CN110777471A - 一种滑感皱纹面料的加工工艺 - Google Patents

一种滑感皱纹面料的加工工艺 Download PDF

Info

Publication number
CN110777471A
CN110777471A CN201910970329.3A CN201910970329A CN110777471A CN 110777471 A CN110777471 A CN 110777471A CN 201910970329 A CN201910970329 A CN 201910970329A CN 110777471 A CN110777471 A CN 110777471A
Authority
CN
China
Prior art keywords
temperature
cloth
smooth
minutes
processing technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910970329.3A
Other languages
English (en)
Inventor
王勇
李�荣
李俊
丁海飞
王养峰
欧有权
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Yaxue Textile Technology Co Ltd
Original Assignee
Zhejiang Yaxue Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Yaxue Textile Technology Co Ltd filed Critical Zhejiang Yaxue Textile Technology Co Ltd
Priority to CN201910970329.3A priority Critical patent/CN110777471A/zh
Publication of CN110777471A publication Critical patent/CN110777471A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种滑感皱纹面料的加工工艺，它包括以下步骤，步骤一，织胚：选用60S人造棉纤维、140D尼龙纤维纬编织造成双面网眼汗布，门幅150cm，克重120g/m2。该滑感皱纹面料的加工工艺加工的面料手感柔软爽滑且具有自然皱印。

Description

一种滑感皱纹面料的加工工艺
技术领域：
本发明涉及纺织印染技术领域，是一种滑感皱纹面料的加工工艺。
背景技术：
现有滑感面料上较难形成视觉自然的皱印，缺少卖点。
发明内容：
本发明所要解决的技术问题是，提供一种手感柔软爽滑且具有自然皱印的滑感皱纹面料的加工工艺。
本发明的技术解决方案是，提供一种滑感皱纹面料的加工工艺，它包括以下步骤，
步骤一，织胚：选用60S人造棉纤维、140D尼龙纤维纬编织造成双面网眼汗布，门幅150cm，克重120g/m2；
步骤二，松布，圆筒松布机自然松弛胚布；
步骤三，前处理，0.5％TF-107T传化渗透剂，1.0％除油剂3302(德高)直升至90℃保持20分钟，然后直降到40℃以下，让布面充分收缩成皱纹；
步骤四，染色，选用丽源环保活性染料0.12％3KE、0.089％3BN、0.075％FBRN、60℃下保持20分钟，单染人造棉，
步骤五，柔软处理，加入质量比为0.3％柠檬酸，9.0％软片S300(传化)，40℃保持20分钟；
步骤六，成品定型：门富士8箱定型机，150℃×30米/min，浆料：0.5g/L柠檬酸、10g/L软滑硅油。
采用以上工艺后与现有技术相比，本发明具有以下优点：采用人棉纤维与尼龙纤维交织，利用两种纤维在快速升温状态下的不同收缩率，使布面形成皱印，人棉纤维与尼龙纤维交织，面料成品后透气性、排湿性良好，手感柔软滑爽。
具体实施方式：
下面就具体实施方式对本发明作进一步说明：
一种滑感皱纹面料的加工工艺，它包括以下步骤，
步骤一，织胚：选用60S人造棉纤维、140D尼龙纤维纬编织造成双面网眼汗布，门幅150cm，克重120g/m2；
步骤二，松布，圆筒松布机自然松弛胚布；
步骤三，前处理，0.5％TF-107T传化渗透剂，1.0％除油剂3302(德高)直升至90℃保持20分钟，然后直降到40℃以下，让布面充分收缩成皱纹；
步骤四，染色，选用丽源环保活性染料0.12％3KE、0.089％3BN、0.075％FBRN、60℃下保持20分钟，单染人造棉，
步骤五，柔软处理，加入质量比为0.3％柠檬酸，9.0％软片S300(传化)，40℃保持20分钟；
步骤六，成品定型：门富士8箱定型机，150℃×30米/min，浆料：0.5g/L柠檬酸、10g/L软滑硅油。
本发明具有以下优点：采用人棉纤维与尼龙纤维交织，利用两种纤维在快速升温状态下的不同收缩率，使布面形成皱印，人棉纤维与尼龙纤维交织，面料成品后透气性、排湿性良好，手感柔软滑爽。
以上仅就本发明较佳的实施例作了说明，但不能理解为是对权利要求的限制。

Claims (1)

1.一种滑感皱纹面料的加工工艺，其特征在于：它包括以下步骤，
步骤一，织胚：选用60S人造棉纤维、140D尼龙纤维纬编织造成双面网眼汗布；
步骤二，松布，圆筒松布机自然松弛胚布；
步骤三，前处理，加入0.3-1％渗透剂，1.0-2.2％除油剂直升至85-90℃保持18-24分钟，然后直降到40℃以下，让布面充分收缩成皱纹；
步骤四，染色，选用丽源环保活性染料0.10-0.2％3KE、0.08-0.09％3BN、0.075％FBRN，60℃下保持20分钟，单染人造棉，
步骤五，柔软处理，加入质量比为0.3％柠檬酸，9.0％软片S300，40℃保持20分钟；
步骤六，成品定型：门富士8箱定型机，150℃×30米/min，浆料中加入0.5g/L柠檬酸、10g/L软滑硅油。
CN201910970329.3A 2019-10-13 2019-10-13 一种滑感皱纹面料的加工工艺 Pending CN110777471A (zh)