CN103992061B - Stain resistant stone-like coating - Google Patents
Stain resistant stone-like coating Download PDFInfo
- Publication number
- CN103992061B CN103992061B CN201410230084.8A CN201410230084A CN103992061B CN 103992061 B CN103992061 B CN 103992061B CN 201410230084 A CN201410230084 A CN 201410230084A CN 103992061 B CN103992061 B CN 103992061B
- Authority
- CN
- China
- Prior art keywords
- coating
- stain resistant
- stone
- lignocellulose
- triazine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of stain resistant stone-like coating, be made up of each component of following weight percent: lignocellulose 3-3.5%, barium sulfate 2-3%, Sodium hexametaphosphate 99 5-6%, organosilicon crylic acid latex 15-18%, ethylene glycol 0.3-0.5%, natural colour sand 55-60%, pure aluminium silicate 3-5%, zeolite powder 1-3%, titanium dioxide 0.1-0.2%, thickening material TT-935? 0.3-0.35%, ethyl cellulose 0.2-0.3%, s-triazine 0.02-0.05%, water 6-9%; Stain resistant stone-like coating of the present invention not only has waterproof, ageing-resistant, hardness high, also possesses good cohesive strength, resistance to cleavage, surface adhesion force, wear resisting property and stain resistant.
Description
Technical field
The present invention relates to a kind of stain resistant stone-like coating.
Background technology
Building coating has the functions such as decoration, architecture protection; cover with paint, lacquer, colour wash, etc. material surface; its color, decorative pattern, gloss, texture etc. can be changed; improve the aesthetic value of object; protection can be coated with the surface of jewelry; prevent the erosion of the light, oxygen, chemical substance, solvent etc. from the external world, improve the work-ing life of coated thing.Along with growth in the living standard, people require more and more higher to the variation of coating, and stone-like coating is as a kind of new coating, the parent receiving people looks at, widely, its decorative effect equals to stone material in the application of stone-like coating, is more suitable for moulding various artistic design again than stone material.Stone-like coating can be used as exterior wall and embossment, the special-shaped wall decoration such as beam column; Also be applicable to do exterior wall mural painting; In addition, also can be used for interior decoration, have grouan, marble, color and luster effect as numb stone, in particular on the decoration such as cylinder, FRP Columns of indoor, the effect of mixing the spurious with the genuine can be obtained; Have a rest a little at the wayside pavilion etc. at the scenic spot such as Scenic Spots, sacred Buddhist site, application stone-like coating is decorated, not only elegant in appearance, and adds natural temperament and interest, brings out the best in each other with sight spot.
At present, the stone-like coating of appearance easily comes off, ftractures, and cohesive strength, resistance to cleavage, surface adhesion force and wear resisting property are all poor, and stain resistant is not strong, is not suitable for promoting.
Summary of the invention
Technical problem to be solved by this invention is, overcomes the shortcoming of above prior art: provide a kind of cohesive strength, resistance to cleavage, surface adhesion force, wear resistance and stain resistant stain resistant stone-like coating of good performance.
Technical solution of the present invention is as follows: a kind of stain resistant stone-like coating, is made up of each component of following weight percent:
Lignocellulose 3-3.5%,
Barium sulfate 2-3%,
Sodium hexametaphosphate 99 5-6%,
Organosilicon crylic acid latex 15-18%,
Ethylene glycol 0.3-0.5%,
Natural colour sand 55-60%,
Pure aluminium silicate 3-5%,
Zeolite powder 1-3%,
Titanium dioxide 0.1-0.2%,
Thickening material TT-9350.3-0.35%,
Ethyl cellulose 0.2-0.3%,
S-triazine 0.02-0.05%,
Water 6-9%.
Described stone-like coating is made up of each component of following weight percent:
Lignocellulose 3.2-3.5%,
Barium sulfate 2-3%,
Sodium hexametaphosphate 99 5.5-6%,
Organosilicon crylic acid latex 15-16%,
Ethylene glycol 0.3-0.5%,
Natural colour sand 58-60%,
Pure aluminium silicate 3-5%,
Zeolite powder 1-3%,
Titanium dioxide 0.1-0.2%,
Thickening material TT-9350.3-0.35%,
Ethyl cellulose 0.2-0.3%,
S-triazine 0.02-0.03%,
Water 6-8%.
It is prepared by following concrete grammar:
First the mixing of Sodium hexametaphosphate 99, zeolite powder, barium sulfate, water and ethylene glycol is placed in stirrer with 600-700 turn/after the rotating speed of min stirs 3-5 minute; Adjusting rotary speed turns/min to 700-800, lignocellulose, organosilicon crylic acid latex, pure aluminium silicate, titanium dioxide, ethyl cellulose is added successively under whipped state, continue to stir after 5-8 minute, continue to stir 15-20 minute after adding natural colour sand, thickening material TT-935, s-triazine under whipped state successively again; Finally add PH conditioning agent and regulate PH to 7-8, namely obtain stain resistant stone-like coating.
Described PH conditioning agent is Tao Shi AMP-95PH conditioning agent.
The invention has the beneficial effects as follows: stain resistant stone-like coating of the present invention not only has waterproof, ageing-resistant, hardness high, also possess good cohesive strength, resistance to cleavage, surface adhesion force, wear resisting property and stain resistant, because China's different areas envrionment conditions differs greatly, for the city of some heavy industry, mining industry prosperity, due to dust in air and other suspended matters more, can make easily to stain coating and lose original decorative effect, thus affect buildings appearance; Therefore, coating should have good contamination resistance, make coating not easily contaminated or pollute after easily wash; The formula of science of the present invention and the synergistic effect of concrete preparation technology make the present invention possess above-mentioned superperformance, suitable popularization.
Embodiment
With specific embodiment, the present invention is described in further details below, but the present invention is not only confined to following specific embodiment.
Embodiment one
Described stone-like coating is made up of each component of following weight percent:
Lignocellulose 3.2%,
Barium sulfate 3%,
Sodium hexametaphosphate 99 5.5%,
Organosilicon crylic acid latex 15%,
Ethylene glycol 0.3%,
Natural colour sand 60%,
Pure aluminium silicate 3%,
Zeolite powder 1.3%,
Titanium dioxide 0.1%,
Thickening material TT-9350.3%,
Ethyl cellulose 0.28%,
S-triazine 0.02%,
Water 8%.
It is prepared by following concrete grammar:
First the mixing of Sodium hexametaphosphate 99, zeolite powder, barium sulfate, water and ethylene glycol is placed in stirrer with 600-700 turn/after the rotating speed of min stirs 3-5 minute; Adjusting rotary speed turns/min to 700-800, lignocellulose, organosilicon crylic acid latex, pure aluminium silicate, titanium dioxide, ethyl cellulose is added successively under whipped state, continue to stir after 5-8 minute, continue to stir 15-20 minute after adding natural colour sand, thickening material TT-935, s-triazine under whipped state successively again; Finally add Tao Shi AMP-95PH conditioning agent and regulate PH to 7-8, namely obtain stain resistant stone-like coating.
The present invention can adopt following constructional method: cleaning metope, execute priming paint, line is taped, is sprayed the present invention.
Embodiment two
Described stone-like coating is made up of each component of following weight percent:
Lignocellulose 3.5%,
Barium sulfate 3%,
Sodium hexametaphosphate 99 5.5%,
Organosilicon crylic acid latex 15%,
Ethylene glycol 0.3%,
Natural colour sand 60%,
Pure aluminium silicate 3%,
Zeolite powder 1%,
Titanium dioxide 0.1%,
Thickening material TT-9350.3%,
Ethyl cellulose 0.27%,
S-triazine 0.03%,
Water 8%.
It is prepared by following concrete grammar:
First the mixing of Sodium hexametaphosphate 99, zeolite powder, barium sulfate, water and ethylene glycol is placed in after stirrer stirs 5 minutes with the rotating speed of 600 turns/min; Adjusting rotary speed to 700 turn/min, lignocellulose, organosilicon crylic acid latex, pure aluminium silicate, titanium dioxide, ethyl cellulose is added successively under whipped state, continue stirring after 5 minutes, after adding natural colour sand, thickening material TT-935, s-triazine successively again under whipped state, continue stirring 20 minutes; Finally add Tao Shi AMP-95PH conditioning agent and regulate PH to 8, namely obtain stain resistant stone-like coating.
Embodiment three
Described stone-like coating is made up of each component of following weight percent:
Lignocellulose 3%,
Barium sulfate 3%,
Sodium hexametaphosphate 99 5.7%,
Organosilicon crylic acid latex 16%,
Ethylene glycol 0.3%,
Natural colour sand 60%,
Pure aluminium silicate 3%,
Zeolite powder 1.3%,
Titanium dioxide 0.1%,
Thickening material TT-9350.3%,
Ethyl cellulose 0.28%,
S-triazine 0.02%,
Water 7%.
It is prepared by following concrete grammar:
First the mixing of Sodium hexametaphosphate 99, zeolite powder, barium sulfate, water and ethylene glycol is placed in after stirrer stirs 3 minutes with the rotating speed of 700 turns/min; Adjusting rotary speed to 800 turn/min, lignocellulose, organosilicon crylic acid latex, pure aluminium silicate, titanium dioxide, ethyl cellulose is added successively under whipped state, continue stirring after 5 minutes, after adding natural colour sand, thickening material TT-935, s-triazine successively again under whipped state, continue stirring 15 minutes; Finally add Tao Shi AMP-95PH conditioning agent and regulate PH to 7, namely obtain stain resistant stone-like coating.
Embodiment four
Described stone-like coating is made up of each component of following weight percent:
Lignocellulose 3.2%,
Barium sulfate 3%,
Sodium hexametaphosphate 99 5.5%,
Organosilicon crylic acid latex 18%,
Ethylene glycol 0.3%,
Natural colour sand 55%,
Pure aluminium silicate 5%,
Zeolite powder 1.3%,
Titanium dioxide 0.1%,
Thickening material TT-9350.3%,
Ethyl cellulose 0.28%,
S-triazine 0.02%,
Water 8%.
It is prepared by following concrete grammar:
First the mixing of Sodium hexametaphosphate 99, zeolite powder, barium sulfate, water and ethylene glycol is placed in after stirrer stirs 4 minutes with the rotating speed of 700 turns/min; Adjusting rotary speed to 800 turn/min, lignocellulose, organosilicon crylic acid latex, pure aluminium silicate, titanium dioxide, ethyl cellulose is added successively under whipped state, continue stirring after 8 minutes, after adding natural colour sand, thickening material TT-935, s-triazine successively again under whipped state, continue stirring 18 minutes; Finally add Tao Shi AMP-95PH conditioning agent and regulate PH to 7, namely obtain stain resistant stone-like coating.
Embodiment five
Described stone-like coating is made up of each component of following weight percent:
Lignocellulose 3.2%,
Barium sulfate 3%,
Sodium hexametaphosphate 99 5.5%,
Organosilicon crylic acid latex 17%,
Ethylene glycol 0.3%,
Natural colour sand 56%,
Pure aluminium silicate 5%,
Zeolite powder 1.3%,
Titanium dioxide 0.1%,
Thickening material TT-9350.3%,
Ethyl cellulose 0.28%,
S-triazine 0.02%,
Water 8%.
It is prepared by following concrete grammar:
First the mixing of Sodium hexametaphosphate 99, zeolite powder, barium sulfate, water and ethylene glycol is placed in after stirrer stirs 5 minutes with the rotating speed of 700 turns/min; Adjusting rotary speed to 750 turn/min, lignocellulose, organosilicon crylic acid latex, pure aluminium silicate, titanium dioxide, ethyl cellulose is added successively under whipped state, continue stirring after 8 minutes, after adding natural colour sand, thickening material TT-935, s-triazine successively again under whipped state, continue stirring 16 minutes; Finally add Tao Shi AMP-95PH conditioning agent and regulate PH to 7-8, namely obtain stain resistant stone-like coating.
The present invention can adopt following constructional method: cleaning metope, execute priming paint, line is taped, is sprayed the present invention.
Claims (3)
1. a stain resistant stone-like coating, is characterized in that: be made up of each component of following weight percent:
Lignocellulose 3-3.5%
Barium sulfate 2-3%,
Sodium hexametaphosphate 99 5-6%,
Organosilicon crylic acid latex 15-18%,
Ethylene glycol 0.3-0.5%,
Natural colour sand 55-60%,
Pure aluminium silicate 3-5%,
Zeolite powder 1-3%,
Titanium dioxide 0.1-0.2%,
Thickening material TT-9350.3-0.35%,
Ethyl cellulose 0.2-0.3%,
S-triazine 0.02-0.05%,
Water 6-9%;
It is prepared by following concrete grammar:
First the mixing of Sodium hexametaphosphate 99, zeolite powder, barium sulfate, water and ethylene glycol is placed in stirrer with 600-700 turn/after the rotating speed of min stirs 3-5 minute; Adjusting rotary speed turns/min to 700-800, lignocellulose, organosilicon crylic acid latex, pure aluminium silicate, titanium dioxide, ethyl cellulose is added successively under whipped state, continue to stir after 5-8 minute, continue to stir 15-20 minute after adding natural colour sand, thickening material TT-935, s-triazine under whipped state successively again; Finally add PH conditioning agent and regulate PH to 7-8, namely obtain stain resistant stone-like coating.
2. stain resistant stone-like coating according to claim 1, is characterized in that: described stone-like coating is made up of each component of following weight percent:
Lignocellulose 3.2-3.5%
Barium sulfate 2-3%,
Sodium hexametaphosphate 99 5.5-6%,
Organosilicon crylic acid latex 15-16%,
Ethylene glycol 0.3-0.5%,
Natural colour sand 58-60%,
Pure aluminium silicate 3-5%,
Zeolite powder 1-3%,
Titanium dioxide 0.1-0.2%,
Thickening material TT-9350.3-0.35%,
Ethyl cellulose 0.2-0.3%,
S-triazine 0.02-0.03%,
Water 6-8%.
3. stain resistant stone-like coating according to claim 1, is characterized in that: described PH conditioning agent is Tao Shi AMP-95PH conditioning agent.