CN108298816A - 一种陶瓷坯釉料及其制作方法 - Google Patents
一种陶瓷坯釉料及其制作方法 Download PDFInfo
- Publication number
- CN108298816A CN108298816A CN201810306674.2A CN201810306674A CN108298816A CN 108298816 A CN108298816 A CN 108298816A CN 201810306674 A CN201810306674 A CN 201810306674A CN 108298816 A CN108298816 A CN 108298816A
- Authority
- CN
- China
- Prior art keywords
- glaze
- white
- ceramic blank
- soil
- feldspar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种陶瓷坯釉料,包括白色釉料、红色釉料、棕色釉料以及玻化砖釉料,所述白色釉料分为传统白、改良白以及综合白,该发明一种陶瓷坯釉料及其制作方法,采用石英、长石、紫木节、大同砂石、章村土、叶蜡石、桃红土、混合粘土、紫木节、仓后土、红岗泥、青草岭、高岭土、红泥、绢英岩等一些基础的原理,即可制成适用于不同颜色的陶瓷坯釉料,适用于各种陶瓷的表面着色处理使用,同时经济成本及其低廉。
Description
技术领域
本发明涉及陶瓷材料的制备方法,具体为一种陶瓷坯釉料及其制作方法。
背景技术
建筑卫生陶瓷行业非常注重采用先进的釉料技术,国内已经出现一大批专业性很强的陶瓷釉料和陶瓷熔块、色料公司。建筑卫生陶瓷产品中所用的釉料越来越丰富多样,目前多数陶企使用的釉料产品,类别与用途可以大致分类如下:1、铅釉和无铅釉;2、生料釉与熔块釉;3、一次烧成或二次烧成用釉;4、瓷砖,餐具,卫生陶瓷与电瓷用釉;5、按施釉方法划分的浸釉、喷釉、浇釉;6、高温釉和低温釉;7、高膨胀釉和低膨胀釉;8、烧成气氛氧化焰、中性焰和还原焰;9、颜色釉与无色釉;10、透明釉与乳浊釉;11、光泽釉、无光釉、半无光釉或花纹釉等等。
现有的陶瓷釉料经济成本高,且原料复杂。
发明内容
本发明的目的在于提供一种陶瓷坯釉料及其制作方法,以解决上述背景技术中提出的问题。
本发明的目的是通过下述技术方案予以实现:一种陶瓷坯釉料,包括白色釉料、红色釉料、棕色釉料以及玻化砖釉料,所述白色釉料分为传统白、改良白以及综合白,传统白的白色釉料的配方按重百分比为石英:25%,长石:35%,紫木节:10%,大同砂石:10%,章村土:10%;改良白的白色釉料的配方按重百分比为石英:35%,长石:26%,叶蜡石:18%,桃红土:2%,混合粘土:21%;综合白的白色釉料的配方按重百分比为白砂石:40%,长石:25%,紫木节:10%,大同砂石:5% 章村土:20%。
本发明中,所述红色釉料的配方按重百分比为石英:15%,长石:5%,仓后土:32%,红岗泥:33%,青草岭:15%。
本发明中,所述棕色釉料的配方按重百分比为石英:15%,长石:15%,高岭土:30%,红泥:40%。
本发明中,所述玻化砖釉料的配方按重百分比为石英24%,长石13%,叶蜡石:16%,绢英岩:30%,紫木节:7%,粘土:10%。
本发明中一种陶瓷坯釉料的制作方法,具体步骤如下:
步骤1:将上的釉料的各组成原料放入搅拌机中充分搅拌直至完全混合;
步骤2:将步骤1中混合的釉原料加入球磨机中,并加入水,得到釉料原料,将釉料原料放入筛布中过滤,同时加入湿式磁选机中除去铁杂质,然后送入烘干机中进行充分烘干;
步骤3:将步骤2中烘干成块的釉料块加入精密粉碎机中进行粉碎,并通过筛网进行筛选去杂质,即可得到陶瓷坯釉料。
本发明的有益效果是:该发明一种陶瓷坯釉料及其制作方法,采用石英、长石、紫木节、大同砂石、章村土、叶蜡石、桃红土、混合粘土、紫木节、仓后土、红岗泥、青草岭、高岭土、红泥、绢英岩等一些基础的原理,即可制成适用于不同颜色的陶瓷坯釉料,适用于各种陶瓷的表面着色处理使用,同时经济成本及其低廉。
具体实施方式
下面结合具体实施方式进一步的说明,但是下文中的具体实施方式不应当做被理解为对本体发明的限制。本领域普通技术人员能够在本发明基础上显而易见地作出的各种改变和变化,应该均在发明的范围之内。
一种陶瓷坯釉料,包括白色釉料、红色釉料、棕色釉料以及玻化砖釉料,所述白色釉料分为传统白、改良白以及综合白,传统白的白色釉料的配方按重百分比为石英:25%,长石:35%,紫木节:10%,大同砂石:10%,章村土:10%;改良白的白色釉料的配方按重百分比为石英:35%,长石:26%,叶蜡石:18%,桃红土:2%,混合粘土:21%;综合白的白色釉料的配方按重百分比为白砂石:40%,长石:25%,紫木节:10%,大同砂石:5% 章村土:20%。
本发明中,所述红色釉料的配方按重百分比为石英:15%,长石:5%,仓后土:32%,红岗泥:33%,青草岭:15%。
本发明中,所述棕色釉料的配方按重百分比为石英:15%,长石:15%,高岭土:30%,红泥:40%。
本发明中,所述玻化砖釉料的配方按重百分比为石英24%,长石13%,叶蜡石:16%,绢英岩:30%,紫木节:7%,粘土:10%。
本发明中一种陶瓷坯釉料的制作方法,具体步骤如下:
步骤1:将上的釉料的各组成原料放入搅拌机中充分搅拌直至完全混合;
步骤2:将步骤1中混合的釉原料加入球磨机中,并加入水,得到釉料原料,将釉料原料放入筛布中过滤,同时加入湿式磁选机中除去铁杂质,然后送入烘干机中进行充分烘干;
步骤3:将步骤2中烘干成块的釉料块加入精密粉碎机中进行粉碎,并通过筛网进行筛选去杂质,即可得到陶瓷坯釉料。
以上描述仅为本申请的较佳实施例以及对所运用技术原理的说明。本领域技术人员应当理解,本申请中所涉及的发明范围,并不限于上述技术特征的特定组合而成的技术方案,同时也应涵盖在不脱离所述发明构思的情况下,由上述技术特征或其等同特征进行任意组合而形成的其它技术方案。例如上述特征与本申请中公开的(但不限于)具有类似功能的技术特征进行互相替换而形成的技术方案。
Claims (5)
1.一种陶瓷坯釉料,包括白色釉料、红色釉料、棕色釉料以及玻化砖釉料,其特征在于:所述白色釉料分为传统白、改良白以及综合白,传统白的白色釉料的配方按重百分比为石英:25%,长石:35%,紫木节:10%,大同砂石:10%,章村土:10%;改良白的白色釉料的配方按重百分比为石英:35%,长石:26%,叶蜡石:18%,桃红土:2%,混合粘土:21%;综合白的白色釉料的配方按重百分比为白砂石:40%,长石:25%,紫木节:10%,大同砂石:5% 章村土:20%。
2.根据权利要求1所述的一种陶瓷坯釉料,其特征在于:所述红色釉料的配方按重百分比为石英:15%,长石:5%,仓后土:32%,红岗泥:33%,青草岭:15%。
3.根据权利要求1所述的一种陶瓷坯釉料,其特征在于:所述棕色釉料的配方按重百分比为石英:15%,长石:15%,高岭土:30%,红泥:40%。
4.根据权利要求1所述的一种陶瓷坯釉料,其特征在于:所述玻化砖釉料的配方按重百分比为石英24%,长石13%,叶蜡石:16%,绢英岩:30%,紫木节:7%,粘土:10%。
5.根据权利要求1-4任一所述釉料的制作方法,其特征在于:具体步骤如下:
步骤1:将上的釉料的各组成原料放入搅拌机中充分搅拌直至完全混合;
步骤2:将步骤1中混合的釉原料加入球磨机中,并加入水,得到釉料原料,将釉料原料放入筛布中过滤,同时加入湿式磁选机中除去铁杂质,然后送入烘干机中进行充分烘干;
步骤3:将步骤2中烘干成块的釉料块加入精密粉碎机中进行粉碎,并通过筛网进行筛选去杂质,即可得到陶瓷坯釉料。