CN106242457B - A kind of long-acting mud - Google Patents
A kind of long-acting mud Download PDFInfo
- Publication number
- CN106242457B CN106242457B CN201610521870.2A CN201610521870A CN106242457B CN 106242457 B CN106242457 B CN 106242457B CN 201610521870 A CN201610521870 A CN 201610521870A CN 106242457 B CN106242457 B CN 106242457B
- Authority
- CN
- China
- Prior art keywords
- long
- water
- agent
- interior decoration
- acting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of long-acting mud, its composition and its quality proportioning are：Inorganic gel agent 46%~48%, diatomite 32%~37%, functional additive 0.8%~1.6%, water-loss reducer 0.6%~1.8%, conditioning agent 0.7%~1.8% of constructing, remaining is packing material.It is only not ornamental very well due to long-acting mud health environment-friendly, it is the house decorative material of new generation for substituting wallpaper and emulsion paint also with feature.
Description
Technical field
The present invention relates to a kind of house decorative material, more particularly, to a kind of long-acting mud of new material, belong to E04B buildings
Field.
Background technology
Non-ignitable or fire retardant, the heat insulation effect although vacuum heat-insulating plate fire-protection rating common at present can be up to state standards
Well.But, they are easily scraped off in work progress, hollowing, gas leak phenomenon occur, and utilization rate is substantially reduced.
In addition the purification function of the interior decoration scavenging material of prior art is relatively low, and performance is not very stable, purification
Efficiency is low.
Like product is mainly diatom ooze to existing long-acting mud on the market, and product quality disunity, testing conditions do not possess, had
A little businessmans directly replace diatom ooze with inner wall putty.Therefore good purification function can not be reached, is unfavorable for the life of people
Health.
The content of the invention
It is an object of the invention to provide a kind of house decorative material with high-efficient purification function, except can be with purifying formaldehyde
With other pernicious gases, the bacterium in the suitable Shu Du lived, decontamination chamber and peculiar smell can be improved with the humidity in regulation room.
The technical scheme is that：
A kind of long-acting mud, its composition and its quality proportioning are：Inorganic gel agent 46%~48%, diatomite 32%~37%, work(
Energy property additive 0.8%~1.6%, water-loss reducer 0.6%~1.8%, conditioning agent 0.7%~1.8% of constructing, remaining is packing material.
Preferably, inorganic gel agent 47%, diatomite 33%~35%, functional additive 1%~1.5%, water-loss reducer 1%~
1.5%, conditioning agent 1%~1.5% of constructing, remaining is packing material.
Preferably, the inorganic gel agent includes at least one of gypsum, grey calcium, lime, white cement.
Preferably, the inorganic gel agent includes gypsum, grey calcium, lime, white cement, described gypsum, grey calcium, stone
Ash, the mass ratio of white cement are 1：（1-1.5）：（2-2.45）：（0.8-1.1）.
Preferably, diatomaceous particle diameter is between 10~325 mesh.
Preferably, the packing material includes quartz sand, iron oxide pigment, composite pigment, coarse whiting, talcum powder, height
At least one of ridge soil.
Preferably, during the functional additive is nano titanium oxide, nano-negative ion, ethylene urea methanal trapping agent
At least one.
Preferably, the water-loss reducer is at least one in hydroxypropyl methyl cellulose, carboxymethyl cellulose, starch ether
Kind.
Preferably, the construction conditioning agent is at least one in high efficiency water reducing agent, cement brighter, dry powder defoamer
Kind.
The application method of foregoing long-acting mud, it is characterised in that add the 0.6~0.8 of mass ratio when in use
After water stirs, by formative technology construction molding.
The beneficial effects of the invention are as follows：
1）There is provided a kind of ornament materials-long-acting mud for having and purifying indoor environment, this kind of long-acting mud has preferably viscous
Power is tied, and with higher compression strength.
2）The harmful substance of interior is removed by inorganic gel agent, diatomite, the absorption of functional additive, decomposition, reached
To the function of purification air, then it is equipped with titanium dioxide isoreactivity material decomposing formaldehyde, prevents bacteria breed.Improve indoor inhabitation ring
Border, improves quality of the life, the ecological health environment of Creating Green.And the product can be decorated by different implementation gimmicks
Interior decoration, enhancing artistic environment.
Embodiment
With reference to implementation process, the present invention will be described in detail, and the description of this part is only exemplary, not to this hair
Bright protection domain makees any limitation.
A kind of composite evacuated heat insulating board of long-acting mud, including vacuum heat-insulating plate and be coated on its periphery it is long-acting
Mud.
By above-mentioned technical proposal, the problem of solving vacuum heat-insulating plate breakage gas leakage in work progress, construction peace
Dress is convenient, and it has excellent heat insulating ability, water resistance, durability and frost resistance, and burning grade is non-ignitable or fire retardant, fire protecting performance
It is excellent.And vacuum thermal insulation plate have eliminate formaldehyde, purification air, regulation humidity, releasing negative oxygen ion, fire protection flame retarding,
Metope is self-cleaning, deodorization and sterilization, is conducive to the physical and mental health of people.
A kind of long-acting mud of indoor decoration, its composition and its quality proportioning are：Inorganic gel agent 45%~50%, diatomite
30%~40%, functional additive 0.5%~2%, water-loss reducer 0.5%~2%, conditioning agent 0.5%~2.0% of constructing, remaining is filling
Material.
Further preferably, inorganic gel agent 46%~48%, diatomite 32%~37%, functional additive 0.8%~1.6%,
Water-loss reducer 0.6%~1.8%, conditioning agent 0.7%~1.8% of constructing, remaining is packing material.
Further preferably, inorganic gel agent 47%, diatomite 33%~35%, functional additive 1%~1.5%, water-loss reducer 1%
~1.5%, conditioning agent 1%~1.5% of constructing, remaining is packing material.
Further preferably, diatomite 35%-40%.
Further preferably, packing material 10%-20%.
Further preferably, functional additive 1%-2%.
Further preferably, construction conditioning agent 1%-2.0%.
Further preferably, functional additive 1%~2%.
Certainly, the long-acting mud of cladding is exactly long-acting mud noted earlier outside vacuum thermal insulation plate.
Inorganic gel agent makes long-acting mud firmly be attached to surface of wall.Meanwhile, these inorganic coagulation materials or chance water are consolidated
Change or meet water, curing, have certain regulatory function to the water capacity of room air, the growth of bacterium can also be suppressed.
In the prior art, the content of inorganic gel agent typically it is mostly be 30% or so, it is therefore not strong with the cohesive force of wall,
And if the content of increase inorganic gel agent, then can be because other compositions ratio declines and causes the functions such as other sterilizations corresponding
Decline, long-acting mud of the invention, by increasing the content of inorganic gel agent, reaches 45-50%, drastically increase mud with
The bonding of wall, meanwhile, by coordinating other compositions, such as diatomite, packing material, functional additive, water-loss reducer, apply
The composition and its quality proportion of work conditioning agent so that whole room is had using long-acting mud to be eliminated formaldehyde, purification air, adjusts wet
The functions such as degree, releasing negative oxygen ion, fire protection flame retarding, metope are self-cleaning, deodorization and sterilization.Additionally since the increasing of the proportion of inorganic gel agent
Plus so that other compositions proportion declines accordingly, also so as to save holistic cost.
Preferably, the inorganic gel agent includes at least one of gypsum, grey calcium, lime, white cement.
It is further used as preferably, the inorganic gel agent includes gypsum, grey calcium, lime, white cement, described gypsum, ash
Calcium, lime, the mass ratio of white cement are 1：（1-1.5）：（2-2.45）：（0.8-1.1）.It is found through experiments that, above-mentioned quality
Under ratio situation, the cohesive force of long-acting mud and wall reaches best.
Preferably, diatomaceous particle diameter is between 10~325 mesh.The diatomite is reached by the size grading of itself
Different texture, effectively raises the content of diatomite in the product, also just improves the absorption of the pernicious gases such as PARA FORMALDEHYDE PRILLS(91,95)
Ability, it is a greater degree of to improve indoor living environment, and the consumption of other packing materials can be effectively reduced, put forward properties of product
It is high.
Further preferably, diatomaceous particle diameter is between 120~205 mesh.By being preferably provided with, enable to ensureing length
Imitate mud performance while, make packing material consumption reach it is smaller, so as to greatly save material and cost.
Preferably, the packing material includes at least one in quartz sand, iron oxide pigment, composite pigment, coarse whiting
Kind.Quartz sand can improve the intensity of product, there is certain scratching function；Pigment can assign long-acting mud different color sensations, fit
It is indoor offer aesthetic feeling the need for together in a variety of crowds.
Preferably, packing material includes quartz sand, iron oxide pigment, composite pigment, four kinds of coarse whiting, matter therein
Amount ratio is（10-15）：（2-2.5）：（1-1.45）：（8-12）.By above-mentioned ratio setting, long-acting mud is enabled to full
It is the house decorative material of new generation for substituting wallpaper and emulsion paint with good dicoration on the basis of the requirement of foot building.
Preferably, during the functional additive is nano titanium oxide, nano-negative ion, ethylene urea methanal trapping agent
At least one.The product with the addition of functional additive on the basis of traditional diatomaceous absorption, can effectively improve long-acting
The absorption of the harmful substances such as mud PARA FORMALDEHYDE PRILLS(91,95), capacity of decomposition, improve the permanence of product.By adding functional additive, energy
The pernicious gases such as formaldehyde, toluene, VOC enough in decomposition air, can play a part of purifying air.
Preferably, the mass ratio of nano titanium oxide, nano-negative ion, ethylene urea methanal trapping agent is (2-2.4)：
（2-2.45）：（0.8-1.2）.Ratio of the invention by increasing nano titanium oxide, nano-negative ion, relative to existing skill
Art, increases the bactericidal action of sterilization ion, on the basis of being absorbed to other harmful substances so that drastically increase to first
The absorption of aldehyde, toluene.
Preferably, the water-loss reducer is at least one in hydroxypropyl methyl cellulose, carboxymethyl cellulose, starch ether
Kind.Using the water conservation system of this compounding, the application property of product can be greatly improved, the cost of product is reduced.Save simultaneously
The consumption of raw material, serves the effect of energy-conservation in terms of energy resource consumption.Added by water-loss reducer, it is to avoid mud because dry and
Caused crackle.
Preferably, the mass ratio of hydroxypropyl methyl cellulose, carboxymethyl cellulose, starch ether is（0.3-0.4）：
（0.5-0.7）：1.By optimal design-aside, mud performance can be caused to be optimal.
Preferably, the construction conditioning agent is at least one in high efficiency water reducing agent, cement brighter, dry powder defoamer
Kind.Conditioning agent construct while workability is improved, the performance after product solidification is improved again, the light of product is improved
Degree, no longer makes such product be confined to matt system.
After above-mentioned raw material accurate measurement, put into agravic dry powder mortar mixing machine, through mechanical mixture 3~5 minutes
Discharging packaging.As long as after addition mass ratio stirs for 0.6~0.8 water when in use, being constructed into by formative technology
Type.
The film that the long-acting mud of the present invention is formed after use, can improve the quality of life of indoor living environment.Eliminate
Formaldehyde, purification air, regulation humidity, releasing negative oxygen ion, fire protection flame retarding, metope are self-cleaning, deodorization and sterilization, are conducive to the body of people
Heart health.
Further illustrated below by specific embodiment.
Embodiment 1
A kind of architecture indoor decorating and renovating material, including quality proportioning distinguish following composition：Inorganic gel agent is stone
Cream：50%, diatomite：30%, water-loss reducer hydroxypropyl methyl cellulose：0.5%, conditioning agent calcium sulphate retarder of constructing：0.2%, construction
Conditioning agent redispersable latex powder：0.3%, functional additive nano-negative ion：0.5%, remaining is filler, is that particle diameter is
The coarse whiting of 325 mesh.
After above-mentioned raw material accurate measurement, put into agravic dry powder mortar mixing machine, through mechanical mixture 3~5 minutes
Discharging packaging.As long as after addition mass ratio stirs for 0.6 water when in use, by formative technology construction molding.
Under this conditions of mixture ratios, smear the thick long-acting mash layer PARA FORMALDEHYDE PRILLS(91,95) purifying properties of 1mm and be more than 76.1%, clean-up effect is held
Long property 65%, is more than 37%, clean-up effect persistence 23%, radioactivity to toluene purifying property（A class finishing materials）External Exposure Index
Do not detect, Outreach services are 0.1,2 grades of Anti-mildew capability, hygroscopic capacity 3h is 2.0 × 10-2Wa (1 × 10-3kg/m2), resistance to compression
Intensity is 9.2MPa.It is effective to improve the living environment of interior.
The improvement of embodiment 1, inorganic gel agent is 50%, wherein described gypsum, grey calcium, lime, the mass ratio of white cement
Example is 1：（1-1.5）：（2-2.45）：（0.8-1.1）.
Under this conditions of mixture ratios, smear the thick long-acting mash layer PARA FORMALDEHYDE PRILLS(91,95) purifying properties of 1mm and be more than 80.1%, clean-up effect is held
Long property 74%, is more than 45%, clean-up effect persistence 30%, radioactivity to toluene purifying property（A class finishing materials）External Exposure Index
Do not detect, Outreach services are 0.1,2 grades of Anti-mildew capability, hygroscopic capacity 3h is 2.2 × 10-2Wa (1 × 10-3kg/m2), is resisted
Compressive Strength is 9.3MPa.It is effective to improve the living environment of interior.
Embodiment 2
A kind of architecture indoor decorating and renovating material, including quality proportioning distinguish following composition：Stone is given birth in inorganic gel agent
Cream：45%, diatomite：35%, water-loss reducer hydroxypropyl methyl cellulose：0.5%, water-loss reducer lignocellulosic：0.5%, construction regulation
Agent gypsum accelerator：0.2%, conditioning agent rubber powder of constructing：1.8%, packing material quartz sand：5%, functional additive nano-silica
Change titanium：0.5%, remaining is the mesh of packing material coarse whiting 325.
After above-mentioned raw material accurate measurement, put into agravic dry powder mortar mixing machine, through mechanical mixture 3~5 minutes
Discharging packaging.As long as after addition mass ratio stirs for 0.6 water when in use, by formative technology construction molding.
Under this conditions of mixture ratios, smear the thick long-acting mash layer PARA FORMALDEHYDE PRILLS(91,95) purifying properties of 1mm and be more than 76.1%, clean-up effect is held
Long property 65%, is more than 39%, clean-up effect persistence 24%, radioactivity to toluene purifying property（A class finishing materials）External Exposure Index
Do not detect, Outreach services are 0.2,2 grades of Anti-mildew capability, hygroscopic capacity 3h is 1.5 × 10-2Wa (1 × 10-3kg/m2), is resisted
Compressive Strength is 7.2MPa.It is effective to improve the living environment of interior.
As an improvement, packing material is quartz sand, iron oxide pigment, composite pigment, four kinds of coarse whiting, mass ratio therein
Example be（10-15）：（2-2.5）：（1-1.45）：（8-12）.By test, in the case where meeting other conditions, compression strength is
8.2MPa, and appearance color is fresh, with good decoration performance.
Embodiment 3
A kind of architecture indoor decorating and renovating material, including quality proportioning distinguish following composition：Inorganic gel agent ash calcium：
50%, diatomite：40%, water-loss reducer hydroxypropyl methyl cellulose：0.5%, water-loss reducer lignocellulosic：0.5%, water-loss reducer starch
Ether：0.3%, conditioning agent rubber powder of constructing：2%, functional additive ethylene urea：1%, remaining is packing material quartz sand.
After above-mentioned raw material accurate measurement, put into agravic dry powder mortar mixing machine, through mechanical mixture 3~5 minutes
Discharging packaging.As long as after addition mass ratio stirs for 0.75 water when in use, by formative technology construction molding.
Under this conditions of mixture ratios, smear the thick long-acting mash layer PARA FORMALDEHYDE PRILLS(91,95) purifying properties of 1mm and be more than 83.2%, clean-up effect is held
Long property 76%, is more than 41% to toluene purifying property, clean-up effect persistence 30%, 1 grade of Anti-mildew capability, and hygroscopic capacity 3h is 2.3 ×
10-2Wa (1 × 10-3kg/m2), compression strength is 8.8MPa.It is effective to improve the living environment of interior.
The further improvement of embodiment 3, water-loss reducer 0.3%, wherein hydroxypropyl methyl cellulose, carboxymethyl cellulose, starch
The mass ratio of ether is（0.3-0.4）：（0.5-0.7）：1.Pass through the setting of water-loss reducer so that properties of product reach quality requirement
In the case of, additionally it is possible to the water retention of raising about 12%.
Embodiment 4
A kind of architecture indoor decorating and renovating material, including quality proportioning distinguish following composition：Inorganic gel agent ash calcium：
50%, diatomite：40%, water-loss reducer hydroxypropyl methyl cellulose：0.8%, water-loss reducer lignocellulosic：0.5%, water-loss reducer starch
Ether：0.4%, conditioning agent rubber powder of constructing：2%, functional additive nano titanium oxide：0.5%, functional additive nanometer bear from
Son：1%, functional additive ethylene urea methanal trapping agent：0.5%, remaining is packing material quartz sand.
After above-mentioned raw material accurate measurement, put into agravic dry powder mortar mixing machine, through mechanical mixture 3~5 minutes
Discharging packaging.As long as after addition mass ratio stirs for 0.70 water when in use, by formative technology construction molding.
Under this conditions of mixture ratios, smear the thick long-acting mash layer PARA FORMALDEHYDE PRILLS(91,95) purifying properties of 1mm and be more than 88%, clean-up effect is lasting
Property 80%, to toluene purifying property be more than 45%, clean-up effect persistence 36%, 1 grade of Anti-mildew capability, hygroscopic capacity 3h be 2.1 ×
10-2Wa (1 × 10-3kg/m2), compression strength is 8.8MPa.It is effective to improve the living environment of interior.
It is used as the improvement of above-described embodiment, functional additive 2.0%, wherein nano titanium oxide, nano-negative ion, second
The mass ratio of alkene ureaformaldehyde capturing agent is (2-2.4)：（2-2.45）：（0.8-1.2）.By above-mentioned setting, 1mm thickness is smeared
Long-acting mash layer PARA FORMALDEHYDE PRILLS(91,95) purifying property is more than 94%, and clean-up effect persistence 87% is more than 55%, purification to toluene purifying property
Effect persistence 47%, 1 grade of Anti-mildew capability.
Aforementioned four embodiment, the technique effect for smearing the thick long-acting mash layers of 1mm is as follows：
It is further used as preferably, inorganic gel agent 46%~48%, diatomite 32%~37%, functional additive 0.8%~
1.6%, water-loss reducer 0.6%~1.8%, conditioning agent 0.7%~1.8% of constructing, remaining is packing material.By selecting above-mentioned numerical value
Ratio, enables to mud whole synthesis performance to improve 5%-7% or so.So-called whole synthesis performance is exactly to ensure that each parameter is full
When sufficient requirement of engineering, the effect above parameter, then will be all with respect to the ratio of the reference data corresponding to each parameter
Ratio be added obtained sum.
Further preferably, inorganic gel agent 47%, diatomite 33%~35%, functional additive 1%~1.5%, water-loss reducer 1%
~1.5%, conditioning agent 1%~1.5% of constructing, remaining is packing material.By selecting above-mentioned number ratios, enable to mud whole
Body combination property improves 7% or so.
In aforementioned four embodiment, the inorganic gel agent includes gypsum, grey calcium, lime, white cement, described stone
Cream, grey calcium, lime, the mass ratio of white cement are 1：（1-1.5）：（2-2.45）：（0.8-1.1）.Under such a be preferably provided with,
Adhesive property can improve 10% or so.
In aforementioned four embodiment, functional additive selection nano titanium oxide, nano-negative ion, ethene ureaformaldehyde
The mass ratio of capturing agent is (2-2.4)：（2-2.45）：（0.8-1.2）.PARA FORMALDEHYDE PRILLS(91,95), the absorption of toluene improve more than 8%.
In aforementioned four embodiment, water-loss reducer chooses hydroxypropyl methyl cellulose, carboxymethyl cellulose, starch ether, its
Mass ratio is（0.3-0.4）：（0.5-0.7）：1, by preferred, water retention can improve 11% or so.
In aforementioned four embodiment, packing material includes quartz sand, iron oxide pigment, composite pigment, coarse whiting four
Kind, mass ratio therein is（10-15）：（2-2.5）：（1-1.45）：（8-12）.By above-mentioned ratio setting, it can make
Obtain long-acting mud and improve voltage endurance capability, 13% or so can be improved.
Although the present invention is disclosed as above with preferred embodiment, the present invention is not limited to this.Any art technology
Personnel, without departing from the spirit and scope of the present invention, can make various changes or modifications, therefore protection scope of the present invention should
It is defined when by claim limited range.
Claims (8)
1. a kind of long-acting mud of interior decoration, its composition and its quality proportioning are：Inorganic gel agent 46%~48%, diatomite 32%~
37%, functional additive 0.8%~1.6%, water-loss reducer 0.6%~1.8%, conditioning agent 0.7%~1.8% of constructing, remaining is filling material
Material；
The inorganic gel agent includes gypsum, grey calcium, lime, white cement, described gypsum, grey calcium, lime, the quality of white cement
Ratio is 1：（1-1.5）：（2-2.45）：（0.8-1.1）.
2. the long-acting mud of interior decoration according to claim 1, it is characterised in that inorganic gel agent 47%, diatomite 33%~
35%, functional additive 1%~1.5%, water-loss reducer 1%~1.5%, conditioning agent 1%~1.5% of constructing, remaining is packing material.
3. the long-acting mud of interior decoration according to claim 1, it is characterised in that diatomaceous particle diameter 10~325 mesh it
Between.
4. the long-acting mud of interior decoration according to claim 1, it is characterised in that the packing material includes quartz sand, oxygen
Change at least one of iron pigment, composite pigment, coarse whiting, talcum powder, kaolin.
5. the long-acting mud of interior decoration according to claim 1, it is characterised in that the functional additive is nano-silica
Change at least one of titanium, nano-negative ion, ethylene urea methanal trapping agent.
6. the long-acting mud of interior decoration according to claim 1, it is characterised in that the water-loss reducer is hydroxypropyl methyl fiber
At least one of element, carboxymethyl cellulose, starch ether.
7. the long-acting mud of interior decoration according to claim 1, it is characterised in that the construction conditioning agent is efficient diminishing
At least one of agent, cement brighter, dry powder defoamer.
8. the application method of the long-acting mud of interior decoration according to one of claim 1-7, it is characterised in that when in use plus
Enter mass ratio be 0.6~0.8 water stir after, by formative technology construction molding.