CN108164193A - A kind of environmental protection integrated board and preparation method thereof - Google Patents
A kind of environmental protection integrated board and preparation method thereof Download PDFInfo
- Publication number
- CN108164193A CN108164193A CN201810008458.XA CN201810008458A CN108164193A CN 108164193 A CN108164193 A CN 108164193A CN 201810008458 A CN201810008458 A CN 201810008458A CN 108164193 A CN108164193 A CN 108164193A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- raw material
- preparation
- gross weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of environmental protection integrated board and preparation method thereof, it is related to inner wall decoration technical field, more particularly to a kind of integrated board and preparation method thereof, its raw material is made of cementitious material, functional filler, common fillers, powder auxiliary agent, its preparation method is proportionally by raw and auxiliary material ball mill grinding, add water stirring that paste is made, it is first dry to be sintered to obtain finished product at 350 DEG C 420 DEG C again through mold compression moulding.After adopting the above technical scheme, the present invention has the beneficial effect that：It gathers multi -function in integral whole, itself be green material, and have superpower environment-protection functional, beautiful dicoration, fire protection flame retarding safety and rapid construction timeliness, also improve resource utilization, mitigate ecological environment burden, meet people to it is environmentally protective the needs of.
Description
Technical field
The present invention relates to inner wall decoration technical fields, and in particular to a kind of environmental protection integrated board and preparation method thereof.
Background technology
With the continuous improvement of living standards, the environmental consciousness of people also constantly enhances, and the requirement to ornament materials is from U.S.
It sees sex reversal and has arrived beautiful and environmental protection merger, also just promote the development of Green environmental-protection building industry.However traditional integrated board
Though there is energy-saving and environment-friendly concept, it can only ensure itself environmental protection enough, can not decompose the volatility other than own
Gas, formaldehyde etc..
Invention content
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of environmentally friendly integrated board and its preparation sides
Method, it gathers multi -function in integral whole, and is green material in itself, and have superpower environment-protection functional, beautiful dicoration,
The timeliness of safety and the rapid construction of fire protection flame retarding, also improves resource utilization, mitigates the burden of ecological environment, meets
Demand of the people to environmentally protective.
To achieve the above object, the present invention is using following technical scheme：Its raw material is filled out by cementitious material, functionality
Material, common fillers, powder auxiliary agent composition；The cementitious material is flyash, clay, by its weight in raw material gross weight ratio
Number occupy ratio and be：20-30 parts of flyash, 30-40 parts of clay；The functional filler is non-calcinated diatomite and receives
Rice material, weight occupy ratio in number of the raw material gross weight than in and are respectively：20-30 parts, 2-3 parts；The powder helps
Agent is carbon fiber, and weight occupies ratio in number of the raw material gross weight than in and is：3-5 parts of carbon fiber；
Its preparation method is to add raw and auxiliary material ball mill grinding according to aforementioned proportion water stirring paste is made, and is suppressed through mold
Molding, it is first dry to be sintered to obtain finished product at 350 DEG C -420 DEG C again.
The operation principle of the present invention：Environmentally protective, nonhazardous waste of its raw material selection etc., imparts the one
The performances such as plate functional environment-friendly, timeliness application property, fire protection flame retarding；Using the diatomite of strong absorption property as main stuffing, assigning should
Money decoration wall material absorption pernicious gas, fire protection flame retarding, sound insulation and noise reduction, moisture absorption temperature function；Nano material is added in, assigns the product
The function of lasting purifying harmful gas；Adding in carbon fiber makes integrated board stable structure, intensity higher；The flyash of addition not only into
One step improves the intensity and durability of integrated board, also mitigates the pressure of ecological environment.
Raw material is as follows used by it：Flyash, effect is to reduce cost, promotes the formation of gel, improves material
Intensity and durability；Clay, effect are to improve cohesive force and sintering character；Non-calcinated diatomite and nano material, diatom
Soil uses the non-calcinated type diatomite of Changbai Mountain area, has the characteristics of large specific surface area, porous light, can assign one
The superpower absorption property of plate；Nano material is the TiO selected2, under illumination condition, free free radical is generated, can play and hold
Toxic and harmful gas in effective decomposing, purifying air long；Carbon fiber, effect are to improve the intensity of material.
After adopting the above technical scheme, the present invention has the beneficial effect that：It gathers multi -function in integral whole, and is environmentally protective in itself
Material, and have superpower environment-protection functional, beautiful dicoration, fire protection flame retarding safety and rapid construction timeliness,
Also improve resource utilization, mitigate the burden of ecological environment, meet people to it is environmentally protective the needs of.
Specific embodiment
Embodiment 1：
The present embodiment uses following technical scheme：Its raw material is by cementitious material, functional filler, common fillers, powder auxiliary agent
Composition；The cementitious material is flyash, clay, and occupying ratio in number of the raw material gross weight than in its weight is：Powder
30 parts of coal ash, 35 parts of clay；The functional filler is non-calcinated diatomite and nano material, and weight is in raw material gross weight
Number than in occupies ratio：30 parts, 2 parts；The powder auxiliary agent is carbon fiber, and weight is in raw material gross weight ratio
In number occupy ratio and be：3 parts of carbon fiber.The environmentally friendly integrated board that the present embodiment is provided, according to aforementioned proportion first by powder
It feeds intake uniformly mixed, then by material ball mill grinding, adds water stirring and paste is made, through mold compression moulding, first dry again 400
Finished product is sintered to obtain at DEG C.
Embodiment 2：
Difference of the present embodiment from embodiment 1 is that the raw material weight component proportion of environmentally friendly integrated board is as follows：The gelling
Material is flyash, clay, and occupying ratio in number of the raw material gross weight than in its weight is：35 parts of flyash, clay 32
Part；The functional filler is non-calcinated diatomite and nano material, and weight is occupied in number of the raw material gross weight than in
Ratio is respectively：27 parts, 3 parts；The powder auxiliary agent be carbon fiber, number occupation ratio of the weight in raw material gross weight than in
Example be：3 parts of carbon fiber.Other compositions and preparation method are same as Example 1.
Embodiment 3：The present embodiment and the difference of embodiment 1 are the raw material weight component proportion of environmentally friendly integrated board such as
Under：The cementitious material is flyash, clay, and occupying ratio in number of the raw material gross weight than in its weight is：Fine coal
32 parts of ash, 40 parts of clay；The functional filler is non-calcinated diatomite and nano material, and weight is in raw material gross weight ratio
In number occupy ratio and be respectively：24 parts, 2 parts；The powder auxiliary agent is carbon fiber, and weight is in raw material gross weight ratio
Number occupy ratio and be：2 parts of carbon fiber.Other compositions and preparation method are same as Example 1.
The above is merely illustrative of the technical solution of the present invention and unrestricted, and those of ordinary skill in the art are to this hair
The other modifications or equivalent replacement that bright technical solution is made, without departing from the spirit and scope of technical solution of the present invention,
It is intended to be within the scope of the claims of the invention.
Claims (4)
1. a kind of environmental protection integrated board and preparation method thereof, it is characterised in that：Its raw material is by cementitious material, functional filler, general
Logical filler, powder auxiliary agent composition；The cementitious material is flyash, clay, by the part of its weight in raw material gross weight than in
Number occupies ratio and is：20-30 parts of flyash, 30-40 parts of clay；The functional filler is non-calcinated diatomite and nanometer material
Material, weight occupy ratio in number of the raw material gross weight than in and are respectively：20-30 parts, 2-3 parts；The powder auxiliary agent is
Carbon fiber, weight occupy ratio in number of the raw material gross weight than in and are：3-5 parts of carbon fiber；
Its preparation method is to add raw and auxiliary material ball mill grinding according to aforementioned proportion water stirring paste is made, and is suppressed through mold
Molding, it is first dry to be sintered to obtain finished product at 350 DEG C -420 DEG C again.
2. a kind of environmental protection integrated board and preparation method thereof, it is characterised in that：The cementitious material is flyash, clay, by it
Weight occupies ratio in number of the raw material gross weight than in：30 parts of flyash, 35 parts of clay；The functional filler is non-
Calcined diatomite and nano material, weight occupy ratio in number of the raw material gross weight than in and are respectively：30 parts, 2 parts；It is described
Powder auxiliary agent for carbon fiber, weight occupies ratio in number of the raw material gross weight than in and is：3 parts of carbon fiber.
3. a kind of environmental protection integrated board and preparation method thereof, it is characterised in that：The cementitious material is flyash, clay, by it
Weight occupies ratio in number of the raw material gross weight than in：35 parts of flyash, 32 parts of clay；The functional filler is non-
Calcined diatomite and nano material, weight occupy ratio in number of the raw material gross weight than in and are respectively：27 parts, 3 parts；It is described
Powder auxiliary agent for carbon fiber, weight occupies ratio in number of the raw material gross weight than in and is：3 parts of carbon fiber.
4. a kind of environmental protection integrated board and preparation method thereof, it is characterised in that：The cementitious material is flyash, clay, by it
Weight occupies ratio in number of the raw material gross weight than in：32 parts of flyash, 40 parts of clay；The functional filler is non-
Calcined diatomite and nano material, weight occupy ratio in number of the raw material gross weight than in and are respectively：24 parts, 2 parts；It is described
Powder auxiliary agent for carbon fiber, weight occupies ratio in number of the raw material gross weight than in and is：2 parts of carbon fiber.