KR100879750B1 - The natural water-soluble painting composite and method of manufacturing the same - Google Patents
The natural water-soluble painting composite and method of manufacturing the same Download PDFInfo
- Publication number
- KR100879750B1 KR100879750B1 KR1020080065575A KR20080065575A KR100879750B1 KR 100879750 B1 KR100879750 B1 KR 100879750B1 KR 1020080065575 A KR1020080065575 A KR 1020080065575A KR 20080065575 A KR20080065575 A KR 20080065575A KR 100879750 B1 KR100879750 B1 KR 100879750B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- natural
- coating composition
- aqueous coating
- Prior art date
Abstract
Description
본 발명은 천연 수성도료 조성물의 제조방법 및 이에 의한 조성물에 관한 것으로, 더욱 상세하게는 수용성인 천연수지와 무기계(inorganic) 미세원형 중공체 분말, 다공성 광물, 해조류(Kelzyme), 맥반석을 이용한 본 조성물은 인체에 무해한 기능성 천연 수성 도료로서 결로방지, 단열성, 항곰팡이성, 원적외선 방출, 축열성, 흡음성, 방음성을 나타내므로 냉방이나 난방에 있어서 에너지비용 절감효과 및 쾌적한 실내 환경, 인체의 기초 신진 대사를 촉진할 수 있는 천연 수성도료 조성물의 제조방법 및 이에 의한 조성물에 관한 것이다.The present invention relates to a method for preparing a natural water-based coating composition and a composition therefrom, and more particularly, to a water-soluble natural resin and an inorganic microcircular hollow powder, porous minerals, seaweeds (Kelzyme), and the present composition using elvan It is a functional natural water-based paint that is harmless to the human body. It prevents dew condensation, heat insulation, anti-mildew, far-infrared emission, heat storage, sound absorption, and sound insulation. It relates to a method for producing a natural aqueous coating composition that can be promoted and a composition thereby.
종래에는 건축자재로 이용되는 합성수지에 인체에 해로운 벤젠, 클로로포름, 아세톤, 스칠렌 및 포름알데히드 등과 같은 유기용제를 사용하는 관계상, 건물내부로 휘발성이 강한 유기화합물을 방출하여 새집증후군(SICKHOUSE SYNDROME)과 같은 심각한 문제를 일으키고 있다.Conventionally, due to the use of organic solvents such as benzene, chloroform, acetone, styrene and formaldehyde, which are harmful to the human body, synthetic resins used as building materials emit highly volatile organic compounds inside the building. It is causing serious problems.
이와 같은 문제를 해결하는 건축자재의 개발이 절실히 요구되고 있는 실정이다.There is an urgent need for the development of building materials to solve these problems.
또한, 소득 증가에 따라 생활수준이 향상되면서 소비자의 고품질 주거공간에 대한 욕구가 증대되어, 인체에 유익한 건강소재를 건축자재에 적용하여 보다 건강하고 쾌적한 주거 공간을 만들고자 하는 시도가 진행되고 있다.In addition, as the standard of living improves as income increases, the consumer's desire for high-quality residential space increases, and an attempt to make a healthier and more comfortable residential space by applying health materials beneficial to the human body to building materials is in progress.
현대사회는 경제발전에 힘입어 종래의 건축용 도료는 그 기능만 충실할 수 있다면, 그 성분의 유해여부에는 무관하게 사용되어 왔다. 최근에 와서 환경문제의 심각성이 대두되며 건축용 도료에 제한을 두는 움직임이 활성화되었다. 종래의 건축용 도료는 환경을 오염시키면 인체에 해로운 물질들이 다량 방출되기도 하였다.In modern society, due to economic development, conventional building paints have been used irrespective of the harmfulness of their components, as long as their function can be fulfilled. In recent years, the seriousness of environmental problems has emerged, and the movement to limit construction paints has been activated. In the conventional building paints, when polluting the environment, a lot of harmful substances are released.
또한, 요즘들어 새집 증후군은 심각한 사회 문제로 대두되고 있으며, 새집증후군에 시달리는 사람들은 간지러움 어지러움, 두통, 피부트러블등의 증상을 갖고있으며, 개인별에 따라 증상이 다양하다.In addition, these days, sick house syndrome has become a serious social problem, people suffering from sick house syndrome has symptoms such as itching, dizziness, headache, skin problems, and varies depending on the individual.
이러한 새집증후군에 대한 정확한 원인은 판명하기 어려우나, 건물내부에 있는 휘발성 물질들이 주요 원인물질로 간주되어지고 있는데, 포름알데히드(HCHO),휘발성 유기화합물(VOC's) 등이 그 예이다.The exact cause of the sick house syndrome is difficult to determine, but volatile substances in the building are considered to be the main causes, such as formaldehyde (HCHO) and volatile organic compounds (VOC's).
이와 같은 유해물질은 새로운 벽지나 장판에서 발생되며, 약 6개월에서 2년정도의 시간동안 지속되는 것으로 알려져 있다.These harmful substances are generated from new wallpaper or floor coverings and are known to last for about six months to two years.
이러한 건축물 내부에서는 유독성 염소가스도 방출되는 것으로 알려져 있는으며, 또한 포름알데히드도 방출되는데, 이는 방부제, 접착제, 합판 등에 널리 쓰이는 물질로서 신경계와 장기 등에 악영향을 주는 발암물질로 알려져 있다.It is known that toxic chlorine gas is also released in these buildings, and formaldehyde is also released, which is widely used in preservatives, adhesives, and plywood, and is known as a carcinogen that adversely affects the nervous system and organs.
한편, 음이온은 인체에 유익하다고 알려져 있어서 이를 환경개선에 활용하기 위하여 음이온을 발생하는 제품들이 연구개발되고 있으나 음이온을 위주로 하는 여 러 제품들은 환경소재로써 역할에 한계가 있으며 또한 인위적으로 음이온을 발생시키는 음이온 발생장치는 음이온 발생 원리상 대부분이 필연적으로 활성산소를 발생시키며 활성산소는 면역성저하, 백혈병 및 암을 유발하는 건강 저해물질로 인식되고 또한 발생장치에서 발생되는 전자파는 신 공해물질로 심각한 건강장애요인으로 나타나고 있는 실정이다.On the other hand, negative ions are known to be beneficial to the human body, and products that generate negative ions have been researched and developed in order to utilize them in improving the environment. However, many products that focus on negative ions have a limited role as environmental materials and artificially generate negative ions. Most of the negative ion generators generate free radicals due to the principle of negative ion generation, and the active oxygen is recognized as a health inhibitor that causes immunodeficiency, leukemia and cancer. It appears to be a factor.
따라서 본 발명이 해결하고자 하는 첫번째 기술적 과제는 수용성인 천연수지와 무기계(inorganic) 미세원형 중공체 분말, 다공성 광물, 해조류(Kelzyme), 맥반석을 이용한 본 조성물은 인체에 무해한 기능성 천연 수성 도료로서 결로방지, 단열성, 항곰팡이성, 원적외선 방출, 축열성, 흡음성, 방음성을 나타내므로 냉방이나 난방에 있어서 에너지비용 절감효과 및 쾌적한 실내 환경, 인체의 기초 신진 대사를 촉진할 수 있는 천연 수성도료 조성물의 제조방법을 제공하는 것이다.Therefore, the first technical problem to be solved by the present invention is a water-soluble natural resin and inorganic (inorganic) micro-circular hollow body powder, porous minerals, seaweed (Kelzyme), the present composition using alvan is a functional natural aqueous coating harmless to the human body to prevent condensation Method for producing natural water-based coating composition which can promote energy saving and pleasant indoor environment, basic metabolism of human body in cooling or heating because it shows heat insulation, anti-mildew, far infrared ray emission, heat storage, sound absorption and sound insulation To provide.
또한, 본 발명이 해결하고자 하는 두번째 기술적 과제는 수용성인 천연수지와 무기계(inorganic) 미세원형 중공체 분말, 다공성 광물, 해조류(Kelzyme), 맥반석을 이용한 본 조성물은 인체에 무해한 기능성 천연 수성 도료로서 결로방지, 단열성, 항곰팡이성, 원적외선 방출, 축열성, 흡음성, 방음성을 나타내므로 냉방이나 난방에 있어서 에너지비용 절감효과 및 쾌적한 실내 환경, 인체의 기초 신진 대사를 촉진할 수 있는 천연 수성도료 조성물을 제공하는 것이다.In addition, the second technical problem to be solved by the present invention is a water-soluble natural resin and inorganic (inorganic) micro-circular hollow body powder, porous minerals, seaweed (Kelzyme), the present composition using alvan is condensation as a functional natural aqueous coating harmless to the human body Provides natural water-based coating composition which can reduce energy cost, pleasant indoor environment, and promote the basic metabolism of human body in cooling or heating because it shows prevention, heat insulation, anti-mildew, far infrared ray emission, heat storage, sound absorption, and sound insulation. It is.
본 발명은 상술한 첫번째 기술적 과제를 달성하기 위하여,The present invention to achieve the first technical problem described above,
아마인유(Linseed Oil) 10 내지 30 중량부, 동유(Tung Oil) 10 내지 30 중량부 및 송진(Rosin) 10 내지 30 중량부를 질소(N2)분위기에서 가열하여 천연수지를 제조하는 단계(S1단계)와 상기 천연수지에 식물류(D-Limonene) 5 내지 10 중량부 및 제1첨가제를 더 가하여 희석된 천연수지를 준비하는 단계(S2단계) 및 상기 희석 된 천연수지에 중공필라 30 내지 90 중량부, 해조류(Kelzyme) 30 내지 40 중량부, 다공성광물 30 내지 40 중량부, 중탄 30 내지 40 중량부, 맥반석 30 내지 40 중량부, 물 35 내지 50 중량부 및 제2첨가제 20 내지 35 중량부를 첨가하여 600 내지 1000rpm으로 교반하는 단계(S3단계)를 포함하는 것을 특징으로 하는 천연 수성도료 조성물의 제조방법을 제공한다.10 to 30 parts by weight of linseed oil, 10 to 30 parts by weight of tung oil and 10 to 30 parts by weight of rosin in a nitrogen (N2) atmosphere to prepare a natural resin (step S1) To prepare a diluted natural resin by adding 5 to 10 parts by weight of plants (D-Limonene) and the first additive to the natural resin (S2 step) and the hollow pillar 30 to 90 parts by weight of the diluted natural resin, Seaweed (Kelzyme) 30 to 40 parts by weight, porous minerals 30 to 40 parts by weight, bicarbonate 30 to 40 parts by weight, elvan 30 to 40 parts by weight, water 35 to 50 parts by weight and 20 to 35 parts by weight of the second additive 600 It provides a method for producing a natural water-based paint composition comprising the step of stirring at 1000rpm (step S3).
본 발명의 일실시예에 의하면, 상기 S1단계에서의 가열하는 온도는 210 내지 260℃일 수 있다.According to one embodiment of the present invention, the heating temperature in step S1 may be 210 to 260 ℃.
본 발명의 다른 실시예에 의하면, 상기 S1단계에서의 가열하는 시간은 10 내지 20시간일 수 있다.According to another embodiment of the present invention, the heating time in step S1 may be 10 to 20 hours.
본 발명의 또 다른 실시예에 의하면, 상기 중공필러(hollow filler)는 폴리아크릴로니트릴(poly acrylonitrile)에 탄산칼슘 및 이산화티탄으로 코팅되어 있는 것이며, 그 크기가 10 내지 40㎛일 수 있다.According to another embodiment of the present invention, the hollow filler is a polyacrylonitrile coated with calcium carbonate and titanium dioxide, the size of which may be 10 to 40㎛.
본 발명의 또 다른 실시예에 의하면, 상기 다공성광물은 다공질의 이산화규소를 주성분으로 하는 규조토일 수 있다.According to another embodiment of the present invention, the porous mineral may be a diatomaceous earth mainly composed of porous silicon dioxide.
삭제delete
본 발명은 상술한 두번째 기술적 과제를 달성하기 위하여,The present invention to achieve the above-described second technical problem,
상술한 제조방법에 의하여 제조되는 천연 수성도료 조성물을 제공한다.It provides a natural aqueous coating composition prepared by the above-described manufacturing method.
본 발명에 따르는 천연 수성도료 조성물의 제조방법 및 이에 의한 조성물에 의하여 수용성인 천연수지와 무기계(inorganic) 미세원형 중공체 분말, 다공성 광물, 해조류(Kelzyme), 맥반석을 이용한 본 조성물은 인체에 무해한 기능성 천연 수성 도료로서 결로방지, 단열성, 항곰팡이성, 원적외선 방출, 축열성, 흡음성, 방음성을 나타내므로 냉방이나 난방에 있어서 에너지비용 절감효과 및 쾌적한 실내 환경, 인체의 기초 신진 대사를 촉진할 수 있는 효과가 있다.The present method using a water-soluble natural resin and inorganic microcircular hollow powder, porous minerals, seaweeds (Kelzyme), and elvan are useful according to the present invention. It is a natural water-based paint that prevents dew condensation, heat insulation, anti-mold, far-infrared radiation, heat storage, sound absorption, and sound insulation, so it can reduce energy costs, improve indoor environment, and promote human body metabolism in cooling and heating. There is.
이하, 본 발명을 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail.
본 발명에 따르는 천연 수성도료 조성물의 제조방법 및 이에 의한 조성물은 수용성인 천연수지와 무기계(inorganic) 미세원형 중공체 분말, 다공성 광물, 해조류(Kelzyme), 맥반석을 이용한 본 조성물은 인체에 무해한 기능성 천연 수성 도료로서 결로방지, 단열성, 항곰팡이성, 원적외선 방출, 축열성, 흡음성, 방음성을 나타내므로 냉방이나 난방에 있어서 에너지비용 절감효과 및 쾌적한 실내 환경, 인체의 기초 신진 대사를 촉진할 수 있는 특징이 있다.Method for producing a natural aqueous coating composition according to the present invention and the composition therefrom is a water-soluble natural resin and inorganic (inorganic) microcircular hollow powder, porous minerals, algae (Kelzyme), the present composition using alvanite is a functional natural harmless to the human body As an aqueous paint, it prevents dew condensation, heat insulation, anti-mold, far-infrared emission, heat storage, sound absorption, and sound insulation, so it can reduce energy costs, improve indoor environment, and promote basic metabolism of human body in cooling and heating. have.
먼저, S1단계를 살펴보면, 아마인유(Linseed Oil) 10 내지 30 중량부, 동유(Tung Oil) 10 내지 30 중량부 및 송진(Rosin) 10 내지 30 중량부를 질소(N2)분위기에서 가열하여 천연수지를 제조하는 단계(S1단계)와 상기 천연수지에 식물류(D-Limonene) 5 내지 10 중량부 및 제1첨가제를 더 가하여 희석된 천연수지를 준비하는 단계이다.First, looking at step S1, natural resin by heating 10 to 30 parts by weight of linseed oil, 10 to 30 parts by weight of tung oil and 10 to 30 parts by weight of rosin in a nitrogen (N 2 ) atmosphere To prepare a step (S1 step) and adding the 5 to 10 parts by weight of plants (D-Limonene) and the first additive to the natural resin to prepare a diluted natural resin.
상기 아마인유는 10 내지 30 중량부를 사용하는데, 만일 10 중량부 미만이면, 유연성이 부족하고 반응하는 중간에 겔(gel)화될 수 있으며, 반대로 30 중량부를 초과하면 실제 시공후에 도막의 성능이 저하될 수 있다.The linseed oil is used 10 to 30 parts by weight, if less than 10 parts by weight, lack of flexibility and can be gelled in the middle of the reaction, on the contrary, if it exceeds 30 parts by weight, the performance of the coating film after the actual construction will be degraded Can be.
또한, 상기 동유는 10 내지 30 중량부를 사용하는데, 만일 10 중량부 미만이면, 시공후 건조가 느리게 진행될 수 있으며, 반대로 30 중량부를 초과하면, 반응중에 수지가 겔화될 수 있다.In addition, the oil is used 10 to 30 parts by weight, if less than 10 parts by weight, drying after construction may proceed slowly, on the contrary, if it exceeds 30 parts by weight, the resin may gel during the reaction.
상기 송진은 10 내지 30 중량부를 사용하는데, 만일 10 중량부 미만이면, 시공후에 접착력의 저하가 발생할 수 있으며, 반대로 30 중량부를 초과하면, 반응중에 수지가 겔화될 수 있다.The rosin is used in 10 to 30 parts by weight, if less than 10 parts by weight, may cause a decrease in adhesive strength after construction, on the contrary, if it exceeds 30 parts by weight, the resin may gel during the reaction.
아울러, 상기 천연수지를 제조하는 단계는 질소분위기에서 수행하게 되는데, 그 이유는 반응속도, 색깔과 같은 반응효율을 상승시키기 위함이다.In addition, the step of preparing the natural resin is carried out in a nitrogen atmosphere, the reason is to increase the reaction efficiency, such as reaction rate, color.
상기 질소 분위기에서 아마인유, 동유 및 송진을 가열하는데, 그 온도는 210 내지 260℃일 수 있다. 만일 210℃ 미만이면, 자동 산화반응 및 디일스알더(Diels Alder)반응성이 부족해질 수 있으며, 반대로, 260℃을 초과하면 색상이 탄화되어 검어질 수 있고 반응중에 겔화될 수 있다.The linseed oil, kerosene and rosin in the nitrogen atmosphere is heated, the temperature may be 210 to 260 ℃. If it is less than 210 ° C., the automatic oxidation and Diels Alder reactivity may be insufficient. On the contrary, if it exceeds 260 ° C., the color may be carbonized and blackened and may gel during the reaction.
또한, 여기서 가열하는 시간은 10 내지 20시간인데, 만일 10시간 미만이면, 반응효율이 저감될 수 있으며, 반대로 20시간을 초과하면 과반응으로 인해 반응중에 겔화될 수 있다.In addition, the heating time here is 10 to 20 hours, if less than 10 hours, the reaction efficiency can be reduced, on the contrary, if it exceeds 20 hours can be gelated during the reaction due to overreaction.
다음으로, S2단계를 보면, 상기 천연수지에 식물류(D-Limonene) 5 내지 10 중량부 및 제1첨가제를 더 가하여 희석된 천연수지를 준비하는 단계이다.Next, looking at step S2, by adding 5 to 10 parts by weight of the plant (D-Limonene) and the first additive to the natural resin to prepare a diluted natural resin.
상술한 S1단계의 반응이 종결된 후에 냉각이 시작되어 약 140℃이하가 되면 상기 식물류 5 내지 10 중량부와 제1첨가제를 가하여 천연수지를 희석하게 된다. 여기서 만일 식물류가 5 중량부 미만이면, 저장안정성이 저감되어 보관시에 불량이 발생할 수 있으며, 반대로 10 중량부를 초과하면 시공후 도막의 특성이 열화될 수 있다.After the reaction of step S1 is terminated, cooling is started, and when the temperature is about 140 ° C. or less, the natural resin is diluted by adding 5 to 10 parts by weight of the plant and the first additive. Here, if the plant is less than 5 parts by weight, storage stability may be reduced and defects may occur during storage. On the contrary, if the amount of plants exceeds 10 parts by weight, the characteristics of the coating after construction may deteriorate.
또한, 상기 제1첨가제는 지르코늄 및 디펜텐으로 이루어진 군에서 선택된 적어도 하나일 수 있다.In addition, the first additive may be at least one selected from the group consisting of zirconium and dipentene.
상기 제1첨가제는 5 내지 10 중량부를 사용하는데, 만일 5 중량부 미만이면, 저장안정성이 저감되고 고점도가 될 수 있으며, 반대로 10 중량부를 초과하면, 인체에 자극적일 수 있다.The first additive is used in 5 to 10 parts by weight, if less than 5 parts by weight, the storage stability may be reduced and high viscosity, and if it exceeds 10 parts by weight, it may be irritating to the human body.
마지막으로, S3단계를 보면, 상기 희석된 천연수지에 중공필라 30 내지 90 중량부, 해조류(Kelzyme) 30 내지 40 중량부, 다공성광물 30 내지 40 중량부, 중탄 30 내지 40 중량부, 맥반석 30 내지 40 중량부, 물 35 내지 50 중량부 및 제2첨가제 20 내지 35 중량부를 첨가하여 600 내지 1000rpm으로 교반하는 단계(S3단계)이다. Finally, look at step S3, 30 to 90 parts by weight of hollow pillars, 30 to 40 parts by weight of seaweed (Kelzyme), 30 to 40 parts by weight of porous minerals, 30 to 40 parts by weight of bicarbonate, and elvan 30 to the diluted natural resin 40 parts by weight, 35 to 50 parts by weight of water and 20 to 35 parts by weight of the second additive are added and stirred at 600 to 1000 rpm (step S3).
상기 중공필라는 폴리아크릴로니트릴(poly acrylonitrile)에 탄산칼슘 및 이 산화티탄으로 코팅되어 있는 것이며, 그 크기가 10 내지 40㎛인 것을 사용하는데, 만일 상기 중공필라가 10㎛ 미만이면, 고점도로 인하여 생산성이 저감될 수 있으며, 반대로 40㎛을 초과하면 표면이 거칠어질 수 있다.The hollow pillar is coated with polyacrylonitrile with calcium carbonate and titanium oxide, and its size is 10 to 40 µm. If the hollow pillar is less than 10 µm, due to high viscosity Productivity can be reduced, on the contrary, if it exceeds 40 mu m, the surface can be roughened.
또한, 상기 중공필라는 30 내지 90 중량부를 사용할 수 있는데, 만일 30 중량부 미만이면, 결로 및 단열의 효과가 낮아질 수 있으며, 반대로 90 중량부를 초과하면 저장안정성이 부족해질 수 있다.In addition, the hollow pillar may be used 30 to 90 parts by weight, if less than 30 parts by weight, the effect of condensation and heat insulation can be lowered, on the contrary, if it exceeds 90 parts by weight may be insufficient storage stability.
또한, 상기 해조류는 바다속의 캐르프라고 하는 해조류의 화석을 분쇄하여 얻어진 분말로서 칼슘, 미네랄, 미생물, 활성효소가 함께 포함되어 있어서, 토양에 혼합하면 식물 및 곡물 수확의 생산 품질을 늘이고 인체에 흡수되면 건강한 피부, 면역력 증가, 노화방지, 골다공증의 예방 효과가 있다. 아울러, 상기 해조류의 성분을 보면, 산화 칼슘(CaO),탄산칼슘(CaCO3), 옥소(I),아연(Zn), 크로미움(3가Cr), 마그네슘(Mg), 철(Fe), 나트륨(Na), 칼륨(K), 망간(Mn), 실리카(Si), 셀렌(Se), 인(P) 및 기타 해조류 미생물을 포함한다.In addition, the algae is a powder obtained by crushing fossils of algae, called kerfs in the sea, and contains calcium, minerals, microorganisms, and active enzymes. If you have healthy skin, increase immunity, anti-aging, osteoporosis preventive effect. In addition, the components of the seaweed, calcium oxide (CaO), calcium carbonate (CaCO 3 ), oxo (I), zinc (Zn), chromium (trivalent Cr), magnesium (Mg), iron (Fe), Sodium (Na), potassium (K), manganese (Mn), silica (Si), selenium (Se), phosphorus (P) and other algae microorganisms.
이러한 해조류를 30 내지 40중량부를 사용하는데, 만일 30 중량부 미만이면, 생리활성화에너지 발산의 효과가 저감될 수 있고, 반대로 40 중량부를 초과하면 다른 구성성분이 상대적으로 적어지게 되어 전체적인 효과에 악영향을 미칠 수 있다.30 to 40 parts by weight of the seaweed is used, if less than 30 parts by weight, the effect of physiological activation energy dissipation can be reduced, on the contrary, if more than 40 parts by weight, the other components are relatively less adversely affect the overall effect Can be crazy
또한, 상기 다공성광물은 다공질의 이산화규소를 주성분으로 하는 규조토를 이용할 수 있으며, 30 내지 40 중량부를 사용한다. 만일, 30 중량부 미만이면, 단열, 탈취 및 습도조절의 효과가 부족하며, 반대로 40 중량부를 초과하면 다른 구성 성분이 상대적으로 부족해질 수 있다. In addition, the porous mineral may be a diatomaceous earth mainly composed of porous silicon dioxide, it uses 30 to 40 parts by weight. If less than 30 parts by weight, the effect of heat insulation, deodorization and humidity control is insufficient, on the contrary, if it exceeds 40 parts by weight, other components may be relatively insufficient.
아울러, 상기 다공성광물의 크기는 30 내지 50㎛인데, 만일 30㎛ 미만이면 고점도로 인하여 조성물 전체의 유동성이 부족해질 수 있으며, 반대로 50㎛을 초과하면 표면이 거칠어질 수 있다. In addition, the size of the porous mineral is 30 to 50㎛, if less than 30㎛ may cause a lack of fluidity of the entire composition due to the high viscosity, on the contrary if the surface exceeds 50㎛ may be rough.
한편, 상기 중탄은 석회석을 원료로하여 제조되는 것으로 통상 체질안료로 사용된다. 여기서의 사용량은 30 내지 40 중량부인데, 만일 30중량부 미만이면 도막의 강도가 부족하고 작업성이 나빠질 수 있으며, 반대로 40중량부를 초과하면 다른 구성성분의 양이 상대적으로 줄어든다. On the other hand, the bicarbonate is produced by using limestone as a raw material is usually used as a sieving pigment. The amount used here is 30 to 40 parts by weight, if less than 30 parts by weight of the coating film may be insufficient strength and poor workability, on the contrary, if it exceeds 40 parts by weight, the amount of other components is relatively reduced.
또한, 상기 맥반석은 무수규산, 산화알루미늄을 주성분으로 하여 인체 및 생물체에 필요한 산화제이철, 칼슘, 망간, 마그네슘 등의 무기질이 다량 함유된 다공질 안료로서 흡착작용, 발육촉진, 독성중화, 암 예방, 탈취, 원적외선 방출 효과가 있다. 이러한 맥반석은 그 크기가 5 내지 20㎛인데, 만일 5㎛ 미만이면, 고점도로 인해 조성물 전체의 유동성이 부족할 수 있으며, 반대로 20㎛을 초과하면 표면이 거칠어질 수 있다. 또한 상기 맥반석은 30 내지 40 중량부를 사용하는데, 만일 30중량부 미만이면 고점도로 인한 유동성 부족이 문제될 수 있으며, 반대로 40중량부를 초과하면 표면이 거칠어질 수 있다. In addition, the ganbanite is a porous pigment containing a large amount of minerals such as ferric oxide, calcium, manganese, magnesium, etc., which are mainly composed of silicic anhydride and aluminum oxide, and are adsorbing, promoting development, neutralizing toxicity, preventing cancer, and deodorizing. It has far infrared ray emission effect. Such elvan has a size of 5 to 20 μm, and if it is less than 5 μm, the high viscosity may result in insufficient fluidity of the entire composition, and if it exceeds 20 μm, the surface may become rough. In addition, the elvan is used 30 to 40 parts by weight, if less than 30 parts by weight may be a problem due to the lack of fluidity due to high viscosity, on the contrary, if it exceeds 40 parts by weight may roughen the surface.
한편, 상기 물은 35 내지 50 중량부를 사용하는데, 만일 35중량부 미만이면 고점도가 되며 작업성에 악영향을 미치고, 반대로 50 중량부를 초과하면 저점도 문제가 발생할 수 있다.On the other hand, the water is used in the 35 to 50 parts by weight, if less than 35 parts by weight becomes a high viscosity adversely affects the workability, on the contrary, if more than 50 parts by weight may cause a low viscosity problem.
한편, 상기 제2첨가제는 잔탄검(Xanthane Cum) 및 탄산나트륨으로 이루어진 군에서 선택된 적어도 하나일 수 있다.On the other hand, the second additive may be at least one selected from the group consisting of Xanthane Cum and sodium carbonate.
만일, 상기 제2첨가제가 20 중량부 미만이면, 유화능이 저감될 수 있으며, 반대로, 35 중량부를 초과하면, 시공후 도막의 내수성이나 접착력이 떨어질 수 있다.If the second additive is less than 20 parts by weight, the emulsification capacity may be reduced. On the contrary, if the second additive is more than 35 parts by weight, the water resistance or adhesive strength of the coating film after construction may be reduced.
상술한 바와 같이, 천연수지에 중공필라, 해조류, 다공성광물, 중탄, 맥반석, 물 및 제2첨가제를 첨가하여 600 내지 1000rpm의 속도로 교반하는데, 만일 600rpm 미만이면 분산효과가 낮아 공정효율이 저감될 수 있으며, 반대로 1000rpm을 초과하면 과분산으로 인하여 불필요한 기포들이 발생할 수 있다.As described above, hollow pillars, seaweeds, porous minerals, bicarbonate, elvan, water and a second additive are added to the natural resin and stirred at a speed of 600 to 1000 rpm. If it is less than 600 rpm, the dispersion effect is low and the process efficiency may be reduced. On the contrary, if it exceeds 1000 rpm, unnecessary bubbles may occur due to overdispersion.
한편, 아마인유(Linseed Oil) 10 내지 30 중량부, 동유(Tung Oil) 10 내지 30 중량부 및 송진(Rosin) 10 내지 30 중량부를 질소(N2)분위기에서 가열하여 천연수지를 제조하는 단계(S1단계)와 상기 천연수지에 식물류(D-Limonene) 5 내지 10 중량부 및 제1첨가제를 더 가하여 희석된 천연수지를 준비하는 단계(S2단계) 및 상기 희석된 천연수지에 중공필라 30 내지 90 중량부, 해조류(Kelzyme) 30 내지 40 중량부, 다공성광물 30 내지 40 중량부, 중탄 30 내지 40 중량부, 맥반석 30 내지 40 중량부, 물 35 내지 50 중량부 및 제2첨가제 20 내지 35 중량부를 첨가하여 600 내지 1000rpm으로 교반하는 단계(S3단계)를 거치며 제조되는 천연 수성도료 조성물은 인체에 무해한 기능성 천연 수성 도료로서 결로방지, 단열성, 항곰팡이성, 원적외선 방출, 축열성, 흡음성, 방음성을 나타내므로 냉방이나 난방에 있어서 에너지비용 절감효과 및 쾌적한 실내 환경, 인체의 기초 신진 대사를 촉진할 수 있다.On the other hand, 10 to 30 parts by weight of linseed oil, 10 to 30 parts by weight of tung oil and 10 to 30 parts by weight of rosin in a nitrogen (N2) atmosphere to prepare a natural resin (S1) Step) and adding 5 to 10 parts by weight of plants (D-Limonene) and the first additive to the natural resin to prepare a diluted natural resin (step S2) and the hollow pillar 30 to 90 weight in the diluted natural resin Part, 30 to 40 parts by weight of seaweed (Kelzyme), 30 to 40 parts by weight of porous minerals, 30 to 40 parts by weight of bicarbonate, 30 to 40 parts by weight of ganban stone, 35 to 50 parts by weight of water and 20 to 35 parts by weight of the second additive Natural water paint composition prepared through the step of stirring at 600 to 1000rpm (step S3) is a functional natural water-based paint harmless to the human body because it shows condensation prevention, heat insulation, anti-mildew, far-infrared emission, heat storage, sound absorption, sound insulation Cooling or heating In reducing energy cost effective and comfortable indoor environment, it is possible to accelerate the metabolic basis of the human body.
실시예Example 1 One
먼저, 아마인유(Linseed Oil) 20 중량부, 동유(Tung Oil) 20 중량부 및 송진(Rosin) 20 중량부를 질소(N2) 분위기에서 230℃로 15 시간 동안 가열하여 천연수지를 제조하였다. 다음으로, 140℃까지 냉각시킨 후에 식물류로 리모넨(D-Limonene) 10중량부, 제1첨가제로 지르코늄과 디펜텐 8 중량부를 더 부가하여 상기 천연수지를 희석하였다. 다음으로, 상기 희석된 천연수지에 중공필라 50 중량부, 해조류(Kelzyme) 40 중량부, 다공성광물로 40 중량부, 중탄 35 중량부, 맥반석 35 중량부, 물 40 중량부 및 제2첨가제로 잔탄검과 탄산나트륨 30 중량부를 첨가하여 800 rpm으로 3시간 동안 교반하여 본 발명에 따르는 천연 수성도료 조성물을 제조하였다.First, natural resin was prepared by heating 20 parts by weight of linseed oil, 20 parts by weight of tung oil and 20 parts by weight of rosin at 230 ° C. in a nitrogen (N 2 ) atmosphere for 15 hours. Subsequently, after cooling to 140 ° C., 10 parts by weight of limonene (D-Limonene) was added to plants, and 8 parts by weight of zirconium and dipentene were added as first additives to dilute the natural resin. Next, 50 parts by weight of hollow pillar, 40 parts by weight of seaweed (Kelzyme), 40 parts by weight of porous minerals, 35 parts by weight of heavy coal, 35 parts by weight of ganban stone, 40 parts by weight of water and a second additive to the diluted natural resin A gum and 30 parts by weight of sodium carbonate were added thereto, and stirred at 800 rpm for 3 hours to prepare a natural aqueous coating composition according to the present invention.
실험예Experimental Example 1 One
실시예 1에 의하여 제조된 천연 수성도료 조성물을 아래 표 1에 나타난 실험방법과 규격으로 시험하여 그 결과를 나타내었다.The natural aqueous coating composition prepared according to Example 1 was tested according to the experimental methods and specifications shown in Table 1 below, and the results are shown.
위 <표 1>을 참조하면, 본 발명에 따르는 천연 수성도료 조성물은 인체에 무해한 기능성 천연 수성 도료로서 결로방지, 단열성, 항곰팡이성, 원적외선 방출, 축열성, 흡음성, 방음성을 나타내므로 냉방이나 난방에 있어서 에너지비용 절감효과 및 쾌적한 실내 환경, 인체의 기초 신진 대사를 촉진할 수 있는 우수한 효과가 있음을 알 수 있다.Referring to <Table 1>, the natural water-based paint composition according to the present invention is a functional natural water-based paint harmless to the human body because it shows condensation prevention, heat insulation, anti-mildew, far-infrared radiation, heat storage, sound absorption, soundproofing In the energy cost reduction effect and comfortable indoor environment, it can be seen that there is an excellent effect to promote the basic metabolism of the human body.
Claims (9)