CN1117288A - 玻璃组合物 - Google Patents
玻璃组合物 Download PDFInfo
- Publication number
- CN1117288A CN1117288A CN94191094A CN94191094A CN1117288A CN 1117288 A CN1117288 A CN 1117288A CN 94191094 A CN94191094 A CN 94191094A CN 94191094 A CN94191094 A CN 94191094A CN 1117288 A CN1117288 A CN 1117288A
- Authority
- CN
- China
- Prior art keywords
- glass
- weight
- nio
- amount
- visible light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种中性色调的吸收红外和紫外线的钠钙硅玻璃，它含有0.25-1.75％(重量)的总铁(以Fe2O3表示)，由下式计算出的亚铁含量(重量)％：FeO(重量)≥0.007+(光密度-0.036)/2.3，该玻璃还含有一种或多种选自Se、Co3O4、Nd2O3、NiO、MnO、V2O5、CeO2、TiO2、CuO、MnO和SnO的着色剂，使得该玻璃在4mm厚时，可见光透过率至少为32％，直接太阳热透过率至少低于可见光透过率7个百分点，紫外线透过率小于25％。
Description
本发明涉及用于窗玻璃的吸收红外(IR)和紫外(UV)线的钠钙硅玻璃组合物。更具体地说，本发明不排它性地涉及车辆如汽车中主要由这种玻璃制成的中性色调的窗。
已经开发了在车辆中使用的、具有低的直接太阳热透过率(DSHT)和紫外线透过率(UVT)的特种玻璃。这些玻璃旨在减少晴天寸，由于车辆内部过热引起的各种问题，并且防止车内设施因为紫外线辐射引起的老化。通常是通过将玻璃中的铁还原为二价态或添加铜来制造具有好的红外吸收性能的玻璃。这些物质使玻璃呈兰色。添加后能获得好的紫外线吸收性的物质有：Fe3+、Ce、Ti或V。达到要求的吸收性所需加入的这种物质的量容易使玻璃呈黄色。因此，如果在同一玻璃既要得到好的UV吸收性又要得到好的IR吸收性，则不可避免地，这种玻璃不是绿色就是兰色。当用CIELAB系统确定玻璃的颜色时，发现这种商用玻璃(厚度4mm，透光率超过60％)不是很绿(-a*＞8)就是很兰(-b*＞7)。从美学角度来看这两种颜色现在都不理想。
人们已经尝试在生产具有好的防IR和UV辐射能力的灰色或青铜色的车辆窗玻璃，但这种玻璃仍容易具有绿黄色的色调。因此，法国专利申请No.2672587公开了一种主波长(λD)在571—580nm的示范玻璃，其色纯度在4.4—15.9％。这些数字表明，这种玻璃具有绿黄色的色调。可从Pilkington玻璃有限公司(St.Helens，England)买到的牌号为ANTISUN Grey(ANTISUN是Pilkington集团的一个商标)的一种中性灰色玻璃，其厚度为4mm时，主波长为454nm，色纯度为2.1％。
我们已经确定了一种具有中性色调的玻璃的范围要求，即，在CIELAB系统中，如果可见光透过率高于60％，玻璃的色坐标为a*轴-6至+5，b*轴-5至+5；如果可见光透过率低于60％，玻璃的色坐标为a*轴-12至+5，b*轴-5至+10。术语“中性色调”在下文中用来描述具有上述色坐标的玻璃。
我们进一步确定对中性色调玻璃的要求，这种玻璃的可见光透过率大于32％(4mm厚时)，但它的直接太阳热透过率应比可见光透过率至少低7个百分点(最好为10个百分点)。通常，已知有些玻璃确实具有低的直接太阳热透过率，但几乎所有这些玻璃都具有低的可见光透过率，因此限制了这种玻璃在车辆中的应用。我们预计，满足上述要求的玻璃在车辆中有更广泛的应用，因为它有高的透光率，尽管如此，但是它的较低的直接太阳热透过率可使汽车内部凉爽。
此外，我们认为如果玻璃的紫外光透过率低于25％将很理想，因为这种低的透过率将降低紫外线对塑料材料和纤维的负作用，尤其是汽车中的这种材料。法国专利申请No.2672587的说明书第5页，32—35行中指出，CoO和NiO降低可见光透过率，但不会增大对紫外线和红外线的吸收，因此，最好不添加这种组分。建议CoO的上限为0.005％，但例举的最高CoO含量为0.001％。这与说明书中指出的不应使用这些物质，如果使用也只能限量使用相一致。
在法国专利2672 587中，除实施例9以外，实施例中所用的Se的量与着色剂大致相同或更多，实施例9中Fe2O3含量低至0.178，色纯度的数值高达9.6，表明透光率大于60％的4mm厚的玻璃，基本上偏离了中性色调。
着色玻璃领域中相对较小的变化就能导致色彩的很大改变。正如一个专利权人所说的，象在草堆中找针。先有申请的专利公开的范围能遇到许多可能，只有具体实施例中的叙述可以确定特定的色调与获得的特定的红外和紫外吸收范围之间的关系。从法国专利2672 587中可清楚看到，没能给出能得到中性色调(指没有不可接受的570nm以上的主波长)的平衡组分。为了获得相对低的DSHT，该法国专利使用了高的FeO含量，尽管它还未被认识到，但本发明发现了这一点，这可以通过添加不引起可见光透过率异常降低的着色剂来补偿。
本发明是基于这样一个令人惊奇的发现，即添加相对较少的某些特定的与绿色互补的着色剂，这种绿色是因为红外和紫外线吸收组分的存在而引起的。
根据本发明，提供了一种吸收IR和UV辐射的中性色调钠钙硅玻璃(如上述定义)，这种玻璃的亚铁含量由下式计算：总的铁含量(用Fe2O3表示)在0.25—1.75％(重量)范围内，该玻璃被下面的一种或多种着色剂着色形成中性颜色：Se，Co3O4，Nd2O3，NiO，MnO，V2O5，CeO2，TiO2，CuO和SnO，该玻璃厚度4mm时，可见光透过率至少32％，UV透过率不超过25％，直接太阳热透过率至少低于可见光透过率7个百分点，其主波长最好小于570nm；如果主波长超过570nm，可见光透过率大于60％，则色纯度不超过4，最好小于2；并且当Se存在时，则至少存在另外一种选自Co3O4、Nd2O3、NiO、MnO、CuO、SnO、V2O5、CeO2和TiO2的着色剂，其量至少为Se量的1.5倍，最好有2倍。优选地，直接太阳热透过率至少低于可见光透过率10个百分点。
Se的添加量最好保持低一些，只要它能形成中性色调的颜色。我们发现当可见光透过率超过60％时，低于5ppm的Se可以得到令人满意的效果。
就本发明的说明书和权利要求书而言，可见光透过率指使用CIE光源A测得的透光率；UVT是指根据国际ISO 9050标准，在280～380nm波长范围内测得的透过率；直接太阳热透过率(DSHT)是指根据相对太阳光谱分布的Parry Moon气团2，在350～2100nm范围内的太阳热透过率的积分；总太阳热透过率指DSHT与在前进方向上吸收与重新辐射的太阳热之和。
在本发明的总范围之内，有几种不同类型的组合物特别引入注意。
因此，在本发明的一个优选方案中，提供了一种玻璃，其可见光透过率不超过60％，总铁含量(用Fe2O3表示)至少为0.7％，并且Co3O4，NiO和Se共同作为着色剂。
使用镍作为着色剂有些出乎意料。在玻璃制造行业都知道镍的存在容易导致玻璃中形成NiS结石，从而使玻璃在退火时破裂。此外，含镍的玻璃组合物在退火时，尤其是弯曲时容易改变颜色。因为这个原因，本领域大多数现有技术都认为应当避免使用镍。因为现到在还不完全清楚的某些原因，我们发现我们可以使用相对较多的镍，不超过275ppm(重量)，而不会引起上述问题。
使用镍确实有一些令人惊奇的优点。首先，如果制造一系列的含镍玻璃，熔体与熔体很容易逐步引入。换句话说，可以改变使用的镍，而不会制造出大量的因为含镍太多而引起的废玻璃。此外，使用Se作为着色剂会产生问题，它易挥发并且有毒性，难以使其在玻璃中稳定存在。事实上，大约有90％的引入熔体中的硒会随废气排放掉。除了它有毒以外，硒的另一个污染环境的特点是它有类似腐烂的卷心菜的臭味。人们还知道加到玻璃熔体中的硒越多，则成比例性的消失越多。通过使用镍以及少量的硒，我们发现可以获得与不用镍而使用大量的硒时获得的色调基本相同。这样，我们明显降低了使用硒对环境造成的污染。
本发明的另一方案中，提供了一种可见光透过率至少60％的玻璃，其总的铁含量(用Fe2O3表示)大约为0.25％～0.77％(重量)范围内，着色剂包括V2O5、CeO2、TiO2、Se、Co3O4、NiO、SnO、Nd2O3和MnO中的至少一种。
在这种情况下，优选地如果总铁含量最大为0.3％(重量)，则着色剂包括至少一种选自由V2O5，CeO2和TiO2组成物组中的物质，还包括至少一种选自由Se，Co3O4，NiO，Nd2O3和MnO组成的物组中的物质。
如果总铁含量至少为0.3％(重量)，优选地，着色剂包括至少一种选自由Se，Co3O4，NiO，Nd2O3和MnO组成物组中的物质。如果需要，还可包括由V2O5，CeO2和TiO2组成物组中的至少一种物质。
这种玻璃组合物令人惊奇并非常有用。尤其是如果其透光率超过70％，因为现在要求汽车风挡最低透光率为70％。如前所述，大多数具有期望的IR，可见光和UV透过率的玻璃为绿色。此外，具有高的铁含量的玻璃通常具有低的透光率。我们惊奇地发现，通过使用少量的其它着色剂，可以很容易改变绿色，尤其是硒更具光学活性，当大量的铁以亚铁形式存在时更是如此。高的亚铁含量意谓着其它着色剂的1或2个ppm浓度的变化就可以使玻璃颜色有很大不同。
下面将说明附图，唯一的附图是一张在一系列灰色玻璃中透过率(UV、太阳热以及光)与FeO含量的关系曲线图，它表明根据本发明，通过增加已知玻璃(玻璃1)中的FeO含量，而同时如本发明指出的，加入其它着色剂来保持中性色调，可以实现性能的改进。玻璃1是一种市场上可买到的灰色玻璃，其DSHT与它的透光率相似，而UV透过率约40％。在玻璃2、3、4中，增加了亚铁离子的含量，若没有补偿的成份变化，通常会使玻璃变兰，并明显降低透光率。UV透过率也降低了，但这会向兰色玻璃中引入绿色。在控制亚铁/三价铁比例的同时，通过钴、钕和硒添加剂的补偿作用，事实上同时保持了玻璃的透光率和中性色调。
硒向玻璃的颜色中引入粉红成份，因而与玻璃中的兰色互补，产生更趋中性的颜色。但是，在氧化性玻璃中硒有无色的形式，而在还原性玻璃中，硒为棕色或无色的聚亚硒酸盐(polyselenides)。因而必须严格控制玻璃的氧化/还原比，以维持硒为粉红色形式。
硒在约20％的亚铁/三价铁比例时滞留量最大，在低于10％的亚铁/三价铁比例，或高于40％的亚铁/三价铁比例时，硒的滞留量明显减少。在使用硒作为中性着色剂的玻璃中，应保持亚铁/三价铁比例在10～40％范围内，以保持硒处于最有效的颜色形式。
尽管钴本身使玻璃呈兰色，它却是一种有用的颜色中和试剂，因为它的吸收是在可见光谱红色那一端，因此可以补偿在1050nm的红外区铁吸收的减少。
氧化钕也以类似的方式起作用，但它是一种更有效的中和剂，因为它是二色性的，根据它所处的光的种类，氧化钕可产生兰色和粉红色两种颜色。但是，氧化钕较贵，因此钴与硒的结合使用是优选的中和剂。
对于厚度为4mm时，DSHT至少比可见光透过率低七个百分点，UV透过率低于25％的玻璃，要求下面的添加剂的组合。
总铁量(以Fe2O3表示)为0.25—1.75％范围内，通常为0.25—1.25％。
根据下式使DSHT随光密度变化的最小FeO含量：
其中光密度＝log10 T/100
其中T是4mm厚的玻璃的可见光透过率的百分数。
它大致相当于：透光率 最低FeO含量80％ 0.033％70％ 0.058％60％ 0.087％50％ 0.122％40％ 0.153％30％ 0.218％
由Fe3+态的氧化铁提供UV吸收性，任选地还可由V2O5和/或CeO2和/或TiO2补充。对大多数色调，仅通过三价铁来获得小于25％的UV透过率。但是，当三价铁(以Fe2O3表示)低于0.3％时，通过添加下面的物质可使UV透过率低于25％：—0.1～1.0CeO2(如果无钒)—0.05—0.2V2O5(如果无铈)
许多玻璃至少含有0.3％的三价铁(用Fe2O3表示)，还含有一定量CeO2和V2O5，以提供增强的防UV能力。
优选地，DSHT应至少比可见光透过率低10个百分点；满足这种优选条件的玻璃的最低FeO含量由下式给出：
这大致相当于：
透光率 最小FeO含量
80％ 0.045％
70％ 0.076％
60％ 0.113％
50％ 0.156％
40％ 0.208％
30％ 0.276％
对大多数中性色调，亚铁/三价铁比例不应低于10％，最好不低于18％。
可以通过添加Se、Co3O4、Nd2O3、NiO、MnO、CuO和SnO中的一种或多种来获得需要的色调。根据所需色调的深度来选择着色剂的数量以及脱色剂的种类，下面给出了一些原则：
Se：不超过50ppm的化学滞留的Se
Co3O4：不超过200ppm
Nd2O3：不超过2.5％(重量)
也可以向玻璃中添加氧化锰以形成粉红色(粉红色是由于Mn3+离子存在而引起的)，但是，最好将其限制在1％(重量)以内，因为添加量过大容易使玻璃因日晒而引起变色。类似地，玻璃中的紫外线吸收剂氧化铈和氧化钒也应小心使用，以防日晒而引起变色。
根据本发明，玻璃中还可以存在的其它组分有氧化铜，CuO的量通常不超过0.1％(重量)，它在一定条件下可以降低太阳热透过率。
根据本发明的玻璃在建筑和汽车领域均很有用，本发明还提供了由本发明玻璃所制成的玻璃窗。汽车窗不仅指挡风玻璃，也指汽车中的其它窗，如后部侧窗以及后窗，它们的可见光透过率可低至30％。
除了实施例1用作比较以外，其它的实施例用来说明而不是限制本发明。在实施例中，所有的份及百分含量均指重量份或重量百分含量：
(a)Fe2O3、FeO、Nd2O3、CeO2、TiO2、V2O5、SnO和MnO以百分含量表示；Se、Co3O4和NiO以ppm表示；
(b)总铁表示为假设所有的铁都以三氧化二铁存在；
(c)以Fe2+表示的总铁百分数利用下式从玻璃的光谱曲线算出的：
其中：OD1000＝玻璃在1000nm波长时的光密度，
t＝玻璃厚度(以毫米计)
Fe2O3＝玻璃中的总铁百分数，以Fe2O3表示；
(d)FeO含量由下式算得：
Fe2O3＝玻璃中总铁百分数(以Fe2O3表示)，(143.7为2×FeO的分子量，159.7为Fe2O3的分子量。实施例
化学添加剂总铁 总铁(以Fe2O3 (以Fe2+计) FeO计) Se Co3O4 Nd2O3CeO2 TiO2V2O5其余％ ％1 0.25 0.043 18％ 11 41 - - - - -2 0.35 0.082 26％ 3 32 0.15 0.4 - - -3 0.38 0.078 23％ 5 32 - 0.34 - - -4 0.38 0.099 29％ 2 32 - 0.4 - - -5 0.25 0.038 17％ 9 - - - - 0.1 -6 0.25 0.065 29％ 3 - - - - 0.1 -7 0.34 0.098 32％ ＜2 32 - 0.4 - - -8 0.45 0.030 7.5％ 24 18 - 0.4 - - -9 0.45 0.093 23％ 5 38 - 0.4 - - -10 0.45 0.142 35％ ＜2 38 - 0.4 - - -11 0.45 0.154 38％ ＜2 38 - 0.4 - - -12 0.45 0.117 29％ ＜2 - 0.2 0.4 - - -13 0.45 0.126 31％ ＜2 - 0.5 0.4 - - -14 0.45 0.122 30％ ＜2 - 0.3 0.4 - - -15 0.45 0.142 35％ ＜2 38 - 0.5 0.25 - -16 0.45 0.134 33％ ＜2 - - 0.4 0.2 - -17 0.45 0.142 35％ ＜2 - 0.3 0.4 - - NiO
100ppm18 0.45 0.146 36％ 5 - 0.3 0.4 - - -19 0.45 0.130 32％ 16 25 - 0.4 - - -20 0.4 0.104 29％ 8 30 - 0.4 - - -21 0.45 0.150 37％ 10 38 - 0.4 - - SnO
1.022 0.4 0.097 27％ 4 18 - - - 0.1 -23 0.6 0.124 23％ ＜2 20 - 0.2 - - -24 0.7 0.088 14％ ＜2 - 0.7 1.0 - - -25 0.7 0.157 25％ 7 38 - - - - -25 0.77 0.090 13％ - - 0.5 1.0 0.5 - -27 0.5 0.122 17％ 12 76 - 0.1 - - - 总铁 总铁(以Fe2O3 (以Fe2+计 FeO计 Se Co3O4Nd2O3CeO2TiC2V2O5其它％ ％28 0.45 0.146 36％ 7 80 - - - - -29 0.675 0.213 35％ 9 57 - - - - -30 1.23 0.443 40％ 11 104 - - - - -31 0.675 0.182 30％ 14 57 - - - - -32 0.7 0.227 36％ 20 80 - - - - -33 0.7 0.227 36％ 20 120 - - - - -34 0.7 0.258 41％ 16 120 - - - -35 0.675 0.249 41％ 3 57 - 0.2 1.036 0.9 0.300 37％ 10 20 - - - - -37 0.7 0.290 46％ 11 2.0 - - - -38 0.8 0.209 29％ 24 81 - - - - -39 1.0 0.225 25％ 14 150 - - - - -40 0.6 0.086 16％ - 20 - 0.4 - - Mn02
1.0241 0.6 0.162 30 ＜2 20 0.1 - - - -42 0.7 0.258 41％ 15 120 - NiO
275ppm13 1.0 0.315 35％ 9 20 - - - - -44 1.23 0.277 25％ 12 104 - - - - -45 1.40 0.252 20％ 10 104 - - - - -46 1.30 0.257 22％ 5 130 - - - - NiO
131ppm47 0.9 0.186 23％ 6 65 - - - - NiO
65ppm48 1.1 0.346 35％ 13 105 - - - - NiO
131ppm49 0.8 0.173 24％ 12 30 0.5 - - - -50 0.6 0.167 31％ 11 30 0.5 - - - -51 0.6 0.157 29％ 17 80 1.0 - - - -52 0.45 0.146 36％ 7 80 - 0.05 -53 0.6 0.119 22％ 20 - 1.0 - - - -透过率、颜色
主波长
LT DSHT UVT a* b* λD 色纯度1 70 70 40 -0.3 1.1 454 2.1％2 69 61 23 -1.9 -1.4 85 2.7％3 68 59 21 -0.8 -2.0 570 1.2％4 68 56 22 -2.4 -0.6 489 2.2％5 82 75 17 -2.2 +4.9 569 3.9％6 80 69 23 -4.5 +4.5 558 3.1％7 73 59 25 -3.5 -3.2 486 4.9％8 80 72 23 -1.4 +1.6 547 0.5％9 64 55 20 -1.4 +1.5 547 0.6％10 64 48 22 -3.7 -1.9 488 4.0％11 64 46 23 -4.9 -3.8 487 6.1％12 72 54 20 -3.0 +2.2 530 0.9％13 71 55 22 -4.0 -1.6 489 3.9％14 73 56 22 -3.4 +0.6 495 1.7％15 64 47 17 -4.3 -0.6 492 3.1％16 74 52 20 -4.6 +3.0 534 1.6％17 67 49 22 -4.5 +2.3 515 1.3％18 65 47 18 -2.3 +3.7 564 2.8％19 57 46 15 +1.0 +9.0 553 3.0％20 64 54 20 -0.3 +3.8 576 3.4％21 60 47 19 -1.9 +2.1 553 1.1％22 69 57 18 -4.7 +4.3 553 3.0％23 71 54 22 -3.8 +1.0 499 1.5％24 67 58 11 -2.0 +3.7 566 2.7％25 61 45 21 -4.4 +0.5 493 3.3％26 73 60 8 -5.7 +3.9 536 2.2％27 48 41 18 -0.8 +1.1 552 0.4％28 51 42 22 -3.8 -2.1 488 4.5％29 50 35 20 -4.0 -0.2 493 2.8％
主波长
LT DSHT UVT a* b* λD 色纯度30 30 16 9 -8.8 -4.1 489 10.3％31 49 36 17 -2.5 +2.5 553 1.7％32 39 29 13 -0.7 +4.9 574 5.6％33 33 25 12 -1.0 +0.9 511 0.3％34 37 27 16 -3.3 -4.3 484 6.9％35 54 36 15 -7.4 -1.3 492 5.5％36 51 29 16 -6.6 +3.3 521 2.1％37 40 28 15 -3.5 -3.4 486 6.0％38 36 27 9 +0.6 +8.4 578 10.9％39 33 26 -3.9 -5.0 485 8.3％40 75 60 13 -6.0 +4.4 543 2.7％41 69 49 23 -5.8 -2.5 489 5.4％42 34 25 17 -4.0 +1.4 504 1.7％43 52 28 15 -9.5 +0.3 496 5.3％44 36 24 7 -5.7 +0.4 496 3.6％45 39 27 5 -7.4 +0.1 496 4.7％46 35 25 7 -7.8 -1.0 493 6.3％47 53 38 16 -6.7 -1.2 492 5.1％48 32 20 9 -7.2 +0.8 498 4.3％49 38 26 8 -3.5 +5.0 563 4.9％50 41 28 13 -3.4 -1.2 501 1.6％51 35 27 9 -0.5 +4.6 575 5.4％52 51 42 22 -3.8 -2.1 487 4.5％53 40 33 8 +2.4 -10.0 581 13％
给出的几个实施例的玻璃具有优越的红外和紫外吸收性，同时具有中性颜色，因而适合作为高性能的建筑玻璃。建筑玻璃的性能通常指6mm厚的玻璃性能，除了DSHT外，还要求总太阳热透过率(TSHT)符合要求。下面给出了一些特别适合用于建筑的实施例：6mm厚的玻璃透过率实施例 透光率 DSHT TSHT UVT3 58％ 48％ 60％ 15％7 65％ 48％ 60％ 20％11 55％ 36％ 51％ 17％13 63％ 44％ 57％ 16％14 65％ 44％ 57％ 16％23 63％ 44％ 57％ 16％
Claims (26)
1. 一种中性色调(如本文所定义)的吸收IR和UV的钠钙硅玻璃，其亚铁含量由下式计算：
总铁含量(以Fe2O3表示)在0.25-1.75％(重量)范围内，
该玻璃被Se、Co3O4、Nd2O3、NiO、MnO、V2O5、CeO2、TiO2、CuO和SnO中的一种或多种染色为中性颜色，
该玻璃厚度为4mm时，其可见光透过率至少为32％，UV透过率不超过25％，直接太阳热透过率至少比可见光透过率低7个百分点，其主波长最好低于570nm，假如主波长大于570nm，可见光透过率大于60％，则其色纯度不大于4，
并且当玻璃中存在Se时，则至少还存在选自Co3O4、Nd2O3、NiO、MnO、CuO、SnO、V2O5、CeO2和TiO2的另一种着色剂，其量至少为Se量的1.5倍。
2. 一种权利要求1的玻璃，其可见光透过率不超过60％，总铁含量(以Fe2O2表示)至少为0.7％，并且Co3O4、NiO和Se共同作为着色剂。
3. 一种权利要求1的玻璃，其可见光透过率至少为60％，总铁含量(以Fe2O3表示)在约0.25～0.77％(重量)范围内，其中着色剂包括V2O5、CeO2、TiO2、Se、Co3O4、NiO、SnO、Nd2O3和MnO中的至少一种。
4. 权利要求3的玻璃，其中总铁含量最大为0.3％(重量)，着色剂包括至少一种选自由V2O5、CeO2和TiO2组成物组中的物质，还包括至少一种选自由Se、Co3O4、NiO、Nd2O3和MnO组成的物组中的物质。
5. 权利要求3的玻璃，其中总铁含量至少为0.3％(重量)，着色剂包括至少一种选自由Se、Co3O4、NiO、Nd2O3和MnO组成的物组中的物质。
6. 权利要求1的玻璃，其中着色剂包括至少三种选自由Se、Co3O4、Nd2O3、CeO2、TiO2、V2O5、NiO、MnO、SnO和CuO组成的物组中的物质的混合物。
7. 权利要求6的玻璃，其中三种着色剂中至少一种是选自由V2O5、CeO2和TiO2组成的物组，并且至少另外一种着色剂选自由Se、CO3O4、Nd2O3、NiO、MnO、SnO和CuO组成的物组。
8. 权利要求3至7的任一项的玻璃，其中Nd2O3的量不超过2.5％(重量)。
9. 权利要求3至7的任一项的玻璃，其中MnO的量不超过1％(重量)。
10. 权利要求3至7的任一项的玻璃，其中CeO2的量约0.1％～1％(重量)。
11. 权利要求3至7的任一项的玻璃，其中V2O5的量约0.05％～0.2％(重量)。
12. 权利要求2至7的任一项的玻璃，其中存在的Se的量不超过50ppm(重量)。
13. 权利要求2至7的任一项的玻璃，其中Co3O4的量不超过200ppm(重量)。
14. 权利要求2至7的任一项的玻璃，其中NiO的量不超过275ppm(重量)。
15. 权利要求2的玻璃，它含有不超过275ppm(重量)的NiO，不超过15ppm(重量)的Se和不超过130ppm(重量)的Co3O4。
16. 权利要求3的玻璃，其中Se的量不超过5ppm(重量)。
17. 权利要求1的玻璃，其可见光透过率不超过60％，总铁含量(以Fe2O3表示)至少为0.8％(重量)，并且Co3O4和Se共同作为着色剂。
18. 权利要求17的玻璃，其中Co3O4的量不超过150ppm(重量)，Se的量不超过15ppm(重量)。
19. 前述任一项权利要求的玻璃，其亚铁含量至少为总铁含量的18％。
20. 前述任一项权利要求的IR和UV吸收玻璃，当厚度为4nm时，其直接太阳热透过率至少低于其可见光透过率10个百分点。
21. 权利要求1的IR和UV吸收玻璃，当厚度为4mm时，其主波长大于570nm，可见光透过率大于60％，其色纯度低于2。
22. 前述任一项权利要求的IR和UV吸收玻璃，它包含Se和至少另外一种选自由Co3O4、Nd2O3、NiO和MnO组成的物组中的着色剂，该着色剂重量至少为Se量的2倍。
23. 一种在上文任一个实施例中叙述的具有中性色调的IR和UV吸收玻璃。
24. 根据前述任一项权利要求的IR和UV吸收玻璃。
25. 一种由前述任一项权利要求的玻璃构成的窗户。
26. 一种由前述任一项权利要求的玻璃组成的车窗。