CN109354915A - The environmental protection type nano material multifunctional water and preparation method thereof of the water-soluble finishing product of dilution - Google Patents
The environmental protection type nano material multifunctional water and preparation method thereof of the water-soluble finishing product of dilution Download PDFInfo
- Publication number
- CN109354915A CN109354915A CN201811197520.0A CN201811197520A CN109354915A CN 109354915 A CN109354915 A CN 109354915A CN 201811197520 A CN201811197520 A CN 201811197520A CN 109354915 A CN109354915 A CN 109354915A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- water
- environmental protection
- protection type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of environmental protection type nano material multifunctional waters and preparation method thereof of the water-soluble finishing product of dilution, and the raw material components of multifunctional water include: nanometer anion powder 1.3-2.6 parts by weight, nano-silver ionic 0.6-1.2 parts by weight, the white bamboo charcoal powder 0.9-1.8 parts by weight of nanometer, nanometer titanium dioxide titanium valve 0.7-1.4 parts by weight, nano medical stone powder 0.8-1.6 parts by weight, nano-tourmaline powder 0.5-1.0 parts by weight, dehydroactic acid sodium 1.0-2.0 parts by weight, sodium cellulosate 0.2-0.4 parts by weight, dispersing agent 1.0-2.0 parts by weight and water 93-186 parts by weight by weight.Environmental protection type nano material multifunctional water provided by the invention can replace water to dilute water-soluble finishing product, can effectively inhibit fungus growth and prevent from going mouldy, and will not influence the service performance that water-soluble finishing product itself has；And the function of having releasing negative oxygen ion and far infrared.
Description
Technical field
The present invention relates to field of material technology, and in particular to a kind of environmental protection type nano material of the water-soluble finishing product of dilution
Multifunctional water and preparation method thereof.
Background technique
In fitment process, many water-soluble products for example white glue with vinyl, emulsion paint, Wall paper adhesive, building adhesive, interface treating agent,
108 glue, glutinous rice glue, adhesive powder for wall paper, glue for tile etc. are required to be diluted with water.It is unclean in dirty and messy construction in dilution
Water and dust will cause the secondary pollution of product, thus to finishing after product hide some dangers for, such as will lead to finishing after
The generation for the situations such as metope blacks, is smelly, and wallpaper goes mouldy, falls off, this has not only broken up the beauty of indoor environment, also polluted ring
Border has extremely serious influence to the health of human body.These problems annoying vast user and construction team for a long time.
Can develop can replace water to dilute the substance of water-soluble finishing product, be urgent problem.
Summary of the invention
For the defects in the prior art, it is an object of that present invention to provide a kind of environment-friendly types of the water-soluble finishing product of dilution
Nano material multifunctional water and preparation method thereof, the environmental protection type nano material multifunctional water can replace water to dilute water-soluble finishing
Product can effectively inhibit fungus growth and prevent from going mouldy, and will not influence the service performance that water-soluble finishing product itself has；
And the function of having releasing negative oxygen ion and far infrared.
To achieve the above object, technical solution provided by the invention are as follows:
The present invention provides a kind of environmental protection type nano material multifunctional waters, and raw material components are by weight, comprising: nanometer is negative
Ion powder 1.3-2.6 parts by weight, nano-silver ionic 0.6-1.2 parts by weight, the white bamboo charcoal powder 0.9-1.8 parts by weight of nanometer, nanometer two
Titanium oxide powder 0.7-1.4 parts by weight, dehydroactic acid sodium 1.0-2.0 parts by weight, sodium cellulosate 0.2-0.4 parts by weight, dispersing agent
1.0-2.0 parts by weight and water 93-186 parts by weight.
Preferably, raw material components further include: nano medical stone powder 0.8-1.6 parts by weight and nano-tourmaline powder 0.5-1.0
Parts by weight.
Preferably, the raw material components of environmental protection type nano material multifunctional water are by weight, comprising: nanometer anion powder
White 1.4 parts by weight of bamboo charcoal powder of 1.9 parts by weight, 0.9 parts by weight of nano-silver ionic, nanometer, 1.0 parts by weight of nanometer titanium dioxide titanium valve,
1.2 parts by weight of nano medical stone powder, 0.75 parts by weight of nano-tourmaline powder, 1.5 parts by weight of dehydroactic acid sodium, sodium cellulosate 0.3
138 parts by weight of parts by weight, 1.5 parts by weight of dispersing agent and water.
Preferably, dehydroactic acid sodium is food-grade sodium dehydroacetate.
Preferably, sodium cellulosate is food-grade cellulose element sodium.
Preferably, dispersing agent is cosmetics-stage dispersing agent；Water is pure water.
Sodium cellulosate that the present invention uses, dehydroactic acid sodium are food rank, and dispersing agent is then cosmetics rank, nanometer
White bamboo charcoal powder, nano-tourmaline powder, nano medical stone powder, nano-silver ionic are natural component, will not be generated to human body any
Injury；And the natural antibacterial agent nanometer of most representative nano-titanium dioxide and latest generation is selected in photocatalyst material
Silver ion is leading electrical with other nano materials such as white bamboo charcoal powder of nanometer anion powder, nanometer, nano medical stone powder and nanometer
Under the collective effect of mountain flour, can effectively degrade the pollution such as the formaldehyde being diluted in product, benzene,toluene,xylene, ammonia, TVOC
Object, can broad-spectrum sterilization antibacterial, a variety of disinfect pathogens being detrimental to health are killed within short a few minutes.And have and its
Efficient extensive antiseptic property, the toxin that can release bacterium or fungi decomposes completely and innoxious cleaning.
The medical stone powder used in the present invention equally has extremely strong adsorptivity, is on the one hand because it is with silicate
It is main, there is good adsorptivity；It on the other hand is that porous sponge shape is special since medical stone contains the clay minerals such as kaolinite more
Structure has strong electrostatic attraction, has very strong adsorption capacity to heavy metal ion and cause evil toxin in water, can remove in water
The harmful substances such as the heavy metals such as mercury, lead, cadmium, arsenic, fluorine and chloride, cyanide, residues of banned pesticides, leucoaurin；Adsorption rate is same
20000 times of surface area activated carbon, to heavy metal adsorption rate and to the inhibiting rates of Escherichia coli up to 96% or more.
In addition, nanometer anion powder, the white bamboo charcoal powder of nanometer, nano-tourmaline powder that the present invention uses be also equipped with it is very excellent
The function of elegant releasing negative oxygen ion and far infrared can enhance the energy of cell, make cell for the cell tissue of human body
Activation helps old dead cell excretion or assigns its regenerated ability；For the circulatory system of human body, then expansion hair can be played
Thin blood vessel enhances blood circulation, and the effect to boost metabolism, this keeps energetic to human body, maintains health and changes
Kind human residential environment has highly significant help.
The present invention also provides the preparation methods of environmental protection type nano material multifunctional water, stir comprising steps of water is put into
In tank, then start to stir；Other surplus stock components are successively put into agitator tank according to metering, are divided at normal temperature
It dissipates；Mixture after dispersion is stirred at normal temperature；Mixture after stirring is subjected to qualification detection, then tank out,
Obtain environmental protection type nano material multifunctional water.
Preferably, the revolving speed of dispersion is greater than 1000 revs/min；The time of dispersion is 15-25 minutes.
Preferably, the time of stirring is 45-55 minutes；The revolving speed of stirring is 50-100 revs/min.
The present invention also protects application of the environmental protection type nano material multifunctional water in the water-soluble finishing product of dilution, water-soluble
Fit up product such as white glue with vinyl, 108 glue, glutinous rice glue, wallpaper rubber powder, emulsion paint and building adhesive etc..
Technical solution provided by the invention, have it is following the utility model has the advantages that
(1) environmental protection type nano material multifunctional water provided by the invention has photocatalyst, and the adhesive that can effectively degrade produces
The pollutants such as formaldehyde, benzene,toluene,xylene, ammonia, TVOC in product, make infringement of the people far from noxious material；
(2) environmental protection type nano material multifunctional water provided by the invention can effectively kill having of being detrimental to health and fall ill
Bacterium and fungi, and the toxin that bacterium and fungi are discharged can be decomposed safely and is made harmless treatment, wall can be eradicated
The phenomenon that smelly wallpaper mildew of face nigrescence etc. endangers living environment, escorts for the health of human body；
(3) environmental protection type nano material multifunctional water provided by the invention has very outstanding releasing negative oxygen ion and remote red
The function of outside line can enhance the energy of human body cell, make cell activation, and can expand the capillary of long human body, enhancing
Blood circulation boosts metabolism, and improves immune function of human body, makes one to keep energetic, play the role of health care；
(4) most of raw material that the present invention uses is natural component in nature, remaining material is food-grade
Cosmetic grade material, it is non-toxic to humans；
(5) environmental protection type nano material multifunctional water attribute provided by the invention is neutral, will not influence making for water-soluble products
Use performance；
(6) environmental protection type nano material multifunctional water provided by the invention is applied widely, is suitable for all water-soluble dresses
It repairs product dilution to use, such as white glue with vinyl, 108 glue, glutinous rice glue, wallpaper rubber powder, emulsion paint, building adhesive；
(7) structure of matter is stablized in environmental protection type nano material multifunctional water provided in the present invention, and property is mild, is easy to store up
Transport is deposited, it is safe and harmless；
(8) preparation flow of environmental protection type nano material multifunctional water provided by the invention is simple, has high efficiency, i.e.,
It is operated convenient for workpeople, and can be good at that enterprise is helped to create profit, there is good commercial value.
Additional aspect and advantage of the invention will be set forth in part in the description, and will partially become from the following description
Obviously, or practice through the invention is recognized.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical solution of the present invention is clearly and completely described.Implement below
Example is only used for clearly illustrating technical solution of the present invention, therefore is intended only as example, and cannot be used as a limitation and limit this hair
Bright protection scope.
Experimental method in following embodiments is unless otherwise specified conventional method.Examination as used in the following examples
Material is tested, is to be commercially available from regular shops unless otherwise specified.Quantitative test in following embodiment, is respectively provided with three
Secondary to repeat to test, data are the average value or mean+SD of three repeated experiments.
The each raw material component for preparing environmental protection type nano material multifunctional water of the present invention is according to parts by weight as matching, in life
When production can according to corresponding ratio increase or reduce, as large-scale production can by kilogram or as unit of ton, small-scale production
Can in grams, weight can increase or reduce, but the quality proportioning constant rate between each composition.
The present invention provides a kind of environmental protection type nano material multifunctional water, and raw material components are by weight, comprising: nanometer bear from
Sub- powder 1.3-2.6 parts by weight, nano-silver ionic 0.6-1.2 parts by weight, the white bamboo charcoal powder 0.9-1.8 parts by weight of nanometer, nano-silica
Change titanium valve 0.7-1.4 parts by weight, food-grade sodium dehydroacetate 1.0-2.0 parts by weight, food-grade cellulose element sodium 0.2-0.4 weight
Part, cosmetics-stage dispersing agent 1.0-2.0 parts by weight and pure water 93-186 parts by weight.
In further embodiment of the invention, raw material components further include: nano medical stone powder 0.8-1.6 parts by weight and
Nano-tourmaline powder 0.5-1.0 parts by weight.
In addition, including the following steps: the present invention also provides the preparation method of above-mentioned environmental protection type nano material multifunctional water
Water is put into agitator tank, then starts to stir；By other surplus stock components, according to metering, successively investment is stirred
In tank, high speed dispersion is carried out at normal temperature；The revolving speed of dispersion is greater than 1000 revs/min, and the time of dispersion is 15-25 minutes；
Mixture after dispersion is subjected to convention stir at normal temperature；The time of stirring is 45-55 minutes；The revolving speed of stirring
It is 50-100 revs/min；
Mixture after stirring is subjected to qualification detection, then tank out, obtains environmental protection type nano material multifunctional water.
Environmental protection type nano material multifunctional water provided by the invention and preparation method thereof is made combined with specific embodiments below
It further illustrates.
Embodiment 1
The present embodiment provides a kind of environmental protection type nano material multifunctional waters, and raw material components are by weight, comprising: nanometer is negative
White 1.4 parts by weight of bamboo charcoal powder of 1.9 parts by weight of ion powder, 0.9 parts by weight of nano-silver ionic, nanometer, 1.0 weight of nanometer titanium dioxide titanium valve
Measure part, 1.5 parts by weight of food-grade sodium dehydroacetate, 0.3 parts by weight of food-grade cellulose element sodium, 1.5 weight of cosmetics-stage dispersing agent
Part and 138 parts by weight of pure water.
Environmental protection type nano material multifunctional water is prepared using preparation method provided by the invention by above-mentioned raw material:
Water is put into agitator tank, then starts to stir；By other surplus stock components, according to metering, successively investment is stirred
In tank, high speed dispersion is carried out at normal temperature；The revolving speed of dispersion is greater than 1000 revs/min, and the time of dispersion is 20 minutes；
By the mixture after dispersion, convention stir stops after 50 minutes at normal temperature；The revolving speed of stirring is 60 revs/min；
Mixture after stirring is subjected to qualification detection, goes out tank after detection is qualified, obtains the more function of environmental protection type nano material
It can water.
Embodiment 2
The present embodiment provides a kind of environmental protection type nano material multifunctional waters, and raw material components are by weight, comprising: nanometer is negative
White 1.4 parts by weight of bamboo charcoal powder of 1.9 parts by weight of ion powder, 0.9 parts by weight of nano-silver ionic, nanometer, 1.0 weight of nanometer titanium dioxide titanium valve
Measure part, 1.2 parts by weight of nano medical stone powder, 0.75 parts by weight of nano-tourmaline powder, 1.5 parts by weight of food-grade sodium dehydroacetate,
0.3 parts by weight of food-grade cellulose element sodium, 138 parts by weight of 1.5 parts by weight of cosmetics-stage dispersing agent and pure water.
Environmental protection type nano material multifunctional water is prepared using preparation method provided by the invention by above-mentioned raw material:
Water is put into agitator tank, then starts to stir；By other surplus stock components, according to metering, successively investment is stirred
In tank, high speed dispersion is carried out at normal temperature；The revolving speed of dispersion is greater than 1000 revs/min, and the time of dispersion is 20 minutes；
By the mixture after dispersion, convention stir stops after 50 minutes at normal temperature；The revolving speed of stirring is 60 revs/min；
Mixture after stirring is subjected to qualification detection, goes out tank after detection is qualified, obtains the more function of environmental protection type nano material
It can water.
Embodiment 3
The present embodiment provides a kind of environmental protection type nano material multifunctional waters, and raw material components are by weight, comprising: nanometer is negative
White 0.9 parts by weight of bamboo charcoal powder of 1.3 parts by weight of ion powder, 1.2 parts by weight of nano-silver ionic, nanometer, 1.4 weight of nanometer titanium dioxide titanium valve
Measure part, 1.0 parts by weight of food-grade sodium dehydroacetate, 0.4 parts by weight of food-grade cellulose element sodium, 1.0 weight of cosmetics-stage dispersing agent
Part and 186 parts by weight of pure water.
Environmental protection type nano material multifunctional water is prepared using preparation method provided by the invention by above-mentioned raw material:
Water is put into agitator tank, then starts to stir；By other surplus stock components, according to metering, successively investment is stirred
In tank, high speed dispersion is carried out at normal temperature；The revolving speed of dispersion is greater than 1000 revs/min, and the time of dispersion is 15 minutes；
By the mixture after dispersion, convention stir stops after 45 minutes at normal temperature；The revolving speed of stirring is 50 revs/min；
Mixture after stirring is subjected to qualification detection, goes out tank after detection is qualified, obtains the more function of environmental protection type nano material
It can water.
Embodiment 4
The present embodiment provides a kind of environmental protection type nano material multifunctional waters, and raw material components are by weight, comprising: nanometer is negative
White 1.8 parts by weight of bamboo charcoal powder of 2.6 parts by weight of ion powder, 0.6 parts by weight of nano-silver ionic, nanometer, 0.7 weight of nanometer titanium dioxide titanium valve
Measure part, 2.0 parts by weight of food-grade sodium dehydroacetate, 0.2 parts by weight of food-grade cellulose element sodium, 2.0 weight of cosmetics-stage dispersing agent
Part and 93 parts by weight of pure water.
Environmental protection type nano material multifunctional water is prepared using preparation method provided by the invention by above-mentioned raw material:
Water is put into agitator tank, then starts to stir；By other surplus stock components, according to metering, successively investment is stirred
In tank, high speed dispersion is carried out at normal temperature；The revolving speed of dispersion is greater than 1000 revs/min, and the time of dispersion is 25 minutes；
By the mixture after dispersion, convention stir stops after 55 minutes at normal temperature；The revolving speed of stirring is 100 revs/min；
Mixture after stirring is subjected to qualification detection, goes out tank after detection is qualified, obtains the more function of environmental protection type nano material
It can water.
Comparative example 1
This comparative example provides a kind of environmental protection type nano material multifunctional water, and raw material components are by weight, comprising: nanometer is negative
White 1.4 parts by weight of bamboo charcoal powder of 1.9 parts by weight of ion powder, 0.9 parts by weight of nano-silver ionic, nanometer, 1.0 weight of nanometer titanium dioxide titanium valve
Measure part, 0.2 parts by weight of nano medical stone powder, 0.75 parts by weight of nano-tourmaline powder, 1.5 parts by weight of food-grade sodium dehydroacetate,
0.3 parts by weight of food-grade cellulose element sodium, 138 parts by weight of 1.5 parts by weight of cosmetics-stage dispersing agent and pure water.
By above-mentioned raw material, environmental protection type nano material multifunctional water is prepared:
Water is put into agitator tank, then starts to stir；By other surplus stock components, according to metering, successively investment is stirred
In tank, high speed dispersion is carried out at normal temperature；The revolving speed of dispersion is greater than 1000 revs/min, and the time of dispersion is 20 minutes；
By the mixture after dispersion, convention stir stops after 50 minutes at normal temperature；The revolving speed of stirring is 60 revs/min；
Mixture after stirring is subjected to qualification detection, goes out tank after detection is qualified, obtains the more function of environmental protection type nano material
It can water.
Comparative example 2
This comparative example provides a kind of environmental protection type nano material multifunctional water, and raw material components are by weight, comprising: nanometer is negative
White 1.4 parts by weight of bamboo charcoal powder of 1.9 parts by weight of ion powder, 0.9 parts by weight of nano-silver ionic, nanometer, 1.0 weight of nanometer titanium dioxide titanium valve
Measure part, 5.6 parts by weight of nano medical stone powder, 0.75 parts by weight of nano-tourmaline powder, 1.5 parts by weight of food-grade sodium dehydroacetate,
0.3 parts by weight of food-grade cellulose element sodium, 138 parts by weight of 1.5 parts by weight of cosmetics-stage dispersing agent and pure water.
By above-mentioned raw material, environmental protection type nano material multifunctional water is prepared:
Water is put into agitator tank, then starts to stir；By other surplus stock components, according to metering, successively investment is stirred
In tank, high speed dispersion is carried out at normal temperature；The revolving speed of dispersion is greater than 1000 revs/min, and the time of dispersion is 20 minutes；
By the mixture after dispersion, convention stir stops after 50 minutes at normal temperature；The revolving speed of stirring is 60 revs/min；
Mixture after stirring is subjected to qualification detection, goes out tank after detection is qualified, obtains the more function of environmental protection type nano material
It can water.
The environmental protection type nano material multifunctional water that the embodiment of the present invention 1 to embodiment 4 is prepared, is tried by function assessment
Test and carry out its effect of system evaluation, and using the environmental protection type nano material multifunctional water that comparative example 1 and comparative example 2 are prepared as pair
According to.
1, negative oxygen ion release performance is tested
1-4 of the embodiment of the present invention, comparative example 1-2 the environmental protection type nano material multifunctional water being prepared are respectively placed in bottom
Area is 1600cm2Square seal box bottom surface on, uniformly spread out, with a thickness of 0.3cm；Then closed, it is surveyed after 12 hours
Measure negative oxygen ion concentration (a/cm2, similarly hereinafter), be then emptied completely (the air in seal box is replaced completely, become with greatly
The identical atmosphere of gas), it is again sealed off other 30 hours and measures negative oxygen ion concentration again after (i.e. 42 hours in total), as a result (3 times
Measure average value) it is as shown in table 1 below.
1 negative oxygen ion release performance test result of table
| Group | Negative oxygen ion concentration after 12 hours | Negative oxygen ion concentration after 42 hours |
| Embodiment 1 | 12465 | 11982 |
| Embodiment 2 | 15624 | 15386 |
| Embodiment 3 | 15239 | 15031 |
| Embodiment 4 | 15340 | 15237 |
| Comparative example 1 | 9134 | 7308 |
| Comparative example 2 | 7592 | 6934 |
2, the effect detection of air is purified
Environmental protection type nano material multifunctional water that 1-4 of the embodiment of the present invention, comparative example 1-2 are prepared, water are routinely
Dosage dilution water emulsion paint, is then applied to metope according to a conventional method, turns off door and window, then monitors indoor environmental quality.Inspection
Surveying time point is 0 day, 10 days, 30 days, 100 days, 200 days and 300 days, and the result detected is as shown in table 2 below.
The content of formaldehyde of 2 different time points of table
Nano material multifunctional water provided by the invention can replace traditional water to dilute water-soluble finishing product, can
It is effective to inhibit fungus growth and prevent from going mouldy；The nano medical stone powder having in multifunctional water has extremely strong adsorption capacity,
In it and photocatalyst material most representative nano-titanium dioxide and under the action of other materials, can thoroughly root out by
The harmful substances such as remaining benzene, formaldehyde in cut-back product escort for environment in family；Also, the nanometer in the present invention bear from
The materials such as sub- powder can release the benefit materials such as negative oxygen ion and far infrared, can play and promote human metabolism and blood
The effect of liquid circulation, it is happy to make one body and mind, is beneficial to health.In addition, the present invention not only can solve above-mentioned problem,
Brilliant effect is played, also will not influence the service performance that water-soluble finishing product itself has.It can be said that provided by the invention
Nano material multifunctional water is the water-soluble finishing unique gold partner of product.
It should be noted that unless otherwise indicated, technical term or scientific term used in this application should be this hair
The ordinary meaning that bright one of ordinary skill in the art are understood.Unless specifically stated otherwise, it otherwise illustrates in these embodiments
Component and opposite step, numerical expression and the numerical value of step are not limit the scope of the invention.It is illustrated and described herein
In all examples, unless otherwise prescribed, any occurrence should be construed as merely illustratively, not as limitation, because
This, other examples of exemplary embodiment can have different values.
In the description of the present invention, it is to be understood that, term " first ", " second " are used for description purposes only, and cannot
It is interpreted as indication or suggestion relative importance or implicitly indicates the quantity of indicated technical characteristic.Define as a result, " the
One ", the feature of " second " can explicitly or implicitly include one or more of the features.In the description of the present invention,
The meaning of " plurality " is two or more, unless otherwise specifically defined.
Finally, it should be noted that the above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations；To the greatest extent
Pipe present invention has been described in detail with reference to the aforementioned embodiments, those skilled in the art should understand that: its according to
So be possible to modify the technical solutions described in the foregoing embodiments, or to some or all of the technical features into
Row equivalent replacement；And these are modified or replaceed, various embodiments of the present invention technology that it does not separate the essence of the corresponding technical solution
The range of scheme should all cover in protection scope of the present invention.
Claims (10)
1. a kind of environmental protection type nano material multifunctional water, which is characterized in that raw material components are by weight, comprising:
Nanometer anion powder 1.3-2.6 parts by weight, nano-silver ionic 0.6-1.2 parts by weight, the white bamboo charcoal powder 0.9-1.8 weight of nanometer
Part, nanometer titanium dioxide titanium valve 0.7-1.4 parts by weight, dehydroactic acid sodium 1.0-2.0 parts by weight, sodium cellulosate 0.2-0.4 parts by weight,
Dispersing agent 1.0-2.0 parts by weight and water 93-186 parts by weight.
2. environmental protection type nano material multifunctional water according to claim 1, which is characterized in that the raw material components also wrap
It includes:
Nano medical stone powder 0.8-1.6 parts by weight and nano-tourmaline powder 0.5-1.0 parts by weight.
3. environmental protection type nano material multifunctional water according to claim 2, which is characterized in that raw material components are by weight
Meter, comprising:
White 1.4 parts by weight of bamboo charcoal powder of 1.9 parts by weight of nanometer anion powder, 0.9 parts by weight of nano-silver ionic, nanometer, nano-silica
Change 1.0 parts by weight of titanium valve, 1.2 parts by weight of nano medical stone powder, 0.75 parts by weight of nano-tourmaline powder, 1.5 weight of dehydroactic acid sodium
Measure part, 138 parts by weight of 0.3 parts by weight of sodium cellulosate, 1.5 parts by weight of dispersing agent and water.
4. environmental protection type nano material multifunctional water according to claim 1-3, it is characterised in that:
The dehydroactic acid sodium is food-grade sodium dehydroacetate.
5. environmental protection type nano material multifunctional water according to claim 1-3, it is characterised in that:
The sodium cellulosate is food-grade cellulose element sodium.
6. environmental protection type nano material multifunctional water according to claim 1-3, it is characterised in that:
The dispersing agent is cosmetics-stage dispersing agent；
The water is pure water.
7. the preparation method of environmental protection type nano material multifunctional water described in any one of claims 1-6, which is characterized in that including
Step:
Water is put into agitator tank, then starts to stir；Other surplus stock components are successively put into agitator tank according to metering,
Dispersed at normal temperature；
Mixture after dispersion is stirred at normal temperature；
Mixture after stirring is subjected to qualification detection, then tank out, obtains the environmental protection type nano material multifunctional water.
8. the preparation method of environmental protection type nano material multifunctional water according to claim 7, it is characterised in that:
The revolving speed of the dispersion is greater than 1000 revs/min；The time of the dispersion is 15-25 minutes.
9. the preparation method of environmental protection type nano material multifunctional water according to claim 7, it is characterised in that:
The time of the stirring is 45-55 minutes；The revolving speed of the stirring is 50-100 revs/min.
10. environmental protection type nano material multifunctional water described in any one of claims 1-6 is in the water-soluble finishing product of dilution
Using.