CN111804323B - 一种光催化剂及其在动力电池光催化环保处理中的应用 - Google Patents

一种光催化剂及其在动力电池光催化环保处理中的应用 Download PDF

Info

Publication number
CN111804323B
CN111804323B CN202010589960.1A CN202010589960A CN111804323B CN 111804323 B CN111804323 B CN 111804323B CN 202010589960 A CN202010589960 A CN 202010589960A CN 111804323 B CN111804323 B CN 111804323B
Authority
CN
China
Prior art keywords
photocatalyst
taon
gas
hollow glass
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202010589960.1A
Other languages
English (en)
Other versions
CN111804323A (zh
Inventor
余海军
彭挺
谢英豪
张学梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Brunp Recycling Technology Co Ltd
Guangdong Brunp Recycling Technology Co Ltd
Hunan Bangpu Automobile Circulation Co Ltd
Original Assignee
Hunan Brunp Recycling Technology Co Ltd
Guangdong Brunp Recycling Technology Co Ltd
Hunan Bangpu Automobile Circulation Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hunan Brunp Recycling Technology Co Ltd, Guangdong Brunp Recycling Technology Co Ltd, Hunan Bangpu Automobile Circulation Co Ltd filed Critical Hunan Brunp Recycling Technology Co Ltd
Priority to CN202010589960.1A priority Critical patent/CN111804323B/zh
Publication of CN111804323A publication Critical patent/CN111804323A/zh
Priority to EP21830124.0A priority patent/EP4163010A4/en
Priority to HU2200204A priority patent/HUP2200204A1/hu
Priority to PCT/CN2021/091554 priority patent/WO2021258856A1/zh
Priority to US18/003,314 priority patent/US11826729B2/en
Application granted granted Critical
Publication of CN111804323B publication Critical patent/CN111804323B/zh
Priority to CL2022003735A priority patent/CL2022003735A1/es
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种光催化剂及其在动力电池光催化环保处理中的应用，所述光催化剂是由Ag‑TaON负载在空心玻璃微珠上得到；所述Ag‑TaON和空心玻璃微珠的质量比为1:(5‑10)。本发明采用Ag‑TaON和空心玻璃微珠进行复合，空心玻璃微珠对光有更好的透过性，不会造成催化剂之间的相互遮挡，这使得反应器内部填充的光催化剂被充分激发，能有效提高光的利用率，从而提高光催化剂的催化转化效率。

Description

一种光催化剂及其在动力电池光催化环保处理中的应用
技术领域
本发明属于催化剂领域，具体涉及一种光催化剂及其在动力电池光催化环保处理中的应用。
背景技术
锂电池电解液是电池中离子传输的载体。一般由锂盐和有机溶剂组成。电解液在锂电池的正、负极之间起到传导离子的作用。电解液由高纯度的有机溶剂、电解质锂盐和必要的添加剂等原料，在一定条件下、按一定比例配制而成。
锂电池电解液为电解质溶于有机溶剂的液体。电解质通常为高氯酸锂、六氟磷酸锂等。有机溶剂通常为碳酸酯类液态有机物。电解液为有机易挥发性液体，而且有明显的腐蚀性，长时间吸入会对呼吸道产生严重损害。锂离子电池回收处理时须收集妥善处理，严格控制电解液的挥发逸散，避免对人体健康和生态环境造成危害。
传统处理电解液的方法是将锂离子电池置于热解炉中，使电解液与其他有机物同时被热解。然而，传统的回收方式，如《一种锂电池无氧裂解回收分选工艺》(CN201810712762.2)，不能单独处理电解液，热解时隔膜也一并被热解去除导致隔膜不能有效回收，资源回收率低，局限性明显。使用目前的催化剂去催化降解电解液还存在催化转化效率低、催化剂成本高和降解率低的问题。
发明内容
本发明的目的是提供一种光催化剂及其在动力电池光催化环保处理中的应用，本发明制备的动力电池光催化剂采用TaON和空心玻璃微珠进行复合，空心玻璃微珠对光有更好的透过性，不会造成催化剂之间的相互遮挡，这使得反应器内部填充的光催化剂能被充分激发，能有效提高光的利用率，从而提高催化转化效率。
为了实现上述目的，本发明采取以下技术方案：
一种光催化剂，是由Ag-TaON负载在空心玻璃微珠上得到；所述Ag-TaON和空心玻璃微珠的质量比为1:(5-10)。
优选地，所述空心玻璃微珠的粒径为10μm-10mm。
优选地，所述空心玻璃微珠的化学组成按质量比为：45-90％SiO2、5-50％Al2O3、4-10％K2O、1-10％CaO和0-12％B2O3。
一种光催化剂的制备方法，包括以下步骤：
(1)将TaON研磨成粉末，再分散在溶剂中，加入可溶性银盐搅拌，光照，离心，洗涤，即得Ag-TaON催化剂；
(2)将Ag-TaON催化剂分散在三聚磷酸钠溶液中，加入空心玻璃微珠，搅拌，烘干，烧结，得到Ag-TaON负载在空心玻璃微珠表面上的所述光催化剂。
优选地，步骤(1)中所述溶剂为水和甲醇；所述TaON、水和甲醇的质量比为1：(20-60)：(15-40)。
优选地，步骤(1)中所述可溶性银盐为AgNO3溶液。
更优选地，所述AgNO3溶液的浓度为0.5-1mol·L-1。
优选地，步骤(1)中所述光照使用的是高压汞灯，气氛为氮气氛围，时间为10-30min。
优选地，步骤(2)中所述三聚磷酸钠溶液的浓度为0.1-1mol·L-1。
优选地，步骤(2)中所述搅拌的转速为400-800r/min，时间为20-60min。
优选地，步骤(2)所述烧结的温度为200℃-300℃，气氛为氮气气氛，时间为1-2小时。
优选地，所述TaON是由以下步骤制备得到：
(1)将钽箔进行预处理；
(2)降温，通入惰性气体，再通入反应气A，升温，保温反应，得到Ta2O5；
(3)降温，通入惰性气体，再通入反应气B，升温，保温反应，得到TaON；步骤(2)中所述反应气A为O2和N2的混合气；步骤(3)中所述反应气B为NH3和N2的混合气。
优选地，步骤(1)所述预处理的具体过程：将盛有钽箔的刚玉瓷舟推入管式炉的中间加热区段，用法兰密闭，常温下以2-30mL·min-1的流速通入惰性气体20-120min；再切换气路以2-30mL·min-1的流速通入预处理气，再以2-8℃·min-1的速率升温至250℃-350℃，保温30-150min。
更优选地，所述预处理气为H2和N2的混合气；所述H2浓度为5％-10％。
优选地，步骤(2)和步骤(3)中所述降温是将温度降至常温。
优选地，步骤(2)和步骤(3)中所述惰性气体为纯N2、Ar或He中的至少一种。
优选地，步骤(2)和步骤(3)中所述通入惰性气体的流速为2-30mL·min-1，时间为20-120min。
优选地，所述O2的浓度为5％-10％。
优选地，步骤(2)中所述通入反应气A的流速为2-30mL·min-1。
优选地，步骤(2)中所述升温的温度为500℃-600℃，升温的速率为2-8℃·min-1。
优选地，步骤(2)中所述保温反应的时间为30-150min。
优选地，所述NH3浓度为5％-10％。
优选地，步骤(3)中所述通入反应气A的流速为2-30mL·min-1。
优选地，步骤(3)中所述升温的温度为800℃-900℃，升温的速率为2-8℃·min-1。
优选地，步骤(3)中所述保温反应的时间为180-300min。
一种动力电池的光催化环保处理方法，包括以下步骤：
(1)将废旧锂电池拆解，热解，得到夹杂电解液的气体；
(2)将夹杂电解液的气体通入清洗液，再通入装有光催化剂的反应器中，用光源照射进行光催化，降解为CO2和H2O。
优选地，步骤(2)中所述清洗液为NaOH、Ca(OH)2或KOH中的至少一种。
优选地，步骤(2)中所述清洗液的浓度为0.1-1mol·L-1。
优选地，步骤(2)中所述光源为紫外光。
装有光催化剂的反应器安装在厂房屋顶目的是采光，太阳光能激发催化剂产生光生电荷从而进行催化氧化作用，将聚乙烯和聚丙烯等材料裂解成小分子。
优选地，步骤(2)中所述反应器的装载率为30％-100％。
有益效果
1.本发明采用Ag-TaON和空心玻璃微珠进行复合，空心玻璃微珠对光有更好的透过性，不会造成催化剂之间的相互遮挡，这使得反应器内部填充的光催化剂能被充分激发，能有效提高光的利用率，从而提高光催化剂的催化转化效率。
2.本发明的催化剂采用光沉积的方式与Ag结合，相比于传统化学还原法，能得到更小的Ag颗粒，使Ag有着更大的分散度，提高了原子利用率，减少了Ag的用量，催化剂成本更低。
3.本发明采用Ag-TaON作为光催化剂，TaON光响应范围能覆盖部分可见光，Ag的引入能起到富集电子作用，Ag-TaON催化剂能在可见光的作用下进行光催化反应。
4.本发明采用Ag-TaON作为光催化剂，采用光催化技术对电解液进行降解，电解液经过碱液除氟后通入光催化反应器，在光催化的作用下直接将电解液中的有机物催化氧化成CO2和H2O，处理过程无需外加其他药剂，处理过程环保、安全、低成本，处理后的尾气无毒无害，可直接排放。
附图说明
图1为本发明的实施例2中Ag-TaON粉末的SEM图；
图2为本发明的实施例2制备的光催化剂的SEM图；
图3为本发明的实施例2中Ag-TaON粉末的XRD图。
具体实施方式
为了让本领域技术人员更加清楚明白本发明所述技术方案，现列举以下实施例进行说明。需要指出的是，以下实施例对本发明要求的保护范围不构成限制作用。
以下实施例中所用的原料、试剂或装置如无特殊说明，均可从常规商业途径得到，或者可以通过现有已知方法得到。
实施例1
一种光催化剂，是由Ag-TaON负载在空心玻璃微珠上得到；Ag-TaON和空心玻璃微珠的质量比为1:5。
一种动力电池光催化剂的制备方法，包括以下步骤：
(1)将盛有钽箔的刚玉瓷舟推入管式炉的中间加热区段，用法兰密闭，在环境温度下以流速2mL·min-1通入纯N2 20min，再切换气路以流速2mL·min-1通入H2和N2的混合气，H2浓度为5％，同时开启控温程序以2℃·min-1的速率将温度升至250℃，保温30min；
(2)将温度降至环境温度，切换气路以流速2mL·min-1通入纯N2 20min，再切换气路以流速2mL·min-1通入O2和N2的混合气，O2浓度为5％，同时开启控温程序以2℃·min-1的速率升温，升至500℃，保温30min，得到Ta2O5；
(3)将温度降至环境温度，切换气路以流速2mL·min-1通入纯N2 20min，再切换气路以流速2mL·min-1通入NH3和N2的混合气，NH3浓度为5％，同时开启控温程序以2℃·min-1的速率升温升至800℃，保温180min，得到TaON；
(4)将温度降至环境温度，取出TaON，研磨成粉末，按比例TaON：水：甲醇＝1g：20mL：15mL加入磁子在磁力剧烈搅拌(转速800r/min)下形成分散体系，将此分散体系置于氮气氛围中，再按负载量0.5％加入0.5mol·L-1AgNO3溶液，再搅拌5min，用高压汞灯照射10min后，离心，洗涤，即得Ag-TaON催化剂；
(5)将Ag-TaON催化剂分散在0.1mol·L-1的三聚磷酸钠溶液中，Ag-TaON：空心玻璃微珠按重量比为1:5加入200目空心玻璃微珠，搅拌(转速400r/min)20min，烘干，在氮气分下200℃烧结1小时，得到Ag-TaON负载在空心玻璃微珠表面上的光催化剂。
一种动力电池的光催化环保处理方法，包括以下步骤：
(1)将废旧锂电池拆解，热解，得到夹杂电解液的气体；
(2)将夹杂电解液的气体通入0.1mol·L-1NaOH溶液，再通入装有光催化剂的反应器中，用紫外灯照射，进行光催化降解电解质，得到的产物为CO2和H2O。
实施例2
一种光催化剂，是由Ag-TaON负载在空心玻璃微珠上得到；Ag-TaON和空心玻璃微珠的质量比为1:8。
一种光催化剂的制备方法，包括以下步骤：
(1)将盛有钽箔的刚玉瓷舟推入管式炉的中间加热区段，用法兰密闭，在环境温度下以流速15mL·min-1通入纯Ar 70min，再切换气路以流速15mL·min-1通入H2和N2的混合气，H2浓度为8％，同时开启控温程序以5℃·min-1的速率将温度升至300℃，保温90min；
(2)将温度降至环境温度，切换气路以流速15mL·min-1并在70min内通入纯Ar，再切换气路以流速15mL·min-1通入O2和N2的混合气，O2浓度为8％，同时开启控温程序以5℃·min-1的速率升温，升至550℃，保温90min，得到Ta2O5；
(3)将温度降至环境温度，切换气路以流速15mL·min-1并在70min内通入纯Ar，再切换气路以流速15mL·min-1通入NH3和N2的混合气，NH3浓度为8％，同时开启控温程序以5℃·min-1的速率升温升至850℃，保温240min，得到TaON；
(4)将温度降至环境温度，取出TaON，研磨成粉末，按TaON:水：甲醇＝1g：40mL：25mL的比例加入磁子在磁力剧烈搅拌(转速1200r/min)下形成分散体系，将此分散体系置于氮气氛围中，再按负载量0.7％加入0.8mol·L-1AgNO3溶液，再搅拌5min，用高压汞灯照射20min后，离心，洗涤，即得Ag-TaON催化剂；
(5)将Ag-TaON催化剂分散在0.5mol·L-1的三聚磷酸钠溶液中，按Ag-TaON和空心玻璃微珠的重量比为1:8加入300目空心玻璃微珠，搅拌(转速600r/min)40min，烘干，在氮气分下250℃烧1.5小时，得到Ag-TaON负载在空心玻璃微珠上的动力电池光催化剂。
一种动力电池的光催化环保处理方法，包括以下步骤：
(1)将废旧锂电池拆解，热解，得到夹杂电解液的气体；
(2)将夹杂电解液的气体通入0.2mol·L-1NaOH溶液，再通入装有光催化剂的反应器中，用紫外灯照射，进行光催化降解电解质，得到的产物为CO2和H2O。
实施例3
一种光催化剂，是由Ag-TaON负载在空心玻璃微珠上得到；Ag-TaON和空心玻璃微珠的质量比为1:8。
一种光催化剂的制备方法，包括以下步骤：
(1)将盛有钽箔的刚玉瓷舟推入管式炉的中间加热区段，用法兰密闭，在环境温度下以流速15mL·min-1通入纯Ar 70min，再切换气路以流速15mL·min-1通入H2和N2的混合气，H2浓度为8％，同时开启控温程序以5℃·min-1的速率将温度升至300℃，保温90min；
(2)将温度降至环境温度，切换气路以流速15mL·min-1并在70min内通入纯Ar，再切换气路以流速15mL·min-1通入O2和N2的混合气，O2浓度为8％，同时开启控温程序以5℃·min-1的速率升温，升至550℃，保温90min，得到Ta2O5；
(3)将温度降至环境温度，切换气路以流速15mL·min-1并在70min内通入纯Ar，再切换气路以流速15mL·min-1通入NH3和N2的混合气，NH3浓度为8％，同时开启控温程序以5℃·min-1的速率升温升至850℃，保温240min，得到TaON；
(4)将温度降至环境温度，取出TaON，研磨成粉末，按TaON:水：甲醇＝1g：40mL：25mL的比例加入磁子在磁力剧烈搅拌(转速1200r/min)下形成分散体系，将此分散体系置于氮气氛围中，再按负载量0.7％加入0.8mol·L-1AgNO3溶液，再搅拌5min，用高压汞灯照射20min后，离心，洗涤，即得Ag-TaON催化剂；
(5)将Ag-TaON催化剂分散在0.5mol·L-1的三聚磷酸钠溶液中，Ag-TaON和空心玻璃微珠按重量比为1:8加入300目空心玻璃微珠，搅拌(转速600r/min)40min，烘干，在氮气分下250℃烧1.5小时，得到Ag-TaON负载在空心玻璃微珠表面上的动力电池光催化剂。
一种动力电池的光催化环保处理方法，包括以下步骤：
(1)将废旧锂电池拆解，热解，得到夹杂电解液的气体；
(2)将夹杂电解液的气体通入0.2mol·L-1NaOH溶液，再通入装有光催化剂的反应器中，用紫外灯照射，进行光催化降解电解质，得到的产物为CO2和H2O。
对比例1
一种TaON催化剂的催化电解液方法，包括以下步骤：
(1)将Ta2O5置于管式炉中，在氨气分中以800℃保温4小时得TaON，研磨成粉末后得到TaON催化剂；
(2)将TaON和空心玻璃微珠加入三聚磷酸钠溶液，搅拌、分散、烘干，200℃烧结，所得催化剂在石英反应器中光催化降解电解液。
对比例2
一种Ag-TaON催化剂的催化电解液方法，包括以下步骤：
(1)将Ta2O5置于管式炉中，在氨气分中以800℃保温4小时得TaON，研磨成粉末后，以0.7％的负载量，加入硝酸银溶液，以硼氢化钠还原，得到Ag-TaON；
(2)将Ag-TaON和空心玻璃微珠加入三聚磷酸钠溶液，搅拌、分散、烘干，200℃烧结，所得催化剂在石英反应器中光催化降解电解液。
降解效果对比：
分别以实施例2和对比例1、对比例2进行电解液的光降解，得到的产物通过气相色谱进行检测，结果见表1。由表1可知，对比例1中的催化剂没有Ag，电解液转化率为73.2％，而实施例2中电解液转化率为96.2％，实施例2电解液转化率要高于对比例1，说明实施例2的催化性能高于对比例1中催化剂。经过300次循环测试后，对比例1中的电解液转化率保持在62.3％，而实施例2中电解液转化率为95.6％，实施例2催化剂的稳定性优于对比例1。这充分体现了Ag提高了催化效率的作用。对比例2中催化剂通过硼氢化钠还原得到Ag-TaON催化剂和实施例2中通过光沉积法得到的Ag-TaON催化剂。虽然对比例2和实施例2中催化剂Ag的含量一致，但同样的Ag量，对比例2的转化率只有85.3％，经过300循环试验后，转化率只有67.7％，因此其性能远低于实施例2。由此说明，本发明的还原方法得到的催化剂性能优于传统方法。
表1 实施例2与对比例1、对比例2的电解液的光降解性能对比
降解率 循环性能(300次转化率)
对比例1 73.2％ 62.3％
对比例2 85.3％ 67.7％
实施例2 96.2％ 95.6％
以上对本发明提供的一种光催化剂及其在动力电池光催化环保处理中的应用进行了详细的介绍，本文中应用了具体实施例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想，包括最佳方式，并且也使得本领域的任何技术人员都能够实践本发明，包括制造和使用任何装置或系统，和实施任何结合的方法。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以对本发明进行若干改进和修饰，这些改进和修饰也落入本发明权利要求的保护范围内。本发明专利保护的范围通过权利要求来限定，并可包括本领域技术人员能够想到的其他实施例。如果这些其他实施例具有不是不同于权利要求文字表述的结构要素，或者如果它们包括与权利要求的文字表述无实质差异的等同结构要素，那么这些其他实施例也应包含在权利要求的范围内。

Claims (9)

1.一种光催化剂，其特征在于，是由Ag-TaON负载在空心玻璃微珠上得到；所述Ag-TaON和空心玻璃微珠的质量比为1:(5-10)；所述的光催化剂的制备方法，包括以下步骤：(1)将TaON研磨成粉末，再分散在溶剂中，加入可溶性银盐搅拌，光照，离心，洗涤，即得Ag-TaON催化剂；(2)将Ag-TaON催化剂分散在三聚磷酸钠溶液中，加入空心玻璃微珠，搅拌，烧结，得到Ag-TaON负载在空心玻璃微珠上的所述光催化剂。
2.根据权利要求1所述的光催化剂，其特征在于，所述空心玻璃微珠的粒径为10μm-10mm。
3.根据权利要求1所述的光催化剂，其特征在于，步骤(1)中所述溶剂为水和甲醇；所述TaON、水和甲醇的质量比为1：(20-60)：(15-40)；所述可溶性银盐为AgNO3溶液。
4.根据权利要求1所述的光催化剂，其特征在于，步骤(2)所述烧结的温度为200℃-300℃，气氛为氮气气氛，时间为1-2小时。
5.根据权利要求1所述的光催化剂，其特征在于，所述TaON是由以下步骤制备得到：
(1)将钽箔进行预处理；
(2)降温，通入惰性气体，再通入反应气A，升温，保温反应，得到Ta2O5；
(3)降温，通入惰性气体，再通入反应气B，升温，保温反应，得到TaON；步骤(2)中所述反应气A为O2和N2的混合气；步骤(3)中所述反应气B为NH3和N2的混合气。
6.根据权利要求5所述的光催化剂，其特征在于，步骤(1)所述预处理的具体过程：将盛有钽箔的刚玉瓷舟推入管式炉的中间加热区段，用法兰密闭，常温下以2-30mL·min-1的流速通入惰性气体20-120min；再切换气路以2-30mL·min-1的流速通入预处理气，再以2-8℃·min-1的速率升温升至250℃-350℃，保温30-150min；所述预处理气为H2和N2的混合气。
7.根据权利要求5所述的光催化剂，其特征在于，步骤(2)和步骤(3)中所述惰性气体为纯N2、Ar或He中的至少一种。
8.一种动力电池的光催化环保处理方法，其特征在于，包括以下步骤：
(1)将废旧锂电池拆解，热解，得到夹杂电解液的气体；
(2)将夹杂电解液的气体通入清洗液，再通入装有权利要求1-7任一项所述的光催化剂的反应器中，用光源照射进行光催化，降解为CO2和H2O。
9.根据权利要求8所述的动力电池的光催化环保处理方法，其特征在于，所述清洗液为NaOH、Ca(OH)2或KOH中的至少一种。
CN202010589960.1A 2020-06-24 2020-06-24 一种光催化剂及其在动力电池光催化环保处理中的应用 Active CN111804323B (zh)