CN107815215A - A kind of water-based stone-like coating formula and water-based imitative stone terrace - Google Patents
A kind of water-based stone-like coating formula and water-based imitative stone terrace Download PDFInfo
- Publication number
- CN107815215A CN107815215A CN201710978255.9A CN201710978255A CN107815215A CN 107815215 A CN107815215 A CN 107815215A CN 201710978255 A CN201710978255 A CN 201710978255A CN 107815215 A CN107815215 A CN 107815215A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- component
- stone
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of water-based stone-like coating formula, including water-base epoxy infiltration priming paint, waterborne organic silicon floating coating, water-based imitative stone finish paint and water-based finishing varnish, water-based imitative stone finish paint are weight score dephasing：Continuous phase：Protect sol solution=2：2：1 composition, dispersed phase and continuous phase are made by following parts by weight raw material proportioning, dispersed phase：50 55 parts of deionized water, 0.3 0.4 parts of defoamer, 0.1 0.2 parts of wetting agent, 0.2 0.4 parts of dispersant, 15 20 parts of inorganic color stuffing, 23 28 parts of organic silicon emulsion, 0.9 1.1 parts of coalescents, 0.5 1 parts of propane diols, 0.8 0.9 parts of auxiliary rheological agents, 0.2 0.3 parts of anticorrosion and bactericidal agent, 0.1 0.2 parts of PH conditioning agents；Continuous phase：25 40 parts of deionized water, 55 70 parts of organic silicon emulsion, 0.2 0.4 parts of defoamer, 23 parts of coalescents, 0.5 1 parts of propane diols, 0.6 0.8 parts of auxiliary rheological agents, 0.1 0.2 parts of anticorrosion and bactericidal agent.The invention also discloses the water-based imitative stone terrace that above-mentioned coating is prepared.Coating of the present invention, which is used for terrace coating outward appearance, can produce height imitation stone effect, low cost, VOC free exhaust emission, safety and environmental protection.
Description
Technical field
The present invention relates to building coating field, more particularly to a kind of water-based stone-like coating formula and the application formula is water-based
Imitative stone terrace.
Background technology
Currently, most often applied oiliness epoxide terrace is because its is seamless in terrace application, and easy to clean, abrasion performance etc. is excellent
Point, it is widely used in terrace application, but existing oiliness epoxide terrace application requires high to the construction environment of job site, deposits
Polluted in VOC emission, easily coating performance does not reach design requirement caused by the reasons such as construction technology, or appearance is bad.
The features such as and marble terrace decorative effect is good, but its cost is high, long in time limit, and process of deployment is frangible greatly limit its development
Space.
The content of the invention
For above-mentioned technical background problem, it is an object of the invention to provide a kind of water-based stone-like coating formula and water-based imitative stone
Terrace, diversified height imitation stone effect and health environment-friendly.
To achieve the above objectives, the invention discloses a kind of water-based stone-like coating formula, including water-base epoxy to permeate priming paint,
Waterborne organic silicon floating coating, water-based imitative stone finish paint and water-based finishing varnish, described water-based imitative stone finish paint are that weight ratio is scattered
Phase：Continuous phase：Protect sol solution=2：2：1 composition, dispersed phase are made with continuous phase by following parts by weight raw material proportioning：
Dispersed phase
Deionized water 50-55 parts, defoamer 0.3-0.4 parts, wetting agent 0.1-0.2 parts, dispersant 0.2-0.4 parts are inorganic
Color stuffing 15-20 parts, organic silicon emulsion 23-28 parts, coalescents 0.9-1.1 parts, propane diols 0.5-1 parts, auxiliary rheological agents 0.8-
0.9 part, anticorrosion and bactericidal agent 0.2-0.3 parts, PH conditioning agent 0.1-0.2 parts；
Continuous phase
Deionized water 25-40 parts, organic silicon emulsion 55-70 parts, defoamer 0.2-0.4 parts, coalescents 2-3 parts, the third two
Alcohol 0.5-1 parts, auxiliary rheological agents 0.6-0.8 parts, anticorrosion and bactericidal agent 0.1-0.2 parts.
Wherein, described water-base epoxy infiltration priming paint includes the component of following parts by weight, component A：Aqueous epoxy emulsion
70-90 parts, defoamer 0.05-0.1 parts, wetting agent 0.1-0.2 parts, deionized water 10-20 parts；B component：Water-base epoxy solidifies
Agent.The ratio of weight and number of component A and B component is 1：(1.5~2).
Wherein, described waterborne organic silicon floating coating includes the component of following parts by weight, deionized water 10-20 parts, divides
Powder 0.5-0.7 parts, wetting agent 0.2-0.3 parts, defoamer 0.2-0.4 parts, PH conditioning agent 0.1-0.5 parts, organic silicon emulsion 40-
50 parts, propane diols 0.5-1 parts, coalescents 1-3 parts, inorganic color stuffing 30-40 parts, auxiliary rheological agents 0.8-1 parts, anticorrosion and bactericidal agent
0.1-0.2 parts.
In one embodiment, described water-based finishing varnish is aqueous polyurethane, and it includes the component of following parts by weight：
Component A：Hydroxyl acrylic aqueous dispersion 60-80 parts, wetting agent 0.1-0.2 parts, auxiliary rheological agents 0.2-0.3 parts, defoaming
Agent 0.1-0.2 parts, levelling agent 0.2-0.4 parts, deionized water 20-40 parts；
B component：Hydrophilic modifying HDI curing agent；The ratio of weight and number of component A and B component is (3~5)：1.
In another embodiment, described water-based finishing varnish is water-based fluorocarbon, and it includes the component of following parts by weight：
Component A：Water-base fluorocarbon emulsion 60-80 parts, wetting agent 0.2-0.3 parts, auxiliary rheological agents 0.2-0.3 parts, defoamer
0.1-0.2 parts, levelling agent 0.2-0.4 parts, deionized water 20-40 parts；B component：Hydrophilic modifying HDI curing agent；Component A and B groups
The ratio of weight and number of part is (8~10)：1.
Preferably, described water-based finishing varnish also includes the effect pigment that parts by weight are 0.5~1 part.So that coating
Face, which is formed, dazzles beautiful metallic travel.
Preferably, described water-based finishing varnish also includes the vertical line agent that parts by weight are 2~3 parts.So that coated side is produced
Raw high-end frosted finish effect.
Preferably, described inorganic color stuffing is one kind in rutile type titanium white, powdered whiting, calcined kaolin
It is or several；Described auxiliary rheological agents are the one or more in hydroxyethyl ether cellulose, polyurethane, alkali swelling type thickener.
The invention also discloses a kind of water-based imitative stone terrace, it is prepared from the bottom to top including above-mentioned coating formula water-based
Epoxy infiltration prime coat, waterborne organic silicon floating coating layer, water-based imitative stone top coat layer and water-based finishing varnish layer.
Wherein, the coated weight of the water-base epoxy infiltration priming paint of described water-base epoxy infiltration prime coat is (0.04~0.05)
Kg/m2, the coated weight of the waterborne organic silicon floating coating of described waterborne organic silicon floating coating layer is (0.15~0.20) kg/m2,
The coated weight of the water-based imitative stone finish paint of described water-based imitative stone top coat layer is (0.8~2) kg/m2, described water-based finishing varnish
The coated weight of the water-based finishing varnish layer of layer is (0.04~0.06) kg/m2.
The beneficial effects of the present invention are：Coating of the present invention, which is used for terrace coating outward appearance, can produce height imitation stone effect, make
Valency is low, and the construction period is short, seamless easy to clean, VOC free exhaust emission, safety and environmental protection.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to invent into
Row is further described.
The invention discloses a kind of water-based stone-like coating formula, including water-base epoxy infiltration priming paint, applied in waterborne organic silicon
Paint, water-based imitative stone finish paint and the coating formula of water-based finishing varnish four.The formula of each layer paint by raw material in table 1 below~table 5 into
Divide and be made.
The water-base epoxy of table 1. permeates priming paint material composition table
The waterborne organic silicon floating coating material composition table of table 2
The water-based imitative stone finish paint dispersed phase material composition tables of table 3-1
The water-based imitative stone finish paint continuous phase material composition tables of table 3-2
The water-based imitative stone finish paint Protection glue solution materials component lists of table 3-3
By table 3-1, table 3-2, table 3-3 prepare dispersed phase, continuous phase and the protection sol solution of water-based imitative stone finish paint respectively, so
2 are pressed afterwards：2：1 ratio feeding is mixed to prepare water-based imitative stone finish paint.
4 water-based finishing varnish of table (aqueous polyurethane system) material composition table
5 water-based finishing varnish of table (water-based fluorocarbon system) material composition table
It is described in detail below for the preparation process of embodiment one, the material composition of embodiment two：
Embodiment one
Present embodiment discloses a kind of water-based stone-like coating formula, including water-base epoxy infiltration priming paint, in waterborne organic silicon
Japanning, water-based imitative stone finish paint and water-based finishing varnish, four layers of paint formula are following to prepare：
1st, water-base epoxy infiltration priming paint is prepared
Aqueous epoxy emulsion is added in stirring container for 90 parts by component A, and NXZ defoamers 0.1 are added under middle stirring at low speed
Part and 0.2 part of Tego270 wetting agent, stirring add 10 parts of deionized water after 5 minutes, and middle stirring at low speed is uniform.
B component：200 parts of high-performance water-based epoxy curing agent.Water-base epoxy infiltration is made with paint for component A and B component
Priming paint.
2nd, prepare waterborne organic silicon and be modified floating coating
11 parts of deionized water is added in stirring container, hydroxyethyl ether cellulose is sequentially added under middle stirring at low speed state
0.1 part of (auxiliary rheological agents), 0.6 part of SN-5040 dispersants, 0.2 part of EF-106 wetting agents, 0.2 part of NXZ defoamers, AMP-95 are adjusted
Save 0.1 part of agent (PH conditioning agents)；Appropriate rotating speed of heightening sequentially adds R706 rutile type titanium whites, powdered whiting, calcining height
Ridge soil (inorganic color stuffing) amounts to 30 parts, and it is qualified to be dispersed to fineness at a high speed；1 part of deionized water is added to reduce the temperature of slurry,
Reduce rotating speed and sequentially add 50 parts of organic silicon emulsion, 2.5 parts of C-12 coalescents, 1 part of propane diols, 0.2 part of NXZ defoamers, poly-
0.4 part of urethane thickener (auxiliary rheological agents), 0.4 part of alkali swelling type thickener (auxiliary rheological agents), 0.2 part of anticorrosion and bactericidal agent, in it is low
Speed stirs.
3rd, water-based imitative stone finish paint is prepared
A dispersed phases
49.8 parts of deionized water is added in stirring container, hydroxyethyl ether cellulose is sequentially added under middle stirring at low speed state
0.9 part of (auxiliary rheological agents), 0.3 part of SN-5040 dispersants, 0.1 part of EF-106 wetting agents, 0.2 part of NXZ defoamers, AMP-95 are adjusted
Save 0.2 part of agent (PH conditioning agents)；It is appropriate to heighten that rotating speed sequentially adds R706 rutile type titanium whites, 4000 mesh calcined kaolins are total to
20 parts of meter, it is qualified to be dispersed at a high speed fineness；0.2 part of deionized water is added to reduce the temperature of slurry, rotating speed is reduced and sequentially adds
28 parts of organic silicon emulsion, 1.1 parts of C-12 coalescents, 0.5 part of propane diols, 0.2 part of NXZ defoamers, 0.2 part of RS preservatives, EPW
0.1 part of mould inhibitor, moderate-speed mixer is uniform.
B continuous phases add 25 parts of deionized water in stirring container, and NXZ defoamers are sequentially added under middle stirring at low speed state
0.2 part, 3 parts of C-12 coalescents, 1 part of propane diols, RS preservatives 0.2,70 parts of silicone acrylic emulsion, TT-935 alkali swollen thickeners
0.6 part of (auxiliary rheological agents), properly increase rotating speed and stir.
C protection sol solutions add 47 parts of deionized water in stirring container, and S482 rubber powders 3 are added under middle stirring at low speed state
Part, scattered 30-40min is transparent at a high speed clarifies glue.
The water-based imitative stone finish paints of d add 20 parts of sol solution of protection into the granulation container of comminutor, and then addition is adjusted to a certain
40 parts of the dispersed phase of color, size setting speed and the time of color tablets are presented according to the color, start comminutor and be granulated；It is each
After the dispersed phase of color is granulated successively, is poured into bigger container by institute's chromoplastid is light and slow, be eventually adding 40 parts of continuous phase, delayed
It is slow well mixed.
4th, water-based finishing varnish is prepared
Component A adds 20 parts of deionized water in stirring container, and EF-106 wettings are sequentially added under middle stirring at low speed state
0.2 part of agent, 0.1 part of BYK028 defoamers, 80 parts of hydroxyl acrylic aqueous dispersion, 0.3 part of BYK333 levelling agents, polyurethane thickener
0.3 part of (auxiliary rheological agents), stir and aqueous polyurethane cover component A is made.
B component hydrophilic modifying HDI curing agent.
According to component A：B component=5：1 is made water-based finishing varnish with paint.
Embodiment two
Present embodiment discloses a kind of water-based stone-like coating formula, according to implementation the step of embodiment one using table 1-3
The proportioning of example two prepares water-base epoxy infiltration priming paint, organic-silicon-modified floating coating and water-based imitative stone finish paint.It is water-based in the present embodiment
Finishing varnish uses water-based fluorocarbon system raw material, and its preparation process is as follows：
Component A adds 20 parts of deionized water in stirring container, and EF-106 wettings are sequentially added under middle stirring at low speed state
0.3 part of agent, 0.1 part of BYK028 defoamers, 80 parts of water-base fluorocarbon emulsion, 0.4 part of BYK333 levelling agents, polyurethane thickener (stream
Become auxiliary agent) 0.2 part, stir and aqueous polyurethane cover component A is made.
B component hydrophilic modifying HDI curing agent.
According to component A：B component=10：1, with paint, adds 0.5 part of effect pigment, stands 2 parts of line agent, that is, water-based cover is made
Varnish.
According to above-described embodiment one, the formula of embodiment two, the invention also discloses a kind of water-based imitative stone terrace.This is water-based
Imitative stone terrace includes water-base epoxy infiltration prime coat, waterborne organic silicon floating coating layer from the bottom to top, water-based imitative stone top coat layer and
Water-based finishing varnish layer.Wherein water-base epoxy infiltration prime coat is by the water-base epoxy infiltration priming paint coating shape in above-described embodiment
Into.Waterborne organic silicon floating coating layer is coated by waterborne organic silicon floating coating and formed.Water-based imitative stone top coat layer is by water-based imitative stone finish paint
Coating is formed.Water-based finishing varnish layer is coated by water-based finishing varnish to be formed.
The construction technology of water-based imitative stone terrace is as follows：
1) roller coat permeates priming paint to twice water-base epoxy together on the mattess after repairing levelling dedusting, and 25 DEG C dry
Dry at least 24h, dosage are (0.04-0.05) kg/ ㎡.
2) after the completion of water-base epoxy infiltration priming paint is dried, one of waterborne organic silicon of roller coat applies in being modified, 25 DEG C of dry 2-4h；
Dosage is (0.15-0.20) kg/ ㎡.
3) apply to dry 2-4h and touch to finger during waterborne organic silicon is modified and do not glue, water-based imitative stone finish paint spraying is carried out, according to required
Imitation stone effect, dosage is (0.8-2) kg/ ㎡；25 DEG C of drying at least 48h.
4) for roller coat together to the water-based finishing varnish of twice, dosage is (0.04-0.06) kg/ ㎡.Drying maintenance 48h for 25 DEG C can
Upper people, 7d can carry out performance test or come into operation.
The water-based imitative stone terrace that the water-based imitative stone floor coatings of the present invention are coated to obtain is according to standard《GB/T 22374-
2008 terrace coating materials》Test its main performance index：
The water-based imitative stone terrace primary coat performance test table of table 6.
The water-based imitative stone terrace surface of table 7. applies performance test table
From table 6, table 7 as can be seen that the water-based imitative stone terrace primary coat of the present invention and face liquid meet standard requirement, excellent performance.
And terrace imitation stone effect is good, it can also as needed be formed and dazzle beautiful metallic travel or high-end frosted finish effect, cost is relatively low,
Suitable popularization and application.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, the change or replacement that can readily occur in,
It should all be included within the scope of the present invention.
Claims (10)
- A kind of 1. water-based stone-like coating formula, it is characterised in that including water-base epoxy permeate priming paint, waterborne organic silicon floating coating, Water-based imitative stone finish paint and water-based finishing varnish, described water-based imitative stone finish paint are that weight ratio is dispersed phase：Continuous phase：Protect peptization Liquid=2：2：1 composition, dispersed phase and continuous phase are made by following parts by weight raw material proportioning：Dispersed phase deionized water 50-55 parts, defoamer 0.3-0.4 parts, wetting agent 0.1-0.2 parts, dispersant 0.2-0.4 parts, nothing Machine color stuffing 15-20 parts, organic silicon emulsion 23-28 parts, coalescents 0.9-1.1 parts, propane diols 0.5-1 parts, auxiliary rheological agents 0.8-0.9 parts, anticorrosion and bactericidal agent 0.2-0.3 parts, PH conditioning agent 0.1-0.2 parts；Continuous phase deionized water 25-40 parts, organic silicon emulsion 55-70 parts, defoamer 0.2-0.4 parts, coalescents 2-3 parts, third Glycol 0.5-1 parts, auxiliary rheological agents 0.6-0.8 parts, anticorrosion and bactericidal agent 0.1-0.2 parts.
- 2. water-based stone-like coating formula as claimed in claim 1, it is characterised in that：Described water-base epoxy infiltration priming paint includes The component of following parts by weight, component A：Aqueous epoxy emulsion 70-90 parts, defoamer 0.05-0.1 parts, wetting agent 0.1-0.2 Part, deionized water 10-20 parts；B component：The ratio of weight and number of aqueous epoxy curing agent, component A and B component is 1：（1.5~2）.
- 3. water-based stone-like coating formula as claimed in claim 1, it is characterised in that：Described waterborne organic silicon floating coating includes The component of following parts by weight, deionized water 10-20 parts, dispersant 0.5-0.7 parts, wetting agent 0.2-0.3 parts, defoamer 0.2- 0.4 part, PH conditioning agent 0.1-0.5 parts, organic silicon emulsion 40-50 parts, propane diols 0.5-1 parts, coalescents 1-3 parts, inorganic face Filler 30-40 parts, auxiliary rheological agents 0.8-1 parts, anticorrosion and bactericidal agent 0.1-0.2 parts.
- 4. water-based stone-like coating formula as claimed in claim 1, it is characterised in that：Described water-based finishing varnish is water-based poly- Urethane, it includes the component of following parts by weight：Component A：Hydroxyl acrylic aqueous dispersion 60-80 parts, wetting agent 0.1-0.2 parts, auxiliary rheological agents 0.2-0.3 parts, defoamer 0.1-0.2 parts, levelling agent 0.2-0.4 parts, deionized water 20-40 parts；B component：Hydrophilic modifying HDI curing agent；The ratio of weight and number of component A and B component is（3~5）：1.
- 5. water-based stone-like coating formula as claimed in claim 1, it is characterised in that：Described water-based finishing varnish is water-based fluorine Carbon, it includes the component of following parts by weight：Component A：Water-base fluorocarbon emulsion 60-80 parts, wetting agent 0.2-0.3 parts, auxiliary rheological agents 0.2-0.3 parts, defoamer 0.1-0.2 Part, levelling agent 0.2-0.4 parts, deionized water 20-40 parts；B component：Hydrophilic modifying HDI curing agent；The weight of component A and B component Portion rate is（8~10)：1.
- 6. the water-based stone-like coating formula as described in claim 4 or 5, it is characterised in that：Described water-based finishing varnish also wraps Include the effect pigment that parts by weight are 0.5~1 part.
- 7. the water-based stone-like coating formula as described in claim 4 or 5, it is characterised in that：Described water-based finishing varnish also includes Parts by weight are 2~3 parts of vertical line agent.
- 8. water-based stone-like coating formula as claimed in claim 1, it is characterised in that：Described inorganic color stuffing is rutile-type One or more in titanium dioxide, powdered whiting, calcined kaolin；Described auxiliary rheological agents are hydroxyethyl ether cellulose, gathered One or more in urethane, alkali swelling type thickener.
- A kind of 9. water-based imitative stone terrace, it is characterised in that：Include the coating as described in any one of claim 1~8 from the bottom to top It is formulated water-base epoxy infiltration prime coat, waterborne organic silicon floating coating layer, water-based imitative stone top coat layer and the water-based cover being prepared Layer of varnish.
- A kind of 10. water-based imitative stone terrace as claimed in claim 9, it is characterised in that：Described water-base epoxy infiltration prime coat Water-base epoxy infiltration priming paint coated weight be（0.04~0.05）kg/m2, described waterborne organic silicon floating coating layer it is water-based The coated weight of organosilicon floating coating is（0.15~0.20）kg/m2, the water-based imitative stone finish paint of described water-based imitative stone top coat layer Coated weight is（0.8~2）Kg/m2, the coated weight of the water-based finishing varnish layer of described water-based finishing varnish layer are（0.04~ 0.06）kg/m2。