CN106121150A - A kind of moisture resistance high-air-permeability wallpaper and preparation method thereof - Google Patents
A kind of moisture resistance high-air-permeability wallpaper and preparation method thereof Download PDFInfo
- Publication number
- CN106121150A CN106121150A CN201610500918.1A CN201610500918A CN106121150A CN 106121150 A CN106121150 A CN 106121150A CN 201610500918 A CN201610500918 A CN 201610500918A CN 106121150 A CN106121150 A CN 106121150A
- Authority
- CN
- China
- Prior art keywords
- wallpaper
- permeability
- bamboo
- moisture resistance
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of moisture resistance high-air-permeability wallpaper, including the waterproof coating layer stacked gradually from the bottom to top, basic unit, bamboo, composite bed, polytetrafluoroethylene floor, described composite bed is made up of the titanium dioxide of 20～25 weight portions, 5～10 fluorescent material, 10～15 tourmaline powder, 10～15 bamboo carbon powders of weight portion of weight portion of weight portion, the binding agent of 20 35 weight portions.And relate to the preparation method of a kind of moisture resistance high-air-permeability wallpaper.
Description
Technical field
The present invention relates to a kind of moisture resistance high-air-permeability wallpaper and preparation method thereof.
Background technology
At present, wallpaper has rich color, change in pattern is various, texture is different, environmental protection, decorative effect noble quality allusion quotation
Refined, efficiency of construction high, it is widely used in family and finishing work.And the wallpaper of prior art is generally passed through by body paper
The processes such as embossing, printing forms, and it is only used as decorative use and does not have moistureproof moisture absorbing, and therefore such wallpaper is at tide
It is easy to go mouldy and breed bacteria when using in the environment of wet.For solving above-mentioned technical problem, necessary offer is a kind of
Having structure improved moistureproof moisture absorption wallpaper, to overcome described defect of the prior art, and people are also more desirable to wallpaper energy
Enough have the most functional.
Summary of the invention
Therefore, for above-mentioned problem, the present invention proposes a kind of simple in construction, can effectively prevent from going mouldy, can making sky
Gas forms anion, the moisture resistance high-air-permeability wallpaper that can effectively sterilize and preparation technology thereof.
For achieving the above object, present invention employs techniques below scheme: a kind of moisture resistance high-air-permeability wallpaper, including by
Under supreme stack gradually waterproof coating layer, basic unit, bamboo, composite bed, polytetrafluoroethylene floor, described composite bed is by 20
～25 titanium dioxide, 5～10 fluorescent material, 10～15 tourmaline powder, 10～15 weight portions of weight portion of weight portion of weight portion
Bamboo carbon powder, 20-35 weight portion binding agent composition.
Further, described composite bed is spliced by a plurality of bulks.
Further, it is additionally provided with nonwoven layer between described composite bed and polytetrafluoroethylene floor.
The preparation method of a kind of moisture resistance high-air-permeability wallpaper, comprises the following steps:
The first step, takes basic unit and adheres to bamboo thereon；
Second step, takes the 1/3 of standby binding agent, is utilized the mode of spraying to be uniformly sprayed in bamboo, then will
Titanium dioxide and 1/2 bamboo carbon powder mix homogeneously after, even spread on the adhesive, is sprayed the most in its surface, water smoke
Grain diameter is less than 5 μm, and spray amount is 1～2L/min*, then stands 10～20 minutes, then dries, and dries temperature
Asking 70～100 DEG C, drying time is 10～15 minutes；
3rd step, mixes the 2/3 of standby binding agent, then with fluorescent powder, tourmaline powder, the bamboo carbon powder of residue 1/2
It is uniformly coated in the coating of titanium dioxide and bamboo carbon powder；
4th step, then fluorescent powder, tourmaline powder coating on cover nonwoven layer；
5th step, covers polytetrafluoroethylene floor in nonwoven layer.
By using preceding solution, the invention has the beneficial effects as follows: this moisture resistance high-air-permeability wallpaper is by waterproof
Dope layer, basic unit, bamboo, composite bed, the setting of polytetrafluoroethylene floor, and composite bed is by titanium dioxide, fluorescent material, electricity
Gas stone powder, bamboo carbon powder, binding agent form, can effectively realize protection against the tide, sterilize, prevent from going mouldy, the high advantage such as ventilative, additionally it is possible to
Wallpaper is made to realize fluorescent effect.And the preparation method of moisture resistance high-air-permeability wallpaper its first take the 1/3 of standby binding agent, be first coated with
Cloth, is then coated the bamboo carbon powder mix homogeneously of titanium dioxide, 1/2 on it, it is achieved for the first time viscous glutinous, again through spraying,
Standing, dry, so that the stability on the surface of titanium dioxide and bamboo carbon powder increases, and the existence of bamboo carbon powder is permissible
Increase permeability, then mix the 2/3 of standby binding agent with fluorescent powder, tourmaline powder, the bamboo carbon powder of residue 1/2
Closing, be coated on it, such that the stability of whole composite bed is more preferably, and each material can play its optimum performance.
Detailed description of the invention
In conjunction with the present invention is further described with detailed description of the invention.
The present embodiment one provides a kind of moisture resistance high-air-permeability wallpaper, including the water-repellent paint stacked gradually from the bottom to top
Layer, basic unit, bamboo, composite bed, nonwoven layer, polytetrafluoroethylene floor, described composite bed is by the titanium dioxide of 20 weight portions
Titanium, the fluorescent material of 5 weight portions, the tourmaline powder of 10 weight portions, the bamboo carbon powder of 10 weight portions, the binding agent group of 20 weight portions
Become.
Its preparation method, comprises the following steps:
The first step, takes basic unit and adheres to bamboo thereon；
Second step, takes the 1/3 of standby binding agent, is utilized the mode of spraying to be uniformly sprayed in bamboo, then will
Titanium dioxide and 1/2 bamboo carbon powder mix homogeneously after, even spread on the adhesive, is sprayed the most in its surface, water smoke
Grain diameter is less than 5 μm, and spray amount is 1L/min*, then stands 10 minutes, then dries, and dries temperature and asks 70 DEG C,
Drying time is 10 minutes；
3rd step, mixes the 2/3 of standby binding agent, then with fluorescent powder, tourmaline powder, the bamboo carbon powder of residue 1/2
It is uniformly coated in the coating of titanium dioxide and bamboo carbon powder；
4th step, then fluorescent powder, tourmaline powder coating on cover nonwoven layer；
5th step, covers polytetrafluoroethylene floor in nonwoven layer.
The present embodiment two provides a kind of moisture resistance high-air-permeability wallpaper based on same inventive concept, itself and embodiment one
Difference is: described composite bed by the titanium dioxide of 25 weight portions, the fluorescent material of 10 weight portions, the tourmaline powder of 15 weight portions,
The bamboo carbon powder of 15 weight portions, the binding agent composition of 35 weight portions.And preparation method second step is: take the 1/3 of standby binding agent,
The mode being utilized spraying is uniformly sprayed in bamboo, and then the bamboo carbon powder mixing by titanium dioxide and 1/2 is equal
After even, even spread on the adhesive, is sprayed the most in its surface, and water fog particle particle diameter is less than 5 μm, and spray amount is 2L/
Min*, then stands 20 minutes, then dries, and dries temperature and asks 100 DEG C, and drying time is 15 minutes.
The present embodiment two provides a kind of moisture resistance high-air-permeability wallpaper based on same inventive concept, itself and embodiment one
Difference is: described composite bed by the titanium dioxide of 22 weight portions, the fluorescent material of 7 weight portions, the tourmaline powder of 12 weight portions, 12
The bamboo carbon powder of weight portion, the binding agent composition of 28 weight portions.And preparation method second step is: take the 1/3 of standby binding agent, will
It utilizes the mode of spraying to be uniformly sprayed in bamboo, then by titanium dioxide and the bamboo carbon powder mix homogeneously of 1/2
After, even spread on the adhesive, is sprayed the most in its surface, and water fog particle particle diameter is less than 5 μm, and spray amount is 1.5L/
Min*, then stands 15 minutes, then dries, and dries temperature and asks 85 DEG C, and drying time is 12 minutes.
This moisture resistance high-air-permeability wallpaper passes through waterproof coating layer, basic unit, bamboo, composite bed, politef
The setting of layer, and composite bed is made up of titanium dioxide, fluorescent material, tourmaline powder, bamboo carbon powder, binding agent, can effectively realize
Moistureproof, sterilize, prevent from going mouldy, the high advantage such as ventilative, additionally it is possible to make wallpaper realize fluorescent effect.And moisture resistance high-air-permeability wall
The preparation method of paper its first take the 1/3 of standby binding agent, be first coated with, then by titanium dioxide, the bamboo carbon powder mix homogeneously of 1/2
It is coated on it, it is achieved the most viscous glutinous, again through spraying, stand, drying, so that titanium dioxide and the table of bamboo carbon powder
The stability in face increases, and the existence of bamboo carbon powder can increase permeability, then by 2/3 and fluorescence of standby binding agent
Powder, tourmaline powder, the bamboo carbon powder mixing of residue 1/2, be coated on it, such that the stability of whole composite bed
More preferably, and each material can play its optimum performance.
Although specifically showing and describe the present invention in conjunction with preferred embodiment, but those skilled in the art should be bright
In vain, in the spirit and scope of the present invention limited without departing from appended claims, in the form and details can be right
The present invention makes a variety of changes, and is protection scope of the present invention.
Claims (4)
1. a moisture resistance high-air-permeability wallpaper, it is characterised in that: include waterproof coating layer, the base stacked gradually from the bottom to top
Layer, bamboo, composite bed, polytetrafluoroethylene floor, described composite bed is by the titanium dioxide of 20～25 weight portions, 5～10 weights
The amount fluorescent material of part, 10～15 tourmaline powder, 10～15 bamboo carbon powders of weight portion of weight portion, the bonding of 20-35 weight portion
Agent forms.
A kind of moisture resistance high-air-permeability wallpaper the most according to claim 1, it is characterised in that: described composite bed is by a plurality of
Bulk is spliced.
A kind of moisture resistance high-air-permeability wallpaper the most according to claim 1, it is characterised in that: described composite bed and polytetrafluoro
Nonwoven layer it is additionally provided with between pvdf layer.
4. according to the preparation method of a kind of moisture resistance high-air-permeability wallpaper described in claim 1 or 2 or 3, it is characterised in that bag
Include following steps:
The first step, takes basic unit and adheres to bamboo thereon；
Second step, takes the 1/3 of standby binding agent, is utilized the mode of spraying to be uniformly sprayed in bamboo, then will
Titanium dioxide and 1/2 bamboo carbon powder mix homogeneously after, even spread on the adhesive, is sprayed the most in its surface, water smoke
Grain diameter is less than 5 μm, and spray amount is 1～2L/min*, then stands 10～20 minutes, then dries, and dries temperature
Asking 70～100 DEG C, drying time is 10～15 minutes；
3rd step, mixes the 2/3 of standby binding agent, then with fluorescent powder, tourmaline powder, the bamboo carbon powder of residue 1/2
It is uniformly coated in the coating of titanium dioxide and bamboo carbon powder；
4th step, then fluorescent powder, tourmaline powder coating on cover nonwoven layer；
5th step, covers polytetrafluoroethylene floor in nonwoven layer.