CN104478338A - Diatom ooze spray coating - Google Patents
Diatom ooze spray coating Download PDFInfo
- Publication number
- CN104478338A CN104478338A CN201410779876.0A CN201410779876A CN104478338A CN 104478338 A CN104478338 A CN 104478338A CN 201410779876 A CN201410779876 A CN 201410779876A CN 104478338 A CN104478338 A CN 104478338A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- weight ratio
- nano titanium
- water
- spray coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a diatom ooze spray coating which consists of the following components: 18-22kg of kieselguhr, 80-90kg of water, 23-27kg of heavy calcium carbonate, 0.8-1.2kg of negative oxygen ions and 0.8-1.2kg of nano titanium dioxide. A construction method of diatom ooze comprises the following steps: at the construction site, stirring the raw materials in a water mixer for 10 minutes according to a weight ratio; constructing the mixture; after the mixed diatom ooze is dried on the surface of a wall, spraying the nano titanium dioxide onto the constructed wall according to a weight ratio; and drying for 40-45 hours to obtain a product. The diatom ooze spray coating provided by the invention can purify indoor air, does not generate poisonous gas and is easily sprayed to form various patterns.
Description
Technical field
The invention belongs to a kind of wallcovering, particularly a kind of diatom ooze spray material.
Background technology
Diatom ooze, as indoor paint, due to its construction, is smeared and is all better than existing decorative paint with pattern-making, due to the adsorptive power that it is superpower, can also absorb the obnoxious flavour in air, therefore be subject to the favor of people, apply more and more wider.
Summary of the invention
The object of the invention is to: a kind of diatom ooze spray material is provided, facilitates household to decorate, without any toxic ingredient, high adsorption capacity, the toxic substances such as energy formaldehyde adsorption.
To achieve these goals, inventive solution is as follows:
A kind of diatom ooze spray material, is characterized in that, be made up of by weight following compositions: diatomite 18-22KG, water 80-90KG, water-ground limestone 23-27KG, negative oxygen ion 0.8-1.2KG, nano titanium oxide 0.8-1.2KG.
Preferably, described diatomite is secondary diatomite.
Constructional method of the present invention is made up of the following step: at the construction field (site), raw material according to weight ratio is stirred 10 minutes in aqua mixing machine, then mixture is constructed, diatom ooze after to be mixed is after the surface drying of metope, again the nano titanium oxide according to weight ratio is sprayed on the metope of construction, after dry 40-45 hour.
Beneficial effect of the present invention is: the present invention compares and common building finishing material, and not containing any toxic substance, diatom ooze has adsorption, and relative to gac, the strong hundreds of times of adsorption, therefore, also possess the effect of absorption degradation obnoxious flavour.
Embodiment
In order to more clearly understand technology contents of the present invention, describe in detail especially exemplified by following examples.
Embodiment one:
A kind of diatom ooze spray material, is made up of following compositions: diatomite 18KG, water 80KG, water-ground limestone 23KG, negative oxygen ion 0.8KG, nano titanium oxide 0.8KG by weight.
The constructional method of the present embodiment is made up of the following step: at the construction field (site), raw material according to weight ratio is stirred 10 minutes in aqua mixing machine, then mixture is constructed, diatom ooze after to be mixed is after the surface drying of metope, again the nano titanium oxide according to weight ratio is sprayed on the metope of construction, after dry 40-45 hour.
Embodiment two:
A kind of diatom ooze spray material, is made up of following compositions: diatomite 20KG, water 85KG, water-ground limestone 25KG, negative oxygen ion 1KG, nano titanium oxide 1KG by weight.
The constructional method of the present embodiment is made up of the following step: at the construction field (site), raw material according to weight ratio is stirred 10 minutes in aqua mixing machine, then mixture is constructed, diatom ooze after to be mixed is after the surface drying of metope, again the nano titanium oxide according to weight ratio is sprayed on the metope of construction, after dry 40-45 hour.
Embodiment three:
A kind of diatom ooze spray material, is made up of following compositions: diatomite 22KG, water 90KG, water-ground limestone 27KG, negative oxygen ion 1.2KG, nano titanium oxide 1.2KG by weight.
The constructional method of the present embodiment is made up of the following step: at the construction field (site), raw material according to weight ratio is stirred 10 minutes in aqua mixing machine, then mixture is constructed, diatom ooze after to be mixed is after the surface drying of metope, again the nano titanium oxide according to weight ratio is sprayed on the metope of construction, after dry 40-45 hour.
Claims (3)
1. a diatom ooze spray material, is characterized in that, is made up of by weight following compositions: diatomite 18-22KG, water 80-90KG, water-ground limestone 23-27KG, negative oxygen ion 0.8-1.2KG, nano titanium oxide 0.8-1.2KG.
2. a kind of diatom ooze spray material according to claim 1, it is characterized in that, described diatomite is secondary diatomite.
3. diatom ooze constructional method as claimed in claim 1, it is characterized in that, be made up of the following step: at the construction field (site), raw material according to weight ratio is stirred 10 minutes in aqua mixing machine, then mixture is constructed, nano titanium oxide according to weight ratio after the surface drying of metope, then sprays on the metope of construction by the diatom ooze after to be mixed, after dry 40-45 hour.