CN107815215B - Formula of water-based stone-like coating and water-based stone-like terrace - Google Patents
Formula of water-based stone-like coating and water-based stone-like terrace Download PDFInfo
- Publication number
- CN107815215B CN107815215B CN201710978255.9A CN201710978255A CN107815215B CN 107815215 B CN107815215 B CN 107815215B CN 201710978255 A CN201710978255 A CN 201710978255A CN 107815215 B CN107815215 B CN 107815215B
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- stone
- coating
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a formula of a water-based stone-like coating, which comprises a water-based epoxy penetrating primer, a water-based organic silicon middle coating, a water-based stone-like finish paint and a water-based finish varnish, wherein the water-based stone-like finish paint is a dispersed phase with the weight ratio: continuous phase: protective gel solution = 2: 2: 1, the dispersed phase and the continuous phase are prepared from the following raw materials in parts by weight: 50-55 parts of deionized water, 0.3-0.4 part of defoaming agent, 0.1-0.2 part of wetting agent, 0.2-0.4 part of dispersing agent, 15-20 parts of inorganic pigment and filler, 23-28 parts of organosilicon emulsion, 0.9-1.1 part of film-forming assistant, 0.5-1 part of propylene glycol, 0.8-0.9 part of rheological assistant, 0.2-0.3 part of antiseptic bactericide and 0.1-0.2 part of pH regulator; continuous phase: 25-40 parts of deionized water, 55-70 parts of organic silicon emulsion, 0.2-0.4 part of defoaming agent, 2-3 parts of film-forming assistant, 0.5-1 part of propylene glycol, 0.6-0.8 part of rheological assistant and 0.1-0.2 part of anticorrosive bactericide. The invention also discloses a water-based stone-like terrace prepared from the coating. The coating disclosed by the invention can generate a high stone-like effect when being used for floor coating, is low in manufacturing cost, free of VOC (volatile organic compound) emission pollution, safe and environment-friendly.
Description
Technical Field
The invention relates to the field of building coatings, in particular to a formula of a water-based stone-like coating and a water-based stone-like terrace applying the formula.
Background
At present, the most commonly used oily epoxy terrace in the terrace coating is widely applied to the terrace coating because of its advantages such as seamless, easy cleanness, wear-resisting, but the current oily epoxy terrace coating has high requirements for the construction environment of job site, has VOC emission pollution, causes the coating performance to reach the designing requirement easily because of reasons such as construction technology, or the outward appearance effect is not good. The marble terrace has good decorative effect, but has the characteristics of high manufacturing cost, long construction period, fragile laying process and the like, thereby greatly limiting the development space of the marble terrace.
Disclosure of Invention
Aiming at the technical background problems, the invention aims to provide a water-based stone-like coating formula and a water-based stone-like terrace, which have diversified high stone-like effects and are healthy and environment-friendly.
In order to achieve the above purposes, the invention discloses a water-based stone-like coating formula, which comprises a water-based epoxy penetrating primer, a water-based organic silicon middle coating, a water-based stone-like finish paint and a water-based finish varnish, wherein the water-based stone-like finish paint comprises the following dispersed phases in percentage by weight: continuous phase: protective colloid solution 2: 2: 1, the dispersed phase and the continuous phase are prepared from the following raw materials in parts by weight:
dispersed phase
50-55 parts of deionized water, 0.3-0.4 part of defoaming agent, 0.1-0.2 part of wetting agent, 0.2-0.4 part of dispersing agent, 15-20 parts of inorganic pigment and filler, 23-28 parts of organosilicon emulsion, 0.9-1.1 part of film-forming assistant, 0.5-1 part of propylene glycol, 0.8-0.9 part of rheological assistant, 0.2-0.3 part of antiseptic bactericide and 0.1-0.2 part of pH regulator;
continuous phase
25-40 parts of deionized water, 55-70 parts of organic silicon emulsion, 0.2-0.4 part of defoaming agent, 2-3 parts of film-forming assistant, 0.5-1 part of propylene glycol, 0.6-0.8 part of rheological assistant and 0.1-0.2 part of anticorrosive bactericide.
The water-based epoxy penetrating primer comprises the following components in parts by weight: 70-90 parts of water-based epoxy emulsion, 0.05-0.1 part of defoaming agent, 0.1-0.2 part of wetting agent and 10-20 parts of deionized water; the component B comprises: a water-based epoxy curing agent. The weight portion ratio of the component A to the component B is 1: (1.5-2).
The water-based organosilicon primer surfacer comprises, by weight, 10-20 parts of deionized water, 0.5-0.7 part of a dispersing agent, 0.2-0.3 part of a wetting agent, 0.2-0.4 part of a defoaming agent, 0.1-0.5 part of a pH regulator, 40-50 parts of an organosilicon emulsion, 0.5-1 part of propylene glycol, 1-3 parts of a film-forming assistant, 30-40 parts of an inorganic pigment and filler, 0.8-1 part of a rheological assistant and 0.1-0.2 part of an anticorrosive bactericide.
In one embodiment, the aqueous finishing varnish is aqueous polyurethane, which comprises the following components in parts by weight:
the component A comprises: 60-80 parts of hydroxyl acrylic acid dispersoid, 0.1-0.2 part of wetting agent, 0.2-0.3 part of rheological additive, 0.1-0.2 part of defoaming agent, 0.2-0.4 part of flatting agent and 20-40 parts of deionized water;
the component B comprises: hydrophilic modified HDI curing agent; the weight part ratio of the component A to the component B is (3-5): 1.
in another embodiment, the water-based finishing varnish is water-based fluorocarbon, and comprises the following components in parts by weight:
the component A comprises: 60-80 parts of water-based fluorocarbon emulsion, 0.2-0.3 part of wetting agent, 0.2-0.3 part of rheological additive, 0.1-0.2 part of defoaming agent, 0.2-0.4 part of flatting agent and 20-40 parts of deionized water; the component B comprises: hydrophilic modified HDI curing agent; the weight part ratio of the component A to the component B is (8-10): 1.
preferably, the water-based finishing varnish also comprises 0.5-1 part by weight of effect pigment. So that the coated surface forms a dazzling metallic glittering effect.
Preferably, the water-based finishing varnish further comprises a pattern raising agent in an amount of 2-3 parts by weight. To produce a high end sanding effect on the coated surface.
Preferably, the inorganic pigment and filler is one or more of rutile titanium dioxide, ground calcium carbonate and calcined kaolin; the rheological additive is one or more of hydroxyethyl cellulose ether, polyurethane and alkali swelling thickener.
The invention also discloses a water-based stone-like floor which comprises a water-based epoxy permeable primer layer, a water-based organic silicon middle paint layer, a water-based stone-like finish paint layer and a water-based finish varnish layer which are prepared by the coating formula from bottom to top.
The coating amount of the water-based epoxy penetrating primer layer is (0.04-0.05) kg/m2, the coating amount of the water-based silicone primer surfacer is (0.15-0.20) kg/m2, the coating amount of the water-based stone-like finish paint layer is (0.8-2) kg/m2, and the coating amount of the water-based finish varnish layer is (0.04-0.06) kg/m 2.
The invention has the beneficial effects that: the coating disclosed by the invention can generate a high stone-like effect when being used for coating the terrace, and is low in manufacturing cost, short in construction period, seamless, easy to clean, free of VOC (volatile organic compound) emission pollution, safe and environment-friendly.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is further described in detail with reference to the following embodiments.
The invention discloses a water-based stone-like coating formula, which comprises four coating formulas of water-based epoxy penetrating primer, water-based organic silicon middle coating, water-based stone-like finish paint and water-based finish varnish. The formulations of the individual layers of paint were prepared from the raw material components in tables 1 to 5 below.
TABLE 1 ingredient Table of water-based epoxy penetrant primer
TABLE 2 ingredient Table of water-based silicone mid-coat paint
TABLE 3-1 ingredient Table of dispersed phase raw materials for aqueous stone-like top-coat
TABLE 3-2 ingredient table of continuous phase raw material of water-based stone-like finish
TABLE 3-3 ingredient table of aqueous stone-like finish protective adhesive solution
Preparing a dispersion phase, a continuous phase and a protective adhesive solution of the water-based stone-like finishing paint according to the following table 3-1, the table 3-2 and the table 3-3 respectively, and then preparing a water-based stone-like finishing paint according to the following table 2: 2: 1 to obtain the water-based stone-like finish paint.
TABLE 4 ingredient Table of aqueous finishing varnish (aqueous polyurethane System)
TABLE 5 ingredient table of water-based finish varnish (water-based fluorocarbon system)
The following detailed description is given of the preparation process of the raw material components of example one and example two:
example one
The embodiment discloses a water-based stone-like paint formula, which comprises a water-based epoxy penetrating primer, a water-based organic silicon middle coating, a water-based stone-like finish paint and a water-based finish varnish, and a four-layer paint formula, and is prepared by the following steps:
1. preparing water-based epoxy penetrating primer
And the component A is prepared by adding 90 parts of water-based epoxy emulsion into a stirring container, adding 0.1 part of NXZ defoaming agent and 0.2 part of Tego270 wetting agent under medium and low speed stirring, stirring for 5 minutes, adding 10 parts of deionized water, and uniformly stirring at medium and low speed.
The component B comprises: 200 parts of high-performance water-based epoxy curing agent. And (3) preparing the component A and the component B into paint to obtain the water-based epoxy penetrating primer.
2. Preparing water-based organic silicon modified primer surfacer
Adding 11 parts of deionized water into a stirring container, and sequentially adding 0.1 part of hydroxyethyl cellulose ether (rheological additive), 0.6 part of SN-5040 dispersing agent, 0.2 part of EF-106 wetting agent, 0.2 part of NXZ defoaming agent and 0.1 part of AMP-95 regulator (PH regulator) under the condition of medium-low speed stirring; properly regulating the rotating speed, sequentially adding 30 parts of R706 rutile type titanium dioxide, ground limestone and calcined kaolin (inorganic pigment and filler), and dispersing at a high speed until the fineness is qualified; adding 1 part of deionized water to reduce the temperature of the slurry, reducing the rotating speed, and sequentially adding 50 parts of organic silicon emulsion, 2.5 parts of C-12 film-forming additive, 1 part of propylene glycol, 0.2 part of NXZ defoaming agent, 0.4 part of polyurethane thickener (rheological additive), 0.4 part of alkali swelling thickener (rheological additive) and 0.2 part of antiseptic bactericide, and uniformly stirring at medium and low speed.
3. Preparing water-based stone-like finish paint
a dispersed phase
Adding 49.8 parts of deionized water into a stirring container, and sequentially adding 0.9 part of hydroxyethyl cellulose ether (rheological additive), 0.3 part of SN-5040 dispersing agent, 0.1 part of EF-106 wetting agent, 0.2 part of NXZ defoaming agent and 0.2 part of AMP-95 regulator (PH regulator) under the condition of medium-low speed stirring; properly increasing the rotating speed, sequentially adding 20 parts of R706 rutile type titanium dioxide and 4000-mesh calcined kaolin, and dispersing at a high speed until the fineness is qualified; adding 0.2 part of deionized water to reduce the temperature of the slurry, reducing the rotating speed, sequentially adding 28 parts of organic silicon emulsion, 1.1 parts of C-12 film-forming assistant, 0.5 part of propylene glycol, 0.2 part of NXZ defoaming agent, 0.2 part of RS preservative and 0.1 part of EPW mildew preventive, and uniformly stirring at medium speed.
And b, adding 25 parts of deionized water into the continuous phase in a stirring container, sequentially adding 0.2 part of NXZ defoaming agent, 3 parts of C-12 film-forming aid, 1 part of propylene glycol, 0.2 part of RS preservative, 70 parts of silicone-acrylate emulsion and 0.6 part of TT-935 alkali swelling thickener (rheological aid) under the condition of medium-low speed stirring, and properly increasing the rotating speed to stir uniformly.
And c, adding 47 parts of deionized water into the protective glue solution in a stirring container, adding 3 parts of S482 glue powder under the medium-low speed stirring state, and dispersing at a high speed for 30-40min to obtain a transparent clear glue solution.
d, adding 20 parts of protective glue solution into a granulation container of a granulator for the water-based stone-like finish paint, then adding 40 parts of dispersed phase which is adjusted to a certain color, setting the rotating speed and time according to the size of color grains presented by the color, and starting the granulator for granulation; and after the dispersed phases of all colors are granulated in sequence, pouring all the colored particles into a larger container, finally adding 40 parts of the continuous phase, and slowly and uniformly mixing.
4. Compounding water-thinned finishing varnish
20 parts of deionized water is added into the component A in a stirring container, 0.2 part of EF-106 wetting agent, 0.1 part of BYK028 defoaming agent, 80 parts of hydroxyl acrylic acid dispersoid, 0.3 part of BYK333 flatting agent and 0.3 part of polyurethane thickener (rheological additive) are sequentially added under the condition of medium-low speed stirring, and the component A is uniformly stirred to obtain the component A of the waterborne polyurethane cover surface.
And the component B is a hydrophilic modified HDI curing agent.
According to the component A: and the component B is 5: 1 preparing paint to obtain the water-based finishing varnish.
Example two
The embodiment discloses a formula of a water-based stone-like coating, which is prepared by adopting the mixture ratio of the second embodiment in the table 1-3 according to the steps of the first embodiment to prepare a water-based epoxy penetrating primer, an organic silicon modified middle coating and a water-based stone-like finish. The water-based finishing varnish in the embodiment adopts water-based fluorocarbon system raw materials, and the preparation process is as follows:
20 parts of deionized water is added into the component A in a stirring container, 0.3 part of EF-106 wetting agent, 0.1 part of BYK028 defoaming agent, 80 parts of aqueous fluorocarbon emulsion, 0.4 part of BYK333 leveling agent and 0.2 part of polyurethane thickener (rheological additive) are sequentially added under the condition of medium-low speed stirring, and the component A of the aqueous polyurethane cover surface is prepared after uniform stirring.
And the component B is a hydrophilic modified HDI curing agent.
According to the component A: the component B is 10: 1, preparing paint, adding 0.5 part of effect pigment and 2 parts of pattern erecting agent to obtain the water-based finishing varnish.
According to the formula of the first embodiment and the second embodiment, the invention also discloses the water-based stone-like terrace. The water-based stone-like terrace comprises a water-based epoxy permeable primer layer, a water-based organic silicon middle paint layer, a water-based stone-like finish paint layer and a water-based finish varnish layer from bottom to top. Wherein the water-based epoxy penetration primer layer is formed by coating the water-based epoxy penetration primer in the above embodiment. The water-based silicone middle paint layer is formed by coating the water-based silicone middle paint. The water-based stone-like finish paint layer is formed by coating water-based stone-like finish paint. The water-based finishing varnish layer is formed by coating water-based finishing varnish.
The construction process of the water-based stone-like terrace comprises the following steps:
1) and (2) rolling one to two water-based epoxy penetrating primers on the concrete ground surface after finishing, leveling and dedusting, and drying at 25 ℃ for at least 24 hours with the dosage of 0.04-0.05 kg/square meter.
2) After the water-based epoxy penetrating primer is dried, roller coating a water-based organic silicon modified middle coating, and drying for 2-4h at 25 ℃; the dosage is 0.15-0.20 kg per square meter.
3) Drying the water-based organic silicon modified middle coat for 2-4h until the middle coat is not sticky to touch with fingers, and spraying water-based stone-like finish paint, wherein the dosage is 0.8-2 kg/square meter according to the required stone-like effect; drying at 25 deg.C for at least 48 h.
4) And (3) rolling one to two water-based finish varnish layers by using the amount of 0.04-0.06 kg per square meter. Drying and curing at 25 deg.C for 48h, and performing performance test or putting into use at 7 d.
The main performance indexes of the water-based stone-like terrace obtained by coating the water-based stone-like terrace coating material are tested according to the standard GB/T22374-2008 terrace coating material:
TABLE 6 Water-based stone-like terrace prime coat performance test table
TABLE 7 test table for water-based stone-like terrace surface coating performance
As can be seen from tables 6 and 7, the water-based stone-like floor base coat and the surface liquid meet the standard requirements and have excellent performance. And the terrace is imitative to be stone effectual, can also form as required and dazzle beautiful metal flash of light effect or high-end dull polish effect, and the cost is lower, suitable popularization and application.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any changes or substitutions that can be easily conceived by those skilled in the art within the technical scope of the present invention are included in the scope of the present invention.
Claims (9)
1. The water-based stone-like coating is characterized by comprising water-based epoxy penetrating primer, water-based organic silicon middle paint, water-based stone-like finish paint and water-based finishing varnish, wherein the water-based stone-like finish paint comprises the following components in percentage by weight: continuous phase: protective gel solution = 2: 2: 1, the dispersed phase, the continuous phase and the protective colloid solution are prepared from the following raw materials in parts by weight:
dispersed phase: 50-55 parts of deionized water, 0.3-0.4 part of defoaming agent, 0.1-0.2 part of wetting agent, 0.2-0.4 part of dispersing agent, 15-20 parts of inorganic pigment and filler, 23-28 parts of organosilicon emulsion, 0.9-1.1 part of film-forming assistant, 0.5-1 part of propylene glycol, 0.8-0.9 part of rheological assistant, 0.2-0.3 part of antiseptic bactericide and 0.1-0.2 part of pH regulator;
continuous phase: 25-40 parts of deionized water, 55-70 parts of organic silicon emulsion, 0.2-0.4 part of defoaming agent, 2-3 parts of film-forming assistant, 0.5-1 part of propylene glycol, 0.6-0.8 part of rheological assistant and 0.1-0.2 part of anticorrosive bactericide;
protective glue solution: 47 parts of deionized water and 3 parts of rubber powder; or 46.5 parts of deionized water and 3.5 parts of rubber powder; or 46 parts of deionized water and 4 parts of rubber powder;
the water-based epoxy penetrating primer comprises the following components in parts by weight: 70-90 parts of water-based epoxy emulsion, 0.05-0.1 part of defoaming agent, 0.1-0.2 part of wetting agent and 10-20 parts of deionized water; the component B comprises: the water-based epoxy curing agent comprises a component A and a component B, wherein the weight part ratio of the component A to the component B is 1: (1.5-2).
2. The aqueous stone-like coating according to claim 1, wherein: the water-based organosilicon primer surfacer comprises, by weight, 10-20 parts of deionized water, 0.5-0.7 part of a dispersing agent, 0.2-0.3 part of a wetting agent, 0.2-0.4 part of a defoaming agent, 0.1-0.5 part of a pH regulator, 40-50 parts of an organosilicon emulsion, 0.5-1 part of propylene glycol, 1-3 parts of a film-forming aid, 30-40 parts of an inorganic pigment and filler, 0.8-1 part of a rheological aid and 0.1-0.2 part of an anticorrosive bactericide.
3. The aqueous stone-like coating according to claim 1, wherein: the water-based finishing varnish is water-based polyurethane, and comprises the following components in parts by weight:
the component A comprises: 60-80 parts of hydroxyl acrylic acid dispersoid, 0.1-0.2 part of wetting agent, 0.2-0.3 part of rheological additive, 0.1-0.2 part of defoaming agent, 0.2-0.4 part of flatting agent and 20-40 parts of deionized water;
the component B comprises: hydrophilic modified HDI curing agent; the weight part ratio of the component A to the component B is (3-5): 1.
4. the aqueous stone-like coating according to claim 1, wherein: the water-based finishing varnish is water-based fluorocarbon and comprises the following components in parts by weight:
the component A comprises: 60-80 parts of water-based fluorocarbon emulsion, 0.2-0.3 part of wetting agent, 0.2-0.3 part of rheological additive, 0.1-0.2 part of defoaming agent, 0.2-0.4 part of flatting agent and 20-40 parts of deionized water; the component B comprises: hydrophilic modified HDI curing agent; the weight part ratio of the component A to the component B is (8-10): 1.
5. the aqueous stone-like coating according to claim 3 or 4, characterized in that: the water-based finishing varnish also comprises 0.5-1 part by weight of effect pigment.
6. The aqueous stone-like coating according to claim 3 or 4, characterized in that: the water-based finishing varnish also comprises 2-3 parts by weight of a standing grain agent.
7. The aqueous stone-like coating according to claim 1, wherein: the inorganic pigment and filler is one or more of rutile titanium dioxide, ground calcium carbonate and calcined kaolin; the rheological additive is one or more of hydroxyethyl cellulose ether, polyurethane and alkali swelling thickener.
8. The utility model provides a stone terrace is imitated to waterborne which characterized in that: the water-based epoxy permeable primer layer, the water-based organic silicon intermediate paint layer, the water-based stone-like finish paint layer and the water-based finish varnish layer which are prepared from the coating of any one of claims 1 to 7 are arranged from bottom to top.
9. The water-based stone-like terrace of claim 8, characterized in that: the coating amount of the water-based epoxy penetrating primer layer is (0.04-0.05) kg/m2The coating amount of the water-based silicone middle coating layer is (0.15-0.20) kg/m2The coating amount of the water-based stone-like finish paint layer is (0.8-2) kg/m2The coating amount of the water-based finish varnish layer is (0.04-0.06) kg/m2。