CN108929069A - A kind of self-cleaning lacquer and preparation method thereof - Google Patents
A kind of self-cleaning lacquer and preparation method thereof Download PDFInfo
- Publication number
- CN108929069A CN108929069A CN201810951927.1A CN201810951927A CN108929069A CN 108929069 A CN108929069 A CN 108929069A CN 201810951927 A CN201810951927 A CN 201810951927A CN 108929069 A CN108929069 A CN 108929069A
- Authority
- CN
- China
- Prior art keywords
- self
- added
- thickener
- solution
- hydroxyethyl cellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of self-cleaning lacquers, its raw material is as follows by weight: deionized water 5%-7%, hydroxyethyl cellulose solution 5%, anti-settling solution 2%-3%, silicone acrylic emulsion 15%-20%, plasticizer 8 ‰ -1%, defoaming agent 0.5 ‰ -1 ‰, sterilization antiseptic 1 ‰ -2 ‰, drying retardant 5 ‰, hydrophober 1%-3%, PH regulator 2 ‰, natural colour sand 70%, surplus are thickener.The present invention is widely applicable, there is excellent adhesive force to various basal planes, weatherability is strong, is amenable to extreme climatic environment, and quality is secure, durability is good, crack resistence effect is good, band self-cleaning property, different from existing lacquer, it meets water energy and generates lotus leaf effect, the water-white phenomenon generated by water resistance can be effectively prevent.
Description
Technical field
The present invention relates to lacquer technical fields more particularly to a kind of self-cleaning lacquer and preparation method thereof.
Background technique
Lacquer is the coating that a kind of decorative effect exactly likes marble, granite.The main natural stone for using various colors
Powder is formulated, applied to the imitation stone effect of external wall, therefore also known as liquid stone.
Building after lacquer finishing has natural true natural colour, gives graceful, harmonious, serious beauty
Sense, is suitable for the indoor and outdoor decoration of all kinds of buildings.Especially decorated on curved-surface building object, it is vivid, there is a kind of recurrence
Natural effect.Lacquer has fire prevention, waterproof, acid and alkali-resistance, anti-pollution.It is nontoxic, tasteless, bonding force is strong, will never fade equal spies
Point, can effectively stop extraneous adverse circumstances to building corrode, extend the service life of building, due to lacquer have it is good
Adhesive force and freeze-thaw resistance property, therefore be suitble to use in cold district.In use we have found that lacquer does not have certainly
Clean ability, rainwater, which can penetrate into time length in lacquer, can leave watermark, affect to appearance.
Summary of the invention
The purpose of the present invention is to solve disadvantage existing in the prior art, and a kind of self-cleaning lacquer that proposes and its
Preparation method.
To achieve the goals above, present invention employs following technical solutions:
A kind of self-cleaning lacquer, raw material are as follows by weight: deionized water 5%-7%, hydroxyethyl cellulose solution 5%, anti-settling
Solution 2%-3%, silicone acrylic emulsion 15%-20%, plasticizer 8 ‰ -1%, defoaming agent 0.5 ‰ -1 ‰, sterilization antiseptic 1 ‰ -2 ‰, slow curing
Agent 5 ‰, hydrophober 1%-3%, PH regulator 2 ‰, natural colour sand 70%, surplus is thickener.
Preferably, the hydroxyethyl cellulose model ER-30M, and hydroxyethyl cellulose solution concentration is 2%.
Preferably, the anti-settling solution concentration is 5%.
Preferably, the thickener is ASE-60 thickener.
Preferably, the defoaming agent model is the defoaming agent of NXZ.
Preferably, the hydrophober can also be wax emulsion.
Preferably, the PH regulator is the PH regulator that model is AMP-95.
The present invention also provides a kind of preparation methods of self-cleaning lacquer, include the following steps:
S1: stock carries out weighing and proportioning according to the ratio of raw material, places after weighing and proportioning spare；
S2: deionized water is added in blender, and sterilization antiseptic is then added to blender and is mixed；
Hydroxyethyl cellulose solution: being added to the solution being mixed in S2 by S3, and after being stirred dissolution, PH regulator is added
After continue stirring after it is spare；
S4: anti-settling solution, silicone acrylic emulsion, plasticizer sterilizing, defoaming agent, drying retardant and hydrophober are added to spare in S3
Solution is mixed evenly；
S5: thickener is continuously added, and is carried out continuing to stir after thickener is added, is stirring evenly and then adding into natural colour sand, is stirred
The preparation process of lacquer can be completed after the completion of uniformly.
Compared with prior art, the beneficial effects of the present invention are: the present invention is widely applicable, have to various basal planes excellent
Adhesive force, weatherability is strong, is amenable to extreme climatic environment, and quality is secure, and durability is good, and crack resistence effect is good, with self-cleaning
Performance, it is different from existing lacquer, it meets water energy and generates lotus leaf effect, can effectively prevent generating because of water resistance water-white existing
As.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Embodiment 1
A kind of self-cleaning lacquer, raw material are as follows by weight: deionized water 5%, hydroxyethyl cellulose solution 5%, anti-settling is molten
Liquid 2%, silicone acrylic emulsion 15%, plasticizer 8 ‰, defoaming agent 0.5 ‰, sterilization antiseptic 1 ‰, drying retardant 5 ‰, hydrophober 1%, PH tune
Save agent 2 ‰, natural colour sand 70%, thickener 3.5 ‰.
Specifically, the hydroxyethyl cellulose model ER-30M, and hydroxyethyl cellulose solution concentration is 2%.
Specifically, the anti-settling solution concentration is 5%.
Specifically, the thickener is ASE-60 thickener.
Specifically, the defoaming agent model is the defoaming agent of NXZ.
Specifically, the PH regulator is the PH regulator that model is AMP-95.
The present invention also provides a kind of preparation methods of self-cleaning lacquer, include the following steps:
S1: stock carries out weighing and proportioning according to the ratio of raw material, places after weighing and proportioning spare；
S2: deionized water is added in blender, and sterilization antiseptic is then added to blender and is mixed；
Hydroxyethyl cellulose solution: being added to the solution being mixed in S2 by S3, and after being stirred dissolution, PH regulator is added
After continue stirring after it is spare；
S4: anti-settling solution, silicone acrylic emulsion, plasticizer sterilizing, defoaming agent, drying retardant and hydrophober are added to spare in S3
Solution is mixed evenly；
S5: thickener is continuously added, and is carried out continuing to stir after thickener is added, is stirring evenly and then adding into natural colour sand, is stirred
The preparation process of lacquer can be completed after the completion of uniformly.
Embodiment 2
A kind of self-cleaning lacquer, raw material are as follows by weight: deionized water 5%, hydroxyethyl cellulose solution 5%, anti-settling is molten
Liquid 2%, silicone acrylic emulsion 15%, plasticizer 1%, defoaming agent 0.6 ‰, sterilization antiseptic 2 ‰, drying retardant 5 ‰, hydrophober 1%, PH are adjusted
Agent 2 ‰, natural colour sand 70%, thickener 0.4 ‰.
Specifically, the hydroxyethyl cellulose model ER-30M, and hydroxyethyl cellulose solution concentration is 2%.
Specifically, the anti-settling solution concentration is 5%.
Specifically, the thickener is ASE-60 thickener.
Specifically, the defoaming agent model is the defoaming agent of NXZ.
Specifically, the PH regulator is the PH regulator that model is AMP-95.
The present invention also provides a kind of preparation methods of self-cleaning lacquer, include the following steps:
S1: stock carries out weighing and proportioning according to the ratio of raw material, places after weighing and proportioning spare；
S2: deionized water is added in blender, and sterilization antiseptic is then added to blender and is mixed；
Hydroxyethyl cellulose solution: being added to the solution being mixed in S2 by S3, and after being stirred dissolution, PH regulator is added
After continue stirring after it is spare；
S4: anti-settling solution, silicone acrylic emulsion, plasticizer sterilizing, defoaming agent, drying retardant and hydrophober are added to spare in S3
Solution is mixed evenly；
S5: thickener is continuously added, and is carried out continuing to stir after thickener is added, is stirring evenly and then adding into natural colour sand, is stirred
The preparation process of lacquer can be completed after the completion of uniformly.
Embodiment 3
A kind of self-cleaning lacquer, raw material are as follows by weight: deionized water 5%, hydroxyethyl cellulose solution 5%, anti-settling is molten
Liquid 2%, silicone acrylic emulsion 15%, plasticizer 8 ‰, defoaming agent 1 ‰, sterilization antiseptic 1.5 ‰, drying retardant 5 ‰, hydrophober 1%, PH tune
Save agent 2 ‰, natural colour sand 70%, thickener 2.5 ‰.
Specifically, the hydroxyethyl cellulose model ER-30M, and hydroxyethyl cellulose solution concentration is 2%.
Specifically, the anti-settling solution concentration is 5%.
Specifically, the thickener is ASE-60 thickener.
Specifically, the defoaming agent model is the defoaming agent of NXZ.
Specifically, the PH regulator is the PH regulator that model is AMP-95.
The present invention also provides a kind of preparation methods of self-cleaning lacquer, include the following steps:
S1: stock carries out weighing and proportioning according to the ratio of raw material, places after weighing and proportioning spare；
S2: deionized water is added in blender, and sterilization antiseptic is then added to blender and is mixed；
Hydroxyethyl cellulose solution: being added to the solution being mixed in S2 by S3, and after being stirred dissolution, PH regulator is added
After continue stirring after it is spare；
S4: anti-settling solution, silicone acrylic emulsion, plasticizer sterilizing, defoaming agent, drying retardant and hydrophober are added to spare in S3
Solution is mixed evenly；
S5: thickener is continuously added, and is carried out continuing to stir after thickener is added, is stirring evenly and then adding into natural colour sand, is stirred
The preparation process of lacquer can be completed after the completion of uniformly.
Embodiment 4
A kind of self-cleaning lacquer, raw material are as follows by weight: deionized water 5%, hydroxyethyl cellulose solution 5%, anti-settling is molten
Liquid 2%, silicone acrylic emulsion 15%, plasticizer 8 ‰, defoaming agent 0.5 ‰, sterilization antiseptic 1 ‰, drying retardant 5 ‰, wax emulsion 1%, PH tune
Save agent 2 ‰, natural colour sand 70%, thickener 3.5 ‰.
Specifically, the hydroxyethyl cellulose model ER-30M, and hydroxyethyl cellulose solution concentration is 2%.
Specifically, the anti-settling solution concentration is 5%.
Specifically, the thickener is ASE-60 thickener.
Specifically, the defoaming agent model is the defoaming agent of NXZ.
Specifically, the PH regulator is the PH regulator that model is AMP-95.
The present invention also provides a kind of preparation methods of self-cleaning lacquer, include the following steps:
S1: stock carries out weighing and proportioning according to the ratio of raw material, places after weighing and proportioning spare；
S2: deionized water is added in blender, and sterilization antiseptic is then added to blender and is mixed；
Hydroxyethyl cellulose solution: being added to the solution being mixed in S2 by S3, and after being stirred dissolution, PH regulator is added
After continue stirring after it is spare；
S4: anti-settling solution, silicone acrylic emulsion, plasticizer sterilizing, defoaming agent, drying retardant and wax emulsion are added to spare in S3
Solution is mixed evenly；
S5: thickener is continuously added, and is carried out continuing to stir after thickener is added, is stirring evenly and then adding into natural colour sand, is stirred
The preparation process of lacquer can be completed after the completion of uniformly.
Embodiment 5
A kind of self-cleaning lacquer, raw material are as follows by weight: deionized water 5%, hydroxyethyl cellulose solution 5%, anti-settling is molten
Liquid 2%, silicone acrylic emulsion 15%, plasticizer 1%, defoaming agent 0.6 ‰, sterilization antiseptic 2 ‰, drying retardant 5 ‰, wax emulsion 1%, PH are adjusted
Agent 2 ‰, natural colour sand 70%, thickener 0.4 ‰.
Specifically, the hydroxyethyl cellulose model ER-30M, and hydroxyethyl cellulose solution concentration is 2%.
Specifically, the anti-settling solution concentration is 5%.
Specifically, the thickener is ASE-60 thickener.
Specifically, the defoaming agent model is the defoaming agent of NXZ.
Specifically, the PH regulator is the PH regulator that model is AMP-95.
The present invention also provides a kind of preparation methods of self-cleaning lacquer, include the following steps:
S1: stock carries out weighing and proportioning according to the ratio of raw material, places after weighing and proportioning spare；
S2: deionized water is added in blender, and sterilization antiseptic is then added to blender and is mixed；
Hydroxyethyl cellulose solution: being added to the solution being mixed in S2 by S3, and after being stirred dissolution, PH regulator is added
After continue stirring after it is spare；
S4: anti-settling solution, silicone acrylic emulsion, plasticizer sterilizing, defoaming agent, drying retardant and wax emulsion are added to spare in S3
Solution is mixed evenly；
S5: thickener is continuously added, and is carried out continuing to stir after thickener is added, is stirring evenly and then adding into natural colour sand, is stirred
The preparation process of lacquer can be completed after the completion of uniformly.
Embodiment 6
A kind of self-cleaning lacquer, raw material are as follows by weight: deionized water 5%, hydroxyethyl cellulose solution 5%, anti-settling is molten
Liquid 2%, silicone acrylic emulsion 15%, plasticizer 8 ‰, defoaming agent 1 ‰, sterilization antiseptic 1.5 ‰, drying retardant 5 ‰, wax emulsion 1%, PH tune
Save agent 2 ‰, natural colour sand 70%, thickener 2.5 ‰.
Specifically, the hydroxyethyl cellulose model ER-30M, and hydroxyethyl cellulose solution concentration is 2%.
Specifically, the anti-settling solution concentration is 5%.
Specifically, the thickener is ASE-60 thickener.
Specifically, the defoaming agent model is the defoaming agent of NXZ.
Specifically, the PH regulator is the PH regulator that model is AMP-95.
The present invention also provides a kind of preparation methods of self-cleaning lacquer, include the following steps:
S1: stock carries out weighing and proportioning according to the ratio of raw material, places after weighing and proportioning spare；
S2: deionized water is added in blender, and sterilization antiseptic is then added to blender and is mixed；
Hydroxyethyl cellulose solution: being added to the solution being mixed in S2 by S3, and after being stirred dissolution, PH regulator is added
After continue stirring after it is spare；
S4: anti-settling solution, silicone acrylic emulsion, plasticizer sterilizing, defoaming agent, drying retardant and wax emulsion are added to spare in S3
Solution is mixed evenly；
S5: thickener is continuously added, and is carried out continuing to stir after thickener is added, is stirring evenly and then adding into natural colour sand, is stirred
The preparation process of lacquer can be completed after the completion of uniformly.
The present invention is widely applicable, has excellent adhesive force to various basal planes, weatherability is strong, is amenable to extreme weather ring
Border, quality is secure, and durability is good, and crack resistence effect is good, band self-cleaning property, different from existing lacquer, meets water energy and generates lotus
Leaf effect can effectively prevent the water-white phenomenon generated by water resistance.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of self-cleaning lacquer, it is characterised in that: its raw material is as follows by weight: deionized water 5%-7%, hydroxyethyl cellulose
Solution 5%, anti-settling solution 2%-3%, silicone acrylic emulsion 15%-20%, plasticizer 8 ‰ -1%, defoaming agent 0.5 ‰ -1 ‰, sterilization and anticorrosion
Agent 1 ‰ -2 ‰, drying retardant 5 ‰, hydrophober 1%-3%, PH regulator 2 ‰, natural colour sand 70%, surplus is thickener.
2. a kind of self-cleaning lacquer according to claim 1, it is characterised in that: the hydroxyethyl cellulose model ER-
30M, and hydroxyethyl cellulose solution concentration is 2%.
3. a kind of self-cleaning lacquer according to claim 1, it is characterised in that: the anti-settling solution concentration is 5%.
4. a kind of self-cleaning lacquer according to claim 1, it is characterised in that: the thickener is ASE-60 thickener.
5. a kind of self-cleaning lacquer according to claim 1, it is characterised in that: the defoaming agent model is the defoaming of NXZ
Agent.
6. a kind of self-cleaning lacquer according to claim 1, it is characterised in that: the hydrophober can also be wax emulsion.
7. a kind of self-cleaning lacquer according to claim 1, it is characterised in that: the PH regulator is that model is AMP-95
PH regulator.
8. a kind of preparation method of self-cleaning lacquer described in claim 1, characterized by the following steps:
S1: stock carries out weighing and proportioning according to the ratio of raw material, places after weighing and proportioning spare；
S2: deionized water is added in blender, and sterilization antiseptic is then added to blender and is mixed；
Hydroxyethyl cellulose solution: being added to the solution being mixed in S2 by S3, and after being stirred dissolution, PH regulator is added
After continue stirring after it is spare；
S4: anti-settling solution, silicone acrylic emulsion, plasticizer sterilizing, defoaming agent, drying retardant and hydrophober are added to spare in S3
Solution is mixed evenly；
S5: thickener is continuously added, and is carried out continuing to stir after thickener is added, is stirring evenly and then adding into natural colour sand, is stirred
The preparation process of lacquer can be completed after the completion of uniformly.