CN104830184A - Water-based imitated marble multi-color paint and preparation and construction method thereof - Google Patents
Water-based imitated marble multi-color paint and preparation and construction method thereof Download PDFInfo
- Publication number
- CN104830184A CN104830184A CN201510259204.1A CN201510259204A CN104830184A CN 104830184 A CN104830184 A CN 104830184A CN 201510259204 A CN201510259204 A CN 201510259204A CN 104830184 A CN104830184 A CN 104830184A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- marble
- waterborne
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to water-based imitated marble multi-color paint which comprises the following components in parts by weight: 200-300 parts of deionized water, 3.5-5.5 parts of hydroxyethyl cellulose, 3.5-5.5 parts of multifunctional additives, 0.5-2.0 parts of a wetting agent, 1.5-2.5 parts of an antifoaming agent, 8.5-10.5 parts of ethylene glycol, 17.5-20.5 parts of a coalescing agent, 2.5-5.5 parts of a polyurethane thickener, 350-450 parts of silicone acrylic emulsion, 2.5-4.5 parts of an alkali soluble thickener, 2.5-4.5 parts of a flatting agent, 2.0-3.0 parts of a suspending agent, 2.0-3.0 parts of a preservative and 200-300 parts of colored slices. The water-based imitated marble multi-color paint disclosed by the invention can be used for brush coating and spraying, has an innovative special technical formula, is resistant to washing, mildew and moss and has excellent fouling resistance, extremely high self-cleaning property, crack resistance and attractive daubing appearance.
Description
Technical field
The present invention relates to a kind of paint, especially a kind of waterborne marble-imitated multicolor paint, preparation method and constructional method thereof
Background technology
Grouan, marble are with its serious texture, and durable quality, various color is subject to the favor of owner.But grouan, marmorean shortcoming are also apparent, one is expensive price, two is that construction is complicated, three is combine difficulty with insulation, a lot of user is hung back, and four at secure context, and it is too high that cladding marble bears a heavy burden to overall building, although be adopt empty extension method, in antidetonation, still there is very large potential safety hazard.
Water-water and cladding marble more simple and fast, for 400 squares, water-water multicolor finish is constructed the 6 day time of two people's manipulation requires, and cladding marble then needs the longer time, and our company's product only can need complete less than two day time.
In product appearance, water-water multicolor finish is difficult in large-area construction, keep pattern consistent, and require very strict to operator, misoperation color relation can grow dim a little, deep mixed.More be hard to keep in repairing especially consistent.
Cladding marble the most easily produces aberration problem, and color is also difficult to be consistent.Because of marble deadweight reason, although a lot of protection has been done in construction, can produce permeable problem in 1 year or shorter time, what marble surface can be become is very dirty, causes overall flooring outward appearance very ugly.With we originally cladding marmorean tall and big on idea run in the opposite direction.
Summary of the invention
The problem to be solved in the present invention is to provide one.
For solving the problems of the technologies described above, waterborne marble-imitated multicolor paint of the present invention comprises the component of following weight part, deionized water 200-300 part, Natvosol 3.5-5.5 part, multifunctional assistant 3.5-5.5 part, wetting agent 0.5-2.0 part, defoamer 1.5-2.5 part, ethylene glycol 8.5-10.5 part, film coalescence aid 17.5-20.5 part, polyurethane thickener 2.5-5.5 part, organosilicon crylic acid latex 350-450 part, alkali swelling thickening material 2.5-4.5 part, flow agent 2.5-4.5 part, anti-sedimentation agent 2.0-3.0 part, sanitas 2.0-3.0 part, colored sliver 200-300 part.
Owing to adding the organosilicon crylic acid latex of optimum proportioning, Natvosol and film coalescence aid, this water-miscible paint more existing water-based parian paint in wear resistance has larger lifting; Due to the optimization of the proportioning of alkali swelling thickening material, flow agent, Natvosol and polyurethane thickener, its resistance to cracking is better; Due to the optimization of the proportioning of film coalescence aid, alkali swelling thickening material, anti-sedimentation agent, organosilicon crylic acid latex and colored sliver, the combination more secure rigid of colored sliver and water-miscible paint, the water tolerance of colored sliver is better, and outward appearance more combines together.The combination of these components and the aforementioned proportion scope of each component, determined by lot of experiments, aforesaid combination and proportional range make waterborne marble-imitated multicolor paint of the present invention have the excellent balance of resistance to cracking, weathering resistance, fidelity, wear resistance and self-cleaning.
Preferably, described flow agent is mixed with the ratio of 1:2 by organically-modified silica alkane flow agent, fluorine-carbon modified ammonium polyacrylate salt flow agent, described wetting agent is alkylphenol polyoxyethylene, described film coalescence aid is that the wrong acid esters of Lauryl Alcohol ester, dipropylene, butyl glycol ether and butyl glycol ether mixes with the ratio of 1:1:1:2, and described defoamer is polysiloxane-polyether copolymer.
Selection and the combination of these auxiliary agents are determined through lot of experiments, and the aforesaid combination of flow agent and the selection of component ratio have a distinct increment to the homogeneity of sliver after coating, also improve the tightness of sliver and water-miscible paint.Film coalescence aid selects aforesaid combination and ratio, improves the resistance to cracking of water-miscible paint.
As most preferred scheme, waterborne marble-imitated multicolor paint of the present invention comprises the component of following weight part, deionized water 250 parts, Natvosol 5.0 parts, multifunctional assistant 4.5 parts, wetting agent 1.5 parts, defoamer 2.0 parts, ethylene glycol 10.0 parts, film coalescence aid 20.0 parts, polyurethane thickener 3.5 parts, organosilicon crylic acid latex 400 parts, alkali swelling thickening material 3.0 parts, flow agent 3.0 parts, anti-sedimentation agent 2.5 parts, sanitas 2.5 parts, colored sliver 250 parts.
Improve as one, also comprise pH adjusting agent 0.1-1.0 part, described pH adjusting agent is 2-amino-2-methyl-1-propanol.
Manufacture the method for above-mentioned waterborne marble-imitated multicolor paint, comprise the following steps,
(1) take deionized water by weight, add Natvosol, 700-900 rev/min is stirred 30 minutes;
(2) take by weight and add multifunctional assistant, wetting agent, defoamer, ethylene glycol, film coalescence aid, 700-900 rev/min is stirred 15 minutes;
(3) take by weight and add polyurethane thickener, organosilicon crylic acid latex, alkali swelling thickening material, flow agent, anti-sedimentation agent, sanitas, 700-900 rev/min stirs;
(4) take by weight and add colored sliver, 400-600 rev/min is stirred 10 minutes.
Improve as one, in (3) step, after adding polyurethane thickener, organosilicon crylic acid latex, be heated to 50-55 degree Celsius, add alkali swelling thickening material, flow agent lentamente, keep 50-55 degree Celsius within 10 minutes, also constantly to stir, be then reduced to normal temperature, add anti-sedimentation agent, sanitas, and continue to stir.
Be incubated for some time at this temperature in the process, each component can be allowed better to merge, better play its performance.
Improve as one, in intensification, add alkali swelling thickening material, flow agent keeps temperature after being reduced to normal temperature, add pH adjusting agent, adjusted to ph to 8.5-9, then adds anti-sedimentation agent, sanitas, and continues stirring.
Add pH adjusting agent by the composition proceeding to above-mentioned steps, adjusted to ph to 8.5-9, then adds, anti-sedimentation agent and colored sliver, sliver and paint can be allowed to combine more firmly, the bonding surface of sliver and paint is not easy to produce bubble, thus makes sliver more wear-resisting.
The constructional method of above-mentioned waterborne marble-imitated multicolor paint, comprises the following steps,
(1) body of wall maintenance: the curing time in new cement wall surface winter is 28 days, and the curing time in summer is 14 days;
(2) processing base level: repair metope with external wall waterproof putty, first local is levelling, fills up large hole and gap with putty or gap-filling glue, after putty drying, detail sanding, then granted full putty makes basic unit smooth;
(3) brushing alkali-resistant sealing primer: base reservoir temperature higher than 15 DEG C and ambient moisture is less than 65% time, after putty complete drying, brushing or spraying an alkali-resistant sealing primer;
(4) blade coating or spraying waterborne marble-imitated multicolor paint: base reservoir temperature higher than 15 DEG C and ambient moisture is less than 65% time, blade coating or spraying waterborne marble-imitated multicolor paint twice after priming paint drying, second time construction interval time is that the drying of first pass paint is firmly smeared afterwards and is as the criterion, glue spread is: blade coating, 1.2 ㎡--1.5 ㎡/kg; Spraying, 1 ㎡--1.2 ㎡/kg, spray gun bore is 8mm--10mm, and pressure is 6mpa-6.5mpa, and muzzle and metope distance are about 50cm;
(5) polish: adopt 70 order sand paper after waterborne marble-imitated multicolor paint drying, tie the particle of spot colored stone paint rat gently;
(6) finishing paint: after lacquer painting has been polished, brushes special coating varnish;
(7) lattice: paste three roads U.S. line paper routing, the U.S. line paper of first posts centered by line, and the U.S. line paper of another twice posts in the U.S. line paper both sides of first respectively, is then torn by the U.S. line paper of centre; Stamp silicone adhesive at the U.S. line paper place that tears floating, after slightly to be dried, more U.S. for both sides line paper is torn.
Aforesaid method is the specific constructional method formulated for paint of the present invention, find through lot of experiments, when blade coating and this waterborne marble-imitated multicolor paint of spraying, temperature is higher than 15 degree, humidity is less than 65%, then the combination of waterborne marble-imitated multicolor paint and priming paint is more firm, be not easy to occur be full of cracks, weathering resistance is better.The setting of glue spread, spray gun also has impact to the effect of construction.
Waterborne marble-imitated multicolor paint of the present invention, both can brush and also can spray, the special technique formula of innovation, washable, the anti-mildew of energy, moss.Have excellent anti-stain characteristic, superpower self-cleaning, resistance to cracking, maintenance is smeared attractive in appearance; Acidproof, alkaline-resisting, chemically-resistant good behaviour, high anti-UV, Super-ageing resistance, anti-yellowing change and resistance to water-white; Just at last because extraneous factor causes lacquer painting breakage also can again fill spray or brush, still not impact effect, also there will not be aberration; Gu containing high, thicker film can be formed, increase external wall waterproof ability, and reduce finish paint consumption.
Waterborne marble-imitated multicolor paint of the present invention, the environmental protection of water-based formulation green, adopts low taste nontoxic, low VOC composition, environmental sound during construction.
In construction, produce quick construction simply, plane, curved surface, arc etc. easily realize.Relative to water-water and cladding marble more simple and fast, for 400 squares, water-water multicolor finish is constructed the 6 day time of two people's manipulation requires, and cladding marble then needs the longer time, and our company's product only can need complete less than two day time
In product appearance, decorative effect is solemnly solemn, and what fully represent lithotome enriches texture.It not only has on all four granite effect, and thoroughly solves the difficult problems such as common true mineral varnish easily pollutes, fidelity difference and grouan, marble construction is complicated, price is high, safety coefficient is low.
Embodiment
Embodiment 1
Manufacture the method for waterborne marble-imitated multicolor paint, comprise the following steps,
(1) take deionized water 200 parts by weight, add Natvosol 3.5 parts, 700 revs/min are stirred 30 minutes;
(2) take by weight and add multifunctional assistant 5.5 parts, wetting agent 0.5 part, defoamer 1.5 parts, ethylene glycol 8.5 parts, film coalescence aid 17.5 parts, 700 revs/min are stirred 15 minutes;
(3) take by weight and add polyurethane thickener 5.5 parts, organosilicon crylic acid latex 450 parts, alkali swelling thickening material 2.5 parts, flow agent 2.5 parts, anti-sedimentation agent 2.0 parts, sanitas 2.0 parts, 700 revs/min are stirred 30 minutes;
(4) take by weight and add colored sliver 200 parts, 600 revs/min are stirred 10 minutes.
Described flow agent is mixed with the ratio of 1:2 by organically-modified silica alkane flow agent, fluorine-carbon modified ammonium polyacrylate salt flow agent, described wetting agent is alkylphenol polyoxyethylene, described film coalescence aid is that the wrong acid esters of Lauryl Alcohol ester, dipropylene, butyl glycol ether and butyl glycol ether mixes with the ratio of 1:1:1:2, and described defoamer is polysiloxane-polyether copolymer.Described multifunctional assistant is multifunctional assistant AMP-95.
Embodiment 2
Manufacture the method for waterborne marble-imitated multicolor paint, comprise the following steps,
(1) take deionized water 300 parts by weight, add Natvosol 5.5 parts, 900 revs/min are stirred 30 minutes;
(2) take by weight and add multifunctional assistant 3.5 parts, wetting agent 2.0 parts, defoamer 2.5 parts, ethylene glycol 10.5 parts, film coalescence aid 20.5 parts, 900 revs/min are stirred 15 minutes;
(3) take by weight and add polyurethane thickener 2.5 parts, organosilicon crylic acid latex 350 parts, alkali swelling thickening material 4.5 parts, flow agent 4.5 parts, anti-sedimentation agent 3.0 parts, sanitas 3.0 parts, 700 revs/min are stirred 30 minutes;
(4) take by weight and add colored sliver 300 parts, 600 revs/min are stirred 10 minutes.
Described flow agent is mixed with the ratio of 1:2 by organically-modified silica alkane flow agent, fluorine-carbon modified ammonium polyacrylate salt flow agent, described wetting agent is alkylphenol polyoxyethylene, described film coalescence aid is that the wrong acid esters of Lauryl Alcohol ester, dipropylene, butyl glycol ether and butyl glycol ether mixes with the ratio of 1:1:1:2, and described defoamer is polysiloxane-polyether copolymer.Described multifunctional assistant is multifunctional assistant AMP-95.
Embodiment 3
Manufacture the method for waterborne marble-imitated multicolor paint, comprise the following steps,
(1) take deionized water 250 parts by weight, add Natvosol 5.0 parts, 900 revs/min are stirred 30 minutes;
(2) take by weight and add multifunctional assistant 4.5 parts, wetting agent 1.5 parts, defoamer 2.0 parts, ethylene glycol 10.0 parts, film coalescence aid 20.0 parts, 900 revs/min are stirred 15 minutes;
(3) take by weight and add polyurethane thickener 3.5 parts, organosilicon crylic acid latex 400 parts, alkali swelling thickening material 3.0 parts, flow agent 3.0 parts, anti-sedimentation agent 2.5 parts, sanitas 2.5 parts, 900 revs/min are stirred 30 minutes;
(4) take by weight and add colored sliver 250 parts, 600 revs/min are stirred 10 minutes.
Described flow agent is mixed with the ratio of 1:2 by organically-modified silica alkane flow agent, fluorine-carbon modified ammonium polyacrylate salt flow agent, described wetting agent is alkylphenol polyoxyethylene, described film coalescence aid is that the wrong acid esters of Lauryl Alcohol ester, dipropylene, butyl glycol ether and butyl glycol ether mixes with the ratio of 1:1:1:2, and described defoamer is polysiloxane-polyether copolymer.Described multifunctional assistant is multifunctional assistant AMP-95.
Embodiment 4
Manufacture the method for waterborne marble-imitated multicolor paint, comprise the following steps,
(1) take deionized water 250 parts by weight, add Natvosol 5.0 parts, 900 revs/min are stirred 30 minutes;
(2) take by weight and add multifunctional assistant 4.5 parts, wetting agent 1.5 parts, defoamer 2.0 parts, ethylene glycol 10.0 parts, film coalescence aid 20.0 parts, 900 revs/min are stirred 15 minutes;
(3) take by weight and add polyurethane thickener 3.5 parts, organosilicon crylic acid latex 400 parts, be heated to 50-55 degree Celsius, add alkali swelling thickening material 3.0 parts, flow agent 3.0 parts lentamente, keep 50-55 degree Celsius within 10 minutes, also constantly to stir, then normal temperature is reduced to, add anti-sedimentation agent 2.5 parts, sanitas 2.5 parts, 900 revs/min are stirred 20 minutes;
(4) take by weight and add colored sliver 300 parts, 400 revs/min are stirred 10 minutes.
Described flow agent is mixed with the ratio of 1:2 by organically-modified silica alkane flow agent, fluorine-carbon modified ammonium polyacrylate salt flow agent, described wetting agent is alkylphenol polyoxyethylene, described film coalescence aid is that the wrong acid esters of Lauryl Alcohol ester, dipropylene, butyl glycol ether and butyl glycol ether mixes with the ratio of 1:1:1:2, and described defoamer is polysiloxane-polyether copolymer.Described multifunctional assistant is multifunctional assistant AMP-95.
Embodiment 5
Manufacture the method for waterborne marble-imitated multicolor paint, comprise the following steps,
(1) take deionized water 250 parts by weight, add Natvosol 5.0 parts, 900 revs/min are stirred 30 minutes;
(2) take by weight and add multifunctional assistant 4.5 parts, wetting agent 1.5 parts, defoamer 2.0 parts, ethylene glycol 10.0 parts, film coalescence aid 20.0 parts, 900 revs/min are stirred 15 minutes;
(3) take by weight and add polyurethane thickener 3.5 parts, organosilicon crylic acid latex 400 parts, be heated to 50-55 degree Celsius, add alkali swelling thickening material 3.0 parts, flow agent 3.0 parts lentamente, keep 50-55 degree Celsius within 10 minutes, also constantly to stir, then normal temperature is reduced to, add pH adjusting agent, adjusted to ph, to 8.5-9, adds anti-sedimentation agent 2.5 parts, sanitas 2.5 parts, and 900 revs/min are stirred 20 minutes;
(4) take by weight and add colored sliver 300 parts, 500 revs/min are stirred 10 minutes.
Described flow agent is mixed with the ratio of 1:2 by organically-modified silica alkane flow agent, fluorine-carbon modified ammonium polyacrylate salt flow agent, described wetting agent is alkylphenol polyoxyethylene, described film coalescence aid is that the wrong acid esters of Lauryl Alcohol ester, dipropylene, butyl glycol ether and butyl glycol ether mixes with the ratio of 1:1:1:2, and described defoamer is polysiloxane-polyether copolymer.Described multifunctional assistant is multifunctional assistant AMP-95.
Comparative example 1
Manufacture the method for waterborne marble-imitated multicolor paint, comprise the following steps,
(1) take deionized water 200 parts by weight, add Natvosol 2.5 parts, 700 revs/min are stirred 30 minutes;
(2) take by weight and add multifunctional assistant 6.5 parts, wetting agent 2.5 parts, defoamer 1.0 parts, ethylene glycol 7.5 parts, film coalescence aid 15.5 parts, 700 revs/min are stirred 15 minutes;
(3) take by weight and add polyurethane thickener 1.5 parts, organosilicon crylic acid latex 550 parts, alkali swelling thickening material 2.0 parts, flow agent 5.5 parts, anti-sedimentation agent 1.5 parts, sanitas 1.5 parts, 700 revs/min are stirred 30 minutes;
(4) take by weight and add colored sliver 200 parts, 600 revs/min are stirred 10 minutes.
Flow agent uses organically-modified silica alkane flow agent, and wetting agent is alkylphenol polyoxyethylene, and film coalescence aid is dipropylene, and defoamer is polysiloxane-polyether copolymer.Multifunctional assistant is multifunctional assistant AMP-95.
Comparative example 2
Manufacture the method for waterborne marble-imitated multicolor paint, comprise the following steps,
(1) take deionized water 220 parts by weight, add Natvosol 4.0 parts, 900 revs/min are stirred 30 minutes;
(2) take by weight and add multifunctional assistant 3.5 parts, wetting agent 1.5 parts, defoamer 2.5 parts, ethylene glycol 9.0 parts, film coalescence aid 18.0 parts, 900 revs/min are stirred 15 minutes;
(3) take by weight and add polyurethane thickener 2.5 parts, organosilicon crylic acid latex 400 parts, alkali swelling thickening material 3.5 parts, flow agent 3.5 parts, anti-sedimentation agent 2.5 parts, sanitas 2.5 parts, 900 revs/min are stirred 30 minutes;
(4) take by weight and add colored sliver 200 parts, 600 revs/min are stirred 10 minutes.
Flow agent uses organically-modified silica alkane flow agent, and wetting agent is alkylphenol polyoxyethylene, and film coalescence aid is dipropylene, and defoamer is polysiloxane-polyether copolymer.Multifunctional assistant is multifunctional assistant AMP-95.
Waterborne marble-imitated multicolor paint of the present invention, both can brush and also can spray, the special technique formula of innovation, washable, the anti-mildew of energy, moss.Have excellent anti-stain characteristic, superpower self-cleaning, resistance to cracking, maintenance is smeared attractive in appearance; Acidproof, alkaline-resisting, chemically-resistant good behaviour, high anti-UV, Super-ageing resistance, anti-yellowing change and resistance to water-white; Just at last because extraneous factor causes lacquer painting breakage also can again fill spray or brush, still not impact effect, also there will not be aberration; Gu containing high, thicker film can be formed, increase external wall waterproof ability, and reduce finish paint consumption.
Specific experiment data are as follows:
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Comparative example 1 | Comparative example 2 | |
| Outward appearance | Fidelity is high | Fidelity is high | Fidelity is high | Fidelity is high | Fidelity is high | Fidelity is lower | Fidelity is higher |
| Water tolerance (hour) | 110 | 110 | 115 | 120 | 135 | 100 | 110 |
| Alkali resistance (hour) | 90 | 95 | 95 | 115 | 115 | 60 | 75 |
| Abrasion resistance/time | 12000 | 13000 | 13500 | 14500 | 15000 | 9500 | 10000 |
The testing method of water tolerance in table: coating priming paint, aqueousance artificial granite coating host, coating varnish by aqueousance artificial granite coatings system system without on fibrous magnesium silicate cement board (150mm × 70mm × 3 ~ 6mm).At standard state maintenance 7d after having applied, then test by first law regulation in GB/T1733-1993.
The testing method of alkali resistance in table: coating priming paint, aqueousance artificial granite coating host, coating varnish by aqueousance artificial granite complex layer coating matching system without on fibrous magnesium silicate cement board (150mm × 70mm × 3 ~ 6mm).At standard state maintenance 7d after having applied, then test by GB/T9265-2009 national standard.
The testing method of abrasion resistance in table: coating priming paint, aqueousance artificial granite coating host, coating varnish by aqueousance artificial granite complex layer coating matching system without on fibrous magnesium silicate cement board (430mm × 70mm × 3 ~ 6mm).At standard state maintenance 7d after having applied, then test by GB/T9266-2009 national standard.
The constructional method of waterborne marble-imitated multicolor paint, comprises the following steps,
(1) body of wall maintenance: the curing time in new cement wall surface winter is 28 days, and the curing time in summer is 14 days;
(2) processing base level: repair metope with external wall waterproof putty, first local is levelling, fills up large hole and gap with putty or gap-filling glue, after putty drying, detail sanding, then granted full putty makes basic unit smooth;
(3) brushing alkali-resistant sealing primer: base reservoir temperature higher than 15 DEG C and ambient moisture is less than 65% time, after putty complete drying, brushing or spraying an alkali-resistant sealing primer;
(4) blade coating or spraying waterborne marble-imitated multicolor paint: base reservoir temperature higher than 15 DEG C and ambient moisture is less than 65% time, blade coating or spraying waterborne marble-imitated multicolor paint twice after priming paint drying, second time construction interval time is that the drying of first pass paint is firmly smeared afterwards and is as the criterion, glue spread is: blade coating, 1.2 ㎡--1.5 ㎡/kg; Spraying, 1 ㎡--1.2 ㎡/kg, spray gun bore is 8mm--10mm, and pressure is 6mpa-6.5mpa, and muzzle and metope distance are about 50cm;
(5) polish: adopt 70 order sand paper after waterborne marble-imitated multicolor paint drying, tie the particle of spot colored stone paint rat gently;
(6) finishing paint: after lacquer painting has been polished, brushes special coating varnish;
(7) lattice: paste three roads U.S. line paper routing, the U.S. line paper of first posts centered by line, and the U.S. line paper of another twice posts in the U.S. line paper both sides of first respectively, is then torn by the U.S. line paper of centre; Stamp silicone adhesive at the U.S. line paper place that tears floating, after slightly to be dried, more U.S. for both sides line paper is torn.
Aforesaid method is the specific constructional method formulated for paint of the present invention, find through lot of experiments, when blade coating and this waterborne marble-imitated multicolor paint of spraying, temperature is higher than 15 degree, humidity is less than 65%, then the combination of waterborne marble-imitated multicolor paint and priming paint is more firm, be not easy to occur be full of cracks, weathering resistance is better.The setting of glue spread, spray gun also has impact to the effect of construction.
Claims (8)
1. a waterborne marble-imitated multicolor paint, it is characterized in that: the component comprising following weight part, deionized water 200-300 part, Natvosol 3.5-5.5 part, multifunctional assistant 3.5-5.5 part, wetting agent 0.5-2.0 part, defoamer 1.5-2.5 part, ethylene glycol 8.5-10.5 part, film coalescence aid 17.5-20.5 part, polyurethane thickener 2.5-5.5 part, organosilicon crylic acid latex 350-450 part, alkali swelling thickening material 2.5-4.5 part, flow agent 2.5-4.5 part, anti-sedimentation agent 2.0-3.0 part, sanitas 2.0-3.0 part, colored sliver 200-300 part.
2. according to waterborne marble-imitated multicolor paint according to claim 1, it is characterized in that: described flow agent is mixed with the ratio of 1:2 by organically-modified silica alkane flow agent, fluorine-carbon modified ammonium polyacrylate salt flow agent, described wetting agent is alkylphenol polyoxyethylene, described film coalescence aid is that the wrong acid esters of Lauryl Alcohol ester, dipropylene, butyl glycol ether and butyl glycol ether mixes with the ratio of 1:1:1:2, and described defoamer is polysiloxane-polyether copolymer.
3. according to the waterborne marble-imitated multicolor paint described in claim 1 or 2, it is characterized in that: the component comprising following weight part, deionized water 250 parts, Natvosol 5.0 parts, multifunctional assistant 4.5 parts, wetting agent 1.5 parts, defoamer 2.0 parts, ethylene glycol 10.0 parts, film coalescence aid 20.0 parts, polyurethane thickener 3.5 parts, organosilicon crylic acid latex 400 parts, alkali swelling thickening material 3.0 parts, flow agent 3.0 parts, anti-sedimentation agent 2.5 parts, sanitas 2.5 parts, colored sliver 250 parts.
4. according to waterborne marble-imitated multicolor paint according to claim 3, it is characterized in that: also comprise pH adjusting agent 0.1-1.0 part, described pH adjusting agent is 2-amino-2-methyl-1-propanol.
5. a method for the waterborne marble-imitated multicolor paint described in manufacturing claims 1-4, is characterized in that: comprise the following steps,
(1) take deionized water by weight, add Natvosol, 700-900 rev/min is stirred 30 minutes;
(2) take by weight and add multifunctional assistant, wetting agent, defoamer, ethylene glycol, film coalescence aid, 700-900 rev/min is stirred 15 minutes;
(3) take by weight and add polyurethane thickener, organosilicon crylic acid latex, alkali swelling thickening material, flow agent, anti-sedimentation agent, sanitas, 700-900 rev/min stirs;
(4) take by weight and add colored sliver, 400-600 rev/min is stirred 10 minutes.
6. according to the method for manufacture waterborne marble-imitated multicolor paint according to claim 5, it is characterized in that: in (3) step, after adding polyurethane thickener, organosilicon crylic acid latex, be heated to 50-55 degree Celsius, add alkali swelling thickening material, flow agent lentamente, keep 50-55 degree Celsius within 10 minutes, also constantly to stir, be then reduced to normal temperature, add anti-sedimentation agent, sanitas, and continue to stir.
7. according to the method for manufacture waterborne marble-imitated multicolor paint according to claim 6, it is characterized in that: in intensification, add alkali swelling thickening material, flow agent keeps temperature after being reduced to normal temperature, add pH adjusting agent, adjusted to ph is to 8.5-9, add anti-sedimentation agent, sanitas again, and continue to stir.
8. a constructional method for the waterborne marble-imitated multicolor paint described in claim 1-7, is characterized in that: comprise the following steps,
(1) body of wall maintenance: the curing time in new cement wall surface winter is 28 days, and the curing time in summer is 14 days;
(2) processing base level: repair metope with external wall waterproof putty, first local is levelling, fills up large hole and gap with putty or gap-filling glue, after putty drying, detail sanding, then granted full putty makes basic unit smooth;
(3) brushing alkali-resistant sealing primer: base reservoir temperature higher than 15 DEG C and ambient moisture is less than 65% time, after putty complete drying, brushing or spraying an alkali-resistant sealing primer;
(4) blade coating or spraying waterborne marble-imitated multicolor paint: base reservoir temperature higher than 15 DEG C and ambient moisture is less than 65% time, blade coating or spraying waterborne marble-imitated multicolor paint twice after priming paint drying, second time construction interval time is that the drying of first pass paint is firmly smeared afterwards and is as the criterion, glue spread is: blade coating, 1.2 ㎡--1.5 ㎡/kg; Spraying, 1 ㎡--1.2 ㎡/kg, spray gun bore is 8mm--10mm, and pressure is 6mpa-6.5mpa, and muzzle and metope distance are about 50cm;
(5) polish: adopt 70 order sand paper after waterborne marble-imitated multicolor paint drying, tie the particle of spot colored stone paint rat gently;
(6) finishing paint: after lacquer painting has been polished, brushes special coating varnish;
(7) lattice: paste three roads U.S. line paper routing, the U.S. line paper of first posts centered by line, and the U.S. line paper of another twice posts in the U.S. line paper both sides of first respectively, is then torn by the U.S. line paper of centre; Stamp silicone adhesive at the U.S. line paper place that tears floating, after slightly to be dried, more U.S. for both sides line paper is torn.