CN106497206A - A kind of environmental protection cracking resistance water-borne decorative plate putty and preparation method thereof - Google Patents
A kind of environmental protection cracking resistance water-borne decorative plate putty and preparation method thereof Download PDFInfo
- Publication number
- CN106497206A CN106497206A CN201611224440.0A CN201611224440A CN106497206A CN 106497206 A CN106497206 A CN 106497206A CN 201611224440 A CN201611224440 A CN 201611224440A CN 106497206 A CN106497206 A CN 106497206A
- Authority
- CN
- China
- Prior art keywords
- cracking resistance
- parts
- water
- environmental protection
- decorative plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of environmental protection cracking resistance water-borne decorative plate putty, and the putty includes the composition of following weight portion：Acrylic resin：5 ~ 10 parts, nanometer cracking resistance resin solution：5 ~ 10 parts, levelling agent：0.05 ~ 0.15 part, wetting agent：0.1 ~ 0.5 part, polyvinyl alcohol：0.1 ~ 0.5 part, water：5 ~ 10 parts, filler：40 ~ 60 parts, cracking resistance powder：20 ~ 30 parts.Use of the putty by cracking resistance powder, improves the cracking of putty, expands performance of the water-borne decorative plate putty on various different timber.
Description
Technical field
The invention belongs to decoration industrial chemicals technical field, specifically, is related to a kind of environmental protection cracking resistance water-borne decorative plate putty
And preparation method thereof.
Background technology
Putty (fillering) is a kind of material of decoration property of smooth surface of wall, is a kind of thick slurry coating material, is coating
Requisite a kind of product before painting.Painting is imposed on priming paint or is directly applied and imposes on object, in order to remove on coated article surface
Rugged defect.It is formulated using paint base, auxiliary agent, mass filler and appropriate coloring pigment on a small quantity, pigment master used
If iron oxide red, carbon black, chrome yellow etc..Filler is mainly calcium bicarbonate, talcum powder etc..Local can be filled up the working surface of depression,
Also can strike off in all surfaces, typically after prime coat is parched, be applied over primer coat surface.It is required that tack is good, toasted
Do not crack in journey.
Decorative panel is a kind of artificial board.It is with multiple special paper after chemical treatment, with HTHP gluing
The thermosetting laminated plastic that agent is made, plate face have various wood grains or pattern, and light is smooth, bright in colour attractive in appearance, while having
The good physical properties such as higher wear-resisting, heat-resisting, cold-resistant, fire prevention.Be particular about in the wall in many senior rooms, roof, making
Cabinet, cupboard, table, bed, the workbench of precision instrument, the experimental bench in laboratory, television set, radio and other broadcast telecommunication equipments
Shell, mostly adopt this new decorative panel.
Decorative panel basic material be wood, primarily serve the purpose of carryings, however, its expand with heat and contract with cold because wood plant difference and not
With the putty of institute's application causes to ftracture often because material is different.If using low film formation temperature resin, though partly can solve out
Split problem, but cost viewpoint and persistence, cause again secondary smear problem, on the contrary increase cost.
For decorative panel putty, the current country is primarily present following patent document：
Patent publication No.：CN105778607A, discloses a kind of environment protection interior wall putty, in parts by weight, including：Interior wall is greasy
100 parts of subbase powder；Glutinous rice glue 5-12 part；Pre-gelatinized starch 5-12 parts；Bamboo-carbon fibre or bamboo charcoal powder 2-6 part；Spices 8-10 parts；Receive
Rice ZnO1-3 parts；Water 20-60 parts.Described inner wall putty original washing powder includes coarse whiting, grey calcium and white cement；The length of bamboo-carbon fibre is
0.5-5 millimeters, a diameter of 10-20 microns；Bamboo charcoal powder fineness 200-300 mesh；A diameter of 10-20 nanometers of nano-ZnO.Additionally
The method for disclosing the environment protection interior wall putty for preparing described.The present invention is coordinated by each materials cooperation of the ratio, can be notable
Increase cracking resistance, hardening strength, packing and mould proof, antibacterial, the prebiotic environmental-protecting performance of described environment protection interior wall putty.So
And, improve the cracking resistance of putty in the patent using glutinous rice glue, aging with colloid, viscosity declines, cracking resistance with
Decline, service life is short.
Content of the invention
For solving above-mentioned problem, it is an object of the invention to provide a kind of environmental protection cracking resistance water-borne decorative plate putty and
Its preparation method, the putty improve the cracking of putty by the use of cracking resistance powder, expand water-borne decorative plate putty various not
With the performance on timber.
For reaching above-mentioned purpose, the technical scheme is that：
A kind of environmental protection cracking resistance water-borne decorative plate putty, the putty include the composition of following weight portion：Acrylic resin：5
～10 parts, nanometer cracking resistance resin solution：5～10 parts, levelling agent：0.05～0.15 part, wetting agent：0.1～0.5 part, polyethylene
Alcohol：0.1～0.5 part, water：5～10 parts, filler：40～60 parts, cracking resistance powder：20～30 parts.
Further, the nanometer cracking resistance resin solution by nanometer cracking resistance resin and water with 1：1 weight ratio is mixed to form.
Preferably, the putty includes the composition of following weight portion：Acrylic resin：8.75 parts, nanometer cracking resistance resin is molten
Liquid：7.5 parts, levelling agent：0.10 part, wetting agent：0.30 part, polyvinyl alcohol：0.20 part, water：8.15 parts, filler：50 parts, cracking resistance
Powder：25 parts.
Preferably, in the nanometer cracking resistance resin solution, 3.75 parts of nanometer cracking resistance resin, 3.75 parts of water.
Separately, described filler is calcium carbonate.
Separately have, the Carbonate Particle Size is 1200～1300 mesh.
Again, the polyvinyl alcohol is water-soluble poval.
Further, the levelling agent is Siloxane-Oxyalkylene Copolymers levelling agent.
And, the cracking resistance powder is flaky inorganic materials.
Wherein, the nanometer cracking resistance resin solution and cracking resistance powder are purchased from Shanghai three and determine Chemical Industry Science Co., Ltd.
Meanwhile, the present invention also provides a kind of preparation method of environmental protection cracking resistance water-borne decorative plate putty, comprises the steps：
1) by acrylic resin, nanometer cracking resistance resin solution according to proportioning, stir under the rotating speed of 300～350 turns/min,
Obtain product I；
2) levelling agent, wetting agent are added in product I, obtains product II；
3) polyvinyl alcohol is added in product II, obtain product III；
4) add filler, cracking resistance powder to stir, and packed product III, obtain the aqueous dress of the environmental protection cracking resistance
Plaque putty.
The beneficial effects of the present invention is：
The decorative panel putty dries simple, minimizing energy loss；Putty grinability increases, non-sticky sand paper；Due to using
Sheet cracking resistance powder so that substrate adhesion increases；Existing product compares cold cycling can increase by three cold cyclings and in difference
Wood plant and will not ftracture above, additionally, the preparation of the decorative panel putty, the addition of raw material components need to be entered in strict accordance with order
OK so that final gained putty steady quality, the whether random mixing or out of order mixing of several components can all affect to decorate
The product quality of plate putty.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail.Following examples will be helpful to the technology of this area
Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the ordinary skill to this area
For personnel, without departing from the inventive concept of the premise, some deformations and improvement can also be made.These belong to the present invention
Protection domain.
A kind of environmental protection cracking resistance water-borne decorative plate putty of the present invention, the putty include the composition of following weight portion：
Acrylic resin：5～10 parts, nanometer cracking resistance resin solution：5～10 parts, levelling agent：0.05～0.15 part, wetting agent：0.1～
0.5 part, polyvinyl alcohol：0.1～0.5 part, water：5～10 parts, filler：40～60 parts, cracking resistance powder：20～30 parts.
Further, the nanometer cracking resistance resin solution by nanometer cracking resistance resin and water with 1：1 weight ratio is mixed to form.
Preferably, the putty includes the composition of following weight portion：Acrylic resin：8.75 parts, nanometer cracking resistance resin is molten
Liquid：7.5 parts, levelling agent：0.10 part, wetting agent：0.30 part, polyvinyl alcohol：0.20 part, water：8.15 parts, filler：50 parts, cracking resistance
Powder：25 parts.
Preferably, in the nanometer cracking resistance resin solution, 3.75 parts of nanometer cracking resistance resin, 3.75 parts of water.
Separately, described filler is calcium carbonate.
Separately have, the Carbonate Particle Size is 1200～1300 mesh.
Again, the polyvinyl alcohol is water-soluble poval.
Further, the levelling agent is Siloxane-Oxyalkylene Copolymers levelling agent.
And, the cracking resistance powder is flaky inorganic materials.
Wherein, the nanometer cracking resistance resin solution and cracking resistance powder are purchased from Shanghai three and determine Chemical Industry Science Co., Ltd.
Meanwhile, the present invention also provides a kind of preparation method of environmental protection cracking resistance water-borne decorative plate putty, comprises the steps：
1) by acrylic resin, nanometer cracking resistance resin solution according to proportioning, stir under the rotating speed of 300～350 turns/min,
Obtain product I；
2) levelling agent, wetting agent are added in product I, obtains product II；
3) polyvinyl alcohol is added in product II, obtain product III；
4) add filler, cracking resistance powder to stir, and packed product III, obtain the aqueous dress of the environmental protection cracking resistance
Plaque putty.
A kind of environmental protection cracking resistance water-borne decorative plate putty provided by the present invention, its cracking resistance test are as follows：
| Cold cycling number of times | Putty-like state (diameter 50mm) | Putty-like state (diameter 100mm) | |
| The present invention | N+3 time | It was found that ftractureing, coming off | It was found that ftractureing, coming off |
| Comparative example | N times | It was found that a small amount of crackle, nothing come off | It was found that a large amount of crackles, coming off substantially |
Wherein, N is 5～10.
Test condition：Specimen size：40mm × 110mm × (0.2～0.3) mm；Blade coating 1mm is thick for putty membrane, thick after polishing
0.8～0.9mm of degree, constant temperature 12 hours at 65～70 DEG C, constant temperature 12 hours at -20 DEG C, used as the circulation that once colds and heat succeed each other.
It should be noted that above example is only in order to illustrating technical scheme and unrestricted.Although with reference to compared with
Good embodiment has been described in detail to the present invention, it will be understood by those within the art that, can be to the technology of invention
Scheme is modified or equivalent, and without deviating from the scope of technical solution of the present invention, which all should cover the power in the present invention
In sharp claimed range.
Claims (10)
1. a kind of environmental protection cracking resistance water-borne decorative plate putty, it is characterised in that the putty includes the composition of following weight portion：Propylene
Acid resin：5 ~ 10 parts, nanometer cracking resistance resin solution：5 ~ 10 parts, levelling agent：0.05 ~ 0.15 part, wetting agent：0.1 ~ 0.5 part, gather
Vinyl alcohol：0.1 ~ 0.5 part, water：5 ~ 10 parts, filler：40 ~ 60 parts, cracking resistance powder：20 ~ 30 parts.
2. a kind of environmental protection cracking resistance water-borne decorative plate putty according to claim 1, it is characterised in that the nanometer cracking resistance tree
Lipoprotein solution is by nanometer cracking resistance resin and water with 1：1 weight ratio is mixed to form.
3. a kind of environmental protection cracking resistance water-borne decorative plate putty according to claim 1, it is characterised in that the putty include as
The composition of lower weight portion：Acrylic resin：8.75 parts, nanometer cracking resistance resin solution：7.5 parts, levelling agent：0.10 part, wetting agent：
0.30 part, polyvinyl alcohol：0.20 part, water：8.15 parts, filler：50 parts, cracking resistance powder：25 parts.
4. a kind of environmental protection cracking resistance water-borne decorative plate putty according to claim 3, it is characterised in that the nanometer cracking resistance tree
In lipoprotein solution, 3.75 parts of nanometer cracking resistance resin, 3.75 parts of water.
5. a kind of environmental protection cracking resistance water-borne decorative plate putty according to claim 3, it is characterised in that described filler is carbonic acid
Calcium.
6. a kind of environmental protection cracking resistance water-borne decorative plate putty according to claim 5, it is characterised in that the Carbonate Particle Size
For 1200 ~ 1300 mesh.
7. a kind of environmental protection cracking resistance water-borne decorative plate putty according to claim 3, it is characterised in that the polyvinyl alcohol is
Water-soluble poval.
8. a kind of environmental protection cracking resistance water-borne decorative plate putty according to claim 3, it is characterised in that the levelling agent is poly-
Ether modified polyorganosiloxane levelling agent.
9. a kind of environmental protection cracking resistance water-borne decorative plate putty according to claim 3, it is characterised in that the cracking resistance powder is piece
Shape inorganic material.
10. a kind of preparation method of a kind of environmental protection cracking resistance water-borne decorative plate putty as any one of claim 1 ~ 9, its
It is characterised by, comprises the steps：
1) by acrylic resin, nanometer cracking resistance resin solution according to proportioning, stir under the rotating speed of 300 ~ 350 turns/min, obtain
Product I；
2) levelling agent, wetting agent are added in product I, obtains product II；
3) polyvinyl alcohol is added in product II, obtain product III；
4) add filler, cracking resistance powder to stir, and packed product III, obtain the environmental protection cracking resistance water-borne decorative plate
Putty.