CN111094006A - 喷墨记录介质 - Google Patents
喷墨记录介质 Download PDFInfo
- Publication number
- CN111094006A CN111094006A CN201880057771.0A CN201880057771A CN111094006A CN 111094006 A CN111094006 A CN 111094006A CN 201880057771 A CN201880057771 A CN 201880057771A CN 111094006 A CN111094006 A CN 111094006A
- Authority
- CN
- China
- Prior art keywords
- ink
- mass
- receiving layer
- parts
- recording medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
[课题]提供具有高显色性,并且特别是在高速单张纸喷墨打印机中使用时,即使在高温多湿条件下打印机运送性也优异的喷墨记录介质。[解决方案]一种喷墨记录介质,其在基纸的至少一个面设置有含有无机颜料、粘合剂、包含阳离子性化合物的喷墨墨液用固定剂以及有机球状粒子的墨液接收层,墨液接收层还含有水溶性金属盐,作为粘合剂,相对于墨液接收层100质量份,含有5质量份以上且15质量份以下的聚合度为700以下的聚乙烯醇(A)、以及20质量份以上且40质量份以下的聚合度为1200以上的聚乙烯醇(B),利用激光衍射/散射法测定的有机球状粒子的体积50%平均粒径(D50)为15.0μm以上。
Description
技术领域
本发明涉及喷墨记录介质。
背景技术
喷墨记录方式由于全彩化容易、打印噪音少等而在近年迅速普及。这一方式是从喷嘴向记录介质使墨液的微小液滴以高速飞出、附着来进行图像、文字等的记录的方式。所以,多颜色、高精细化容易,特别是在近年来的高分辨率全彩打印机中,能够打印与彩色印刷、银盐照片相比也几乎不逊色的图像。因此,现在一般家庭中引入了许多喷墨打印机,主要在通过喷墨记录来打印来自数码相机的图像来制作直接邮寄卡、贺年明信片等的用途中使用。
但是,对于家庭用喷墨打印机的印刷速度而言,与通过胶版印刷机等的印刷相比处理时间过长,难以在商业上实现喷墨记录。因此,主要在商业用途中出现了大幅缩短了印刷时间、即能够实现高速印刷的行头(ラインヘッド)搭载型打印机(例如,参照专利文献1)。对于行头搭载型打印机而言,与墨液喷头移动来进行印刷的现有的喷墨打印机不同,装备有线状的墨液喷头,其下方喷墨记录介质搭在带上以高速运送。所以,每一张的打印时间为几秒或1秒以下,与家庭用喷墨打印机相比能够实现压倒性的高速打印。而且,在打印机内部具有使记录用纸反转的机构,也能够进行双面打印。然而,虽然能够实现高速/双面打印,但对记录用纸的要求特性也日渐变高。
如果喷墨记录介质的运送性不良,则会发生未被运送至打印机内的“空送”(日文原文:空送),或会发生多张重叠运送的“重送”(日文原文:重送),而产生问题。特别是,在高温多湿条件下堆叠的喷墨记录介质之间的摩擦系数变高,容易发生重送。这在家庭用喷墨打印机中也是问题,特别是在以高速打印为特征的商业用途的高速单张纸打印机中成为致命的问题。
而且,虽然公开了在墨液接收层中含有有机球状粒子而使喷墨记录介质的表面与背面之间的静摩擦系数降低的方法(参照专利文献3),但其以家庭用喷墨打印机为对象,对于商业用途的高速单张纸打印机来说并不优选。
现有技术文献
专利文献
专利文献1:日本特开2004-276486号公报
专利文献2:日本特开平8-278357号公报
专利文献1:日本特开2002-292997号公报
发明内容
发明要解决的问题
然而,特别是在具有行头的高速单张纸喷墨打印机中使用时,要求在高温多湿条件下的打印机运送性。所谓高温,是指例如30℃以上,所谓多湿,是指例如80%RH以上。
用于解决问题的方案
本发明的发明人等为了解决上述问题而进行了深入研究,结果发现,通过使用以下的构成,能够达成本发明的目的。
即,本发明为一种喷墨记录介质,其在基纸的至少一个面设置有含有无机颜料、粘合剂、包含阳离子性化合物的喷墨墨液用固定剂(定着剤)以及有机球状粒子的墨液接收层,所述墨液接收层还含有水溶性金属盐,作为所述粘合剂,相对于所述墨液接收层100质量份,含有5质量份以上且15质量份以下的聚合度为700以下的聚乙烯醇(A)、以及20质量份以上且40质量份以下的聚合度为1200以上的聚乙烯醇(B),利用激光衍射/散射法测定的所述有机球状粒子的体积50%平均粒径(D50)为15.0μm以上。
优选所述有机球状粒子的所述体积50%平均粒径(D50)大于20.0μm且为35.0μm以下。
优选相对于所述无机颜料100质量份,含有0.5质量份以上且7质量份以下的所述有机球状粒子。
优选所述水溶性金属盐的阳离子为选自镁离子、钙离子及铝离子中的1种,阴离子为选自硫酸离子、硝酸离子及氯离子中的1种。
优选相对于所述墨液接收层100质量份,含有3质量份~15质量份的所述水溶性金属盐。
优选所述无机颜料含有所述体积50%平均粒径(D50)为6μm~14μm的合成非晶质二氧化硅,相对于所述无机颜料,所述合成非晶质二氧化硅占60质量%以上。
优选在所述基纸的两个面设置有所述墨液接收层。
发明效果
根据本发明,可得到具有高显色性,并且特别是在具有行头的高速单张纸喷墨打印机中使用时,即使在高温多湿条件下打印机运送性也优异的喷墨记录介质。
具体实施方式
本发明的墨液接收层含有无机颜料、粘合剂、包含阳离子性化合物的喷墨墨液用固定剂以及有机球状粒子。
本发明中,关于能够得到具有高显色性,并且特别是在具有行头的高速单张纸喷墨打印机中使用时,即使在高温多湿条件下打印机运送性也优异的喷墨记录介质的理由,如以下地进行说明。
作为打印机中发生运送问题的原因,可认为是堆叠的喷墨记录介质之间的摩擦系数未处于合适的范围。如果摩擦系数、特别是静摩擦系数过高,则喷墨记录介质间的滑动变差,多张喷墨记录介质在打印机内集中并错位,发生多张重叠运送的重送。反之,如果摩擦系数、特别是动静摩擦系数过低,则由于喷墨记录介质过于滑动,因此发生喷墨记录介质未被运送至打印机内的空送。特别是在高温多湿条件下,发现摩擦系数、特别是静摩擦系数有变高的倾向,所以容易发生重送。
因此,为了即使在高温多湿条件下也将喷墨记录介质的表面与背面之间的摩擦系数调整至合适范围,设为上述墨液接收层的构成。
作为用于本发明的墨液接收层的无机颜料,可以使用现有公知的白色颜料。例如,为轻质碳酸钙、重质碳酸钙、高岭土、煅烧高岭土、粘土、滑石、硫酸钙、硫酸钡、二氧化钛、氧化锌、硫化锌、碳酸锌、缎光白(サ于ンホワイト)、硅酸铝、硅藻土、硅酸钙、硅酸镁、合成非晶质二氧化硅、胶体二氧化硅、胶体氧化铝、勃姆石、拟勃姆石、氢氧化铝、氧化铝、锌钡白、沸石、水解埃洛石、碳酸镁、氢氧化镁等。
这些之中,优选相对于全部无机颜料以60质量%以上的比例含有利用激光衍射/散射法测定的体积50%平均粒径(D50)为6~14μm的合成非晶质二氧化硅,能够得到印刷品质良好的喷墨记录介质。
合成非晶质二氧化硅的D50小于6μm时,存在墨液吸收性不足从而印刷品质下降的可能性。并且,合成非晶质二氧化硅的D50大于14μm时,存在无机颜料粒子间的空隙变得过多从而墨液吸收性变得过剩,打印浓度下降的可能性。
墨液接收层的无机颜料也可全部(100质量%)为合成非晶质二氧化硅。
在此,作为激光衍射/散射法的测定装置,例如有崛场制作所公司的粒径分布测定装置“Partica”、Malvern公司的粒度分布测定装置“MASTERSIZER S”等。
作为用于本发明的墨液接收层的有机球状粒子,可举出聚酰胺树脂、聚酯树脂、聚碳酸酯树脂、聚醚树脂、聚烯烃树脂、聚砜系树脂、聚苯乙烯系树脂、聚氨酯系树脂、聚丙烯酸系树脂、聚氯乙烯系树脂、聚偏二氯乙烯系树脂、乙烯-乙酸乙烯酯共聚树脂、苯乙烯共聚树脂等通常的有机物的球状粒子。
在此,为了降低墨液接收层的摩擦系数,确保打印机运送性,而使用有机球状粒子。
本发明中,将有机球状粒子的利用激光衍射/散射法测定的体积50%平均粒径(D50)设为15.0μm以上,使得有机球状粒子难以埋入墨液接收层中。平均粒径D50小于15.0μm时,有机球状粒子容易埋入墨液接收层中,摩擦系数的降低效果不足。
而且,有机球状粒子的平均粒径优选大于20.0μm且为35.0μm以下,更优选为22.0μm以上且30.0μm以下。
如果平均粒径大于35.0μm,则会有特别是动静摩擦系数的降低效果变得过剩,导致容易发生空送的情况。
有机球状粒子的平均粒径利用激光衍射/散射法测定。作为激光衍射/散射法的测定装置,如上所述。
而且,相对于无机颜料100质量份,优选在墨液接收层中以0.5质量份以上且7质量份以下的范围含有有机球状粒子,更优选以1.5质量份以上且5.5质量份以下的范围含有有机球状粒子。有机球状粒子不足0.5质量份时,会有特别是静摩擦系数的降低效果小,容易发生重送的情况。并且,含量超过7质量份时,会有特别是动静摩擦系数的降低效果变得过剩,容易发生空送的情况。
本发明中,墨液接收层含有后述的水溶性金属盐,以及作为粘合剂的、相对于墨液接收层100质量份为5质量份以上且15质量份以下的聚合度为700以下的聚乙烯醇(PVA)(A)以及20质量份以上且40质量份以下的聚合度为1200以上的聚乙烯醇(B)。
通过墨液接收层以特定量含有聚乙烯醇(B),从而容易兼顾墨液接收层的强度与墨液吸收性。另一方面,如果墨液接收层中不含有聚乙烯醇(A),则水溶性金属盐对聚乙烯醇(B)发生作用,聚乙烯醇(B)的覆膜附着于有机球状粒子的周围,所以有机球状粒子埋入墨液接收层中,在表面露出的比例减少。推测其结果为,基于有机球状粒子的配合而实现的墨液接收层的摩擦系数的降低效果变小。
另一方面,水溶性金属盐即使对聚乙烯醇(A)发生作用,也不会产生聚乙烯醇(B)那样厚度的覆膜,所以如果墨液接收层以特定量含有聚乙烯醇(A),则上述有机球状粒子的埋入被抑制,墨液接收层的摩擦系数的降低效果变大。
聚乙烯醇(A)小于5质量份时,不能充分地抑制上述有机球状粒子的埋入。而且,含量超过15质量份时,后述的水溶性金属盐的效果、即颜料墨液使用时的打印适合性的提高受损,因此特别是利用颜料打印机的打印浓度劣化。
聚乙烯醇(B)小于20质量份时,墨液接收层的强度不足,喷墨记录介质的处理变得困难。而且,含量超过40质量份时,墨液吸收性不足,印刷品质劣化。
特别地,聚乙烯醇(A)为10质量份以上时,有机球状粒子的埋入被抑制,墨液接收层的摩擦系数的降低效果可靠地产生,打印机的重送减少,所以优选。
作为本发明的聚乙烯醇(A)及聚乙烯醇(B),可以使用完全皂化聚乙烯醇、部分皂化聚乙烯醇、羧基改性聚乙烯醇、二丙酮改性聚乙烯醇、乙酰乙酰基改性聚乙烯醇、酰胺改性聚乙烯醇、磺酸改性聚乙烯醇、缩丁醛改性聚乙烯醇、烯烃改性聚乙烯醇、腈改性聚乙烯醇、吡咯烷酮改性聚乙烯醇、硅烷醇改性聚乙烯醇、阳离子改性聚乙烯醇、末端烷基改性聚乙烯醇等现有公知的聚乙烯醇。
作为上述聚乙烯醇以外的用于本发明的墨液接收层中的粘合剂,可例示除聚乙烯醇(A)、(B)之外的上述聚乙烯醇;羟基乙基纤维素、甲基纤维素、乙基纤维素、羧甲基纤维素、乙酰纤维素等纤维素醚及其衍生物;淀粉、酶改性淀粉、热化学改性淀粉、氧化淀粉、酯化淀粉、醚化淀粉(例如,羟乙基化淀粉等)、阳离子化淀粉等淀粉类;聚丙烯酰胺、阳离子性聚丙烯酰胺、阴离子性聚丙烯酰胺、两性聚丙烯酰胺等聚丙烯酰胺类;聚酯聚氨酯系树脂、聚醚聚氨酯系树脂、聚氨酯系离聚物树脂等氨基甲酸酯系树脂;包含(甲基)丙烯酸以及能够与(甲基)丙烯酸共聚的单体成分(除烯烃之外)的丙烯酸系树脂;苯乙烯-丁二烯共聚物、苯乙烯-丁二烯-丙烯腈共聚物、苯乙烯-丁二烯-丙烯酸共聚物等苯乙烯-丁二烯系树脂;聚乙酸乙烯酯,氯乙烯-乙酸乙烯酯共聚物、乙烯-乙酸乙烯酯共聚物等聚烯烃系树脂;聚氯乙烯;聚偏二氯乙烯;聚丙烯酸酯;阿拉伯胶;聚乙烯醇缩丁醛;聚苯乙烯(ポリスチ口一ス)及它们的共聚物;有机硅树脂;石油树脂;萜烯树脂;酮树脂;香豆酮树脂等。在不损害本发明的效果的范围内,这些粘合剂可以单独或混合2种以上使用。
为了提高特别是利用染料打印机的打印适合性,本发明的墨液接收层中含有包含阳离子性化合物的喷墨墨液用固定剂。
作为用于本发明的墨液接收层中的、包含阳离子性化合物的喷墨墨液用固定剂,可列举仲胺、叔胺及作为季铵盐的聚乙烯亚胺盐、二甲胺表卤醇缩合物、聚乙烯基胺盐、聚烯丙基胺盐、聚甲基丙烯酸二甲基氨基乙基酯季盐(ポリヅメチルアミノ工チルメタクリレ一ト四級塩)、聚二烯丙基二甲基铵盐、二烯丙基氨基丙烯酰胺共聚物盐、聚苯乙烯的季铵盐等。这些物质可以单独或混合2种以上使用。
本发明中,相对于墨液接收层100质量份,优选以3质量份以上且15质量份以下的范围含有喷墨墨液用固定剂。喷墨墨液用固定剂不足3质量份时,难以充分地提高利用染料打印机的打印适合性。而且,含量超过15质量份时,存在墨液吸收性不足从而印刷品质下降的可能性。
需要说明的是,作为利用染料打印机的打印适合性,可列举打印浓度和耐水性。
为了提高利用颜料打印机的打印适合性,本发明的墨液接收层中含有水溶性金属盐。
优选水溶性金属盐的阳离子为选自镁离子、钙离子及铝离子中的1种,阴离子为选自硫酸离子、硝酸离子及氯离子中的1种。作为这样的水溶性金属盐的例子,可列举出硫酸镁、硫酸钙、硫酸铝、硝酸镁、氯化镁等。
本发明中,相对于墨液接收层100质量份,优选以3质量份以上且15质量份以下的范围含有水溶性金属盐。水溶性金属盐不足3质量份时,难以充分地提高利用颜料打印机的打印适合性。而且,含量超过15质量份时,存在容易对聚乙烯醇(B)产生作用,墨液接收层的摩擦系数的降低效果变小的可能性。
需要说明的是,作为利用颜料打印机的打印适合性,可列举打印浓度。
而且,在不损害本发明的效果的范围内,本发明的墨液接收层中还可以根据需要适宜含有施胶剂、颜料分散剂、增稠剂、流动性改进剂、表面活性剂、消泡剂、抑泡剂、脱模剂、发泡剂、浸透剂、着色染料、荧光增白剂、紫外线吸收剂、抗氧化剂、防腐剂、防霉剂、耐水化剂、湿润纸力增强剂、干燥纸力增强剂、保水剂等。
本发明的喷墨记录介质在基纸的至少一个面设置有墨液接收层而成。基纸虽然没有特别的限制,但优选使用以木材纸浆为主成分的纸。作为木材纸浆,可以将化学纸浆(针叶树的漂白或未漂白牛皮纸浆、阔叶树的漂白或未漂白牛皮纸浆等)、机械纸浆(磨制纸浆、热磨机械纸浆、化学热磨机械纸浆等)、脱墨纸浆等纸浆单独使用或以任意比例混合使用。
当基纸中含有填料时,基纸的不透明度和平滑性提高,所以优选。作为填料,可以例示出水合硅酸、白炭黑、滑石、高岭土、粘土、碳酸钙、氧化钛、合成树脂填料等公知的填料。另外,也可以根据要求品质而并用这些填料。
将基纸材进行抄纸时的pH可以为酸性、中性、碱性中的任意者,基纸的克重(日文原文:坪量)没有特别限制。另外,在不损害本发明的效果的范围内,在基纸中可以根据需要而含有硫酸铝、施胶剂、纸力增强剂、成品率提高剂、着色剂、染料、消泡剂、pH调节剂等助剂。
出于增强纸力、赋予施胶性等目的,也可以对基纸浸渗或涂覆含有淀粉、聚乙烯醇、施胶剂等的施胶液。另外,在不损害本发明的效果的范围内,在施胶液中可以根据需要而含有荧光染料、导电剂、保水剂、耐水化剂、pH调节剂、消泡剂、润滑剂、防腐剂、表面活性剂等助剂。对施胶液的浸渗或涂覆的方法没有特别限制,可以例示出以磅(ポンド)式施胶压制为代表的浸渗法、或者以棒式计量施胶压制、门辊涂布机、刮刀涂布机为代表的涂覆法。
本发明中,关于设置于基纸上的墨液接收层的总数及构成没有特别的限制。墨液接收层的涂覆量(干燥涂覆量)优选为每单面4g/m2~10g/m2,进一步优选为5g/m2~9g/m2。
如果墨液接收层的涂覆量小于4g/m2,则存在墨液吸收性不足从而印刷品质下降的可能性。而且,如果墨液接收层的涂覆量超过10g/m2,则存在墨液吸收性变得过剩从而打印浓度下降的可能性,并且还存在有机球状粒子埋入墨液接收层,墨液接收层的摩擦系数的降低效果变小的可能性。
为了将墨液接收层设置于基纸的表面,本发明中,可以在机或机外使用作为通常的涂覆装置的各种刮刀涂布机、辊涂机、气刀涂布机、棒涂机、门辊涂布机、帘式涂布机、凹版涂布机、柔性凹版涂布机、喷涂机、施胶压制机等各种装置。而且,在涂覆墨液接收层之后,也可以用机械压光机、超级压光机、软压光机等压光机装置对墨液接收层进行表面处理。
实施例
以下举出实施例更具体地对本发明进行说明,但本发明不受其限制。并且,“份”及“%”只要没有明确说明,则表示质量份及质量%。
(基纸)
作为纸浆原料,使用CSF340ml的阔叶树漂白牛皮纸浆(LBKP)100份,将相对于纸浆100份配合了纸力增强剂(阳离子化淀粉)0.4份、硫酸铝0.4份、碳酸钙16份而成的纸料用长网抄造机进行抄造。之后,在该原纸的两面将氧化淀粉7%的液体利用施胶压制以干燥涂覆量在两面为3g/m2的方式进行涂覆,干燥后用机械压光机处理,得到克重94g/m2的基材。
需要说明的是,表中的“克重”为墨液接收层涂覆后的喷墨记录介质的值。
(墨液接收层)
将下述物质以表1所示的比例混合,适当添加稀释水,制备各实施例及比较例中使用的涂覆液。作为无机颜料的合成非晶质二氧化硅的、凝胶法二氧化硅(制品名:BS-380N:平均粒径D50=10.0μm,DSL.Japan株式会社制)、沉降法二氧化硅(制品名:X-60:平均粒径D50=7.0μm,Oriental Silicas Corporation公司制);作为粘合剂的、聚乙烯醇(A)(制品名:GL-05:聚合度500,日本合成化学工业株式会社制)、聚乙烯醇(B)(制品名:PVA117:聚合度1700,可乐丽株式会社制)、以及乙烯-乙酸乙烯酯(制品名:BE-585:日本涂料树脂株式会社制);作为喷墨墨液用固定剂的、聚胺表卤醇共聚物(制品名:DK6872,星光PMC株式会社制);作为有机球状粒子的、亚克力珠(アクリルビ一ズ)(制品名:Art Pearl GR-200透明:平均粒径D50=32.0μm,根上工业株式会社制)、亚克力珠(制品名:Art Pearl GR-300透明:平均粒径D50=22.0μm,根上工业株式会社制)、亚克力珠(制品名:Art Pearl G-400透明:平均粒径D50=15.0μm,根上工业株式会社制)、亚克力珠(制品名:Art Pearl GR-600透明:平均粒径D50=10.0μm,根上工业株式会社制);作为水溶性金属盐的硫酸镁(MgSO4)。
使用刮刀涂布机(バ一ブレ一ドコ一タ一)将该涂覆液以其干燥涂覆量为每单面7.0g/m2的方式涂布于基纸的单面或两面,得到各实施例及比较例的喷墨记录介质。
有机球状微粒的平均粒径D50利用激光衍射/散射法(崛场制作所公司的粒径分布测定机“Partica”)来测定。
需要说明的是,表中,关于两面墨液接收层的实施例及比较例,在各栏的左侧与右侧中记载每单面的特性及评价。
对于各实施例及比较例中得到的喷墨记录介质,进行以下评价,所得结果示于表1、表2中。需要说明的是,对于表1、表2中在两面设置有墨液接收层的情况,各实施例及比较例并列记载了各面的印刷品质。
<印刷品质>
分别用染料打印机(制品名:EP-306,精工爱普生株式会社制,印刷条件:特级纸、标准)、颜料打印机(制品名:PX-5600,精工爱普生株式会社制,印刷条件:特级纸、洁净)进行打印。
打印浓度
关于青色、品红色、黄色、黑色打印各自的实心图像(ベタ画像),在23℃、50%RH的环境下静置24小时之后,用反射浓度计(GretagMacbeth RD-19I)测定各图像部的打印浓度。4色的打印浓度合计值为染料墨液:4.50以上、颜料墨液:4.60以上时,实用上没有问题。
实心不均(ベタムラ)
进行邻接的绿色的实心打印(纵2cm×横3cm),以以下的标准进行评价。实心不均的评价为3、2时,实用上没有问题。
3:没有不均,得到均匀实心,未发现实心部周围的渗染。
2:部分地发现少许不均,但得到大致均匀的实心,未发现实心部周围的渗染。
1:部分地发现不均,或者发现实心部周围的渗染。
<打印机运送性>
将各试样在23℃/65%RH的环境下静置8小时后,在23℃/50%RH或30℃/80%RH的环境下,在喷墨打印机(制品名:PIXUS MG7130,佳能株式会社制,印刷条件:普通纸、洁净)中各试样放置20张并进行运送。反复进行5次该操作,合计运送100张,以以下的基准进行评价。评价为○、△时,实用上没有问题。
<重送>
○:未发生重送。
△:共发生1~2张重送。
×:共发生3张以上的重送。
<空送>
○:未发生空送。
△:共发生1~2张空送。
×:共发生3张以上的空送。
[表1]
[表2]
由表1、表2可知,各实施例中,印刷品质优异,打印机运送性也优异。
墨液接收层中的聚乙烯醇(A)的含量小于10质量份的实施例4、14中,与其它实施例相比重送多,打印机运送性略差,但实用上没有问题。
需要说明的是,使用平均粒径D50超过20.0μm的有机球状粒子的实施例1、2、11、12中,与其它实施例相比,高温多湿条件下(30℃/80%RH)的打印机运送性更加优异。
而且,使用平均粒径D50超过30.0μm的有机球状粒子的实施例5、15中,与其它实施例相比空送多,打印机运送性略差,但实用上没有问题。
墨液接收层中的有机球状粒子的含量小于1.5质量份的实施例6、16中,与其它实施例相比空送多,打印机运送性略差,但实用上没有问题。
墨液接收层中的有机球状粒子的含量超过5.5质量份的实施例7、17中,与其它实施例相比重送多,打印机运送性略差,但实用上没有问题。
与此相对,墨液接收层中不含有聚合度700以下的聚乙烯醇(A)的比较例1、11中,打印机运送性差。可认为这是因为:由于不含有聚乙烯醇(A),所以聚乙烯醇(B)的覆膜附着于有机球状粒子的周围,墨液接收层的摩擦系数的降低效果被抑制。
墨液接收层中仅含有D50小于15.0μm的有机球状粒子的比较例2、12中,打印机运送性差。可认为这是因为:由于有机球状粒子小,所以有机球状粒子埋入墨液接收层中,在表面露出的比例减少,摩擦系数的降低效果变小。
墨液接收层中不含有水溶性金属盐的比较例3、13中,颜料墨液使用时的印刷品质差。
Claims (7)
1.一种喷墨记录介质,在基纸的至少一个面设置有墨液接收层,所述墨液接收层含有无机颜料、粘合剂、包含阳离子性化合物的喷墨墨液用固定剂以及有机球状粒子,
所述墨液接收层还含有水溶性金属盐,
作为所述粘合剂,相对于所述墨液接收层100质量份,含有5质量份以上且15质量份以下的聚合度为700以下的聚乙烯醇A、以及20质量份以上且40质量份以下的聚合度为1200以上的聚乙烯醇B,
利用激光衍射/散射法测定的所述有机球状粒子的体积50%平均粒径D50为15.0μm以上。
2.根据权利要求1所述的喷墨记录介质,其中,所述有机球状粒子的所述体积50%平均粒径D50大于20.0μm且为35.0μm以下。
3.根据权利要求1或2所述的喷墨记录介质,其中,相对于所述无机颜料100质量份,含有0.5质量份以上且7质量份以下的所述有机球状粒子。
4.根据权利要求1~3中任一项所述的喷墨记录介质,其中,所述水溶性金属盐的阳离子为选自镁离子、钙离子及铝离子中的1种,阴离子为选自硫酸离子、硝酸离子及氯离子中的1种。
5.根据权利要求1~4中任一项所述的喷墨记录介质,其中,相对于所述墨液接收层100质量份,含有3质量份~15质量份的所述水溶性金属盐。
6.根据权利要求1~5中任一项所述的喷墨记录介质,其中,所述无机颜料含有所述体积50%平均粒径D50为6μm~14μm的合成非晶质二氧化硅,相对于所述无机颜料,所述合成非晶质二氧化硅占60质量%以上。
7.根据权利要求1~6中任一项所述的喷墨记录介质,其中,在所述基纸的两个面设置有所述墨液接收层。