KR20080100012A - The composition of paint and the manufacturing method thereof - Google Patents

Abstract

A paint composition using natural soil does not peel off with water and is environment-friendly when being used as an alternative of paint and a wallpaper adhesive. A paint composition using natural soil is uniformly mixed with at least one enhancer selected from a soil hardening agent 10 ~ 30 liter, dispersing agent 1 ~ 2 liter, waterproofing emulsion 1 ~ 2 liter and lacquer resin 0.3 ~ 0.5 liter; a natural adhesive 106.2 ~ 164.215kg; and mud 1000 kg. The paint composition is used as paint or adhesive. The natural adhesive is comprised of bio adhesive 4 ~ 6kg, CMC 0.2 ~1kg, water 100 ~150kg and salt water 2 ~5kg having the salinity of 5% or includes rosin 1kg and methanol 0.5 liter, salt water 2 ~5kg having the salinity of 5%, water 100 ~150kg, water reducing agent 0.2 ~ 1kg, water glass 0.5 ~ 1kg, bio adhesive 4 ~ 6kg, and CMC 0.2 ~ 1kg.

Description

Coating composition using natural soil and its manufacturing method {the composition of paint and the manufacturing method

The present invention relates to a coating composition using natural soil, and a method for manufacturing the same, comprising: natural grass mixed with biopool, siemci, water, and brine; Mud; A paint composition is prepared by mixing and stirring a soil hardener, a dispersant, and a waterproofing solution, wherein the paint composition is further mixed with a lacquer solution to give a color, and at least one functional material selected from sulfuric water, phytoncide, kaolinite, and zeolite. The coating composition is prepared by mixing, and as the prepared coating composition is used as a paint substitute, wallpaper adhesive, etc., it is not peeled off by water, so it is durable, and since the main material is a natural material, it is environmentally friendly and contains functional materials. It is good for the human body.

As the general paint is applied to a building such as an exterior wall, an interior wall, or applied to an object, the paint makes the building look beautiful while primarily protecting the building and the object.

Since most of these paints are chemically constituents, the respirator can be used during manufacturing, mixing with other mixtures (for diluting or mixing two or more colors to give different colors), painting, etc. In order to prevent the components of the furnace from being inhaled and do not adhere to the skin, there were inconveniences such as putting on a mask and keeping them away from the skin.

In addition, when the above paint is applied inside a building space, or when painted on indoor furniture, the paint component is continuously exposed in daily life, and it is not good for people who use the space such as sick house syndrome, headache, or discomfort. There was a problem that did not affect.

Recently, there have been attempts to apply ocher to the exterior wall of a building to a certain thickness in order to give an appearance such as eco-friendly paint or loess, but ocher has a problem of being cracked when it dries and easily damaged by rain or snow because of poor adhesion. there was.

Therefore, the present invention is to solve the above problems, bio-pool, siemci, water, and natural water mixed with brine; Mud; The paint composition which mixed and stirred the soil hardening | curing agent, a dispersing agent, and a waterproofing liquid is manufactured, and it is used for the said paint composition as a paint substitute, wallpaper adhesive, etc., It aims at providing the eco-friendly coating composition, without peeling off with water.

In addition, the natural grass is replaced with a resin composed of rosin dissolved in methanol, diluted brine, water-reducing agent, water glass, bio-pool, siemsi, and the purpose is to improve the adhesion, waterproofing, and shorten the curing time.

In addition, the natural grass is replaced with a terpine oil, diluted brine, water-reducing agent, water glass, bio-pool, Siemsi, the purpose is to improve the adhesion, waterproofing, and shorten the curing time.

In addition, the coating composition is further mixed with lacquer liquid to give a color, the purpose of using the paint as a substitute for more beautiful appearance.

Furthermore, the coating composition is prepared by further mixing at least one functional material selected from sulfuric water, phytoncide, kaolinite, zeolite, and sulfuric water to produce a coating composition, and by the functional material, prevent the sick house syndrome to the human body. There is another purpose to do this.

The present invention relates to a coating composition using natural soil, and a method for manufacturing the same, comprising: natural grass mixed with biopool, siemci, water, and brine; Mud; A paint composition is prepared by mixing and stirring a soil hardener, a dispersant, and a waterproofing solution, wherein the paint composition is further mixed with a lacquer solution to give a color, and at least one functional material selected from sulfuric water, phytoncide, kaolinite, and zeolite. The paint composition is prepared by mixing, and as the prepared paint composition is used as a paint substitute, wallpaper adhesive, etc., it is not peeled off by water, so it is durable, and since the main material is a natural material, it is environmentally friendly and contains functional materials. It is good for the human body.

The paint composition according to the present invention is composed of natural grass, mud, improver and functional material, but first, the method of producing natural grass, but the natural grass is divided into three examples according to the material and the manufacturing method The first embodiment will be described below.

First, the natural grass according to the first embodiment is composed of a mixing ratio of 4 to 6 kg of bio-pool, 0.2 to 1 kg of CMC (CMC), 100 to 150 kg of water, 2 to 5 kg of brine having a salinity of 5%, Referring to the production method of natural grass in detail as follows.

First, 4-6 kg biopool and a portion of the water are mixed and sufficiently stirred, and 0.2-1 kg of Siemshi and the remaining water are mixed and sufficiently stirred, and the water and the biopool are mixed and stirred, respectively. Mix and stir the water and the Siemshi in one place, and 2-5 kg of brine having a 5% salinity is poured while stirring sufficiently to prepare a natural grass.

In the natural grass according to the second embodiment, 1 kg of rosin and 0.5 L of methanol are uniformly mixed to prepare a rosin-methanol mixture in which rosin is dissolved in methanol, and water of 2 to 5 kg of brine having a 5% salinity of 100 Diluted by adding ~ 150kg, the mixture is added uniformly by adding 0.2-1kg of water reducing agent and 0.5-1kg of water glass to the diluted brine, and mixing the rosin methanol mixture in the mixture uniformly, and bioful 4 to the mixture. 6 kg and 0.2-1 kg of Siemshi (CMC) are sequentially added while stirring to form a uniformly mixed natural grass.

In addition, the natural grass according to the third embodiment is a mixture of terrapine oil in place of the rosin methanol mixture, which will be described in detail, further dilute 100 to 150 kg of water in 2 to 5 kg of salt water having a 5% salinity, 0.2-1 kg of water reducing agent and 0.5-1 kg of water glass are added to the diluted salt water, and the mixture is uniformly mixed. 0.25 liters of terapine oil, 4-6 kg of biofule, and 0.2-1 kg of Siemshi (CMC) are sequentially added to the mixture, followed by stirring. Make up natural blends.

For reference, the bio-pool is a paste (adhesive) made of starch as a main component, and is used as a common one that can be easily obtained in general commercially.In the natural pool, by adding salt water, the antiseptic performance and hardenability of the natural pool In order to increase the viscosity and increase the adhesive performance, seawater may be used as a substitute for the brine.

In addition, siemci (CMC, sodium carboxy methyl cellulose, sodium carboxymethyl cellulose, water-soluble fibrin derivative) is a tasteless and odorless white powder obtained by acting sodium monochlorate on alkali fibre, a natural polymer material having a viscosity in aqueous solution It is used for dyeing paste, paper size agent, emulsion stabilizer of ice cream or margarine, and caking agent of paint or cosmetics. It is harmless to the human body, nontoxic and biologically safe.

In addition, rosin refers to balsam secreted when a pine tree is damaged, and because of its hardening property, after melting with methanol, further mixing, the natural grass according to the second embodiment, rosin by such a manufacturing method It does not harden again, and it has the characteristics (effect) which improves adhesiveness and waterproofness by rosin, and others (methanol about 0.79) and a water reducing agent use a normal thing.

And terapin oil refers to the essence oil extracted from pine, pine, etc., having a similar effect (characteristics) to the rosin, using a commercially available terapin oil (the terapin oil has a specific gravity of about 0.86 to 0.875, In the present invention, the specific gravity of terrapine oil is applied to 0.86 for weight conversion, which is merely for calculation, and does not mean that the present invention uses only terapine oil having a specific gravity of 0.86), and also glass water. Is an alkali aqueous silicate salt obtained by melting silicon dioxide and alkali into a thick aqueous solution. The inclusion of the water glass shortens the curing time and improves the adhesion performance.

Subsequently, the method of making the mud is poured into the clay to saturate it, and after mixing and stirring sufficiently, removing suspended matter, foreign matter, large lumps, and contaminants, and filtering the sieve of 150 to 300 mesh. Discard thicker than sieve thickness and collect what passed through the sieve.

Water is then poured into the sieve through the sieve and stirred sufficiently, which is left for at least two hours, and the mud is prepared by pouring the clear water of the upper layer.

On the other hand, in order to obtain a better mud, clean water is poured again into the mud, mixed and agitated sufficiently, and after leaving it alone, the process of discarding the clear water of the upper layer can be repeated to produce a better mud. have.

For reference, if you continue to use the drained water without throwing away water, you can save water, and if you pour more water, stir, and repeat the pouring process, the ocher particles contained in the mud will be more solid and fine (fine). There is a characteristic.

In addition, when the mud process is complicated, the mud is prepared by completely drying the loess and then making it into a very fine powder and saturating water by pouring water into the finely powdered loess.

Accordingly, among the embodiments of the natural grass, that is, the natural grass (106.2 to 162 kg) according to the first embodiment, the natural grass (108.395 to 163.395 kg) according to the second embodiment, and the natural grass according to the third embodiment One selected natural grass (107.115 ~ 164.215kg) and 1000kg of mud prepared by the above method is sufficiently stirred to complete the paint composition, and to improve the physical properties of the paint composition, several kinds of improvers are further included. Is as follows.

The improving agent may be selected from at least one of a soil hardener, a dispersant, a waterproofing agent, and a lacquer solution. The soil hardener requires 10 to 30 l, and the soil hardener is used because the mud is made of loess of the paint casting. The inclusion of such soil hardeners makes the coating composition harder.

And the dispersing agent is mixed 1 ~ 2L, it is preferable to use a dispersing agent of sodium polycarboxylic acid, the dispersing agent is included in the coating composition to keep each particle is well dispersed without agglomeration.

In addition, the waterproofing liquid is mixed with 1-2 L, and the waterproofing liquid uses a transparent color. For example, a waterproofing liquid of a water glass product can be used, and the waterproofing liquid is contained in the coating composition, and after the coating composition is applied and cured, Since it can be applied to the interior and exterior walls of the building.

In addition, the lacquer juice is required 0.3 ~ 0.5kg, the lacquer juice is extracted from the lacquer tree, the true lacquer juice extracted from the oak tree is suitable, this lacquer liquid is to match the color to suit the desired color within the appropriate amount range Moderately add or subtract.

The improvement agent selected from the soil hardener, the dispersant, the waterproofing agent, and the lacquer solution is further included in the paint composition consisting of natural grass and mud, thereby forming a paint composition having further improved function. The paint composition further includes a functional material. To further improve the functionality of the paint composition, the functional material will be described as follows.

The functional material is selected from at least one selected from phytoncide, kaolinite, zeolite, and sulfuric water, and the amount of the addition is further mixed with a functional material having a weight corresponding to 2 to 4% of the weight of the prepared coating composition. To form a coating composition with improved functionality.

Briefly about the functional substance, first, sulfur soil water (土 黃土 水), to dissolve the sulfur while boiling sulfur and evenly mixed water, stirred with stirring more well to put the yellow soil, and then leave it for a while while cooling Sit up, collecting the supernatant water is called sulfur water, the additional mixing of such sulfur water is characterized by increasing the antimicrobial properties of the coating composition.

And phytoncide is a generic term for aromatic antibiotics that are emitted from the air or in the ground to protect themselves from surrounding pests or microorganisms, and there are various phytoncide species depending on the species. Antibacterial, antioxidant, antiseptic and forest bathing effects can be obtained.

Zeolite is a mineral that appears to melt when bubbles are rapidly heated, and it is a mineral produced by the action of hydrolysis of three volcanic ashes in the New Era. It is a hydrous alumina silicate mineral that has a large specific surface area due to its porosity, and is excellent in adsorption characteristics of heavy metals by pores, deodorization, and moisture absorption, and it shows characteristics of humidity control and deodorization, especially for heavy metals such as mercury, zinc and cadmium. It adsorbs well and has the characteristic of having selective adsorption to ammonia.

In addition, kaolinite (kaolinite), which is a main component of kaolin and is used in the raw material of the ceramics and cement industry, is excellent in the adsorption of heavy metals, such kaolinite and zeolite is far-infrared radiation is beneficial to the human body.

In addition, the compounding material and the compounding quantity of each Example of the said coating composition are shown in following [Table 1].

Kinds material Compounding amount Remarks         Natural grass   First embodiment Biofull 4 to 6 kg Based on starch Siem Reap (CMC) 0.2-1kg Carboxymethyl Cellulose Sodium water 100-150 kg 100-150ℓ brine 2-5 kg Improved viscosity, antiseptic, hardening Natural grass total weight according to the first embodiment: 106.2 ~ 162kg    Second embodiment Rosin 1 kg Improved adhesiveness and waterproofness Methanol 0.5ℓ  Specific gravity: approx.0.79, weight: 0.395kg brine 2-5 kg 5% salinity water 100-150 kg 100-150ℓ Water reducing agent 0.2-1 kg water glass 0.5-1 kg Biofull 4 to 6 kg Based on starch Siem Reap (CMC) 0.2-1kg Carboxymethyl Cellulose Sodium Natural grass total weight according to the second embodiment: 108.395 ~ 163.395kg    Third embodiment Terrafin oil 0.25ℓ Specific gravity 0.86, weight 0.215kg brine 2-5 kg 5% salinity water 100-150 kg 100-150ℓ Water reducing agent 0.2-1 kg water glass 0.5-1 kg Biofull 4 to 6 kg Based on starch Siem Reap (CMC) 0.2-1kg Carboxymethyl Cellulose Sodium Total weight of natural grass according to the third embodiment: 107.115 to 164.215 kg Mud Ocher, water 1000 kg  Improver Soil hardener 10 to 30ℓ Soil hardener Dispersant 1 to 2ℓ Sodium Polycarboxylate Waterproof 1 to 2ℓ Transparent Lacquer 0.3-0.5ℓ   Functional material Phytoncide Added at 2-4% weight of the resulting paint composition Kaolinite 〃 Zeolite 〃 Sulfur water 항균, antibacterial properties

Since the coating composition is adhesive and water-curable, it is resistant to moisture and moisture as it is applied to interior and exterior walls of a building or used as a substitute for other paints, so it is also durable in rain and snow, and its color is natural. It has a beautiful appearance by giving an atmosphere like ocher house, and in particular, since it has a waterproof function by including a waterproofing liquid, it can be used in places or objects that require other waterproof functions.

In addition, the coating composition, as it is applied as a substitute for painting indoors or wallpaper paste, the coating composition itself is composed of natural substances and beneficial substances (mud, functional substances) and the like is beneficial to the human body, sick house syndrome It can be used as a substitute for chemical adhesives.

As described above, the present invention is a natural grass mixed with bio-pool, siem-shi, water, brine; Mud; The coating composition which mixed and stirred the soil hardening | curing agent, the dispersing agent, and the waterproofing liquid is manufactured, and can use the said coating composition as a paint substitute, wallpaper adhesive, etc., and can provide an environmentally friendly coating composition without peeling off with water.

In addition, the natural grass is replaced with a resin composed of rosin dissolved in methanol, diluted brine, water-reducing agent, water glass, bio-pool, siemsi, has the effect of improving the adhesion, waterproofing, and shorten the curing time.

In addition, the natural grass is replaced with terrapine oil, diluted brine, water-reducing agent, water glass, bio-pool, Siemsi, has the effect of improving the adhesion, waterproofing, and shorten the curing time.

In addition, the paint composition is further mixed with lacquer juice to give a color, it is used as a substitute for paint has a more beautiful effect.

Furthermore, the coating composition is prepared by further mixing at least one functional material selected from sulfuric water, phytoncide, kaolinite, zeolite, and sulfuric water to produce a coating composition, and by the functional material, prevent the sick house syndrome to the human body. It has a beneficial effect.

Claims (8)

At least one improving agent selected from 10 to 30 L of soil hardener, 1 to 2 L of dispersant, 1 to 2 L of waterproofing liquid, and 0.3 to 0.5 L of lacquer; Natural grass 106.2-164.215 kg; Paint composition of 1000 kg of mud is mixed uniformly, Coating composition using natural soil, characterized in that the coating composition is used as a paint or an adhesive. The method of claim 1, The natural grass, Biopool 4-6kg, CMC 0.2-1kg, water 100-150kg, salt water 2-5kg having a 5% salinity, Coating composition using natural soil, characterized in that to improve the adhesion of the coating composition. The method of claim 1, The natural grass, It consists of 1 kg of rosin and 0.5 L of methanol, 2 to 5 kg of salt water with 5% salinity, 100 to 150 kg of water, 0.2 to 1 kg of water reducing agent, 0.5 to 1 kg of water glass, 4 to 6 kg of biofule, and 0.2 to 1 kg of CMC. Coating composition using natural soil, characterized in that to improve the adhesion and waterproofness of the coating composition. The method of claim 1, The natural grass, It consists of 2 to 5 kg of salt water with 5% salinity, 100 to 150 kg of water, 0.2 to 1 kg of water reducing agent, 0.5 to 1 kg of water glass, 0.25 L of terafin oil, 4 to 6 kg of biofule, and 0.2 to 1 kg of CMC, Coating composition using natural soil, characterized in that to improve the adhesion and waterproofness of the coating composition. The method according to any one of claims 1 to 4, At least one functional material selected from phytoncide, kaolinite and zeolite is provided, In addition, a functional material having a weight corresponding to 2 to 4% of the weight of the coating composition, Coating composition using natural soil, characterized in that to enhance the functionality of the coating composition. Biopool 4-6kg, CMC 0.2-1kg, water 100-150kg, 2-5kg brine with 5% salinity, divide the provided water, mix and stir the biopool and CMC separately with water Preparing natural grass prepared by mixing and stirring the biopool mixed with water and CMC, respectively; Preparing a mud 1000kg of fine particles of ocher having a saturated state; Uniformly mixing the natural grass and mud; At least one improving agent selected from 10 to 30 L of soil curing agent, 1 to 2 L of dispersant, 1 to 2 L of waterproofing liquid and 0.3 to 0.5 L of lacquer liquid is further mixed with the mixture of the mud and natural grass; At least one functional material selected from phytoncide, kaolinite and zeolite is provided;  A mixture of mud and natural grass and an improving agent; By constructing a paint composition composed of a mixture of the mud and the weight of the functional material equivalent to 2 to 4% of the weight of the mixture of natural grass and improver, Method for producing a coating composition using natural soil, characterized in that the coating composition is used as a paint or an adhesive. Dissolving 1 kg of rosin in 0.5 L of methanol to prepare a rosin methanol mixture; 2 to 5 kg of salt water having a 5% salinity, 100 to 150 kg of water, 0.2 to 1 kg of water reducing agent, and 0.5 to 1 kg of water glass were mixed uniformly, and then the prepared rosin methanol mixture, biofule 4 to 6 kg, CMC 0.2 Prepare a natural grass prepared so that the mixture is stirred uniformly by mixing 1 ~ 1kg sequentially one by one, Preparing a mud 1000kg of fine particles of ocher having a saturated state; Uniformly mixing the natural grass and mud; At least one improving agent selected from 10 to 30 L of soil curing agent, 1 to 2 L of dispersant, 1 to 2 L of waterproofing liquid and 0.3 to 0.5 L of lacquer liquid is further mixed with the mixture of the mud and natural grass; At least one functional material selected from phytoncide, kaolinite and zeolite is provided;  A mixture of mud and natural grass and an improving agent; By constructing a paint composition composed of a mixture of the mud and the weight of the functional material equivalent to 2 to 4% of the weight of the mixture of natural grass and improver, Method for producing a coating composition using natural soil, characterized in that the coating composition is used as a paint or an adhesive. 2 to 5 kg of salt water having a 5% salinity, 100 to 150 kg of water, 0.2 to 1 kg of water reducing agent and 0.5 to 1 kg of water glass were added uniformly, and then mixed uniformly, 0.25 liter of terapine oil, 4 to 6 kg of biofull, Prepare 0.2 ~ 1 kg of CMC, the natural grass prepared to be uniformly mixed with sufficient stirring while mixing one by one, Preparing a mud 1000kg of fine particles of ocher having a saturated state; Uniformly mixing the natural grass and mud; At least one improving agent selected from 10 to 30 L of soil curing agent, 1 to 2 L of dispersant, 1 to 2 L of waterproofing liquid and 0.3 to 0.5 L of lacquer liquid is further mixed with the mixture of the mud and natural grass; At least one functional material selected from phytoncide, kaolinite and zeolite is provided;  A mixture of mud and natural grass and an improving agent; By constructing a paint composition composed of a mixture of the mud and the weight of the functional material equivalent to 2 to 4% of the weight of the mixture of natural grass and improver, Method for producing a coating composition using natural soil, characterized in that the coating composition is used as a paint or an adhesive.