CN111690134A - 一种提升阴极片软韧性的分散剂 - Google Patents
一种提升阴极片软韧性的分散剂 Download PDFInfo
- Publication number
- CN111690134A CN111690134A CN202010637254.XA CN202010637254A CN111690134A CN 111690134 A CN111690134 A CN 111690134A CN 202010637254 A CN202010637254 A CN 202010637254A CN 111690134 A CN111690134 A CN 111690134A
- Authority
- CN
- China
- Prior art keywords
- polyimide
- acid
- dispersant
- dispersing agent
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种提升阴极片软韧性的分散剂，将二羟基丁二酸与聚氮杂环丙烷混合，反应后获取带有羟基的聚酰亚胺，所述聚酰亚胺作为欲制分散剂的骨架，对获取的所述聚酰亚胺进行溶剂化链的嫁接，将嫁接后的所述聚合物与正磷酸酯或一个或两个分子的无机酸去掉一分子水而成的氧化物混合反应，以制成成品分散剂。该提升阴极片软韧性的分散剂，该分散剂能够明显提高阴极片的软韧性，其将二羟基丁二酸与聚氮杂环丙烷混合，反应后获取带有羟基的聚酰亚胺，对获取的所述聚酰亚胺进行溶剂化链的嫁接，将嫁接后的所述聚合物与酸酐反应，使得阴极片更为柔韧，同时提高了阴极片的导电性能，具有广泛的使用前景。
Description
技术领域
本发明涉及分散剂领域，具体为一种提升阴极片软韧性的分散剂。
背景技术
分散剂是一种在分子内同时具有亲油性和亲水性两种相反性质的界面活性剂。可均一分散那些难于溶解于液体的无机，有机颜料的固体及液体颗粒，同时也能防止颗粒的沉降和凝聚，形成安定悬浮液所需的两亲性试剂；
分散剂的作用是使用润湿分散剂减少完成分散过程所需要的时间和能量，稳定所分散的颜料分散体，改性颜料粒子表面性质，调整颜料粒子的运动性，具体体现在以下几个方面：
1、提升光泽，增加流平效果光泽实际最主要取决涂料表面对光的散射(即一定的平整度即可。当然需检测仪器决定是否够平整,不但考虑原生粒子数目,形状,并考虑他们的结合方式),当粒子粒径小于入射光1/2(这个数值不确定)时,表现为折射光，光泽不会再提高，同理遮盖力依靠散射提供主要遮盖力的遮盖力也不会增加(除炭黑主要靠吸收光，有机颜料忘了)。注：该入射光是指可见光的范围流平说不好；但注意粒子原生数目减少，是减少其结构黏度，但比表面的增加会使自由树脂的数量减少，是否有平衡点说不好，但一般粉末涂料流平并不是越细越好。
2、防止浮色发花。
3、提高着色力注意着色力在自动调色系统中并非越高越好。
4、降低粘度，增加颜料载入量。
5、减少絮凝是这样的，但越细粒子表面能越高，需要越高吸附强度的分散剂，但吸附强度太高的分散剂可能造成对涂膜性能的不利。
6、增加贮藏稳定性其实原因和上相似，一旦分散剂稳定强度不够，反而贮藏稳定性变差(当然从你的图片上看是没问题的)。
7、增加展色性，增加颜色饱和度、增加透明度(有机颜料)或遮盖力(无机颜料；
而现有分散剂在使用时存在一定的弊端，没有应用于阴极片上，无法显著提高阴极片的软韧性，为此，一种提升阴极片软韧性的分散剂。
发明内容
本发明提供如下技术方案：一种提升阴极片软韧性的分散剂，将二羟基丁二酸与聚氮杂环丙烷混合，反应后获取带有羟基的聚酰亚胺，所述聚酰亚胺作为欲制分散剂的骨架，对获取的所述聚酰亚胺进行溶剂化链的嫁接，将嫁接后的所述聚合物与正磷酸酯或一个或两个分子的无机酸去掉一分子水而成的氧化物混合反应，以制成成品分散剂。
优选的，所述一个或两个分子的无机酸去掉一分子水而成的氧化物，优选实用酸酐。
优选的，二羟基丁二酸与聚氮杂环丙烷的摩尔比为1：1:1-1.1。
优选的，在90-110℃、常压下，二羟基丁二酸与聚氮杂环丙烷搅拌反应30-50min，浓缩干燥得到带有羟基的聚酰亚胺。
优选的，搅拌状态下，在碱溶液中，加入一个或两个分子的无机酸去掉一分子水而成的氧化物，溶解后，在温度为10-15℃时，滴加入醋酸配成的溶液与正磷酸酯，形成分散剂。
优选的，所述醋酸的浓度为36％--38％。
与现有技术相比，本发明提供了一种提升阴极片软韧性的分散剂，该分散剂能够明显提高阴极片的软韧性，其将二羟基丁二酸与聚氮杂环丙烷混合，反应后获取带有羟基的聚酰亚胺，对获取的所述聚酰亚胺进行溶剂化链的嫁接，将嫁接后的所述聚合物与酸酐反应，使得阴极片更为柔韧，同时提高了阴极片的导电性能，具有广泛的使用前景。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
一种提升阴极片软韧性的分散剂，将二羟基丁二酸与聚氮杂环丙烷混合，反应后获取带有羟基的聚酰亚胺，所述聚酰亚胺作为欲制分散剂的骨架，对获取的所述聚酰亚胺进行溶剂化链的嫁接，将嫁接后的所述聚合物与正磷酸酯或一个或两个分子的无机酸去掉一分子水而成的氧化物混合反应，以制成成品分散剂。
一个或两个分子的无机酸去掉一分子水而成的氧化物，优选实用酸酐。
二羟基丁二酸与聚氮杂环丙烷的摩尔比为1：1:1-1.1。
在90-110℃、常压下，二羟基丁二酸与聚氮杂环丙烷搅拌反应30-50min，浓缩干燥得到带有羟基的聚酰亚胺。
搅拌状态下，在碱溶液中，加入一个或两个分子的无机酸去掉一分子水而成的氧化物，溶解后，在温度为10-15℃时，滴加入醋酸配成的溶液与正磷酸酯，形成分散剂。
所述醋酸的浓度为36％--38％。
实施例1
该分散剂在制备时，将二羟基丁二酸与聚氮杂环丙烷混合，反应后获取带有羟基的聚酰亚胺，所述聚酰亚胺作为欲制分散剂的骨架，对获取的所述聚酰亚胺进行溶剂化链的嫁接，将嫁接后的所述聚合物与正磷酸酯或一个或两个分子的无机酸去掉一分子水而成的氧化物混合反应，以制成成品分散剂；
经检测，该分散剂耐电化学腐蚀能力强，放置于硫酸中24h，无腐蚀情况，锂离子电池的循环充放电的正常进行，导电性能提高24％。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (6)
1.一种提升阴极片软韧性的分散剂，其特征在于，将二羟基丁二酸与聚氮杂环丙烷混合，反应后获取带有羟基的聚酰亚胺，所述聚酰亚胺作为欲制分散剂的骨架，对获取的所述聚酰亚胺进行溶剂化链的嫁接，将嫁接后的所述聚合物与正磷酸酯或一个或两个分子的无机酸去掉一分子水而成的氧化物混合反应，以制成成品分散剂。
2.根据权利要求1所述的一种提升阴极片软韧性的分散剂，其特征在于：所述一个或两个分子的无机酸去掉一分子水而成的氧化物，优选实用酸酐。
3.根据权利要求1所述的一种提升阴极片软韧性的分散剂，其特征在于：二羟基丁二酸与聚氮杂环丙烷的摩尔比为1：1:1-1.1。
4.根据权利要求1所述的一种提升阴极片软韧性的分散剂，其特征在于：在90-110℃、常压下，二羟基丁二酸与聚氮杂环丙烷搅拌反应30-50min，浓缩干燥得到带有羟基的聚酰亚胺。
5.根据权利要求1所述的新型润滑油配方的制备方法，其特征在于：搅拌状态下，在碱溶液中，加入一个或两个分子的无机酸去掉一分子水而成的氧化物，溶解后，在温度为10-15℃时，滴加入醋酸配成的溶液与正磷酸酯，形成分散剂。
6.根据权利要求5所述的新型润滑油配方的制备方法，其特征在于：所述醋酸的浓度为36％--38％。