CN106121150B - A kind of moisture resistance high-air-permeability wallpaper and preparation method thereof - Google Patents
A kind of moisture resistance high-air-permeability wallpaper and preparation method thereof Download PDFInfo
- Publication number
- CN106121150B CN106121150B CN201610500918.1A CN201610500918A CN106121150B CN 106121150 B CN106121150 B CN 106121150B CN 201610500918 A CN201610500918 A CN 201610500918A CN 106121150 B CN106121150 B CN 106121150B
- Authority
- CN
- China
- Prior art keywords
- powder
- bamboo
- adhesive
- bamboo carbon
- carbon powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of preparation methods of moisture resistance high-air-permeability wallpaper, which comprises the following steps: the first step takes base to adhere to bamboo on it；Second step; take the 1/3 of spare adhesive, it be uniformly sprayed in bamboo in the way of spraying, then by titanium dioxide, with 1/2 bamboo carbon powder after mixing; even spread is on the adhesive; then spraying on the surface thereof, for water fog particle partial size less than 5 μm, spray amount is 1~2L/min* ㎡; then stands 10~20 minutes; is then dried, drying temperature is 70~100 DEG C, and drying time is 10~15 minutes；Third step is mixed with the bamboo carbon powder of fluorescent powder, tourmaline powder, residue 1/2 by the 2/3 of spare adhesive, is then uniformly coated on the coating of titanium dioxide and bamboo carbon powder；4th step, then fluorescent powder, tourmaline powder coating on cover nonwoven layer；5th step, covers polytetrafluoroethylene ethylene layer in nonwoven layer.
Description
Technical field
The present invention relates to a kind of moisture resistance high-air-permeability wallpapers and preparation method thereof.
Background technique
Currently, wallpaper has, rich in color, change in pattern is various, texture is different, environmentally protective, decorative effect noble quality allusion quotation
Refined, the features such as construction efficiency is high, it is widely used in family and finishing work.And the wallpaper of the prior art is usually passed through by body paper
The techniques such as embossing, printing are process, and are only used as decorative use without moisture-proof moisture absorbing, therefore such wallpaper is in tide
It is easy to occur to go mouldy when using under wet environment and breeds bacterium.In order to solve the above technical problems, it is necessory to provide one kind
With structure improved moisture-proof moisture absorption wallpaper, to overcome the defect in the prior art, and people also prefer to wallpaper energy
It is enough that there are more functionality.
Summary of the invention
Therefore, for above-mentioned problem, the present invention proposes that a kind of structure is simple, can effectively prevent mildew, can make sky
Gas forms anion, the moisture resistance high-air-permeability wallpaper that can effectively sterilize and its preparation process.
To achieve the above object, the invention adopts the following technical scheme: a kind of moisture resistance high-air-permeability wallpaper, including by
Under the supreme waterproof coating layer stacked gradually, base, bamboo, composite layer, polytetrafluoroethylene ethylene layer, the composite layer is by 20
The titanium dioxide of~25 parts by weight, the fluorescent powder of 5~10 parts by weight, the tourmaline powder of 10~15 parts by weight, 10~15 parts by weight
Bamboo carbon powder, 20-35 parts by weight adhesive composition.
Further, the composite layer is spliced by a plurality of bulks.
Further, nonwoven layer is additionally provided between the composite layer and polytetrafluoroethylene ethylene layer.
A kind of preparation method of moisture resistance high-air-permeability wallpaper, comprising the following steps:
The first step takes base to adhere to bamboo on it；
Second step takes the 1/3 of spare adhesive, it is uniformly sprayed in bamboo in the way of spraying, and
Afterwards by titanium dioxide, with 1/2 bamboo carbon powder after mixing, even spread is on the adhesive, then spraying on the surface thereof,
For water fog particle partial size less than 5 μm, spray amount is 1~2L/min* ㎡, then stands 10~20 minutes, is then dried, and is dried
Temperature asks 70~100 DEG C, and drying time is 10~15 minutes；
Third step is mixed the 2/3 of spare adhesive with the bamboo carbon powder of fluorescent powder, tourmaline powder, residue 1/2,
Then it is uniformly coated on the coating of titanium dioxide and bamboo carbon powder；
4th step, then fluorescent powder, tourmaline powder coating on cover nonwoven layer；
5th step, covers polytetrafluoroethylene ethylene layer in nonwoven layer.
By using preceding solution, the beneficial effects of the present invention are: this moisture resistance high-air-permeability wallpaper passes through waterproof
The setting of dope layer, base, bamboo, composite layer, polytetrafluoroethylene ethylene layer, and composite layer is by titanium dioxide, fluorescent powder, electricity
Gas mountain flour, bamboo carbon powder, adhesive composition can effectively realize moisture-proof, the advantages that sterilizing, preventing mildew, is high ventilative, additionally it is possible to
So that wallpaper realizes fluorescent effect.And the preparation method of moisture resistance high-air-permeability wallpaper its first take the 1/3 of spare adhesive, first apply
The bamboo carbon powder of titanium dioxide, 1/2 is then uniformly mixed and is coated thereon by cloth, realize it is viscous glutinous for the first time, and pass through it is spraying,
It stands, drying, so that the stability on the surface of titanium dioxide and bamboo carbon powder increases, and the presence of bamboo carbon powder can be with
Increase permeability, then by the 2/3 of spare adhesive with fluorescent powder, tourmaline powder, remaining 1/2 bamboo carbon powder mix
It closes, is coated thereon, such that the stability of entire composite layer is more preferably, and each substance can play its optimum performance.
Specific embodiment
Now in conjunction with the present invention is further described with specific embodiment.
The present embodiment one provides a kind of moisture resistance high-air-permeability wallpaper, including the water-repellent paint stacked gradually from the bottom to top
Layer, base, bamboo, composite layer, nonwoven layer, polytetrafluoroethylene ethylene layer, the composite layer by 20 parts by weight titanium dioxide
Titanium, the fluorescent powder of 5 parts by weight, the tourmaline powder of 10 parts by weight, the bamboo carbon powder of 10 parts by weight, 20 parts by weight adhesive group
At.
Preparation method, comprising the following steps:
The first step takes base to adhere to bamboo on it；
Second step takes the 1/3 of spare adhesive, it is uniformly sprayed in bamboo in the way of spraying, and
Afterwards by titanium dioxide, with 1/2 bamboo carbon powder after mixing, even spread is on the adhesive, then spraying on the surface thereof,
For water fog particle partial size less than 5 μm, spray amount is 1L/min* ㎡, then stands 10 minutes, is then dried, drying temperature is asked
70 DEG C, drying time is 10 minutes；
Third step is mixed the 2/3 of spare adhesive with the bamboo carbon powder of fluorescent powder, tourmaline powder, residue 1/2,
Then it is uniformly coated on the coating of titanium dioxide and bamboo carbon powder；
4th step, then fluorescent powder, tourmaline powder coating on cover nonwoven layer；
5th step, covers polytetrafluoroethylene ethylene layer in nonwoven layer.
The present embodiment two provides a kind of moisture resistance high-air-permeability wallpaper based on the same inventive concept, with embodiment one
Difference is: the composite layer by the titanium dioxide of 25 parts by weight, the fluorescent powder of 10 parts by weight, 15 parts by weight tourmaline powder,
The adhesive composition of the bamboo carbon powder of 15 parts by weight, 35 parts by weight.And preparation method second step are as follows: the 1/3 of spare adhesive is taken,
It is uniformly sprayed in bamboo in the way of spraying, is then mixed by titanium dioxide, with 1/2 bamboo carbon powder
After even, on the adhesive, then spraying on the surface thereof, water fog particle partial size is less than 5 μm, spray amount 2L/ for even spread
Min* ㎡ then stands 20 minutes, is then dried, and drying temperature asks 100 DEG C, and drying time is 15 minutes.
The present embodiment three provides a kind of moisture resistance high-air-permeability wallpaper based on the same inventive concept, with embodiment one
Difference is: the composite layer is by the titanium dioxide of 22 parts by weight, the fluorescent powder of 7 parts by weight, the tourmaline powder of 12 parts by weight, 12
The adhesive composition of the bamboo carbon powder of parts by weight, 28 parts by weight.And preparation method second step are as follows: the 1/3 of spare adhesive is taken, it will
It is uniformly sprayed in bamboo in the way of spraying, is then uniformly mixed by titanium dioxide, with 1/2 bamboo carbon powder
Afterwards, on the adhesive, then spraying on the surface thereof, water fog particle partial size is less than 5 μm, spray amount 1.5L/ for even spread
Min* ㎡ then stands 15 minutes, is then dried, and drying temperature asks 85 DEG C, and drying time is 12 minutes.
This moisture resistance high-air-permeability wallpaper passes through waterproof coating layer, base, bamboo, composite layer, polytetrafluoroethylene (PTFE)
The setting of layer, and composite layer is made of titanium dioxide, fluorescent powder, tourmaline powder, bamboo carbon powder, adhesive, can effectively be realized
Moisture-proof, the advantages that sterilizing, preventing mildew, is high ventilative, additionally it is possible to so that wallpaper realizes fluorescent effect.And moisture resistance high-air-permeability wall
It first takes the 1/3 of spare adhesive to the preparation method of paper, is first coated with, and is then uniformly mixed the bamboo carbon powder of titanium dioxide, 1/2
It is coated thereon, it is viscous glutinous to realize first time, and pass through spraying, standing, drying, so that the table of titanium dioxide and bamboo carbon powder
The stability in face increases, and the presence of bamboo carbon powder can increase permeability, then by the 2/3 of spare adhesive and fluorescence
The bamboo carbon powder mixing of powder, tourmaline powder, residue 1/2, is coated thereon, such that the stability of entire composite layer
More preferably, and each substance can play its optimum performance.
Although specifically showing and describing the present invention in conjunction with preferred embodiment, those skilled in the art should be bright
It is white, it is not departing from the spirit and scope of the present invention defined by the appended claims, it in the form and details can be right
The present invention makes a variety of changes, and is protection scope of the present invention.
Claims (2)
1. a kind of preparation method of moisture resistance high-air-permeability wallpaper, which comprises the following steps:
The first step takes base to adhere to bamboo on it；
Second step takes the 1/3 of spare adhesive, it is uniformly sprayed in bamboo in the way of spraying, then will
Titanium dioxide, with 1/2 bamboo carbon powder after mixing, even spread is on the adhesive, then spraying on the surface thereof, water mist
For grain diameter less than 5 μm, spray amount is 1~2L/min* ㎡, then stands 10~20 minutes, is then dried, drying temperature
It is 70~100 DEG C, drying time is 10~15 minutes；
Third step is mixed the 2/3 of spare adhesive with the bamboo carbon powder of fluorescent powder, tourmaline powder, residue 1/2, then
It is uniformly coated on the coating of titanium dioxide and bamboo carbon powder；
4th step, then fluorescent powder, tourmaline powder coating on cover nonwoven layer；
5th step, covers polytetrafluoroethylene ethylene layer in nonwoven layer.
2. a kind of preparation method of moisture resistance high-air-permeability wallpaper according to claim 1, it is characterised in that: adhesive,
Titanium dioxide, bamboo carbon powder, fluorescent powder, tourmaline powder combine composite layer, the composite layer by 22~25 parts by weight dioxy
Change titanium, the fluorescent powder of 5~10 parts by weight, the tourmaline powder of 10~15 parts by weight, the bamboo carbon powder of 10~15 parts by weight, 20-35
The adhesive of parts by weight forms.