CN108025925B - 含镍锰的复合氢氧化物及其制造方法 - Google Patents

含镍锰的复合氢氧化物及其制造方法 Download PDF

Info

Publication number
CN108025925B
CN108025925B CN201680052014.5A CN201680052014A CN108025925B CN 108025925 B CN108025925 B CN 108025925B CN 201680052014 A CN201680052014 A CN 201680052014A CN 108025925 B CN108025925 B CN 108025925B
Authority
CN
China
Prior art keywords
positive electrode
manganese
nickel
active material
electrode active
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201680052014.5A
Other languages
English (en)
Chinese (zh)
Other versions
CN108025925A (zh
Inventor
金田治辉
安藤孝晃
牛尾亮三
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Metal Mining Co Ltd
Original Assignee
Sumitomo Metal Mining Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Metal Mining Co Ltd filed Critical Sumitomo Metal Mining Co Ltd
Publication of CN108025925A publication Critical patent/CN108025925A/zh
Application granted granted Critical
Publication of CN108025925B publication Critical patent/CN108025925B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C01G53/80—Compounds containing nickel, with or without oxygen or hydrogen, and containing one or more other elements
    • C01G53/82—Compounds containing nickel, with or without oxygen or hydrogen, and containing two or more other elements
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C01G53/40—Complex oxides containing nickel and at least one other metal element
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C01G53/40—Complex oxides containing nickel and at least one other metal element
    • C01G53/42—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2
    • C01G53/44—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2 containing manganese
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G53/00—Compounds of nickel
    • C01G53/40—Complex oxides containing nickel and at least one other metal element
    • C01G53/42—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2
    • C01G53/44—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2 containing manganese
    • C01G53/50—Complex oxides containing nickel and at least one other metal element containing alkali metals, e.g. LiNiO2 containing manganese of the type (MnO2)n-, e.g. Li(NixMn1-x)O2 or Li(MyNixMn1-x-y)O2
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B1/00—Conductors or conductive bodies characterised by the conductive materials; Selection of materials as conductors
    • H01B1/06—Conductors or conductive bodies characterised by the conductive materials; Selection of materials as conductors mainly consisting of other non-metallic substances
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/50—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese
    • H01M4/505—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/52—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron
    • H01M4/525—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/20—Two-dimensional structures
    • C01P2002/22—Two-dimensional structures layered hydroxide-type, e.g. of the hydrotalcite-type
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/30—Particle morphology extending in three dimensions
    • C01P2004/32—Spheres
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/30—Particle morphology extending in three dimensions
    • C01P2004/40—Particle morphology extending in three dimensions prism-like
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/50—Agglomerated particles
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/51—Particles with a specific particle size distribution
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/11—Powder tap density
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/40—Electric properties
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M2004/026—Electrodes composed of, or comprising, active material characterised by the polarity
    • H01M2004/028—Positive electrodes
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Battery Electrode And Active Subsutance (AREA)
  • Inorganic Compounds Of Heavy Metals (AREA)
CN201680052014.5A 2015-09-30 2016-09-27 含镍锰的复合氢氧化物及其制造方法 Active CN108025925B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2015-193650 2015-09-30
JP2015193650A JP6582824B2 (ja) 2015-09-30 2015-09-30 ニッケルマンガン含有複合水酸化物およびその製造方法
PCT/JP2016/078344 WO2017057311A1 (ja) 2015-09-30 2016-09-27 ニッケルマンガン含有複合水酸化物およびその製造方法

Publications (2)

Publication Number Publication Date
CN108025925A CN108025925A (zh) 2018-05-11
CN108025925B true CN108025925B (zh) 2021-03-02

Family

ID=58427553

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201680052014.5A Active CN108025925B (zh) 2015-09-30 2016-09-27 含镍锰的复合氢氧化物及其制造方法

Country Status (6)

Country Link
US (1) US10553870B2 (enExample)
EP (1) EP3357867B1 (enExample)
JP (1) JP6582824B2 (enExample)
KR (1) KR102553596B1 (enExample)
CN (1) CN108025925B (enExample)
WO (1) WO2017057311A1 (enExample)

Families Citing this family (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109983601B (zh) * 2016-12-28 2022-07-26 松下知识产权经营株式会社 非水电解质二次电池用正极及非水电解质二次电池
JP7114876B2 (ja) * 2017-10-23 2022-08-09 住友金属鉱山株式会社 遷移金属複合水酸化物粒子およびその製造方法、リチウムイオン二次電池用正極活物質およびその製造方法、並びに、リチウムイオン二次電池
US11873234B2 (en) 2017-11-28 2024-01-16 Sumitomo Metal Mining Co., Ltd. Positive electrode active material precursor for non-aqueous electrolyte secondary battery, and method of manufacturing positive electrode active material precursor for non-aqueous electrolyte secondary battery
US11855284B2 (en) 2017-11-28 2023-12-26 Sumitomo Metal Mining Co., Ltd. Positive electrode active material precursor for non-aqueous electrolyte secondary battery
JP7220849B2 (ja) * 2017-12-13 2023-02-13 住友金属鉱山株式会社 ニッケル含有水酸化物およびその製造方法
JP7273260B2 (ja) * 2018-06-20 2023-05-15 住友金属鉱山株式会社 リチウムイオン二次電池用正極活物質とその製造方法およびリチウムイオン二次電池
CN108946827B (zh) * 2018-07-03 2020-09-29 华友新能源科技（衢州）有限公司 一种超小粒径镍钴锰氢氧化物及其制备方法
KR102306547B1 (ko) * 2018-09-14 2021-09-30 주식회사 엘지화학 리튬 이차전지용 양극재의 제조 방법 및 이에 의해 제조된 리튬 이차전지용 양극재
JP6669920B1 (ja) * 2018-09-21 2020-03-18 株式会社田中化学研究所 二次電池用正極活物質及びその製造方法
US12126018B2 (en) 2018-11-23 2024-10-22 Research Institute Of Industrial Science & Technology Positive electrode active material for rechargeable lithium battery, production method therefor and rechargeable lithum battery comprising same
JP7262230B2 (ja) * 2019-01-22 2023-04-21 株式会社田中化学研究所 非水電解質二次電池用複合水酸化物小粒子
EP3793011B1 (en) * 2019-03-29 2024-04-24 JX Metals Corporation Oxide-based positive electrode active material for all-solid-state lithium ion batteries, method for producing precursor of oxide-based positive electrode active material for all-solid-state lithium ion batteries, method for producing oxide-based positive electrode active material for all-solid-state lithium ion batteries, and all-solid-state lithium ion battery
JP7379856B2 (ja) * 2019-04-22 2023-11-15 住友金属鉱山株式会社 ニッケルマンガンコバルト含有複合水酸化物およびその製造方法、リチウムニッケルマンガンコバルト含有複合酸化物およびその製造方法、リチウムイオン二次電池用正極活物質およびその製造方法、並びに、リチウムイオン二次電池
JP7345729B2 (ja) * 2019-06-18 2023-09-19 住友金属鉱山株式会社 遷移金属複合水酸化物の製造方法
JP7255386B2 (ja) * 2019-06-18 2023-04-11 住友金属鉱山株式会社 遷移金属複合水酸化物の製造方法
KR20220043199A (ko) * 2019-08-06 2022-04-05 가부시끼가이샤 다나까 가가꾸 겡뀨쇼 니켈 복합 수산화물 입자, 니켈 복합 수산화물 입자를 전구체로 한 양극 활물질 및 양극 활물질의 제조 방법
CN110921723B (zh) * 2019-12-16 2022-05-27 金驰能源材料有限公司 一种中空型锂离子电池正极材料前驱体的制备方法
PL4080615T3 (pl) * 2020-01-29 2025-03-03 Lg Energy Solution, Ltd. Materiał aktywny elektrody dodatniej dla baterii wielokrotnego ładowania i litowa bateria wielokrotnego ładowania zawierająca taki materiał
CN111600015B (zh) * 2020-07-27 2020-11-13 金驰能源材料有限公司 一种窄分布小粒度球形镍钴锰氢氧化物前驱体及其制备方法
CN114436342B (zh) * 2020-10-31 2024-03-01 华友新能源科技（衢州）有限公司 一种单晶外层包覆氢氧化物的前驱体及其制备方法
CN112919553B (zh) * 2021-01-28 2022-10-18 广东邦普循环科技有限公司 一种正极材料前驱体及其制备方法和应用
CN113479943A (zh) * 2021-07-01 2021-10-08 昆山宝创新能源科技有限公司 三元正极材料前驱体及其制备方法、自动控制进料系统和应用
CN113772743B (zh) * 2021-09-30 2023-06-23 青岛天尧新材料有限公司 一种锰钴复合氧化物粉体的制备方法
CN114204008A (zh) * 2021-11-23 2022-03-18 格林美（江苏）钴业股份有限公司 一种高电压钴酸锂正极材料的制备方法
CN114314695A (zh) * 2022-01-04 2022-04-12 厦门厦钨新能源材料股份有限公司 一种层状多元前驱体及其制备方法与应用
CN115353157B (zh) * 2022-09-20 2024-03-01 宁波容百新能源科技股份有限公司 一种窄粒度分布小粒径镍钴锰三元前驱体、其制备方法及锂离子电池
CN115924990B (zh) * 2022-11-30 2024-04-26 湖南中伟新能源科技有限公司 钠离子电池材料多核前驱体及其制备方法、钠离子电池正极材料、钠离子电池和涉电设备

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6040090A (en) * 1997-04-15 2000-03-21 Sanyo Electric Co., Ltd. Positive electrode material for use in non-aqueous electrolyte battery, process for preparing the same, and non-aqueous electrolyte battery
JP4175026B2 (ja) 2001-05-31 2008-11-05 三菱化学株式会社 リチウム遷移金属複合酸化物及びリチウム二次電池用正極材料の製造方法、リチウム二次電池用正極、並びにリチウム二次電池
JP3827545B2 (ja) 2001-09-13 2006-09-27 松下電器産業株式会社 正極活物質、その製造方法および非水電解質二次電池
JP2003151546A (ja) 2001-11-08 2003-05-23 Nichia Chem Ind Ltd リチウムイオン二次電池用正極活物質及びその製造方法
JP4234418B2 (ja) 2002-12-27 2009-03-04 株式会社田中化学研究所 マンガンニッケル複合水酸化物粒子
JP2008147068A (ja) 2006-12-12 2008-06-26 Ise Chemicals Corp 非水電解液二次電池用リチウム複合酸化物
CN101409342B (zh) * 2008-10-31 2011-12-21 深圳市贝特瑞新能源材料股份有限公司 复合正极材料的制备方法
CN106395918A (zh) * 2009-10-22 2017-02-15 户田工业株式会社 镍-钴-锰类化合物颗粒粉末和锂复合氧化物颗粒粉末及其制造方法和非水电解质二次电池
JP2011113792A (ja) * 2009-11-26 2011-06-09 Nippon Chem Ind Co Ltd リチウム二次電池用正極活物質、その製造方法及びリチウム二次電池
JP5638232B2 (ja) * 2009-12-02 2014-12-10 住友金属鉱山株式会社 非水系電解質二次電池正極活物質用ニッケルコバルトマンガン複合水酸化物粒子とその製造方法、非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池
JP5973128B2 (ja) * 2010-11-29 2016-08-23 住友金属鉱山株式会社 非水系電解質二次電池用正極活物質およびその製造方法、ならびに該正極活物質を用いた非水系電解質二次電池
JP5741932B2 (ja) * 2011-06-01 2015-07-01 住友金属鉱山株式会社 非水系電解質二次電池用正極活物質の前駆体となる遷移金属複合水酸化物とその製造方法、及び非水系電解質二次電池用正極活物質の製造方法
JP5316726B2 (ja) * 2011-06-07 2013-10-16 住友金属鉱山株式会社 ニッケル複合水酸化物とその製造方法、非水系電解質二次電池用正極活物質とその製造方法、および、非水系電解質二次電池
JP2013129589A (ja) * 2011-11-22 2013-07-04 Tanaka Chemical Corp 複合酸化物及びその製造方法、リチウム二次電池用正極、並びにリチウム二次電池
WO2014061399A1 (ja) * 2012-10-15 2014-04-24 日本碍子株式会社 リチウム二次電池用正極活物質及びそれを用いた正極
JP5847352B2 (ja) * 2013-03-04 2016-01-20 三井金属鉱業株式会社 リチウム金属複合酸化物粉体

Also Published As

Publication number Publication date
KR20180059753A (ko) 2018-06-05
US10553870B2 (en) 2020-02-04
US20180316006A1 (en) 2018-11-01
EP3357867B1 (en) 2023-08-30
CN108025925A (zh) 2018-05-11
EP3357867A1 (en) 2018-08-08
EP3357867A4 (en) 2019-01-09
JP2017065975A (ja) 2017-04-06
JP6582824B2 (ja) 2019-10-02
WO2017057311A1 (ja) 2017-04-06
KR102553596B1 (ko) 2023-07-11

Similar Documents

Publication Publication Date Title
CN108025925B (zh) 含镍锰的复合氢氧化物及其制造方法
CN107615531B (zh) 含过渡金属的复合氢氧化物及制造方法、非水电解质二次电池及其正极活性物质及制造方法
JP4915488B1 (ja) ニッケルマンガン複合水酸化物粒子とその製造方法、非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池
KR102203425B1 (ko) 전이 금속 복합 수산화물 입자와 그의 제조 방법, 비수전해질 이차 전지용 정극 활물질과 그의 제조 방법, 및 비수전해질 이차 전지
JP4941617B2 (ja) ニッケル複合水酸化物粒子および非水系電解質二次電池
JP6142929B2 (ja) ニッケルマンガン複合水酸化物粒子とその製造方法、非水電解質二次電池用正極活物質とその製造方法、および非水電解質二次電池
JP5880426B2 (ja) ニッケル複合水酸化物及びその製造方法、並びに正極活物質の製造方法
JP5971109B2 (ja) ニッケル複合水酸化物とその製造方法、非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池
JP5638232B2 (ja) 非水系電解質二次電池正極活物質用ニッケルコバルトマンガン複合水酸化物粒子とその製造方法、非水系電解質二次電池用正極活物質とその製造方法、および非水系電解質二次電池
JP4840545B1 (ja) ニッケル複合水酸化物粒子および非水系電解質二次電池
JP5877817B2 (ja) 非水系二次電池用正極活物質及びその正極活物質を用いた非水系電解質二次電池
JP5590337B2 (ja) マンガン複合水酸化物粒子、非水系電解質二次電池用正極活物質、および非水系電解質二次電池と、それらの製造方法
CN109845003B (zh) 非水系电解质二次电池用正极活性物质及其制造方法、和非水系电解质二次电池
CN107078292B (zh) 非水系电解质二次电池用的正极活性物质及其制造方法、以及非水系电解质二次电池
CN107534143B (zh) 正极活性物质和其制造方法、以及非水系电解质二次电池
WO2016017783A1 (ja) 非水系電解質二次電池用正極活物質とその製造方法
KR20140008445A (ko) 비수계 전해질 2차 전지용 정극 활물질의 전구체가 되는 전이 금속 복합 수산화물과 그 제조방법, 그 비수계 전해질 2차 전지용 정극 활물질과 그 제조방법, 및 상기 정극 활물질을 이용한 비수계 전해질 2차 전지
WO2012169083A1 (ja) ニッケルマンガン複合水酸化物粒子とその製造方法、非水系電解質二次電池用正極活物質とその製造方法、ならびに、非水系電解質二次電池
CN109997260A (zh) 非水系电解质二次电池用正极活性物质及其制造方法、和使用了该正极活性物质的非水系电解质二次电池
CN114521300A (zh) 锂离子二次电池用正极活性物质以及锂离子二次电池
JP7664896B2 (ja) 高強度リチウムイオン二次電池用正極活物質、及び、該正極活物質を用いたリチウムイオン二次電池
CN107922212B (zh) 锰镍复合氢氧化物及制造方法、锂锰镍复合氧化物及制造方法、以及非水系电解质二次电池
JP2011116583A5 (enExample)
WO2015198676A1 (ja) マンガン複合水酸化物及びその製造方法、正極活物質及びその製造方法、並びに非水系電解質二次電池
CN119890295A (zh) 金属复合氢氧化物及其制造方法、非水电解质二次电池用正极活性物质及其制造方法、以及非水电解质二次电池

Legal Events

Date Code Title Description
PB01 Publication
PB01 Publication
SE01 Entry into force of request for substantive examination
SE01 Entry into force of request for substantive examination
GR01 Patent grant
GR01 Patent grant