CN110408288A - Aqueous fired slab marble paint - Google Patents

Aqueous fired slab marble paint Download PDF

Info

Publication number
CN110408288A
CN110408288A CN201910766578.0A CN201910766578A CN110408288A CN 110408288 A CN110408288 A CN 110408288A CN 201910766578 A CN201910766578 A CN 201910766578A CN 110408288 A CN110408288 A CN 110408288A
Authority
CN
China
Prior art keywords
parts
paint
marble
fungicide
fired slab
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910766578.0A
Other languages
Chinese (zh)
Inventor
周成
杨秀梅
程玉喜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian Zhongkai Coating Making Co Ltd
Original Assignee
Dalian Zhongkai Coating Making Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian Zhongkai Coating Making Co Ltd filed Critical Dalian Zhongkai Coating Making Co Ltd
Priority to CN201910766578.0A priority Critical patent/CN110408288A/en
Publication of CN110408288A publication Critical patent/CN110408288A/en
Pending legal-status Critical Current

Abstract

Aqueous fired slab marble paint of the invention, is made in parts by weight of following substance: 400~500 parts of glass microballoon, 100~150 parts of ultra-thin resin compounded piece, 15~30 parts of inorganic gel, 120~200 parts of silicone acrylic emulsion, 0.5~2 part of anti-settling agent, 200~300 parts of water, 0.5~1 part of fungicide, 0.5~1 part of defoaming agent.Aqueous fired slab marble paint of the invention, formula rationally, stablize by product system, is granite, marmorean substitute, and the upgraded product of conventional lacquer.Its product system is stable, not stratified, and quality is good;Compensate for the problems such as granite, marble are at high cost, safety coefficient is low;Thoroughly solve the disadvantages such as lacquer easy to pollute, floating, fidelity be low.It is widely portable to the high-grade buildings such as hotel, office building, government-works, various buildings.

Description

Aqueous fired slab marble paint
Technical field
The present invention relates to coating and application method more particularly to a kind of aqueous fired slab marble paints.
Background technique
In building decoration, the metope often decorated using marble, this decoration elegant, service life is long, But there is also many disadvantages, and such as at high cost, colour consistency is poor, and wall load-bearing is big, just can not update or change after use Color, the later period difficulty of repairing are big.For this purpose, a kind of imitative natural planes marble new coating --- marble paint comes into being, It overcomes the defect of existing fibrous gypsum decorative exterior wall: if marble unit square meter weight is up to tens of kg, increasing building body Load-bearing pressure, and difficulty of construction is big, at high cost for stone decoration, is not suitable for the moulding of the parts such as curved surface and thin side, Lines is not reproducible, and the exploitation of raw material also largely expends natural resources and human resources, damages to environment, unfavorable In energy conservation and environmental protection.But existing marble paint is also unreasonable because of its compatibility, and finished product is easy to change, and deposits layering, poor quality.
Summary of the invention
The present invention provides a kind of aqueous fired slab marble paint for above-mentioned the deficiencies in the prior art.
Aqueous fired slab marble paint of the invention, is made: glass microballoon 400~500 in parts by weight of following substance Part, 100~150 parts of ultra-thin resin compounded piece, 15~30 parts of inorganic gel, 120~200 parts of silicone acrylic emulsion, anti-settling agent 0.5~2 Part, 200~300 parts of water, 0.5~1 part of fungicide, 0.5~1 part of defoaming agent.
The defoaming agent be liquid metal system defoaming agent, the anti-settling agent be organobentonite, fumed silica, Polyolefin-wax;The fungicide is LWJ-688 fungicide.
Preparation method is as follows:
A, the preparation of dispersion liquid: sequentially adding silicone acrylic emulsion, anti-settling agent, fungicide, defoaming agent in water and disperse 5 minutes, adjustment Mixed liquor pH value obtains dispersion liquid to 8.5~9;
B, the preparation of base paint: increase inorganic gel for being added in dispersion liquid made from a step, base paint is made;
C, glass microballoon, ultra-thin resin compounded the preparation of aqueous fired slab marble paint: will be added in base paint made from b step Piece obtains finished product after mixing evenly.
Aqueous fired slab marble paint of the invention is only 0.8~1.5kg from heavy and light unit square meter weight, substantially reduces To the load-bearing pressure of building body;Environmentally friendly, nontoxic, the easy construction of paint vehicle is arbitrarily modulated a variety of according to the natural granite imitated The raw material of color, spraying application one-pass molding, effect are true to nature;Any asymmetric buildings metope is adapted to, any be bent, carefully can be decorated Rim portion, building shape-designing easy to accomplish;Can large-area construction application, be easy to control batch color difference, the later period renovates repairing side Just.
Aqueous fired slab marble paint of the invention, rationally, it is granite, marmorean substitution that product system is stablized to formula Product, and the upgraded product of conventional lacquer.Its product system is stable, not stratified, and quality is good;Compensate for granite, big The problems such as fibrous gypsum is at high cost, safety coefficient is low;Thoroughly solve the disadvantages such as lacquer easy to pollute, floating, fidelity be low.It can It is widely used in the high-grade buildings such as hotel, office building, government-works, various buildings.
Specific embodiment
Embodiment 1
Aqueous fired slab marble paint of the invention, is made in parts by weight of following substance: 400 parts of glass microballoon, ultra-thin tree 100 parts of rouge composite sheet, 15 parts of inorganic gel, 120 parts of silicone acrylic emulsion, 0.5 part of organobentonite, 200 parts of water, fungicide 0.5 Part, 0.5 part of defoaming agent.
It is obtained through the following steps:
A, the preparation of dispersion liquid: sequentially adding silicone acrylic emulsion, anti-settling agent, fungicide, defoaming agent in water and disperse 5 minutes, adjustment Mixed liquor pH value obtains dispersion liquid to 8.5~9;
B, the preparation of base paint: increase inorganic gel for being added in dispersion liquid made from a step, base paint is made;
C, glass microballoon, ultra-thin resin compounded the preparation of aqueous fired slab marble paint: will be added in base paint made from b step Piece obtains finished product after mixing evenly.
Embodiment 2
Aqueous fired slab marble paint of the invention, is made in parts by weight of following substance: 500 parts of glass microballoon, ultra-thin tree 150 parts of rouge composite sheet, 200 parts of silicone acrylic emulsion, 2 parts of fumed silica, 300 parts of water, 1 part of fungicide, disappears at 30 parts of inorganic gel 1 part of infusion.
Preparation method is the same as embodiment 1.
Embodiment 3
Aqueous fired slab marble paint of the invention, is made in parts by weight of following substance: glass is 300 parts micro-, ultra-thin resin 120 parts of composite sheet, 20 parts of inorganic gel, 180 parts of silicone acrylic emulsion, 1 part of polyolefin-wax, 250 parts of water, LWJ-688 fungicide 0.8 Part, 0.8 part of defoaming agent.
Preparation method is the same as embodiment 1.
The method that imitative fibrous gypsum is made in aqueous fired slab marble paint spraying made from Application Example 1-3, including the following steps:
A, base treatment: removing basal plane surface layer attachment, keep its smooth with putty Pi Gua base, maintains 18 hours, i.e. completion base Layer processing;Wherein the coating weight of putty is 1kg/ ㎡;
B, prime: in the processing base through a step, spraying or roller coating priming paint, 3 hours dry from top to bottom, that is, completes Prime, wherein the coating weight of priming paint is 0.15kg/ ㎡;
C, floating coat sprays: on the coating handled through b step, spraying texture coating from top to bottom, it is small then to spontaneously dry 24 Then Shi Hou, then spraying or roller coating colored paint from top to bottom are spontaneously dried 12 hours, i.e. completion floating coat brushing;Wherein, matter The coating weight for feeling coating is 1.5kg/ ㎡, and the coating weight of colored paint is 0.3kg/ ㎡;
D, aqueous fired slab marble paint spraying: on the coating handled through step c, spraying from top to bottom one time or more aqueous fire Foliation mineral varnish is burnt, each time is in that right-angled intersection sprays with upper one time, spray distance 30cm, then natural drying 24 hours, i.e., Aqueous fired slab marble paint spraying is completed, wherein the coating weight of aqueous fired slab marble paint is 1.5kg/ ㎡;
E, finish brushing: on the coating handled through Step d, spraying or roller coating finish, then spontaneously dry 8 from top to bottom Hour, i.e. the imitative fibrous gypsum construction of completion fired slab marble paint, wherein the coating weight of finish is 0.1kg/ ㎡.
The priming paint is used to improve the adhesive force of finishing coat, the richness for increasing finishing coat, provides alkali resistance, provides anti-corrosion function It can wait, while can guarantee the uniform pickup of finishing coat, coating system is made to play optimum efficiency;Texture coating used makes entirely to paint Face generates thickness, while realizing the texture of three-dimensional, so that coating is showed concave-convex texture, visually shows the true to nature of fibrous gypsum Effect;Finish used is to can protect paint layer surface, prolong the service life, and can also play the role of completely cutting off moisture.
Imitative fibrous gypsum is made in aqueous fired slab marble paint spraying made from Application Example 1~3, complies fully with country to building The environmental requirement of coating, lighter in weight will not bring load-bearing to wall, thoroughly prevent the hidden danger that falls off of Bartlit;It is suitable The complicated building of design is closed, the ideal effects of demand of client can be reached, natural granite can be imitated on color;It is constructed week Phase is short, quick, sprayable also to criticize painting, by upper pot formula lacquer spray gun, is not necessarily to Special vacuum Spray painting tool.Dry speed Degree is very fast, not sagging, one-pass molding smaller by weather influence factor when construction, therefore can greatly save the construction time;With good Ductility and resistance to flexibility, effectively cover the fine cracks on metope, keep that coating is firm does not crack;The storage period is long, It is thickened after being not present, phenomena such as discoloration.

Claims (2)

1. aqueous fired slab marble paint, is made in parts by weight of following substance: 400~500 parts of glass microballoon, ultra-thin resin 100~150 parts of composite sheet, 15~30 parts of inorganic gel, 120~200 parts of silicone acrylic emulsion, 0.5~2 part of anti-settling agent, water 200~ 300 parts, 0.5~1 part of fungicide, 0.5~1 part of defoaming agent;
The defoaming agent is liquid metal system defoaming agent, and the anti-settling agent is organobentonite, fumed silica, polyene Chloroflo;The fungicide is LWJ-688 fungicide.
2. preparing aqueous fired slab marble paint described in claim 1, operating procedure is as follows:
A, the preparation of dispersion liquid: sequentially adding silicone acrylic emulsion, anti-settling agent, fungicide, defoaming agent in water and disperse 5 minutes, adjustment Mixed liquor pH value obtains dispersion liquid to 8.5~9;
B, the preparation of base paint: increase inorganic gel for being added in dispersion liquid made from a step, base paint is made;
C, glass microballoon, ultra-thin resin compounded the preparation of aqueous fired slab marble paint: will be added in base paint made from b step Piece obtains finished product after mixing evenly.
CN201910766578.0A 2019-08-20 2019-08-20 Aqueous fired slab marble paint Pending CN110408288A (en)