CN110467747A - 具有希夫碱结构的金属离子阻燃络合物及制备方法 - Google Patents
具有希夫碱结构的金属离子阻燃络合物及制备方法 Download PDFInfo
- Publication number
- CN110467747A CN110467747A CN201910791259.5A CN201910791259A CN110467747A CN 110467747 A CN110467747 A CN 110467747A CN 201910791259 A CN201910791259 A CN 201910791259A CN 110467747 A CN110467747 A CN 110467747A
- Authority
- CN
- China
- Prior art keywords
- salen
- fire
- solvent
- schiff bases
- complex compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了具有希夫碱结构的金属离子阻燃络合物及制备方法,主要涉及反应型阻燃剂领域。结构式是其中,R是本发明的有益效果在于:通过将Salen‑H6‑2DPCP与金属络合生成一系列阻燃络合物Salen‑DPCP‑M,其中的含磷有机片段在高分子材料燃烧时发挥气相阻燃机理,希夫碱与金属在燃烧过程分别发挥交联与催化成炭的凝聚相阻燃作用。
Description
技术领域
本发明涉及反应型阻燃剂技术领域,具体是具有希夫碱结构的金属离子阻燃络合物及制备方法。
背景技术
希夫碱结构阻燃剂可以赋予高分子材料抗熔滴性能,在高分子材料发生火灾危险时降低二次燃烧带来的人身与财产损失。专利CN201510817559.8公开了一种基于希夫碱结构的高温自交联阻燃抗熔滴共聚酯。发现其在高温下会发生化学交联,提高共聚酯的熔体黏度,从而赋予了聚酯良好的阻燃抗熔滴特性。
专利CN201610825104提供一种阻燃性电线电缆料及其制备方法,所述阻燃性电线电缆料包含阻燃树脂组合物,所述阻燃树脂组合物包含含溴阻燃剂、含硫阻燃剂和/或含磷阻燃剂,以及无卤环氧树脂。但不难看出,该类型阻燃剂含有含溴阻燃剂,在使用中会有溴化氢有毒气体的释放,会对人身健康产生严重的二次伤害。
发明内容
本发明的目的在于提供具有希夫碱结构的金属离子阻燃络合物及制备方法,通过将Salen-H6-2DPCP与金属络合生成一系列阻燃络合物Salen-DPCP-M,其中的含磷有机片段在高分子材料燃烧时发挥气相阻燃机理,希夫碱与金属在燃烧过程分别发挥交联与催化成炭的凝聚相阻燃作用。
本发明为实现上述目的,通过以下技术方案实现:
具有希夫碱结构的金属离子阻燃络合物,结构式如式Ⅰ所示,
式Ⅰ:
其中,
R是:且R能够位于芳环上其余四处的任一位置,其所在位置由所用二羟基苯甲醛的结构类型所决定;
所述M为金属离子,选自Ni(Ⅱ)、Zn(Ⅱ)、Cu(Ⅱ)、Fe(Ⅲ)、Mn(Ⅱ)中的任一种。
所述具有希夫碱结构的金属离子阻燃络合物是以乙二胺、二羟基苯甲醛、氯磷酸二苯酯为原料,与金属盐络合得到的,中心离子是金属M,而配体是有机磷与希夫碱结构的阻燃络合物Salen-DPCP-M。
进一步的,其络合剂按物质的量计比例为:
乙二胺 1份;
二羟基苯甲醛 2.0~2.3份;
氯磷酸二苯酯 2.3~2.6份;
氯磷酸二苯酯与缚酸剂的物质的量比为1:1.0~2.0;
反应获得中间产物Salen-H6-2DPCP,Salen-H6-2DPCP与金属盐的物质的量比为1:1.0~1.3。
所述缚酸剂为三乙胺、吡啶、氢氧化钠、氢氧化钾中的任一种。
所述具有希夫碱结构的金属离子阻燃络合物,通过以下方法制得:
步骤1,将二羟基苯甲醛、溶剂1、乙二胺混合,并在惰性气体保护下30℃搅拌反应12h,过滤得到黄色沉淀,所述黄色沉淀依次经过减压过滤、溶剂1洗涤、真空干燥后,得到中间产物N,N′-双(二羟基亚水样基)-1,2-苯二胺,即Salen-H6;
其中,所述溶剂1为甲醇、乙醇、季戊四醇中的一种;
其中,所述二羟基苯甲醛为2,3-二羟基苯甲醛、2,4-二羟基苯甲醛、2,5- 二羟基苯甲醛、2,6-二羟基苯甲醛中的一种;
步骤2,混合Salen-H6、缚酸剂、溶剂2,并在0℃条件下滴加氯磷酸二苯酯,在惰性气体保护下30℃搅拌反应6h,减压蒸干溶剂2后,依次使用二氯甲烷萃取 3次,有机相用去离子水洗3次,再减压蒸干二氯甲烷得到黄色液体,分离提纯后,得到N,N′-双(2-羟基-(磷酸二苯酯基)亚水样基)-1,2-苯二胺,即 Salen-H6-2DPCP;
所述分离提纯,是指利用柱层析体积比V/V石油醚:乙酸乙酯=1:1或体积比 V/V二氯甲烷:甲醇=20:1对黄色液体进行分离提纯。
其中,所述溶剂2是苯、甲苯、二甲苯、二氯甲烷、三氯甲烷、四氢呋喃、丙酮、丁酮、N,N-二甲基甲酰胺中的一种;
其中,所述缚酸剂为三乙胺、吡啶、氢氧化钠、氢氧化钾中的任一种。
步骤3,混合Salen-H6-2DPCP、溶剂3,并逐滴滴加金属盐水溶液,在惰性气体保护下30℃搅拌反应4h,对生成的沉淀依次进行减压过滤、溶剂3洗涤、真空干燥,得到具有希夫碱结构的金属离子阻燃络合物,即Salen-DPCP-M;
其中,所述溶剂3是苯、甲苯、二氯甲烷、三氯甲烷、四氢呋喃、丙酮、丁酮、N,N-二甲基甲酰胺、乙醇、甲醇、乙腈、异丙醇中的一种。
其中,所述金属盐为硝酸镍(Ⅱ)、硝酸锌(Ⅱ)、硝酸亚铁(Ⅱ)、硝酸铜(Ⅱ)、硝酸锰(Ⅱ)、醋酸镍(Ⅱ)、醋酸锌(Ⅱ)、醋酸铜(Ⅱ)、醋酸锰(Ⅱ)、醋酸亚铁(Ⅱ)、氯化铁(Ⅲ)、氯化亚铁(Ⅱ)、氯化铜(Ⅱ)中的任一种。
其中,所述步骤1~步骤3中的惰性气体为氩气、氦气、氮气中的一种。
对比现有技术,本发明的有益效果在于:
该络合物因为有salen希夫碱结构,具有交联抗熔滴特性。同时,该阻燃剂含有有机磷与金属,不仅可在凝聚相发挥协同阻燃作用,磷组分也可在气相发挥中断气相自由基反应的气相阻燃效果。该系列阻燃剂具有无卤、环境友好等特点,而且在制备阻燃复合材料时只需简单的共混即可,制备工艺简单。
附图说明
附图1是本发明Salen-DPCP-M的合成工艺路线(其中,二羟基苯甲醛以2,4- 二羟基苯甲醛为例,金属盐以硝酸镍为例)。
附图2为Salen-DPCP-Ni的1H-NMR(其中,二羟基苯甲醛以2,4-二羟基苯甲醛为例,金属盐以硝酸镍为例)。
附图3为Salen-DPCP-Ni的实物照片(其中,二羟基苯甲醛以2,4-二羟基苯甲醛为例,金属盐以硝酸镍为例)。
具体实施方式
下面结合具体实施例,进一步阐述本发明。应理解,这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解,在阅读了本发明讲授的内容之后,本领域技术人员可以对本发明作各种改动或修改,这些等价形式同样落于本申请所限定的范围。
实施例1:具有希夫碱结构的金属离子阻燃络合物
结构式如下
其中,
其中,M为金属离子份,具体是Cu、Fe。
实施例2:具有希夫碱结构的金属离子阻燃络合物
结构式如下
其中,
其中,M为金属离子份,具体是Ni、Zn。
实施例3:
在装有搅拌、加热、控温装置的反应容器中加入2.0mol 2,4-二羟基苯甲醛、乙醇、1.0mol乙二胺,加料完毕后在氮气保护下30℃搅拌反应12h;将黄色沉淀减压过滤、乙醇洗涤、真空烘箱干燥,得到中间产物N,N′-双(2,4-二羟基亚水样基)-1,2-乙二胺(Salen-H6);再在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-H6、2.3mol三乙胺、二氯甲烷,在0℃条件下将2.3mol 氯磷酸二苯酯(DPCP)滴加进体系,加料完毕后在氮气保护下30℃搅拌反应6h;减压蒸干二氯甲烷,用二氯甲烷萃取3次,有机相用去离子水洗3次,减压蒸干二氯甲烷得到黄色液体;利用柱层析体积比V/V石油醚:乙酸乙酯=1:1或体积比V/V二氯甲烷:甲醇=20:1分离提纯产品,黄色液体即为N,N′-双(2-羟基-4 (磷酸二苯酯基)亚水样基)-1,2-乙二胺(Salen-H6-2DPCP);最后,在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-DPCP、乙醇,再将1.0mol Ni(NO3)2·6H2O水溶液逐滴滴入体系,惰性气体保护下30℃搅拌反应4h有黄色沉淀生成,减压过滤、乙醇洗涤、真空烘箱干燥,得到N,N′-双(2-羟基-4(磷酸二苯酯基)亚水样基)-1,2-乙二胺合镍(Salen-DPCP-Ni)。
实施例4:
在装有搅拌、加热、控温装置的反应容器中加入2.3mol 2,4-二羟基苯甲醛、乙醇、1.0mol乙二胺,加料完毕后在氮气保护下30℃搅拌反应12h;将黄色沉淀减压过滤、乙醇洗涤、真空烘箱干燥,得到中间产物N,N′-双(2,4-二羟基亚水样基)-1,2-乙二胺(Salen-H6);再在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-H6、5.2mol三乙胺、二氯甲烷,在0℃条件下将2.6mol 氯磷酸二苯酯(DPCP)滴加进体系,加料完毕后在氮气保护下30℃搅拌反应6h;减压蒸干二氯甲烷,用二氯甲烷萃取3次,有机相用去离子水洗3次,减压蒸干二氯甲烷得到黄色液体;利用柱层析体积比V/V石油醚:乙酸乙酯=1:1或体积比V/V二氯甲烷:甲醇=20:1分离提纯产品,黄色液体即为N,N′-双(2-羟基-4 (磷酸二苯酯基)亚水样基)-1,2-乙二胺(Salen-H6-2DPCP);最后,在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-DPCP、乙醇,再将1.3mol Ni(NO3)2·6H2O水溶液逐滴滴入体系,惰性气体保护下30℃搅拌反应4h有黄色沉淀生成,减压过滤、乙醇洗涤、真空烘箱干燥,得到N,N′-双(2-羟基-4(磷酸二苯酯基)亚水样基)-1,2-乙二胺合镍(Salen-DPCP-Ni)。
实施例5:
在装有搅拌、加热、控温装置的反应容器中加入2.15mol 2,4-二羟基苯甲醛、乙醇、1.0mol乙二胺,加料完毕后在氮气保护下30℃搅拌反应12h;将黄色沉淀减压过滤、乙醇洗涤、真空烘箱干燥,得到中间产物N,N′-双(2,4- 二羟基亚水样基)-1,2-乙二胺(Salen-H6);再在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-H6、3.7mol三乙胺、二氯甲烷,在0℃条件下将 2.45mol氯磷酸二苯酯(DPCP)滴加进体系,加料完毕后在氮气保护下30℃搅拌反应6h;减压蒸干二氯甲烷,用二氯甲烷萃取3次,有机相用去离子水洗3次,减压蒸干二氯甲烷得到黄色液体;利用柱层析体积比V/V石油醚:乙酸乙酯=1:1 或体积比V/V二氯甲烷:甲醇=20:1分离提纯产品,黄色液体即为N,N′-双(2- 羟基-4(磷酸二苯酯基)亚水样基)-1,2-乙二胺(Salen-H6-2DPCP);最后,在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-DPCP、乙醇,再将 1.15mol Ni(NO3)2·6H2O水溶液逐滴滴入体系,惰性气体保护下30℃搅拌反应 4h有黄色沉淀生成,减压过滤、乙醇洗涤、真空烘箱干燥,得到N,N′-双(2- 羟基-4(磷酸二苯酯基)亚水样基)-1,2-乙二胺合镍(Salen-DPCP-Ni)。
实施例6:
在装有搅拌、加热、控温装置的反应容器中加入2.0mol 2,4-二羟基苯甲醛、乙醇、1.0mol乙二胺,加料完毕后在氮气保护下30℃搅拌反应12h;将黄色沉淀减压过滤、乙醇洗涤、真空烘箱干燥,得到中间产物N,N′-双(2,4-二羟基亚水样基)-1,2-乙二胺(Salen-H6);再在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-H6、2.3mol三乙胺、二氯甲烷,在0℃条件下将2.3mol 氯磷酸二苯酯(DPCP)滴加进体系,加料完毕后在氮气保护下30℃搅拌反应6h;减压蒸干二氯甲烷,用二氯甲烷萃取3次,有机相用去离子水洗3次,减压蒸干二氯甲烷得到黄色液体;利用柱层析体积比V/V石油醚:乙酸乙酯=1:1或体积比V/V二氯甲烷:甲醇=20:1分离提纯产品,黄色液体即为N,N′-双(2-羟基-4 (磷酸二苯酯基)亚水样基)-1,2-乙二胺(Salen-H6-2DPCP);最后,在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-DPCP、乙醇,再将1.0mol Zn(CH3COO)2·2H2O水溶液逐滴滴入体系,惰性气体保护下30℃搅拌反应4h有黄色沉淀生成,减压过滤、乙醇洗涤、真空烘箱干燥,得到N,N′-双(2-羟基-4 (磷酸二苯酯基)亚水样基)-1,2-乙二胺合锌(Salen-DPCP-Zn)。
实施例7:
在装有搅拌、加热、控温装置的反应容器中加入2.3mol 2,4-二羟基苯甲醛、乙醇、1.0mol乙二胺,加料完毕后在氮气保护下30℃搅拌反应12h;将黄色沉淀减压过滤、乙醇洗涤、真空烘箱干燥,得到中间产物N,N′-双(2,4-二羟基亚水样基)-1,2-乙二胺(Salen-H6);再在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-H6、5.2mol三乙胺、二氯甲烷,在0℃条件下将2.6mol 氯磷酸二苯酯(DPCP)滴加进体系,加料完毕后在氮气保护下30℃搅拌反应6h;减压蒸干二氯甲烷,用二氯甲烷萃取3次,有机相用去离子水洗3次,减压蒸干二氯甲烷得到黄色液体;利用柱层析体积比V/V石油醚:乙酸乙酯=1:1或体积比V/V二氯甲烷:甲醇=20:1分离提纯产品,黄色液体即为N,N′-双(2-羟基-4 (磷酸二苯酯基)亚水样基)-1,2-乙二胺(Salen-H6-2DPCP);最后,在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-DPCP、乙醇,再将1.3mol Zn(CH3COO)2·2H2O水溶液逐滴滴入体系,惰性气体保护下30℃搅拌反应4h有黄色沉淀生成,减压过滤、乙醇洗涤、真空烘箱干燥,得到N,N′-双(2-羟基-4 (磷酸二苯酯基)亚水样基)-1,2-乙二胺合锌(Salen-DPCP-Zn)。
实施例8:
在装有搅拌、加热、控温装置的反应容器中加入2.15mol 2,4-二羟基苯甲醛、乙醇、1.0mol乙二胺,加料完毕后在氮气保护下30℃搅拌反应12h;将黄色沉淀减压过滤、乙醇洗涤、真空烘箱干燥,得到中间产物N,N′-双(2,4- 二羟基亚水样基)-1,2-乙二胺(Salen-H6);再在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-H6、3.7mol三乙胺、二氯甲烷,在0℃条件下将 2.45mol氯磷酸二苯酯(DPCP)滴加进体系,加料完毕后在氮气保护下30℃搅拌反应6h;减压蒸干二氯甲烷,用二氯甲烷萃取3次,有机相用去离子水洗3次,减压蒸干二氯甲烷得到黄色液体;利用柱层析体积比V/V石油醚:乙酸乙酯=1:1 或体积比V/V二氯甲烷:甲醇=20:1分离提纯产品,黄色液体即为N,N′-双(2- 羟基-4(磷酸二苯酯基)亚水样基)-1,2-乙二胺(Salen-H6-2DPCP);最后,在装有搅拌、加热、控温装置的反应容器中加入1.0mol Salen-DPCP、乙醇,再将 1.15mol Zn(CH3COO)2·2H2O水溶液逐滴滴入体系,惰性气体保护下30℃搅拌反应4h有黄色沉淀生成,减压过滤、乙醇洗涤、真空烘箱干燥,得到N,N′-双(2- 羟基-4(磷酸二苯酯基)亚水样基)-1,2-乙二胺合锌(Salen-DPCP-Zn)。
实施例9:
纯环氧树脂及加入该阻燃剂的环氧树脂制备及阻燃性能测试如下(其中,二羟基苯甲醛以2,4-二羟基苯甲醛为例):
(1)纯环氧树脂制备
称取60g环氧树脂(E51)在120℃搅拌10分钟,加入13g 4,4′-二氨基二苯甲烷(DDM)搅拌均匀后倒入聚四氟乙烯模具中,然后140℃固化6小时固化成型,即得到纯环氧树脂材料(命名:EP)。
(2)阻燃环氧树脂制备
称取60g环氧树脂(E51)在120℃搅拌10分钟,先加入8.11g通过上述实施例3-8所制得的阻燃络合物,搅拌均匀,获得八组混合树脂原料,再加入13g 4,4′-二氨基二苯甲烷(DDM)搅拌,倒入聚四氟乙烯模具中,然后140℃固化 6小时固化成型,即得到质量分数3%的阻燃环氧树脂材料(命名:10% Salen-DPCP-M/EP)。
(3)阻燃性能测试
根据ISO 5660-1标准采用锥形量热仪对阻燃材料进行阻燃性能测试,具体测试结果见表1,测试结果与本课题组单纯磷系阻燃剂作比较(Yang B,Li X, Wang L,et al.Anefficient flame retardant for epoxy resin:Preparation and pyrolytic behaviour[J].High Performance Polymers,2018: 0954008318815730.)。结果表明本发明阻燃剂的添加量更少,而总热释放量 (THR)降幅更大。极限氧指数(LOI,依照标准:ASTMD2863-97)与垂直燃烧等级(UL-94,依照标准:ASTM D3801)测试结果也较环氧树脂有很大提升:
表1阻燃剂Salen-DPCP-Ni对环氧树脂的阻燃性能测试结果
表1阻燃剂Salen-DPCP-M对环氧树脂的阻燃性能测试结果。
Claims (10)
1.具有希夫碱结构的金属离子阻燃络合物,其特征在于,结构式如Ⅰ所示,
式Ⅰ:
其中,
R是:且R能够位于芳环上其余四处的任一位置;
M为金属离子,选自Ni(Ⅱ)、Zn(Ⅱ)、Cu(Ⅱ)、Fe(Ⅲ)、Mn(Ⅱ)中的任一种。
2.如权利要求1所述的具有希夫碱结构的金属离子阻燃络合物,其特征在于,是以乙二胺、二羟基苯甲醛、氯磷酸二苯酯为络合剂,与金属盐络合得到的,中心离子是金属M,而配体是有机磷与希夫碱结构的阻燃络合物Salen-DPCP-M,
其络合剂按物质的量计比例为:
乙二胺 1份;
二羟基苯甲醛 2.0~2.3份;
氯磷酸二苯酯 2.3~2.6份;
氯磷酸二苯酯与缚酸剂的物质的量比为1:1.0~2.0;
反应获得中间产物Salen-H6-2DPCP,Salen-H6-2DPCP与金属盐的物质的量比为1:1.0~1.3。
3.如权利要求2所述的具有希夫碱结构的金属离子阻燃络合物,其特征在于,通过以下方法制得:
步骤1,将二羟基苯甲醛、溶剂1、乙二胺混合,并在惰性气体保护下30℃搅拌反应12h,过滤得到黄色沉淀,所述黄色沉淀依次经过减压过滤、溶剂1洗涤、真空干燥后,得到中间产物N,N′-双(二羟基亚水样基)-1,2-乙二胺,即Salen-H6;
其中,所述溶剂1为甲醇、乙醇、季戊四醇中的一种;
步骤2,混合Salen-H6、缚酸剂、溶剂2,并在0℃条件下滴加氯磷酸二苯酯,在惰性气体保护下30℃搅拌反应6h,减压蒸干溶剂2后,依次使用二氯甲烷萃取3次,有机相用去离子水洗3次,再减压蒸干二氯甲烷得到黄色液体,分离提纯后,得到N,N′-双(2-羟基-(磷酸二苯酯基)亚水样基)-1,2-乙二胺,即Salen-H6-2DPCP;
其中,所述溶剂2是苯、甲苯、二甲苯、二氯甲烷、三氯甲烷、四氢呋喃、丙酮、丁酮、N,N-二甲基甲酰胺中的一种;
步骤3,混合Salen-H6-2DPCP、溶剂3,并逐滴滴加金属盐水溶液,在惰性气体保护下30℃搅拌反应4h,对生成的沉淀依次进行减压过滤、溶剂3洗涤、真空干燥,得到具有希夫碱结构的金属离子阻燃络合物,即Salen-DPCP-M;
其中,所述溶剂3是苯、甲苯、二氯甲烷、三氯甲烷、四氢呋喃、丙酮、丁酮、N,N-二甲基甲酰胺、乙醇、甲醇、乙腈、异丙醇中的一种。
4.如权利要求2所述的具有希夫碱结构的金属离子阻燃络合物,其特征在于,所述缚酸剂为三乙胺、吡啶、氢氧化钠、氢氧化钾中的任一种。
5.如权利要求3所述的具有希夫碱结构的金属离子阻燃络合物,其特征在于,所述步骤1中,所述二羟基苯甲醛为2,3-二羟基苯甲醛、2,4-二羟基苯甲醛、2,5-二羟基苯甲醛、2,6-二羟基苯甲醛中的一种;
和/或
所述步骤3中,所述金属盐为硝酸镍(Ⅱ)、硝酸锌(Ⅱ)、硝酸亚铁(Ⅱ)、硝酸铜(Ⅱ)、硝酸锰(Ⅱ)、醋酸镍(Ⅱ)、醋酸锌(Ⅱ)、醋酸铜(Ⅱ)、醋酸锰(Ⅱ)、醋酸亚铁(Ⅱ)、氯化铁(Ⅲ)、氯化亚铁(Ⅱ)、氯化铜(Ⅱ)中的任一种。
6.如权利要求3所述的具有希夫碱结构的金属离子阻燃络合物,其特征在于,所述步骤1~步骤3中的惰性气体为氩气、氦气、氮气中的一种。
7.如权利要求3所述的具有希夫碱结构的金属离子阻燃络合物,其特征在于,所述步骤2中的分离提纯,是指利用柱层析体积比V/V石油醚:乙酸乙酯=1:1或体积比V/V二氯甲烷:甲醇=20:1对黄色液体进行分离提纯。
8.如权利要求1-7任一项具有希夫碱结构的金属离子阻燃络合物的制备方法,其特征在于,是以乙二胺、二羟基苯甲醛、氯磷酸二苯酯为络合剂,与金属盐络合得到的,其络合剂按物质的量计比例为:
乙二胺 1份;
二羟基苯甲醛 2.0~2.3份;
氯磷酸二苯酯 2.3~2.6份;
氯磷酸二苯酯与缚酸剂的物质的量比为1:1.0~2.0;
反应获得中间产物Salen-H6-2DPCP,Salen-H6-2DPCP与金属盐的物质的量比为1:1.0~1.3;
所述缚酸剂为三乙胺、吡啶、氢氧化钠、氢氧化钾中的任一种。
9.如权利要求8所述的具有希夫碱结构的金属离子阻燃络合物的制备方法,其特征在于,通过以下方法制得:
步骤1,将二羟基苯甲醛、溶剂1、乙二胺混合,并在惰性气体保护下30℃搅拌反应12h,过滤得到黄色沉淀,所述黄色沉淀依次经过减压过滤、溶剂1洗涤、真空干燥后,得到中间产物N,N′-双(二羟基亚水样基)-1,2-乙二胺,即Salen-H6;
其中,所述溶剂1为甲醇、乙醇、季戊四醇中的一种;
步骤2,混合Salen-H6、缚酸剂、溶剂2,并在0℃条件下滴加氯磷酸二苯酯,在惰性气体保护下30℃搅拌反应6h,减压蒸干溶剂2后,依次使用二氯甲烷萃取3次,有机相用去离子水洗3次,再减压蒸干二氯甲烷得到黄色液体,分离提纯后,得到N,N′-双(2-羟基-(磷酸二苯酯基)亚水样基)-1,2-乙二胺,即Salen-H6-2DPCP;
其中,所述溶剂2是苯、甲苯、二甲苯、二氯甲烷、三氯甲烷、四氢呋喃、丙酮、丁酮、N,N-二甲基甲酰胺中的一种;
步骤3,混合Salen-H6-2DPCP、溶剂3,并逐滴滴加金属盐水溶液,在惰性气体保护下30℃搅拌反应4h,对生成的沉淀依次进行减压过滤、溶剂3洗涤、真空干燥,得到具有希夫碱结构的金属离子阻燃络合物,即Salen-DPCP-M;
其中,所述溶剂3是苯、甲苯、二氯甲烷、三氯甲烷、四氢呋喃、丙酮、丁酮、N,N-二甲基甲酰胺、乙醇、甲醇、乙腈、异丙醇中的一种。
10.如权利要求9所述的具有希夫碱结构的金属离子阻燃络合物的制备方法,其特征在于,通过以下方法制得:
所述步骤1中,所述二羟基苯甲醛为2,3-二羟基苯甲醛、2,4-二羟基苯甲醛、2,5-二羟基苯甲醛、2,6-二羟基苯甲醛中的一种;
和/或
所述步骤3中,所述金属盐为硝酸镍(Ⅱ)、硝酸锌(Ⅱ)、硝酸亚铁(Ⅱ)、硝酸铜(Ⅱ)、硝酸锰(Ⅱ)、醋酸镍(Ⅱ)、醋酸锌(Ⅱ)、醋酸铜(Ⅱ)、醋酸锰(Ⅱ)、醋酸亚铁(Ⅱ)、氯化铁(Ⅲ)、氯化亚铁(Ⅱ)、氯化铜(Ⅱ)中的任一种;
和/或
所述步骤1~步骤3中的惰性气体为氩气、氦气、氮气中的一种;
和/或
所述步骤2中的分离提纯,是指利用柱层析体积比V/V石油醚:乙酸乙酯=1:1或体积比V/V二氯甲烷:甲醇=20:1对黄色液体进行分离提纯。