CN113797766A - 一种高通量改性氧化钛复合超滤膜及其应用 - Google Patents
一种高通量改性氧化钛复合超滤膜及其应用 Download PDFInfo
- Publication number
- CN113797766A CN113797766A CN202010540187.XA CN202010540187A CN113797766A CN 113797766 A CN113797766 A CN 113797766A CN 202010540187 A CN202010540187 A CN 202010540187A CN 113797766 A CN113797766 A CN 113797766A
- Authority
- CN
- China
- Prior art keywords
- titanium oxide
- membrane
- solution
- sol
- silane coupling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高通量改性氧化钛复合超滤膜及其应用，本发明选择磺基丙氨酸来对膜层表面进行改性，磺基丙氨酸上的羧基会与陶瓷膜上的硅烷偶联剂发生反应，提高膜层的亲水性，使氧化钛膜层的水表面接触角从38°提高到6‑10°，这是由于磺基丙氨酸亲水基团包括了酰磺基和氨基两部分，磺基丙氨酸的亲水基团部分能和溶剂形成多重氢键，使膜层表面具有很强的亲水性，提升了抗污染性能和水通量。
Description
技术领域
本发明属于膜分离技术领域，具体涉及一种高通量改性氧化钛复合超滤膜及其应用。
背景技术
随着社会经济的快速发展，人们在生产生活中产生大量的含油废水。研究调查表明，在化工、食品、石油、冶金、医药等工业领域都会产生含油废水，地球上每年都有大量的含油废水被直接排入自然水中，这些含油废水会对环境造成巨大的危害，用含油废水灌溉农田，会造成农作物减产或死亡，牲畜饮用了含油废水会导致食道的感染致病，并会通过食物链危及人体健康。因此，对如何高效处理含油废水成为研究人员关注的热点。
含油废水的传统处理工艺主要包括离心分离、重力分离、化学处理及颗粒填料过滤等。经过传统过滤的含油废水基本可以满足排放要求，但滤水的含油量及粒径往往很难达到一级排放标准。近些年来，膜分离法对含油废水进行深度处理成为研究热点。膜分离法不仅可以快速处理解决水污染问题，而且不会带来二次污染，可以实现循环利用，节约资源保护环境。早期采用有机超滤膜进行含油废水的处理，利用膜孔对悬浮油滴的截留，达到油水分离效果。但是由于膜本身受温度的限制，不能在较高温度下操作，因此寿命不长。随着科技日新月异，无机陶瓷膜开始走上历史舞台。陶瓷膜的优良特性使其在处理含油废水的行业中显示出非常好的前景。但是含油废水易腐蚀陶瓷膜且容易堵塞膜孔，降低使用寿命。因此对陶瓷膜进行改性显得尤为重要，其中提高陶瓷膜的亲水性是解决问题的关键。
发明内容
本发明的目的在于克服现有技术缺陷，提供一种高通量改性氧化钛复合超滤膜。
本发明的另一目的在于提供上述高通量改性氧化钛复合超滤膜的制备方法。
本发明的再一目的在于提供上述高通量改性氧化钛复合超滤膜的应用。
本发明的技术方案如下：
一种高通量改性氧化钛复合超滤膜，包括多孔陶瓷膜支撑体和氧化钛分离膜层，该氧化钛分离膜上通过硅烷偶联剂接枝有磺基丙氨酸使得氧化钛分离膜层的表面的水接触角为6-10°。
在本发明的一个优选实施方案中，所述硅烷偶联剂为3-氨丙基三乙氧基硅烷。
本发明的另一技术方案如下：
上述高通量改性氧化钛复合超滤膜的制备方法，其特征在于：包括如下步骤：
(1)通过溶胶凝胶法制备氧化钛溶胶；
(2)在氧化钛溶胶中加入增塑剂、粘结剂和消泡剂，制成涂膜液；
(3)在多孔陶瓷膜支撑体上浸涂上述涂膜液，再经干燥和烧结后，制得氧化钛分离膜层；
(4)将上述氧化钛分离膜层经碱活化后浸泡于硅烷偶联剂溶液中，室温下进行反应，经充分冲洗后进行干燥，获得接枝硅烷偶联剂的氧化钛分离膜层；
(5)将上述接枝硅烷偶联剂的氧化钛分离膜层浸泡于磺基丙氨酸溶液中，于78-82℃反应3-5h，即得。
在本发明的一个优选实施方案中，所述步骤(1)为：将分散剂加入有机钛溶液中，再加入酸进行解胶，解胶后的溶胶的pH为2-5，再加入分散剂混合均匀，制成氧化钛溶胶。
进一步优选的，所述有机钛溶液的溶质为钛酸正丁酯或钛酸异丙醇酯。
在本发明的一个优选实施方案中，所述硅烷偶联剂溶液的浓度为1.9-2.1mmol/L，所述磺基丙氨酸溶液的浓度为1-5mol/L。
在本发明的一个优选实施方案中，所述分散剂为聚乙二醇或甘油。
在本发明的一个优选实施方案中，所述增塑剂为聚乙烯醇，所述粘结剂为纤维素类化合物，所述消泡剂为有机硅消泡剂。
在本发明的一个优选实施方案中，所述步骤(3)中，所述干燥和煅烧具体为：于室温以1-3℃/min的速度升温至80-120℃后保温干燥2-5h，再以1-5℃/min的速度升温至500-700℃，保温烧结2-5h后自然冷却。
本发明的再一技术方案如下：
上述高通量改性氧化钛复合超滤膜在处理含油废水中的应用。
本发明的有益效果是：本发明选择磺基丙氨酸来对膜层表面进行改性，磺基丙氨酸上的羧基会与陶瓷膜上的硅烷偶联剂发生反应，提高膜层的亲水性，使氧化钛膜层的水表面接触角从38°提高到6-10°，这是由于磺基丙氨酸亲水基团包括了酰磺基和氨基两部分，磺基丙氨酸的亲水基团部分能和溶剂形成多重氢键，使膜层表面具有很强的亲水性，提升了抗污染性能和水通量。
具体实施方式
以下通过具体实施方式对本发明的技术方案进行进一步的说明和描述。
对比例1
(1)采用溶胶凝胶法制备氧化钛溶胶：将0.5％的分散剂聚乙二醇加入0.5mol/L钛酸正丁酯溶液中，在溶胶凝胶反应中，钛酸正丁酯和水的摩尔比为1∶10，再加入酸进行解胶，解胶后的溶胶pH为4，获得二氧化钛溶胶，再加入1％的分散剂聚乙二醇，并混合均匀，制成分散良好的氧化钛溶胶。
(2)将制成分散良好的氧化钛溶胶加入2％的聚乙烯醇和5％的羟乙基纤维素，充分混匀后，再加入0.01％的消泡剂，制成分散均匀的涂膜液。
(3)将上述涂膜液采用浸涂的方式涂于平均孔径为0.1μm的多孔陶瓷膜支撑体上，然后于室温以3℃/min的速度升温至120℃后保温干燥5h，再以3℃/min的速度升温至600℃，保温烧结3h后自然冷却，制得对比膜(氧化钛膜层的水表面接触角为38°)。
在0.1MPa和25℃条件下，本对比例制得的对比膜过滤含油量为15g/L的含油废水截留率约95，含油废水通量为300LHM。
对比例2
(1)采用溶胶凝胶法制备氧化钛溶胶：将0.5％的分散剂聚乙二醇加入0.8mol/L钛酸正丁酯溶液中，在溶胶凝胶反应中，钛酸正丁酯和水的摩尔比为1∶50，再加入酸进行解胶，解胶后的溶胶pH为4，获得二氧化钛溶胶，再加入1％的分散剂聚乙二醇，并混合均匀，制成分散良好的氧化钛溶胶。
(2)将制成分散良好的氧化钛溶胶加入3％的聚乙烯醇和5％的羟乙基纤维素，充分混匀后，再加入0.01％的消泡剂，制成分散均匀的涂膜液。
(3)将上述涂膜液采用浸涂的方式涂于平均孔径为0.1μm的多孔陶瓷膜支撑体上，然后于室温以1℃/min的速度升温至120℃后保温干燥5h，再以5℃/min的速度升温至600℃，保温烧结5h后自然冷却。
(4)将步骤(3)所得的物料用1mol/L氢氧化钠溶液浸泡5h，100℃下烘干24h，冷却后浸泡在浓度为2mmol/L的3-氨丙基三乙氧基硅烷乙醇溶液中，在室温下反应12h，然后依次用乙醇和去离子水冲洗数次，放入烘箱中以温度设定值150℃干燥12h后随炉冷却获得接枝后的陶瓷膜。
(5)将接枝后的陶瓷膜浸泡于浓度为0.5mol/L的磺基丙氨酸水溶液中，浸泡10min后取出膜管在烘箱80℃下反应3h，制备获得对比膜(氧化钛膜层的水表面接触角为22°)。
在0.1MPa和25℃条件下，本对比例制得的对比膜过滤含油量为15g/L的含油废水截留率96％，含油废水通量为420LHM。
实施例1
(1)-(3)同对比例2。
(4)将步骤(3)所得的物料用1mol/L氢氧化钠溶液浸泡5h，100℃下烘干24h，冷却后浸泡在浓度为2mmol/L的3-氨丙基三乙氧基硅烷乙醇溶液中，在室温下反应12h，然后依次用乙醇和去离子水冲洗数次，放入烘箱中以温度设定值150℃干燥12h后随炉冷却获得接枝后的陶瓷膜。
(5)将接枝后的陶瓷膜浸泡于浓度为1mol/L的磺基丙氨酸水溶液中，浸泡10min后取出膜管在烘箱80℃下反应3h，制备获得所述高通量改性氧化钛复合超滤膜(氧化钛膜层的水表面接触角为10°)。
在0.1MPa和25℃条件下，本对比例制得的高通量改性氧化钛复合超滤膜过滤含油量为15g/L的含油废水截留率99％，含油废水通量为530LHM。
实施例2
(1)采用溶胶凝胶法制备氧化钛溶胶：将0.5％的分散剂聚乙二醇加入1mol/L钛酸正丁酯溶液中，在溶胶凝胶反应中，钛酸正丁酯和水的摩尔比为1∶100，再加入酸进行解胶，解胶后的溶胶pH为5，获得二氧化钛溶胶，再加入1％的分散剂聚乙二醇，并混合均匀，制成分散良好的氧化钛溶胶。
(2)将制成分散良好的氧化钛溶胶加入3％的聚乙烯醇和2％的羟乙基纤维素，充分混匀后，再加入0.1％的消泡剂，制成分散均匀的涂膜液。
(3)将上述涂膜液采用浸涂的方式涂于平均孔径为0.1μm的多孔陶瓷膜支撑体上，然后于室温以1℃/min的速度升温至120℃后保温干燥5h，再以5℃/min的速度升温至700℃，保温烧结5h后自然冷却。
(4)将步骤(3)所得的物料用1mol/L氢氧化钠溶液浸泡5h，100℃下烘干24h，冷却后浸泡在浓度为2mmol/L的3-氨丙基三乙氧基硅烷乙醇溶液中，在室温下反应12h，然后依次用乙醇和去离子水冲洗数次，放入烘箱中以温度设定值150℃干燥12h后随炉冷却获得接枝后的陶瓷膜。
(5)将接枝后的陶瓷膜浸泡于浓度为3mol/L的磺基丙氨酸水溶液中，浸泡10min后取出膜管在烘箱80℃下反应5h，制备获得所述高通量改性氧化钛复合超滤膜(氧化钛膜层的水表面接触角为7°)。
在0.1MPa和25℃条件下，本实施例制得的高通量改性氧化钛复合超滤膜过滤含油量为15g/L的含油废水截留率98％，含油废水通量550LHM。
实施例3
(1)-(4)同实施例2。
(5)将接枝后的陶瓷膜浸泡于浓度为5mol/L的磺基丙氨酸水溶液中，浸泡10min后取出膜管在烘箱80℃下反应5h，制备获得所述高通量改性氧化钛复合超滤膜(氧化钛膜层的水表面接触角为6°)。
在0.1MPa和25℃条件下，本实施例制得的高通量改性氧化钛复合超滤膜过滤含油量为15g/L的含油废水截留率98％，含油废水通量570LHM。
以上所述，仅为本发明的较佳实施例而已，故不能依此限定本发明实施的范围，即依本发明专利范围及说明书内容所作的等效变化与修饰，皆应仍属本发明涵盖的范围内。
Claims (10)
1.一种高通量改性氧化钛复合超滤膜，其特征在于：包括多孔陶瓷膜支撑体和氧化钛分离膜层，该氧化钛分离膜上通过硅烷偶联剂接枝有磺基丙氨酸使得氧化钛分离膜层的表面的水接触角为6-10°。
2.如权利要求1所述的一种高通量改性氧化钛复合超滤膜，其特征在于：所述硅烷偶联剂为3-氨丙基三乙氧基硅烷。
3.权利要求1或2所述的一种高通量改性氧化钛复合超滤膜的制备方法，其特征在于：包括如下步骤：
(1)通过溶胶凝胶法制备氧化钛溶胶；
(2)在氧化钛溶胶中加入增塑剂、粘结剂和消泡剂，制成涂膜液；
(3)在多孔陶瓷膜支撑体上浸涂上述涂膜液，再经干燥和烧结后，制得氧化钛分离膜层；
(4)将上述氧化钛分离膜层经碱活化后浸泡于硅烷偶联剂溶液中，室温下进行反应，经充分冲洗后进行干燥，获得接枝硅烷偶联剂的氧化钛分离膜层；
(5)将上述接枝硅烷偶联剂的氧化钛分离膜层浸泡于磺基丙氨酸溶液中，于78-82℃反应3-5h，即得。
4.如权利要求3所述的制备方法，其特征在于：所述步骤(1)为：将分散剂加入有机钛溶液中，再加入酸进行解胶，解胶后的溶胶的pH为2-5，再加入分散剂混合均匀，制成氧化钛溶胶。
5.如权利要求4所述的制备方法，其特征在于：所述有机钛溶液的溶质为钛酸正丁酯或钛酸异丙醇酯。
6.如权利要求3所述的制备方法，其特征在于：所述硅烷偶联剂溶液的浓度为1.9-2.1mmol/L，所述磺基丙氨酸溶液的浓度为1-5mol/L。
7.如权利要求3所述的制备方法，其特征在于：所述分散剂为聚乙二醇或甘油。
8.如权利要求3所述的制备方法，其特征在于：所述增塑剂为聚乙烯醇，所述粘结剂为纤维素类化合物，所述消泡剂为有机硅消泡剂。
9.如权利要求3所述的制备方法，其特征在于：所述步骤(3)中，所述干燥和煅烧具体为：于室温以1-3℃/min的速度升温至80-120℃后保温干燥2-5h，再以1-5℃/min的速度升温至500-700℃，保温烧结2-5h后自然冷却。
10.权利要求1或2所述的高通量改性氧化钛复合超滤膜在处理含油废水中的应用。