CN112236288A - 片及片的制造方法 - Google Patents
片及片的制造方法 Download PDFInfo
- Publication number
- CN112236288A CN112236288A CN201980037796.9A CN201980037796A CN112236288A CN 112236288 A CN112236288 A CN 112236288A CN 201980037796 A CN201980037796 A CN 201980037796A CN 112236288 A CN112236288 A CN 112236288A
- Authority
- CN
- China
- Prior art keywords
- sheet
- plastic
- resin
- group
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供应变得到了抑制的薄壁片。本发明的片是由塑料制成的厚度为0.1~5mm的片,所述塑料包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种,该片的延迟值的最大值与最小值之差为3000nm以下。本发明的片例如可以如下所述地制造:对包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种的塑料实施挤出成型而得到片状塑料,对得到的片状塑料实施真空成型、压空成型、或真空压空成型。
Description
技术领域
本发明涉及一种低应变性优异的片及其制造方法。本申请主张于2018年6月5日向日本申请的日本特愿2018-108102号的优先权,在此援用其内容。
背景技术
塑料制眼镜的镜片、头盔的护罩通常通过对作为原料的塑料实施注塑成型而制造(例如专利文献1)。然而,在使塑料以高速在狭窄的流道通过的注塑成型中,容易在所得成型体中残留有大的应变。而且,已知在通过注塑成型制造经薄化的镜片、护罩的情况下,会残留特别大的应变。如果镜片、护罩存在大的应变,则会引发眼睛疲劳、头痛等症状,存在难以长时间佩戴的问题。另外,存在大的应变的镜片、护罩在实施加工时容易发生破裂。因此,谋求一种应变得到了抑制的薄化镜片、薄化护罩。
现有技术文献
专利文献
专利文献1:日本特开2010-37475号公报
发明内容
发明所要解决的问题
因此,本发明的目的在于提供一种应变得到了抑制的薄壁片。
本发明的其它目的在于提供一种应变得到了抑制的镜片或护罩。
本发明的其它目的在于提供一种具备应变得到了抑制的片的防护用具。
本发明的其它目的在于提供一种抑制了应变且具有曲面形状的薄壁片的制造方法。
解决问题的方法
本发明认为了解决上述问题而进行了深入研究,结果发现通过对特定的塑料实施挤出成型,可以得到应变得到了抑制的薄壁片。本发明是基于这些见解而完成的。
即,本发明提供一种片,其是由塑料制成的厚度为0.1~5mm的片,所述塑料包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种,该片的延迟值的最大值与最小值之差为3000nm以下。
另外,本发明提供上述片,其具有曲面形状。
另外,本发明提供上述片,其雾度值为5%以下。
另外,本发明提供上述片,其中,上述塑料在23℃下的光弹性系数为0.1×10-12~100×10-12cm2/dyn。
另外,本发明提供上述片,其中,上述塑料为包含脂环式聚酰胺树脂的塑料。
另外,本发明提供上述片,其中,上述脂环式聚酰胺树脂具有下述式(ad)表示的重复单元。
[化学式1]
(式中,X表示单键或2价烃基,L表示2价烃基。R1、R2表示烷基,m、n表示0~4的整数)。
另外,本发明提供一种镜片,其包含上述片作为构成要素。
另外,本发明提供一种护罩,其包含上述片作为构成要素。
另外,本发明提供一种防护用具,其具备包含上述片作为构成要素的镜片或护罩。
另外,本发明提供上述片的制造方法,该方法包括:通过对包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种的塑料实施挤出成型而得到片状塑料,对得到的片状塑料实施真空成型、压空成型、或真空压空成型,由此得到具有曲面形状的片。
需要说明的是,在本说明书中,用双折射率(Δn)与厚度(d)之积定义片的延迟值(Retardation;Δn·d)。
发明的效果
本发明的片薄且为低应变。而且透明性优异。因此,包含本发明的片的镜片、护罩的视觉辨认性优异,使用该片时,能够消除由应变引发的眼睛疲劳、头痛等问题。另外,该片是轻质的。因此,可以舒适地长时间佩戴。此外,加工性优异,可以抑制加工成眼镜、头盔等时发生破裂,提高成品率。
特别是在本发明的片由含有特定的聚酰胺树脂的塑料形成的情况下,其尤为轻质,应变小,而且即使直接开孔也不易发生龟裂等,加工性优异。另外,耐热性及耐药品性也优异。
因此,本发明的片可以适宜地用于眼镜(例如太阳镜、护目镜等)、头盔(例如作业用头盔、摩托车用头盔、运动用头盔)、医疗用防护面罩、面部防护用具等。
具体实施方式
[片]
本发明的片由塑料形成,所述塑料包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种。
本发明的片的厚度为0.1~5mm,上限优选为4mm、特别优选为2mm。另外,下限优选为0.5mm、特别优选为1mm。
本发明的片的延迟值的偏差小,上述片(尺寸:纵30cm×横30cm)的延迟值的最大值与最小值之差为3000nm以下、优选为2000mm以下、特别优选为800mm以下、最优选为500nm以下、尤其优选为400nm以下。因此,本发明的片为低应变,使用本发明的片形成的镜片、护罩不易引发眼睛疲劳、头痛等症状,可以舒适地长时间佩戴。
另外,在本发明的片中,特别是平面状片的延迟值的最大值例如为3000nm以下、优选为2500nm以下、特别优选为1800nm以下、最优选为1000nm以下、尤其优选为500nm以下、尤其优选为400nm以下。另外,最大值的下限例如为100nm、其中为150nm。
另外,在本发明的片中,特别是平面状片的延迟值的最小值例如小于100nm、优选为70nm以下、特别优选小于50nm、最优选为45nm以下。另外,最小值的下限例如为10nm、其中为5nm。
本发明的片中,特别是曲面形状的片(例如6曲面镜片)的延迟值的最大值例如为3000nm以下、优选为2500nm以下、更优选为2000nm以下、特别优选为1000nm以下、最优选为600nm以下、尤其优选为400nm以下。另外,最大值的下限例如为100nm、其中为150nm、特别地为200nm。
在本发明的片中,特别是曲面形状的片的延迟值的最小值例如小于100nm、优选为70nm以下、特别优选小于50nm、最优选为45nm以下。另外,最小值的下限例如为10nm、其中为5nm。
本发明的片可以具有曲面形状,例如,可以为镜片形状、护罩形状。具有曲面形状的本发明的片中包含例如4~8曲面镜片。上述镜片的中心厚度例如为0.5~2.5mm、优选为1.0~2.0mm、特别优选为1.5~2.0mm。
本发明的片的透明性优异,雾度值例如为5%以下、优选为2%以下、特别优选为1%以下、最优选为0.9%以下。因此,可以适宜地用作镜片、护罩。需要说明的是,本发明中的雾度值通过基于JIS K 7136(2000)的方法来测定。
从可以将应变抑制为特别小的水平的方面考虑,形成本发明的片的塑料在23℃下的光弹性系数优选为例如0.1×10-12~100×10-12cm2/dyn、更优选为0.1×10-12~50×10- 12cm2/dyn、进一步优选为0.1×10-12~10×10-12cm2/dyn、特别优选为0.2×10-12~7×10- 12cm2/dyn、最优选为1×10-12~5×10-12cm2/dyn。
本发明的片可以通过对包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种的塑料实施挤出成型而制造。
需要说明的是,挤出成型是指,将在挤出机内加热熔融后的塑料从模口喷出并成型为期望的形状的方法。
加热熔融温度可以根据塑料材料适当选择,例如为180~350℃、优选为200~330℃、更优选为230~320℃。
本发明的片中的具有曲面形状的片可以如下所述地制造:对包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种的塑料实施挤出成型而得到片状塑料(或者是本发明的片中的平面状片),对得到的片状塑料实施真空成型、压空成型、或真空压空成型而制造。
作为待进行成型的片状塑料的厚度,优选比期望的成型品的壁厚厚,例如优选为超过期望的成型品的壁厚的1倍且为2倍以下,特别优选为1.5~2倍。
需要说明的是,真空成型是指下述方法:对经过挤出成型而得到的片状塑料进行加热而使其软化,使片状塑料蔓延至期望的曲面形状的凸模或凹模、或两模中,对模具内进行真空抽吸,使片状塑料密合于模具而进行成型。
压空成型是指,除了代替真空抽吸而通过压空而使片密合于模具以外与真空成型同样的方法。
真空压空成型是指,除了通过同时或隔开时间差实施真空抽吸和压空密合从而使片密合于模具以外与真空成型同样的方法。
根据这些方法,可以抑制在得到的片的内部残留应力,其结果,可以抑制应变的发生。另外,与注塑成型等相比,可以得到进一步薄化的片。
上述塑料含有后述的选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种。此外,在不损害光学特性、处理性等的范围内,作为添加剂,可以含有选自例如调光材料、光吸收剂(紫外线、蓝色光、红外线等)、着色剂、热稳定剂、光稳定剂、抗氧剂、增塑剂、阻燃剂、抗静电剂、粘度调整剂等中的一种或两种以上,但上述树脂在塑料总量(100重量%)中所占的比例(含有两种以上的情况下为其总量)例如为80重量%以上、优选为90重量%以上、特别优选为95重量%以上。需要说明的是,树脂所占的比例的上限为100重量%。
作为上述塑料,从可得到应变被抑制为极小水平的薄壁片(或者镜片或护罩)的方面考虑,优选含有选自后述的聚酰胺树脂、酰化纤维素树脂、及丙烯酸树脂中的至少一种。
作为上述塑料,从可得到应变被抑制为极小水平、且透明性特别优异的薄壁片(或者镜片或护罩)的方面考虑,优选含有选自后述的酰化纤维素树脂及丙烯酸树脂中的至少一种。
作为上述塑料,从可得到应变被抑制为极小水平、且透明性特别优异的薄壁片(或者镜片或护罩)的方面、以及轻质且加工性优异的方面考虑,优选含有选自后述的聚酰胺树脂及聚碳酸酯树脂中的至少一种,尤其优选至少含有聚酰胺树脂、
(聚酰胺树脂)
聚酰胺树脂是多个单体通过酰胺键键合而成的聚合物,可列举作为单体的二胺成分与二羧酸成分的缩聚物、作为单体的内酰胺类的开环聚合物。二胺成分及二羧酸成分可以分别单独使用一种、或者组合使用两种以上。另外,内酰胺类也可以单独使用一种、或者组合使用两种以上。
作为上述二胺成分,可列举例如下述式(a)表示的化合物。
[化学式2]
H2N-L1-NH2 (a)
(式中,L1表示2价烃基)
上述2价烃基包含2价脂肪族烃基、2价脂环式烃基、2价芳香族烃基。
作为2价脂肪族烃基,可列举例如:亚甲基、甲基亚甲基、二甲基亚甲基、亚乙基、亚丙基、三亚甲基等碳原子数1~20的直链或支链状的亚烷基;亚乙烯基、1-甲基亚乙烯基、亚丙烯基、1-亚丁烯基、2-亚丁烯基、1-亚戊烯基、2-亚戊烯基等碳原子数2~20的直链或支链状亚烯基;亚乙炔基、亚丙炔基、3-甲基-1-亚丙炔基、亚丁炔基、1,3-亚丁二炔基、2-亚戊炔基、2-亚戊炔基、2,4-亚戊二炔基、2-亚己炔基、1,3,5-亚己三炔基、3-亚庚炔基、4-亚辛炔基、4-亚壬炔基、5-亚癸炔基、6-亚十一碳炔基、6-亚十二碳炔基等碳原子数2~20的直链或支链状亚炔基。
2价脂环式烃基是从脂环的结构式中去除2个氢原子后的基团,作为上述脂环,可列举例如:环丙烷、环戊烷、环己烷、环庚烷、环辛烷环等3~20元环烷烃环;环戊烯、环己烯环等3~20元环烯烃环;全氢化萘、降冰片烷、降冰片烯、金刚烷、三环[5.2.1.02,6]癸烷、四环[4.4.0.12,5.17,10]十二烷环等桥环等。上述脂环也可以具有取代基(例如碳原子数1~5的烷基等)。另外,也可以是2个以上上述脂环经由单键或连结基团(例如2价脂肪族烃基)键合在一起。
2价芳香族烃基是从芳环的结构式中去除2个氢原子后的基团,作为上述芳环,可列举例如:苯、萘、蒽、芴环等碳原子数6~20的芳环。上述芳环也可以具有取代基(例如碳原子数1~5的烷基、碳原子数3~6的环烷基等)。另外,也可以是2个以上上述芳环经由单键或连结基团(例如2价脂肪族烃基、2价脂环式烃基)键合在一起。
作为上述式(a)中的L1为2价脂肪族烃基的化合物(=脂肪族二胺),可列举例如:六亚甲基二胺、三甲基六亚甲基二胺等。
作为上述式(a)中的L1为2价脂环式烃基的化合物(=脂环式二胺),可列举例如:双(对氨基环己基)甲烷、双(4-氨基-3-甲基环己基)甲烷等。
作为上述式(a)中的L1为2价芳香族烃基的化合物(=芳香族二胺),可举出例如:间苯二甲胺等。
作为上述二羧酸成分,可举出例如:下述式(c)表示的化合物。
[化学式3]
HOOC-L3-COOH (c)
(式中,L2表示2价烃基)
作为L2中的2价烃基,可举出与L1中的2价烃基同样的例子。
作为上述式(c)中的L2为2价脂肪族烃基的化合物(=脂肪族二羧酸),可列举例如:己二酸、十二烷二酸等。
作为上述式(c)中的L2为2价脂环式烃基的化合物(=脂环式二羧酸),可举出例如:环己烷-1,4-二羧酸等。
作为上述式(c)中的L2为2价芳香族烃基的化合物(=芳香族二羧酸),可列举例如:间苯二甲酸、对苯二甲酸等。
作为上述内酰胺类,可列举例如:α-内酰胺、β-内酰胺、γ-内酰胺、δ-内酰胺、ε-己内酰胺、ω-月桂内酰胺等具有3~13元环的内酰胺。
在本发明中,其中,从透明性、耐药品性、耐冲击性、耐油性、及尺寸稳定性优异的方面考虑,优选脂环式聚酰胺树脂[=二胺成分与二羧酸成分的缩聚物,且二胺成分与二羧酸成分中的至少一者为具有脂环结构的化合物(例如脂环式二胺、脂环式二羧酸)的缩聚物]。
作为上述脂环式聚酰胺树脂,特别优选为脂环式二胺与脂肪族二羧酸的缩聚物,尤其优选为具有下述式(ad)表示的重复单元的缩聚物。
[化学式4]
(式中,X表示单键或2价烃基,L表示2价烃基。R1、R2表示烷基,m、n表示0~4的整数)
作为X、L中的2价烃基,可列举与L1中的2价烃基同样的例子。X、L可以相同,也可以不同。
R1、R2表示烷基,可列举例如:甲基、乙基、丙基、异丙基等碳原子数1~5的直链或支链状的烷基。R1、R2可以相同,也可以不同。另外,在m、n为2以上的整数的情况下,2个以上的R1、R2可以分别相同,也可以不同。在本发明中,其中优选m、n均为零。
聚酰胺树脂的重均分子量(聚苯乙烯换算)例如为6000~300000、优选为20000~200000。
另外,聚酰胺树脂可以是结晶性及非晶性中的任意树脂,但其中,从透明性优异的方面考虑,优选结晶度低的聚酰胺树脂、或者结晶尺寸比光的波长小的微小结晶性的树脂、非晶性聚酰胺(非晶性尼龙或者微晶性聚酰胺)。
聚酰胺树脂的熔解温度例如为100~350℃、优选为100~320℃左右。
聚酰胺树脂的阿贝数一般较高,例如为35以上(例如35~65)、优选为40以上(例如40~65)、更优选为45以上(例如40~60)、特别优选为50以上(例如50~60)。
另外,聚酰胺树脂的折射率例如为1.1~2.0、优选为1.2~1.9、更优选为1.3~1.8。
阿贝数高的原材料存在折射率变低的倾向,但聚酰胺树脂的阿贝数和折射率均高,平衡良好地具有理想的光学功能。
作为聚酰胺树脂,可以适宜地使用例如:Daicel Evonik株式会社制造的“Trogamid CX7323”、EMS-Chemie Japan株式会社制造的“Grilamid TR-90”等市售品。
由聚酰胺树脂形成的塑料的光弹性系数特别小,因此,可以将应变抑制为极低水平。另外,耐热性、耐药品性优异。而且,具备适度的硬度并且加工性优异,在加工成防护用具时可以抑制裂缝的产生,有助于成品率的提高。此外,其为轻质的,使用了由聚酰胺树脂形成的塑料的防护用具轻,可以长时间舒适地佩戴。
(聚碳酸酯树脂)
聚碳酸酯树脂是具有下述式(d)表示的重复单元的聚合物。
[化学式5]
(式中,L3表示2价烃基)
L3为2价烃基,可列举与L1中的2价烃基同样的例子。作为L3,其中优选为2价芳香族烃基。
聚碳酸酯树脂可以通过例如使二羟基化合物(优选为芳香族二羟基化合物、特别优选为双酚A)与碳酸二酯(例如碳酸二苯酯等)进行酯交换反应的方法等来制造。
聚碳酸酯树脂的重均分子量(聚苯乙烯换算)例如为5000~300000、优选为20000~200000。
由聚碳酸酯树脂形成的塑料的耐热性优异,硬度高。并且,冲击强度也强,因此,在用作防护用具时可以抑制裂缝的产生,有助于成品率的提高。
(酰化纤维素树脂)
酰化纤维素树脂是位于构成纤维素的β-1,4键合的葡萄糖单元的2位、3位及6位的碳原子中的至少1个上键合有酰基的聚合物(高分子)。在本发明中,其中,上述酰基优选为碳原子数2~4的酰基,尤其优选至少含有乙酰基。因此,在具有两种以上酰基的情况下,优选乙酰基、与丙酰基或丁酰基的组合。
酰化纤维素树脂的总酰基取代度例如为1.0~2.97,其中,从耐药品性和加工性优异的方面考虑,优选为2.0~2.9。
因此,作为酰化纤维素树脂,优选例如:二乙酸纤维素、三乙酸纤维素等乙酸纤维素;乙酸丙酸纤维素、乙酸丁酸纤维素等乙酸C3-6酸纤维素,尤其优选三乙酸纤维素。
酰化纤维素树脂可以通过使位于纤维素的2位、3位及6位的碳原子上键合的羟基中的至少1个经酰基化而制造。在上述纤维素原料中,可以使用棉绒、木浆(例如阔叶树浆、针叶树浆)。
酰化纤维素树脂的重均分子量(聚苯乙烯换算)例如为50000~200000、优选为60000~160000。
由酰化纤维素树脂形成的塑料的光弹性系数小,因此,可以将应变抑制为极低水平。而且,耐热性优异,硬度高,并且是轻质的。因此,使用了由酰化纤维素树脂形成的塑料的防护用具轻,可以长时间舒适地佩戴、
(丙烯酸树脂)
丙烯酸树脂是具有下述式(e)表示的重复单元的聚合物。丙烯酸树脂除下述式(e)表示的重复单元以外,还可以具有能与下述式(e)表示的重复单元共聚的其它重复单元。
[化学式6]
(式中,R3表示氢原子或甲基,R4表示氢原子或1价烃基)
作为R4中的1价烃基,可列举与L1中的2价烃基相对应的1价基团。
作为丙烯酸树脂,可列举例如:(甲基)丙烯酸酯的均聚物或共聚物、(甲基)丙烯酸-氨基甲酸酯共聚物(特别是(甲基)丙烯酸-氨基甲酸酯接枝共聚物)、苯乙烯-(甲基)丙烯酸酯共聚物、乙酸乙烯酯-(甲基)丙烯酸酯共聚物、乙烯-(甲基)丙烯酸酯共聚物、乙烯-(甲基)丙烯酸共聚物、(甲基)丙烯酸酯-(甲基)丙烯酸共聚物、苯乙烯-丙烯腈-(甲基)丙烯酸酯共聚物、苯乙烯-(甲基)丙烯酸酯-(甲基)丙烯酸共聚物、苯乙烯-丙烯腈-(甲基)丙烯酸酯-(甲基)丙烯酸共聚物、乙烯-乙酸乙烯酯-(甲基)丙烯酸酯共聚物、乙烯基吡咯烷酮-(甲基)丙烯酸酯共聚物、苯乙烯-丁二烯-(甲基)丙烯酸共聚物等。
丙烯酸树脂的重均分子量(以聚苯乙烯换算)例如为6000~500000、优选为20000~350000。
由丙烯酸树脂形成的塑料的光弹性系数小,因此,可以将应变抑制为极低水平。另外,耐热性优异,硬度高,是轻质的。因此,使用了由丙烯酸树脂形成的塑料的防护用具轻,可以长时间舒适地佩戴。
[镜片]
本发明的镜片包含上述片作为构成要素。或者,本发明的镜片由上述片(特别是具有曲面形状的片)制成。本发明的镜片可以仅由上述片构成,也可以除上述片以外还包含其它构成要素,例如,可以使具备期望的功能的层(例如硬涂层、防反射层、防雾层、防污层、镜面层等功能层)中的1层或2层以上隔着粘接层层叠于片表面。
作为形成上述粘接层的粘接剂,只要能够将本发明的片与功能层粘接就没有特别限定,可以使用例如丙烯酸类、氨基甲酸酯类(例如酯类聚氨酯、醚类聚氨酯)、环氧类、乙酸乙烯酯类等常用的粘接剂。其中,从粘接强度优异的方面考虑,优选使用氨基甲酸酯类粘接剂。例如,市售有包含作为主剂的酯类聚氨酯“TM-595”(TOYO MORTON株式会社制)与固化剂(商品名“CAT-10L”、“CAT-RT85”、以上TOYO MORTON株式会社制)等的组合的氨基甲酸酯类的干法层压用粘接剂。
粘接剂优选在使固化后的厚度达到例如0.1~80μm、优选1~60μm、特别优选5~40μm的范围内进行涂布。
粘接剂的涂布可以通过例如印刷法、涂布法等进行。具体而言,可列举网版印刷法、掩模印刷法、胶版印刷法、喷墨印刷法、苯胺印刷法、凹版印刷法、冲压法、分配法(dispense)、刮板(squeegee)印刷法、丝网印刷法、喷雾法、刷涂法等。
本发明的镜片具备应变被抑制为极低水平的上述片,因此,可以抑制眼睛疲劳、头痛等问题的发生。另外,是轻质的。因此,可以舒适地长时间佩戴。
[护罩]
本发明的护罩包含上述片作为构成要素。或者,本发明的护罩由上述片(特别是具有曲面形状的片)制成。本发明的护罩可以仅由上述片构成,也可以除上述片以外还包含其它构成要素,例如,可以使具备期望的功能的层(例如硬涂层、防反射层、防雾层、防污层、镜面层等功能层)中的1层或2层以上隔着粘接层层叠于片表面。
本发明的护罩具备应变被抑制为极低水平的上述片,因此,可以抑制眼睛疲劳、头痛等问题的发生。另外,是轻质的。因此,可以舒适地长时间佩戴。
[防护用具]
本发明的防护用具具备上述镜片或护罩。本发明的防护用具包括例如眼镜(例如太阳镜、护目镜等)、头盔(例如作业用头盔、摩托车用头盔、运动用头盔)、医疗用防护面罩、面部防护用具等。
本发明的防护用具具备轻质且应变被抑制为极低水平的上述镜片或护罩,因此,可以抑制眼睛疲劳、头痛等问题的发生,可以舒适地长时间佩戴。
实施例
以下,通过实施例对本发明更具体地进行说明,但本发明不限定于这些实施例。
实施例1
(挤出成型)
将聚酰胺树脂[Daicel Evonik株式会社制、商品名“Trogamid CX7323”、阿贝数45、玻璃化转变温度140℃]在290℃下加热熔融并对其实施挤出成型,得到了片状塑料(1)(纵×横=30cm×30cm、厚:2mm)。
(真空成型)
使用汤姆逊刀将得到的片状塑料(1)冲裁成长径80mm×短径50mm的椭圆形状,使用切削加工成镜片6曲面形状的金属模具(模具温度90℃)进行真空成型,由此得到了6曲面眼镜用镜片(1)(中心厚度:1.9mm)。
实施例2
使用聚碳酸酯树脂(商品名“Iupilon”、三菱工程株式会社制)来代替聚酰胺树脂,除此以外,与实施例1同样地得到了片状塑料(2)(厚度:4mm)。
另外,使用了片状塑料(2)来代替片状塑料(1),除此以外,与实施例1同样地得到了眼镜用镜片(2)(厚度:3.9mm)。
实施例3
使用了三乙酸纤维素树脂(商品名“TENITE”、Eastman公司制)来代替聚酰胺树脂,除此以外,与实施例1同样地得到了片状塑料(3)(厚度:0.5mm)。
另外,使用了片状塑料(3)来代替片状塑料(1),除此以外,与实施例1同样地得到了眼镜用镜片(3)(厚度:0.5mm)。
实施例4
使用了丙烯酸树脂(商品名“Parapet”、株式会社可乐丽制)来代替聚酰胺树脂,除此以外,与实施例1同样地得到了片状塑料(4)(厚度:2mm)。
另外,使用片状塑料(4)来代替片状塑料(1),除此以外,与实施例1同样地得到了眼镜用镜片(4)(厚度:1.8mm)。
比较例1
代替挤出成型而进行了注塑成型(使用Fanuc株式会社制注塑成型机,树脂温度290℃、模具温度90℃),除此以外,与实施例1同样地得到了片状塑料(5)(纵×横=30cm×30cm、厚:2mm)。
比较例2
代替挤出成型而进行了注塑成型,除此以外,与实施例1同样地得到了眼科用镜片(6)(纵×横=6cm×8cm、厚:1.9mm)。
通过以下的方法对实施例及比较例中得到的片状塑料的延迟值、雾度值、及光弹性系数进行了测定。
延迟值:使用延迟测定装置RETS-4200RV(大塚电子株式会社制)进行了测定。
雾度值:使用浊度计NDH 7000(日本电色株式会社制)进行了测定。
光弹性系数:使用圆偏振光测定装置KOBRA-WPR(王子计测机器株式会社制)进行了测定。
通过与上述同样的方法对实施例及比较例中得到的眼镜用镜片的延迟值、雾度值、及光弹性系数进行了测定。
将上述结果总结示于下述表。
[表1]
作为上述的总结,将本发明的构成及其变形附记如下。
[1]一种片,其是由塑料制成的厚度为0.1~5mm的片,所述塑料包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种,该片的延迟值的最大值与最小值之差为3000nm以下。
[2]根据[1]所述的片,其中,塑料含有选自聚酰胺树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种。
[3]根据[1]所述的片,其中,塑料含有选自酰化纤维素树脂及丙烯酸树脂中的至少一种。
[4]根据[1]所述的片,其中,塑料含有选自聚酰胺树脂及聚碳酸酯树脂中的至少一种。
[5]根据[1]~[4]中任一项所述的片,其中,酰化纤维素树脂的总酰基取代度为1.0~2.97(优选为1.0~2.9)。
[6]根据[1]~[4]中任一项所述的片,其中,酰化纤维素树脂的总酰基取代度为1.0~2.97(优选为2.0~2.97)。
[7]根据[1]~[6]中任一项所述的片,其中,酰化纤维素树脂为乙酸C3-6酸纤维素。
[8]根据[1]~[7]中任一项所述的片,其具有曲面形状。
[9]根据[1]~[7]中任一项所述的片,其为4~8曲面镜片。
[10]根据[1]~[9]中任一项所述的片,其雾度值为5%以下。
[11]根据[1]~[10]中任一项所述的片,其中,上述塑料在23℃下的光弹性系数为0.1×10-12~100×10-12cm2/dyn。
[12]根据[1]~[11]中任一项所述的片,其中,上述塑料为含有脂环式聚酰胺树脂的塑料。
[13]根据[12]所述的片,其中,上述脂环式聚酰胺树脂具有式(ad)表示的重复单元。
[14]一种镜片,其包含[1]~[13]中任一项所述的片作为构成要素。
[15]一种护罩,其包含[1]~[13]中任一项所述的片作为构成要素。
[16]一种防护用具,其具备包含[1]~[13]中任一项所述的片作为构成要素的镜片或护罩。
[17]一种片的制造方法,其是制造[1]~[13]中任一项所述的片的方法,所述制造方法包括:对包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种的塑料实施挤出成型而得到片状塑料,对得到的片状塑料实施真空成型、压空成型、或真空压空成型,由此得到具有曲面形状的片。
工业实用性
本发明的片薄且为低应变。另外,透明性优异。并且是轻质的。此外,加工性优异,可以在加工成眼镜、头盔等时抑制裂缝的产生,提高成品率。因此,可以适宜用作眼镜、头盔的护罩、医疗用防护面罩、面部防护用具等。
Claims (10)
1.一种片,其是由塑料制成的厚度为0.1~5mm的片,所述塑料包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种,
该片的延迟值的最大值与最小值之差为3000nm以下。
2.根据权利要求1所述的片,其具有曲面形状。
3.根据权利要求1或2所述的片,其雾度值为5%以下。
4.根据权利要求1~3中任一项所述的片,其中,
所述塑料在23℃下的光弹性系数为0.1×10-12~100×10-12cm2/dyn。
5.根据权利要求1~4中任一项所述的片,其中,
所述塑料为包含脂环式聚酰胺树脂的塑料。
7.一种镜片,其包含权利要求1~6中任一项所述的片作为构成要素。
8.一种护罩,其包含权利要求1~6中任一项所述的片作为构成要素。
9.一种防护用具,其具备包含权利要求1~6中任一项所述的片作为构成要素的镜片或护罩。
10.一种片的制造方法,其是制造权利要求1~6中任一项所述的片的方法,所述制造方法包括:
对包含选自聚酰胺树脂、聚碳酸酯树脂、酰化纤维素树脂及丙烯酸树脂中的至少一种的塑料实施挤出成型而得到片状塑料,对得到的片状塑料实施真空成型、压空成型、或真空压空成型,由此得到具有曲面形状的片。