CN1176230A - 绿色隐蔽玻璃 - Google Patents
绿色隐蔽玻璃 Download PDFInfo
- Publication number
- CN1176230A CN1176230A CN97113730A CN97113730A CN1176230A CN 1176230 A CN1176230 A CN 1176230A CN 97113730 A CN97113730 A CN 97113730A CN 97113730 A CN97113730 A CN 97113730A CN 1176230 A CN1176230 A CN 1176230A
- Authority
- CN
- China
- Prior art keywords
- glass
- weight
- goods
- perviousness
- concentration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了透光性为60%以下的绿色红外和紫外辐射吸收玻璃。该玻璃制品的组合物采用标准的钠－钙－硅玻璃基础组成和外加的铁、钴、硒和铬以及任选的钛作为红外和紫外辐射吸收物质及着色剂。本发明的玻璃的颜色特征为主波长约为480—565纳米,色纯度为不高于约20%,该玻璃组合物根据特定的运用和所需的透光性,可以具有不同的光学性能。
Description
发明背景
本发明涉及绿色钠-钙-硅玻璃，该玻璃具有较低的透光性，它特别适用于用作车辆隐蔽玻璃窗，例如货车的侧窗和后窗。更进一步地说，该玻璃具有60％或更低，优选地为约10-40％的透光性。用于本文时，术语“绿色”是指包括主波长约为480-565纳米(nm)并且颜色为兰绿色、黄绿色或灰绿色的玻璃。此外，本发明的玻璃与用于汽车的典型绿色玻璃相比通常具有较低的红外和紫外辐射透过性。该玻璃还可以与浮法玻璃制造工艺相匹配。
在本领域中已经知道有多种深色红外和紫外辐射吸收玻璃组合物。在典型的深色着色汽车隐蔽玻璃中的主要着色剂是铁，它们通常是以Fe2O3和FeO两种形式存在。某些玻璃采用钴、硒和任选的镍与铁组合在一起以进一步控制红外和紫外辐射以及颜色，例如参见美国专利4873206(Jones)、5278108(Cheng等人)、5308805(Baker等人)和5393593(Gulotta等人)以及欧洲专利申请0705800。其它着色剂还包括与这些着色剂组合在一起的铬，例如参见美国专利4104076(Pons)、4339541(DelaRuye)、5023210(Krumwiede等人)和5352640(Combes等人)、欧洲专利申请0536049、法国专利2331527和加拿大专利2148954。另外，其它玻璃还可以包括外加物质，例如在WO96/00194中所说的物质，该专利指出在该玻璃组合物中包括氟、锆、锌、铈、钛和铜并且要求碱土金属氧化物的总量低于玻璃的10％重量。
在制造红外和紫外辐射吸收玻璃时，必须将铁和其它外加剂的相对含量严格控制在操作范围内以提供所需的颜色和光学性能。人们需要可以用作为车辆隐蔽窗的深色绿色玻璃以补充通常用于汽车中的绿色玻璃，它们具有特别好的太阳性能并且可以与工业浮法玻璃制造工艺相匹配。
本发明的概要
本发明提供了透光性为60％以下的绿色红外和紫外辐射吸收玻璃。该玻璃制品的组合物采用标准的钠-钙-硅玻璃基础组成和外加的铁、钴、硒和铬以及任选的钛作为红外和紫外辐射吸收物质及着色剂。本发明的玻璃的颜色特征为主波长约为480-565纳米，优选地约为495-560纳米，色纯度为不高于约20％，优选地为不高于约10％，更优选地为不高于约7％。该玻璃组合物根据特定的运用和所需的透光性，可以具有不同的光学性能。
在本发明的一个具体实施方案中，绿色红外和紫外辐射吸收钠-钙-硅玻璃制品的玻璃组合物包括太阳辐射吸收和着色剂部分，它主要由约0.60-4％重量总铁、约0.13-0.9％重量FeO、约40-500PPMCoO、约5-70PPMSe、约15-800PPMCr2O3和约0.02-1％重量TiO2组成。在本发明的另一个具体实施方案中，该绿色红外和紫外辐射吸收钠-钙-硅玻璃制品的玻璃组合物包括太阳辐射吸收和着色剂部分，它主要由1至小于1.4％重量总铁、约0.2-0.6％重量FeO、多于200-约500PPMCoO、约5-70PPMSe、高于200-约800PPMCr2O3和0-约1％重量TiO2组成。
本发明的详细描述
本发明的基础玻璃，即没有红外和紫外辐射吸收物质和/或着色剂(本发明的目的)的玻璃的主要成分是工业钠-钙-硅玻璃，其特征在于具有下列组成：
重量％
SiO2 66-75
Na2O 10-20
CaO 5-15
MgO 0-5
Al2O30-5
K2O 0-5用于本文时，所有的“重量％”值均是基于最终玻璃组合物的总重量。
向该基础玻璃中，本发明以铁、钴、硒、铬和任选的钛形式加入红外和紫外辐射吸收物质和着色剂。如本发明中所说，铁以Fe2O3和FeO表示，钴以CoO表示，硒以Se表示，铬以Cr2O3表示而钛以TiO2表示。应当明白，本发明中所说的玻璃组合物还可以含有少量其它物质，例如熔化和澄清助剂、外来物质或杂质。还应该明白，在本发明的一个具体方案中，在该玻璃中还可以含有少量外加物质在改进该玻璃的太阳性能，正如在下文中详细描述的那样。
在玻璃组合物中的铁氧化物有几个功能。三价铁，Fe2O3是强紫外辐射吸收剂并且在该玻璃中起黄色着色剂的作用。二价铁，FeO是强红外辐射吸收剂并起兰色着色剂的作用。在本发明的玻璃中存在的铁的总量根据标准分析操作获得并以Fe2O3来表示，但并不是说所有的铁实际上均以Fe2O3存在于玻璃中，类似地，二价铁的量以FeO报导，尽管它实际上并不一定以FeO存在于玻璃中。为了反映二价铁和三价铁在所说的玻璃中的相对含量，术语“氧化还原比”是指二价铁(以FeO表示)的量除以总铁量(以Fe2O3表示)。此外，除非另有说明，在本说明书中，术语“总铁”是指以Fe2O3表示的总铁，术语“FeO”是指以FeO表示的二价铁。
硒是一种紫外和红外辐射吸收着色剂，它可以使钠-钙-硅玻璃呈粉红色或棕色。硒还可以吸收某些红外辐射，使用它可以降低氧化还原比。CoO可以作为一种兰色着色剂，并且不具有任何合适的紫外或红外辐射吸收性能。Cr2O3使玻璃呈绿色并且有助于控制最终的玻璃颜色。可以相信铬可以提供某些紫外辐射吸收。TiO2是一种紫外辐射吸收剂，它可以作为一种着色剂而使该玻璃组合物呈黄色。因此，需要在铁，即二价铁和三价铁氧化物、铬、硒、钴和任选的钛含量之间有一种适当的平衡，以获得具有所需的光学性能的绿色隐蔽玻璃。
本发明的玻璃可以以连续的、大规模工业熔化操作工艺熔化并澄清，通过浮法工艺形成各种厚度的平板玻璃，在所说的浮法工艺中，熔融玻璃在保持玻璃带形状并冷却时支承在熔融金属，通常为锡的浴槽上。应当明白由于在熔融锡上形成该玻璃，因此可能会有可测出数量的氧化锡迁移到与锡接触的玻璃一侧表面中。典型地，浮法玻璃片在与锡接触的玻璃表面最初的25微米中至少含有0.05-2％重量浓度的二氧化锡。典型的二氧化锡背底值可以高达30PPM。
用来制造本发明的玻璃组合物的熔化和成型装置包括但不限于常规的顶部燃烧连续熔化操作(如本领域中熟知的那样)或多阶段熔化操作，例如在Kunkle等人的美国专利4381934、Pecoraro等人的美国专利4792536和Cerutti等人的美国专利4886539中所说。如果需要，可以在玻璃制造过程中的熔化和/或成型阶段中使用一种搅拌装置来均化玻璃，从而制造具有最高光学质量的玻璃。
表1、2和3表示体现本发明原则的玻璃组合物的实施例。在表1和2中的实施例是计算机模拟的组合物，它们是由PPG工业公司开发出来的玻璃颜色和光学性能计算机模型产生的。表3中的实施例是真实的实验熔体。表1和3中的光学性能是基于0.160英寸(4.06毫米)的参考厚度，而表2中的光学性能是基于0.154英寸(3.91毫米)的参考厚度。为了进行比较，可以采用在美国专利4792536中所说的方程式将这些实施例的光学性能在不同的厚度下近似。在这些表中仅仅例出了实施例中的铁、钴、硒、铬和钛。在表中所给出的透光性数据方面，透光性(LTA)是在380-770纳米波长范围内采用2度观测器采用C.I.E.标准光源“A”测定的，而根据主波长和色纯度的玻璃颜色是采用2度观测器采用C.I.E.标准光源“A”、按照在ASYM E308-90中所说的方法测定的。总太阳紫外透过性(TSUV)是在300-400纳米波长范围内测定的，总太阳红外透过性(TSIR)是在720-2000纳米波长范围内测定的，总太阳能透过性(TSET)是在300-2000纳米波长范围内测定的。TSUV、TSIR和TSEI透过性数据采用Parry Monn空气质量2.0直接太阳辐射数据计算并且采用本领域内已知的梯形法则进行积分。
在表1和表2中所说的光学性能是具有通常如本文中所说的基础玻璃组合物和着色剂的玻璃的性能，它们以该玻璃成分的吸收系数为基础(假定该玻璃是完全均匀的并且采用本领域内已知的常规方法来制造)。
表3中的信息是基于具有下列配合料成分的实验熔体：
碎玻璃A 125克
碎玻璃B 22.32克
碎玻璃C 8.93克
铁粉 0.32克
Cr2O3 0.0461克
TiO2 0.3-0.6克
Se 0.0037-0.0073克
石墨 0.015克用于此熔体中的碎玻璃包括各种数量的铁、钴、硒、铬和/或钛。更进一步地说，碎玻璃A包括0.811％重量总铁、0.212％重量FeO、101PPMCoO、17PPMSe、8PPMCr2O3和0.02％重量TiO2。碎玻璃B包括1.417％重量总铁、0.362％重量FeO、211.25PPM CoO、25PPMSe和7.5PPMCr2O3。碎玻璃C包括0.93％重量总铁、0.24％重量FeO、6PPMCr2O3和0.02％重量TiO2。在制备该熔体时，将成分称出并混合。然后将这些物料放入4英寸铂坩埚并加热到2600华氏度(1427℃)，保持30分钟，而后加热到2650华氏度(1454℃)达1小时。随后，将熔融玻璃在水中制成熔块，干燥，并放入2英寸铂坩埚中，在2650华氏度(1454℃)下再加热至少1小时。然后将熔融玻璃从坩埚中倒出，形成玻璃块并退火。将样品从该玻璃块上切下并研磨抛光以进行分析。该玻璃组合物的化学分析结果采用RIGAKU 3370 X射线荧光分光光度计来测定。采用本领域内已知的化学方法来测定FeO含量。该玻璃的光学性能在将玻璃钢化或向紫外辐射长时间暴露(它可能影响该玻璃的光学性能)之前采用Perkin-Elmer Lambda 9 UV/VIS/NIR分光光度计在经过退火的样品上测定。
下面是表3中所说的特定的实验熔体有代表性的基础氧化物，它们也落在前面所说的基础玻璃组合物的范围中：
SiO2 70-72％重量
Na2O 12-14％重量
CaO 8-10％重量
MgO 3-4％重量
Al2O3 0.1-0.6％重量
K2O 0.01-0.15％重量这些熔体的分析结果还说明这些玻璃含有约0.081％重量MnO2。可以认为MnO2是作为碎玻璃中的成分而进入该玻璃熔体中的。
表1
表1(续)
| 例1 | 例2 | 例3 | 例4 | 例5 | 例6 | 例7 | 例8 | 例9 | 例10 | 例11 | 例12 | |
| FeO(wt.％) | 0.4320 | 0.5580 | 0.7240 | 0.4775 | 0.5225 | 0.5143 | 0.5670 | 0.6545 | 0.6110 | 0.4725 | 0.6938 | 0.5980 |
| 总铁(wt.％) | 1.920 | 1.860 | 1.810 | 1.910 | 1.900 | 1.870 | 1.890 | 1.870 | 1.880 | 1.890 | 1.850 | 1.840 |
| 模型氧化还原比 | 0.2250 | 0.3000 | 0.4000 | 0.2500 | 0.2750 | 0.2750 | 0.3000 | 0.3500 | 0.3250 | 0.2500 | 0.3750 | 0.3250 |
| Cr2O3(wt.％) | 0.0365 | 0.0350 | 0.0350 | 0.0365 | 0.0365 | 0.0340 | 0.0365 | 0.0370 | 0.0365 | 0.0350 | 0.0370 | 0.0355 |
| CoO(wt.％) | 0.0391 | 0.0356 | 0.0310 | 0.0377 | 0.0364 | 0.0370 | 0.0351 | 0.0326 | 0.0338 | 0.0379 | 0.0314 | 0.0344 |
| Se(wt.％) | 0.0047 | 0.0050 | 0.0054 | 0.0048 | 0.0049 | 0.0048 | 0.0050 | 0.0052 | 0.0051 | 0.0047 | 0.0053 | 0.0050 |
| TiO2(wt.％) | 0.1800 | 0.2400 | 0.4900 | 0.3400 | 0.4400 | |||||||
| LTA(％) | 5.02 | 5.04 | 5.05 | 5.05 | 5.06 | 5.08 | 5.08 | 5.10 | 5.10 | 5.12 | 5.12 | 5.13 |
| TSUV(％) | 2.48 | 2.88 | 3.58 | 2.62 | 2.77 | 2.59 | 2.94 | 3.29 | 3.11 | 2.52 | 3.51 | 2.95 |
| TSIR(％) | 7.28 | 3.84 | 1.73 | 5.76 | 4.59 | 4.78 | 3.68 | 2.41 | 2.97 | 5.91 | 2.00 | 3.16 |
| TSET(％) | 6.33 | 4.42 | 3.18 | 5.50 | 4.85 | 4.96 | 4.33 | 3.60 | 3.93 | 5.61 | 3.37 | 4.05 |
| DW(nm) | 551.02 | 550.90 | 550.96 | 551.29 | 550.79 | 550.61 | 550.68 | 550.52 | 550.92 | 550.76 | 550.81 | 550.64 |
| Pe(％) | 3.58 | 3.57 | 3.62 | 3.72 | 3.72 | 3.85 | 3.76 | 3.85 | 3.84 | 3.86 | 3.83 | 3.98 |
| 例13 | 例14 | 例15 | 例16 | 例17 | 例18 | 例19 | 例20 | 例21 | 例22 | 例23 | 例24 | |
| FeO(wt.％) | 0.7360 | 0.4298 | 0.6825 | 0.6405 | 0.3860 | 0.3860 | 0.3750 | 0.3750 | 0.8750 | 0.3750 | 0.8125 | 0.3750 |
| 总铁(wt：％) | 1.840 | 1.910 | 1.820 | 1.830 | 1.930 | 1.930 | 1.500 | 1.500 | 3.500 | 1.500 | 3.250 | 1.500 |
| 模型氧化还原比 | 0.4000 | 0.2250 | 0.3750 | 0.3500 | 0.2000 | 0.2000 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 |
| Cr2O3(wt.％) | 0.0370 | 0.0340 | 0.0340 | 0.0345 | 0.0375 | 0.0330 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0250 |
| CoO(wt.％) | 0.0302 | 0.0390 | 0.0320 | 0.0330 | 0.0398 | 0.0400 | 0.0450 | 0.0400 | 0.0220 | 0.0220 | 0.0220 | 0.0350 |
| Se(wt.％) | 0.0054 | 0.0046 | 0.0052 | 0.0051 | 0.0045 | 0.0044 | 0.0027 | 0.0027 | 0.0027 | 0.0060 | 0.0027 | 0.0027 |
| TiO2(wt.％) | 0.2600 | 0.4500 | 0.3900 | 0.3900 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | ||
| LTA(％) | 5.13 | 5.15 | 5.16 | 5.19 | 5.20 | 5.28 | 6.54 | 7.80 | 8.59 | 8.73 | 9.20 | 9.33 |
| TSUV(％) | 3.72 | 2.41 | 3.29 | 3.16 | 2.40 | 2.24 | 6.17 | 6.21 | 1.07 | 2.86 | 1.32 | 6.24 |
| TSIR(％) | 1.64 | 7.38 | 2.11 | 2.58 | 9.28 | 9.29 | 9.94 | 9.99 | 0.89 | 9.98 | 1.18 | 10.04 |
| TSET(％) | 3.16 | 6.44 | 3.44 | 3.73 | 7.50 | 7.54 | 9.18 | 9.65 | 3.64 | 9.09 | 4.10 | 10.20 |
| DW(nm) | 551.01 | 550.93 | 550.70 | 550.93 | 550.63 | 550.86 | 478.05 | 479.92 | 549.82 | 581.29 | 549.90 | 482.49 |
| Pe(％) | 3.86 | 3.70 | 3.89 | 3.92 | 3.76 | 3.89 | 30.19 | 23.61 | 18.23 | 38.27 | 16.69 | 16.75 |
表1(续)
表1(续)
| 例25 | 例26 | 例27 | 例28 | 例29 | 例30 | 例31 | 例32 | 例33 | 例34 | 例35 | 例36 | |
| FeO(wt.％) | 0.375 | 0.75 | 0.225 | 0.6875 | 0.375 | 0.175 | 0.375 | 0.625 | 0.5625 | 0.375 | 0.225 | 0.5 |
| 总铁(wt.％) | 1.5000 | 3.0000 | 0.9000 | 2.7500 | 1.5000 | 0.7000 | 1.5000 | 2.5000 | 2.2500 | 1.5000 | 0.9000 | 2.0000 |
| 模型氧化还原比 | 0.250 | 0.250 | 0.250 | 0.250 | 0.250 | 0.250 | 0.250 | 0.250 | 0.250 | 0.250 | 0.250 | 0.250 |
| Cr2O3(wt.％) | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0210 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0250 |
| CoO(wt.％) | 0.0220 | 0.0220 | 0.0450 | 0.0220 | 0.0220 | 0.0450 | 0.0300 | 0.0220 | 0.0220 | 0.0220 | 0.0400 | 0.0220 |
| Se(wt.％) | 0.0053 | 0.0027 | 0.0017 | 0.0027 | 0.0046 | 0.0011 | 0.0027 | 0.0027 | 0.0027 | 0.0039 | 0.0017 | 0.0027 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 9.74 | 9.86 | 10.49 | 10.56 | 10.90 | 10.99 | 11.19 | 11.33 | 12.15 | 12.23 | 12.42 | 13.04 |
| TSUV(％) | 3.39 | 1.62 | 18.98 | 2.00 | 4.01 | 26.80 | 6.28 | 2.49 | 3.11 | 4.74 | 19.09 | 3.91 |
| TSIR(％) | 10.02 | 1.58 | 23.31 | 2.11 | 10.06 | 30.76 | 10.09 | 2.85 | 3.88 | 10.10 | 23.41 | 5.30 |
| TSET(％) | 9.54 | 4.64 | 19.61 | 5.29 | 10.08 | 24.75 | 10.84 | 6.09 | 7.09 | 10.72 | 20.37 | 8.36 |
| DW(nm) | 579.72 | 549.97 | 474.57 | 550.01 | 577.57 | 473.07 | 487.02 | 550.02 | 549.99 | 574.14 | 475.74 | 549.87 |
| Pe(％) | 31.58 | 15.12 | 43.48 | 13.51 | 24.63 | 50.78 | 9.78 | 11.87 | 10.21 | 17.48 | 37.70 | 8.51 |
| 例37 | 例38 | 例39 | 例40 | 例41 | 例42 | 例43 | 例44 | 例45 | 例46 | 例47 | 例48 | |
| FeO(wt.％) | 0.6 | 0.175 | 0.375 | 0.5625 | 0.375 | 0.375 | 0.525 | 0.375 | 0.375 | 0.4375 | 0.4875 | 0.375 |
| 总铁(wt.％) | 1.500 | 0.700 | 1.500 | 1.500 | 1.500 | 1.500 | 1.500 | 1.500 | 1.500 | 1.750 | 1.500 | 1.500 |
| 模型氧化还原比 | 0.4000 | 0.2500 | 0.2500 | 0.3750 | 0.2500 | 0.2500 | 0.3500 | 0.2500 | 0.2500 | 0.2500 | 0.3250 | 0.2500 |
| Cr2O3(wt.％) | 0.0250 | 0.0210 | 0.0800 | 0.0250 | 0.0250 | 0.0700 | 0.0250 | 0.0250 | 0.0600 | 0.0250 | 0.0250 | 0.0500 |
| CoO(wt.％) | 0.0220 | 0.0400 | 0.0220 | 0.0220 | 0.0250 | 0.0220 | 0.0220 | 0.0220 | 0.0220 | 0.0220 | 0.0220 | 0.0220 |
| Se(wt.％) | 0.0027 | 0.0011 | 0.0027 | 0.0027 | 0.0027 | 0.0027 | 0.0027 | 0.0032 | 0.0027 | 0.0027 | 0.0027 | 0.0027 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 13.10 | 13.12 | 13.23 | 13.40 | 13.45 | 13.53 | 13.70 | 13.78 | 13.85 | 14.00 | 14.02 | 14.17 |
| TSUV(％) | 9.03 | 26.97 | 6.09 | 8.50 | 6.31 | 6.13 | 8.00 | 5.62 | 6.18 | 4.96 | 7.54 | 6.22 |
| TSIR(％) | 3.24 | 30.90 | 10.05 | 3.89 | 10.14 | 10.07 | 4.69 | 10.14 | 10.09 | 7.31 | 5.66 | 10.11 |
| TSET(％) | 7.78 | 25.64 | 10.89 | 8.22 | 11.61 | 11.10 | 8.74 | 11.50 | 11.31 | 10.00 | 9.37 | 11.54 |
| DW(nm) | 488.02 | 474.18 | 554.18 | 489.76 | 502.78 | 553.79 | 492.18 | 566.66 | 553.27 | 549.62 | 496.03 | 552.58 |
| Pe(％) | 11.44 | 45.13 | 12.49 | 9.38 | 3.22 | 11.14 | 7.32 | 10.21 | 9.78 | 6.79 | 5.31 | 8.43 |
表1(续)
表1(续)
| 例49 | 例50 | 例51 | 例52 | 例53 | 例54 | 例55 | 例56 | 例57 | 例58 | 例59 | 例60 | |
| FeO(wt.％) | 0.4500 | 0.3750 | 0.4125 | 0.2250 | 0.3750 | 0.3750 | 0.3750 | 0.3750 | 0.3750 | 0.3750 | 0.2948 | 0.3750 |
| 总铁(wt.％) | 1.500 | 1.500 | 1.500 | 0.900 | 1.500 | 1.500 | 1.500 | 1.500 | 1.500 | 1.500 | 1.310 | 1.500 |
| 模型氧化还原比 | 0.3000 | 0.2500 | 0.2750 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2250 | 0.2500 |
| Cr2O3(wt.％) | 0.0250 | 0.0400 | 0.0250 | 0.0250 | 0.0300 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0280 | 0.0250 |
| CoO(wt.％) | 0.0220 | 0.0220 | 0.0220 | 0.0350 | 0.0220 | 0.0220 | 0.0220 | 0.0220 | 0.0220 | 0.0220 | 0.0235 | 0.0220 |
| Se(wt.％) | 0.0027 | 0.0027 | 0.0027 | 0.0017 | 0.0027 | 0.0027 | 0.0027 | 0.0027 | 0.0027 | 0.0027 | 0.0028 | 0.0027 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.8000 | 0.7000 | 0.6000 | 0.5000 | 0.4000 | 0.3000 | |
| LTA(％) | 14.34 | 14.51 | 14.68 | 14.74 | 14.86 | 14.90 | 14.93 | 14.95 | 14.97 | 14.99 | 15.01 | 15.01 |
| TSUV(％) | 7.11 | 6.27 | 6.71 | 19.20 | 6.31 | 5.44 | 5.58 | 5.72 | 5.87 | 6.02 | 7.47 | 6.18 |
| TSIR(％) | 6.86 | 10.14 | 8.34 | 23.52 | 10.16 | 10.17 | 10.17 | 10.17 | 10.17 | 10.17 | 15.69 | 10.17 |
| TSET(％) | 10.12 | 11.77 | 11.04 | 21.26 | 12.02 | 11.97 | 12.00 | 12.03 | 12.05 | 12.08 | 15.28 | 12.11 |
| DW(nm) | 503.82 | 551.62 | 525.32 | 477.06 | 550.13 | 558.49 | 557.46 | 556.28 | 554.91 | 553.31 | 550.91 | 551.42 |
| Pe(％) | 3.46 | 7.08 | 2.97 | 31.54 | 5.72 | 8.18 | 7.66 | 7.14 | 6.61 | 6.09 | 3.66 | 5.57 |
| 例61 | 例62 | 例63 | 例64 | 例65 | 例66 | 例67 | 例68 | 例69 | 例70 | 例71 | 例72 | |
| FeO(wt.％) | 0.3750 | 0.3750 | 0.3750 | 0.3493 | 0.3810 | 0.3250 | 0.4960 | 0.4650 | 0.3750 | 0.2600 | 0.3750 | 0.2880 |
| 总铁(wt.％) | 1.500 | 1.500 | 1.500 | 1.270 | 1.270 | 1.300 | 1.240 | 1.240 | 1.500 | 1.300 | 1.500 | 1.280 |
| 模型氧化还原此 | 0.2500 | 0.2500 | 0.2500 | 0.2750 | 0.3000 | 0.2500 | 0.4000 | 0.3750 | 0.2500 | 0.2000 | 0.2500 | 0.2250 |
| Cr2O3(wt.％) | 0.0250 | 0.0250 | 0.0250 | 0.0255 | 0.0260 | 0.0280 | 0.0290 | 0.0260 | 0.0250 | 0.0270 | 0.0250 | 0.0260 |
| CoO(wt.％) | 0.0220 | 0.0220 | 0.0220 | 0.0222 | 0.0212 | 0.0226 | 0.0178 | 0.0189 | 0.0220 | 0.0245 | 0.0220 | 0.0240 |
| Se(wt.％) | 0.0027 | 0.0027 | 0.0027 | 0.0029 | 0.0030 | 0.0029 | 0.0033 | 0.0032 | 0.0027 | 0.0027 | 0.0027 | 0.0027 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.3000 | 0.1500 | 0.2000 | 0.1000 | 0.1300 | 0.0200 | 0.4800 | ||
| LTA(％) | 15.04 | 15.04 | 15.04 | 15.04 | 15.05 | 15.05 | 15.05 | 15.06 | 15.06 | 15.07 | 15.08 | 15.08 |
| TSUV(％) | 6.34 | 6.34 | 6.34 | 7.81 | 8.35 | 7.82 | 10.25 | 9.45 | 6.50 | 7.10 | 6.63 | 6.98 |
| TSIR(％) | 10.17 | 10.17 | 10.17 | 11.67 | 9.85 | 13.30 | 5.43 | 6.36 | 10.17 | 19.02 | 10.17 | 16.29 |
| TSET(％) | 12.14 | 12.14 | 12.14 | 13.09 | 12.09 | 13.99 | 9.57 | 10.11 | 12.17 | 17.12 | 12.20 | 15.62 |
| DW(nm) | 549.10 | 549.10 | 549.10 | 550.99 | 550.72 | 550.89 | 551.07 | 550.60 | 546.28 | 550.76 | 543.54 | 550.58 |
| Pe(％) | 5.04 | 5.04 | 5.04 | 3.66 | 3.57 | 3.69 | 3.79 | 3.60 | 4.53 | 3.54 | 4.12 | 3.82 |
表1(续)
表1(续)
| 例73 | 例74 | 例75 | 例76 | 例77 | 例78 | 例79 | 例80 | 例81 | 例82 | 例83 | 例84 | |
| FeO(wt.％) | 0.4410 | 0.4375 | 0.3200 | 0.3548 | 0.4688 | 0.4095 | 0.4960 | 0.3840 | 0.2640 | 0.4128 | 0.3750 | 0.3375 |
| 总铁(wt.％) | 1.260 | 1.250 | 1.280 | 1.290 | 1.250 | 1.260 | 1.240 | 1.280 | 1.320 | 1.270 | 1.500 | 1.500 |
| 模型氧化还原比 | 0.3500 | 0.3500 | 0.2500 | 0.2750 | 0.3750 | 0.3250 | 0.4000 | 0.3000 | 0.2000 | 0.3250 | 0.2500 | 0.2250 |
| Cr2O3(wt.％) | 0.0290 | 0.0260 | 0.0260 | 0.0290 | 0.0290 | 0.0260 | 0.0250 | 0.0290 | 0.0280 | 0.0290 | 0.0200 | 0.0250 |
| CoO(wt.％) | 0.0193 | 0.0197 | 0.0230 | 0.0217 | 0.0185 | 0.0205 | 0.0182 | 0.0208 | 0.0242 | 0.0200 | 0.0220 | 0.0220 |
| Se(wt.％) | 0.0032 | 0.0031 | 0.0028 | 0.0029 | 0.0032 | 0.0030 | 0.0032 | 0.0030 | 0.0027 | 0.0031 | 0.0027 | 0.0027 |
| TiO2(wt.％) | 0.3000 | 0.3500 | 0.3900 | 0.4400 | 0.2000 | 0.2000 | ||||||
| LTA(％) | 15.09 | 15.09 | 15.09 | 15.09 | 15.11 | 15.14 | 15.14 | 15.15 | 15.16 | 15.16 | 15.22 | 15.40 |
| TSUV(％) | 9.38 | 8.87 | 7.42 | 8.20 | 9.82 | 8.34 | 9.35 | 8.59 | 7.18 | 8.99 | 6.36 | 5.98 |
| TSIR(％) | 7.19 | 7.33 | 13.67 | 11.32 | 6.24 | 8.48 | 5.44 | 9.69 | 18.60 | 8.33 | 10.18 | 12.44 |
| TSET(％) | 10.59 | 10.66 | 14.20 | 12.91 | 10.05 | 11.32 | 9.58 | 12.02 | 16.92 | 11.26 | 12.27 | 13.49 |
| DW(nm) | 550.53 | 550.77 | 550.65 | 550.53 | 550.80 | 550.87 | 550.70 | 551.1 1 | 550.86 | 550.82 | 547.74 | 559.28 |
| Pe(％) | 3.77 | 3.79 | 3.76 | 3.79 | 3.80 | 3.95 | 3.93 | 3.89 | 3.70 | 3.85 | 4.37 | 7.45 |
| 例85 | 例86 | 例87 | 例88 | 例89 | 例90 | 例91 | 例92 | 例93 | 例94 | 例95 | 例96 | |
| FeO(wt.％) | 0.3750 | 0.3750 | 0.1750 | 0.3000 | 0.3750 | 0.3750 | 0.3750 | 0.2250 | 0.3120 | 0.2990 | 0.2860 | 0.2990 |
| 总铁(wt.％) | 1.500 | 1.500 | 0.700 | 1.500 | 1.500 | 1.500 | 1.500 | 0.900 | 1.200 | 1.150 | 1.100 | 1.100 |
| 模型氧化还原比 | 0.2500 | 0.2500 | 0.2500 | 0.2000 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2600 | 0.2600 | 0.2600 | 0.2720 |
| Cr2O3(wt.％) | 0.0250 | 0.0100 | 0.0210 | 0.0250 | 0.0005 | 0.0250 | 0.0250 | 0.0250 | 0.0230 | 0.0280 | 0.0320 | 0.0320 |
| CoO(wt.％) | 0.0220 | 0.0220 | 0.0350 | 0.0220 | 0.0220 | 0.0200 | 0.0220 | 0.0300 | 0.0196 | 0.0200 | 0.0201 | 0.0198 |
| Se(wt.％) | 0.0025 | 0.0027 | 0.0011 | 0.0027 | 0.0027 | 0.0027 | 0.0020 | 0.0017 | 0.0025 | 0.0024 | 0.0025 | 0.0025 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.0280 | 0.0280 | 0.0280 | 0.0280 |
| LTA(％) | 15.58 | 15.59 | 15.72 | 15.78 | 15.95 | 16.20 | 17.04 | 17.54 | 18.03 | 18.05 | 18.02 | 18.06 |
| TSUV(％) | 6.65 | 6.40 | 27.14 | 5.65 | 6.45 | 6.35 | 7.50 | 19.31 | 9.55 | 10.19 | 10.64 | 10.87 |
| TSIR(％) | 10.18 | 10.21 | 31.05 | 15.27 | 10.23 | 10.19 | 10.22 | 23.63 | 11.9 | 12.88 | 13.95 | 12.88 |
| TSET(％) | 12.43 | 12.54 | 26.69 | 15.14 | 12.80 | 12.53 | 13.22 | 22.30 | 15.38 | 15.96 | 16.53 | 15.95 |
| DW(nm) | 528.36 | 543.24 | 475.35 | 564.59 | 533.25 | 560.22 | 496.92 | 478.60 | 556.5 | 547.3 | 549.7 | 545.6 |
| Pe(％) | 3.26 | 3.03 | 39.04 | 9.88 | 1.81 | 8.39 | 5.84 | 25.04 | 4.43 | 3.36 | 3.62 | 3.27 |
表1(续)
表1(续)
| 例97 | 例98 | 例99 | 例100 | 例101 | 例102 | 例103 | 例104 | 例106 | 例106 | 例107 | 例108 | |
| FeO(wt.％) | 0.3750 | 0.1750 | 0.2250 | 0.3750 | 0.2250 | 0.2250 | 0.3750 | 0.1750 | 0.1750 | 0.2250 | 0.3750 | 0.1750 |
| 总铁(wt.％) | 1.500 | 0.700 | 0.900 | 1.500 | 0.900 | 0.900 | 1.500 | 0.700 | 0.700 | 0.900 | 1.500 | 0.700 |
| 模型氧化还原比 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 |
| Cr2O3(wt.％) | 0.0250 | 0.0210 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0210 | 0.0210 | 0.0250 | 0.0250 | 0.0210 |
| CoO(wt.％) | 0.0220 | 0.0300 | 0.0107 | 0.0150 | 0.0250 | 0.0107 | 0.0220 | 0.0070 | 0.0250 | 0.0107 | 0.0100 | 0.0070 |
| Se(wt.％) | 0.0015 | 0.0011 | 0.0060 | 0.0027 | 0.0017 | 0.0053 | 0.0008 | 0.0060 | 0.0011 | 0.0046 | 0.0027 | 0.0053 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 18.68 | 18.88 | 19.28 | 19.57 | 20.92 | 21.12 | 21.31 | 21.65 | 22.73 | 23.19 | 23.68 | 23.86 |
| TSUV(％) | 8.46 | 27.31 | 7.87 | 6.39 | 19.42 | 9.14 | 10.02 | 9.26 | 27.48 | 10.62 | 6.42 | 10.85 |
| TSIR(％) | 10.25 | 31.19 | 23.35 | 10.25 | 23.73 | 23.46 | 10.29 | 31.12 | 31.34 | 23.57 | 10.30 | 31.22 |
| TSET(％) | 14.13 | 27.91 | 20.49 | 13.63 | 23.52 | 21.34 | 15.65 | 25.68 | 29.35 | 22.31 | 14.95 | 26.65 |
| DW(nm) | 491.19 | 476.64 | 583.88 | 568.92 | 480.62 | 582.85 | 487.95 | 585.96 | 478.18 | 581.60 | 572.24 | 585.04 |
| Pe(％) | 10.53 | 32.49 | 41.80 | 16.72 | 18.24 | 36.18 | 17.10 | 49.85 | 25.55 | 30.33 | 24.81 | 44.03 |
| 例109 | 例110 | 例111 | 例112 | 例113 | 例114 | 例115 | 例116 | 例117 | 例118 | 例119 | 例120 | |
| FeO(wt.％) | 0.2250 | 0.2060 | 0.3185 | 0.2970 | 0.3600 | 0.2750 | 0.3263 | 0.3440 | 0.3395 | 0.2585 | 0.2925 | 0.2040 |
| 总铁(wt.％) | 0.900 | 1.030 | 0.980 | 0.990 | 0.960 | 1.000 | 0.870 | 0.860 | 0.970 | 0.940 | 0.900 | 1.020 |
| 模型氧化还原比 | 0.2500 | 0.2000 | 0.3250 | 0.3000 | 0.3750 | 0.2750 | 0.3750 | 0.4000 | 0.3500 | 0.2750 | 0.3250 | 0.2000 |
| Cr2O3(wt.％) | 0.0250 | 0.0240 | 0.0240 | 0.0240 | 0.0250 | 0.0240 | 0.0270 | 0.0280 | 0.0240 | 0.0250 | 0.0260 | 0.0235 |
| CoO(wt.％) | 0.0200 | 0.0170 | 0.0138 | 0.0144 | 0.0126 | 0.0150 | 0.0135 | 0.0131 | 0.0132 | 0.0155 | 0.0145 | 0.0172 |
| Se(wt.％) | 0.0017 | 0.0018 | 0.0022 | 0.0021 | 0.0023 | 0.0020 | 0.0022 | 0.0022 | 0.0022 | 0.0020 | 0.0021 | 0.0018 |
| TiO2(wt.％) | 0.2000 | 0.3000 | 0.4700 | 0.2600 | 0.3100 | 0.2600 | ||||||
| LTA(％) | 25.01 | 25.01 | 25.04 | 25.06 | 25.07 | 25.08 | 25.08 | 25.08 | 25.08 | 25.08 | 25.09 | 25.09 |
| TSUV(％) | 19.53 | 12.29 | 14.95 | 14.39 | 16.20 | 13.84 | 16.42 | 16.44 | 15.57 | 13.87 | 15.07 | 11.78 |
| TSIR(％) | 23.84 | 26.16 | 13.98 | 15.73 | 11.18 | 17.75 | 13.41 | 12.18 | 12.48 | 19.46 | 16.12 | 26.47 |
| TSET(％) | 24.95 | 25.29 | 18.67 | 19.63 | 17.11 | 20.75 | 18.38 | 17.65 | 17.85 | 21.69 | 19.87 | 25.45 |
| DW(nm) | 483.91 | 550.56 | 551.23 | 551.01 | 550.87 | 551.07 | 550.51 | 550.63 | 550.78 | 550.87 | 550.95 | 550.70 |
| Pe(％) | 11.21 | 3.69 | 3.72 | 3.71 | 3.75 | 3.75 | 3.55 | 3.88 | 3.65 | 3.67 | 3.65 | 3.94 |
表1(续)
| 例121 | 例122 | 例123 | 例124 | 例125 | 例126 | 例127 | 例128 | 例129 | 例130 | 例131 | 例132 | |
| FeO(wt.％) | 0.2183 | 0.2400 | 0.3800 | 0.2525 | 0.3115 | 0.2295 | 0.2760 | 0.2250 | 0.1750 | 0.1750 | 0.2250 | 0.4250 |
| 总铁(wt.％) | 0.970 | 0.960 | 0.950 | 1.010 | 0.890 | 1.020 | 0.920 | 0.900 | 0.700 | 0.700 | 0.900 | 1.700 |
| 模型氧化还原比 | 0.2250 | 0.2500 | 0.4000 | 0.2500 | 0.3500 | 0.2250 | 0.3000 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 |
| Cr2O3(wt.％) | 0.0230 | 0.0240 | 0.0250 | 0.0240 | 0.0270 | 0.0240 | 0.0250 | 0.0250 | 0.0210 | 0.0210 | 0.0250 | 0.0250 |
| CoO(wt.％) | 0.0167 | 0.0162 | 0.0120 | 0.0156 | 0.0140 | 0.0162 | 0.0150 | 0.0107 | 0.0070 | 0.0200 | 0.0107 | 0.0107 |
| Se(wt.％) | 0.0019 | 0.0019 | 0.0023 | 0.0020 | 0.0021 | 0.0019 | 0.0020 | 0.0039 | 0.0046 | 0.0011 | 0.0032 | 0.0017 |
| TiO2(wt.％) | 0.2300 | 0.4200 | 0.4500 | 0.4300 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | |||
| LTA(％) | 25.09 | 25.10 | 25.13 | 25.15 | 25.17 | 25.19 | 25.27 | 25.52 | 26.35 | 27.45 | 28.15 | 28.38 |
| TSUV(％) | 12.79 | 12.80 | 16.85 | 13.34 | 15.24 | 12.83 | 14.09 | 12.33 | 12.71 | 27.65 | 14.33 | 9.99 |
| TSIR(％) | 24.41 | 21.59 | 10.06 | 20.12 | 14.53 | 22.90 | 17.66 | 23.68 | 31.33 | 31.49 | 23.80 | 8.20 |
| TSET(％) | 24.40 | 22.83 | 16.50 | 22.08 | 18.99 | 23.60 | 20.77 | 23.44 | 27.77 | 31.06 | 24.75 | 16.22 |
| DW(nm) | 550.83 | 550.53 | 551.00 | 550.49 | 550.57 | 551.12 | 550.65 | 579.95 | 584.02 | 480.17 | 577.51 | 545.94 |
| Pe(％) | 3.51 | 3.84 | 3.74 | 3.71 | 3.91 | 3.80 | 3.82 | 24.29 | 37.88 | 18.25 | 18.11 | 7.52 |
表1(续)
| 例133 | 例134 | 例135 | 例136 | Ex.137 | 例138 | 例139 | 例140 | 例141 | 例142 | 例143 | 例144 | |
| FeO(wt.％) | 0.3750 | 0.4000 | 0.1750 | 0.3750 | 0.2250 | 0.3500 | 0.2250 | 0.2250 | 0.2250 | 0.3250 | 0.3600 | 0.2250 |
| 总铁(wt.％) | 1.500 | 1.600 | 0.700 | 1.500 | 0.900 | 1.400 | 0.900 | 0.900 | 0.900 | 1.300 | 0.900 | 0.900 |
| 模型氧化还原比 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.4000 | 0.2500 |
| Cr2O3(wt.％) | 0.0250 | 0.0250 | 0.0210 | 0.0250 | 0.0250 | 0.0250 | 0.0800 | 0.0250 | 0.0700 | 0.0250 | 0.0250 | 0.0600 |
| CoO(wt.％) | 0.0050 | 0.0107 | 0.0070 | 0.0107 | 0.0150 | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0107 |
| Se(wt.％) | 0.0027 | 0.0017 | 0.0039 | 0.0017 | 0.0017 | 0.0017 | 0.0017 | 0.0025 | 0.0017 | 0.0017 | 0.0017 | 0.0017 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 28.72 | 29.13 | 29.19 | 29.91 | 29.96 | 30.71 | 30.71 | 31.14 | 31.44 | 31.53 | 32.11 | 32.20 |
| TSUV(％) | 6.46 | 10.84 | 14.90 | 11.76 | 19.65 | 12.78 | 19.13 | 16.64 | 19.24 | 13.90 | 23.95 | 19.35 |
| TSIR(％) | 10.35 | 9.34 | 31.44 | 10.65 | 23.95 | 12.15 | 23.80 | 23.91 | 23.84 | 13.89 | 11.55 | 23.89 |
| TSET(％) | 16.56 | 17.23 | 29.09 | 18.35 | 26.65 | 19.59 | 25.48 | 26.29 | 25.96 | 20.97 | 20.75 | 26.46 |
| DW(nm) | 574.22 | 546.65 | 582.80 | 547.43 | 492.96 | 548.31 | 556.15 | 573.03 | 556.08 | 549.30 | 492.90 | 555.97 |
| Pe(％) | 32.55 | 7.16 | 31.42 | 6.80 | 4.27 | 6.44 | 11.87 | 11.83 | 10.56 | 6.07 | 5.63 | 9.24 |
表1(续)
| 例145 | 例146 | 例147 | 例148 | 例149 | 例150 | 例151 | 例152 | 例153 | 例154 | 例155 | 例156 | |
| FeO(wt.％) | 0.3000 | 0.1750 | 0.3375 | 0.2250 | 0.3150 | 0.1750 | 0.2750 | 0.2250 | 0.2925 | 0.2250 | 0.2700 | 0.2500 |
| 总铁(wt.％) | 1.200 | 0.700 | 0.900 | 0.900 | 0.900 | 0.700 | 1.100 | 0.900 | 0.900 | 0.900 | 0.900 | 1.000 |
| 模型氧化还原比 | 0.2500 | 0.2500 | 0.3750 | 0.2500 | 0.3500 | 0.2500 | 0.2500 | 0.2500 | 0.3250 | 0.2500 | 0.3000 | 0.2500 |
| Cr2O3(wt.％) | 0.0250 | 0.0210 | 0.0250 | 0.0500 | 0.0250 | 0.0210 | 0.0250 | 0.0250 | 0.0250 | 0.0400 | 0.0250 | 0.0250 |
| CoO(wt.％) | 0.0107 | 0.0070 | 0.0107 | 0.0107 | 0.0107 | 0.0150 | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0107 |
| Se(wt.％) | 0.0017 | 0.0032 | 0.0017 | 0.0017 | 0.0017 | 0.0011 | 0.0017 | 0.0020 | 0.0017 | 0.0017 | 0.0017 | 0.0017 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 32.37 | 32.44 | 32.57 | 32.99 | 33.05 | 33.22 | 33.24 | 33.52 | 33.54 | 33.80 | 34.03 | 34.14 |
| TSUV(％) | 15.15 | 17.46 | 23.17 | 19.46 | 22.43 | 27.83 | 16.52 | 18.52 | 21.72 | 19.57 | 21.03 | 18.05 |
| TSIR(％) | 15.90 | 31.55 | 13.01 | 23.93 | 14.68 | 31.64 | 18.23 | 24.00 | 16.58 | 23.98 | 18.74 | 20.92 |
| TSET(％) | 22.52 | 30.63 | 21.68 | 26.98 | 22.72 | 33.10 | 24.24 | 27.54 | 23.89 | 27.52 | 25.21 | 26.19 |
| DW(nm) | 550.42 | 581.19 | 495.48 | 555.80 | 499.55 | 483.52 | 551.73 | 565.70 | 507.34 | 555.55 | 524.51 | 553.17 |
| Pe(％) | 5.71 | 24.72 | 4.48 | 7.93 | 3.37 | 10.68 | 5.36 | 7.33 | 2.42 | 6.61 | 2.27 | 5.00 |
表1(续)
| 例157 | 例158 | 例159 | 例160 | 例161 | 例162 | 例163 | 例164 | 例165 | 例166 | 例167 | 例168 | |
| FeO(wt.％) | 0.2475 | 0.2250 | 0.2250 | 0.2250 | 0.2250 | 0.2250 | 0.2250 | 0.2250 | 0.3038 | 0.2050 | 0.1760 | 0.1680 |
| 总铁(wt.％) | 0.900 | 0.900 | 0.900 | 0.900 | 0.900 | 0.900 | 0.900 | 0.900 | 0.810 | 0.820 | 0.880 | 0.840 |
| 模型氧化还原比 | 0.2750 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.3750 | 0.2500 | 0.2000 | 0.2000 |
| Cr2O3(wt.％) | 0.0250 | 0.0300 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0250 | 0.0270 | 0.0250 | 0.0280 | 0.0270 |
| CoO(wt.％) | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0107 | 0.0084 | 0.0113 | 0.0119 | 0.0122 |
| Se(wt.％) | 0.0017 | 0.0017 | 0.0017 | 0.0017 | 0.0017 | 0.0017 | 0.0017 | 0.0017 | 0.0020 | 0.0017 | 0.0016 | 0.0016 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.8000 | 0.7000 | 0.6000 | 0.5000 | 0.4000 | 0.3000 | 0.2200 | 0.1500 | ||
| LTA(％) | 34.54 | 34.63 | 34.75 | 34.80 | 34.85 | 34.91 | 34.96 | 35.01 | 35.02 | 35.03 | 35.05 | 35.05 |
| TSUV(％) | 20.38 | 19.69 | 16.79 | 17.24 | 17.72 | 18.20 | 18.70 | 19.22 | 24.83 | 21.12 | 20.29 | 20.31 |
| TSIR(％) | 21.22 | 24.03 | 24.05 | 24.05 | 24.05 | 24.05 | 24.05 | 24.05 | 15.60 | 26.90 | 31.69 | 33.17 |
| TSET(％) | 26.70 | 28.08 | 27.94 | 28.01 | 28.08 | 28.15 | 28.23 | 28.30 | 23.83 | 30.05 | 32.59 | 33.42 |
| DW(nm) | 544.21 | 555.15 | 562.59 | 561.76 | 560.81 | 559.69 | 558.39 | 556.81 | 550.61 | 550.96 | 550.65 | 550.80 |
| Pe(％) | 3.34 | 5.30 | 7.81 | 7.28 | 6.76 | 6.23 | 5.70 | 5.17 | 3.72 | 3.47 | 3.73 | 3.55 |
表1(续)
| 例169 | 例170 | 例171 | 例172 | 例173 | 例174 | 例175 | 例176 | 例177 | 例178 | 例179 | 例180 | |
| FeO(wt.％) | 0.2250 | 0.2250 | 0.2250 | 0.1868 | 0.2730 | 0.2550 | 0.2150 | 0.2365 | 0.3200 | 0.2250 | 0.2870 | 0.1958 |
| 总铁(wt.％) | 0.900 | 0.900 | 0.900 | 0.830 | 0.840 | 0.850 | 0.860 | 0.860 | 0.800 | 0.900 | 0.820 | 0.870 |
| 模型氧化还原比 | 0.2500 | 0.2500 | 0.2500 | 0.2250 | 0.3250 | 0.3000 | 0.2500 | 0.2750 | 0.4000 | 0.2500 | 0.3500 | 0.2250 |
| Cr2O3(wt.％) | 0.0250 | 0.0250 | 0.0250 | 0.0270 | 0.0280 | 0.0280 | 0.0280 | 0.0280 | 0.0270 | 0.0250 | 0.0270 | 0.0280 |
| CoO(wt.％) | 0.0107 | 0.0107 | 0.0107 | 0.0118 | 0.0092 | 0.0097 | 0.0108 | 0.0102 | 0.0079 | 0.0107 | 0.0088 | 0.0113 |
| Se(wt.％) | 0.0017 | 0.0017 | 0.0017 | 0.0016 | 0.0019 | 0.0018 | 0.0017 | 0.0018 | 0.0020 | 0.0017 | 0.0019 | 0.0017 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.3200 | 0.1000 | |||||||
| LTA(％) | 35.06 | 35.06 | 35.06 | 35.08 | 35.09 | 35.09 | 35.10 | 35.11 | 35.11 | 35.11 | 35.12 | 35.13 |
| TSUV(％) | 19.75 | 19.75 | 19.75 | 20.17 | 23.31 | 22.65 | 21.54 | 21.99 | 25.59 | 20.29 | 24.15 | 20.91 |
| TSIR(％) | 24.05 | 24.05 | 24.05 | 29.82 | 18.43 | 20.35 | 25.42 | 22.54 | 14.29 | 24.05 | 17.08 | 28.33 |
| TSET(％) | 28.37 | 28.37 | 28.37 | 31.58 | 25.39 | 26.45 | 29.23 | 27.65 | 23.15 | 28.45 | 24.69 | 30.81 |
| DW(nm) | 554.86 | 554.86 | 554.86 | 550.80 | 550.76 | 550.70 | 550.37 | 550.89 | 550.75 | 552.42 | 551.11 | 550.97 |
| Pe(％) | 4.64 | 4.64 | 4.64 | 3.81 | 3.93 | 3.91 | 3.76 | 3.92 | 3.76 | 4.11 | 3.79 | 3.81 |
表1(续)
| 例181 | 例182 | 例183 | 例184 | 例185 | 例186 | 例187 | 例188 | 例189 | 例190 | 例192 | 例192 | |
| FeO(wt.％) | 0.2228 | 0.2250 | 0.2730 | 0.2568 | 0.2888 | 0.2430 | 0.3040 | 0.2250 | 0.2025 | 0.2250 | 0.1800 | 0.2250 |
| 总铁(wt.％) | 0.810 | 0.900 | 0.780 | 0.790 | 0.770 | 0.810 | 0.760 | 0.900 | 0.900 | 0.900 | 0.900 | 0.900 |
| 模型氧化还原比 | 0.2750 | 0.2500 | 0.3500 | 0.3250 | 0.3750 | 0.3000 | 0.4000 | 0.2500 | 0.2250 | 0.2500 | 0.2000 | 0.2500 |
| Cr2O3(wt.％) | 0.0260 | 0.0250 | 0.0260 | 0.0265 | 0.0260 | 0.0250 | 0.0255 | 0.0200 | 0.0250 | 0.0250 | 0.0250 | 0.0250 |
| CoO(wt.％) | 0.0108 | 0.0107 | 0.0095 | 0.0098 | 0.0089 | 0.0104 | 0.0086 | 0.0107 | 0.0107 | 0.0100 | 0.0107 | 0.0107 |
| Se(wt.％) | 0.0017 | 0.0017 | 0.0018 | 0.0018 | 0.0019 | 0.0017 | 0.0019 | 0.0017 | 0.0017 | 0.0017 | 0.0017 | 0.0015 |
| TiO2(wt.％) | 0.3200 | 0.0200 | 0.4600 | 0.2900 | 0.2700 | 0.4900 | 0.4200 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 35.15 | 35.15 | 35.16 | 35.17 | 35.18 | 35.20 | 35.21 | 35.50 | 35.59 | 35.97 | 36.14 | 36.14 |
| TSUV(％) | 21.34 | 20.74 | 22.52 | 22.73 | 24.12 | 20.99 | 24.01 | 19.80 | 19.14 | 19.76 | 18.55 | 20.61 |
| TSIR(％) | 24.35 | 24.05 | 18.45 | 20.16 | 16.93 | 21.77 | 15.59 | 24.07 | 27.29 | 24.06 | 31.00 | 24.08 |
| TSET(％) | 28.67 | 28.51 | 25.41 | 26.39 | 24.63 | 27.24 | 23.87 | 28.67 | 30.27 | 28.68 | 32.42 | 28.96 |
| DW(nm) | 550.59 | 549.96 | 550.81 | 550.78 | 550.91 | 550.73 | 550.79 | 554.47 | 560.86 | 559.34 | 564.72 | 537.17 |
| Pe(％) | 3.72 | 3.69 | 3.98 | 3.79 | 3.73 | 3.96 | 3.87 | 3.99 | 5.98 | 5.81 | 7.33 | 2.96 |
表1(续)
| 例193 | 例194 | 例195 | 例196 | 例197 | 例198 | 例199 | 例200 | 例201 | 例202 | 例203 | 例204 | |
| FeO(wt.％) | 0.1750 | 0.2250 | 0.2250 | 0.3500 | 0.3250 | 0.1750 | 0.1750 | 0.3000 | 0.1750 | 0.2250 | 0.1750 | 0.2750 |
| 总铁(wt.％) | 0.700 | 0.900 | 0.900 | 1.400 | 1.300 | 0.700 | 0.700 | 1.200 | 0.700 | 0.900 | 0.700 | 1.100 |
| 模型氧化还原比 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 | 0.2500 |
| Cr2O3(wt.％) | 0.0210 | 0.0100 | 0.0005 | 0.0210 | 0.0210 | 0.0210 | 0.0800 | 0.0210 | 0.0700 | 0.0250 | 0.0210 | 0.0210 |
| CoO(wt.％) | 0.0070 | 0.0107 | 0.0107 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0107 | 0.0100 | 0.0070 |
| Se(wt.％) | 0.0025 | 0.0017 | 0.0017 | 0.0011 | 0.0011 | 0.0020 | 0.0011 | 0.0011 | 0.0011 | 0.0008 | 0.0011 | 0.0011 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 36.15 | 36.39 | 37.27 | 37.74 | 38.74 | 39.14 | 39.29 | 39.76 | 40.23 | 40.24 | 40.32 | 40.81 |
| TSUV(％) | 20.46 | 19.92 | 20.03 | 15.66 | 16.96 | 22.92 | 27.23 | 18.38 | 27.37 | 23.94 | 28.00 | 19.95 |
| TSIR(％) | 31.66 | 24.12 | 24.16 | 12.05 | 13.79 | 31.74 | 31.55 | 15.80 | 31.61 | 24.20 | 31.79 | 18.13 |
| TSET(％) | 32.46 | 29.28 | 29.89 | 22.48 | 23.95 | 33.97 | 33.23 | 25.58 | 33.85 | 31.25 | 35.55 | 27.40 |
| DW(nm) | 578.76 | 553.07 | 549.31 | 541.05 | 542.27 | 575.77 | 555.78 | 543.64 | 555.68 | 494.01 | 494.99 | 545.18 |
| Pe(％) | 17.83 | 2.68 | 1.44 | 5.63 | 5.36 | 12.83 | 11.51 | 5.09 | 10.21 | 6.17 | 3.20 | 4.83 |
表1(续)
| 例205 | 例206 | 例207 | 例208 | 例209 | 例210 | 例211 | 例212 | 例213 | 例214 | 例215 | 例216 | |
| FeO(wt.％) | 0.1750 | 0.2500 | 0.1750 | 0.2800 | 0.1750 | 0.2625 | 0.2250 | 0.2450 | 0.1750 | 0.2250 | 0.2275 | 0.2000 |
| 总铁(wt.％) | 0.700 | 1.000 | 0.700 | 0.700 | 0.700 | 0.700 | 0.900 | 0.700 | 0.700 | 0.900 | 0.700 | 0.800 |
| 模型氧化还原此 | 0.2500 | 0.2500 | 0.2500 | 0.4000 | 0.2500 | 0.3750 | 0.2500 | 0.3500 | 0.2500 | 0.2500 | 0.3250 | 0.2500 |
| Cr2O3(wt.％) | 0.0600 | 0.0210 | 0.0500 | 0.0210 | 0.0210 | 0.0210 | 0.0210 | 0.0210 | 0.0400 | 0.0250 | 0.0210 | 0.0210 |
| CoO(wt.％) | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0050 | 0.0070 | 0.0070 |
| Se(wt.％) | 0.0011 | 0.0011 | 0.0011 | 0.0011 | 0.0015 | 0.0011 | 0.0011 | 0.0011 | 0.0011 | 0.0017 | 0.0011 | 0.0011 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 41.21 | 41.90 | 42.22 | 42.25 | 42.45 | 42.74 | 43.01 | 43.24 | 43.27 | 43.29 | 43.76 | 44.16 |
| TSUV(％) | 27.52 | 21.68 | 27.67 | 32.61 | 25.67 | 31.79 | 23.59 | 31.01 | 27.82 | 19.88 | 30.25 | 25.73 |
| TSIR(％) | 31.66 | 20.83 | 31.72 | 17.65 | 31.82 | 19.44 | 23.97 | 21.44 | 31.78 | 24.18 | 23.65 | 27.63 |
| TSET(％) | 34.49 | 29.44 | 35.15 | 28.68 | 35.70 | 29.79 | 31.73 | 31.01 | 35.85 | 31.10 | 32.35 | 34.32 |
| DW(nm) | 555.53 | 546.93 | 555.32 | 494.20 | 569.54 | 496.90 | 548.91 | 501.21 | 555.00 | 570.22 | 509.20 | 551.16 |
| Pe(％) | 8.90 | 4.57 | 7.59 | 4.43 | 7.81 | 3.54 | 4.31 | 2.70 | 6.29 | 14.10 | 2.01 | 4.06 |
表1(续)
| 例217 | 例218 | 例219 | 例220 | 例221 | 例222 | 例223 | 例224 | 例225 | 例226 | 例227 | 例228 | |
| FeO(wt.％) | 0.2100 | 0.1750 | 0.1925 | 0.1750 | 0.1750 | 0.2210 | 0.1440 | 0.2600 | 0.2380 | 0.2100 | 0.2345 | 0.1460 |
| 总铁(wt.％) | 0.700 | 0.700 | 0.700 | 0.700 | 0.700 | 0.680 | 0.720 | 0.650 | 0.680 | 0.700 | 0.670 | 0.730 |
| 模型氧化还原比 | 0.3000 | 0.2500 | 0.2750 | 0.2500 | 0.2500 | 0.3250 | 0.2000 | 0.4000 | 0.3500 | 0.3000 | 0.3500 | 0.2000 |
| Cr2O3(wt.％) | 0.0210 | 0.0300 | 0.0210 | 0.0210 | 0.0210 | 0.0210 | 0.0240 | 0.0250 | 0.0250 | 0.0255 | 0.0215 | 0.0245 |
| CoO(wt.％) | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0060 | 0.0079 | 0.0047 | 0.0053 | 0.0060 | 0.0057 | 0.0077 |
| Se(wt.％) | 0.0011 | 0.0011 | 0.0011 | 0.0011 | 0.0011 | 0.0012 | 0.0010 | 0.0013 | 0.0013 | 0.0012 | 0.0012 | 0.0010 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.8000 | 0.7000 | 0.2000 | 0.2000 | 0.3000 | ||||
| LTA(％) | 44.28 | 44.35 | 44.81 | 44.95 | 45.01 | 45.03 | 45.04 | 45.05 | 45.06 | 45.07 | 45.07 | 45.07 |
| TSUV(％) | 29.51 | 27.97 | 28.80 | 23.80 | 24.47 | 30.09 | 26.82 | 34.11 | 32.22 | 30.62 | 30.22 | 27.82 |
| TSIR(％) | 26.11 | 31.83 | 28.84 | 31.89 | 31.89 | 24.54 | 38.12 | 19.73 | 22.30 | 26.10 | 22.75 | 37.68 |
| TSET(％) | 33.83 | 36.57 | 35.46 | 36.68 | 36.77 | 33.15 | 40.43 | 30.51 | 31.90 | 33.96 | 32.14 | 40.25 |
| DW(nm) | 525.66 | 554.49 | 543.44 | 562.94 | 562.02 | 550.93 | 551.27 | 550.47 | 550.26 | 550.86 | 550.56 | 550.90 |
| Pe(％) | 2.00 | 4.99 | 2.82 | 6.99 | 6.46 | 3.55 | 3.78 | 3.71 | 3.76 | 3.87 | 3.72 | 3.59 |
表1(续)
| 例229 | 例230 | 例231 | 例232 | 例233 | 例234 | 例235 | 例236 | 例237 | 例238 | 例239 | 例240 | |
| FeO(wt.％) | 0.1953 | 0.1750 | 0.1725 | 0.2513 | 0.1800 | 0.1750 | 0.2243 | 0.1643 | 0.1750 | 0.2475 | 0.2560 | 0.1750 |
| 总铁(wt.％) | 0.710 | 0.700 | 0.690 | 0.670 | 0.720 | 0.700 | 0.690 | 0.730 | 0.700 | 0.660 | 0.640 | 0.700 |
| 模型氧化还原比 | 0.2750 | 0.2500 | 0.2500 | 0.3750 | 0.2500 | 0.2500 | 0.3250 | 0.2250 | 0.2500 | 0.3750 | 0.4000 | 0.2500 |
| Cr2O3(wt.％) | 0.0255 | 0.0210 | 0.0230 | 0.0255 | 0.0245 | 0.0210 | 0.0255 | 0.0245 | 0.0210 | 0.0210 | 0.0215 | 0.0210 |
| CoO(wt.％) | 0.0064 | 0.0070 | 0.0070 | 0.0049 | 0.0068 | 0.0070 | 0.0056 | 0.0072 | 0.0070 | 0.0054 | 0.0052 | 0.0070 |
| Se(wt.％) | 0.0011 | 0.0011 | 0.0011 | 0.0013 | 0.0011 | 0.0011 | 0.0012 | 0.0011 | 0.0011 | 0.0012 | 0.0012 | 0.0011 |
| TiO2(wt.％) | 0.6000 | 0.1500 | 0.5000 | 0.4000 | 0.4200 | 0.5200 | 0.3000 | |||||
| LTA(％) | 45.07 | 45.08 | 45.10 | 45.12 | 45.13 | 45.15 | 45.15 | 45.17 | 45.21 | 45.22 | 45.27 | 45.28 |
| TSUV(％) | 29.87 | 25.16 | 28.73 | 33.06 | 29.08 | 25.86 | 31.45 | 28.35 | 26.59 | 30.17 | 30.49 | 27.34 |
| TSIR(％) | 28.38 | 31.89 | 32.33 | 20.71 | 30.96 | 31.89 | 24.08 | 33.90 | 31.89 | 21.16 | 20.19 | 31.89 |
| TSET(％) | 35.20 | 36.86 | 37.40 | 31.04 | 36.65 | 36.96 | 32.90 | 38.24 | 37.05 | 31.29 | 30.75 | 37.15 |
| DW(nm) | 550.41 | 560.95 | 551.62 | 550.70 | 550.88 | 559.66 | 550.68 | 550.94 | 558.12 | 550.89 | 550.76 | 556.18 |
| Pe(％) | 3.79 | 5.93 | 3.61 | 3.88 | 3.72 | 5.40 | 3.87 | 3.71 | 4.87 | 3.90 | 4.01 | 4.35 |
表1(续)
| 例241 | 例242 | 例243 | 例244 | 例245 | 例246 | 例247 | 例248 | 例249 | 例250 | 例251 | 例252 | |
| FeO(wt.％) | 0.1925 | 0.2070 | 0.1750 | 0.1750 | 0.1750 | 0.1620 | 0.1750 | 0.1750 | 0.1750 | 0.1575 | 0.1400 | 0.1500 |
| 总铁(wt.％) | 0.700 | 0.690 | 0.700 | 0.700 | 0.700 | 0.720 | 0.700 | 0.700 | 0.700 | 0.700 | 0.700 | 0.600 |
| 模型氧化还原比 | 0.2750 | 0.3000 | 0.2500 | 0.2500 | 0.2500 | 0.2250 | 0.2500 | 0.2500 | 0.2500 | 0.2250 | 0.2000 | 0.2500 |
| Cr2O3(wt.％) | 0.0230 | 0.0210 | 0.0210 | 0.0210 | 0.0210 | 0.0220 | 0.0210 | 0.0200 | 0.0210 | 0.0210 | 0.0210 | 0.0210 |
| CoO(wt.％) | 0.0066 | 0.0064 | 0.0070 | 0.0070 | 0.0070 | 0.0075 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 | 0.0070 |
| Se(wt.％) | 0.0011 | 0.0011 | 0.0011 | 0.0011 | 0.0011 | 0.0010 | 0.0011 | 0.0011 | 0.0011 | 0.0011 | 0.0011 | 0.0011 |
| TiO2(wt.％) | 0.2000 | 0.3800 | 0.2000 | 0.2000 | 0.2000 | 0.3000 | 0.1000 | 0.2000 | 0.0200 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 45.29 | 45.35 | 45.35 | 45.35 | 45.35 | 45.35 | 45.42 | 45.46 | 45.47 | 45.90 | 46.46 | 46.57 |
| TSUV(％) | 28.78 | 28.32 | 28.11 | 28.11 | 28.11 | 26.77 | 28.90 | 28.12 | 29.56 | 27.44 | 26.79 | 30.79 |
| TSIR(％) | 28.84 | 26.57 | 31.89 | 31.89 | 31.89 | 34.36 | 31.89 | 31.89 | 31.89 | 35.28 | 39.06 | 36.86 |
| TSET(％) | 35.54 | 34.31 | 37.25 | 37.25 | 37.25 | 38.55 | 37.35 | 37.33 | 37.43 | 39.23 | 41.41 | 40.58 |
| DW(nm) | 550.70 | 550.64 | 553.71 | 553.71 | 553.71 | 550.30 | 550.44 | 553.59 | 546.98 | 559.73 | 563.70 | 556.63 |
| Pe(％) | 3.77 | 3.80 | 3.82 | 3.82 | 3.82 | 3.71 | 3.29 | 3.69 | 2.87 | 4.84 | 5.88 | 3.57 |
表1(续)
| 例253 | 例254 | 例255 | 例256 | |
| FeO(wt.％) | 0.1750 | 0.1750 | 0.1750 | 0.1750 |
| 总铁(wt.％) | 0.700 | 0.700 | 0.700 | 0.700 |
| 模型氧化还原比 | 0.2500 | 0.2500 | 0.2500 | 0.2500 |
| Cr2O3(wt.％) | 0.0100 | 0.0210 | 0.0005 | 0.0210 |
| CoO(wt.％) | 0.0070 | 0.0070 | 0.0070 | 0.0050 |
| Se(wt.％) | 0.0011 | 0.0008 | 0.0011 | 0.0011 |
| TiO2(wt.％) | 0.2000 | 0.2000 | 0.2000 | 0.2000 |
| LTA(％) | 46.61 | 47.69 | 47.75 | 49.07 |
| TSUV(％) | 28.28 | 30.09 | 28.43 | 28.18 |
| TSIR(％) | 31.95 | 31.93 | 32.01 | 31.95 |
| TSET(％) | 38.11 | 38.53 | 38.89 | 38.50 |
| DW(nm) | 551.69 | 509.82 | 545.77 | 565.18 |
| Pe(％) | 2.39 | 2.14 | 1.16 | 7.39 |
表2
| 例257 | 例258 | 例259 | 例260 | 例261 | 例262 | 例263 | 例264 | 例265 | |
| FeO(wt.％) | 0.3232 | 0.2980 | 0.3080 | 0.2980 | 0.3500 | 0.2890 | 0.3500 | 0.3500 | 0.3080 |
| 总铁(wt.％) | 1.103 | 1.103 | 1.100 | 1.103 | 1.083 | 1.070 | 1.083 | 1.083 | 1.100 |
| 模型氧化还原比 | 0.2929 | 0.2702 | 0.2800 | 0.2702 | 0.3232 | 0.2701 | 0.3232 | 0.3232 | 0.2800 |
| Cr2O3(wt.％) | 0.0302 | 0.0302 | 0.0302 | 0.0302 | 0.0293 | 0.0302 | 0.0293 | 0.0293 | 0.0302 |
| CoO(wt.％) | 0.0128 | 0.0125 | 0.0128 | 0.0119 | 0.0110 | 0.0119 | 0.0100 | 0.0090 | 0.0100 |
| Se(wt.％) | 0.0010 | 0.0010 | 0.0010 | 0.0009 | 0.0010 | 0.0009 | 0.0010 | 0.0010 | 0.0010 |
| TiO2(wt.％) | 0.1940 | 0.1940 | 0.1940 | 0.1940 | 0.3510 | 0.1940 | 0.3510 | 0.3510 | 0.1940 |
| LTA(％) | 31.13 | 31.95 | 32.59 | 33.18 | 33.47 | 33.52 | 34.63 | 35.84 | 35.87 |
| TSUV(％) | 16.53 | 15.93 | 20.62 | 16.28 | 19.74 | 16.79 | 19.76 | 19.78 | 20.69 |
| TSIR(％) | 12.31 | 14.26 | 13.45 | 14.27 | 10.54 | 15.05 | 10.54 | 10.55 | 13.47 |
| TSET(％) | 21.38 | 22.72 | 22.93 | 23.23 | 21.37 | 23.84 | 21.74 | 22.12 | 23.98 |
| DW(nm) | 497.4 | 502.2 | 493.5 | 502.5 | 497.8 | 502.1 | 502.2 | 509.2 | 505.2 |
| Pe(％) | 6.57 | 5.03 | 6.86 | 5.14 | 5.59 | 5.1 | 4.52 | 3.69 | 3.75 |
表3
| 例266 | 例267 | 例268 | 例269 | |
| FeO(wt.％) | 0.3060 | 0.3080 | 0.3400 | 0.3500 |
| 总铁(wt.％) | 1.099 | 1.103 | 1.101 | 1.110 |
| 模型氧化还原比 | 0.2790 | 0.2800 | 0.3100 | 0.3160 |
| Cr2O3(wt.％) | 0.0286 | 0.0302 | 0.0288 | 0.0323 |
| CoO(wt.％) | 0.0128 | 0.0128 | 0.0129 | 0.0129 |
| Se(wt.％) | 0.0012 | 0.0010 | 0.0008 | 0.0007 |
| TiO2(wt.％) | 0.3550 | 0.1940 | 0.3500 | 0.1940 |
| LTA(％) | 28.33 | 29.47 | 29.91 | 30.25 |
| TSUV(％) | 14.14 | 15.72 | 16.28 | 19.16 |
| TSIR(％) | 12.99 | 12.72 | 10.44 | 9.31 |
| TSET(％) | 19.56 | 20.12 | 19.13 | 18.93 |
| DW(nm) | 509.2 | 497.2 | 494.2 | 491.1 |
| Pe(％) | 4.06 | 5.59 | 8.89 | 11.88 |
参见表1、2和3，本发明提供了一种绿色玻璃，它采用标准的钠-钙-硅玻璃基础组分和另外的铁、钴、硒和铬以及另选的钛作为红外或紫外吸收物质及着色剂。可以看出，不是所有的实施例均具有相同的颜色，正如由主波长(DW)和色纯度(Pe)所表示的。在本发明中，优选地该玻璃具有主波长为约480-565纳米，优选地为约495-560纳米、色纯度不超过约20％，优选地不超过约10％，更优选地不超过约7％的颜色。可以预见该玻璃的颜色可以在该主波长范围内变化以提供所需的产品。举例来说，可以在主波长为约485-515纳米，优选地约490-510纳米、色纯度不超过10％，优选地不超过7％的情况下制造一种兰绿色玻璃，也可以在主波长为约535-565纳米，优选地约540-560纳米、色纯度不超过10％，优选地不超过5％的情况下制造一种黄绿色玻璃。
本发明中所说的绿色红外和紫外吸收玻璃具有不超过60％的透光性(LTA)。在本发明的一个特定的方案中，该玻璃含有约0.6-4％重量总铁、约0.13-0.9％重量FeO、约40-500PPMCoO、约5-70PPMSe、约15-800PPMCr2O3和0.02-约1％重量TiO2。在本发明的另一个特定的方案中，该玻璃含有约1-1.4％重量以下总铁、约0.2-0.60％重量FeO、超过200-约500PPMCoO、约5-70PPMSe、大于200-约800PPMCr2O3和0-约1％重量TiO2。这些玻璃的氧化还原比保持在约0.20-0.40，优选地在约0.22-0.35、更优选地为约0.23--0.28之间这些玻璃组合物还具有不超过约40％，优选地不超过约35％的TSUV、不超过约45％，优选地不超过约40％的TSIR以及不超过约50％，优选地不超过约45％的TSET。
本发明的玻璃组合物可以具有不同的光学性能，取决于特定的用途和所需的透光性。在本发明的一个实施方案中，对于在厚度至少为1.8-5.0毫米下LTA低于20％的绿色红外和紫外吸收玻璃来说，该玻璃组合物含有约1-1.4％重量以下总铁、约0.22-0.5％重量FeO，优选地为约0.3-0.5％重量、超过200-约450PPMCoO，优选地为超过200-约350PPM、约10-60PPMSe，优选地为约35-50PPM、约250-400PPMCr2O3，优选地为约250-350PPM和0-约1％重量TiO2，优选地为约0.02-0.5％重量。在该透光范围内的玻璃组合物具有不超过约30％的TSUV，优选地不超过约12％、不超过约35％的TSIR，优选地为不超过约20％、以及不超过约30％的TSET，优选地为不超过约20％的TSET。
在本发明的另一个实施方案中，对于在厚度至少为1.8-5.0毫米下LTA低于20-60％的绿色红外和紫外吸收玻璃来说，该玻璃组合物含有约1-低于1.4％重量总铁、约0.25-0.4％重量FeO，超过200-约250PPMCoO，约10-30PPMSe，大于200-约250PPMCr2O3，和0.02-0.5％重量TiO2。在该透光范围内的玻璃组合物具有不超过约35％的TSUV，优选地不超过约20％、不超过约40％的TSIR，优选地为不超过约15％、以及不超过约45％的TSET，优选地为不超过约25％。
在本发明的另一个实施方案中，对于在参考厚度为4.06毫米下LTA为20-60％的绿色红外和紫外吸收玻璃来说，该玻璃组合物含有大于0.7-约2％重量总铁，优选地约0.8-1.5％重量、约0.13-0.6％重量FeO，优选地为约0.14-0.43％重量、超过200-约300PPMCoO，优选地为超过200-约250PPM、约5-70PPMSe，优选地为约8-60PPM、超过200-约300PPMCr2O3，优选地为超过200-约250PPM和0-约1％重量TiO2，优选地为约0.02-0.5％重量。在该透光范围内的玻璃组合物具有不超过约35％的TSUV，不超过约40％的TSIR，以及不超过约45％的TSET。
在本发明的另一个实施方案中，该绿色红外和紫外吸收玻璃组合物含有0.9-1.3％重量总铁，优选地1.083-1.11％重量、0.25-0.40％重量FeO，优选地为0.306-0.35％重量、80-130PPMCoO，优选地为90-128PPM、8-15PPMSe，优选地为10-12PPM、250-350PPMCr2O3，优选地为286-302PPM和0.1-0.5％重量TiO2，优选地为0.194-0.355％重量。这些玻璃具有25-40％的透光性(LTA)、约25％或更低的总太阳紫外透过性(TSUV)，约20％或更低的总太阳红外透过性(TSIR)，以及约30％或更低的总太阳能透过性(TSET)。
可以预见本发明中所说的玻璃组合物的光学性能在将玻璃钢化或向紫外辐射长时间暴露(通常称为太阳化)以后将会发生变化。更进一步地说，可以认为本发明中所说的玻璃组合物的钢化和太阳化会增加LTA、降低TSUV、TSIR和TSET。结果，在本发明的一个实施方案中，玻璃组合物会具有开始时落在上述范围以外而在钢化和/或太阳化以后落在上述范围以内的光学性能。
通过浮法工艺制成的玻璃一般其板厚度为约1毫米-10毫米。用于车辆窗中时，优选地具有上述组合物和光学性能的玻璃板其厚度为0.071-0.197英寸(1.8-5毫米)。可以预见当采用单块玻璃板时可以将该玻璃钢化，例如用于车辆侧窗或后窗，而当采用多块玻璃时，可以将该玻璃退火并采用热塑性粘结剂，如聚乙烯醇缩丁醛进行夹层。
可以设想用钒来部分或全部取代本发明和玻璃组合物中的铬。更进一步地说，在本文中用V2O5表示的钒使该玻璃呈黄绿色并且在不同价态下吸收紫外和红外辐射。可以相信上述在约25-800PPM范围内的Cr2O3可以完全被约0.01-0.32％重量的V2O5取代。
如前所说，可以将其它物质加入到本发明所说的玻璃组合物中以进一步降低紫外和红外辐射透过性和/或控制玻璃颜色。更进一步地说，可以设想将下列物质加入到本发明所说的含有铁、钴、硒、铬和钛的钠-钙-硅玻璃中：MnO2 0-0.5重量％SnO2 0-2重量％ZnO 0-0.5重量％Mo 0-0.015重量％CeO2 0-2重量％NiO 0-0.1重量％应当明白，考虑到这些外加物质的着色和/或氧化还原影响能力，可以对基础的铁、钴、硒、铬和/或钛组分进行调整。
对于熟悉本领域的人员来说是已知的其它变化应被认为没有脱离本发明如后面权利要求书所限定的范围。
Claims (50)
1.一种绿色红外和紫外辐射吸收玻璃制品，该玻璃制品具有由下列基础玻璃部分和下列太阳辐射吸收及着色部分组成的组合物：
其中基础玻璃部分包括：
重量％
SiO2 66-75
Na2O 10-20
CaO 5-15
MgO 0-5
Al2O3 0-5
K2O 0-5
太阳辐射吸收及着色部分基本由下列成分组成：
总铁 约0.60-4％重量
FeO 约0.13-0.9％重量
CoO 约40-500PPM
Se 约5-70PPM
Cr2O3 约15-800PPM
TiO2 约0.02-1％重量该玻璃的透光性(LTA)为不超过约60％。
2.权利要求1所说的制品，其中该玻璃的氧化还原比为约0.2-0.4。
3.权利要求1所说的制品，其中该玻璃具有约40％或更低的总太阳紫外透过性(TSUV)，约45％或更低的总太阳红外透过性(TSIR)，以及约50％或更低的总太阳能透过性(TSET)。
4.权利要求3所说的制品，其中该玻璃具有约35％或更低的总太阳紫外透过性(TSUV)，约40％或更低的总太阳红外透过性(TSIR)，以及约45％或更低的总太阳能透过性(TSET)。
5.权利要求1所说的制品，其中该玻璃的颜色特征为主波长约为480-565纳米，色纯度为不高于约20％。
6.权利要求5所说的制品，其中该玻璃的颜色特征为主波长约为485-515纳米，色纯度为不高于约10％。
7.权利要求6所说的制品，其中该玻璃的颜色特征为主波长约为490-510纳米，色纯度为不高于约7％。
8.权利要求5所说的制品，其中该玻璃的颜色特征为主波长约为535-565纳米，色纯度为不高于约10％。
9.权利要求8所说的制品，其中该玻璃的颜色特征为主波长约为540-560纳米，色纯度为不高于约5％。
10.权利要求1所说的制品，其中该玻璃在厚度至少为1.8-5.0毫米下具有低于20％的透光性。
11.权利要求1所说的制品，其中该玻璃在厚度至少为1.8-5.0毫米下具有20-60％的透光性。
12.权利要求1所说的制品，它包括平板玻璃板。
13.权利要求12所说的制品，其中所说的板在表面部分含有微量氧化锡。
14.一种绿色红外和紫外辐射吸收玻璃制品，该玻璃制品具有由下列基础玻璃部分和下列太阳辐射吸收及着色部分组成的组合物：
其中基础玻璃部分包括：
重量％
SiO2 66-75
Na2O 10-20
CaO 5-15
MgO 0-5
Al2O3 0-5
K2O 0-5
太阳辐射吸收及着色部分基本由下列成分组成：
总铁 1-低于约1.4％重量
FeO 约0.2-0.6％重量
CoO 高于200-约500PPM
Se 约5-70PPM
Cr2O3 高于200-约800PPM
TiO2 0-约1％重量该玻璃的透光性(LTA)为不超过约60％。
15.权利要求14所说的制品，其中该玻璃的氧化还原比为约0.2-0.4。
16.权利要求14所说的制品，其中该玻璃具有约40％或更低的总太阳紫外透过性(TSUV)，约45％或更低的总太阳红外透过性(TSIR)，以及约50％或更低的总太阳能透过性(TSET)。
17.权利要求16所说的制品，其中该玻璃具有约35％或更低的总太阳紫外透过性(TSUV)，约40％或更低的总太阳红外透过性(TSIR)，以及约45％或更低的总太阳能透过性(TSET)。
18.权利要求14所说的制品，其中该玻璃的颜色特征为主波长约为480-565纳米，色纯度为不高于约20％。
19.权利要求18所说的制品，其中该玻璃的颜色特征为主波长约为485-515纳米，色纯度为不高于约10％。
20.权利要求19所说的制品，其中该玻璃的颜色特征为主波长约为490-510纳米，色纯度为不高于约7％。
21.权利要求18所说的制品，其中该玻璃的颜色特征为主波长约为535-565纳米，色纯度为不高于约10％。
22.权利要求21所说的制品，其中该玻璃的颜色特征为主波长约为540-560纳米，色纯度为不高于约5％。
23.权利要求14所说的制品，其中该玻璃在厚度至少为1.8-5.0毫米下具有低于20％的透光性。
24.权利要求23所说的制品，其中FeO的浓度为约0.22-0.5％重量、CoO的浓度为多于200-约450PPM、Se的浓度为约10-60PPM、Cr2O3的浓度为约250-400PPM和TiO2的浓度为约0.02-0.5％重量。
25.权利要求24所说的制品，其中FeO的浓度为约0.3-0.5％重量、CoO的浓度为多于200-约350PPM、Se的浓度为约35-50PPM、Cr2O3的浓度为约250-350PPM。
26.权利要求24所说的制品，其中该玻璃具有约30％或更低的总太阳紫外透过性(TSUV)，约35％或更低的总太阳红外透过性(TSIR)，以及约30％或更低的总太阳能透过性(TSET)。
27.权利要求26所说的制品，其中该玻璃具有约12％或更低的总太阳紫外透过性(TSUV)，约20％或更低的总太阳红外透过性(TSIR)，以及约20％或更低的总太阳能透过性(TSET)。
28.权利要求24所说的制品，其中该玻璃的颜色特征为主波长约为480-565纳米，色纯度为不高于约20％。
29.权利要求28所说的制品，其中该玻璃的颜色特征为主波长约为540-560纳米，色纯度为不高于约5％。
30.权利要求14所说的制品，其中该玻璃在厚度至少为1.8-5.0毫米下具有20-60％的透光性。
31.权利要求30所说的制品，其中FeO的浓度为约0.25-0.4％重量、CoO的浓度为多于200-约250PPM、Se的浓度为约10-30PPM、Cr2O3的浓度为约高于200-250PPM和TiO2的浓度为约0.02-0.5％重量。
32.权利要求31所说的制品，其中该玻璃具有约35％或更低的总太阳紫外透过性(TSUV)，约40％或更低的总太阳红外透过性(TSIR)，以及约45％或更低的总太阳能透过性(TSET)。
33.权利要求32所说的制品，其中该玻璃具有约20％或更低的总太阳紫外透过性(TSUV)，约15％或更低的总太阳红外透过性(TSIR)，以及约25％或更低的总太阳能透过性(TSET)。
34.权利要求31所说的制品，其中该玻璃的颜色特征为主波长约为480-565纳米，色纯度为不高于约20％。
35.权利要求34所说的制品，其中该玻璃的颜色特征为主波长约为490-510纳米，色纯度为不高于约7％。
36.权利要求14所说的制品，它包括平板玻璃板。
37.权利要求36所说的制品，其中所说的板在表面部分含有微量氧化锡。
38.一种绿色红外和紫外辐射吸收玻璃制品，该玻璃制品具有由下列基础玻璃部分和下列太阳辐射吸收及着色部分组成的组合物：
其中基础玻璃部分包括：
重量％
SiO2 66-75
Na2O 10-20
CaO 5-15
MgO 0-5
Al2O3 0-5
K2O 0-5
太阳辐射吸收及着色部分基本由下列成分组成：
总铁 高于0.7-约2％重量
FeO 约0.13-0.6％重量
CoO 高于200-约300PPM
Se 约5-70PPM
Cr2O3 高于200-约300PPM
TiO2 0-约1％重量在参考厚度为4.06毫米下，该玻璃的透光性(LTA)为20-60％。
39.权利要求38所说的制品，其中总铁的浓度为约0.8-1.5％重量、FeO的浓度为约0.14-0.43％重量、CoO的浓度为多于200-约250PPM、Se的浓度为约8-60PPM、Cr2O3的浓度为约高于200-250PPM和TiO2的浓度为约0.02-0.5％重量。
40.权利要求38所说的制品，其中该玻璃具有约35％或更低的总太阳紫外透过性(TSUV)，约40％或更低的总太阳红外透过性(TSIR)，以及约45％或更低的总太阳能透过性(TSET)。
41.权利要求38所说的制品，其中该玻璃的颜色特征为主波长约为480-565纳米，色纯度为不高于约20％。
42.权利要求41所说的制品，其中该玻璃的颜色特征为主波长约为490-510纳米，色纯度为不高于约7％。
43.权利要求38的制品，其中该玻璃的氧化还原比为约0.2-0.4。
44.权利要求38所说的制品，它包括平板玻璃板。
45.权利要求44所说的制品，其中所说的板在表面部分含有微量氧化锡。
46.一种绿色红外和紫外辐射吸收玻璃制品，该玻璃制品具有由下列基础玻璃部分和下列太阳辐射吸收及着色部分组成的组合物：
其中的基础玻璃部分包括：
重量％
SiO2 66-75
Na2O 10-20
CaO 5-15
MgO 0-5
Al2O3 0-5
K2O 0-5
太阳辐射吸收及着色部分基本由下列成分组成：
总铁 0.9-1.3％重量
FeO 0.25-0.40％重量
CoO 80-130PPM
Se 8-15PPM
Cr2O3 250-350PPM
TiO2 0.1-0.5％重量该玻璃的透光性(LTA)为25-40％。
47.权利要求46所说的制品，其中总铁的浓度为约1.083-1.11％重量、FeO的浓度为约0.306-0.35％重量、CoO的浓度为90-128PPM、Se的浓度为约10-12PPM、Cr2O3的浓度为约286-302PPM和TiO2的浓度为约0.194-0.355％重量。
48.权利要求47所说的制品，其中该玻璃具有约25％或更低的总太阳紫外透过性(TSUV)，约20％或更低的总太阳红外透过性(TSIR)，以及约30％或更低的总太阳能透过性(TSET)。
49.一种绿色红外和紫外辐射吸收玻璃制品，该玻璃制品具有由下列基础玻璃部分和下列太阳辐射吸收及着色部分组成的组合物：
其中基础玻璃部分包括：
重量％
SiO2 66-75
Na2O 10-20
CaO 5-15
MgO 0-5
Al2O3 0-5
K2O 0-5
太阳辐射吸收及着色部分基本由下列成分组成：
总铁 约0.60-4％重量
FeO 约0.13-0.9％重量
CoO 约40-500PPM
Se 约5-70PPM
TiO2 约0.02-1％重量
Cr2O3 0-约0.08％重量
V2O5 0-约0.32％重量
MnO2 0-约0.5重量％
SnO2 0-约2重量％
ZnO 0-约0.5重量％
Mo 0-约0.015重量％
CeO2 0-约2重量％
NiO 0-约0.1重量％其中Cr2O3浓度和V2O5浓度的25％之和至少为0.0015％重量，并且该玻璃的透光性(LTA)为不超过60％。
50.一种绿色红外和紫外辐射吸收玻璃制品，该玻璃制品具有由下列基础玻璃部分和下列太阳辐射吸收及着色部分组成的组合物：
其中基础玻璃部分包括：
重量％
SiO2 66-75
Na2O 10-20
CaO 5-15
MgO 0-5
Al2O3 0-5
K2O 0-5
太阳辐射吸收及着色部分基本由下列成分组成：
总铁 1-低于约1.4％重量
FeO 约0.2-0.6％重量
CoO 高于200-约450PPM
Se 约5-70PPM
TiO2 0-约1％重量
Cr2O3 0-约0.08％重量
V2O5 0-约0.32％重量
MnO2 0-约0.5重量％
SnO2 0-约2重量％
ZnO 0-约0.5重量％
Mo 0-约0.015重量％
CeO2 0-约2重量％
NiO 0-约0.1重量％其中Cr2O3浓度和V2O5浓度的25％之和至少为0.0200％重量，并且该玻璃的透光性(LTA)为不超过60％。