CN105670422A - Environment-friendly rough coatings - Google Patents
Environment-friendly rough coatings Download PDFInfo
- Publication number
- CN105670422A CN105670422A CN201410661386.0A CN201410661386A CN105670422A CN 105670422 A CN105670422 A CN 105670422A CN 201410661386 A CN201410661386 A CN 201410661386A CN 105670422 A CN105670422 A CN 105670422A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- silane
- barium sulfate
- hollow glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of coatings and particularly relates to environment-friendly rough coatings. The environment-friendly rough coatings provided by the invention are energy-saving and environment-friendly and are high in alkali resistance and high in cracking resistance. The technical scheme adopted by the invention is as follows: the environment-friendly rough coatings provided by the invention contain the following ingredients in parts by mass: 20-40 parts of elastic acrylic emulsion, 20-40 parts of water, 5-10 parts of nano titanium dioxide, 6-9 parts of barium sulfate, 5-7 parts of quartz powder, 5-10 parts of heavy calcium carbonate, 3-8 parts of diatomite, 1-3 parts of zinc stearate, 5-10 parts of hollow glass beads, 1-3 parts of defoamer, 1-5 parts of alkali-swelling thickener, 2-3 parts of cellulose thickener, 1-5 parts of film coalescing aid, 1-2 parts of wetting agent, 0.1-0.5 part of pentaerythritol triacrylate and 0.3-1 part of vinyltri(beta-methoxyethoxy)silane.
Description
Technical field
The present invention relates to paint field, it is specifically related to a kind of environmental protection plucking paint.
Background technology
At present, energy-saving and emission-reduction have become national government extremely important work. In China's building trade, just proposing thermal isolation technique requirement, become industry specification at present before 20 years, particularly in northern, these extremely cold, extremely hot areas, south, building heat insulation has become industry Compulsory Feature. In building, the concrete measure of heat-insulation and heat-preservation has interior wall inside holding, external wall outer insulation etc., mainly carries out Slate hanging construction with cystose.
Building coating is decoration that building trade is indispensable, protecting function material, no matter is indoor or outdoor, it is necessary to carry out coating protection. Indoor are painted with master with flat, and outdoor exterior wall take three-dimensional pattern as primary decoration form. Anti-cracking, decorative pattern are fine and smooth, stereoeffect is approved by vast building trade especially by force and likes because it has for external wall elastic galling paint, are generally adopted by building trade at present, but current external wall elastic galling paint does not possess heat-insulation and heat-preservation function.
Further, its many employing volatile organic material, knows from experience generation detrimentally affect to people, and the feature of environmental protection is poor.
Summary of the invention
It is an object of the invention to provide a kind of energy-conserving and environment-protective, alkali resistance wall, a kind of environmental protection plucking paint that splitting resistance is strong.
For realizing the above-mentioned purpose of the present invention, the present invention adopts following technical scheme: a kind of environmental protection plucking enamel-cover of the present invention is drawn together: elastomeric propylene yogurt liquid 20～40 parts of (massfractions, lower same), 20～40 parts, water, nano titanium oxide 5～10 parts, 6～9 parts, barium sulfate, silica powder 5～7 parts, heavy calcium 5～10 parts, 3～8 parts, diatomite, Zinic stearas 1～3 part, hollow glass micropearl 5～10 parts, defoamer 1～3 part, alkali swollen thickener 1～5 part, cellulose thickener 2～3 parts, film coalescence aid 1～5 part, wetting agent 1～2 part, pentaerythritol triacrylate 0.1～0.5 part, 0.3～1 part, vinyl three (β～methoxy ethoxy) silane.
The preparation method of the present invention: by elastomeric propylene yogurt liquid, water, nano titanium oxide, barium sulfate, silica powder, heavy calcium, diatomite, Zinic stearas, hollow glass micropearl, adds in reactor, stirs, and temperature of reaction is 40～60 DEG C, stirs 0.5～1 hour;Add in reactor again, pentaerythritol triacrylate and vinyl three (β～methoxy ethoxy) silane, stir 0.5～1 hour at 70～80 DEG C; Finally, add itself and component, mix and blend, after filtration, obtain the present invention.
The useful effect of the present invention: 1, the present invention is not containing volatile organic compounds, and the feature of environmental protection is good, and the person is harmless.
2, the present invention by adding nano titanium oxide in coating, when being subject to illumination, automatically can be decomposed by the volatile organic compounds in air, reach the object of purification air; Improve the environmental-protecting performance of the present invention further.
3, coating of the present invention is by the combination of the hollow glass micropearl of specified proportion, heavy calcium, diatomite and silica powder; reach the propagation hindering the light wave of different wave length, sound wave, Thermal Infra-Red; play effect heat insulation, insulation; give traditional external wall elastic galling paint with heat-insulation and heat-preservation function; and by other auxiliary agent, maintain the function of coatings decoration and protection.
4, the present invention has more wear-resistant and anti-cracking advantage than common flat painting or elastic coating, pliable and tough speciality can the be full of cracks of effective bridging body of wall, it is strongly regional that the ultra-violet radiation resisting function of its excellence is particularly useful for sunshine. Through the texture of stereo natural, the outer decorations effect of building can be improved.
Embodiment
Embodiment 1.
A kind of environmental protection plucking enamel-cover of the present invention is drawn together: elastomeric propylene yogurt liquid 30 parts, 30 parts, water, nano titanium oxide 7 parts, 8 parts, barium sulfate, silica powder 6 parts, heavy calcium 8 parts, 6 parts, diatomite, Zinic stearas 2 parts, hollow glass micropearl 7 parts, defoamer 2 parts, alkali swollen thickener 3 parts, cellulose thickener 2 parts, film coalescence aid 3 parts, wetting agent 2 parts, pentaerythritol triacrylate 0.3 part, 0.7 part, vinyl three (β～methoxy ethoxy) silane.
The preparation method of the present invention: by elastomeric propylene yogurt liquid, water, nano titanium oxide, barium sulfate, silica powder, heavy calcium, diatomite, Zinic stearas, hollow glass micropearl, adds in reactor, stirs, and temperature of reaction is 50 DEG C, stirs 0.7 hour; Add in reactor again, pentaerythritol triacrylate and vinyl three (β～methoxy ethoxy) silane, stir 0.6 hour at 75 DEG C; Finally, add itself and component, mix and blend, after filtration, obtain the present invention.
Embodiment 2.
A kind of environmental protection plucking enamel-cover of the present invention is drawn together: elastomeric propylene yogurt liquid 20 parts, 20 parts, water, nano titanium oxide 5 parts, 6 parts, barium sulfate, silica powder 5 parts, heavy calcium 5 parts, 3 parts, diatomite, Zinic stearas 1 part, hollow glass micropearl 5 parts, defoamer 1 part, alkali swollen thickener 1 part, cellulose thickener 2 parts, film coalescence aid 1 part, wetting agent 1 part, pentaerythritol triacrylate 0.1 part, 0.3 part, vinyl three (β～methoxy ethoxy) silane.
The preparation method of the present invention: by elastomeric propylene yogurt liquid, water, nano titanium oxide, barium sulfate, silica powder, heavy calcium, diatomite, Zinic stearas, hollow glass micropearl, adds in reactor, stirs, and temperature of reaction is 40 DEG C, stirs 0.5 hour; Add in reactor again, pentaerythritol triacrylate and vinyl three (β～methoxy ethoxy) silane, stir 0.5 hour at 70 DEG C; Finally, add itself and component, mix and blend, after filtration, obtain the present invention.
Embodiment 3.
A kind of environmental protection plucking enamel-cover of the present invention is drawn together: elastomeric propylene yogurt liquid 40 parts, 40 parts, water, nano titanium oxide 10 parts, 9 parts, barium sulfate, silica powder 7 parts, heavy calcium 10 parts, 8 parts, diatomite, Zinic stearas 3 parts, hollow glass micropearl 10 parts, defoamer 3 parts, alkali swollen thickener 5 parts, cellulose thickener 3 parts, film coalescence aid 5 parts, wetting agent 2 parts, pentaerythritol triacrylate 0.5 part, 1 part, vinyl three (β～methoxy ethoxy) silane.
The preparation method of the present invention: by elastomeric propylene yogurt liquid, water, nano titanium oxide, barium sulfate, silica powder, heavy calcium, diatomite, Zinic stearas, hollow glass micropearl, adds in reactor, stirs, and temperature of reaction is 60 DEG C, stirs 1 hour; Add in reactor again, pentaerythritol triacrylate and vinyl three (β～methoxy ethoxy) silane, stir 1 hour at 80 DEG C; Finally, add itself and component, mix and blend, after filtration, obtain the present invention.
Through test: performance index of the present invention are as follows.
1, time of drying (25 DEG C): 25min done by table, does solid work 30h.
2, snappiness mm≤1.
3, hardness >=2H.
4, high temperature resistant (130 DEG C) >=490h.
5, shock-resistance 50.
6, salt spray resistance (120h level) >=3.
7, water tolerance (29 ± 1 DEG C of 240h): non-foaming, does not come off.
8, oil resistant (90# gasoline, 56h): non-foaming, does not come off.
9, alkali resistance (GB/T9755～2001): by 48 hours.
10, artificial weathering ageing resistance (GB/T9755～2001): by 1200 hours.
The feature of the present invention.
1, outward appearance is plentiful.
2, excellent resistance to cleavage.
3, good permeability, Moisture-proof water-resistant.
4, excellent sticking power and perfectly hide performance.
The dilution of the present invention.
1, should stir evenly before using.
2, do not add water as far as possible during construction, it is coated with brushing effects for reaching best, during roller coat, not clear water more than 5% can be used to dilute according to practical situation.
The present invention need to leave the shady and cool dry and comfortable place of 5～35 DEG C in.
Claims (8)
1. an environmental protection plucking paint, it is characterized in that: comprising: elastomeric propylene yogurt liquid 20～40 parts of (massfractions, lower same), 20～40 parts, water, nano titanium oxide 5～10 parts, 6～9 parts, barium sulfate, silica powder 5～7 parts, heavy calcium 5～10 parts, 3～8 parts, diatomite, Zinic stearas 1～3 part, hollow glass micropearl 5～10 parts, defoamer 1～3 part, alkali swollen thickener 1～5 part, cellulose thickener 2～3 parts, film coalescence aid 1～5 part, wetting agent 1～2 part, pentaerythritol triacrylate 0.1～0.5 part, 0.3～1 part, vinyl three (β～methoxy ethoxy) silane.
2. a kind of environmental protection plucking paint according to claim 1, it is characterised in that: by by elastomeric propylene yogurt liquid, water, nano titanium oxide, barium sulfate, silica powder, heavy calcium, diatomite, Zinic stearas, hollow glass micropearl, add in reactor, stirring, temperature of reaction is 40～60 DEG C, stirs 0.5～1 hour; Add in reactor again, pentaerythritol triacrylate and vinyl three (β～methoxy ethoxy) silane, stir 0.5～1 hour at 70～80 DEG C; Finally, adding itself and component, mix and blend, the method for filtration obtains.
3. a kind of environmental protection plucking paint according to claim 1, it is characterised in that: comprising: elastomeric propylene yogurt liquid 30 parts, 30 parts, water, nano titanium oxide 7 parts, 8 parts, barium sulfate, silica powder 6 parts, heavy calcium 8 parts, 6 parts, diatomite, Zinic stearas 2 parts, hollow glass micropearl 7 parts, defoamer 2 parts, alkali swollen thickener 3 parts, cellulose thickener 2 parts, film coalescence aid 3 parts, wetting agent 2 parts, pentaerythritol triacrylate 0.3 part, 0.7 part, vinyl three (β～methoxy ethoxy) silane.
4. a kind of environmental protection plucking paint according to claim 3, it is characterised in that: by by elastomeric propylene yogurt liquid, water, nano titanium oxide, barium sulfate, silica powder, heavy calcium, diatomite, Zinic stearas, hollow glass micropearl, add in reactor, stirring, temperature of reaction is 50 DEG C, stirs 0.7 hour;Add in reactor again, pentaerythritol triacrylate and vinyl three (β～methoxy ethoxy) silane, stir 0.6 hour at 75 DEG C; Finally, adding itself and component, mix and blend, the method for filtration obtains.
5. a kind of environmental protection plucking paint according to claim 1, it is characterised in that: comprising: elastomeric propylene yogurt liquid 20 parts, 20 parts, water, nano titanium oxide 5 parts, 6 parts, barium sulfate, silica powder 5 parts, heavy calcium 5 parts, 3 parts, diatomite, Zinic stearas 1 part, hollow glass micropearl 5 parts, defoamer 1 part, alkali swollen thickener 1 part, cellulose thickener 2 parts, film coalescence aid 1 part, wetting agent 1 part, pentaerythritol triacrylate 0.1 part, 0.3 part, vinyl three (β～methoxy ethoxy) silane.
6. a kind of environmental protection plucking paint according to claim 5, it is characterised in that: by by elastomeric propylene yogurt liquid, water, nano titanium oxide, barium sulfate, silica powder, heavy calcium, diatomite, Zinic stearas, hollow glass micropearl, add in reactor, stirring, temperature of reaction is 40 DEG C, stirs 0.5 hour; Add in reactor again, pentaerythritol triacrylate and vinyl three (β～methoxy ethoxy) silane, stir 0.5 hour at 70 DEG C; Finally, adding itself and component, mix and blend, the method for filtration obtains.
7. a kind of environmental protection plucking paint according to claim 1, it is characterised in that: comprising: elastomeric propylene yogurt liquid 40 parts, 40 parts, water, nano titanium oxide 10 parts, 9 parts, barium sulfate, silica powder 7 parts, heavy calcium 10 parts, 8 parts, diatomite, Zinic stearas 3 parts, hollow glass micropearl 10 parts, defoamer 3 parts, alkali swollen thickener 5 parts, cellulose thickener 3 parts, film coalescence aid 5 parts, wetting agent 2 parts, pentaerythritol triacrylate 0.5 part, 1 part, vinyl three (β～methoxy ethoxy) silane.
8. a kind of environmental protection plucking paint according to claim 7, it is characterised in that: by by elastomeric propylene yogurt liquid, water, nano titanium oxide, barium sulfate, silica powder, heavy calcium, diatomite, Zinic stearas, hollow glass micropearl, add in reactor, stirring, temperature of reaction is 60 DEG C, stirs 1 hour; Add in reactor again, pentaerythritol triacrylate and vinyl three (β～methoxy ethoxy) silane, stir 1 hour at 80 DEG C; Finally, adding itself and component, mix and blend, the method for filtration obtains.