CN113372250B - 多硫醇化合物、其制备方法、由其制备的透明氨基甲酸酯类树脂以及光学体 - Google Patents
多硫醇化合物、其制备方法、由其制备的透明氨基甲酸酯类树脂以及光学体 Download PDFInfo
- Publication number
- CN113372250B CN113372250B CN202110681547.2A CN202110681547A CN113372250B CN 113372250 B CN113372250 B CN 113372250B CN 202110681547 A CN202110681547 A CN 202110681547A CN 113372250 B CN113372250 B CN 113372250B
- Authority
- CN
- China
- Prior art keywords
- formula
- compound
- sch
- polythiol
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种具有三个或大于三个官能团的新颖多硫醇化合物、由其制备的透明氨基甲酸酯类树脂以及光学体。特别地，本发明涉及一种聚(硫)氨基甲酸酯类树脂以及一种使用树脂制造的光学体，例如透镜，其中通过以下来制备聚(硫)氨基甲酸酯类树脂：获得新颖多元醇；且随后将由所获得的多元醇制备的多硫醇与聚异(硫)氰酸酯结合。
Description
本发明是2018年02月13日所提出的申请号为201880011987.3、发明名称为《多元醇或多硫醇化合物、其制备方法、由其制备的透明氨基甲酸酯类树脂以及光学体》的发明专利申请的分案申请。
技术领域
本发明涉及一种新颖多元醇或多硫醇、一种制备所述多元醇或多硫醇的方法以及一种由其制备的聚氨基甲酸酯树脂。具体地说，本发明涉及一种由聚(硫)氨基甲酸酯树脂形成的光学体，通过使新颖多硫醇与聚异(硫)氰酸酯化合物反应来制备所述聚(硫)氨基甲酸酯树脂。
背景技术
近年来，需要用于塑料透镜的树脂以具有进一步改进的性能，以及高折射率、高阿贝数(Abbe's number)、低比重、高耐热性以及类似物。当前，用于塑料透镜的各种树脂已经研发并用于所属领域中。具体地说，通常用于塑料透镜的聚(硫)氨基甲酸酯树脂近来应用于光学装置，所述光学装置包含眼镜镜片、相机镜头以及类似物。
通过使多硫醇与聚异(硫)氰酸酯化合物反应来获得聚(硫)氨基甲酸酯树脂。多硫醇或作为其中间化合物的多元醇作为以下的原材料广泛地用于各种应用：光学体、聚(硫)氨基甲酸酯树脂或合成树脂、交联剂、环氧树脂固化剂、硫化剂、聚合调节剂、金属错合物以及生物化学润滑添加剂。
虽然可经由修改用作聚(硫)氨基甲酸酯树脂的组分的聚异(硫)氰酸酯化合物来向用于透镜和光学体的聚(硫)氨基甲酸酯树脂提供各种功能，但存在其种类受限的问题。因此，可修改用作其另一组分的多硫醇以向聚(硫)氨基甲酸酯树脂提供各种功能，且需要各种多硫醇。
所属领域中的各种文件(例如专利文件1至专利文件3)中公开制备这类多硫醇的方法。专利文件1公开一种制备多硫醇化合物的方法，其中存在于2-巯基乙醇中的特定添加剂的含量限于预定范围内。
专利文件2公开一种方法，其中存在于硫脲中的钙的含量限于预定范围内。专利文件3涉及一种多硫醇组合物以及其用途，且公开一种具有至少三个巯基的多硫醇化合物和一种包括少量含氮化合物的多硫醇组合物，其中多硫醇化合物的一个巯基经羟基取代。专利文件1、专利文件2以及专利文件3皆公开使用2-巯基乙醇制备多硫醇化合物的方法。具体地说，专利文件2公开一种用于通过使2-巯基乙醇与表卤代醇化合物反应来制备多硫醇化合物的通用方法。当前，2-巯基乙醇的制备限制性地源于环氧乙烷(ethylene oxide)。
另一方面，专利文件4是基于韩国专利申请案第10-2017-0020263号(申请日期：2017年2月15日)申请的且于2017年7月7日发布。本文件公开一种多硫醇化合物，通过以下来制备所述多硫醇化合物：由环氧丙烷制备1-巯基-2-丙醇，随后与表氯醇反应。然而，此专利文件的发明在以下方面具有各种问题：在公开由多元醇中间化合物制备多硫醇中间化合物的实例中无法确保所需多硫醇化合物的制备。
现有文献
专利文件
(专利文件1)国际公开案第WO 2007/129449号
(专利文件2)国际公开案第WO 2007/129450号
(专利文件3)国际公开案第WO 2014/027665号
(专利文件4)韩国专利特许公开公布第10-2017-0078139号
发明内容
技术问题
对于现有技术中报道的聚(硫)氨基甲酸酯树脂来说，难以制造满足染色特性同时维持高耐热性的光学透镜。染色特性是指经由多硫醇与聚异(硫)氰酸酯化合物的反应制备的透明树脂的物理特性。通过将树脂染色来获得特定树脂的染色特性以用于屏蔽可见光。一般来说，树脂的耐热性的上升使得其染色特性下降，且树脂的染色特性的上升使得其耐热性下降。因此，需要一种能够满足由聚(硫)氨基甲酸酯组合物制备的透明树脂的高耐热性以及高染色特性的多硫醇。
本发明的发明人已进行各种及密集研究以研发满足这些要求的多硫醇。因此，发现可通过以下来改进透明树脂的耐热性：调节侧链的体积和大小同时在影响透明树脂的玻璃转化温度(Tg)的因素之中维持分子中的相同结构。基于可改进透明树脂的耐热性同时维持其染色特性的这一发现，本发明人经由修改多硫醇的分子结构发明一种新颖多硫醇。
本发明旨在提供一种多元醇或多硫醇化合物和一种制备所述多元醇或多硫醇化合物的方法，所述多元醇或多硫醇化合物使用起始材料替代所属领域中使用的2-巯基乙醇来制备，且可确保其形成的透明透镜的高耐热性同时允许透明透镜的易着色和良好染色特性。另外，本发明旨在提供由聚(硫)氨基甲酸酯树脂形成的光学体，所述聚(硫)氨基甲酸酯树脂通过使新颖多硫醇与聚异(硫)氰酸酯化合物反应来制备。
技术解决方案
本发明的一个方面涉及一种多元醇或多硫醇化合物或其异构体，所述多元醇或多硫醇化合物具有至少三个官能团且由式(a)或式(b)表示：
(其中Y为氧原子或硫原子；
Ra为低碳数烷基；
i)对于多元醇，Rb为-CH2CH(OH)CH2F、-CH2CH(OH)CH2Cl、-CH2CH(OH)CH2Br、-CH2CH(OH)CH2I、-CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH3、
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH(CH3)CH2OH、
-CH2CH(OH)CH2OH、-CH2CH(OH)CH2SCH2CH(OH)CH3、
-CH2CH(OH)CH2SCH(CH3)CH2OH、
-CH2CH(OH)CH2SCH2CH(OH)CH2CH3、-CH2CH(OH)CH2SCH(CH2CH3)CH2OH、
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH2CH3或
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH(CH2CH3)CH2OH；
ii)对于多硫醇，Rb为-CH(CH2SH)CH2SH、-CH2CH(CH2SH)SH、
-CH2CH(CH2SH)SCH(CH3)CH2SH、-CH2CH(CH2SH)SCH2CH(CH3)SH、
-CH(CH2SH)CH2SCH(CH3)CH2SH、-CH(CH2SH)CH2SCH2CH(CH3)SH、
-CH2CH(CH2SH)SCH(CH2CH3)CH2SH、-CH2CH(CH2SH)SCH2CH(CH2CH3)SH、
-CH(CH2SH)CH2SCH(CH2CH3)CH2SH、-CH(CH2SH)CH2SCH2CH(CH2CH3)SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH2CH(CH3)SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH2CH(CH3)SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH(CH3)CH2SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH2CH(CH3)SH、
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH(CH3)CH2SH、
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH2CH(CH3)SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH2CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH2CH(CH2CH3)SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH(CH2CH3)CH2SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH2CH(CH2CH3)SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH(CH2CH3)CH2SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH2CH(CH2CH3)SH、
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH(CH2CH3)CH2SH或
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH2CH(CH2CH3)SH)。
在式(a)或式(b)中，Y可以是氧原子，Ra可以是甲基或乙基，且Rb可为由以下取代基所组成的族群中选出的一个取代基：
-CH2CH(OH)CH2F、-CH2CH(OH)CH2Cl、-CH2CH(OH)CH2Br、-CH2CH(OH)CH2I、
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH3、
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH(CH3)CH2OH、
-CH2CH(OH)CH2OH、
-CH2CH(OH)CH2SCH2CH(OH)CH3、
-CH2CH(OH)CH2SCH(CH3)CH2OH、
-CH2CH(OH)CH2SCH2CH(OH)CH2CH3、
-CH2CH(OH)CH2SCH(CH2CH3)CH2OH、
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH2CH3，以及
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH(CH2CH3)CH2OH。
另外，在式(a)或式(b)中，Y可以是硫原子，Ra可以是甲基或乙基，且Rb可为由以下取代基所组成的族群中选出的一个取代基：
-CH(CH2SH)CH2SH、-CH2CH(CH2SH)SH、-CH2CH(CH2SH)SCH(CH3)CH2SH、
-CH2CH(CH2SH)SCH2CH(CH3)SH、-CH(CH2SH)CH2SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH3)SH、-CH2CH(CH2SH)SCH(CH2CH3)CH2SH、
-CH2CH(CH2SH)SCH2CH(CH2CH3)SH、-CH(CH2SH)CH2SCH(CH2CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH2CH3)SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH2CH(CH3)SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH2CH(CH3)SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH(CH3)CH2SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH2CH(CH3)SH、
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH(CH3)CH2SH、
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH2CH(CH3)SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH2CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH2CH(CH2CH3)SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH(CH2CH3)CH2SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH2CH(CH2CH3)SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH(CH2CH3)CH2SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH2CH(CH2CH3)SH、
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH(CH2CH3)CH2SH，以及
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH2CH(CH2CH3)SH。
本发明的另一方面涉及一种根据反应式1制备由式(1)表示的多硫醇或其异构体的方法，所述方法包括以下步骤：
(1)通过使式(2)的巯基化合物与式(4)的表卤代醇化合物以1:1的当量比反应来制备式(5)的中间化合物；
(2)通过将硫化钠水溶液添加到所制备的式(5)的中间化合物中以及通过使其反应来制备式(6)的多元醇化合物；以及
(3)将无机酸和硫脲添加到所制备的式(6)的多元醇化合物中，将无机酸、硫脲以及多元醇化合物的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
(反应式1)
(其中，
X为由以下所组成的族群中选出的一个：F、Cl、Br以及I，
R1'为由以下所组成的族群中选出的一个：-CH2CH(OH)CH2F、-CH2CH(OH)CH2Cl、-CH2CH(OH)CH2Br以及-CH2CH(OH)CH2I，
R1”为-CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH3或
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH(CH3)CH2OH，以及
R3为由以下所组成的族群中选出的一个：
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH2CH(CH3)SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH2CH(CH3)SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH(CH3)CH2SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH2CH(CH3)SH、
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH(CH3)CH2SH，以及
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH2CH(CH3)SH)。
本发明的又一方面涉及一种根据反应式2制备由式(1)表示的多硫醇或其异构体的方法，所述方法包括以下步骤：
(1)通过使1当量的式(3)的巯基化合物与1当量的式(4)的表卤代醇化合物反应来制备式(7)的中间化合物；
(2)通过将硫化钠水溶液添加到所制备的式(7)的中间化合物中以及通过使其反应来制备式(8)的多元醇化合物；以及
(3)将无机酸和硫脲添加到所制备的式(8)的多元醇化合物中，将无机酸、硫脲以及多元醇化合物的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
(反应式2)
(其中，
X为由以下所组成的族群中选出的一个：F、Cl、Br以及I，
R2'为由以下所组成的族群中选出的一个：-CH2CH(OH)CH2F、-CH2CH(OH)CH2Cl、-CH2CH(OH)CH2Br以及-CH2CH(OH)CH2I，
R2”为-CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH3或
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH(CH3)CH2OH，
R3为由以下所组成的族群中选出的一个：
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH2CH(CH3)SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH2CH(CH3)SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH(CH3)CH2SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH2CH(CH3)SH、
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH(CH3)CH2SH，以及
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH2CH(CH3)SH)。
本发明的又一方面涉及一种根据反应式3制备由式(1)表示的多硫醇或其异构体的方法，所述方法包括以下步骤：
(1)通过使式(2)或式(3)的巯基化合物与缩水甘油化合物以1:1的当量比反应来制备式(5)或式(7)的多元醇化合物；以及
(2)将无机酸和硫脲添加到所制备的式(5)或式(7)的多元醇化合物中，将无机酸、硫脲以及多元醇的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
(反应式3)
(其中，R1'和R2'各自为-CH2CH(OH)CH2OH，且R3为-CH(CH2SH)CH2SH或-CH2CH(CH2SH)SH)。
本发明的又一方面涉及一种根据反应式4制备由式(1)表示的多硫醇或其异构体的方法，所述方法包括以下步骤：
(1)通过使式(2)或式(3)的巯基化合物与式(4)的表卤代醇化合物以2:1的当量比反应来制备式(5)或式(7)的多元醇化合物；以及
(2)将无机酸和硫脲添加到所制备的式(5)或式(7)的多元醇化合物中，将无机酸、硫脲以及多元醇的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
(反应式4)
(其中X为由以下所组成的族群中选出的一个：F、Cl、Br以及I，
R1'和R2'各自为-CH2CH(OH)CH2SCH2CH(OH)CH3或-CH2CH(OH)CH2SCH(CH3)CH2OH，以及
R3为-CH2CH(CH2SH)SCH2CH(CH3)SH、-CH2CH(CH2SH)SCH(CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH3)SH或-CH(CH2SH)CH2SCH(CH3)CH2SH)。
本发明的又一方面涉及一种根据反应式5制备由式(11)表示的多硫醇的方法，所述方法包括以下步骤：
(1)通过使式(12)的巯基化合物与式(4)的表卤代醇化合物以1:1的当量比反应来制备式(15)的中间化合物；
(2)通过将硫化钠水溶液添加到所制备的式(15)的中间化合物中以及通过使其反应来制备式(16)的多元醇化合物；以及
(3)将无机酸和硫脲添加到所制备的式(16)的多元醇化合物中，将无机酸、硫脲以及多元醇化合物的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
(反应式5)
(其中X和R1'与反应式1的每一取代基相同，
R1”为--CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH2CH3，
R3为由以下所组成的族群中选出的一个：
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH2CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH2CH(CH2CH3)SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH(CH2CH3)CH2SH、
-CH(CH2SH)CH2SCH(CH2SH)CH2SCH2CH(CH2CH3)SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH(CH2CH3)CH2SH、
-CH2CH(CH2SH)SCH2CH(CH2SH)SCH2CH(CH2CH3)SH、
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH(CH2CH3)CH2SH，以及
-CH2CH(CH2SH)SCH(CH2SH)CH2SCH2CH(CH2CH3)SH)。
本发明的又一方面涉及一种根据反应式6制备由式(11)表示的多硫醇或其异构体的方法，所述方法包括以下步骤：
(1)通过使式(12)的巯基化合物与式(4)的表卤代醇化合物以2:1的当量比反应来制备式(15)的多元醇化合物；以及
(2)将无机酸和硫脲添加到所制备的式(15)的多元醇化合物中，将无机酸、硫脲以及多元醇的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
(反应式6)
(其中，
X为由以下所组成的族群中选出的一个：F、Cl、Br以及I，
R1'为CH2CH(OH)CH2SCH2CH(OH)CH2CH3，
R3为-CH2CH(CH2SH)SCH(CH2CH3)CH2SH、-CH2CH(CH2SH)SCH2CH(CH2CH3)SH、-CH(CH2SH)CH2SCH(CH2CH3)CH2SH或-CH(CH2SH)CH2SCH2CH(CH2CH3)SH)。
在制备由式(1)表示的多硫醇的方法中，三乙基铝(TEA)或氢氧化钠(NaOH)可用作催化剂。此外，在制备由式(1)表示的多硫醇的方法中，无机酸可以是盐酸、硝酸、硫酸或氢溴酸。此外，碱性水溶液可以是氨水溶液、氢氧化钠水溶液、氢氧化锂水溶液或肼。
式(5)、式(7)或式(15)的醇中间化合物通过以下来制备且具有对称结构：使经低碳数烷基取代的约2或大于2当量的巯基乙基醇(例如反应式4中的式(2)或式(3)的化合物或反应式6中的式(12)的化合物)作为起始材料与1当量的式(4)的表氯醇化合物反应。
另外，式(5)、式(7)或式(15)的卤代醇中间化合物通过以下来制备：使经低碳数烷基取代的约1当量的巯基乙基醇(例如反应式1中的式(2)的化合物、反应式2中的式(3)的化合物或反应式5中的式(12)的化合物)作为起始材料与1当量的式(4)的表氯醇化合物反应。
式(6)、式(8)或式(16)的多元醇中间化合物通过以下来制备且具有对称结构：使约1当量的反应式1中的式(5)的化合物、反应式2中的式(7)的化合物或反应式5中的式(15)的化合物与0.5当量的Na2S反应。
如背景技术中所提及，在专利文件4(KR专利特许公开公布第10-2017-0078139号)的制备实例(1)和比较例(1)中，经卤代烷基取代的表氯醇化合物或环氧化合物与巯基乙基醇或经低碳数烷基取代的巯基乙基醇反应。然而，因为通过这一反应制备的多元醇中间化合物具有不对称结构，所以根据反应式1到反应式6，无法由这类多元醇中间化合物或经由这类不对称多元醇中间化合物制备多硫醇。
本发明的又一方面涉及一种作为多硫醇化合物的中间化合物的多元醇化合物，可通过反应式1或反应式2中的制备式(6)或式(8)的多元醇的方法来制备所述多元醇化合物，所述方法包含步骤(1)和步骤(2)。另外，可通过反应式3或反应式4中的制备式(7)的多元醇的方法来制备另一多元醇化合物，所述方法包含步骤(1)。如在制备多硫醇的方法中，制备作为中间化合物的多元醇化合物的方法可采用TEA或NaOH作为催化剂。
本发明的又一方面涉及一种聚(硫)氨基甲酸酯树脂组成物，其包括具有至少三个官能团的多硫醇以及聚异氰酸酯，所述具有至少三个官能团的多硫醇是通过上文所描述的方法中的一个来制备的。本文中，聚异氰酸酯的官能团(-NCO)与多硫醇化合物的官能团(-SH)的摩尔比(＝NCO/SH)在以下范围内：0.6到2.0，优选为0.8到1.3，更优选为0.9到1.1。在这一范围内，聚(硫)氨基甲酸酯树脂组成物可确保用于塑料透镜的光学材料和透明材料所需的各种功能之间的平衡，所述各种功能包含折射率、耐热性以及类似物。
本发明的又一方面涉及一种聚(硫)氨基甲酸酯树脂，所述聚(硫)氨基甲酸酯树脂是通过加热并固化聚(硫)氨基甲酸酯树脂组成物而形成的。此外，本发明的又一方面涉及一种聚(硫)氨基甲酸酯塑料光学体，所述聚(硫)氨基甲酸酯塑料光学体是通过制备聚(硫)氨基甲酸酯塑料透镜的方法而制造的，所述方法包含在模具中聚合聚(硫)氨基甲酸酯树脂组成物以及从模具中脱模经模制产物。本文中，聚异氰酸酯的官能团(-NCO)与多硫醇化合物的官能团(-SH)的摩尔比(＝NCO/SH)在以下范围内：0.6到2.0，优选为0.8到1.3，更优选为0.9到1.1。
虽然本发明的塑料光学体不仅可应用于光学透镜，并且还可应用于建筑物和类似物中使用的大面积窗，例如推拉窗、单悬窗或双悬窗、侧铰链窗以及类似物，在以下描述中，将塑料光学透镜主要描述为塑料光学体的一个实例。
附图说明
图1示出根据本发明的实例1(化合物1)的1H-NMR谱。
图2示出根据本发明的实例3(化合物3)的1H-NMR谱。
图3示出根据本发明的实例4(化合物4)的1H-NMR谱。
图4示出根据本发明的实例5(化合物5)的1H-NMR谱。
图5示出根据本发明的实例7(化合物7)的1H-NMR谱。
图6示出根据本发明的实例8(化合物8)的1H-NMR谱。
图7示出根据本发明的实例9(化合物9)的1H-NMR谱。
图8示出根据本发明的实例10(化合物10-1到化合物10-4的混合物，GPT)的1H-NMR谱。
图9示出根据本发明的实例11(化合物11-1到化合物11-4的混合物，MPT)的1H-NMR谱。
图10示出根据本发明的实例12(化合物12-1到化合物12-10的混合物，BPT)的1H-NMR谱。
图11示出根据本发明的实例13(化合物13-1到化合物13-10的混合物，BBT)的1H-NMR谱。
图12示出根据本发明的实例14(化合物14-1到化合物14-4的混合物，MBT)的1H-NMR谱。
具体实施方式
在下文中，将参考附图详细地描述本发明的实施例。
在由聚氨基甲酸酯树脂制备的透镜的机械特性之中，透镜的耐热性与聚氨基甲酸酯树脂的玻璃转化温度(Tg)有关，所述玻璃转化温度与其涉及色彩均匀度的染色特性具有相关度。因此，玻璃转化温度Tg的升高往往会使染色特性下降。一般来说，可从主链的灵活性和侧链的灵活性的视角来检测影响聚合物化合物的玻璃转化温度Tg的化学结构。与主链的灵活性相比，其中具有苯环的主链比不具有苯环的主链具有更低的灵活性，且使玻璃转化温度Tg升高。与侧链的灵活性相比，具有造成空间位阻的块官能团的侧链由于可旋转性劣化而具有较低灵活性，由此使得玻璃转化温度Tg升高。可通过实例叙述聚乙烯和聚丙烯。因此，可确认含有聚丙二醇的聚合物比含有聚乙二醇的聚合物具有更高的玻璃转化温度Tg。
基于这一事实，本发明的本发明人尝试使用环氧丙烷或环氧丁烷(而非所属领域中使用的环氧乙烷)作为用于制备2-巯基乙醇的起始材料来合成新颖多硫醇。在这种情况下，从环氧乙烷(C-2)到环氧丙烷(C-3)、环氧丁烷(C-4)以及类似物的单位分子改变同时在分子中维持相同结构序列。随后，预期在乙基的氢原子的数目由于甲基分子而增大时，玻璃转化温度Tg将由于侧链的影响而升高，由此达成本发明。
根据本发明，具有至少三个官能团且由式(a)或式(b)表示的多元醇或多硫醇化合物可通过根据反应式1到反应式6的过程来制备。
在本文中，除非另外确切地说明，否则由‘X’表示的‘卤素’是指氟、氯、溴或碘，优选为氯。
在本文中，‘低碳数烷基’是指具有1个到8个碳原子、优选为1个到6个碳原子、更优选为1个到4个碳原子的直链或分支链烷基。具体来说，低碳数烷基可以是甲基、乙基、正丙基、正丁基、正戊基、正己基、正庚基、正辛基、异丙基、异丁基、第二丁基、第三丁基、异戊基或类似基团，优选为甲基或乙基。
由式(a)或式(b)表示的多元醇化合物1到多元醇化合物9可具有以下结构且如下命名，在所述多元醇化合物1到多元醇化合物9中，其中Y为氧原子，Ra为甲基或乙基，且Rb为由前文所提及的取代基所组成的族群中选出的一个取代基。
此外，在由式(a)或式(b)表示的化合物之中获得具有以下结构且各自具有如下异构体的多硫醇化合物10到多硫醇化合物14，在所述由式(a)或式(b)表示的化合物中，Y为硫原子，Ra为甲基或乙基，且Rb为由前述取代基所组成的族群中选出的一个。
在多硫醇化合物的制备中，可确认在经由使上文所提及的多元醇中间化合物中的每一个与硫脲/盐酸反应来制备硫醚中间化合物后，可经由因空间位阻引起的重新排列来制备中间化合物。在中间化合物的水解后，可获得初级多硫醇作为所得化合物。由于对由根据本发明的方法制备的多硫醇进行的结构分析，可确认制备初级硫醇化合物与次级多硫醇一起作为主要产物。因此，可确认由根据本发明的方法制备的多硫醇组合物由异构体的混合物组成。下表示出理论上可产生的异构体。
(1)化合物10(GPT)和化合物11(MPT)的异构体
(2)化合物12(BPT)的异构体
代表性化合物12-1到化合物12-3的通用名称如下且省略其它化合物的名称：
-化合物12-1：3,3'-硫双(2-(1-巯基丙烷-2-基)硫基)-1-丙硫醇；
-化合物12-2：2-((3-巯基-2-((1-巯基丙烷-2-基)硫基)丙基)硫基)-3-((1-巯基丙烷-2-基)硫基)丙烷-1-硫醇；以及-化合物12-3：2,2'-硫双(3-(1-巯基丙烷-2-基)硫基)-1-丙硫醇
(3)化合物13(BBT)和化合物14(MBT)的异构体
虽然化合物13(BBT)可具有10个异构体，但化合物13-1、化合物13-2以及化合物13-3示出为其代表性异构体，且虽然化合物14(MBT)可具有四个异构体，但化合物14-1和化合物14-2示出为其代表性异构体。
接下来，将描述一种制备多元醇化合物1到多元醇化合物9的方法，和一种由所制备的多元醇化合物制备多硫醇化合物10到多硫醇化合物16的方法。
(多元醇制备方法)
如反应式1到反应式6中所示出，根据本发明的多元醇化合物可通过以下来制备：使表卤代醇化合物或缩水甘油化合物与作为多硫醇的中间化合物的巯基化合物以1:1的当量比或以2:1的当量比反应，如上文所描述。
表卤代醇化合物可由式4(其中X为卤素原子)表示且可从可商购产品获得：
另外，缩水甘油化合物(缩水甘油；羟甲基环氧乙烷)可由下式表示且可从中可商购产品获得：
显然，这类缩水甘油化合物可通过使过氧化苯甲酰与烯丙醇反应来制备，或通过以下来制备：加热表氯醇以及乙酸酐钾以制备乙酸盐；以及由所属领域中已知的方法用乙醚中的氢氧化钠处理所制备的乙酸盐。
多元醇的合成反应可在10℃到50℃、优选为20℃到30℃的温度下执行。如果在低于10℃的温度下执行反应，那么可由于反应速率的降低而使反应转化率下降。如果在高于50℃的温度下执行反应，那么与反应式中的表氯醇反应的式(2)、式(3)或式(12)的化合物可与杂质或二聚体一起制备出来。另外，可将用作巯基化合物的起始材料的式(2)、式(3)或式(12)的化合物添加0.5小时到10小时，优选为1小时到2小时。如果将起始材料添加小于0.5小时，那么可难以控制反应速率，且式(2)、式(3)或式(12)的化合物可与杂质或二聚体一起制备出来。可根据待使用的每一反应物和溶剂的特性而在上述范围内适当地调节反应温度和反应时间。
对于化合物1、化合物2、化合物3以及化合物7，可相对于1摩尔的表卤代醇以1摩尔、优选为0.9摩尔到1.1摩尔的量使用式(2)、式(3)以及式(12)的化合物中的每一个。如果以小于0.9的量使用化合物，那么未反应的表卤代醇可作为影响后续反应的杂质而残留。如果以大于1.1摩尔的量使用化合物，那么未反应的2-巯基丙醇与反应产物反应以制备具有对称结构的杂质，其中2-巯基丙醇与表卤代醇的两侧偶联。然而，对于化合物4和化合物9，式(2)、式3)以及式(12)的化合物中的每一个可相对于1摩尔的表卤代醇以2摩尔、优选为2摩尔到3摩尔的量使用。如果以小于2摩尔的量使用化合物，那么具有不对称结构的杂质可经由1摩尔的2-巯基丙醇与1摩尔的表卤代醇的反应而制备，且可影响后续反应。如果以大于3摩尔的量使用化合物，那么未反应的式(2)、式3)或式(12)化合物可残留且影响后续反应。虽然可由上述方法制备化合物5、化合物6以及化合物8，但可以类似当量使用式(2)、式3)以及式(12)的化合物中的每一个，以便抑制杂质的产生。
(多硫醇制备方法)
另外，将卤化钠添加到所制备的多元醇化合物中，且将无机酸和硫脲添加到混合物中，随后将混合物加热、搅拌并使其冷却到室温。随后，将碱性水溶液施加于混合物，以经由混合物的水解制备多硫醇化合物。所制备的多硫醇化合物可经历处理(work-up)过程，例如溶剂移除、过滤、汽化、纯化以及类似物。
如本文中所使用，无机酸可由以下中选出：盐酸、硝酸、硫酸、氢溴酸以及类似物。在用作无机酸时，氢溴酸可相对于1摩尔的多元醇化合物以3摩尔到5摩尔的量使用。本文中，可在100℃到105℃的温度下执行反应。如果在低于100℃的温度下执行反应，那么反应速率可显著地降低。反应可执行3小时到8小时，且可基于多元醇化合物是否完全耗尽而确认反应完成时间。对于无机酸，盐酸可相对于1摩尔的多元醇化合物以3摩尔到5摩尔的量使用。本文中，可在105℃到110℃的温度下执行反应。反应可执行12小时到24小时，且可基于多元醇化合物是否完全耗尽而确认反应完成时间。
如对于水解所使用的，碱性水溶液可由以下中选出：氨水溶液、氢氧化钠水溶液、氢氧化锂水溶液以及肼，优选为氨水溶液。虽然氢氧化钠和氢氧化锂可导致具有低溶解度的杂质的沉淀以及产率的下降，但氢氧化钠和氢氧化锂并不影响纯度。碱性水溶液可相对于1摩尔的多元醇化合物以3摩尔到10摩尔的量使用。本文中，反应可在20℃到100℃、优选为40℃到70℃的温度下执行。虽然反应可在没有溶剂的情况下发生，但溶剂可由以下中选出：甲苯、二氯甲烷、二甲苯、氯苯以及二氯苯，优选为甲苯。
一般来说，聚氨基甲酸酯类眼镜镜片通过以下来制备：在玻璃模具中热固化均匀光学组合物，随后从玻璃模具中脱模经模制产物，其中均匀光学组合物通过以下来制备：将作为具有液相(I)的聚氨基甲酸酯化合物的聚异氰酸酯与具有液相(II)的多元醇或多硫醇化合物混合，随后进行脱气(degassing)。
对于具有液相(I)的化合物，聚异(硫)氰酸酯化合物可由具有至少一个异(硫)氰酸酯基的任何化合物中选出，且不受限于特定化合物。聚异(硫)氰酸酯化合物的实例可分类成脂族聚异氰酸酯、脂环族聚异氰酸酯以及芳族聚异氰酸酯，且其特定实例于现有文件中公开且因此本文中不专门叙述。
在这些聚异氰酸酯化合物之中，优选使用间二甲苯基二异氰酸酯(XDI)、2,5(6)-双(异氰酸酯甲基)-双环[2,2,1]庚烷(NBDI)、1,6-六亚甲基二异氰酸酯(HDI)、异佛尔酮二异氰酸酯(IPDI)以及二环己基甲烷二异氰酸酯(HMDI)，且还可使用异氰酸酯的缩二脲衍生物和异氰酸酯的三聚体衍生物(例如聚异氰脲酸酯)。
可使用以下作为原材料来容易地制备缩二脲型异氰酸酯：1,2-亚乙基二异氰酸酯、1,3-亚丙基二异氰酸酯、1,4-亚丁基二异氰酸酯、1,6-六亚甲基二异氰酸酯、1,7-七亚甲基二异氰酸酯、1,8-八亚甲基二异氰酸酯、1,9-九亚甲基二异氰酸酯或1,10-十亚甲基二异氰酸酯。另外，所制备的缩二脲型异氰酸酯可在纯化之后使用或作为原单体材料的混合物使用。或者，缩二脲型异氰酸酯可从可商购产品获得，所述可商购产品例如德士模都(Desmodur)N100(拜耳公司(Bayer Co.,Ltd.))或罗地亚(Tolonate)HDB LV(帕斯公司(Perstop Co.,Ltd.))。另外，三聚体型异氰酸酯可使用与用于缩二脲型异氰酸酯的原材料相同的原材料而容易地制备，或可从可商购产品获得，所述可商购产品例如罗地亚HDT LV(康睿公司(Vencorex Co.,Ltd.))以及类似物。
另外，对于具有液相(II)的化合物，多硫醇可进一步包含由根据本发明的方法制备的额外多硫醇化合物以及多硫醇化合物。额外多硫醇化合物可由具有至少一个硫醇基的任何化合物或其混合物中选出，但不限于。具体地说，多硫醇化合物可包含由以下所组成的族群中选出的至少一个：
1,2-双(2-巯基乙基硫基)-3-巯基丙烷、三羟甲基丙烷三(巯基丙酸酯)、季戊四醇四(巯基丙酸酯)、2,3-双(2-巯基乙基硫基)丙烷-1-醇、2-(2-巯基乙基硫基)-3-[2-(3-巯基-2-(2-巯基乙基硫基)-丙基硫基]乙基硫基-丙烷-1-醇、2-(2-巯基乙基硫基)-3-{2-巯基-3-[3-巯基-2-(2-巯基乙基硫基)-丙基硫基]丙基硫基}-丙烷-1-醇、三羟甲基丙烷三(巯基丙酸酯、三羟甲基乙烷三(巯基丙酸酯)、丙三醇三(巯基丙酸酯)、三羟甲基氯三(巯基丙酸酯)、三羟甲基丙烷三(巯基乙酸酯)、三羟甲基乙烷三(巯基乙酸酯)、季戊四醇四(巯基丙酸酯)、季戊四醇四(巯基乙酸酯)、[1,4]二噻烷-2-基-甲硫醇、2-(2-巯基-乙基磺酰基)-丙烷-1,3-二硫醇、2-([1,4]二噻烷-2-基甲基磺酰基)-乙硫醇、3-(3-巯基-丙酰基磺酰基)-丙酸2-羟基甲基-3-(3-巯基-丙酰氧基)-2-(3-巯基-丙酰氧基甲基)-丙基酯、3-(3-巯基-丙酰基磺酰基)-丙酸3-(3-巯基-丙酰氧基)-2,2-双-(3-巯基-丙酰氧基甲基)-丙基酯、(5-巯基甲基-[1,4]二噻烷-2-基)-甲硫醇、1,3-双(2-巯基乙基硫基)丙烷-2-醇(GST)、(3,6,10,13-四硫杂十五烷-1,8,15-三硫醇)(SET)、2-(2-巯基乙基硫基)丙烷-1,3-二硫醇(GMT)、4,8-二巯基甲基-1,11-二巯基-3,6,9-三硫杂十一烷(DMDDU)以及其混合物。
在这些多硫醇化合物之中，优选使用1,3-双(2-巯基乙基硫基)丙烷-2-醇(GST)、(3,6,10,13-四硫杂十五烷-1,8,15-三硫醇)(SET)以及季戊四醇四(巯基丙酸酯)(PEMP)。更优选地，使用1,3-双(2-巯基乙基硫基)丙烷-2-醇(GST)与季戊四醇四(巯基丙酸酯)(PEMP)的混合物。
用作具有液相(I)的化合物的聚异氰酸酯的官能团(-NCO)与用作具有液相(II)的化合物的多硫醇的官能团(-SH)的摩尔比(NCO/SH)可介于0.5到1.5的范围内。优选地，摩尔比在0.9到1.1范围内，更优选为1.0，从而确保进一步改进光学透镜的特性。
在HDI缩二脲、HDI三聚体(HDI衍生物)、HDI以及IPDI一起使用作为聚异氰酸酯时，这些化合物可以30-40:20-30:30-40的重量比使用。虽然可单独使用由根据本发明的方法制备的多硫醇，但视需要，例如GST、PEMP以及类似物的典型聚硫醇可适当地与其混合，从而实现所需折射率和耐冲击性。
在根据本发明的可聚合组合物的制备中，组合物可包含各种添加剂，以便视需要获得透镜的必需光学特性，例如由可聚合组合物制备的树脂的透明度、折射率、比重、耐冲击性、耐热性以及粘度。组合物可进一步包含UV或近红外吸收剂、染料、光稳定剂、抗氧化剂以及类似物作为添加剂。此外，组合物可进一步包含可与氨基甲酸酯树脂组成物共聚合的环氧化合物、硫-环氧化合物、含乙烯基或不饱和基团的化合物或金属化合物。
此外，为了调节反应速率，组合物可进一步包含催化剂。催化剂可以是例如用于氨基甲酸酯反应的催化剂，且可由锡化合物中选出，例如二丁基二月桂酸锡、二氯化二丁基锡、二氯化二甲基锡、四甲基二乙酰氧基二锡氧烷、四乙基二乙酰氧基二锡氧烷、四丙基二乙酰氧基二锡氧烷以及四丁基二乙酰氧基二锡氧烷，或包含三级胺的胺化合物。这些可单独使用或以其混合物形式使用。催化剂可按组合物的单体的总重量计以0.001重量％到1重量％的量存在。在这一范围内，组合物可在由其制备的树脂的聚合性、适用期(pot life)、透明度、各种光学特性或耐光性方面具有良好特性。
另外，根据本发明的用于光学透镜的树脂组成物可进一步包含用于矫正透镜的初始色彩的上蓝剂(bluing agent)。上蓝剂的实例可包含有机染料、有机色素、无机颜料以及类似物。这类有机染料可在用于光学透镜的树脂组成物中以0.1ppm到50,000ppm、优选为0.5ppm到10,000ppm的量存在，从而实现透镜的色彩矫正以及UV吸收剂、光学树脂以及单体的添加。
根据本发明的用于光学透镜的树脂组成物可进一步包含典型脱模剂和典型聚合起始剂。脱模剂可由以下所组成的族群中选出：氟类非离子表面活性剂、硅类非离子表面活性剂、烷基四级铵盐以及其混合物。优选地，脱模剂为磷酸酯。另外，聚合起始剂可由胺类化合物和锡类化合物中选出。这些可单独使用或以其混合物形式使用。
针对眼镜镜片的特性评估根据本发明的聚氨基甲酸酯透镜。针对特性的评估，由以下方法来评估(1)折射率和阿贝数(υd)，(2)耐热性(Tg)，以及(3)热分析。
(1)折射率和阿贝数(υd)：在20℃下使用ABBE折射计(爱宕株式会社(ATAGOCo.,Ltd.)的1T模型)测量折射率和阿贝数。
(2)耐热性：样本的玻璃转化温度(Tg)是使用热分析仪DSC N-650(兴和公司(SCINCOCo.,Ltd.))来测量的，且经定义为耐热性。
(3)热分析：使用D-1(兴和公司)直接对塑料透镜样本执行透镜的热分析。
(制造光学透镜的代表性方法)
将构成聚异氰酸酯的单体和构成多硫醇的单体以特定比率混结合搅拌。随后，将预定量的脱模剂、UV吸收剂、有机染料以及固化催化剂添加到所制备的混合物中。随后，所制备的聚氨基甲酸酯光学树脂组成物经历预定时间段的脱气并注入到由粘合带组装的玻璃模具中。
此后，将含有混合物玻璃模具放置在强制循环式烘箱中。在烘箱中，通过以下来聚合混合物：在室温下维持混合物预定时段，逐渐升高混合物的温度，且在高温下维持混合物，随后冷却混合物。
在聚合完成之后，所得产物与模具分离，由此提供氨基甲酸酯光学透镜。随后，透镜在120℃下经历1小时和40分钟退火。在退火之后，未处理的透镜从玻璃模具中脱模，由此提供具有1.2毫米厚度的光学透镜。所制备的光学透镜经处理为直径为80毫米，且依序经历：在碱水清洗液体中的超音波洗涤、在120℃下退火2小时，以及通过浸渍在矽酮类硬性液体中来涂布，随后热干燥。
根据本发明的光学透镜可视需要经历物理处理和化学处理，例如出于给予抗反射特性、高硬度、耐磨性、耐化学性、防雾特性、时尚性以及类似物的目的的表面研磨、抗静电处理、硬涂布处理、非反射涂布处理、染色处理以及光致变色处理。
(实例)
在下文中，将结合制备实例和实例更详细地描述本发明。然而，应理解，这些制备实例和实例仅为了说明而提供，且本发明不限于此。
可容易地由环氧丙烷制备制备起始材料。由奥德里奇公司(Aldrich GmbH)的产品获得1-巯基丙烷-2-醇，且由博克西奇公司(Bocsic Co.,Ltd)的产品获得2-巯基丙烷-1-醇。
(多元醇的制备实例1到制备实例9)
制备实例1：1-氯-3-((2-羟丙基)硫基)丙烷-2-醇[化合物1]
将500克(5.43摩尔)的1-巯基丙烷-2-醇(奥德里奇公司)和54.9克的三乙胺放置在反应器中。随后，在将反应器的温度设置为15℃的情况下，将502克(5.43摩尔)的表氯醇缓慢逐滴添加到溶液中，由此制备1,002克的化合物1。根据图1的NMR-数据，化合物具有以下化学特性：1H-NMR(D2O),δppm＝1.26(3H,d,CH3),2.66到2.90(4H,m,CH2-S),3.70到3.82(2H,m,CH2-Cl)。
制备实例2：2-((3-氯-2-羟丙基)硫基)丙烷-1-醇[化合物2]
将500克(5.43摩尔)的2-巯基丙烷-1-醇和55.0克的三乙胺放置在反应器中。随后，在将反应器的温度设置为15℃的情况下，将502克(5.43摩尔)的表氯醇缓慢逐滴添加到溶液中，由此制备1,002克的化合物2。根据NMR-数据，化合物具有以下化学特性：1H-NMR(D2O),δppm＝1.25(3H,d,CH3),2.66到2.90(4H,m,CH2-S),3.65到3.82(2H,m,CH2-Cl)。
制备实例3：3-((2-羟丙基)硫基)丙烷-1,2-二醇[化合物3]
在将200克的H2O供应到反应器中之后，向其中添加105克(1.03摩尔)的三乙胺且将反应器的温度设置为25℃，同时搅拌反应器中的混合物。将200克(2.17摩尔)的1-巯基丙烷-2-醇添加到反应器中，且在将反应器的温度设置为20℃的情况下，将169克(2.28摩尔)的缩水甘油逐滴添加到溶液持续约1小时并另外搅拌，由此制备353.6克的化合物3。根据图2的NMR-数据，化合物具有以下化学特性：1H-NMR(D2O),δppm＝1.22(6H,d,CH3),2.63到2.81(4H,m,CH2-S),3.47到4.1(4H,m,CH-O,CH2-O),4.80(3H,s,OH)。
制备实例4：13-双[(2-羟丙基)硫基]-2-丙烷-2-醇[化合物4]
在将87.5克的H2O供应到反应器中之后，向其中添加87.3克(1.09摩尔)的氢氧化钠且将反应器的温度设置为25℃，同时搅拌反应器中的混合物。将199.2克(2.16摩尔)的1-巯基丙烷-2-醇添加到反应器中，随后将所述反应器的温度设置为20℃。此后，将100克(1.08摩尔)的表氯醇逐滴添加到反应器中持续约1小时，随后搅拌1小时，由此制备259.4克的化合物4。根据图3的NMR-数据，化合物具有以下化学特性：1H-NMR(D2O),δppm＝1.24(6H,d,CH3),2.63到2.87(8H,m,CH2-S),3.97(3H,m,CH-O),4.80(3H,s,OH)。
制备实例5：双[3-((2-羟丙基)硫基)-2-羟丙基]硫醚[化合物5]
在反应器维持于40℃的情况下，将890克(2.71摩尔)的硫化钠水溶液缓慢逐滴添加到制备实例1中所制备的化合物1中，随后搅拌1小时，由此制备896.6克的化合物5。根据图4的NMR-数据，化合物具有以下化学特性：1H-NMR(D2O),δppm＝1.29(6H,d,CH3),2.67到2.95(8H,m,CH2-S),4.02(4H,m,CH-O)
制备实例6：双[3-((1-羟基-丙烷-2-基)硫基)-2-羟丙基]硫醚[化合物6]
在反应器维持于40℃的情况下，将890克(2.71摩尔)的硫化钠水溶液缓慢逐滴添加到制备实例2中所制备的化合物2中，随后搅拌1小时，由此制备892.3克的化合物6。根据NMR-数据，化合物具有以下化学特性：1H-NMR(D2O),δppm＝1.25(6H,d,CH3),2.65到2.95(8H,m,CH2-S),4.07(4H,m,CH-O)。
制备实例7：1-((3-氯-2-羟丙基)硫基)丁烷-2醇[化合物7]
将500克(4.71摩尔)的1-巯基丁烷-2-醇和47.6克的三乙胺放置在反应器中。随后，在将反应器的温度设置为15℃的情况下，将435.7克(4.71摩尔)的表氯醇缓慢逐滴添加到溶液中，由此制备935.6克的化合物7。根据图5的NMR-数据，化合物具有以下化学特性：1H-NMR(MeOD),δppm＝0.94(3H,t,CH3),1.4到1.65(2H,m,CH2),2.58到2.82(4H,m,CH2-S-CH2),3.58到3.92(3H,m,CH-O/CH2-Cl),4.82(2H,s,OH)
制备实例8：双[3-((2-羟丁基)硫基)-2-羟丙基]硫醚[化合物8]
在反应器维持于40℃的情况下，将782克(2.35摩尔)的硫化钠水溶液缓慢逐滴添加到制备实例7中所制备的化合物7中，随后搅拌1小时，由此制备844.2克的化合物8。根据图6的NMR-数据，化合物具有以下化学特性。
1H-NMR(MeOD),δppm＝0.96(6H,t,CH3),1.41到1.68(4H,m,CH2),2.58到2.89(12H,m,CH2-S),3.61(2H,m,CH-O),3.88(2H,m,CH-O),4.81(4H,S,OH)
制备实例9：1,3-双[(2-羟丁基)硫基]丙烷-2-醇[化合物9]
在将87.5克的H2O供应到反应器中之后，向其中添加87.3克(1.09摩尔)的氢氧化钠且将反应器的温度设置为25℃，同时搅拌反应器中的混合物。将229.5克(2.16摩尔)的1-巯基丁烷-2-醇添加到反应器中，随后将所述反应器设置为20℃。此后，将100克(1.08摩尔)的表氯醇逐滴添加到反应器中持续约1小时，随后搅拌1小时，由此制备290.1克的化合物9。根据图7的NMR-数据，化合物具有以下化学特性。
1H-NMR(MeOD),δppm＝0.95(6H,t,CH3),1.40到1.68(4H,m,CH2),2.58到2.89(12H,m,CH2-S),3.61(2H,m,CH-O),3.88(2H,m,CH-O),4.91(3H,s,OH)
(多硫醇的实例10到实例12)
制备实例10：(2-((1-巯基丙烷-2-基)硫基)丙烷-1,3-二硫醇)[化合物10-1到化合物10-4]的制备(GPT)
在反应器中，将904克(8.68摩尔)的35％ HCl水溶液添加到制备实例3中所制备的化合物3中，随后添加512克(6.72摩尔)的硫脲。随后，在温度升高以及回流条件下在110℃下搅拌组分12小时到24小时。此后，在混合物冷却到室温的情况下，将600毫升的甲苯添加到混合物中，且将663.68克(9.76摩尔)的25％氨水缓慢地添加到混合物中，随后在65℃下水解3小时。由上述过程获得的有机层冷却到室温，随后依序用以下洗涤：200毫升的36％盐酸溶液、200毫升的水、200毫升的经稀释氨水以及200毫升的水洗涤三次。有机层经分离且经历真空蒸发，由此制备300克的无色且透明的多硫醇化合物。
作为在与制备实例11的高效液相层析法的条件相同的条件下分析所制备的化合物的结果，所制备的化合物由以下：组成约60％到约70％的化合物10-1作为主反应产物，以及40％或小于40％的作为化合物10-1的异构体的化合物10-2到化合物10-4。参看示出化合物10-1到化合物10-4的混合物的NMR-数据的图8，化合物10-1到化合物10-4具有以下化学特性：1H-NMR(CDCl3),δppm＝1.25到1.42(3H,m,CH3),1.68到2.0(3H,m,SH),2.59到3.33(8H,m,CH2-S,CH-S)；折射率1.618
制备实例11：(3-((1-巯基丙烷-2-基)硫基)-2((1-巯基丙烷-2-基)硫基)丙烷-1-硫醇)的制备)[化合物11-1到化合物11-4](MPT)
在反应器中，将394克(3.78摩尔)的35％ HCl水溶液添加(在30℃或小于30℃下)到制备实例4中所制备的化合物4中，随后添加250.9克(3.30摩尔)的硫脲。随后，在温度升高以及回流条件下在110℃下搅拌组分12小时到24小时。随后，在混合物冷却到室温的情况下，将550毫升的甲苯添加到混合物中，且将282.7克(4.32摩尔)的25％氨水缓慢地添加到混合物中，随后在65℃下水解3小时。使由上述过程获得的有机层的温度冷却到室温，随后依序用57毫升的36％盐酸溶液和400毫升的水洗涤。有机层经分离且经历真空蒸发，由此制备290克的无色且透明的多硫醇化合物。
制备实例11中所制备的化合物也具有四个异构体。因此，作为在与下文描述的高效液相层析法的条件相同的条件下分析所制备的化合物的结果，化合物11-1(主反应产物)以约84％到约88％的量存在，且作为化合物11-1的异构体的化合物11-2到化合物11-4中的每一个以8％或小于8％的量存在。根据图9NMR-数据，化合物11-1到化合物11-4具有以下化学特性：1H-NMR(CDCl3),δppm＝1.35到1.42(6H,m,CH3),1.70到2.28(3H,m,SH),2.59到3.16(11H,m,CH2-S,CH-S)；CH-S)；折射率1.601
用于异构体的确认的高效液相层析法(high performance liquid chromatography，HLPC)的条件如下：
用于高效液相层析法(HLPC)的条件
柱：Wathers ODS(Φ6毫米×250毫米)
移动相：乙腈/10毫摩尔-醋酸钠水溶液
90/10(vol/vol)→0/100(vol/vol)(20分钟的变化)
柱温：25℃
通量：1.0毫升/分钟
检测器：UV检测器，波长：215纳米
测量溶液浓度：100毫克的样本于10毫升乙腈中
注入量：10微升
异构体的峰面积比率
计算每一异构体的整合面积与作为多硫醇化合物的主反应产物制备的化合物11-1和作为其异构体制备的化合物11-2、化合物11-3以及化合物11-4的总面积的总和的比率。因此，化合物11-2以0.03到0.04的比率存在，化合物11-3以0.04到0.05的比率存在，且化合物11-4以0.03到0.08的比率存在。
制备实例12：3,3'-硫双(2-((1-巯基丙烷-2-基)硫基)-1-丙硫醇)[化合物12-1到化合物12-10](BPT)
在反应器中，将2,239.6克(13.5摩尔)的49％氢溴酸和836.3克(10.9摩尔)的硫脲添加到制备实例5中所制备的化合物5中，随后在105℃下加热6小时同时搅拌混合物。随后，使混合物冷却到室温，且将2,000克的甲苯和1,700克的水添加到混合物中，随后将所述混合物缓慢地加热到70℃。随后，将1,596克(9摩尔)的25％氨水缓慢逐滴添加到混合物中。从混合物中移除水层，且有机层经冷却到室温并经用100克的36％盐酸和1,000克的蒸馏水洗涤，随后真空蒸馏，由此制备1,070克的化合物12-1到化合物12-10。
作为在与制备实例11的高效液相层析法的条件相同的条件下分析所制备的化合物的结果，化合物12-1作为主反应产物以约63％到约70％的量存在，且作为化合物12-1的异构体的化合物12-2和化合物12-3中的每一个以14％或小于14％的量存在。其它异构体以约2％到约8％的总量存在。参看示出化合物12-1到化合物12-10的混合物的NMR-数据的图10，化合物12-1具有以下化学特性：
1H-NMR(CDCl3),δppm＝1.36到1.4(6H,m,CH3),1.65到2.32(4H,m,SH),2.6到3.18(16H,m,CH2-S,CH-S)；折射率1.621
制备实例13：2,2'-((硫双(1-巯基丙烷-3,2-二基))双(砜二基))双(丁烷-1-硫醇)[化合物13-1到化合物13-10](BBT)
在反应器中，将1,225.2克(11.8摩尔)的35％ HCl水溶液添加(在30℃或小于30℃下)到制备实例8中所制备的化合物8中，随后添加727.6克(9.56摩尔)的硫脲。随后，在温度升高以及回流条件下在110℃下搅拌组分12小时到24小时。此后，在混合物冷却到室温的情况下，将2,000毫升的甲苯添加到混合物中，且将846.6克(12.95摩尔)的25％氨水缓慢地添加到混合物中，随后在65℃下水解3小时。由上述过程获得的有机层冷却到室温，随后依序用100毫升的36％盐酸溶液和1000毫升的水洗涤。有机层经分离且经历真空蒸发，由此制备1,104克的无色且透明的多硫醇化合物作为化合物15。
作为在与制备实例11的高效液相层析法的条件相同的条件下分析所制备的化合物的结果，化合物13-1作为主反应产物以约60％到约70％的量存在，且作为化合物13-1的异构体的化合物13-2和化合物13-3中的每一个以15％或小于15％的量存在。其它异构体以约2％到约3％的总量存在。根据图11的NMR-数据，化合物具有以下化学特性。
1H-NMR(CDCl3),δppm＝1.11(6H,m,CH3),1.65(4H,m,SH),1.75到1.91(4H,m,CH2),2.62到3.15(16H,m,CH-S/CH2-S)；折射率1.602/>
制备实例14：3-((1-巯基丁烷-2-基)硫基)-2-((1-巯基丁烷-2-基)硫基)丙烷-1-硫醇[化合物14-1到化合物14-4](MBT)在反应器中，将394克(3.78摩尔)的35％ HCl水溶液添加(在30℃或小于30℃下)到制备实例9中所制备的化合物9中，随后添加250.9克(3.30摩尔)的硫脲。随后，在温度升高以及回流条件下在110℃下搅拌组分12小时到24小时。此后，在混合物冷却到室温的情况下，将550毫升的甲苯添加到混合物中，且将282.7克(4.32摩尔)的25％氨水缓慢地添加到混合物中，随后在65℃下水解3小时。由上述过程获得的有机层冷却到室温，随后依序用57毫升的36％盐酸溶液和400毫升的水洗涤。有机层经分离且经历真空蒸发，由此制备318.2克的无色且透明的多硫醇化合物作为化合物14-1到化合物14-4。
作为在与制备实例11的高效液相层析法的条件相同的条件下分析所制备的化合物的结果，化合物14-1作为主反应产物以约80％到约95％的量存在，且作为化合物14-1的异构体的化合物14-2到化合物14-4中的每一个以5％或小于5％的量存在。根据图12的NMR-数据，化合物具有以下化学特性。
1H-NMR(CDCl3),δppm＝1.11(6H,t,CH3),1.62(3H,m,SH),1.75到1.89(4H,m,CH2),2.62到3.0(9H,m,CH-S/CH2-S)；折射率1.599
如上文所描述，根据本发明的化合物由含有初级硫醇的多硫醇主要产物与含有次级硫醇的多硫醇异构体的混合物构成，所述初级硫醇具有巯基甲基。因此，根据本发明，可理解化合物10(GPT)的多硫醇化合物理论上由一个主化合物和4个异构体组成，且化合物11(MPT)和化合物14(MBT)中的每一个的多硫醇化合物理论上由一个主化合物以及其10个异构体之中的4个异构体组成，所述4个异构体不包含具有相同原子排列的异构体。另一方面，化合物12(BPT)和化合物13(BBT)中的每一个的多硫醇化合物具有其16个异构体之中的10个异构体，所述10个异构体不包含具有相同原子排列的异构体。
另一方面，如背景技术中所提及，专利文件4公开在于酸性条件下经由使含硫多元醇与硫脲反应制备异硫脲鎓盐(isothiouronium salt)化合物时具有羟基的碳位置处的异硫脲鎓盐的取代物。然而，认为允许经由空间位阻选择性引入硫脲的重新排列还在产生具有硫原子的表锍盐的活化过程中发生。随后，具有经修改的主链结构的异硫脲鎓盐化合物水解，由此产生一种化合物，所述化合物中巯基甲基经引入到多硫醇化合物的主链结构中。
综上所述，在制备根据本发明的多硫醇化合物的过程中，不认为在不经由空间位阻重新排列的情况下仅产生具有在具有羟基的碳位置处经取代的异硫脲鎓盐的化合物，如专利文件4中所公开。因此，认为无法将在放置多元醇中间化合物的羟基的碳位置处具有硫醇基的次级硫醇化合物制备为现有专利文件的制备实例(1)中的主反应产物。
接下来，使用根据本发明的多硫醇化合物以及所属领域中通常使用的聚异氰酸酯来制造光学透镜，且将其与比较例1到比较例4的光学透镜进行比较。具体地说，透镜经制备以根据透镜制备实例1到透镜制备实例13中的每一多硫醇评估透镜的特性。
1)根据制造上文所描述的光学透镜的代表性方法，制备实例中所制备的多硫醇化合物中的每一个、聚异氰酸酯化合物以及添加剂(脱模剂和聚合起始剂)以如表1到表4中列出的量混合，且在模具中经由聚合形成为光学透镜，随后评估折射率、阿贝数、耐热性以及类似物。
本文中，脱模剂为泽乐克(Zelec)UN(杜邦(Dupont))。聚合起始剂由二氯化二丁基锡和锡化合物中选出。另外，视需要使用UV吸收剂、上蓝剂(有机染料、有机颜料、无机颜料以及类似物)以及类似物。在以下实例中，参照公克(g)按照重量％表示每一组分的含量。
2)通过在75％ RH(相对湿度)和80℃的内部温度的条件下静置所制备的透镜1小时来观测多层分离。通过以下标准来评估分离：A：不分离，B：1或大于1分离标记，以及C：显著分离。
3)对于染色特性的评估，在85℃到95℃的温度下将使用各表中列出的例如XDI/BPT、XDI/BET、XDI/MPT、XDI/GST以及类似物的组合物制备的塑料透镜中的每一个浸渍在染色浴中5分钟，所述染色浴填充有500克的蒸馏水和17.5克的ONS黑的混合物。随后，评估每一透镜的染色的程度。
4)在实例1到实例13以及表1到表4中，BPT、MPT、GPT、BBT以及MBT分别是指制备实例10、制备实例11、制备实例12、制备实例14以及制备实例15中所制备的化合物，且这些化合物的缩略词示出于上述表中。另外，上文还提及与例如GST和BET(3,3'-硫双[2-[(2-巯基乙基)硫基]-1-丙硫醇)的熟知多硫醇化合物一起使用的异氰酸酯化合物，例如XDI、缩二脲、HDI、NBDI、IPDI以及HMDI，且因此将省略其详细描述。
在透镜制备实例1和透镜制备实例2中，分别使用XDI作为异氰酸酯以及MPT和BPT(替代GST以及BET)作为根据本发明的多硫醇化合物来制备透镜。随后，将所制备的透镜与比较例1和比较例2的可商购透镜进行比较。
在透镜制备实例3和透镜制备实例4中，分别使用缩二脲化合物作为异氰酸酯以及MPT和BPT(替代GST和BET)来制备透镜。随后，将所制备的透镜与比较例3和比较例4的可商购透镜进行比较。在透镜制备实例5到透镜制备实例10中，使用各种异氰酸酯(NBDI、IPDI以及HMDI)替代XDI来制备透镜。表3示出因玻璃转化温度Tg的升高而导致的例如耐热性和染色特性的功能的改进。另外，使用XDI和新颖多硫醇化合物作为根据本发明的多硫醇化合物来制备透镜，所述新颖多硫醇化合物例如GPT、MBT以及BBT。表4示出这些透镜的折射率、阿贝数、耐热性、染色特性以及功能。
透镜制备实例1和透镜制备实例2
下表示出根据本发明的透镜以及比较例的透镜中的每一个的折射率、阿贝数、耐热性以及多层分离。
[表1]
1)比较例1：三井化学公司的可商购产品，折射率(1.657)，且
耐热性：85℃
2)比较例2：三井化学公司的可商购产品，折射率(1.655)，且
耐热性：100℃
3)染色特性：◎：极佳，○：良好，△：正常，X：较差
4)分离：A：不分离，B：一或多个分离标记；C：显著分离
比较例1的透镜主要由作为异氰酸酯的XDI以及作为多硫醇化合物的GST构成，且具有约85℃的玻璃转化温度Tg以及耐热性较低的缺点。所属领域中已知这一透镜在例如蒸汽浴以及类似物的高温条件下经历多层涂布分离。另一方面，这一透镜具有良好染色特性，以便改进功能例如UV或日光屏蔽。为了解决低耐热性的问题，三井化学公司研发了一种新颖产物(比较例2)。比较例2的透镜主要由XDI和替代GST作为多硫醇化合物的BET构成。然而，所属领域中已知的这一透镜未能满足对于改进功能的染色特性，尽管耐热性已改进。
在表1中，将经历多层涂布的分离的比较例1的透镜与根据本发明的实例1-1到实例1-3的透镜进行比较。参看表1，实例的透镜具有类似于比较例1的透镜的折射率，且相比于比较例1的透镜具有12.3℃的更高耐热性，以及改进的阿贝数，具体地说染色特性。在透镜制造之后的多层涂布时，比较例1的透镜在75％ RH和80℃的条件下经受多层涂布的损坏，然而实例1的透镜在不于相同条件下受多层涂布损坏的情况下维持其初始形状。因此，可确认对应于根据本发明的多硫醇化合物的MPT比所属领域中使用的GST具有更好的特性。
另外，实例2-1到实例2-3的透镜比比较例2的透镜具有略微更好的折射率和耐热性，且呈现良好染色特性。因此，可确认对应于根据本发明的多硫醇化合物的BPT具有与所属领域中使用的BET类似的特性或具有比所属领域中使用的BET更好的特性。
透镜制备实例3和透镜制备实例4
由与以上实例相同的方法制备透镜，不同之处在于使用六亚甲基二异氰酸酯缩二脲作为异氰酸酯替代XDI，且用于化合物的组分的量如表1中所列发生改变。
[表2]
在表2中，如比较例3和比较例4的透镜，使用相同异氰酸酯(即缩二脲)来制备实例3和实例4的透镜。与比较例1的透镜相比，实例3的透镜的耐热性改进约10℃或大于10℃，且实例3的透镜呈现极好染色特性，尽管折射率降低。在透镜制造之后的多层涂布时，比较例3的透镜在75％ RH和80℃的条件下经受多层涂布的损坏。然而，实例3的透镜在不于相同条件下经受多层涂布的损坏的情况下维持其初始形状。因此，可确认对应于根据本发明的多硫醇化合物的MPT比所属领域中使用的GST具有更好的特性。
与比较例4的透镜相比，实例4的透镜的耐热性改进约10℃或大于10℃，且实例4的透镜呈现极好染色特性(因为实例4的透镜具有良好染色特性，所以两个透镜具有类似染色特性)，尽管折射率降低。因此，可确认对应于根据本发明的多硫醇化合物的BPT具有与所属领域中使用的BET类似的特性或具有比所属领域中使用的BET更好的特性。
透镜制备实例5到透镜制备实例10
由与以上实例相同的方法制备透镜，不同之处在于使用NBDI作为异氰酸酯，且用于化合物的组分的量如表1中所列出发生改变。
[表3]
[表3]示出可适用于透明光学透镜的非黄化异氰酸酯之中的NBDI、IPDI以及HMDI的含量。本文中，根据MPT和BPT来比较由与上述实例中相同的方法制备的透镜的特性。作为实例5和实例6的透镜的制备中使用的异氰酸酯化合物，NBDI提供约1.604到1.614的折射率，且NBDI-BPT的组合提供约43的极高阿贝数。NBDI-BPT的组合提供133.3℃的极高耐热性，且NBDI-MPT的组合还提供124.7℃的极高耐热性且因此可适用于改进耐热性。这些透镜还在染色特性和多层分离的抑制方面呈现良好特性。
使用IPDI制备实例7和实例8的透镜。使用IPDI-MPT的组合制备的实例7的透镜具有约106.1℃的耐热性且呈现良好染色特性，所述染色特性与耐热性有关。实例8的透镜具有约123.1℃的耐热性，且因此实现耐热性的显著改进。
使用HMDI制备实例9和实例10的透镜。使用HMDI-MPT的组合制备的实例9的透镜具有约45的极高阿贝数和极好染色特性。
透镜制备实例11到透镜制备实例13
评估使用各种异氰酸酯制备的透镜的特性以便确定作为透明透镜的透镜的可用性。本文中，针对折射率、阿贝数、耐热性、染色特性以及类似物评估透镜。另外，使用XDI作为异氰酸酯和具有细长链结构的GPT、MBT或BBT(例如氧化丁烯)作为替代MPT或BPT(其为环氧丙烷的衍生物)的多硫醇制备透镜，从而确定GPT、MBT和BBT以及XDI的适用性。
[表4]
在表4中，实例11、实例12以及实例13的透镜具有1.63或大于1.63的折射率，尽管折射率低于表1中所示出的比较例1和比较例2的透镜的折射率，由此示出根据本发明的化合物可应用于需要相对较高折射率和超高折射率的材料。另外，这些实例中制备的透镜呈现耐热性、染色特性以及多层分离的抑制的改进。
对于实例11的透镜，这类差异实际上由使用GPT替代表1中的比较例1的透镜的制备中所使用的GST而产生，所述GPT为使用化合物3的多元醇制备的多硫醇，所述化合物3的多元醇是使用来源于环氧丙烷的1-巯基丙烷-2-醇和替代表氯醇的缩水甘油制备的。根据本发明，在多硫醇的体积经由甲基或乙基对多硫醇的侧链的取代而增大时，透镜的玻璃转化温度维持在110℃下，由此改进耐热性同时针对功能的改进提供良好染色特性。
使用多元醇和多硫醇制备实例12和实例13的透镜，其是由氧化丁烯替代环氧丙烷而制备的。使用MBT替代GST制备的实例12的透镜呈现高折射率和良好染色特性，尽管玻璃转化温度Tg出乎意料地低。使用BBT替代BET制备的实例13的透镜具有1.638的高折射率和94.2℃的玻璃转化温度Tg，从而提供适合于上色的耐热性。从这些结果中，可看出，根据本发明的多元醇和多硫醇化合物具有对于新颖多硫醇或氨基甲酸酯光学材料的适用性。
将使用根据本发明的各种多硫醇化合物制备的实例1到实例13的光学透镜的特性与比较例1到比较例4的透镜的特性进行比较。因此，可看出，根据本发明的透镜通常具有改进的耐热性以在高温条件下抑制多层分离，所述高温条件例如蒸汽浴以及类似物。另外，可看出，根据本发明的透镜经改变以经由放大方法呈现最适合的耐热性。此外，可看出，根据本发明的透镜具有染色特性和阿贝数的改进，从而即使在用户长时间段佩戴所述透镜时仍减少眼睛的疲乏。因此，可看出，可使用根据本发明的新颖多硫醇来制造相比于所属领域中的透镜具有耐热性、染色特性、阿贝数的改进且抑制多层分离的透镜。
因此，在根据本发明的多硫醇化合物用作氨基甲酸酯类光学材料的可聚合组合物的主要组分时，可制造具有良好耐热性的光学透镜。具体地说，常规的多硫醇化合物源于‘2-巯基乙醇’，然而根据本发明的多硫醇化合物源于‘2-巯基丙醇’、‘1-巯基丙烷-2-醇’或‘1-巯基丁烷-2-醇’。因此，认为根据本发明的多硫醇化合物实现用于光学材料的便宜氨基甲酸酯类树脂的制备，且因此可广泛地应用于用于光学透镜的材料。
作为常规多硫醇化合物的起始材料，2-巯基乙醇由环氧乙烷和硫化氢制备，然而根据本发明的多硫醇化合物的1-巯基丙烷-2-醇可由环氧丙烷和硫化氢制备。所属领域中所使用的环氧乙烷在室温下具有气相且具有难以处理和在室温下爆炸的高可能性的问题，然而本发明中所使用的环氧丙烷在室温下具有液相且易于处理且在室温下稳定性良好。因此，认为根据本发明的多硫醇化合物使得能够经济上便宜地制备1-巯基丙烷-2-醇，且因此比常规的多硫醇化合物具有更好的经济可行性。
根据本发明的用于光学材料的聚氨基甲酸酯树脂不受限于透镜。举例来说，可对聚氨基甲酸酯树脂衬底施加偏振功能(polarizing function)(使允许仅在特定角度下透射光的非金属材料的表面上的反射最小化的功能)和调光功能(dimming function)(使得能够基于周围环境和空间用途来自动控制照明强度的功能)。此外，可对用于眼镜镜片的聚氨基甲酸酯树脂衬底施加视力矫正功能。
另一方面，聚氨基甲酸酯树脂衬底作为以上描述中的光学体应用于眼镜镜片。然而，应理解，根据本发明的光学体还可视需要作为构造材料应用于建筑物和类似物中使用的大面积窗，例如推拉窗、单悬窗或双悬窗、侧铰链窗以及类似物。为了将根据本发明的聚氨基甲酸酯树脂组成物应用于这类大面积窗，聚氨基甲酸酯树脂组成物可进一步包含对应于额外功能的添加剂。举例来说，树脂组成物可形成为对应于窗框的形状，在具有各种形状的玻璃模具中经固化，且从模具中脱模以用于建筑物中。
Claims (16)
1.一种多硫醇化合物，所述多硫醇化合物具有至少三个官能团且由式a或式b表示：
其中Y为硫原子；
Ra为甲基或乙基；
Rb为-CH(CH2SH)CH2SH、
-CH2CH(CH2SH)SCH(CH3)CH2SH、
-CH2CH(CH2SH)SCH(CH2CH3)CH2SH、
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH3)CH2SH或
-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH2CH3)CH2SH。
2.一种制备由式1表示的多硫醇的方法，所述方法包括以下步骤：
通过使式2的巯基化合物与式4的表卤代醇化合物以1:1的当量比反应来制备式5的中间化合物；
通过将硫化钠水溶液添加到所制备的所述式5的中间化合物中以及通过使其反应来制备式6的多元醇化合物； 以及
将无机酸和硫脲添加到所制备的所述式6的多元醇化合物中，将所述无机酸、所述硫脲以及所述式6的多元醇化合物的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
反应式1
其中
X为由以下所组成的族群中选出的一个：F、Cl、Br以及I，
R1'为由以下所组成的族群中选出的一个：-CH2CH(OH)CH2F、-CH2CH(OH)CH2Cl、-CH2CH(OH)CH2Br以及-CH2CH(OH)CH2I，
R1”为-CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH3或-CH2CH(OH)CH2SCH2CH(OH)CH2SCH(CH3)CH2OH， 以及
R3为-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH3)CH2SH。
3.一种制备由式1表示的多硫醇的方法，所述方法包括以下步骤：
通过使1当量的式3的巯基化合物与1当量的式4的表卤代醇化合物反应来制备式7的中间化合物；
通过将硫化钠水溶液添加到所制备的所述式7的中间化合物中以及通过使其反应来制备式8的多元醇化合物； 以及
将无机酸和硫脲添加到所制备的所述式8的多元醇化合物中，将所述无机酸、所述硫脲以及所述式8的多元醇化合物的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
反应式2
其中
X为由以下所组成的族群中选出的一个：F、Cl、Br以及I，
R2'为由以下所组成的族群中选出的一个： -CH2CH(OH)CH2F、-CH2CH(OH)CH2Cl、-CH2CH(OH)CH2Br以及-CH2CH(OH)CH2I，
R2"为-CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH3或
-CH2CH(OH)CH2SCH2CH(OH)CH2SCH(CH3)CH2OH，
R3为-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH3)CH2SH。
4.一种制备由式1表示的多硫醇的方法，所述方法包括以下步骤：
通过使式2的巯基化合物或式3的巯基化合物与缩水甘油化合物以1:1的当量比反应来制备式5的多元醇化合物或式7的多元醇化合物； 以及
将无机酸和硫脲添加到所制备的所述式5的多元醇化合物或所述式7的多元醇化合物中，将所述无机酸、所述硫脲以及所述式5的多元醇化合物或所述式7的多元醇化合物的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
反应式3
其中R1'和R2'各自为-CH2CH(OH)CH2OH，且R3为-CH(CH2SH)CH2SH。
5.一种制备由式1表示的多硫醇的方法，所述方法包括以下步骤：
通过使式2的巯基化合物或式3的巯基化合物与式4的表卤代醇化合物以2:1的当量比反应来制备式5的多元醇化合物或式7的多元醇化合物； 以及
将无机酸和硫脲添加到所制备的所述式5的多元醇化合物或所述式7的多元醇化合物中，将所述无机酸、所述硫脲以及所述式5的多元醇化合物或所述式7的多元醇化合物的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
反应式4
其中X由以下所组成的族群中选出：F、Cl、Br以及I，
R1'和R2'各自为-CH2CH(OH)CH2SCH2CH(OH)CH3或-CH2CH(OH)CH2SCH(CH3)CH2OH，以及
R3为-CH2CH(CH2SH)SCH(CH3)CH2SH。
6.一种制备由式11表示的多硫醇的方法，所述方法包括以下步骤：
通过使式12的巯基化合物与式4的表卤代醇化合物以1:1的当量比反应来制备式15的中间化合物；
通过将硫化钠水溶液添加到所制备的所述式15的中间化合物中以及通过使其反应来制备式16的多元醇化合物； 以及
将无机酸和硫脲添加到所制备的所述式16的多元醇化合物中，将所述无机酸、所述硫脲以及所述式16的多元醇化合物的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
反应式5
其中
X为由以下所组成的族群中选出的一个：F、Cl、Br以及I，
R1'为由以下所组成的族群中选出的一个： -CH2CH(OH)CH2F、-CH2CH(OH)CH2Cl、-CH2CH(OH)CH2Br以及-CH2CH(OH)CH2I，
R1”为-CH2CH(OH)CH2SCH2CH(OH)CH2SCH2CH(OH)CH2CH3， 以及
R3为-CH(CH2SH)CH2SCH2CH(CH2SH)SCH(CH2CH3)CH2SH。
7.一种制备由式11表示的多硫醇的方法，所述方法包括以下步骤：
通过使式12的巯基化合物与式4的表卤代醇化合物以2:1的当量比反应来制备式15的多元醇化合物； 以及
将无机酸和硫脲添加到所制备的所述式15的多元醇化合物中，将所述无机酸、所述硫脲以及所述式15的多元醇化合物的混合物加热、搅拌并使其冷却到室温，然后将碱性水溶液添加到所得产物中以使所述所得产物水解：
反应式6
其中
X为由以下所组成的族群中选出的一个：F、Cl、Br以及I，
R1'为CH2CH(OH)CH2SCH2CH(OH)CH2CH3， 以及
R3为-CH2CH(CH2SH)SCH(CH2CH3)CH2SH。
8.根据权利要求3至7中任一项所述的制备多硫醇的方法，其中三乙基铝或氢氧化钠用作催化剂。
9.根据权利要求3至7中任一项所述的制备多硫醇的方法，其中所述无机酸为盐酸、硝酸、硫酸或氢溴酸。
10.根据权利要求3至7中任一项所述的制备多硫醇的方法，其中所述碱性水溶液为氨水溶液、氢氧化钠水溶液、氢氧化锂水溶液或肼。
11.一种聚(硫)氨基甲酸酯树脂组合物，包括如权利要求1所述的具有至少三个官能团的多硫醇化合物以及聚异氰酸酯。
12.根据权利要求11所述的聚(硫)氨基甲酸酯树脂组合物，其中所述聚异氰酸酯的官能团(-NCO)与所述多硫醇化合物的官能团(-SH)的摩尔比(NCO/SH)在0.8到1.3范围内。
13.一种聚(硫)氨基甲酸酯树脂，通过加热并固化如权利要求11所述的聚(硫)氨基甲酸酯树脂组合物来制备。
14.一种聚(硫)氨基甲酸酯类塑料光学体，通过以下来制备：在模具中聚合如权利要求11所述的聚(硫)氨基甲酸酯树脂组合物； 以及从所述模具中脱模经模制产物。
15.根据权利要求14所述的聚(硫)氨基甲酸酯类塑料光学体，其中所述聚异氰酸酯的官能团(-NCO)与多所述硫醇化合物的官能团(-SH)的摩尔比(NCO/SH)在0.8到1.3范围内。
16.根据权利要求14或15所述的聚(硫)氨基甲酸酯类塑料光学体，其中所述聚(硫)氨基甲酸酯类塑料光学体为光学眼镜或光学透镜。