CN102060557B - Nanocomposite diatom ooze material and construction method thereof - Google Patents
Nanocomposite diatom ooze material and construction method thereof Download PDFInfo
- Publication number
- CN102060557B CN102060557B CN2010105270988A CN201010527098A CN102060557B CN 102060557 B CN102060557 B CN 102060557B CN 2010105270988 A CN2010105270988 A CN 2010105270988A CN 201010527098 A CN201010527098 A CN 201010527098A CN 102060557 B CN102060557 B CN 102060557B
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- powder
- nano
- powder material
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a nanocomposite diatom ooze material and a construction method thereof. The material consists of a diatom ooze powder material and nano-titanium dioxide dispersion liquid, wherein the diatom ooze powder material consists of calcined diatomite, quartz sand, gray calcium powder, bentonite, wollastonite, seaweed gel, cellulose ether and negative ion powder. The construction method comprises the following steps of: mixing the diatom ooze powder material and water according to the weight ratio of 1:0.9 in the field; after stirring for 15 minutes by using an electric stirrer, performing batch-scraping coating texture modeling construction; uniformly spraying the nano-titanium dioxide dispersion liquid, namely photocatalyst solution to a construction surface by using a spraying gun after the surface is dried; and drying for 48 hours. By using the construction method, the problems that nano-titanium dioxide powder is difficult to disperse and easy to agglomerate, and has large additive amount, the production cost is high, and a nano-titanium dioxide material is wasted in the preparation process of the diatom ooze are solved, the functionality of the diatom ooze for purifying and decomposing harmful gases is improved, and the overall cost of the product is reduced.
Description
Technical field
The present invention relates to a kind of interior wall material, particularly a kind of nano combined diatom mud material and constructional method thereof.
Technical background
Directly add the powder nano titanium oxide in existing a kind of diatom ooze interior wall material prescription; Wherein nano titanium oxide is a photocatalyst, because nano-titanium dioxide powder prepares difficulties in dispersion in the process at diatom ooze, gathers group easily; Addition is big; Production cost is high, has reduced the functional of diatom ooze purification, resolving harmful gas, has improved the whole cost of product.
Summary of the invention
The purpose of this invention is to provide a kind of nano combined diatom mud material and constructional method thereof; The present invention has improved the carrying method of existing nano titanium oxide; With the technology of directly adding the powder nano titanium oxide in the original diatom ooze prescription, changing on diatom ooze construction surface is that the nanometer titanium dioxide titanium solution loads in the micropore on diatom ooze top layer with photocatalyst through the spraying mode of loading, has solved because nano-titanium dioxide powder prepares difficulties in dispersion in the process at diatom ooze; Gather group easily; Addition is big, the problem that production cost is high and nanometer titanic oxide material is wasted; Improve the functional of diatom ooze purification, resolving harmful gas, reduced the whole cost of product.
The present invention utilizes the adsorption of the diatomaceous porousness of natural mineral to obnoxious flavour; Utilize biological seaweed gel to make organic adhesive; Silica sand or white sand as aggregate, negative ion powder and nano titanium oxide etc. can decomposing harmful substances functional additive, the novel wall surface finishing material that is prepared from.
The present invention's material is to be made up of diatom ooze powder material and nano titanium oxide dispersion;
Diatom ooze powder material wherein is made up of the component of following weight per-cent:
200～400 purpose calcined diatomite 20%-50%
20～80 purpose silica sand 20%-35%
400～800 purposes ash calcium powder 10%-40%
800～1000 purpose wilkinite 5%-10%
800～1000 purpose wollastonite 2%-10%
Seaweed gel 0.6%-3%
Ether of cellulose 0.5%-1%
Negative ion powder 1%-3%
Said components adds an amount of pigment and forms diatom ooze powder material through evenly stirring.
Nano titanium oxide dispersion is a currently available products.
The model of said negative ion powder is: 20000 types, manufacturer is: the source nanosecond science and technology ltd of Hebei rock.
The present invention's constructional method: on-the-spot with diatom ooze powder material and water according to 1: 0.9 mixed of weight ratio; Stir criticize after 15 minutes to scrape with electric mixer and smear the skin texture moulding and construct; After surface drying, be that photocatalyst liquid evenly sprays to construction surface with nano titanium oxide dispersion with spray gun; Make photocatalyst liquid uniformly penetrating in the zeyssatite micropore on diatom ooze surface, get final product after dry 48 hours.
Beneficial effect of the present invention:
1, do not add any objectionable impurities in the material of the present invention, not only can not distribute obnoxious flavoures such as formaldehyde, benzene, ammonia, TVOC, but also have the function of absorption, resolving harmful gas, and have certain breathing humidity conditioning function.Possess transportation, construction characteristic of simple simultaneously.
2, the present invention has mainly improved the carrying method of nano titanium oxide; With the technology that original diatom ooze prescription adds the powder nano titanium oxide, change on diatom ooze construction surface and photo-catalytic nano titania solution (photocatalyst) is loaded in the micropore on diatom ooze top layer through the spraying mode of loading, solved owing to nano-titanium dioxide powder prepares difficulties in dispersion in the process at diatom ooze; Gather group easily; Addition is big, the problems such as waste of production cost height and nano material; Improve the functional of diatom ooze purification, resolving harmful gas, reduced the whole cost of product.
3, zeyssatite main effect in the present invention is: play the absorption obnoxious flavour and regulate humidity; And as the carrier of nano titanium oxide and negative ion powder; Porousness through diatom ooze is adsorbed onto the free formaldehyde that exists in the room air and other obnoxious flavour in the diatom ooze coating; Decomposition through photocatalyst (nano titanium oxide) and negative ion powder is decomposed into harmless carbonic acid gas and water with it, thereby reaches the purpose that purifies air.
Embodiment
The present invention's material is to be made up of diatom ooze powder material and nano titanium oxide dispersion;
The product that nano titanium oxide dispersion selects for use Guangzhou Ao Yin Environmental Protection Technology Co., Ltd to produce.
The embodiment 1 of diatom ooze powder material:
200～400 purpose calcined diatomite 50kg
20～80 purpose silica sand 20kg
400～800 purposes ash calcium powder 10kg
800～1000 purpose wilkinite 5kg
800～1000 purpose wollastonite 10kg
Seaweed gel 3kg
Ether of cellulose 1kg
Negative ion powder 2kg.
The embodiment 2 of diatom ooze powder material:
200～400 purpose calcined diatomite 20kg
20～80 purpose silica sand 35kg
400～800 purposes ash calcium powder 30.9kg
800～1000 purpose wilkinite 10kg
800～1000 purpose wollastonite 2kg
Seaweed gel 0.6kg
Ether of cellulose 0.5kg
Negative ion powder 1kg.
The embodiment 3 of diatom ooze powder material:
200～400 purpose calcined diatomite 21.3kg
20～80 purpose silica sand 25kg
400～800 purposes ash calcium powder 40kg
800～1000 purpose wilkinite 6kg
800～1000 purpose wollastonite 3kg
Seaweed gel 1kg
Ether of cellulose 0.7kg
Negative ion powder 3kg.
The embodiment 4 of diatom ooze powder material:
200～400 purpose calcined diatomite 30kg
20～80 purpose silica sand 20kg
400～800 purposes ash calcium powder 30kg
800～1000 purpose wilkinite 5kg
800～1000 purpose wollastonite 9kg
Seaweed gel 3kg
Ether of cellulose 1kg
Negative ion powder 2kg.
Constituent materials among above-mentioned four embodiment is dried to water cut less than after 5%, adds an amount of pigment and put into powder stirrer, fully stirred 30 minutes, make the material thorough mixing, after the assay was approved, adopt weather-proof dressing, pack can be dispatched from the factory.
The present invention's constructional method: on-the-spot with diatom ooze powder body material and water according to 1: 0.9 mixed of weight ratio; Stir criticize after 15 minutes to scrape with electric mixer and smear the skin texture moulding and construct; After surface drying, be that photocatalyst liquid evenly sprays to construction surface with nano titanium oxide dispersion with spray gun; Make photocatalyst liquid uniformly penetrating in the zeyssatite micropore on diatom ooze surface, get final product after dry 48 hours.
Claims (1)
1. a nano combined diatom mud material is characterized in that: be to be made up of diatom ooze powder material and nano titanium oxide dispersion;
Diatom ooze powder material wherein is made up of the component of following weight per-cent:
Said components adds an amount of pigment and forms diatom ooze powder material through evenly stirring; During construction; On-the-spot with diatom ooze powder material and water according to 1: 0.9 mixed of weight ratio; Stir criticize after 15 minutes to scrape with electric mixer and smear the skin texture moulding and construct; After surface drying, be that photocatalyst liquid evenly sprays to construction surface with nano titanium oxide dispersion, make photocatalyst liquid uniformly penetrating in the zeyssatite micropore on diatom ooze surface, get final product after dry 48 hours with spray gun.