CN105462391A - Interior wall latex paint having efficient sterilization and anion releasing functions - Google Patents
Interior wall latex paint having efficient sterilization and anion releasing functions Download PDFInfo
- Publication number
- CN105462391A CN105462391A CN201510937935.7A CN201510937935A CN105462391A CN 105462391 A CN105462391 A CN 105462391A CN 201510937935 A CN201510937935 A CN 201510937935A CN 105462391 A CN105462391 A CN 105462391A
- Authority
- CN
- China
- Prior art keywords
- latex paint
- wall latex
- parts
- negative ion
- interior wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses interior wall latex paint having efficient sterilization and anion releasing functions. The interior wall latex paint is prepared from, by weight parts, 10-20 parts of water, 0.6-1.2 parts of alkali swelling thickening agent, 0.1-0.2 part of pH modifier, 0.2-0.5 of antifoaming agent, 0.1-0.3 part of wetting agent, 0.3-0.6 part of dispersing agent, 1.0-1.5 parts of ethylene glycol, 1.0-1.5 parts of coalescing agent, 15.0-20.0 parts of titanium dioxide, 20.0-30.0 parts of calcium triple superphosphate, 1.0-1.5 parts of anion fission, 20.0-25.0 parts of polyacrylic emulsion, 0.01-0.03 part of nanometer silver oxide, 0.5-1.0 part of metal ion bactericide and 0.3-0.5 part of polyurethane thickening agent. The interior wall latex paint prepared from the materials is suitable for decoration of the interior wall surface of a building, meets the the standard which regular interior wall latex paint can reach, has the efficient long sterilization function, can release anion for a long time to purify air and can be widely utilized in the indoor air purification of the building and effectively protect the health and safety of indoor people.
Description
Technical field
The present invention relates to emulsion paint field, specifically a kind of interiro wall latex paint with efficient sterilizing, negative ion-releasing function.
Background technology
Interiro wall latex paint popular in the market, major part adopts Mierocrystalline cellulose to make thickening material, and bacterium easily grows in a large number as nutriment, produces many problems: one is occur after causing coating system to lose thickening power that a point depositing in water falls, and affects quality product; Two is cause sending nauseating stink in tank, and impact construction, pollutes IAQ (indoor air quality); Three is be coated with to install to after on indoor wall, causes metope being introduced a large amount of bacterium and mould, the indoor population health of serious harm; Meanwhile, such emulsion paint only possesses the effect of protection body of wall, there is no the specific function effectively improved IAQ (indoor air quality) and improve HUMAN HEALTH; At present, a lot of document and patent reports common interiro wall latex paint, also has the interiro wall latex paint of anion releasing, but the interiro wall latex paint patent with long-acting bactericidal and anion releasing have not been reported, the interiro wall latex paint that R and D have long-acting bactericidal and anion releasing will meet environmental protection, safe finishing requirement greatly, has great market outlook.
Summary of the invention
The object of the present invention is to provide a kind of safety, environmental protection, there is the interiro wall latex paint of efficient sterilizing, negative ion-releasing function, to solve the problem proposed in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme:
There is an interiro wall latex paint for efficient sterilizing, negative ion-releasing function, be prepared from by the raw material of following weight part:
As the further scheme of the present invention: described in there is the interiro wall latex paint of efficient sterilizing, negative ion-releasing function, be prepared from by the raw material of following weight part:
As the present invention's further scheme: described in there is the interiro wall latex paint of efficient sterilizing, negative ion-releasing function, be prepared from by the raw material of following weight part:
As the present invention's further scheme: described ACRYLIC EMULSION is filmogen, and ACRYLIC EMULSION comprises benzene emulsion, one or more in pure-acrylic emulsion and acetate emulsion, VOC content≤30 grams per liter in ACRYLIC EMULSION and not containing formaldehyde in ACRYLIC EMULSION.
As the present invention's further scheme: described in there is the preparation method of interiro wall latex paint of efficient sterilizing, negative ion-releasing function, comprise the following steps:
1) pull an oar the stage: in stirring tank, add tap water by formula ratio, under the speed conditions of 600r/min, add defoamer, alkali swollen thickener and pH adjusting agent successively, wetting agent, dispersion agent, ethylene glycol, film coalescence aid, titanium dioxide, coarse whiting, anion powder and nano phase ag_2 o is added successively after system thickening evenly, promote rotating speed and disperse 28-32min to 1200-1500r/min, system fineness is down to below 50um;
2) letdown phase: after the slurry system fineness of step 1 is down to below 50um, adds ACRYLIC EMULSION, defoamer and metal ion sterilant by formula ratio and is uniformly dispersed, then add polyurethane thickener, by demand regulation system viscosity.
As the present invention's further scheme: also add in the slurry of step 2 and drive fly plum extraction juice and peppermint extraction juice, obtain finished product interiro wall latex paint.
Compared with prior art, the invention has the beneficial effects as follows: the present invention is water emulsion paint for internal wall, has efficient sterilizing, the function of anion releasing, the indoor population health of favourable protection; Anion powder prodigiosin sustained release negative ion, eliminates foreign flavor indoors and toxic and harmful, improves indoor crowd's mental status; Nano phase ag_2 o, inertia is very high, can and bacterial body protein denaturation poisoning and dead, reach the object of long-acting bactericidal; Metal ion sterilant mainly kills bacterium in paint can and algae, in order to avoid bring the bacterium in tank into indoor, in tank, thickening germicidal action is long; Adopt alkali swollen thickener to replace Mierocrystalline cellulose, cancel the nutriment source of bacterium, make bacterium be difficult to growth and breeding, thus eliminate room atmosphere and metope fouled by microzyme from source; The negative ion increase dissolved oxygen content soluble in water of anion powder release, can kill the bacterium under the wet environments such as towel; Thickening material in the present invention uses alkali swollen thickener early stage, and the later stage uses polyurethane thickener, and both have more anti-microbial property than Mierocrystalline cellulose than cellulose thickener; The present invention has efficient permanent sterilizing function, and energy long-term negative ion release, purifies air, can be widely used in the purifying air of Indoor environment, and the indoor crowd's of available protecting is healthy and safe.
Accompanying drawing explanation
Fig. 1 is process flow sheet of the present invention.
Embodiment
Be described in more detail below in conjunction with the technical scheme of embodiment to this patent.
Embodiment 1
There is an interiro wall latex paint for efficient sterilizing, negative ion-releasing function, be prepared from by the raw material of following weight part:
Embodiment 2
There is an interiro wall latex paint for efficient sterilizing, negative ion-releasing function, be prepared from by the raw material of following weight part:
Embodiment 3
There is an interiro wall latex paint for efficient sterilizing, negative ion-releasing function, be prepared from by the raw material of following weight part:
Embodiment 4
There is an interiro wall latex paint for efficient sterilizing, negative ion-releasing function, be prepared from by the raw material of following weight part:
Embodiment 5
There is an interiro wall latex paint for efficient sterilizing, negative ion-releasing function, be prepared from by the raw material of following weight part:
ACRYLIC EMULSION described in embodiment 1-5 is filmogen, and ACRYLIC EMULSION comprises benzene emulsion, one or more in pure-acrylic emulsion and acetate emulsion, VOC content≤30 grams per liter in ACRYLIC EMULSION and not containing formaldehyde in ACRYLIC EMULSION.
Refer to Fig. 1, Fig. 1 is process flow sheet of the present invention, and the preparation method of interiro wall latex paint with efficient sterilizing, negative ion-releasing function described in embodiment 1-5, comprises the following steps:
1) pull an oar the stage: in stirring tank, add tap water by formula ratio, under the speed conditions of 600r/min, add defoamer, alkali swollen thickener and pH adjusting agent successively, wetting agent, dispersion agent, ethylene glycol, film coalescence aid, titanium dioxide, coarse whiting, anion powder and nano phase ag_2 o is added successively after system thickening evenly, promote rotating speed and disperse 28-32min to 1200-1500r/min, system fineness is down to below 50um;
2) letdown phase: after the slurry system fineness of step 1 is down to below 50um, adds ACRYLIC EMULSION, defoamer and metal ion sterilant by formula ratio and is uniformly dispersed, then add polyurethane thickener, by demand regulation system viscosity;
3) also add in the slurry of step 2 and drive fly plum and extract juice and peppermint extracts juice, obtain finished product interiro wall latex paint.
Construction application of the present invention:
Described in embodiment 1-5 there is efficient sterilizing, the construction application of interiro wall latex paint of negative ion-releasing function comprises base treatment, batch Puttying, be coated with seal coat and construction emulsion paint of the present invention, concrete steps are as follows:
1) base treatment: need the basal plane of construction necessary smooth, solid, dry, clean;
2) criticize Puttying: Pi Gua 2-3 road putty, a smooth solid basal plane is provided;
3) seal coat is coated with: on the putty of drying, be coated with one deck close alkali-resistant primer;
4) construction emulsion paint: roller coat or spraying have the interiro wall latex paint 1-2 road of efficient sterilizing, negative ion-releasing function on dry priming paint.
Concrete technology requires to be shown in Table 1.
The construction technology process of table 1 interiro wall latex paint of the present invention and requirement
Performance study of the present invention:
Disclosed by the inventionly have efficient sterilizing, the interiro wall latex paint of negative ion-releasing function has long-acting bactericidal, the function of anion releasing, other performance meets GB GB/T9756-2009 requirement.
Compared with prior art, the present invention has following excellent function:
1) long-acting bactericidal
Long-acting performance of killing of the present invention is realized by following four aspects:
A. nano phase ag_2 o, adopt heavy metal silver and bacterial body protein bound bacterium can be made poisoning and dead, and silver-colored inertia is very high, not perishable, thus has the effect of long-acting kill bacteria;
B. metal ion sterilant, adopt complexing of metal ion form as sterilant, the similar bacterium of packaging more can be killed effectively for a long time than common Kathon CG and imidazoles phosphorus ketone sterilant, thus effectively avoid bacterium in bucket, the growing and breeding of mould and algae, avoid again bringing bacterium and atmospheric pollution into indoor and metope;
C. alkali swollen thickener, adopts alkali swollen thickener to substitute conventional fibre element class thickening material, cancels the bacterium nutriment in pail pack, allow bacterium lose the material conditions of Growth and reproduction;
D. anion powder, the ability of the negative ion increase dissolved oxygen soluble in water of indoor release, can kill the bacterium under the wet environments such as towel.
2) anion releasing
The present invention, by adopting titanium dioxide, utilizes nano-TiO
2under illumination condition, produce strong degradation function, thus the toxic and harmful such as benzene, toluene, formaldehyde produced in effectively degrade indoor furniture or floor, make it resolve into CO
2and H
2o, protection population health; Can also effectively kill indoor various bacteria, harmful poison gas indoor bacteria cell or bacterium sent resolves into CO
2and H
2o, protection population health;
3) GB interiro wall latex paint GB/T9756-2009 requirement is reached
By adding the ACRYLIC EMULSION of q.s, color filters etc., reach the requirements such as the scrubbing resistance of Standard, contrast ratio.
Above the better embodiment of this patent is explained in detail, but this patent is not limited to above-mentioned embodiment, in the ken that one skilled in the relevant art possesses, can also makes a variety of changes under the prerequisite not departing from this patent aim.
Claims (6)
1. there is an interiro wall latex paint for efficient sterilizing, negative ion-releasing function, it is characterized in that, be prepared from by the raw material of following weight part:
2. the interiro wall latex paint with efficient sterilizing, negative ion-releasing function according to claim 1, is characterized in that, is prepared from by the raw material of following weight part:
3. the interiro wall latex paint with efficient sterilizing, negative ion-releasing function according to claim 1, is characterized in that, is prepared from by the raw material of following weight part:
4. according to the arbitrary described interiro wall latex paint with efficient sterilizing, negative ion-releasing function of claim 1-3, it is characterized in that, described ACRYLIC EMULSION is filmogen, ACRYLIC EMULSION comprises benzene emulsion, one or more in pure-acrylic emulsion and acetate emulsion, VOC content≤30 grams per liter in ACRYLIC EMULSION and not containing formaldehyde in ACRYLIC EMULSION.
5., according to the arbitrary described preparation method of interiro wall latex paint with efficient sterilizing, negative ion-releasing function of claim 1-4, it is characterized in that, comprise the following steps:
1) pull an oar the stage: in stirring tank, add tap water by formula ratio, under the speed conditions of 600r/min, add defoamer, alkali swollen thickener and pH adjusting agent successively, wetting agent, dispersion agent, ethylene glycol, film coalescence aid, titanium dioxide, coarse whiting, anion powder and nano phase ag_2 o is added successively after system thickening evenly, promote rotating speed and disperse 28-32min to 1200-1500r/min, system fineness is down to below 50um;
2) letdown phase: after the slurry system fineness of step 1 is down to below 50um, adds ACRYLIC EMULSION, defoamer and metal ion sterilant by formula ratio and is uniformly dispersed, then add polyurethane thickener, by demand regulation system viscosity.
6. the preparation method of interiro wall latex paint with efficient sterilizing, negative ion-releasing function according to claim 5, is characterized in that, also adds to drive fly plum and extract juice and peppermint extracts juice in the slurry of step 2, obtains finished product interiro wall latex paint.