子，搅拌混合均匀，经冷却后得到彩泥沙成品。本发明具有较高的强度，制成作品后不易发生开裂问题，而且能够使产品具有沙雕的效果，材料环保健康，不会对人体造成伤害。
Description
技术领域
本发明涉及彩泥技术领域，具体地说是一种环保彩泥沙及其制备方法。
背景技术
彩泥沙作为一种揉捏的用具，可以用于捏出各种图案作品，深得各类人群喜爱，尤其是孩童群体，对其更为青睐。
目前的彩泥沙，虽然已经具备各种颜色，但是彩泥沙本身的强度有所欠缺，制作成作品干燥后，存在由于强度不够而容易开裂的问题，不利于作品的长时间存放，难以确保作品的品质。
发明内容
本发明要解决的技术问题是提供一种环保彩泥沙及其制备方法。
为了解决上述技术问题，本发明采取以下技术方案：
一种环保彩泥沙，包括以下按照重量份数计的原材料组成：
面粉20-30份，沙子48-55份，盐3-4份，油3-4份，色粉0.5-2份，水20-30份，氯化钙8.3-9.3份。
所述彩泥沙还包括按照重量份数计的防腐剂0.2-0.5份。
所述沙子为河沙。
所述水为纯净水。
所述油为植物油或动物油，优选为植物油。
所述防腐剂采用食品防腐剂，具体为酸性防腐剂、酯型防腐剂或无机盐防腐剂。
所述酸性防腐剂为苯甲酸和苯甲酸钠、脱氢醋酸和脱氢醋酸钠、山梨酸和山梨酸钾；无机盐防腐剂为亚硫酸盐、焦亚硫酸盐。
一种环保彩泥沙的制备方法，包括以下步骤：
制彩泥，按照设定用量比例称取面粉、盐、色粉、防腐剂一起在搅拌缸中搅拌10-15分钟实现搅拌均匀，然后加入水温大于60℃的热水，继续搅拌20分钟以上的时间得到混合物料；
混合物料升高温度到95℃，加入油继续搅拌20-40分钟使得混合均匀，得到彩泥坯料，取出部分彩泥坯料出来冷却测试柔软不粘手即合格，不再加热，将氯化钙加入，搅拌均匀后取出彩泥坯料装入盛装瓶中，密封并冷却1-2天到35℃以下，形成彩泥成品；
制泥沙，按照设定比例取彩泥放入搅拌机中搅拌，并将温度保持在 45℃下加入沙子搅拌均匀，取出后冷却，即得到彩泥沙。
所述加入氯化钙时，将氯化钙分成均等的三份，分三次加入。
本发明中，通过采用面料、盐、水等材料，整体材料环保，绿色健康，有效提升了整体强度，使得通过本发明的彩泥沙制作而成的作品，不易开裂，而且表面具有沙雕的效果，提升视觉性，可广泛的用于制备各类型的益智玩具。
具体实施方式
为能进一步了解本发明的特征、技术手段以及所达到的具体目的、功能，下面结合具体实施方式对本发明作进一步详细描述。
实施例一
一种环保彩泥沙，包括以下按照重量份数计的原材料组成：面粉20 份，沙子48份，盐3份，油3份，防腐剂0.2份，色粉0.5份，水20份，氯化钙8.3份。其中，沙子选择河沙，避免使用海沙，从而可以确保制备，的产品不具备腐蚀性。油，可选择为植物油，面粉可选用小麦面粉，对于是高筋面粉，低筋面粉，则可以根据需要来选择。水通常选择为纯净水，在水量不足时，也可以选用自来水。
主要成分为面粉、水和沙子，材料环保安全，而且面粉作为粘合剂，起到塑形的作用。通过加入盐，可以起到一定的防腐杀菌作用，而再单独加入防腐剂，可以进一步确保整体的防腐性能，在制备过程上既能够进行杀菌，制备成品也能够形成有效的防腐性。而通过添加油，起到了保湿作用，使产品在干燥后也不易发生开裂的问题，具有更加温和的手感，提升使用体验。利用添加的色粉，为产品提供丰富多彩的颜色，满足不同人群的需求。而作为溶剂的水，则起到将材料充分混合均匀的作用。通过添加氯化钙，可以有将我提升产品的韧性，这也能够使产品在制备成作品后具有更好的拉伸性，也能够促进产品不易开裂。
所述防腐剂采用食品防腐剂，具体选择为酸性防腐剂，尤其是苯甲酸和苯甲酸钠。
在具体制备时，分成两部分进行。
制彩泥，按照设定用量比例称取面粉、盐、色粉、防腐剂一起在搅拌缸中搅拌10分钟实现混合均匀，然后加入水温60℃的热水，继续搅拌20 分钟的时间，在搅拌过程中，需要确保搅拌的空间环境是密闭的，通过两次搅拌处理，使各材料混合融合，得到混合物料。
混合物料升高温度到95℃，加入油继续搅拌20分钟进一步混合均匀，得到彩泥坯料，取出部分彩泥坯料出来进行冷却测试，测试结果为柔软不粘手即合格，不再加热，将将氯化钙分成均等的三份，分三次加入，搅拌均匀后取出彩泥坯料装入盛装瓶中，密封1天时间，并且自然冷却到35℃，形成彩泥成品。
制泥沙，按照设定比例取彩泥放入搅拌机中搅拌，并将温度保持在 45℃下加入沙子搅拌均匀，取出后冷却，即得到彩泥沙。
采用自动灌装线进行灌装、包装，完成整体的制备。
通过以上制备得到的彩泥沙，玩彩泥的过程中彩泥不会粘在手上，也不会有颜色残留在手上，利用色粉的特性，可互相混合，变化出更多更丰富的色调。可以创作出各种类型的作品，并且能够使作品在干燥后长时间不发生开裂问题。
实施例二
一种环保彩泥沙，包括以下按照重量份数计的原材料组成：面粉25 份，沙子452份，盐3份，油4份，防腐剂0.3份，色粉1份，水25份，氯化钙9份。
所述防腐剂采用食品防腐剂，具体选择为酸性防腐剂，尤其是苯甲酸和苯甲酸钠。
在具体制备时，分成两部分进行。
制彩泥，按照设定用量比例称取面粉、盐、色粉、防腐剂一起在搅拌缸中搅拌15分钟实现混合均匀，然后加入水温70℃的热水，继续搅拌25 分钟的时间，在搅拌过程中，需要确保搅拌的空间环境是密闭的，通过两次搅拌处理，使各材料混合融合，得到混合物料。
混合物料升高温度到100℃，加入油继续搅拌25分钟进一步混合均匀，得到彩泥坯料，取出部分彩泥坯料出来进行冷却测试，测试结果为柔软不粘手即合格，不再加热，将将氯化钙分成均等的三份，分三次加入，搅拌均匀后取出彩泥坯料装入盛装瓶中，密封2天时间，并且自然冷却到 30℃，形成彩泥成品。
制泥沙，按照设定比例取彩泥放入搅拌机中搅拌，并将温度保持在 50℃下加入沙子搅拌均匀，取出后冷却，即得到彩泥沙。
采用自动灌装线进行灌装、包装，完成整体的制备。
实施例三
一种环保彩泥沙，包括以下按照重量份数计的原材料组成：面粉30 份，沙子55份，盐4份，油4份，防腐剂0.5份，色粉2份，水30份，氯化钙9.3份。其中，沙子选择河沙，避免使用海沙，从而可以确保制备，的产品不具备腐蚀性。油，可选择为植物油，面粉可选用小麦面粉，对于是高筋面粉，低筋面粉，则可以根据需要来选择。水通常选择为纯净水，在水量不足时，也可以选用自来水。
主要成分为面粉、水和沙子，材料环保安全，而且面粉作为粘合剂，起到塑形的作用。通过加入盐，可以起到一定的防腐杀菌作用，而再单独加入防腐剂，可以进一步确保整体的防腐性能，在制备过程上既能够进行杀菌，制备成品也能够形成有效的防腐性。而通过添加油，起到了保湿作用，使产品在干燥后也不易发生开裂的问题，具有更加温和的手感，提升使用体验。利用添加的色粉，为产品提供丰富多彩的颜色，满足不同人群的需求。而作为溶剂的水，则起到将材料充分混合均匀的作用。通过添加氯化钙，可以有将我提升产品的韧性，这也能够使产品在制备成作品后具有更好的拉伸性，也能够促进产品不易开裂。
所述防腐剂采用食品防腐剂，具体选择为酸性防腐剂，尤其是苯甲酸和苯甲酸钠。
在具体制备时，分成两部分进行。
制彩泥，按照设定用量比例称取面粉、盐、色粉、防腐剂一起在搅拌缸中搅拌10分钟实现混合均匀，然后加入水温60℃的热水，继续搅拌20 分钟的时间，在搅拌过程中，需要确保搅拌的空间环境是密闭的，通过两次搅拌处理，使各材料混合均匀，得到混合物料。
混合物料升高温度到95℃，加入油继续搅拌20分钟进一步混合均匀，得到彩泥坯料，取出部分彩泥坯料出来进行冷却测试，测试结果为柔软不粘手即合格，不再加热，将将氯化钙分成均等的三份，分三次加入，搅拌均匀后取出彩泥坯料装入盛装瓶中，密封1天时间，并且自然冷却到35℃，形成彩泥成品。
制泥沙，按照设定比例取彩泥放入搅拌机中搅拌，并将温度保持在 45℃下加入沙子搅拌均匀，取出后冷却，即得到彩泥沙。
采用自动灌装线进行灌装、包装，完成整体的制备。
需要说明的是，以上仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，但是凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (9)
1.一种环保彩泥沙，其特征在于，包括以下按照重量份数计的原材料组成：
面粉20-30份，沙子48-55份，盐3-4份，油3-4份，色粉0.5-2份，水20-30份，氯化钙8.3-9.3份。
2.根据权利要求1所述的环保彩泥沙，其特征在于，所述彩泥沙还包括按照重量份数计的防腐剂0.2-0.5份。
3.根据权利要求2所述的环保彩泥沙，其特征在于，所述沙子为河沙。
4.根据权利要求3所述的环保彩泥沙，其特征在于，所述水为纯净水。
5.根据权利要求4所述的环保彩泥沙，其特征在于，所述油为植物油或动物油，优选为植物油。
6.根据权利要求5所述的环保彩泥沙，其特征在于，所述防腐剂采用食品防腐剂，具体为酸性防腐剂、酯型防腐剂或无机盐防腐剂。
7.根据权利要求6所述的环保彩泥沙，其特征在于，所述酸性防腐剂为苯甲酸和苯甲酸钠、脱氢醋酸和脱氢醋酸钠、山梨酸和山梨酸钾；无机盐防腐剂为亚硫酸盐、焦亚硫酸盐。
8.一种根据权利要求1-7中任一项所述的环保彩泥沙的制备方法，其特征在于，包括以下步骤：
制彩泥，按照设定用量比例称取面粉、盐、色粉、防腐剂一起在搅拌缸中搅拌10-15分钟实现搅拌均匀，然后加入水温大于60℃的热水，继续搅拌20分钟以上的时间得到混合物料；
混合物料升高温度到95℃，加入油继续搅拌20-40分钟使得混合均匀，得到彩泥坯料，取出部分彩泥坯料出来冷却测试柔软不粘手即合格，不再加热，将氯化钙加入，搅拌均匀后取出彩泥坯料装入盛装瓶中，密封并冷却1-2天到35℃以下，形成彩泥成品；
制泥沙，按照设定比例取彩泥放入搅拌机中搅拌，并将温度保持在45℃下加入沙子搅拌均匀，取出后冷却，即得到彩泥沙。
9.根据权利要求8所述的环保彩泥沙的制备方法，其特征在于，所述加入氯化钙时，将氯化钙分成均等的三份，分三次加入。