CN104727500B - Art flexible face brick and construction method thereof - Google Patents

Art flexible face brick and construction method thereof Download PDF

Info

Publication number
CN104727500B
CN104727500B CN201310696755.5A CN201310696755A CN104727500B CN 104727500 B CN104727500 B CN 104727500B CN 201310696755 A CN201310696755 A CN 201310696755A CN 104727500 B CN104727500 B CN 104727500B
Authority
CN
China
Prior art keywords
parts
face brick
filleting
layer
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310696755.5A
Other languages
Chinese (zh)
Other versions
CN104727500A (en
Inventor
杨戈斌
宋亚萍
胡晓霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pingdingshan University
Original Assignee
Pingdingshan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pingdingshan University filed Critical Pingdingshan University
Priority to CN201310696755.5A priority Critical patent/CN104727500B/en
Publication of CN104727500A publication Critical patent/CN104727500A/en
Application granted granted Critical
Publication of CN104727500B publication Critical patent/CN104727500B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to an art flexible brick and a construction method thereof. The art flexible brick comprises a caulking leveling course which is arranged on the external surface of a base layer; the external surface of the caulking leveling course is provided with a base enamel layer; the external surface of the base enamel layer is provided with a face brick sizing layer; the external surface of the face brick is provided with a waterproof enamel layer. The construction method of the art flexible brick comprises the following steps of base layer processing, caulking leveling course preparation, base enamel layer preparation, caulking, shape arrangement, face brick sizing layer preparation, face brick sizing layer shaping, cleaning and polishing and waterproof enamel layer preparation. The art flexible brick has the advantages that the materials of the arc flexible face brick and materials of an insulating layer of a construction wall are same flexible materials; the technical index is similar, compatible and well matched, the bonding strength is high, the material is light, the construction is simple, the costs are low, the unit area load is light, the safety coefficient is high, and the construction method is simple; compared with a traditional pasting tile, the construction efficiency can be improved by 50% and the construction costs can be reduced by 10% to 20%; the construction is simple, costs are low, the bonding strength is high, flexible anti-crack and weather fastness performances are strong, the waterproof air permeability is strong, and fade is not easy.

Description

A kind of fine arts flexible face brick and its construction method
Technical field
The present invention relates to building product technical field, and in particular to a kind of face brick for building, more particularly to a kind of fine arts Flexible face brick and its construction method.
Background technology
Building energy conservation exterior-wall heat insulation has turned into the mandatory standard of China's building trade, on traditional exterior-wall heat insulation finish coat The rigid materials such as equal sticking brick, mosaic, but because insulating layer of external wall is composite soft wall, built-in density is small, intensity Low, the overcoat facing sand of heat-insulation layer slurry and the adhesive strength of moisturizing plate only have >=0.1Mpa, and every square metre of loading 50KG of ceramic tile Left and right, therefore the basic unit of the combined wall of exterior wall heat-preserving system formation is in soft characteristic, insulation layer material is in flexible material, and porcelain The materials such as brick, mosaic belong to rigid, the technology such as two kinds of the expansion variable coefficients of material, line breathing amount and Temperature stress Performance indications differ greatly, and so cause the materials such as the ceramic tile pasted on exterior-wall heat insulation facing, mosaic easily to come off, ftracture, Cause to injure, kill people and smash the safe thing such as property by a crashing object, the moment around people is there is potential safety hazard.
Socially also occur in that a kind of fine arts flexible face brick in addition, existing, it be inorganic material as main base material, be equipped with High molecular polymer, then by the special a kind of new decorating inner and external walls facestock for processing, because it has rich color, thickness The advantages of degree thin, light weight, is more and more used, but existing fine arts flexible face brick is existed, and construction is complicated, cost It is high, flexible and crack resistance is poor, weatherability and water-proof breathable properties are poor, the shortcomings of easily fade.
The content of the invention
A kind of easy construction for being there is provided it is an object of the invention to overcome the deficiencies in the prior art, low cost, Adhesive strength is high, flexible break resistant, weatherability are strong, strong waterproof and breathable performance, fine arts flexible face brick not easy to fade and its construction party Method.
The object of the present invention is achieved like this:
A kind of fine arts flexible face brick, it includes being arranged on the filleting screed-coat of base layer exterior surface, described filleting screed-coat Outer surface be provided with ground glaze layer, the outer surface of described ground glaze layer is provided with face brick pulp layer, described face brick pulp layer Outer surface is provided with waterproof adamantine layer;
Wherein described filleting screed-coat is made up of each raw material according to following weight:Portland cement 20 ~ 35 Part, 5 ~ 15 parts of sierozem power, 1.5 ~ 4.0 parts of high molecular polymer, 0.5 ~ 1.5 part of pva powder, hydroxyphenylmethyl cellulose 0.4 ~ 0.8 part, 0.2 ~ 0.5 part of lignin, 0.1 ~ 0.3 part of polypropene staple, 0.2 ~ 0.5 part of organosilan powder, bentonite 2.0 ~ 4.0 parts, 0.1 ~ 0.5 part of starch ether, 15 ~ 25 parts of powdered whiting, 0.2 ~ 0.5 part of inorganic pigment;
Described ground glaze layer is made up of each raw material according to following weight:30 ~ 50 parts of polyacrylic resin, propylene 10 ~ 20 parts of acid resin, 2.0 ~ 5.0 parts of Ludox, 0.1 ~ 0.5 part of preservative, 0.1 ~ 0.3 part of defoamer, dispersant 0.5 ~ 1.0 Part, 0.1 ~ 0.3 part of hydroxyethyl cellulose, 0.05 ~ 0.2 part of aminomethyl propanol, 0.5 ~ 2.0 part of ethylene glycol, titanium dioxide 1.0 ~ 2.0 Part, 10 ~ 15 parts of powdered whiting, 10 ~ 15 parts of talcum powder, 2.0 ~ 2.5 parts of coalescents, 0.2 ~ 0.5 part of thickener, carbon black 2.0 ~ 3.0 parts;
Described face brick pulp layer is made up of each raw material according to following weight:10 ~ 15 parts of silicone acrylic emulsion, silicon are molten 2.0 ~ 5.0 parts of glue, 0.15 ~ 0.3 part of hydroxyethyl cellulose, 0.8 ~ 1.5 part of ethylene glycol, 0.15 ~ 0.3 part of aminomethyl propanol, film forming 0.8 ~ 1.5 part of auxiliary agent, 0.1 ~ 0.3 part of starch ether, 0.2 ~ 0.5 part of thixotropic agent, 0.3 ~ 0.5 part of lignin, 70 ~ 75 parts of colored stone sand, 0.2 ~ 0.5 part of metasilicate pentahydrate sodium;
Described waterproof adamantine layer is made up of each raw material according to following weight:30 ~ 50 parts of silicone acrylic emulsion, silicon are molten 3.0 ~ 5.0 parts of glue, 1.5 ~ 3.0 parts of coalescents, 0.15 ~ 0.3 part of aminomethyl propanol, 1.0 ~ 1.5 parts of ethylene glycol, preservative 1.5 ~ 3.0 parts, 0.2 ~ 0.5 part of metasilicate pentahydrate sodium, 0.1 ~ 0.2 part of defoamer.
Described portland cement is the portland cement marked as 425.
Described inorganic pigment is the iron oxide pigment of 80 ~ 120 mesh of drying.
Described high molecular polymer is monocomponent polyurethane or dual-component polyurethane or liquid resin or methyl Methyl acrylate.
Described preservative uses coating antiseptic, and it includes isothiazolinone derivatives, benzimidazole esters, 1,2- benzene And isothiazoline -3- ketone;Described defoamer uses polyethers defoamer or higher alcohols or polyether-modified silicon or poly- silicon Oxygen alkane defoamer;Described dispersant is derived using triethyl group hexyl phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol, cellulose One kind in thing, polyacrylamide, guar gum;Described coalescents use propylene glycol methyl ether acetate;Described thickener Using the one kind in polyacrylamide, polyvinyl alcohol, polyvinylpyrrolidone, polyethylene glycol oxide;Described thixotropic agent uses hydrogen Change the one kind in castor oil, polyamide wax, metallic soap.
The construction method of described fine arts flexible face brick, the construction method comprises the following steps:
Step 1, base treatment:Reject protrusion, weaker zone and the dust greasy dirt of substrate surface;
The preparation of step 2, filleting screed-coat:20 ~ 35 parts of portland cement, 5 ~ 15 parts of sierozem power, polyphosphazene polymer are taken first 1.5 ~ 4.0 parts of compound, 0.5 ~ 1.5 part of pva powder, 0.4 ~ 0.8 part of hydroxyphenylmethyl cellulose, lignin 0.2 ~ 0.5 Part, 0.1 ~ 0.3 part of polypropene staple, 0.2 ~ 0.5 part of organosilan powder, 2.0 ~ 4.0 parts of bentonite, starch ether 0.1 ~ 0.5 Part, 15 ~ 25 parts of powdered whiting, 0.2 ~ 0.5 part of inorganic pigment, feeding powder stirrer are mixed, and obtain filleting rubber cement powder, Then it is with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, water 0.25-0.35 parts, feeding mixer stirring is equal It is even to be made filleting mortar, place 10 ~ 15 minutes, be again stirring for, finally using by the way of batch scraping or spray by the setting of filleting mortar Filleting screed-coat is obtained in basic unit after step 1 treatment;
The preparation of step 3, ground glaze layer:30 ~ 50 parts of polyacrylic resin, 10 ~ 20 parts of acrylic resin, Ludox are taken first 2.0 ~ 5.0 parts, 0.1 ~ 0.5 part of preservative, 0.1 ~ 0.3 part of defoamer, 0.5 ~ 1.0 part of dispersant, hydroxyethyl cellulose 0.1 ~ 0.3 Part, 0.05 ~ 0.2 part of aminomethyl propanol, 0.5 ~ 2.0 part of ethylene glycol, 1.0 ~ 2.0 parts of titanium dioxide, 10 ~ 15 parts of powdered whiting, cunning 10 ~ 15 parts of stone flour, 2.0 ~ 2.5 parts of coalescents, 0.2 ~ 0.5 part of thickener, 2.0 ~ 3.0 parts of carbon black, system in feeding mixing plant Into ground-coat enamel solvent, then ground-coat enamel solvent coating is dried 24 hours on the filleting screed-coat that step 2 is obtained;
Step 4:Levelling and setting shape:First on the ground glaze layer that step 3 is obtained, by being ferreted out at the point of building ± 0.00 The horizontal line of ground glaze layer and vertical line is hung, and eject control line, then by the size and decorative pattern lines of construction requirement, in water Cellular snap line on horizontal line and vertical line, pastes filleting adhesive tape;
Step 5:The preparation of face brick pulp layer:It is fine that 10 ~ 15 parts of silicone acrylic emulsion, 2.0 ~ 5.0 parts of Ludox, ethoxy are taken first 0.15 ~ 0.3 part of dimension element, 0.8 ~ 1.5 part of ethylene glycol, 0.15 ~ 0.3 part of aminomethyl propanol, 0.8 ~ 1.5 part of coalescents, starch ether 0.1 ~ 0.3 part, 0.2 ~ 0.5 part of thixotropic agent, 0.3 ~ 0.5 part of lignin, 70 ~ 75 parts of colored stone sand, metasilicate pentahydrate sodium 0.2 ~ 0.5 Part, using water as decentralized medium, face brick slurry is uniformly mixed to get, then using spray or scrape or roller or painting or smear Form of construction work be coated on step 4 it is levelling and set shape treatment after ground glaze layer on;
Step 6:The shaping of face brick pulp layer:Before face brick slurry initial set in the preparation of step 5 face brick pulp layer, gently Throw off filleting adhesive tape, obtain step 4 it is levelling and set shape in default face brick shape;
Step 7:Cleaning polishing:Face brick slurry drying 48 hours after being processed in the shaping of step 6 face brick pulp layer is extremely After being completely dried, the burr of cleaning polishing face brick pulp layer surface galling and protrusion;
Step 8:The preparation of waterproof adamantine layer:Take 30 ~ 50 parts of silicone acrylic emulsion, 3.0 ~ 5.0 parts of Ludox, coalescents 1.5 ~ 3.0 parts, 0.15 ~ 0.3 part of aminomethyl propanol, 1.0 ~ 1.5 parts of ethylene glycol, 1.5 ~ 3.0 parts of preservative, metasilicate pentahydrate sodium 0.2 ~ 0.5 part, 0.1 ~ 0.2 part of defoamer, are obtained waterproof enamel solvent, and waterproof enamel solvent is covered with paint, lacquer, colour wash, etc. after step 7 clears up polishing Face brick slurry layer surface, completes the construction of fine arts flexible face brick.
Drying in the preparation of described step 3 ground glaze layer and step 7 cleaning polishing is doing naturally under normal temperature state It is dry.
Compared to the prior art, the present invention has the following advantages:
The material of fine arts flexible face brick of the invention belongs to same flexible material with the insulation layer material of construction wall, and technology refers to Mark is close, compatible, match, and adhesive strength is high, material light, easy construction, low cost, Unit area loading are light, safety Coefficient is high, and using inorganic pigment as dyestuff, natural color stone is aggregate, the Ministry of Public Security is fully achieved and lives to build veneer material required by portion Material will reach the standard of B grades of fire prevention, effectively solve the full hidden danger of exterior-wall heat insulation facing presence, and Building Energy-saving Work is played Positive impetus.
In addition, the present invention include be arranged on base layer exterior surface filleting screed-coat and be arranged on filleting screed-coat outside from The interior ground glaze layer being sequentially distributed to outward, face brick pulp layer and waterproof adamantine layer, simple structure, convenient to carry out and popularization;The present invention In construction using spraying or scraping or roller or painting or be layered by the way of smearing is constructed, form of construction work is more easy, one As staff can complete, comparing with traditional sticking brick can improve efficiency of construction 50%, reduce construction cost 10%~20%; Further, the present invention is made of the light and environmentally friendly industrial chemicals of quality, each raw material it is cheap, the fine arts so of the invention are soft Property face brick just there is volume light, environmental protection, low cost, in practice it has proved that, the unit area of fine arts flexible face brick of the invention Load is only gently 3KG/ ㎡ very much, and adhesive strength is high, flexible break resistant, weatherability strong and waterproof and breathable, using inorganic pigment as dye Toner, colorability is strong and does not allow fugitive color, elegant in appearance, great sight;The present invention need not in whole work progress High temperature, heating and all components are non-toxic material, achieving environmental protection and energy saving, and the present invention has easy construction, low cost, bonding strong Degree height, flexible break resistant, weatherability are strong, waterproof and breathable performance is strong, advantage not easy to fade.
Brief description of the drawings
Fig. 1 is the cross-sectional view of fine arts flexible face brick of the invention.
In figure:1st, basic unit 2, filleting screed-coat 3, ground glaze layer 4, face brick pulp layer 5, waterproof adamantine layer.
Specific embodiment
The present invention is described further with reference to the accompanying drawings and examples.
Embodiment 1
As shown in figure 1, a kind of fine arts flexible face brick, it includes being arranged on the filleting screed-coat 2 of the outer surface of basic unit 1, described The outer surface of filleting screed-coat 2 be provided with ground glaze layer 3, the outer surface of described ground glaze layer 3 is provided with face brick pulp layer 4, institute The outer surface of the face brick pulp layer 4 stated is provided with waterproof adamantine layer 5;
Wherein described filleting screed-coat 2 be by portland cement 20kg, sierozem power 5kg, high molecular polymer 1.5kg, Pva powder 0.5kg, hydroxyphenylmethyl cellulose 0.4kg, lignin 0.2kg, polypropene staple 0.1kg, organosilicon Alkane powder 0.2kg, bentonite 2.0kg, starch ether 0.1kg, powdered whiting 15kg, inorganic pigment 0.2kg are made;
Described ground glaze layer 3 is by polyacrylic resin 30kg, acrylic resin 10kg, Ludox 2.0kg, preservative 0.1kg, defoamer 0.1kg, dispersant 0.5kg, hydroxyethyl cellulose 0.1kg, aminomethyl propanol 0.05kg, ethylene glycol 0.5kg, titanium dioxide 1.0kg, powdered whiting 10kg, talcum powder 10kg, coalescents 2.0kg, thickener 0.2kg, carbon black 2.0kg;
Described face brick pulp layer 4 is by silicone acrylic emulsion 10kg, Ludox 2.0kg, hydroxyethyl cellulose 0.15kg, second two Alcohol 0.8kg, aminomethyl propanol 0.15kg, coalescents 0.8kg, starch ether 0.1kg, thixotropic agent 0.2kg, lignin 0.3kg, coloured silk Stone sand 70kg, metasilicate pentahydrate sodium 0.2kg are made;
Described waterproof adamantine layer 5 be by silicone acrylic emulsion 30kg, Ludox 3.0kg parts, coalescents 1.5kg, aminomethyl Propyl alcohol 0.15kg, ethylene glycol 1.0kg, preservative 1.5kg, metasilicate pentahydrate sodium 0.2kg, defoamer 0.1kg are made.
A kind of construction method of described fine arts flexible face brick, the construction method comprises the following steps:
Step 1, basic unit 1 are processed:Reject protrusion, weaker zone and the dust greasy dirt on the surface of basic unit 1;
The preparation of step 2, filleting screed-coat 2:Portland cement 20kg, sierozem power 5kg, high molecular polymer are taken first 1.5kg, pva powder 0.5kg, hydroxyphenylmethyl cellulose 0.4kg, lignin 0.2kg, polypropene staple 0.1kg, Organosilan powder 0.2kg, bentonite 2.0kg, starch ether 0.1kg, powdered whiting 15kg, inorganic pigment 0.2kg, send into dry powder Mixer is mixed, and obtains filleting rubber cement powder, is then with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, Water 0.25-0.35 parts, feeding mixer stirs and is made filleting mortar, places 10~15 minutes, is again stirring for, and finally uses Criticize the mode scraped or spray and filleting mortar is arranged in the basic unit after step 1 is processed 1 prepared filleting screed-coat 2;
The preparation of step 3, ground glaze layer 3:Polyacrylic resin 30kg, acrylic resin 10kg, Ludox are taken first 2.0kg, preservative 0.1kg, defoamer 0.1kg, dispersant 0.5kg, hydroxyethyl cellulose 0.1kg, aminomethyl propanol 0.05kg, ethylene glycol 0.5kg, titanium dioxide 1.0kg, powdered whiting 10kg, talcum powder 10kg, coalescents 2.0kg, thickener 0.2kg, carbon black 2.0kg, feeding mixing plant in be made ground-coat enamel solvent, then by ground-coat enamel solvent coating in step 2 obtain it is embedding On seam screed-coat 2, dry 24 hours;
Step 4:Levelling and setting shape:First on the ground glaze layer 3 that step 3 is obtained, by being copied at the point of building ± 0.00 Go out the horizontal line of ground glaze layer 3 and hang vertical line, and eject control line, then by the size and decorative pattern lines of construction requirement, The cellular snap line on horizontal line and vertical line, pastes filleting adhesive tape;
Step 5:The preparation of face brick pulp layer 4:Silicone acrylic emulsion 10kg, Ludox 2.0kg, hydroxyethyl cellulose are taken first 0.15kg, ethylene glycol 0.8kg, aminomethyl propanol 0.15kg, coalescents 0.8kg, starch ether 0.1kg, thixotropic agent 0.2kg, wood Quality 0.3kg, colored stone sand 70kg, metasilicate pentahydrate sodium 0.2kg, using water as decentralized medium, are uniformly mixed to get face brick slurry, Then using spray or scrape or roller or painting or the form of construction work smeared to be coated on step 4 levelling and after setting shape treatment On ground glaze layer 3;
Step 6:The shaping of face brick pulp layer 4:Before face brick slurry initial set in the preparation of step 5 face brick pulp layer 4, gently Gently throw off filleting adhesive tape, obtain step 4 it is levelling and set shape in default face brick shape;
Step 7:Cleaning polishing:Face brick slurry drying 48 hours after being processed in the shaping of step 6 face brick pulp layer 4 is extremely After being completely dried, the burr of the surface galling of cleaning polishing face brick pulp layer 4 and protrusion;
Step 8:The preparation of waterproof adamantine layer 5:Take silicone acrylic emulsion 30kg, Ludox 3.0kg parts, coalescents 1.5kg, ammonia Methylpropanol 0.15kg, ethylene glycol 1.0kg, preservative 1.5kg, metasilicate pentahydrate sodium 0.2kg, defoamer 0.1kg, are obtained anti- Water enamel solvent, the surface of face brick pulp layer 4 after step 7 clears up polishing is covered with paint, lacquer, colour wash, etc. by waterproof enamel solvent, completes the fine arts flexible The construction of face brick.
Drying in the preparation of described step 3 ground glaze layer 3 and step 7 cleaning polishing is doing naturally under normal temperature state It is dry.
The pH value of flexible panel of the invention answers≤10, water content≤15%, and temperature during construction is controlled at 5 DEG C~35 DEG C Temperature condition under, hot weather more than 35 DEG C should have sunshading facility or adjustment engineering time when constructing, less than 0 DEG C of temperature Should not construct;When being constructed by the way of spraying, the pressure of air compressor is adjusted to 0.6~0.8Mpa, nozzle diameter selection 5 ~8mm, gun slot is advisable with the distance of metope with 40cm~60cm, and nozzle axial line should be vertical with metope during spraying, and spray gun should Parallel to metope movement, translational speed answers uniformity, close in BMidcoat after spray gun spraying metope, and two edge coating materials are sparse, 1/3 repetition that the spraying pressure lastrow that should often be gone during spraying is sprayed is sprayed, and spraying should be carried out in sequence, be turned in the spraying of every row Folding direction is that should not have acute angle to move towards, and coating connects batch position and must stay at dividing joint.
Embodiment 2
As shown in figure 1, a kind of fine arts flexible face brick, it includes being arranged on the filleting screed-coat 2 of the outer surface of basic unit 1, described The outer surface of filleting screed-coat 2 be provided with ground glaze layer 3, the outer surface of described ground glaze layer 3 is provided with face brick pulp layer 4, institute The outer surface of the face brick pulp layer 4 stated is provided with waterproof adamantine layer 5;
Wherein described filleting screed-coat 2 be by portland cement 25kg, sierozem power 7kg, high molecular polymer 2.5kg, Pva powder 1kg, hydroxyphenylmethyl cellulose 0.6kg, lignin 0.3kg, polypropene staple 0.2kg, organosilan Powder 0.3kg, bentonite 3.0kg, starch ether 0.2kg, powdered whiting 20kg, inorganic pigment 0.3kg are made;
Described ground glaze layer 3 is by polyacrylic resin 40kg, acrylic resin 15kg, Ludox 2.5kg, preservative 0.3kg, defoamer 0.2kg, dispersant 0.8kg, hydroxyethyl cellulose 0.2kg, aminomethyl propanol 0.1kg, ethylene glycol 1kg, titanium White powder 1.5kg, powdered whiting 13kg, talcum powder 13kg, coalescents 2.3kg, thickener 0.3kg, carbon black 2.5kg;
Described face brick pulp layer 4 is by silicone acrylic emulsion 13kg, Ludox 3.0kg, hydroxyethyl cellulose 0.2kg, second two Alcohol 1.2kg, aminomethyl propanol 0.2kg, coalescents 1kg, starch ether 0.2kg, thixotropic agent 0.4kg, lignin 0.4kg, colored stone Sand 73kg, metasilicate pentahydrate sodium 0.3kg are made;
Described waterproof adamantine layer 5 be by silicone acrylic emulsion 40kg, Ludox 4.0kg parts, coalescents 2kg, aminomethyl third Alcohol 0.2kg, ethylene glycol 1.0kg, preservative 2.0kg, metasilicate pentahydrate sodium 0.4kg, defoamer 0.15kg are made.
A kind of construction method of described fine arts flexible face brick, the construction method comprises the following steps:
Step 1, basic unit 1 are processed:Reject protrusion, weaker zone and the dust greasy dirt on the surface of basic unit 1;
The preparation of step 2, filleting screed-coat 2:Portland cement 25kg, sierozem power 7kg, high molecular polymer are taken first 2.5kg, pva powder 1kg, hydroxyphenylmethyl cellulose 0.6kg, lignin 0.3kg, polypropene staple 0.2kg, have Machine silane powder 0.3kg, bentonite 3.0kg, starch ether 0.2kg, powdered whiting 20kg, inorganic pigment 0.3kg, feeding dry powder are stirred Machine mixing is mixed, filleting rubber cement powder is obtained, is then with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, water 0.25-0.35 parts, feeding mixer stirs and is made filleting mortar, places 10~15 minutes, is again stirring for, and finally uses and criticizes Be arranged on for filleting mortar filleting screed-coat 2 be obtained in the basic unit after step 1 is processed 1 by the mode scraped or spray;
The preparation of step 3, ground glaze layer 3:Polyacrylic resin 40kg, acrylic resin 15kg, Ludox are taken first 2.5kg, preservative 0.3kg, defoamer 0.2kg, dispersant 0.8kg, hydroxyethyl cellulose 0.2kg, aminomethyl propanol 0.1kg, Ethylene glycol 1kg, titanium dioxide 1.5kg, powdered whiting 13kg, talcum powder 13kg, coalescents 2.3kg, thickener 0.3kg, carbon Black 2.5kg, is made ground-coat enamel solvent, the filleting screed-coat 2 that then ground-coat enamel solvent coating is obtained in step 2 in feeding mixing plant On, dry 24 hours;
Step 4:Levelling and setting shape:First on the ground glaze layer 3 that step 3 is obtained, by being copied at the point of building ± 0.00 Go out the horizontal line of ground glaze layer 3 and hang vertical line, and eject control line, then by the size and decorative pattern lines of construction requirement, The cellular snap line on horizontal line and vertical line, pastes filleting adhesive tape;
Step 5:The preparation of face brick pulp layer 4:Silicone acrylic emulsion 13kg, Ludox 3.0kg, hydroxyethyl cellulose are taken first 0.2kg, ethylene glycol 1.2kg, aminomethyl propanol 0.2kg, coalescents 1kg, starch ether 0.2kg, thixotropic agent 0.4kg, lignin 0.4kg, colored stone sand 73kg, metasilicate pentahydrate sodium 0.3kg, using water as decentralized medium, are uniformly mixed to get face brick slurry, then Using spray or scrape or roller or painting or the form of construction work smeared to be coated on step 4 levelling and set the ground-coat enamel after shape is processed On layer 3;
Step 6:The shaping of face brick pulp layer 4:Before face brick slurry initial set in the preparation of step 5 face brick pulp layer 4, gently Gently throw off filleting adhesive tape, obtain step 4 it is levelling and set shape in default face brick shape;
Step 7:Cleaning polishing:Face brick slurry drying 48 hours after being processed in the shaping of step 6 face brick pulp layer 4 is extremely After being completely dried, the burr of the surface galling of cleaning polishing face brick pulp layer 4 and protrusion;
Step 8:The preparation of waterproof adamantine layer 5:Take silicone acrylic emulsion 40kg, Ludox 4.0kg parts, coalescents 2kg, ammonia first Base propyl alcohol 0.2kg, ethylene glycol 1.0kg, preservative 2.0kg, metasilicate pentahydrate sodium 0.4kg, defoamer 0.15kg, are obtained waterproof Enamel solvent, the surface of face brick pulp layer 4 after step 7 clears up polishing is covered with paint, lacquer, colour wash, etc. by waterproof enamel solvent, completes fine arts flexible face The construction of brick.
Drying in the preparation of described step 3 ground glaze layer 3 and step 7 cleaning polishing is doing naturally under normal temperature state It is dry.
The pH value of flexible panel of the invention answers≤10, water content≤15%, and temperature during construction is controlled at 5 DEG C~35 DEG C Temperature condition under, hot weather more than 35 DEG C should have sunshading facility or adjustment engineering time when constructing, less than 0 DEG C of temperature Should not construct;When being constructed by the way of spraying, the pressure of air compressor is adjusted to 0.6~0.8Mpa, nozzle diameter selection 5 ~8mm, gun slot is advisable with the distance of metope with 40cm~60cm, and nozzle axial line should be vertical with metope during spraying, and spray gun should Parallel to metope movement, translational speed answers uniformity, close in BMidcoat after spray gun spraying metope, and two edge coating materials are sparse, 1/3 repetition that the spraying pressure lastrow that should often be gone during spraying is sprayed is sprayed, and spraying should be carried out in sequence, be turned in the spraying of every row Folding direction is that should not have acute angle to move towards, and coating connects batch position and must stay at dividing joint.
Embodiment 3
As shown in figure 1, a kind of fine arts flexible face brick, it includes being arranged on the filleting screed-coat 2 of the outer surface of basic unit 1, described The outer surface of filleting screed-coat 2 be provided with ground glaze layer 3, the outer surface of described ground glaze layer 3 is provided with face brick pulp layer 4, institute The outer surface of the face brick pulp layer 4 stated is provided with waterproof adamantine layer 5;
Wherein described filleting screed-coat 2 is by portland cement 30kg, sierozem power 10kg, high molecular polymer 3kg, poly- Vinyl alcohol powder 1kg, hydroxyphenylmethyl cellulose 0.7kg, lignin 0.4kg, polypropene staple 0.2kg, organosilan powder 0.4kg, bentonite 3.5kg, starch ether 0.4kg, powdered whiting 23kg, inorganic pigment 0.4kg are made;
Described ground glaze layer 3 is by polyacrylic resin 50kg, acrylic resin 20kg, Ludox 5kg, preservative 0.5kg, defoamer 0.3kg, dispersant 1.0kg, hydroxyethyl cellulose 0.3kg, aminomethyl propanol 0.2kg, ethylene glycol 2.0kg, Titanium dioxide 2.0kg, powdered whiting 15kg, talcum powder 15kg, coalescents 2.5kg, thickener 0.5kg, carbon black 3.0kg;
Described face brick pulp layer 4 is by silicone acrylic emulsion 15kg, Ludox 5.0kg, hydroxyethyl cellulose 0.3kg, second two Alcohol 1.5kg, aminomethyl propanol 0.3kg, coalescents 1.5kg, starch ether 0.3kg, thixotropic agent 0.5kg, lignin 0.5kg, coloured silk Stone sand 75kg, metasilicate pentahydrate sodium 0.5kg are made;
Described waterproof adamantine layer 5 be by silicone acrylic emulsion 50kg, Ludox 5.0kg parts, coalescents 3.0kg, aminomethyl Propyl alcohol 0.3kg, ethylene glycol 1.5kg, preservative 3.0kg, metasilicate pentahydrate sodium 0.5kg, defoamer 0.2kg are made.
A kind of construction method of described fine arts flexible face brick, the construction method comprises the following steps:
Step 1, basic unit 1 are processed:Reject protrusion, weaker zone and the dust greasy dirt on the surface of basic unit 1;
The preparation of step 2, filleting screed-coat 2:Portland cement 30kg, sierozem power 10kg, high molecular polymer are taken first It is 3kg, pva powder 1kg, hydroxyphenylmethyl cellulose 0.7kg, lignin 0.4kg, polypropene staple 0.2kg, organic Silane powder 0.4kg, bentonite 3.5kg, starch ether 0.4kg, powdered whiting 23kg, inorganic pigment 0.4kg are made, and send into dry powder Mixer is mixed, and obtains filleting rubber cement powder, is then with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, Water 0.25-0.35 parts, feeding mixer stirs and is made filleting mortar, places 10~15 minutes, is again stirring for, and finally uses Criticize the mode scraped or spray and filleting mortar is arranged in the basic unit after step 1 is processed 1 prepared filleting screed-coat 2;
The preparation of step 3, ground glaze layer 3:Take first polyacrylic resin 50kg, acrylic resin 20kg, Ludox 5kg, Preservative 0.5kg, defoamer 0.3kg, dispersant 1.0kg, hydroxyethyl cellulose 0.3kg, aminomethyl propanol 0.2kg, ethylene glycol 2.0kg, titanium dioxide 2.0kg, powdered whiting 15kg, talcum powder 15kg, coalescents 2.5kg, thickener 0.5kg, carbon black 3.0kg, is made ground-coat enamel solvent, the filleting screed-coat 2 that then ground-coat enamel solvent coating is obtained in step 2 in feeding mixing plant On, dry 24 hours;
Step 4:Levelling and setting shape:First on the ground glaze layer 3 that step 3 is obtained, by being copied at the point of building ± 0.00 Go out the horizontal line of ground glaze layer 3 and hang vertical line, and eject control line, then by the size and decorative pattern lines of construction requirement, The cellular snap line on horizontal line and vertical line, pastes filleting adhesive tape;
Step 5:The preparation of face brick pulp layer 4:Silicone acrylic emulsion 15kg, Ludox 5.0kg, hydroxyethyl cellulose are taken first It is 0.3kg, ethylene glycol 1.5kg, aminomethyl propanol 0.3kg, coalescents 1.5kg, starch ether 0.3kg, thixotropic agent 0.5kg, wooden Plain 0.5kg, colored stone sand 75kg, metasilicate pentahydrate sodium 0.5kg, using water as decentralized medium, are uniformly mixed to get face brick slurry, so Afterwards using spray or scrape or roller or painting or the form of construction work smeared to be coated on step 4 levelling and set the bottom after shape treatment In glaze layer 3;
Step 6:The shaping of face brick pulp layer 4:Before face brick slurry initial set in the preparation of step 5 face brick pulp layer 4, gently Gently throw off filleting adhesive tape, obtain step 4 it is levelling and set shape in default face brick shape;
Step 7:Cleaning polishing:Face brick slurry drying 48 hours after being processed in the shaping of step 6 face brick pulp layer 4 is extremely After being completely dried, the burr of the surface galling of cleaning polishing face brick pulp layer 4 and protrusion;
Step 8:The preparation of waterproof adamantine layer 5:Take silicone acrylic emulsion 50kg, Ludox 5.0kg parts, coalescents 3.0kg, ammonia Methylpropanol 0.3kg, ethylene glycol 1.5kg, preservative 3.0kg, metasilicate pentahydrate sodium 0.5kg, defoamer 0.2kg, are obtained waterproof Enamel solvent, the surface of face brick pulp layer 4 after step 7 clears up polishing is covered with paint, lacquer, colour wash, etc. by waterproof enamel solvent, completes fine arts flexible face The construction of brick.
Drying in the preparation of described step 3 ground glaze layer 3 and step 7 cleaning polishing is doing naturally under normal temperature state It is dry.
The pH value of flexible panel of the invention answers≤10, water content≤15%, and temperature during construction is controlled at 5 DEG C~35 DEG C Temperature condition under, hot weather more than 35 DEG C should have sunshading facility or adjustment engineering time when constructing, less than 0 DEG C of temperature Should not construct;When being constructed by the way of spraying, the pressure of air compressor is adjusted to 0.6~0.8Mpa, nozzle diameter selection 5 ~8mm, gun slot is advisable with the distance of metope with 40cm~60cm, and nozzle axial line should be vertical with metope during spraying, and spray gun should Parallel to metope movement, translational speed answers uniformity, close in BMidcoat after spray gun spraying metope, and two edge coating materials are sparse, 1/3 repetition that the spraying pressure lastrow that should often be gone during spraying is sprayed is sprayed, and spraying should be carried out in sequence, be turned in the spraying of every row Folding direction is that should not have acute angle to move towards, and coating connects batch position and must stay at dividing joint.
Embodiment 4
As shown in figure 1, a kind of fine arts flexible face brick, it includes being arranged on the filleting screed-coat 2 of the outer surface of basic unit 1, described The outer surface of filleting screed-coat 2 be provided with ground glaze layer 3, the outer surface of described ground glaze layer 3 is provided with face brick pulp layer 4, institute The outer surface of the face brick pulp layer 4 stated is provided with waterproof adamantine layer 5;
Wherein described filleting screed-coat 2 is by portland cement 35kg, sierozem power 15kg, high molecular polymer 4kg, poly- Vinyl alcohol powder 1.5kg, hydroxyphenylmethyl cellulose 0.8kg, lignin 0.5kg, polypropene staple 0.3kg, organosilan Powder 0.5kg, bentonite 4.0kg, starch ether 0.5kg, powdered whiting 25kg, inorganic pigment 0.5kg are made;
Described ground glaze layer 3 is by polyacrylic resin 45kg, acrylic resin 17kg, Ludox 3.5kg, preservative 0.4kg, defoamer 0.25kg, dispersant 0.9kg, hydroxyethyl cellulose 0.25kg, aminomethyl propanol 0.15kg, ethylene glycol 1.5kg, titanium dioxide 1.8kg, powdered whiting 14kg, talcum powder 14kg, coalescents 2.4kg, thickener 0.4kg, carbon black 2.7kg;
Described face brick pulp layer 4 is by silicone acrylic emulsion 14kg, Ludox 4.0kg, hydroxyethyl cellulose 0.25kg, second two Alcohol 1.4kg, aminomethyl propanol 0.25kg, coalescents 1.3kg, starch ether 0.25kg, thixotropic agent 0.3kg, lignin 0.45kg, Colored stone sand 74kg, metasilicate pentahydrate sodium 0.4kg are made;
Described waterproof adamantine layer 5 be by silicone acrylic emulsion 45kg, Ludox 4.5kg parts, coalescents 2.5kg, aminomethyl Propyl alcohol 0.25kg, ethylene glycol 1.3kg, preservative 2.5kg, metasilicate pentahydrate sodium 0.45kg, defoamer 0.17kg are made.
A kind of construction method of described fine arts flexible face brick, the construction method comprises the following steps:
Step 1, basic unit 1 are processed:Reject protrusion, weaker zone and the dust greasy dirt on the surface of basic unit 1;
The preparation of step 2, filleting screed-coat 2:Portland cement 35kg, sierozem power 15kg, high molecular polymer are taken first 4kg, pva powder 1.5kg, hydroxyphenylmethyl cellulose 0.8kg, lignin 0.5kg, polypropene staple 0.3kg, have Machine silane powder 0.5kg, bentonite 4.0kg, starch ether 0.5kg, powdered whiting 25kg, inorganic pigment 0.5kg, feeding dry powder are stirred Machine mixing is mixed, filleting rubber cement powder is obtained, is then with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, water 0.25-0.35 parts, feeding mixer stirs and is made filleting mortar, places 10~15 minutes, is again stirring for, and finally uses and criticizes Be arranged on for filleting mortar filleting screed-coat 2 be obtained in the basic unit after step 1 is processed 1 by the mode scraped or spray;
The preparation of step 3, ground glaze layer 3:Polyacrylic resin 45kg, acrylic resin 17kg, Ludox are taken first 3.5kg, preservative 0.4kg, defoamer 0.25kg, dispersant 0.9kg, hydroxyethyl cellulose 0.25kg, aminomethyl propanol 0.15kg, ethylene glycol 1.5kg, titanium dioxide 1.8kg, powdered whiting 14kg, talcum powder 14kg, coalescents 2.4kg, thickener 0.4kg, carbon black 2.7kg, feeding mixing plant in be made ground-coat enamel solvent, then by ground-coat enamel solvent coating in step 2 obtain it is embedding On seam screed-coat 2, dry 24 hours;
Step 4:Levelling and setting shape:First on the ground glaze layer 3 that step 3 is obtained, by being copied at the point of building ± 0.00 Go out the horizontal line of ground glaze layer 3 and hang vertical line, and eject control line, then by the size and decorative pattern lines of construction requirement, The cellular snap line on horizontal line and vertical line, pastes filleting adhesive tape;
Step 5:The preparation of face brick pulp layer 4:Silicone acrylic emulsion 14kg, Ludox 4.0kg, hydroxyethyl cellulose are taken first 0.25kg, ethylene glycol 1.4kg, aminomethyl propanol 0.25kg, coalescents 1.3kg, starch ether 0.25kg, thixotropic agent 0.3kg, wood Quality 0.45kg, colored stone sand 74kg, metasilicate pentahydrate sodium 0.4kg, using water as decentralized medium, are uniformly mixed to get face brick slurry Material, then using spray or scrape or roller or painting or the form of construction work smeared to be coated on step 4 levelling and set shape treatment On ground glaze layer 3 afterwards;
Step 6:The shaping of face brick pulp layer 4:Before face brick slurry initial set in the preparation of step 5 face brick pulp layer 4, gently Gently throw off filleting adhesive tape, obtain step 4 it is levelling and set shape in default face brick shape;
Step 7:Cleaning polishing:Face brick slurry drying 48 hours after being processed in the shaping of step 6 face brick pulp layer 4 is extremely After being completely dried, the burr of the surface galling of cleaning polishing face brick pulp layer 4 and protrusion;
Step 8:The preparation of waterproof adamantine layer 5:Take silicone acrylic emulsion 45kg, Ludox 4.5kg parts, coalescents 2.5kg, ammonia Methylpropanol 0.25kg, ethylene glycol 1.3kg, preservative 2.5kg, metasilicate pentahydrate sodium 0.45kg, defoamer 0.17kg, are obtained Waterproof enamel solvent, the surface of face brick pulp layer 4 after step 7 clears up polishing is covered with paint, lacquer, colour wash, etc. by waterproof enamel solvent, completes the fine arts soft The construction of property face brick.
Drying in the preparation of described step 3 ground glaze layer 3 and step 7 cleaning polishing is doing naturally under normal temperature state It is dry.
The pH value of flexible panel of the invention answers≤10, water content≤15%, and temperature during construction is controlled at 5 DEG C~35 DEG C Temperature condition under, hot weather more than 35 DEG C should have sunshading facility or adjustment engineering time when constructing, less than 0 DEG C of temperature Should not construct;When being constructed by the way of spraying, the pressure of air compressor is adjusted to 0.6~0.8Mpa, nozzle diameter selection 5 ~8mm, gun slot is advisable with the distance of metope with 40cm~60cm, and nozzle axial line should be vertical with metope during spraying, and spray gun should Parallel to metope movement, translational speed answers uniformity, close in BMidcoat after spray gun spraying metope, and two edge coating materials are sparse, 1/3 repetition that the spraying pressure lastrow that should often be gone during spraying is sprayed is sprayed, and spraying should be carried out in sequence, be turned in the spraying of every row Folding direction is that should not have acute angle to move towards, and coating connects batch position and must stay at dividing joint.
Embodiment 5
As shown in figure 1, a kind of fine arts flexible face brick, it includes being arranged on the filleting screed-coat 2 of the outer surface of basic unit 1, described The outer surface of filleting screed-coat 2 be provided with ground glaze layer 3, the outer surface of described ground glaze layer 3 is provided with face brick pulp layer 4, institute The outer surface of the face brick pulp layer 4 stated is provided with waterproof adamantine layer 5;
Wherein described filleting screed-coat 2 be by portland cement 20kg, sierozem power 5kg, high molecular polymer 1.5kg, Pva powder 0.5kg, hydroxyphenylmethyl cellulose 0.4kg, lignin 0.2kg, polypropene staple 0.1kg, organosilicon Alkane powder 0.2kg, bentonite 2.0kg, starch ether 0.1kg, powdered whiting 15kg, inorganic pigment 0.2kg are made;
Described ground glaze layer 3 is by polyacrylic resin 30kg, acrylic resin 10kg, Ludox 2.0kg, preservative 0.1kg, defoamer 0.1kg, dispersant 0.5kg, hydroxyethyl cellulose 0.1kg, aminomethyl propanol 0.05kg, ethylene glycol 0.5kg, titanium dioxide 1.0kg, powdered whiting 10kg, talcum powder 10kg, coalescents 2.0kg, thickener 0.2kg, carbon black 2.0kg;
Described face brick pulp layer 4 is by silicone acrylic emulsion 10kg, Ludox 2.0kg, hydroxyethyl cellulose 0.15kg, second two Alcohol 0.8kg, aminomethyl propanol 0.15kg, coalescents 0.8kg, starch ether 0.1kg, thixotropic agent 0.2kg, lignin 0.3kg, coloured silk Stone sand 70kg, metasilicate pentahydrate sodium 0.2kg are made;
Described waterproof adamantine layer 5 be by silicone acrylic emulsion 30kg, Ludox 3.0kg parts, coalescents 1.5kg, aminomethyl Propyl alcohol 0.15kg, ethylene glycol 1.0kg, preservative 1.5kg, metasilicate pentahydrate sodium 0.2kg, defoamer 0.1kg are made.
Described portland cement is the portland cement marked as 425.Described inorganic pigment is the 80 ~ 120 of drying Purpose iron oxide pigment.Described high molecular polymer is monocomponent polyurethane or dual-component polyurethane or liquid resin Or methyl methacrylate.Described preservative uses coating antiseptic, and it includes isothiazolinone derivatives, benzimidazole Esters, BIT;Described defoamer uses polyethers defoamer or higher alcohols or polyether-modified Silicon or polysiloxane defoaming agent;Described dispersant using triethyl group hexyl phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol, One kind in cellulose derivative, polyacrylamide, guar gum;Described coalescents use propylene glycol methyl ether acetate;Institute The thickener stated is using the one kind in polyacrylamide, polyvinyl alcohol, polyvinylpyrrolidone, polyethylene glycol oxide;Described touches Become agent using the one kind in rilanit special, polyamide wax, metallic soap.
A kind of construction method of described fine arts flexible face brick, the construction method comprises the following steps:
Step 1, basic unit 1 are processed:Reject protrusion, weaker zone and the dust greasy dirt on the surface of basic unit 1;
The preparation of step 2, filleting screed-coat 2:Portland cement 20kg, sierozem power 5kg, high molecular polymer are taken first 1.5kg, pva powder 0.5kg, hydroxyphenylmethyl cellulose 0.4kg, lignin 0.2kg, polypropene staple 0.1kg, Organosilan powder 0.2kg, bentonite 2.0kg, starch ether 0.1kg, powdered whiting 15kg, inorganic pigment 0.2kg, send into dry powder Mixer is mixed, and obtains filleting rubber cement powder, is then with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, Water 0.25-0.35 parts, feeding mixer stirs and is made filleting mortar, places 10~15 minutes, is again stirring for, and finally uses Criticize the mode scraped or spray and filleting mortar is arranged in the basic unit after step 1 is processed 1 prepared filleting screed-coat 2;
The preparation of step 3, ground glaze layer 3:Polyacrylic resin 30kg, acrylic resin 10kg, Ludox are taken first 2.0kg, preservative 0.1kg, defoamer 0.1kg, dispersant 0.5kg, hydroxyethyl cellulose 0.1kg, aminomethyl propanol 0.05kg, ethylene glycol 0.5kg, titanium dioxide 1.0kg, powdered whiting 10kg, talcum powder 10kg, coalescents 2.0kg, thickener 0.2kg, carbon black 2.0kg, feeding mixing plant in be made ground-coat enamel solvent, then by ground-coat enamel solvent coating in step 2 obtain it is embedding On seam screed-coat 2, dry 24 hours;
Step 4:Levelling and setting shape:First on the ground glaze layer 3 that step 3 is obtained, by being copied at the point of building ± 0.00 Go out the horizontal line of ground glaze layer 3 and hang vertical line, and eject control line, then by the size and decorative pattern lines of construction requirement, The cellular snap line on horizontal line and vertical line, pastes filleting adhesive tape;
Step 5:The preparation of face brick pulp layer 4:Silicone acrylic emulsion 10kg, Ludox 2.0kg, hydroxyethyl cellulose are taken first 0.15kg, ethylene glycol 0.8kg, aminomethyl propanol 0.15kg, coalescents 0.8kg, starch ether 0.1kg, thixotropic agent 0.2kg, wood Quality 0.3kg, colored stone sand 70kg, metasilicate pentahydrate sodium 0.2kg, using water as decentralized medium, are uniformly mixed to get face brick slurry, Then using spray or scrape or roller or painting or the form of construction work smeared to be coated on step 4 levelling and after setting shape treatment On ground glaze layer 3;
Step 6:The shaping of face brick pulp layer 4:Before face brick slurry initial set in the preparation of step 5 face brick pulp layer 4, gently Gently throw off filleting adhesive tape, obtain step 4 it is levelling and set shape in default face brick shape;
Step 7:Cleaning polishing:Face brick slurry drying 48 hours after being processed in the shaping of step 6 face brick pulp layer 4 is extremely After being completely dried, the burr of the surface galling of cleaning polishing face brick pulp layer 4 and protrusion;
Step 8:The preparation of waterproof adamantine layer 5:Take silicone acrylic emulsion 30kg, Ludox 3.0kg parts, coalescents 1.5kg, ammonia Methylpropanol 0.15kg, ethylene glycol 1.0kg, preservative 1.5kg, metasilicate pentahydrate sodium 0.2kg, defoamer 0.1kg, are obtained anti- Water enamel solvent, the surface of face brick pulp layer 4 after step 7 clears up polishing is covered with paint, lacquer, colour wash, etc. by waterproof enamel solvent, completes the fine arts flexible The construction of face brick.
Drying in the preparation of described step 3 ground glaze layer 3 and step 7 cleaning polishing is doing naturally under normal temperature state It is dry.
The pH value of flexible panel of the invention answers≤10, water content≤15%, and temperature during construction is controlled at 5 DEG C~35 DEG C Temperature condition under, hot weather more than 35 DEG C should have sunshading facility or adjustment engineering time when constructing, less than 0 DEG C of temperature Should not construct;When being constructed by the way of spraying, the pressure of air compressor is adjusted to 0.6~0.8Mpa, nozzle diameter selection 5 ~8mm, gun slot is advisable with the distance of metope with 40cm~60cm, and nozzle axial line should be vertical with metope during spraying, and spray gun should Parallel to metope movement, translational speed answers uniformity, close in BMidcoat after spray gun spraying metope, and two edge coating materials are sparse, 1/3 repetition that the spraying pressure lastrow that should often be gone during spraying is sprayed is sprayed, and spraying should be carried out in sequence, be turned in the spraying of every row Folding direction is that should not have acute angle to move towards, and coating connects batch position and must stay at dividing joint.
Embodiment 6
As shown in figure 1, a kind of fine arts flexible face brick, it includes being arranged on the filleting screed-coat 2 of the outer surface of basic unit 1, described The outer surface of filleting screed-coat 2 be provided with ground glaze layer 3, the outer surface of described ground glaze layer 3 is provided with face brick pulp layer 4, institute The outer surface of the face brick pulp layer 4 stated is provided with waterproof adamantine layer 5;
Wherein described filleting screed-coat 2 be by portland cement 25kg, sierozem power 7kg, high molecular polymer 2.5kg, Pva powder 1kg, hydroxyphenylmethyl cellulose 0.6kg, lignin 0.3kg, polypropene staple 0.2kg, organosilan Powder 0.3kg, bentonite 3.0kg, starch ether 0.2kg, powdered whiting 20kg, inorganic pigment 0.3kg are made;
Described ground glaze layer 3 is by polyacrylic resin 40kg, acrylic resin 15kg, Ludox 2.5kg, preservative 0.3kg, defoamer 0.2kg, dispersant 0.8kg, hydroxyethyl cellulose 0.2kg, aminomethyl propanol 0.1kg, ethylene glycol 1kg, titanium White powder 1.5kg, powdered whiting 13kg, talcum powder 13kg, coalescents 2.3kg, thickener 0.3kg, carbon black 2.5kg;
Described face brick pulp layer 4 is by silicone acrylic emulsion 13kg, Ludox 3.0kg, hydroxyethyl cellulose 0.2kg, second two Alcohol 1.2kg, aminomethyl propanol 0.2kg, coalescents 1kg, starch ether 0.2kg, thixotropic agent 0.4kg, lignin 0.4kg, colored stone Sand 73kg, metasilicate pentahydrate sodium 0.3kg are made;
Described waterproof adamantine layer 5 be by silicone acrylic emulsion 40kg, Ludox 4.0kg parts, coalescents 2kg, aminomethyl third Alcohol 0.2kg, ethylene glycol 1.0kg, preservative 2.0kg, metasilicate pentahydrate sodium 0.4kg, defoamer 0.15kg are made.
Described portland cement is the portland cement marked as 425.Described inorganic pigment is the 80 ~ 120 of drying Purpose iron oxide pigment.Described high molecular polymer is monocomponent polyurethane or dual-component polyurethane or liquid resin Or methyl methacrylate.Described preservative uses coating antiseptic, and it includes isothiazolinone derivatives, benzimidazole Esters, BIT;Described defoamer uses polyethers defoamer or higher alcohols or polyether-modified Silicon or polysiloxane defoaming agent;Described dispersant using triethyl group hexyl phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol, One kind in cellulose derivative, polyacrylamide, guar gum;Described coalescents use propylene glycol methyl ether acetate;Institute The thickener stated is using the one kind in polyacrylamide, polyvinyl alcohol, polyvinylpyrrolidone, polyethylene glycol oxide;Described touches Become agent using the one kind in rilanit special, polyamide wax, metallic soap.
A kind of construction method of described fine arts flexible face brick, the construction method comprises the following steps:
Step 1, basic unit 1 are processed:Reject protrusion, weaker zone and the dust greasy dirt on the surface of basic unit 1;
The preparation of step 2, filleting screed-coat 2:Portland cement 25kg, sierozem power 7kg, high molecular polymer are taken first 2.5kg, pva powder 1kg, hydroxyphenylmethyl cellulose 0.6kg, lignin 0.3kg, polypropene staple 0.2kg, have Machine silane powder 0.3kg, bentonite 3.0kg, starch ether 0.2kg, powdered whiting 20kg, inorganic pigment 0.3kg, feeding dry powder are stirred Machine mixing is mixed, filleting rubber cement powder is obtained, is then with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, water 0.25-0.35 parts, feeding mixer stirs and is made filleting mortar, places 10~15 minutes, is again stirring for, and finally uses and criticizes Be arranged on for filleting mortar filleting screed-coat 2 be obtained in the basic unit after step 1 is processed 1 by the mode scraped or spray;
The preparation of step 3, ground glaze layer 3:Polyacrylic resin 40kg, acrylic resin 15kg, Ludox are taken first 2.5kg, preservative 0.3kg, defoamer 0.2kg, dispersant 0.8kg, hydroxyethyl cellulose 0.2kg, aminomethyl propanol 0.1kg, Ethylene glycol 1kg, titanium dioxide 1.5kg, powdered whiting 13kg, talcum powder 13kg, coalescents 2.3kg, thickener 0.3kg, carbon Black 2.5kg, is made ground-coat enamel solvent, the filleting screed-coat 2 that then ground-coat enamel solvent coating is obtained in step 2 in feeding mixing plant On, dry 24 hours;
Step 4:Levelling and setting shape:First on the ground glaze layer 3 that step 3 is obtained, by being copied at the point of building ± 0.00 Go out the horizontal line of ground glaze layer 3 and hang vertical line, and eject control line, then by the size and decorative pattern lines of construction requirement, The cellular snap line on horizontal line and vertical line, pastes filleting adhesive tape;
Step 5:The preparation of face brick pulp layer 4:Silicone acrylic emulsion 13kg, Ludox 3.0kg, hydroxyethyl cellulose are taken first 0.2kg, ethylene glycol 1.2kg, aminomethyl propanol 0.2kg, coalescents 1kg, starch ether 0.2kg, thixotropic agent 0.4kg, lignin 0.4kg, colored stone sand 73kg, metasilicate pentahydrate sodium 0.3kg, using water as decentralized medium, are uniformly mixed to get face brick slurry, then Using spray or scrape or roller or painting or the form of construction work smeared to be coated on step 4 levelling and set the ground-coat enamel after shape is processed On layer 3;
Step 6:The shaping of face brick pulp layer 4:Before face brick slurry initial set in the preparation of step 5 face brick pulp layer 4, gently Gently throw off filleting adhesive tape, obtain step 4 it is levelling and set shape in default face brick shape;
Step 7:Cleaning polishing:Face brick slurry drying 48 hours after being processed in the shaping of step 6 face brick pulp layer 4 is extremely After being completely dried, the burr of the surface galling of cleaning polishing face brick pulp layer 4 and protrusion;
Step 8:The preparation of waterproof adamantine layer 5:Take silicone acrylic emulsion 40kg, Ludox 4.0kg parts, coalescents 2kg, ammonia first Base propyl alcohol 0.2kg, ethylene glycol 1.0kg, preservative 2.0kg, metasilicate pentahydrate sodium 0.4kg, defoamer 0.15kg, are obtained waterproof Enamel solvent, the surface of face brick pulp layer 4 after step 7 clears up polishing is covered with paint, lacquer, colour wash, etc. by waterproof enamel solvent, completes fine arts flexible face The construction of brick.
Drying in the preparation of described step 3 ground glaze layer 3 and step 7 cleaning polishing is doing naturally under normal temperature state It is dry.
The pH value of flexible panel of the invention answers≤10, water content≤15%, and temperature during construction is controlled at 5 DEG C~35 DEG C Temperature condition under, hot weather more than 35 DEG C should have sunshading facility or adjustment engineering time when constructing, less than 0 DEG C of temperature Should not construct;When being constructed by the way of spraying, the pressure of air compressor is adjusted to 0.6~0.8Mpa, nozzle diameter selection 5 ~8mm, gun slot is advisable with the distance of metope with 40cm~60cm, and nozzle axial line should be vertical with metope during spraying, and spray gun should Parallel to metope movement, translational speed answers uniformity, close in BMidcoat after spray gun spraying metope, and two edge coating materials are sparse, 1/3 repetition that the spraying pressure lastrow that should often be gone during spraying is sprayed is sprayed, and spraying should be carried out in sequence, be turned in the spraying of every row Folding direction is that should not have acute angle to move towards, and coating connects batch position and must stay at dividing joint.
Embodiment 7
As shown in figure 1, a kind of fine arts flexible face brick, it includes being arranged on the filleting screed-coat 2 of the outer surface of basic unit 1, described The outer surface of filleting screed-coat 2 be provided with ground glaze layer 3, the outer surface of described ground glaze layer 3 is provided with face brick pulp layer 4, institute The outer surface of the face brick pulp layer 4 stated is provided with waterproof adamantine layer 5;
Wherein described filleting screed-coat 2 is by portland cement 30kg, sierozem power 10kg, high molecular polymer 3kg, poly- Vinyl alcohol powder 1kg, hydroxyphenylmethyl cellulose 0.7kg, lignin 0.4kg, polypropene staple 0.2kg, organosilan powder 0.4kg, bentonite 3.5kg, starch ether 0.4kg, powdered whiting 23kg, inorganic pigment 0.4kg are made;
Described ground glaze layer 3 is by polyacrylic resin 50kg, acrylic resin 20kg, Ludox 5kg, preservative 0.5kg, defoamer 0.3kg, dispersant 1.0kg, hydroxyethyl cellulose 0.3kg, aminomethyl propanol 0.2kg, ethylene glycol 2.0kg, Titanium dioxide 2.0kg, powdered whiting 15kg, talcum powder 15kg, coalescents 2.5kg, thickener 0.5kg, carbon black 3.0kg;
Described face brick pulp layer 4 is by silicone acrylic emulsion 15kg, Ludox 5.0kg, hydroxyethyl cellulose 0.3kg, second two Alcohol 1.5kg, aminomethyl propanol 0.3kg, coalescents 1.5kg, starch ether 0.3kg, thixotropic agent 0.5kg, lignin 0.5kg, coloured silk Stone sand 75kg, metasilicate pentahydrate sodium 0.5kg are made;
Described waterproof adamantine layer 5 be by silicone acrylic emulsion 50kg, Ludox 5.0kg parts, coalescents 3.0kg, aminomethyl Propyl alcohol 0.3kg, ethylene glycol 1.5kg, preservative 3.0kg, metasilicate pentahydrate sodium 0.5kg, defoamer 0.2kg are made.
Described portland cement is the portland cement marked as 425.Described inorganic pigment is the 80 ~ 120 of drying Purpose iron oxide pigment.Described high molecular polymer is monocomponent polyurethane or dual-component polyurethane or liquid resin Or methyl methacrylate.Described preservative uses coating antiseptic, and it includes isothiazolinone derivatives, benzimidazole Esters, BIT;Described defoamer uses polyethers defoamer or higher alcohols or polyether-modified Silicon or polysiloxane defoaming agent;Described dispersant using triethyl group hexyl phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol, One kind in cellulose derivative, polyacrylamide, guar gum;Described coalescents use propylene glycol methyl ether acetate;Institute The thickener stated is using the one kind in polyacrylamide, polyvinyl alcohol, polyvinylpyrrolidone, polyethylene glycol oxide;Described touches Become agent using the one kind in rilanit special, polyamide wax, metallic soap.
A kind of construction method of described fine arts flexible face brick, the construction method comprises the following steps:
Step 1, basic unit 1 are processed:Reject protrusion, weaker zone and the dust greasy dirt on the surface of basic unit 1;
The preparation of step 2, filleting screed-coat 2:Portland cement 30kg, sierozem power 10kg, high molecular polymer are taken first It is 3kg, pva powder 1kg, hydroxyphenylmethyl cellulose 0.7kg, lignin 0.4kg, polypropene staple 0.2kg, organic Silane powder 0.4kg, bentonite 3.5kg, starch ether 0.4kg, powdered whiting 23kg, inorganic pigment 0.4kg are made, and send into dry powder Mixer is mixed, and obtains filleting rubber cement powder, is then with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, Water 0.25-0.35 parts, feeding mixer stirs and is made filleting mortar, places 10~15 minutes, is again stirring for, and finally uses Criticize the mode scraped or spray and filleting mortar is arranged in the basic unit after step 1 is processed 1 prepared filleting screed-coat 2;
The preparation of step 3, ground glaze layer 3:Take first polyacrylic resin 50kg, acrylic resin 20kg, Ludox 5kg, Preservative 0.5kg, defoamer 0.3kg, dispersant 1.0kg, hydroxyethyl cellulose 0.3kg, aminomethyl propanol 0.2kg, ethylene glycol 2.0kg, titanium dioxide 2.0kg, powdered whiting 15kg, talcum powder 15kg, coalescents 2.5kg, thickener 0.5kg, carbon black 3.0kg, is made ground-coat enamel solvent, the filleting screed-coat 2 that then ground-coat enamel solvent coating is obtained in step 2 in feeding mixing plant On, dry 24 hours;
Step 4:Levelling and setting shape:First on the ground glaze layer 3 that step 3 is obtained, by being copied at the point of building ± 0.00 Go out the horizontal line of ground glaze layer 3 and hang vertical line, and eject control line, then by the size and decorative pattern lines of construction requirement, The cellular snap line on horizontal line and vertical line, pastes filleting adhesive tape;
Step 5:The preparation of face brick pulp layer 4:Silicone acrylic emulsion 15kg, Ludox 5.0kg, hydroxyethyl cellulose are taken first It is 0.3kg, ethylene glycol 1.5kg, aminomethyl propanol 0.3kg, coalescents 1.5kg, starch ether 0.3kg, thixotropic agent 0.5kg, wooden Plain 0.5kg, colored stone sand 75kg, metasilicate pentahydrate sodium 0.5kg, using water as decentralized medium, are uniformly mixed to get face brick slurry, so Afterwards using spray or scrape or roller or painting or the form of construction work smeared to be coated on step 4 levelling and set the bottom after shape treatment In glaze layer 3;
Step 6:The shaping of face brick pulp layer 4:Before face brick slurry initial set in the preparation of step 5 face brick pulp layer 4, gently Gently throw off filleting adhesive tape, obtain step 4 it is levelling and set shape in default face brick shape;
Step 7:Cleaning polishing:Face brick slurry drying 48 hours after being processed in the shaping of step 6 face brick pulp layer 4 is extremely After being completely dried, the burr of the surface galling of cleaning polishing face brick pulp layer 4 and protrusion;
Step 8:The preparation of waterproof adamantine layer 5:Take silicone acrylic emulsion 50kg, Ludox 5.0kg parts, coalescents 3.0kg, ammonia Methylpropanol 0.3kg, ethylene glycol 1.5kg, preservative 3.0kg, metasilicate pentahydrate sodium 0.5kg, defoamer 0.2kg, are obtained waterproof Enamel solvent, the surface of face brick pulp layer 4 after step 7 clears up polishing is covered with paint, lacquer, colour wash, etc. by waterproof enamel solvent, completes fine arts flexible face The construction of brick.
Drying in the preparation of described step 3 ground glaze layer 3 and step 7 cleaning polishing is doing naturally under normal temperature state It is dry.
The pH value of flexible panel of the invention answers≤10, water content≤15%, and temperature during construction is controlled at 5 DEG C~35 DEG C Temperature condition under, hot weather more than 35 DEG C should have sunshading facility or adjustment engineering time when constructing, less than 0 DEG C of temperature Should not construct;When being constructed by the way of spraying, the pressure of air compressor is adjusted to 0.6~0.8Mpa, nozzle diameter selection 5 ~8mm, gun slot is advisable with the distance of metope with 40cm~60cm, and nozzle axial line should be vertical with metope during spraying, and spray gun should Parallel to metope movement, translational speed answers uniformity, close in BMidcoat after spray gun spraying metope, and two edge coating materials are sparse, 1/3 repetition that the spraying pressure lastrow that should often be gone during spraying is sprayed is sprayed, and spraying should be carried out in sequence, be turned in the spraying of every row Folding direction is that should not have acute angle to move towards, and coating connects batch position and must stay at dividing joint.
Embodiment 8
As shown in figure 1, a kind of fine arts flexible face brick, it includes being arranged on the filleting screed-coat 2 of the outer surface of basic unit 1, described The outer surface of filleting screed-coat 2 be provided with ground glaze layer 3, the outer surface of described ground glaze layer 3 is provided with face brick pulp layer 4, institute The outer surface of the face brick pulp layer 4 stated is provided with waterproof adamantine layer 5;
Wherein described filleting screed-coat 2 is by portland cement 35kg, sierozem power 15kg, high molecular polymer 4kg, poly- Vinyl alcohol powder 1.5kg, hydroxyphenylmethyl cellulose 0.8kg, lignin 0.5kg, polypropene staple 0.3kg, organosilan Powder 0.5kg, bentonite 4.0kg, starch ether 0.5kg, powdered whiting 25kg, inorganic pigment 0.5kg are made;
Described ground glaze layer 3 is by polyacrylic resin 45kg, acrylic resin 17kg, Ludox 3.5kg, preservative 0.4kg, defoamer 0.25kg, dispersant 0.9kg, hydroxyethyl cellulose 0.25kg, aminomethyl propanol 0.15kg, ethylene glycol 1.5kg, titanium dioxide 1.8kg, powdered whiting 14kg, talcum powder 14kg, coalescents 2.4kg, thickener 0.4kg, carbon black 2.7kg;
Described face brick pulp layer 4 is by silicone acrylic emulsion 14kg, Ludox 4.0kg, hydroxyethyl cellulose 0.25kg, second two Alcohol 1.4kg, aminomethyl propanol 0.25kg, coalescents 1.3kg, starch ether 0.25kg, thixotropic agent 0.3kg, lignin 0.45kg, Colored stone sand 74kg, metasilicate pentahydrate sodium 0.4kg are made;
Described waterproof adamantine layer 5 be by silicone acrylic emulsion 45kg, Ludox 4.5kg parts, coalescents 2.5kg, aminomethyl Propyl alcohol 0.25kg, ethylene glycol 1.3kg, preservative 2.5kg, metasilicate pentahydrate sodium 0.45kg, defoamer 0.17kg are made.
Described portland cement is the portland cement marked as 425.Described inorganic pigment is the 80 ~ 120 of drying Purpose iron oxide pigment.Described high molecular polymer is monocomponent polyurethane or dual-component polyurethane or liquid resin Or methyl methacrylate.Described preservative uses coating antiseptic, and it includes isothiazolinone derivatives, benzimidazole Esters, BIT;Described defoamer uses polyethers defoamer or higher alcohols or polyether-modified Silicon or polysiloxane defoaming agent;Described dispersant using triethyl group hexyl phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol, One kind in cellulose derivative, polyacrylamide, guar gum;Described coalescents use propylene glycol methyl ether acetate;Institute The thickener stated is using the one kind in polyacrylamide, polyvinyl alcohol, polyvinylpyrrolidone, polyethylene glycol oxide;Described touches Become agent using the one kind in rilanit special, polyamide wax, metallic soap.
A kind of construction method of described fine arts flexible face brick, the construction method comprises the following steps:
Step 1, basic unit 1 are processed:Reject protrusion, weaker zone and the dust greasy dirt on the surface of basic unit 1;
The preparation of step 2, filleting screed-coat 2:Portland cement 35kg, sierozem power 15kg, high molecular polymer are taken first 4kg, pva powder 1.5kg, hydroxyphenylmethyl cellulose 0.8kg, lignin 0.5kg, polypropene staple 0.3kg, have Machine silane powder 0.5kg, bentonite 4.0kg, starch ether 0.5kg, powdered whiting 25kg, inorganic pigment 0.5kg, feeding dry powder are stirred Machine mixing is mixed, filleting rubber cement powder is obtained, is then with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, water 0.25-0.35 parts, feeding mixer stirs and is made filleting mortar, places 10~15 minutes, is again stirring for, and finally uses and criticizes Be arranged on for filleting mortar filleting screed-coat 2 be obtained in the basic unit after step 1 is processed 1 by the mode scraped or spray;
The preparation of step 3, ground glaze layer 3:Polyacrylic resin 45kg, acrylic resin 17kg, Ludox are taken first 3.5kg, preservative 0.4kg, defoamer 0.25kg, dispersant 0.9kg, hydroxyethyl cellulose 0.25kg, aminomethyl propanol 0.15kg, ethylene glycol 1.5kg, titanium dioxide 1.8kg, powdered whiting 14kg, talcum powder 14kg, coalescents 2.4kg, thickener 0.4kg, carbon black 2.7kg, feeding mixing plant in be made ground-coat enamel solvent, then by ground-coat enamel solvent coating in step 2 obtain it is embedding On seam screed-coat 2, dry 24 hours;
Step 4:Levelling and setting shape:First on the ground glaze layer 3 that step 3 is obtained, by being copied at the point of building ± 0.00 Go out the horizontal line of ground glaze layer 3 and hang vertical line, and eject control line, then by the size and decorative pattern lines of construction requirement, The cellular snap line on horizontal line and vertical line, pastes filleting adhesive tape;
Step 5:The preparation of face brick pulp layer 4:Silicone acrylic emulsion 14kg, Ludox 4.0kg, hydroxyethyl cellulose are taken first 0.25kg, ethylene glycol 1.4kg, aminomethyl propanol 0.25kg, coalescents 1.3kg, starch ether 0.25kg, thixotropic agent 0.3kg, wood Quality 0.45kg, colored stone sand 74kg, metasilicate pentahydrate sodium 0.4kg, using water as decentralized medium, are uniformly mixed to get face brick slurry Material, then using spray or scrape or roller or painting or the form of construction work smeared to be coated on step 4 levelling and set shape treatment On ground glaze layer 3 afterwards;
Step 6:The shaping of face brick pulp layer 4:Before face brick slurry initial set in the preparation of step 5 face brick pulp layer 4, gently Gently throw off filleting adhesive tape, obtain step 4 it is levelling and set shape in default face brick shape;
Step 7:Cleaning polishing:Face brick slurry drying 48 hours after being processed in the shaping of step 6 face brick pulp layer 4 is extremely After being completely dried, the burr of the surface galling of cleaning polishing face brick pulp layer 4 and protrusion;
Step 8:The preparation of waterproof adamantine layer 5:Take silicone acrylic emulsion 45kg, Ludox 4.5kg parts, coalescents 2.5kg, ammonia Methylpropanol 0.25kg, ethylene glycol 1.3kg, preservative 2.5kg, metasilicate pentahydrate sodium 0.45kg, defoamer 0.17kg, are obtained Waterproof enamel solvent, the surface of face brick pulp layer 4 after step 7 clears up polishing is covered with paint, lacquer, colour wash, etc. by waterproof enamel solvent, completes the fine arts soft The construction of property face brick.
Drying in the preparation of described step 3 ground glaze layer 3 and step 7 cleaning polishing is doing naturally under normal temperature state It is dry.
The pH value of flexible panel of the invention answers≤10, water content≤15%, and temperature during construction is controlled at 5 DEG C~35 DEG C Temperature condition under, hot weather more than 35 DEG C should have sunshading facility or adjustment engineering time when constructing, less than 0 DEG C of temperature Should not construct;When being constructed by the way of spraying, the pressure of air compressor is adjusted to 0.6~0.8Mpa, nozzle diameter selection 5 ~8mm, gun slot is advisable with the distance of metope with 40cm~60cm, and nozzle axial line should be vertical with metope during spraying, and spray gun should Parallel to metope movement, translational speed answers uniformity, close in BMidcoat after spray gun spraying metope, and two edge coating materials are sparse, 1/3 repetition that the spraying pressure lastrow that should often be gone during spraying is sprayed is sprayed, and spraying should be carried out in sequence, be turned in the spraying of every row Folding direction is that should not have acute angle to move towards, and coating connects batch position and must stay at dividing joint.

Claims (7)

1. a kind of fine arts flexible face brick, it is characterised in that:It includes being arranged on the filleting screed-coat of base layer exterior surface, described The outer surface of filleting screed-coat is provided with ground glaze layer, and the outer surface of described ground glaze layer is provided with face brick pulp layer, described face The outer surface of brick pulp layer is provided with waterproof adamantine layer;Wherein described filleting screed-coat is according to following weight by each raw material Part proportioning is made:20 ~ 35 parts of portland cement, 5 ~ 15 parts of sierozem power, 1.5 ~ 4.0 parts of high molecular polymer, poly- second 0.5 ~ 1.5 part of enol powder, 0.4 ~ 0.8 part of hydroxyphenylmethyl cellulose, 0.2 ~ 0.5 part of lignin, the short fibre of polypropylene Dimension 0.1 ~ 0.3 part, 0.2 ~ 0.5 part of organosilan powder, 2.0 ~ 4.0 parts of bentonite, 0.1 ~ 0.5 part of starch ether, 15 ~ 25 parts of powdered whiting, 0.2 ~ 0.5 part of inorganic pigment;Described ground glaze layer is according to following weight by each raw material Part proportioning is made:It is 30 ~ 50 parts of polyacrylic resin, 10 ~ 20 parts of acrylic resin, 2.0 ~ 5.0 parts of Ludox, anti- 0.1 ~ 0.5 part of rotten agent, 0.1 ~ 0.3 part of defoamer, 0.5 ~ 1.0 part of dispersant, 0.1 ~ 0.3 part of hydroxyethyl cellulose, ammonia 0.05 ~ 0.2 part of methylpropanol, 0.5 ~ 2.0 part of ethylene glycol, 1.0 ~ 2.0 parts of titanium dioxide, 10 ~ 15 parts of powdered whiting, talcum 10 ~ 15 parts of powder, 2.0 ~ 2.5 parts of coalescents, 0.2 ~ 0.5 part of thickener, 2.0 ~ 3.0 parts of carbon black;Described face Brick pulp layer is made up of each raw material according to following weight:10 ~ 15 parts of silicone acrylic emulsion, Ludox 2.0 ~ 5.0 Part, 0.15 ~ 0.3 part of hydroxyethyl cellulose, 0.8 ~ 1.5 part of ethylene glycol, 0.15 ~ 0.3 part of aminomethyl propanol, film forming are helped 0.8 ~ 1.5 part of agent, 0.1 ~ 0.3 part of starch ether, 0.2 ~ 0.5 part of thixotropic agent, 0.3 ~ 0.5 part of lignin, 70 ~ 75 parts of colored stone sand, five 0.2 ~ 0.5 part of water sodium metasilicate;Described waterproof adamantine layer is made up of each raw material according to following weight:Silicon 30 ~ 50 parts of acrylic emulsion, 3.0 ~ 5.0 parts of Ludox, 1.5 ~ 3.0 parts of coalescents, 0.15 ~ 0.3 part of aminomethyl propanol, 1.0 ~ 1.5 parts of ethylene glycol, 1.5 ~ 3.0 parts of preservative, 0.2 ~ 0.5 part of metasilicate pentahydrate sodium, defoamer 0.1 ~ 0.2 Part.
2. the fine arts flexible face brick as described in claim 1, it is characterised in that:Described portland cement be marked as 425 portland cement.
3. a kind of fine arts flexible face brick as described in claim 1, it is characterised in that:Described inorganic pigment is drying The iron oxide pigment of 80 ~ 120 mesh.
4. a kind of fine arts flexible face brick as described in claim 1, it is characterised in that:Described high molecular polymer is single Component polyurethane or dual-component polyurethane or liquid resin or methyl methacrylate.
5. a kind of fine arts flexible face brick as described in claim 1, it is characterised in that:Described preservative uses coating Preservative, it includes isothiazolinone derivatives, benzimidazole esters, 1,2- benzisothiazole -3- ketone;It is described Defoamer use polyethers defoamer or higher alcohols or polyether-modified silicon or polysiloxane defoaming agent;Described Dispersant uses triethyl group hexyl phosphoric acid, lauryl sodium sulfate, methyl anyl alcohol, cellulose derivative, polyacrylamide, Gu One kind in your glue;Described coalescents use propylene glycol methyl ether acetate;Described thickener uses polyacrylamide One kind in amine, polyvinyl alcohol, polyvinylpyrrolidone, polyethylene glycol oxide;Described thixotropic agent using rilanit special, One kind in polyamide wax, metallic soap.
6. the construction method of a kind of fine arts flexible face brick as described in claim 1-5 is any, it is characterised in that:The construction Method comprises the following steps:Step 1, base treatment:Reject protrusion, weaker zone and the dust greasy dirt of substrate surface; The preparation of step 2, filleting screed-coat:20 ~ 35 parts of portland cement, 5 ~ 15 parts of sierozem power, high molecular polymerization are taken first 1.5 ~ 4.0 parts of thing, 0.5 ~ 1.5 part of pva powder, 0.4 ~ 0.8 part of hydroxyphenylmethyl cellulose, lignin 0.2 ~ 0.5 part, 0.1 ~ 0.3 part of polypropene staple, 0.2 ~ 0.5 part of organosilan powder, 2.0 ~ 4.0 parts of bentonite, starch 0.1 ~ 0.5 part of ether, 15 ~ 25 parts of powdered whiting, 0.2 ~ 0.5 part of inorganic pigment, feeding powder stirrer are mixed, Filleting rubber cement powder is obtained, is then with the weight ratio of water according to filleting rubber cement powder:1 part of filleting rubber cement powder, water 0.25-0.35 Part, feeding mixer stirs and is made filleting mortar, places 10 ~ 15 minutes, is again stirring for, and finally scrapes or sprays using batch Mode filleting mortar is arranged on filleting screed-coat is obtained in the basic unit after step 1 is processed;Step 3, ground glaze layer Prepare:30 ~ 50 parts of polyacrylic resin, 10 ~ 20 parts of acrylic resin, 2.0 ~ 5.0 parts of Ludox, anti-is taken first 0.1 ~ 0.5 part of rotten agent, 0.1 ~ 0.3 part of defoamer, 0.5 ~ 1.0 part of dispersant, 0.1 ~ 0.3 part of hydroxyethyl cellulose, 0.05 ~ 0.2 part of aminomethyl propanol, 0.5 ~ 2.0 part of ethylene glycol, 1.0 ~ 2.0 parts of titanium dioxide, powdered whiting 10 ~ 15 Part, 10 ~ 15 parts of talcum powder, 2.0 ~ 2.5 parts of coalescents, 0.2 ~ 0.5 part of thickener, 2.0 ~ 3.0 parts of carbon black, feeding stirring set Ground-coat enamel solvent is made in standby, then ground-coat enamel solvent coating is dried 24 hours on the filleting screed-coat that step 2 is obtained ;Step 4:Levelling and setting shape:First on the ground glaze layer that step 3 is obtained, by being ferreted out bottom at the point of building ± 0.00 The horizontal line of glaze layer and vertical line is hung, and eject control line, then by the size and decorative pattern lines of construction requirement, in level Line and hang cellular snap line on vertical line, paste filleting adhesive tape;Step 5:The preparation of face brick pulp layer:The breast of silicon third is taken first 10 ~ 15 parts of liquid, 2.0 ~ 5.0 parts of Ludox, 0.15 ~ 0.3 part of hydroxyethyl cellulose, 0.8 ~ 1.5 part of ethylene glycol, ammonia 0.15 ~ 0.3 part of methylpropanol, 0.8 ~ 1.5 part of coalescents, 0.1 ~ 0.3 part of starch ether, thixotropic agent 0.2 ~ 0.5 Part, 0.3 ~ 0.5 part of lignin, 70 ~ 75 parts of colored stone sand, 0.2 ~ 0.5 part of metasilicate pentahydrate sodium, are situated between using water as dispersion Matter, is uniformly mixed to get face brick slurry, then using spray or scrapes or roller or painting or the form of construction work smeared are coated on step Rapid 4 it is levelling and set shape treatment after ground glaze layer on;Step 6:The shaping of face brick pulp layer:In step 5 face In the preparation of brick pulp layer face brick slurry initial set before, gently throw off filleting adhesive tape, obtain step 4 it is levelling and set shape In default face brick shape;Step 7:Cleaning polishing:Face after being processed in the shaping of step 6 face brick pulp layer Brick slurry drying clears up the burr of polishing face brick pulp layer surface galling and protrusion in 48 hours to after being completely dried;Step Rapid 8:The preparation of waterproof adamantine layer:Take 30 ~ 50 parts of silicone acrylic emulsion, 3.0 ~ 5.0 parts of Ludox, coalescents 1.5 ~ 3.0 parts, 0.15 ~ 0.3 part of aminomethyl propanol, 1.0 ~ 1.5 parts of ethylene glycol, 1.5 ~ 3.0 parts of preservative, five water metasilicic acids 0.2 ~ 0.5 part of sodium, 0.1 ~ 0.2 part of defoamer, are obtained waterproof enamel solvent, and waterproof enamel solvent is covered with paint, lacquer, colour wash, etc. in step 7 Face brick slurry layer surface after cleaning polishing, completes the construction of fine arts flexible face brick.
7. the construction method of fine arts flexible face brick as claimed in claim 6, it is characterised in that:Described step 3 bottom Drying in the preparation of glaze layer and step 7 cleaning polishing is the natural drying under normal temperature state.
CN201310696755.5A 2013-12-18 2013-12-18 Art flexible face brick and construction method thereof Expired - Fee Related CN104727500B (en)