CN1083769A - 刚塑复合头枕的制造方法及其设备 - Google Patents
刚塑复合头枕的制造方法及其设备 Download PDFInfo
- Publication number
- CN1083769A CN1083769A CN 93108811 CN93108811A CN1083769A CN 1083769 A CN1083769 A CN 1083769A CN 93108811 CN93108811 CN 93108811 CN 93108811 A CN93108811 A CN 93108811A CN 1083769 A CN1083769 A CN 1083769A
- Authority
- CN
- China
- Prior art keywords
- epidermis
- heat seal
- steel
- mould
- high frequency
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
刚塑复合头枕的制作方法及其设备,本发明为座
椅头枕新的生产方法和设备,它先在专用的注射模具
上把软性塑料注射成外壁封闭、内壁开口的内腔表皮
(1),再将预制好的刚性中心骨架(7、8)放入头枕表皮
(1)内腔中,然后用高频热合模具将表皮内腔内缘开
口部分高频热合,最后放入发泡模具内将高回弹聚氨
酯注入表皮内腔中发泡定型。此方法工艺简便,设备
简单、操作容易,便于产品的花色品种快速调换,对提
高产品质量、外观和生产效率有显著效果。
Description
本发明涉及一种头枕的制作方法及其设备,特别是一种座椅头枕的生产方法及其专用设备。
现有座椅头枕,如汽车座椅头枕,由中心骨架外包高弹海绵体,海绵体外用表面修饰膜包围,其制造方法一般是先制成中心骨架,把中心骨架置于模具中,将发泡塑料注入模具中发泡成型,将此发泡成型件再包裹上表面修饰膜,如包塑料膜或皮革制品等,此种制作方法的缺陷是表皮接缝较多,影响外观和内在质量,且附属的缝合工具设备较多,品种多、批量少时,生产成本较高。国外也有采用先制作枕皮,后置刚性骨架,再发泡定型的方法,采用吹塑或搪塑工艺制造枕皮,设备要求高,工艺条件复杂,难于保证质量。CN1048814A公开一种模塑复合品制造方法,所生产的产品包括底板、中间支撑物和表面,但无弹性不适合座椅头枕生产要求。
本发明目的是针对上述生产座椅头枕工艺和设备所存在问题,设计一种工艺简单、设备少,适合品种多、批量小的企业生产出成本低廉外观和质量都达到用户要求的产品。
本发明采用下述方案实现上述目标:
一种刚塑复合头枕的制作方法,其特征在于:用注射成型将塑料制作成外壁封闭的软性表皮,将刚性骨架置于所述表皮内,用高频热合模将表面内壁热合形成内腔,将所述成型的内腔表皮置于发泡模具内,在所述内腔中注入发泡材料及引发剂等混合物,升温发泡,保温定型。
一种制造塑复合头枕的设备,它包括制造软性表皮的注塑模具、热合表皮内壁缝线的高频热合模具和发泡定型模具,其特征在于表皮注射成型模具由定模型腔、模芯、动模型腔、导向杆和连杆组成,模芯通过导向杆、顶杆与动模腔定位紧固,连杆一端与模芯活接,连杆另一端与动模型腔的中下部固接,在动、定模腔分离后,推动顶杆,模芯被推出动模腔,并定位在适当位置。
上述方案的优点在于设备简单、制作容易,与国外常规采用的吹塑或搪塑法制作无缝线枕皮相比,节省大量设备和资金投入。制作工艺简化,普通注射机采用常规注射工艺即可实现保质保量的枕皮生产。注塑模、高频热合模和发泡模的模腔基本相似,因此模具设计制作也简化。品种翻新时,只要上述3付模具调换即可实现品种调换,生产效率显著提高,对提高产品质量和外观效果显著。
图1为座椅头枕结构示意图。
图2为图1的A-A剖面视图。
图3为制作座椅头枕表皮专用模具结构示意图。
图4为高频热合模具主视图及部分剖面图。
图5为高频热合模具的下模腔俯视图。
以下结合附图描述本发明实施例结构和设备。
座椅头枕一般为接插式,可常见于美容座椅、牙科座椅和汽车座椅头枕,如图1、2所示,中心骨架(7、8)外包围高弹性物(9),高弹性物外包裹表皮(1),现在大批量生产的表皮(1)都为软性塑料,如聚氯乙烯膜、聚乙烯或聚丙烯膜、聚丙烯酸脂膜,高弹性物一般采用聚氨脂发泡混合材料,中心骨架(7、8)制成
形,可用圆钢、铜、铝、锌或它们的合金,骨架的两只脚为头枕的插脚(4),图1、2中,还有凸起的枕臂(2)和不凸起的枕脚(3),插脚(4)上有缺口(5)它与座椅内插口的弹性扣相配合,加固头枕作用。软性表皮分二步接合缝线,头枕外边缘四周有内凹的装饰缝线(10),它是由模具的凸起部分形成的,并不是缝合线。头枕内边缘为高频热合缝线。
生产座椅头枕表皮的设备由注射机及其专用模具组成,注射机为常用螺杆式设备,容量500g以内,注射压力50~100kg即可使用。注射的塑料模具(图3所示),则是专门设计的,它由定模腔(21)、模芯(22)和动模腔(24)组成,定模腔(21)和动模腔(24)之间4个导柱(27)定位合模和固紧,定位圈(20)用于锁模。模芯(22)通过连杆(23)与动模腔(24)相连,连杆(23)一端与模芯(22)活接,另一端与动模腔(24)固接,模芯(22)沿着连杆(23)平行移动,或离开动模腔(24),或与动模腔(24)合拢。当模芯(22)与动模腔(24)合拢时由导向杆(25)定位和固紧,顶杆(26)穿过动模腔(24)后,与注射机液压顶杆相连,可将模芯(22)顶出。
高频热合机是由产生高频的电源和高频热合模具(图4、5)组成,高频电源容量为30KVA,高频输出功率为15KVA,振荡频率为27MHZ,三相全波硅整流桥式整流器,调谐器包括板式可变电容器和电动机传动件。高频热合模具由上模腔(35)、下模腔(36)组成,上、下模腔之间由导柱(31)定位并紧固,在模腔内凹(38)部分与模腔凸起(37)边缘(与头枕表皮内腔边缘相对应)布置电极(32、33),电极与高频电源相接(图4、5未描出)。固定架(39)用于固定中心骨架的脚架(4)。
以下结合附图描述利用上述设备制作座椅头枕的工艺过程。
表皮制作过程,用软性塑料PVC(聚氯乙烯)着色造粒备用,表皮模具为钢模,模腔壁刻各种装饰花纹,采用螺杆式注射机,料筒加热温度150℃~180℃,注射压力50~100kg,保压压力40~80kg,保压时间5~10秒,冷却时间5~10秒,成型周期2分种左右。打开模腔,将动模腔(24)开启至合适位置,再将模芯(22)顶向动模腔(24)和定模腔(21)中间位置,取出注塑成型的头枕表皮(1),把模芯(22)推回动模腔(24)原始位置,定位紧固,然后合模,锁模,完成一个工作周期。
中心骨架制作,以汽车座椅头枕为例,可采用Φ10圆钢,在专用工夹模具上弯曲成冂型,两插脚(4)上的横条用焊接法固接于插脚(4)上,并在插脚(4)上加工定位扣缺口(6),然后表面镀铬。若用不锈钢或其他合金线材,可不必表面电镀。
将已制作好的上述中心骨架(7、8)置于上述已制作好的注塑表皮内腔中,然后将已放置过中心骨架的表皮放于高频热合模具上,合拢上、下模腔(35、36),使表皮(1)内腔边缘被热合模具凸起部压紧,即为电极(32、33)压紧,通高频电源进行常规高频热合,然后冷却、开模、取出热合件,切除毛边。
将上述的热合成品放入发泡模具内,定位、锁模,再将混合均匀冷熟化的聚胺酯经过浇入口(5)注入表皮(1)内,进行发泡8~15分钟,模温控制20~40℃,发泡完成后,开模取出成品,除毛刺修整、检验合格,即完成整个座椅头枕生产过程。
Claims (6)
1、一种刚塑复合头枕的制造方法,其特征在于:
a.用注射成型将塑料制作成外壁封闭的软性表皮(1);
b.将刚性骨架(7、8)置于所述的表皮(1)内;
c.用高频热合模具将所述的表皮(1)内壁热合,形成内腔;
d.将所述内腔的表皮置于发泡模具内,在所述内腔中注入发泡材料、引发剂等混合物,升温发泡,保温定型。
2、如权利要求1所述的刚塑复合头枕的制造方法,其特征在于软性表皮分二步接合缝线,表皮外壁封闭线在注射机注射模具上直接成凹形接合线(10),中心骨架(18)置入表皮(1)后再在高频热合机热合模具上将表皮内壁开口进行高频热合。
3、如权利要求1或2所述的刚塑复合头枕的制造方法,其特征在于注射成型枕皮的料筒加热温度为150~180℃,注射压力50~100公斤,保压压力40~80公斤,保压时间5~10秒。
4、如权利要求1所述的刚塑复合头枕的制造方法,其特征在于中心骨架(7、8)先弯曲成冂型,两插脚(4)上的横条用焊接法固接于插脚(4)上,并在插脚(4)上加工定位扣缺口(6)。
5、一种制造刚塑复合头枕的设备,它包括制造软性表皮的注射模具,热合表皮内壁缝线的高频热合模具和发泡定型模具,其特征在于表皮注射模具由定模型腔(21)、模芯(22)、动模(24)、导向杆(25)和连杆(23)组成。模芯(22)通过导向杆(25)、顶杆(26)与动模腔(24)定位紧固,连杆一端与模芯(22)活接,连杆(23)另一端与动模型腔(24)的中下部固接,在动、定模腔分离后,推动顶杆(23)、模芯(22)被推出动模腔(24),并定位在适当的位置。
6、如权利要求5所述的刚塑复合头枕的制造方法,其特征在于高频热合模具由上模腔(35)、下模腔(36)组成,上、下模腔之间由导柱(31)定位并紧固,在模腔内凹(38)部分与模腔凸起(37)部分的边缘布置电极(32、33)。