CN110294955A - A kind of interior wall moistureproof and mildewproof color lacquer putty - Google Patents
A kind of interior wall moistureproof and mildewproof color lacquer putty Download PDFInfo
- Publication number
- CN110294955A CN110294955A CN201910529754.9A CN201910529754A CN110294955A CN 110294955 A CN110294955 A CN 110294955A CN 201910529754 A CN201910529754 A CN 201910529754A CN 110294955 A CN110294955 A CN 110294955A
- Authority
- CN
- China
- Prior art keywords
- parts
- mildewproof
- interior wall
- color lacquer
- lacquer putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of interior wall moistureproof and mildewproof color lacquer putties, by weight include white cement 500-600 parts, 400-500 parts of inorganic filler, 3-10 parts of calcium lignosulfonate, 4-6 parts of dry powder mould inhibitor, 2-3 parts of dispersing agent, 30-50 parts of colour stone powder, 10-15 parts of redispersible rubber powder, 1-2 parts of starch ether, 3-5 parts of cellulose ether, 10-15 parts of xanthan gum, 10-20 parts of nano-titanium dioxide, 5-10 parts of active carbon, 5-10 parts of zeolite, 1-2 parts of graphene, 8-12 parts of high hydroscopic resin.Using a kind of interior wall moistureproof and mildewproof color lacquer putty of the invention, have the effect of moistureproof and mildewproof, and can absorb and decompose the pernicious gases such as indoor formaldehyde.
Description
Technical field
The present invention relates to a kind of interior wall moistureproof and mildewproof color lacquer putties, belong to inner wall putty technical field.
Background technique
Putty is most common one kind in building decoration materials, and traditional putty main component is talcum powder and glue etc..
Putty further for be a kind of substrate levelling for wall-surface patching, for decoration (brush paint wallpaper) in next step
It lays a good foundation.Putty is divided into interior wall and two kinds of exterior wall, and exterior wall putty to resist exposing to the weather so colloidality is big, intensity
Height, environmentally friendly index are slightly lower.Inner wall putty composite index is preferable, health environment-friendly, so interior wall not external application, exterior wall is not interior to be used.Usually
Putty is gypsum or cement base, and such rough surface is easier bonding securely, but still will be when construction
A bed boundary Ji Lai sealing base is brushed in base while improving the adhesive force of metope, allows putty that can preferably be bonded in basal plane
On.
Traditional powder of lacquer putty for use in the production process, needs to be added glue and improves viscosity, but may contain remaining toxic component,
Such as formaldehyde, benzene, toluene etc., in addition, generally there are a large amount of formaldehyde, pollution sources include various wood-based plates in newly-decorated house
Material, wallpaper, wall paper, paint etc., for human health, just needing to divulge information more than half a year can move in, but the Form aldehyde release phase is up to 3-
15 years, even if ventilation more than half a year, not can guarantee indoor formaldehyde content lower than house civil standards yet.
At present in interior wall decorative engineering, it can generally be criticized on original cement mortar wall before brushing paint and scrape one
Layer putty material, main function be it is levelling, increase the aesthetics of decoration, and be commonly exactly that interior wall is greasy in inner wall decoration
Son.Nowadays interior putty has been the essential auxiliary material of inner wall of building coating project.With the development of architectural finish, interior wall is greasy
Son using more and more extensive.That there are moisture resistances is poor for common putty paste, causes service life to reduce, while in actual use
That there are cohesive forces is poor, easy picking and easy to crack, and in addition when air humidity is larger for a long time, Yi Zisheng bacterium mould etc. meets not
Coating Market requirement.
Summary of the invention
Goal of the invention of the invention is: in view of the above problems, a kind of interior wall moistureproof and mildewproof color lacquer putty is provided,
Moistureproof and mildewproof of the present invention, and can be with resolving harmful gas.
The technical solution adopted by the invention is as follows:
A kind of interior wall moistureproof and mildewproof color lacquer putty includes white cement 500-600 parts by weight, inorganic filler 400-500
Part, 3-10 parts of calcium lignosulfonate, 4-6 parts of dry powder mould inhibitor, 2-3 parts of dispersing agent, 30-50 parts of colour stone powder, redispersible rubber powder 10-15
Part, 1-2 parts of starch ether, 3-5 parts of cellulose ether, 10-15 parts of xanthan gum, 10-20 parts of nano-titanium dioxide, 5-10 parts of active carbon,
5-10 parts of zeolite, 1-2 parts of graphene, 8-12 parts of high hydroscopic resin.
Preferably, the inorganic filler is one of precipitated calcium carbonate, powdered whiting and talcum powder or a variety of.
It is raw material by natural plants preferably, the starch ether is hydroxypropyl starch ether, not plasticizer-containing, ring
Health care health.
Preferably, the nano-titanium dioxide is nanometer anatase titania, nanometer anatase titania has
Good photocatalysis effect can decompose aerial pernicious gas and part inorganic compound, and inhibit bacterial growth and disease
The activity of poison reaches air cleaning, sterilization, deodorization, mould proof.
Preferably, the nano-titanium dioxide is the nano-titanium dioxide by visible light-inducing, nanometer can be improved
Photocatalytic activity of the titanium dioxide to visible light.
Preferably, the zeolite is modified zeolite.
Preferably, the zeolite is HDTMA modified zeolite, PARA FORMALDEHYDE PRILLS(91,95) adsorption capacity is stronger.
Preferably, the active carbon is active fruit shell carbon.
Preferably, the active carbon is cocoanut active charcoal, with hole prosperity, absorption property is good, intensity is high, easily again
The advantages that life, economy and durability.
Preferably, further including ion exchange resin in the color lacquer putty, arranges in pairs or groups and use with high hydroscopic resin.
Preferably, the weight of the ion exchange resin is the 50-80% of high hydroscopic resin.
A kind of interior wall moistureproof and mildewproof color lacquer putty of the invention, can adsorb indoor formaldehyde etc. using active carbon and zeolite
Pernicious gas, nano-titania photocatalyst have the function of antibacterial and are capable of harmful gas of degrading activity charcoal and zeolite absorption
Body, fungus and mildew resistance, while the moisture content under wet environment can be absorbed using the water imbibition of high hydroscopic resin, to play moisture-proof
Effect.
It should be noted that active carbon and zeolite are used cooperatively the adsorption capacity that the two can be enhanced, due to active carbon and boiling
The adsorption rate of stone is higher than the decomposition rate of nano-titanium dioxide, and therefore, the combination of active carbon, zeolite and nano-titanium dioxide can
To there is better effect, using the adsorption capacity of active carbon and zeolite, first the pernicious gases such as indoor formaldehyde is adsorbed, are being utilized
Nano-titania photocatalyst capacity of decomposition resolving harmful gas, so that solving active carbon and zeolite can only adsorb and cannot divide
Solution, and adsorption capacity has the defect of saturation value, and the defect for using nano-titanium dioxide decomposition rate slow merely.
It should be noted that common nano-titanium dioxide just has sterilization and resolving harmful gas under action of ultraviolet light
Effect, and pass through doping techniques carry out visible light-inducing nano-titanium dioxide then can issue the effect of waving in visible light action,
Effect can be good, especially, arranges in pairs or groups and uses with graphene, and absorption of the nano-titanium dioxide to visible light can be enhanced in graphene, increases
The antibacterial and photo-catalysis capability of strong nano-titanium dioxide.
The present invention is haved the function that moisture-proof using the water absorbing capacity of high hydroscopic resin, but dispersing agent can be added in putty
Equal auxiliary agents, and often the auxiliary agents such as dispersing agent are the auxiliary agents of ionic, but the water absorbing capacity meeting of high hydroscopic resin in the case
It substantially reducing, water absorbing capacity only has normal 10%, therefore, be used cooperatively using high hydroscopic resin and ion exchange resin, every
From outer ion and high hydroscopic resin, to guarantee the performance and moisture protection of high hydroscopic resin.
In conclusion by adopting the above-described technical solution, the beneficial effects of the present invention are: effect with moistureproof and mildewproof
Fruit, and can absorb and decompose the pernicious gases such as indoor formaldehyde；It is reasonably combined to keep moisture protection strong, and absorb decomposing formaldehyde etc.
The effect of pernicious gas is good；Effect is beautiful, and only needs a coating, is not required to brushing emulsion paint again, save the cost.
Specific embodiment
All features disclosed in this specification or disclosed all methods or in the process the step of, in addition to mutually exclusive
Feature and/or step other than, can combine in any way.
Any feature disclosed in this specification unless specifically stated can be equivalent or with similar purpose by other
Alternative features are replaced.That is, unless specifically stated, each feature is an example in a series of equivalent or similar characteristics
?.
In a specific embodiment of the invention, the starch ether is hydroxypropyl starch ether；The nano-titanium dioxide is warp
The nanometer anatase titania of overdoping technology progress visible light-inducing；The zeolite is HDTMA modified zeolite；The work
Property charcoal be cocoanut active charcoal；The colour stone powder is added according to required color.
Embodiment 1
A kind of interior wall moistureproof and mildewproof color lacquer putty of the present embodiment, including 500 parts of white cement, 500 parts of precipitated calcium carbonate, wood
10 parts of calcium, 6 parts of dry powder mould inhibitor, 3 parts of dispersing agent, 50 parts of colour stone powder, 15 parts of redispersible rubber powder, 2 parts of starch ether, fiber
5 parts of plain ether, 15 parts of xanthan gum, 20 parts of nano-titanium dioxide, 10 parts of active carbon, 10 parts of zeolite, 2 parts of graphene, high hydroscopic resin 8
Part, 4 parts of ion exchange resin.
Embodiment 2
A kind of interior wall moistureproof and mildewproof color lacquer putty of the present embodiment, including 600 parts of white cement, 400 parts of talcum powder, calcium lignosulfonate 3
Part, 4 parts of dry powder mould inhibitor, 2 parts of dispersing agent, 30 parts of colour stone powder, 10 parts of redispersible rubber powder, 1 part of starch ether, cellulose ether
3 parts, 10 parts of xanthan gum, 10 parts of nano-titanium dioxide, 5 parts of active carbon, 5 parts of zeolite, 1 part of graphene, 12 parts of high hydroscopic resin,
10 parts of ion exchange resin.
Embodiment 3
A kind of interior wall moistureproof and mildewproof color lacquer putty of the present embodiment, including 550 parts of white cement, 450 parts of powdered whiting, wood
It is 6 parts of calcium, 5 parts of dry powder mould inhibitor, 2 parts of dispersing agent, 40 parts of colour stone powder, 13 parts of redispersible rubber powder, 1.5 parts of starch ether, fine
Plain 4 parts of the ether of dimension, 13 parts of xanthan gum, 15 parts of nano-titanium dioxide, 7 parts of active carbon, 7 parts of zeolite, 1.5 parts of graphene, super absorbent resin
10 parts of rouge, 7 parts of ion exchange resin.
Comparative example 1
A kind of interior wall moistureproof and mildewproof color lacquer putty of the present embodiment, including 550 parts of white cement, 450 parts of powdered whiting, wood
It is 6 parts of calcium, 5 parts of dry powder mould inhibitor, 2 parts of dispersing agent, 40 parts of colour stone powder, 13 parts of redispersible rubber powder, 1.5 parts of starch ether, fine
Plain 4 parts of the ether of dimension, 13 parts of xanthan gum, 15 parts of nano-titanium dioxide, 7 parts of active carbon, 7 parts of zeolite, 1.5 parts of graphene, super absorbent resin
10 parts of rouge.
Comparative example 2
A kind of interior wall moistureproof and mildewproof color lacquer putty of the present embodiment, including 550 parts of white cement, 450 parts of powdered whiting, wood
It is 6 parts of calcium, 5 parts of dry powder mould inhibitor, 2 parts of dispersing agent, 40 parts of colour stone powder, 13 parts of redispersible rubber powder, 1.5 parts of starch ether, fine
Plain 4 parts of ether is tieed up, 13 parts of xanthan gum, 15 parts of nano-titanium dioxide, 7 parts of active carbon, 7 parts of zeolite, 10 parts of high hydroscopic resin, ion is handed over
Change 7 parts of resin.
Comparative example 3
A kind of interior wall moistureproof and mildewproof color lacquer putty of the present embodiment, including 550 parts of white cement, 450 parts of powdered whiting, wood
It is 6 parts of calcium, 5 parts of dry powder mould inhibitor, 2 parts of dispersing agent, 40 parts of colour stone powder, 13 parts of redispersible rubber powder, 1.5 parts of starch ether, fine
Plain 4 parts of the ether of dimension, 13 parts of xanthan gum, 15 parts of nano-titanium dioxide, 14 parts of active carbon, 1.5 parts of graphene, 10 parts of high hydroscopic resin,
7 parts of ion exchange resin.
Comparative example 4
A kind of interior wall moistureproof and mildewproof color lacquer putty of the present embodiment, including 550 parts of white cement, 450 parts of powdered whiting, wood
It is 6 parts of calcium, 5 parts of dry powder mould inhibitor, 2 parts of dispersing agent, 40 parts of colour stone powder, 13 parts of redispersible rubber powder, 1.5 parts of starch ether, fine
Plain 4 parts of the ether of dimension, 13 parts of xanthan gum, 15 parts of nano-titanium dioxide, 14 parts of zeolite, 1.5 parts of graphene, 10 parts of high hydroscopic resin, from
7 parts of sub-exchange resin.
Comparative example 5
A kind of interior wall moistureproof and mildewproof color lacquer putty of the present embodiment, including 550 parts of white cement, 450 parts of powdered whiting, wood
It is 6 parts of calcium, 5 parts of dry powder mould inhibitor, 2 parts of dispersing agent, 40 parts of colour stone powder, 13 parts of redispersible rubber powder, 1.5 parts of starch ether, fine
Plain 4 parts of the ether of dimension, 13 parts of xanthan gum, 15 parts of nano-titanium dioxide, 7 parts of active carbon, 7 parts of zeolite, 1.5 parts of graphene.
By above-described embodiment and comparative example construction under identical environment, its performance is tested.
By test, embodiment 1-3 can have the function that eliminate formaldehyde well have preferable hygroscopic capacity, thus
Guarantee indoor environment humidity, moistureproof and mildewproof；Graphene is not added in comparative example 2 can make Formaldehyde decomposition reduced capability, indoor formaldehyde
Content increases；Comparative example 3 and comparative example 4 use merely active carbon and zeolite, and formaldehyde adsorption ability reduces, use of not arranging in pairs or groups
Effect is good, and content of formaldehyde equally increases；Ion exchange resin is not added in comparative example 1, hygroscopic capacity lowers, and dampproof effect becomes
Difference is not added with high hydroscopic resin in comparative example 5, substantially without moisture protection.
In conclusion having the effect of moistureproof and mildewproof, and energy using a kind of interior wall moistureproof and mildewproof color lacquer putty of the invention
Enough absorb decomposes the pernicious gases such as indoor formaldehyde；It is reasonably combined to keep moisture protection strong, and harmful gas such as absorb decomposing formaldehyde
The effect of body is good；Effect is beautiful, and only needs a coating, is not required to brushing emulsion paint again, save the cost.
The invention is not limited to specific embodiments above-mentioned.The present invention, which expands to, any in the present specification to be disclosed
New feature or any new combination, and disclose any new method or process the step of or any new combination.
Claims (10)
1. a kind of interior wall moistureproof and mildewproof color lacquer putty, it is characterised in that: it by weight include white cement 500-600 parts, it is inorganic to fill out
400-500 parts of material, 3-10 parts of calcium lignosulfonate, 4-6 parts of dry powder mould inhibitor, 2-3 parts of dispersing agent, 30-50 parts of colour stone powder, redispersible
10-15 parts of rubber powder, 1-2 parts of starch ether, 3-5 parts of cellulose ether, 10-15 parts of xanthan gum, 10-20 parts of nano-titanium dioxide, activity
5-10 parts of charcoal, 5-10 parts of zeolite, 1-2 parts of graphene, 8-12 parts of high hydroscopic resin.
2. interior wall moistureproof and mildewproof color lacquer putty as described in claim 1, it is characterised in that: the inorganic filler is lightweight carbonic acid
One of calcium, powdered whiting and talcum powder are a variety of.
3. interior wall moistureproof and mildewproof color lacquer putty as described in claim 1, it is characterised in that: the starch ether is hydroxypropul starch
Ether.
4. interior wall moistureproof and mildewproof color lacquer putty as described in claim 1, it is characterised in that: the nano-titanium dioxide is rutile titania
Type nano-titanium dioxide.
5. interior wall moistureproof and mildewproof color lacquer putty as described in claim 1, it is characterised in that: the nano-titanium dioxide is to pass through
The nano-titanium dioxide of doping techniques progress visible light-inducing.
6. interior wall moistureproof and mildewproof color lacquer putty as described in claim 1, it is characterised in that: the zeolite is modified zeolite.
7. interior wall moistureproof and mildewproof color lacquer putty as claimed in claim 6, it is characterised in that: the zeolite is the modified boiling of HDTMA
Stone.
8. interior wall moistureproof and mildewproof color lacquer putty as described in claim 1, it is characterised in that: the active carbon is shell activity
Charcoal.
9. interior wall moistureproof and mildewproof color lacquer putty as described in claim 1, it is characterised in that: further include in the color lacquer putty from
Sub-exchange resin is arranged in pairs or groups with high hydroscopic resin and is used.
10. interior wall moistureproof and mildewproof color lacquer putty as claimed in claim 9, it is characterised in that: the weight of the ion exchange resin
Amount is the 50-80% of high hydroscopic resin.