CN107572900A - A kind of tasteless environment-friendly dry powder diatom ooze and preparation method thereof - Google Patents
A kind of tasteless environment-friendly dry powder diatom ooze and preparation method thereof Download PDFInfo
- Publication number
- CN107572900A CN107572900A CN201710994038.9A CN201710994038A CN107572900A CN 107572900 A CN107572900 A CN 107572900A CN 201710994038 A CN201710994038 A CN 201710994038A CN 107572900 A CN107572900 A CN 107572900A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatom ooze
- dry powder
- mesh
- tasteless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of tasteless environment-friendly dry powder diatom ooze and preparation method thereof, the dry powder diatom ooze includes the component of following mass parts：Tasteless 3~7 parts of redispersable latex powder, 20~40 parts of diatomite, 1~6 part of nano titanium oxide, 1~30 part of titanium dioxide, 10~35 parts of grey calcium, 10~30 parts of coarse whiting, 5~45 parts of silica flour, 10~30 parts of kaolin, 0.3~1 part of hydroxypropyl methyl cellulose ether, 0.1~0.5 part of starch ether；It is obtained by the way that the component is well mixed.Tasteless redispersable latex powder is added as main bonding material in the tasteless environment-friendly dry powder diatom ooze of the present invention, and acted synergistically with other components, so that dry powder diatom ooze is tasteless, containing extremely low harmful substance, there is high-adhesion energy, good film formation at low temp performance etc..
Description
Technical field
The invention belongs to the technical field of building coating, and in particular to a kind of tasteless environment-friendly dry powder diatom ooze and its preparation
Method.
Background technology
With the high speed development of society, people require more and more higher, art coatings, wall to the environmental-protecting performance of decorations
Paper, emulsion paint etc. can meet the requirement of aesthetic property, but more serious for the damage ratio of room air, can influence the body of human body
Heart health, therefore diatom ooze arises at the historic moment.
Diatom ooze (Diatom mud) is a kind of green inner wall decoration wall material using diatomite as main raw material(s), and it has
Eliminate the functions such as formaldehyde, purification air, regulation humidity, releasing negative oxygen ion, fire protection flame retarding, the self-cleaning, deodorization and sterilization of metope.
But current diatom ooze has the problem of more, smell is larger before and after construction, and content of formaldehyde is higher, adhesive property
Difference, easily there is dry linting phenomenon.
The content of the invention
In order to solve the above technical problems, it is an object of the invention to provide a kind of tasteless environment-friendly dry powder diatom ooze and its system
Preparation Method, any smell will not be given out before and after diatom ooze construction, the content of harmful substance is extremely low, it may have adsorption-decomposition function first
The effect of aldehyde, indoor humidity can be adjusted, it is high to the adhesive force of base material, the features such as storage transport and construction is simple.
Specifically, the invention provides a kind of tasteless environment-friendly dry powder diatom ooze, the dry powder diatom ooze to include following quality
The component of part：Tasteless 3~7 parts of redispersable latex powder, 20~40 parts of diatomite, 1~6 part of nano titanium oxide, titanium dioxide 1
~30 parts, 10~35 parts of grey calcium, 10~30 parts of coarse whiting, 5~45 parts of silica flour, 10~30 parts of kaolin, hydroxypropyl methyl fiber
Plain 0.3~1 part of ether, 0.1~0.5 part of starch ether.
Further, the tasteless redispersable latex powder is 6088G rubber powders.6088G rubber powders do not have any bad gas
Taste, so as to get dry powder diatom ooze there is no smell, and its adhesion strength and moisture absorption and desorption property also increase.
Further, the diatomite is one kind in non-calcinated diatomite or calcined diatomite, and diatomaceous mesh number is
325~1250 mesh.
Further, the particle diameter of the nano titanium oxide is 5~10nm.
Further, the titanium dioxide is one kind in rutile type titanium white or anatase thpe white powder.
Further, whiteness >=90 of the grey calcium, mesh number are 325~1000 mesh.
Further, the coarse whiting is the one or more in 400 mesh, 800 mesh, 1250 mesh.
Further, the silica flour is the one or more in 20~40 mesh, 40~80 mesh, 80~120 mesh, 320 mesh.
Further, the kaolin is calcined kaolin, and mesh number is 1250 mesh or 3000 mesh.
Second aspect, present invention also offers a kind of preparation method of the tasteless environment-friendly dry powder diatom ooze, this method
Comprise the following steps：By tasteless redispersable latex powder, diatomite, nano titanium oxide, titanium dioxide, the ash of the mass parts
Calcium, coarse whiting, silica flour, kaolin, hydroxypropyl methyl cellulose ether, starch ether are added in dry-mixed machine, are sufficiently mixed uniformly, i.e.,
The dry powder diatom ooze can be obtained.
Beneficial effects of the present invention are：Tasteless redispersible breast is added in the tasteless environment-friendly dry powder diatom ooze of the present invention
Rubber powder is as main bonding material, tasteless redispersable latex powder and other components synergy so that dry powder diatom ooze is
It is tasteless, containing extremely low harmful substance, there is high-adhesion energy, good film formation at low temp performance etc..
Embodiment
Technical solution of the present invention is illustrated to be clearer, the skill below in conjunction with embodiment to the present invention
Art scheme is further elaborated：
In the specific embodiment of the present invention, the invention provides a kind of tasteless environment-friendly dry powder diatom ooze,
The dry powder diatom ooze includes the component of following mass parts：Tasteless 3~7 parts of redispersable latex powder, diatomite 20~40 part, nanometer
1~6 part of titanium dioxide, 1~30 part of titanium dioxide, 10~35 parts of grey calcium, 10~30 parts of coarse whiting, 5~45 parts of silica flour, kaolin
10~30 parts, 0.3~1 part of hydroxypropyl methyl cellulose ether, 0.1~0.5 part of starch ether.
Further, the tasteless redispersable latex powder of addition is 6088G rubber powders, and 6088G rubber powders are based on VAE
Water-based redispersable latex powder, be that Beijing treasured occasion joint Science and Technology Co., Ltd. specially researches and develops it is a kind of it is tasteless, environment-friendly type is newborn
Rubber powder, suitable for the application field high to environmental requirement.
Further, the diatomite is one kind in non-calcinated diatomite or calcined diatomite, and mesh number is 325~1250
Mesh.
Further, the particle diameter of the nano titanium oxide is 5~10nm.Because diatom ooze only adsorbs in itself, do not have
Degradation of organic substances function, after saturation absorption is reached, adsorbed pernicious gas material understands some desorption, it is possible to weight
Newly disengage.Nano titanium oxide can make up the defects of diatom ooze, and nano titanium oxide is supported on into diatom ooze particle surface,
Its light-catalysed characteristic is played under the light sources such as sunlight, room fluorescent lights, be able to can also not only be risen with pernicious gases such as formaldehyde adsorptions
To the effect of degraded, the air pollution brought so as to the finishing in thorough decomposition chamber.
Further, the titanium dioxide is one kind in rutile type titanium white or anatase thpe white powder.Titanium dioxide is made
The whiteness and covering power of diatom ooze can be improved for Chinese white.
Further, whiteness >=90 of the grey calcium, mesh number are 325~1000 mesh.Grey calcium, can as inorganic coagulation material
To significantly improve the adhesion strength of diatom ooze.
Further, the coarse whiting is the one or more in 400 mesh, 800 mesh, 1250 mesh.Coarse whiting improves diatom ooze
The hardness and wearability of surface film.
Preferably, the silica flour is the one or more in 20~40 mesh, 40~80 mesh, 80~120 mesh, 320 mesh.Root
According to the difference of done diatom ooze moulding, the silica flour of different meshes and volume is added, and is favorably improved the bonding of diatom ooze
Performance.
Further, kaolin is calcined kaolin, and mesh number is 1250 mesh or 3000 mesh.
In another specific embodiment of the present invention, the invention provides a kind of tasteless environment-friendly dry powder silicon
The preparation method of algal gel, this method comprise the following steps：By the tasteless redispersable latex powder for stating mass parts, diatomite,
Nano titanium oxide, titanium dioxide, grey calcium, coarse whiting, silica flour, kaolin, hydroxypropyl methyl cellulose ether, starch ether are added to
In dry-mixed machine, it is sufficiently mixed uniformly, you can obtain the dry powder diatom ooze.Then according to different shaping, amount of water is 40~80%
Between, it is added into water and uniformly stirred construction usage.
Above-mentioned embodiment is further illustrated below by embodiment, but is not therefore limited the present invention to described
Scope of embodiments among.The experimental method of unreceipted actual conditions in the following example, conventionally and condition, or press
Selected according to catalogue.
6088G rubber powders are the special rubber powder of diatom ooze purchased from Beijing treasured occasion joint Science and Technology Co., Ltd., other not do
Reagent, raw material and the instrument and equipment of special instruction can directly be bought by commercial sources.
Embodiment 1
A kind of tasteless environment-friendly dry powder diatom ooze includes the component of following mass parts：3 parts of 6088G rubber powders, 20 parts of diatomite,
1 part of nano titanium oxide, 1 part of titanium dioxide, 10 parts of grey calcium, 10 parts of coarse whiting, 5 parts of silica flour, 10 parts of kaolin, hydroxypropyl methyl
0.3 part of cellulose ether, 0.1 part of starch ether.
Wherein, the diatomite is the non-calcinated diatomite of 325~1250 purposes；The particle diameter of the nano titanium oxide is 5
~10nm；The titanium dioxide is rutile type titanium white；Whiteness >=90 of the grey calcium, mesh number are 325~1000 mesh；It is described
Coarse whiting is two kinds in 400 mesh, 800 mesh；The mesh number of the silica flour is 20~40 mesh；The kaolin is the calcining of 1250 mesh
Kaolin.
The preparation method of above-mentioned tasteless environment-friendly dry powder diatom ooze comprises the following steps：By the 6088G glue of above-mentioned mass parts
Powder, diatomite, nano titanium oxide, titanium dioxide, grey calcium, coarse whiting, silica flour, kaolin, hydroxypropyl methyl cellulose ether, shallow lake
Powder ether is added in dry-mixed machine, is sufficiently mixed uniformly, you can obtain the dry powder diatom ooze.
Embodiment 2
A kind of tasteless environment-friendly dry powder diatom ooze includes the component of following mass parts：6 parts of 6088G rubber powders, 30 parts of diatomite,
3 parts of nano titanium oxide, 2 parts of titanium dioxide, 20 parts of grey calcium, 20 parts of coarse whiting, 15 parts of silica flour, 20 parts of kaolin, hydroxypropyl first
0.5 part of base cellulose ether, 0.2 part of starch ether.
Wherein, the diatomite is the non-calcinated diatomite of 325~1250 purposes；The particle diameter of the nano titanium oxide is 5
~10nm；The titanium dioxide is anatase thpe white powder；Whiteness >=90 of the grey calcium, mesh number are 325~1000 mesh；It is described heavy
The mesh number of calcium is 1250 mesh；The silica flour is two kinds in 40~80 mesh, 80~120 mesh；The kaolin is 3000 purposes
Calcined kaolin.
The preparation method of above-mentioned tasteless environment-friendly dry powder diatom ooze comprises the following steps：By the 6088G glue of above-mentioned mass parts
Powder, diatomite, nano titanium oxide, titanium dioxide, grey calcium, coarse whiting, silica flour, kaolin, hydroxypropyl methyl cellulose ether, shallow lake
Powder ether is added in dry-mixed machine, is sufficiently mixed uniformly, you can obtain the dry powder diatom ooze.
Embodiment 3
A kind of tasteless environment-friendly dry powder diatom ooze includes the component of following mass parts：7 parts of 6088G rubber powders, 40 parts of diatomite,
6 parts of nano titanium oxide, 30 parts of titanium dioxide, 35 parts of grey calcium, 30 parts of coarse whiting, 45 parts of silica flour, 30 parts of kaolin, hydroxypropyl first
1 part of base cellulose ether, 0.5 part of starch ether.
Wherein, the diatomite is the non-calcinated diatomite of 325~1250 purposes；The particle diameter of the nano titanium oxide is 5
~10nm；The titanium dioxide is anatase thpe white powder；Whiteness >=90 of the grey calcium, mesh number are 325~1000 mesh；It is described heavy
The mesh number of calcium is 800 mesh；The mesh number of the silica flour is 320 mesh；The kaolin is the calcined kaolin of 1250 mesh.
The preparation method of above-mentioned tasteless environment-friendly dry powder diatom ooze comprises the following steps：By the 6088G glue of above-mentioned mass parts
Powder, diatomite, nano titanium oxide, titanium dioxide, grey calcium, coarse whiting, silica flour, kaolin, hydroxypropyl methyl cellulose ether, shallow lake
Powder ether is added in dry-mixed machine, is sufficiently mixed uniformly, you can obtain the dry powder diatom ooze.
Comparative example 1
A kind of dry powder diatom ooze includes the component of following mass parts：6 parts of import EVA rubber powders, 30 parts of diatomite, nano-silica
Change 3 parts of titanium, 2 parts of titanium dioxide, 20 parts of grey calcium, 20 parts of coarse whiting, 15 parts of silica flour, 20 parts of kaolin, hydroxypropyl methyl cellulose
0.5 part of ether, 0.2 part of starch ether.
Preparation method is the same as embodiment 1.
Comparative example 2
A kind of dry powder diatom ooze includes the component of following mass parts：Domestic 6 parts of EVA rubber powders, 30 parts of diatomite, nano-silica
Change 3 parts of titanium, 2 parts of titanium dioxide, 20 parts of grey calcium, 20 parts of coarse whiting, 15 parts of silica flour, 20 parts of kaolin, hydroxypropyl methyl cellulose
0.5 part of ether, 0.2 part of starch ether.
Preparation method is the same as embodiment 1.
Comparative example 3
A kind of dry powder diatom ooze includes the component of following mass parts：6 parts of pure third rubber powder of import, part, nanometer two of diatomite 30
3 parts of titanium oxide, 2 parts of titanium dioxide, 20 parts of grey calcium, 20 parts of coarse whiting, 15 parts of silica flour, 20 parts of kaolin, hydroxypropyl methyl fiber
Plain 0.5 part of ether, 0.2 part of starch ether.
Preparation method is the same as embodiment 1.
Comparative example 4
A kind of dry powder diatom ooze includes the component of following mass parts：6 parts of import EVA rubber powders, 30 parts of diatomite, nano-silica
Change 3 parts of titanium, 2 parts of titanium dioxide, 20 parts of grey calcium, 20 parts of coarse whiting, 15 parts of silica flour, 20 parts of kaolin, hydroxypropyl methyl cellulose
0.5 part of ether, 0.2 part of starch ether.
Preparation method is the same as embodiment 1.
The performance test results
Performance test is carried out to embodiment 1-3 and comparative example 1-4, test result is as shown in Table 1 and Table 2.
Table 1
Table 2
As shown in table 1-2, added in dry powder diatom ooze of the invention for tasteless redispersable latex powder, dry powder can be made
Diatom ooze finished product does not contain any smell, it is not necessary to adds eliminating smell agent or essence, you can reaches demand of the market to smell；And
And dry powder diatom ooze does not have smell not only, while nano titanium oxide is added, the filler such as diatomite also ensure that diatom ooze
Feature, the adhesion strength of dry powder diatom ooze of the invention is high and has splendid moisture absorption and desorption property.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Any modification, equivalent substitution and simple modifications for being made in content etc., should be included in the scope of the protection.
Claims (10)
1. a kind of tasteless environment-friendly dry powder diatom ooze, it is characterised in that the dry powder diatom ooze includes the component of following mass parts：Nothing
3~7 parts of taste redispersable latex powder, 20~40 parts of diatomite, 1~6 part of nano titanium oxide, 1~30 part of titanium dioxide, grey calcium
10~35 parts, 10~30 parts of coarse whiting, 5~45 parts of silica flour, 10~30 parts of kaolin, hydroxypropyl methyl cellulose ether 0.3~1
Part, 0.1~0.5 part of starch ether.
2. tasteless environment-friendly dry powder diatom ooze according to claim 1, it is characterised in that the tasteless Redispersable latex
Powder is 6088G rubber powders.
3. tasteless environment-friendly dry powder diatom ooze according to claim 1, it is characterised in that the diatomite is non-calcinated silicon
One kind in diatomaceous earth or calcined diatomite, mesh number are 325~1250 mesh.
4. tasteless environment-friendly dry powder diatom ooze according to claim 1, it is characterised in that the grain of the nano titanium oxide
Footpath is 5~10nm.
5. tasteless environment-friendly dry powder diatom ooze according to claim 1, it is characterised in that the titanium dioxide is rutile
One kind in type titanium dioxide or anatase thpe white powder.
6. tasteless environment-friendly dry powder diatom ooze according to claim 1, it is characterised in that whiteness >=90 of the grey calcium,
Mesh number is 325~1000 mesh.
7. tasteless environment-friendly dry powder diatom ooze according to claim 1, it is characterised in that the coarse whiting is 400 mesh, 800
One or more in mesh, 1250 mesh.
8. tasteless environment-friendly dry powder diatom ooze according to claim 1, it is characterised in that the silica flour is 20~40
One or more in mesh, 40~80 mesh, 80~120 mesh, 320 mesh.
9. tasteless environment-friendly dry powder diatom ooze according to claim 1, it is characterised in that the kaolin is calcining kaolinite
Soil, mesh number are 1250 mesh or 3000 mesh.
A kind of 10. method for preparing tasteless environment-friendly dry powder diatom ooze described in claim 1, it is characterised in that this method includes
Following steps：By the tasteless redispersable latex powder of the mass parts, diatomite, nano titanium oxide, titanium dioxide, grey calcium,
Coarse whiting, silica flour, kaolin, hydroxypropyl methyl cellulose ether, starch ether are added in dry-mixed machine, are sufficiently mixed uniformly, you can
Obtain the dry powder diatom ooze.