CN104312342A - Environmentally-friendly interior wall coating and preparation method thereof - Google Patents
Environmentally-friendly interior wall coating and preparation method thereof Download PDFInfo
- Publication number
- CN104312342A CN104312342A CN201410494234.6A CN201410494234A CN104312342A CN 104312342 A CN104312342 A CN 104312342A CN 201410494234 A CN201410494234 A CN 201410494234A CN 104312342 A CN104312342 A CN 104312342A
- Authority
- CN
- China
- Prior art keywords
- parts
- deionized water
- environment
- absorbent resin
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environmentally-friendly interior wall coating, and belongs to the field of building materials. The coating includes 30-35 parts of deionized water, 10-15 parts of a pure acrylic emulsion, 10-20 parts of titanium dioxide powder, 10-15 parts of shell powder, 0.1-0.4 parts of a dispersant, 0.1-0.4 parts of an antifoaming agent, 0.1-0.5 parts of chitosan oligosaccharide, 0.1-0.8 parts of nanometer TiO2, 0.2-0.5 parts of a thickener, and 4-6 parts of water-absorbent resin. The environmentally-friendly interior wall coating has the efficacies of heat insulation, bacteriostasis, formaldehyde adsorption, peculiar smell elimination, air humidity adjustment and electrostatic prevention, and is used for coating interior walls of rooms, classrooms, offices and hospitals.
Description
Technical field
The invention belongs to building material field, be specifically related to a kind of Environment-friendlyinternal internal wall paint and preparation method thereof.
Background technology
Along with the enforcement of country about environmental protection and energy saving policy and the raising of people's living standard, the environmental protection and energy saving of people are realized and obviously strengthen the pursuit of health, to the comfort level of life living environment, Safety and Environmental Protection requires more and more higher, room temp and relative air humidity are the important environmental parameters of life 2 of comfort level, when room temp is 20 DEG C ~ 23 DEG C, when relative air humidity is 50 ~ 60%, human body sensory the most comfortable, indoor VOC concentration lower soluble heavy metal content is fewer, its feature of environmental protection is better, indoor aseptic (or few bacterium) is without microbial reproduction and survival, for health of human body creates condition.
Traditional interior wall coating is because of containing objectionable impurities, and the particularly obnoxious flavour such as formaldehyde, long-term hazards people's is healthy, and will gradually by market.
The beneficial effect of oyster shell whiting: (1) purifies air, oyster shell whiting subparticle through calcination processing is porous fibrous double helix structure, the peculiar smell effectively can removed the objectionable impurities such as free formaldehyde, benzene, ammonia in air and produce because of pet, smoking, rubbish, purifies the air of a room.(2) odor function is eliminated, the compound of calcium is used for deodovization agent in life, therefore the assorted taste of smell and indoor that oyster shell whiting can distribute indoor smoke, patient infant, pet, mould all has effectively dispels effect, especially has adsorption to the carbon monoxide that cigarette distributes in indoor with the Dust Capacity that swims.(3) antibacterial, bacteriostatic action, has extremely strong antibacterial and germicidal action through the special oyster shell whiting film firing process to intestinal bacteria, also has remarkable effect in addition to Salmonellas, yellow glucose fungus.Not only there is high performance germ resistance, and there is the function of anticorrosion, anti-flat lice.(4) antistatic performance, the biological coating of oyster shell whiting is with the natural many microtextures duct shell through special processing for starting material, and its composition 100% is calcium, therefore has good antistatic performance.(5) adjusting air humidity, unique " aquatic respiration " function, through the oyster shell whiting of calcination processing from as high intensity, porous structure, so there is good aquatic respiration function, at subatmospheric, under high humidity state, metope does not condense, and when drying, the moisture stored within the walls slowly can be discharged.Therefore its respiratory function is the conditioning agent of indoor humidity, prevents the generation of condensation and microorganism, so be described as the coating of " can breathe ".
Summary of the invention
The invention provides a kind of Environment-friendlyinternal internal wall paint and preparation method thereof, to make up the deficiencies in the prior art.
A kind of Environment-friendlyinternal internal wall paint, comprises following component: deionized water 30-35 part, pure-acrylic emulsion 10-15 part, titanium dioxide 10-20 part, oyster shell whiting 10-15 part, dispersion agent 0.1-0.4 part, defoamer 0.1-0.4 part, oligochitosan 0.1-0.5 part, nano-TiO
20.1-0.8 part, thickening material 0.2-0.5 part, absorbent resin 4-6 part.
Further, described absorbent resin is one or more in polyacrylate, polyacrylamide, acrylic acid-acrylamide copolymer.
A kind of Environment-friendlyinternal internal wall paint, its preparation method comprises the steps:
(1) deionized water of 1/2, oyster shell whiting, dispersion agent are added in dispersion cylinder stir 30 min, add nano-TiO
2powder, high speed dispersion 1 h, then through repeatedly grinding particle diameter is less than the nano slurry of 100 nm;
(2) with the deionized water of 1/4, absorbent resin is dissolved into solution;
(3) residue deionized water is added in Scattered Kettle, add nano slurry, titanium dioxide, oligochitosan, absorbent resin solution stirring, high speed dispersion 45min, reach the slurry of 50 nm through mesh-of-grind;
(4) squeeze in paint mixing tank by ground slurry, middle stirring at low speed adds pure-acrylic emulsion, defoamer, thickening material, filters discharging after stirring.
Beneficial effect of the present invention is: this environment-friendly type coating has effect of insulation, antibacterial, formaldehyde adsorption, elimination peculiar smell, adjusting air humidity, anti-electrostatic, for the application of the interior walls such as room, classroom, office, hospital.
Embodiment
Embodiment 1
A kind of Environment-friendlyinternal internal wall paint, described coating comprises following component: deionized water 30 parts, pure-acrylic emulsion 10 parts, titanium dioxide 10 parts, oyster shell whiting 10 parts, dispersion agent 0.1 part, defoamer 0.2 part, oligochitosan 0.2 part, nano-TiO
20.3 part, thickening material 0.2 part, polyacrylate 4 parts.
A kind of Environment-friendlyinternal internal wall paint, its preparation method comprises the steps:
(1) deionized water of 1/2, oyster shell whiting, dispersion agent are added in dispersion cylinder stir 30 min, add nano-TiO
2powder, high speed dispersion 1 h, then through repeatedly grinding particle diameter is less than the nano slurry of 100 nm;
(2) with the deionized water of 1/4, absorbent resin is dissolved into solution;
(3) residue deionized water is added in Scattered Kettle, add nano slurry, titanium dioxide, oligochitosan, absorbent resin solution stirring, high speed dispersion 45min, reach the slurry of 50 nm through mesh-of-grind;
(4) squeeze in paint mixing tank by ground slurry, middle stirring at low speed adds pure-acrylic emulsion, defoamer, thickening material, filters discharging after stirring.
This environment-friendly type coating has effect of insulation, antibacterial, formaldehyde adsorption, elimination peculiar smell, adjusting air humidity, anti-electrostatic, for the application of the interior walls such as room, classroom, office, hospital.
Embodiment 2
A kind of Environment-friendlyinternal internal wall paint, described coating comprises following component: deionized water 35 parts, pure-acrylic emulsion 15 parts, titanium dioxide 20 parts, oyster shell whiting 15 parts, dispersion agent 0.4 part, defoamer 0.4 part, oligochitosan 0.5 part, nano-TiO
20.8 part, thickening material 0.5 part, polyacrylamide 6 parts.
A kind of Environment-friendlyinternal internal wall paint, its preparation method comprises the steps:
(1) deionized water of 1/2, oyster shell whiting, dispersion agent are added in dispersion cylinder stir 30 min, add nano-TiO
2powder, high speed dispersion 1 h, then through repeatedly grinding particle diameter is less than the nano slurry of 100 nm;
(2) with the deionized water of 1/4, absorbent resin is dissolved into solution;
(3) residue deionized water is added in Scattered Kettle, add nano slurry, titanium dioxide, oligochitosan, absorbent resin solution stirring, high speed dispersion 45min, reach the slurry of 50 nm through mesh-of-grind;
(4) squeeze in paint mixing tank by ground slurry, middle stirring at low speed adds pure-acrylic emulsion, defoamer, thickening material, filters discharging after stirring.
This environment-friendly type coating has effect of insulation, antibacterial, formaldehyde adsorption, elimination peculiar smell, adjusting air humidity, anti-electrostatic, for the application of the interior walls such as room, classroom, office, hospital.
Embodiment 3
A kind of Environment-friendlyinternal internal wall paint, described coating comprises following component: deionized water 32 parts, pure-acrylic emulsion 12 parts, titanium dioxide 15 parts, oyster shell whiting 12 parts, dispersion agent 0.3 part, defoamer 0.3 part, oligochitosan 0.3 part, nano-TiO
20.6 part, thickening material 0.4 part, acrylic acid-acrylamide copolymer 5 parts.
A kind of Environment-friendlyinternal internal wall paint, its preparation method comprises the steps:
(1) deionized water of 1/2, oyster shell whiting, dispersion agent are added in dispersion cylinder stir 30 min, add nano-TiO
2powder, high speed dispersion 1 h, then through repeatedly grinding particle diameter is less than the nano slurry of 100 nm;
(2) with the deionized water of 1/4, absorbent resin is dissolved into solution;
(3) residue deionized water is added in Scattered Kettle, add nano slurry, titanium dioxide, oligochitosan, absorbent resin solution stirring, high speed dispersion 45min, reach the slurry of 50 nm through mesh-of-grind;
(4) squeeze in paint mixing tank by ground slurry, middle stirring at low speed adds pure-acrylic emulsion, defoamer, thickening material, filters discharging after stirring.
This environment-friendly type coating has effect of insulation, antibacterial, formaldehyde adsorption, elimination peculiar smell, adjusting air humidity, anti-electrostatic, for the application of the interior walls such as room, classroom, office, hospital.
Claims (3)
1. an Environment-friendlyinternal internal wall paint, it is characterized in that, comprise following component: deionized water 30-35 part, pure-acrylic emulsion 10-15 part, titanium dioxide 10-20 part, oyster shell whiting 10-15 part, dispersion agent 0.1-0.4 part, defoamer 0.1-0.4 part, oligochitosan 0.1-0.5 part, nano-TiO
20.1-0.8 part, thickening material 0.2-0.5 part, absorbent resin 4-6 part.
2. a kind of Environment-friendlyinternal internal wall paint according to claim 1, is characterized in that, described absorbent resin is one or more in polyacrylate, polyacrylamide, acrylic acid-acrylamide copolymer.
3. a kind of Environment-friendlyinternal internal wall paint according to claim 1, is characterized in that, the preparation method of described Environment-friendlyinternal internal wall paint comprises the steps:
(1) deionized water of 1/2, oyster shell whiting, dispersion agent are added in dispersion cylinder stir 30 min, add nano-TiO
2powder, high speed dispersion 1 h, then through repeatedly grinding particle diameter is less than the nano slurry of 100 nm;
(2) with the deionized water of 1/4, absorbent resin is dissolved into solution;
(3) residue deionized water is added in Scattered Kettle, add nano slurry, titanium dioxide, oligochitosan, absorbent resin solution stirring, high speed dispersion 45min, reach the slurry of 50 nm through mesh-of-grind;
(4) squeeze in paint mixing tank by ground slurry, middle stirring at low speed adds pure-acrylic emulsion, defoamer, thickening material, filters discharging after stirring.