CN104974627A - Aqueous fire board marble simulation paint, preparation method and construction method thereof - Google Patents
Aqueous fire board marble simulation paint, preparation method and construction method thereof Download PDFInfo
- Publication number
- CN104974627A CN104974627A CN201510402502.1A CN201510402502A CN104974627A CN 104974627 A CN104974627 A CN 104974627A CN 201510402502 A CN201510402502 A CN 201510402502A CN 104974627 A CN104974627 A CN 104974627A
- Authority
- CN
- China
- Prior art keywords
- paint
- sliver
- parts
- water
- marble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides to an aqueous fire board marble simulation paint, a preparation method and a construction method thereof, and relates to a coating material and a use method thereof. The aqueous fire board marble simulation paint is prepared from water, an emulsion, a film-forming additive, a wetting agent, a defoamer, propylene glycol, a preservative, a multifunctional additive, a thickener aqueous solution, rock sheet and color sand. The preparation method comprises three steps such as dispersion preparation, base paint preparation and aqueous fire board marble simulation paint preparation. The construction method comprises five steps such as base layer treatment, prime coat brushing, middle coating spraying, aqueous fire board marble simulation paint spraying, and top coat brushing. According to the present invention, the process is simple, the product system is system, the construction is simple and quick, the aqueous fire board marble simulation paint has the granite effect, and the limitations of cumbersome color blending, complex process, instable product system and high construction difficulty of the water-in-water multi-color coating material; the difficult problems of high cost, low safety factor and the like of the granite and the marble are overcome; and the disadvantages of easy pollution, color blur, low simulation and the like of the stone paint are solved.
Description
Technical field
The present invention relates to coating and using method, particularly relate to a kind of water-based fired slab marble paint and preparation method and constructional method.
Background technology
Grouan is with the texture of its uniqueness and color, be widely used in the decoration of exterior wall field of buildings, but, natural granite unit square meter weight can reach tens of kg, add the load-bearing pressure of building body, and stone decoration difficulty of construction is large, cost is high, it is not suitable for the moulding of the part such as curved surface and thin limit, its lines is not reproducible, add the difficulty of later stage repairing, and raw-material exploitation is also a large amount of expends natural resources and manpower, environment is damaged, is unfavorable for energy-conserving and environment-protective.For these reasons, Ye You unit in charge of construction uses true mineral varnish to realize the grain effect of natural granite, but true mineral varnish consumption is large, construction cost is high, the color of natural colour sand and the color of true mineral varnish places one's entire reliance upon, the natural colour sand of different zones, all there is color distortion in the color sand of the Deep mining processing that even same mineral resources is different, repairs bring very large difficulty to the later stage; Moreover the construction of true mineral varnish is the monochromatic difference repeatedly spraying application more than more than 3 kinds generally, and difficulty is comparatively large, is difficult to realize final effect.
Summary of the invention
The present invention, for above-mentioned the deficiencies in the prior art, provides a kind of water-based fired slab marble paint preparation method and constructional method.
Water-based fired slab marble paint of the present invention is made up by weight of following material: 200 ~ 300 parts, water, emulsion 120 ~ 200 parts, film coalescence aid 5 ~ 8 parts, wetting agent 0.2 ~ 1 part, defoamer 0.5 ~ 1 part, propylene glycol 5 ~ 10 parts, sanitas 1 ~ 3 part, multifunctional assistant 1 ~ 3 part, aqueous thickener solution 5 ~ 10 parts, sliver 100 ~ 150 parts and 400 ~ 500 parts, color sand;
Described emulsion is organosilicon crylic acid latex, described film coalescence aid is Lauryl Alcohol ester, described wetting agent is alkyl aryl polyether or polyoxyethylene alkyl aryl ether, described defoamer is liquid metal system defoamer, described sanitas is isothiazolones, described multifunctional assistant is alkanolamine, and described thickening material is polypropylene soda acid swelling type emulsion, and the mass percent concentration of aqueous thickener solution is 20% ~ 40%.
As a further improvement on the present invention, described sliver is the sliver mixing composition of multiple color, and the specification of its sliver is 0.1 ~ 50mm.
As a further improvement on the present invention, described sliver is made up of white sliver, grey sliver and black sliver, wherein 5 ~ 10mm specification white sliver 11 parts, 3 ~ 5mm specification white sliver 10 parts, 1 ~ 3mm specification white sliver 15 parts, 5 ~ 10mm specification grey sliver 30 parts, 3 ~ 5mm specification grey sliver 20 parts, 1 ~ 3mm specification grey sliver 16 parts, 3 ~ 5mm specification black sliver 20 parts, 1 ~ 3mm specification black sliver 11 parts.
As a further improvement on the present invention, described color sand is mixed by the one in Snow Flower White, China Dark, cream colour, yellow fraction or its several arbitrary proportion to form, and its specification is 10 ~ 200 orders.
Water-based fired slab marble paint of the present invention, its preparation method is as follows:
The preparation of a, dispersion liquid: add emulsion successively in water, film coalescence aid, wetting agent, defoamer, propylene glycol, sanitas disperse 5 minutes, then add multifunctional assistant adjustment mixed solution pH value to 8.5 ~ 9, be i.e. obtained dispersion liquid;
The preparation of b, base paint: add aqueous thickener solution in the dispersion liquid obtained by a step, obtained base paint;
The preparation of c, water-based fired slab marble paint: add sliver and color sand in the base paint obtained by b step, after stirring, i.e. obtained finished product.
The method of the obtained imitative reason stone of the water-based fired slab marble paint spraying that application aforesaid method obtains, comprises the following steps:
A, base treatment: remove basal plane top layer dirt settling, make it smooth with putty or Jiao Pigua basic unit of wiping one's face, maintain 18 ~ 48 hours, namely complete base treatment; Wherein the glue spread of putty is the glue spread of 0.5 ~ 2.5kg/ ㎡ or glue of wiping one's face is 1 ~ 5kg/ ㎡;
B, prime: in the process basic unit through a step, from top to bottom spraying or roller coating priming paint, dry 3 ~ 5 hours, namely complete prime, wherein the glue spread of priming paint was 0.05 ~ 0.3kg/ ㎡;
C, floating coat spray: in the coating through b step process, spray texture coating from top to bottom, then seasoning is after 18 ~ 26 hours, then spray from top to bottom or roller coating Color paint, and then seasoning 8 ~ 16 hours, namely completes floating coat brushing; Wherein, the glue spread of texture coating is 1 ~ 1.5kg/ ㎡, and the glue spread of Color paint is 0.2 ~ 0.3kg/ ㎡;
D, water-based fired slab marble paint spray: in the coating through step c process, spray the water-based fired slab marble paint of more than a time from top to bottom, each sprays in right-angled intersection all over upper one time, spray distance is 30 ~ 40cm, then seasoning 18 ~ 30 hours, namely complete the spraying of water-based fired slab marble paint, wherein the glue spread of water-based fired slab marble paint is 1 ~ 2kg/ ㎡;
E, finishing paint brushing: in the coating through Step d process, from top to bottom spraying or roller coating finishing paint, then seasoning 8 ~ 24 hours, namely complete the imitative reason stone construction of fired slab marble paint, wherein the glue spread of finishing paint is 0.05 ~ 0.2kg/ ㎡.
Water-based fired slab marble paint of the present invention, it is only 1 ~ 2kg from heavy and light unit square meter weight, greatly reduces the load-bearing pressure to building body; Paint vehicle environmental protection, nontoxic, easily construct, according to imitated natural granite, the arbitrarily raw material of modulation multiple color, spraying application once shaped, effect is true to nature, also energy-conserving and environment-protective more; Adapt to any asymmetric buildings metope, any bending, thin edge can be decorated and divide, easily realize building shape-designing; Large-area construction can apply, easily control batch aberration, later stage renovation is repaired conveniently.
Water-based fired slab marble paint of the present invention has the NEW PAINT SYSTEMS FOR BUILDINGS compared with high technology content, simply, practical, convenient, its production technique is simple, product system is stablized, construct simple and easy, quick, the grouan of most cost performance, marmorean substitute are also the upgraded products of conventional true mineral varnish.There is on all four granite effect, to revolutionize on market that the toning of water-water multicolor finish is loaded down with trivial details, complex manufacturing, product system unstable, difficulty of construction large, require high limitation; Compensate for the difficult problems such as grouan, marble cost is high, safety coefficient is low; Thoroughly solve the shortcomings such as true mineral varnish easily pollutes, floating, fidelity are low.The high-grade buildingss such as hotel, office building, government-works, various buildings can be widely used in.
Embodiment
Embodiment 1
Water-based fired slab marble paint of the present invention is made up by weight of following material: 220 parts, water, organosilicon crylic acid latex 170, Lauryl Alcohol ester 7 parts, alkyl aryl polyether 0.5 part, liquid metal system defoamer 0.7 part, propylene glycol 8 parts, isothiazolones 1 part, alkanolamine 2 parts, the polypropylene soda acid swelling type emulsion aqueous solution 7 parts of (mass percent concentration is 33%), sliver 100 parts and 400 parts, color sand;
Its preparation method is as follows:
The preparation of a, dispersion liquid: singly weigh according to formula, add 220 parts, water, emulsion 170 parts, film coalescence aid 7 parts, wetting agent 0.5 part, defoamer 0.7 part, propylene glycol 8 parts, sanitas 1 part dispersion 5 minutes in order successively, add multifunctional assistant 2 parts adjustment mixed solution pH value to 8.5 ~ 9 again, obtained dispersion liquid;
The preparation of b, base paint: add aqueous thickener solution 7 parts (mass percent concentration is 40%) in the dispersion liquid obtained by a step, obtained base paint;
The preparation of c, water-based fired slab marble paint: add the brown sliver of 30 ~ 50mm specification 20 parts, the orange sliver of 5 ~ 10mm specification 50 parts, 0.1 ~ 0.5mm specification coffee-like sliver 30 parts, 300 parts, 80-120 object yellow fraction color sand and 100 parts, 40-80 object yellow fraction color sand in the base paint obtained by b step, after stirring, i.e. obtained water-based fired slab marble paint; Wherein sliver specification is the longest distance of on sliver same side 2.
Embodiment 2
Water-based fired slab marble paint of the present invention is made up by weight of following material: 200 parts, water, organosilicon crylic acid latex 120, Lauryl Alcohol ester 5 parts, alkyl aryl polyether 0.2 part, liquid metal system defoamer 0.5 part, propylene glycol 5 parts, isothiazolones 1 part, alkanolamine 1 part, the polypropylene soda acid swelling type emulsion aqueous solution 5 parts of (mass percent concentration is 33%), sliver 100 parts and 400 parts, color sand.
Liquid metal system defoamer used is Japanese Nuo Pu section Nopco defoamer NXZ, and it is widely used in latex, emulsion and coating based on this and bonding agent.
Its preparation method is with embodiment 1.
Embodiment 3
Water-based fired slab marble paint of the present invention, be made up by weight of following material: 300 parts, water, organosilicon crylic acid latex 200 parts, Lauryl Alcohol ester 8 parts, polyoxyethylene alkyl aryl ether 1 part, liquid metal system defoamer 1 part, propylene glycol 10 parts, isothiazolones 2 parts, alkanolamine 3 parts, the polypropylene soda acid swelling type emulsion aqueous solution 10 parts (mass percent concentration is 20%), 5 ~ 10mm specification white sliver 11 parts, 3 ~ 5mm specification white sliver 10 parts, 1 ~ 3mm specification white sliver 15 parts, 5 ~ 10mm specification grey sliver 30 parts, 3 ~ 5mm specification grey sliver 20 parts, 1 ~ 3mm specification grey sliver 16 parts, 3 ~ 5mm specification black sliver 20 parts, 1 ~ 3mm specification black sliver 11 parts, 80-120 object Snow Flower White 400 parts, 20-40 object China Dark 40 parts, wherein sliver specification is the longest distance of on sliver same side 2.
Its preparation method is with embodiment 1.
Embodiment 4
The method of the obtained imitative reason stone of water-based fired slab marble paint spraying that Application Example 1 is obtained, comprises the following steps:
A, base treatment: remove basal plane top layer dirt settling, make it smooth with putty Pi Gua basic unit, maintain 18 hours, namely complete base treatment; Wherein the glue spread of putty is 1kg/ ㎡;
B, prime: in the process basic unit through a step, from top to bottom spraying or roller coating priming paint, dry 3 hours, namely complete prime, wherein the glue spread of priming paint was 0.15kg/ ㎡;
C, floating coat spray: in the coating through b step process, spray texture coating from top to bottom, then seasoning is after 24 hours, then spray from top to bottom or roller coating Color paint, and then seasoning 12 hours, namely completes floating coat brushing; Wherein, the glue spread of texture coating is 1.5kg/ ㎡, and the glue spread of Color paint is 0.3kg/ ㎡;
D, water-based fired slab marble paint spray: in the coating through step c process, spray the water-based fired slab marble paint of more than a time from top to bottom, each sprays in right-angled intersection all over upper one time, spray distance is 30cm, then seasoning 24 hours, namely complete the spraying of water-based fired slab marble paint, wherein the glue spread of water-based fired slab marble paint is 1.5kg/ ㎡;
E, finishing paint brushing: in the coating through Step d process, from top to bottom spraying or roller coating finishing paint, then seasoning 8 hours, namely complete the imitative reason stone construction of fired slab marble paint, wherein the glue spread of finishing paint is 0.1kg/ ㎡.
Described priming paint for improve finish paint sticking power, increase finish paint fullness ratio, alkali-resistivity is provided, anti-corrosion function etc. is provided, the uniform pickup of finish paint can be ensured simultaneously, make vanish system play best effect; Texture coating used makes whole lacquer painting produce thickness, realizes the texture of three-dimensional simultaneously, makes coating present concavo-convex texture, visually shows the vivid effect of reason stone; Finishing paint used be can protective paint layer surface, increase the service life, and the effect of isolated moisture can also be played.
Embodiment 5
The method of the obtained imitative reason stone of water-based fired slab marble paint spraying that Application Example 2 is obtained, comprises the following steps:
A, base treatment: the dirt settling such as dirt, dust removing basal plane top layer, Jiao Pigua basic unit of wiping one's face makes it smooth, maintains 48 hours, namely completes base treatment; The glue spread of glue of wherein wiping one's face is 5kg/ ㎡;
B, prime: in the process basic unit through a step, from top to bottom spraying or roller coating priming paint, dry 5 hours, namely complete prime, wherein the glue spread of priming paint was 0.2kg/ ㎡;
C, floating coat spray: in the coating through b step process, spray texture coating from top to bottom, then seasoning is after 24 hours, then spray from top to bottom or roller coating Color paint, and then seasoning 12 hours, namely completes floating coat brushing; Wherein, the glue spread of texture coating is 1.5kg/ ㎡, and the glue spread of Color paint is 0.3kg/ ㎡;
D, water-based fired slab marble paint spray: in the coating through step c process, spray the water-based fired slab marble paint of more than a time from top to bottom, each sprays in right-angled intersection all over upper one time, spray distance is 40cm, then seasoning 24 hours, namely complete the spraying of water-based fired slab marble paint, wherein the glue spread of water-based fired slab marble paint is 2kg/ ㎡;
E, finishing paint brushing: in the coating through Step d process, from top to bottom spraying or roller coating finishing paint, then seasoning 24 hours, namely completes finishing paint brushing, and wherein the glue spread of finishing paint is 0.2kg/ ㎡, namely completes the construction of fired slab marble paint.
Embodiment 6
The method of the obtained imitative reason stone of water-based fired slab marble paint spraying that Application Example 3 is obtained, comprises the following steps:
A, base treatment: remove basal plane top layer dirt settling, with wiping one's face, Jiao Pigua basic unit makes it smooth, maintains 36 hours, namely completes base treatment; Wherein, the glue spread of glue of wiping one's face is 2.5kg/ ㎡;
B, prime: in the process basic unit through a step, from top to bottom spraying or roller coating priming paint, dry 4 hours, namely complete prime, wherein the glue spread of priming paint was 0.1kg/ ㎡;
C, floating coat spray: in the coating through b step process, spray texture coating from top to bottom, then seasoning is after 26 hours, then spray from top to bottom or roller coating Color paint, and then seasoning 12 hours, namely completes floating coat brushing; Wherein, the glue spread of texture coating is 1.3kg/ ㎡, and the glue spread of Color paint is 0.25kg/ ㎡;
D, water-based fired slab marble paint spray: in the coating through step c process, spray the water-based fired slab marble paint of more than a time from top to bottom, each sprays in right-angled intersection all over upper one time, spray distance is 35cm, then seasoning 28 hours, namely complete the spraying of water-based fired slab marble paint, wherein the glue spread of water-based fired slab marble paint is 1.5kg/ ㎡;
E, finishing paint brushing: in the coating through Step d process, from top to bottom spraying or roller coating finishing paint, then seasoning 18 hours, namely completes finishing paint brushing, and wherein the glue spread of finishing paint is 0.1kg/ ㎡, namely completes the construction of fired slab marble paint.
The water-based fired slab marble paint that embodiment 1 ~ 3 is obtained, unit construction area consumption is few, true mineral varnish is constructed general 4-5kg/ ㎡, and water-based fired slab marble paint only needs 1-2kg/ ㎡, more saves that material meets national energy-saving, economizes on water, saves land, " four joints " requirement of material-saving.In addition, water-based fired slab marble paint multiple color material matching, can arbitrarily modulate, the color of natural colour sand and the color of true mineral varnish places one's entire reliance upon.For adding large-engineering, when true mineral varnish demand is larger, often because the continuity of time causes color distortion between color sand different batches comparatively large, bring certain passive situation to enterprise production and management.
The water-based fired slab marble paint that embodiment 1 ~ 3 obtains is easier than true mineral varnish constructs.Different according to imitated natural granite, generally comprise the raw material of 5-10 kind color, spraying application once shaped, multiple form and aspect are interlaced in grouan effect true to nature.And the true mineral varnish artificial granite way generally monochromatic difference repeatedly spraying application more than more than 3 kinds, difficulty is comparatively large, is difficult to realize final effect.
The obtained imitative reason stone of water-based fired slab marble paint spraying that Application Example 1 ~ 3 is obtained, meet the environmental requirement of country to building coating completely, its lighter in weight, can not bring load-bearing to body of wall, has thoroughly stopped the hidden danger that comes off of Bartlit; Be applicable to the buildings that design is complicated, the effects of demand that client is desirable can be reached, color can imitate natural granite; Its short construction period, quick, can spray and also can criticize painting, by the true mineral varnish spray gun of upper kettle formula, without the need to Special vacuum Spray painting tool.Rate of drying is very fast, not sagging, less by weather effect factor during construction, once shaped, therefore greatly can save the engineering time; There is good ductility and resistance to flexibility, effectively hide the fine cracks on metope, keep that coating is firm not to ftracture; Memory cycle is long, there is not rear thickening, the phenomenons such as variable color.
Claims (6)
1. water-based fired slab marble paint is made up by weight of following material: 200 ~ 300 parts, water, emulsion 120 ~ 200 parts, film coalescence aid 5 ~ 8 parts, wetting agent 0.2 ~ 1 part, defoamer 0.5 ~ 1 part, propylene glycol 5 ~ 10 parts, sanitas 1 ~ 3 part, multifunctional assistant 1 ~ 3 part, aqueous thickener solution 5 ~ 10 parts, sliver 100 ~ 150 parts and 400 ~ 500 parts, color sand;
Described emulsion is organosilicon crylic acid latex, described film coalescence aid is Lauryl Alcohol ester, described wetting agent is alkyl aryl polyether or polyoxyethylene alkyl aryl ether, described defoamer is liquid metal system defoamer, described sanitas is isothiazolones, described multifunctional assistant is alkanolamine, and described thickening material is polypropylene soda acid swelling type emulsion, and the mass percent concentration of aqueous thickener solution is 20% ~ 40%.
2. water-based fired slab marble paint as claimed in claim 1, it is characterized in that described sliver is the sliver mixing composition of multiple color, the specification of its sliver is 0.1 ~ 50mm.
3. water-based fired slab marble paint as claimed in claim 2, it is characterized in that described sliver is made up of white sliver, grey sliver and black sliver, wherein 5 ~ 10mm specification white sliver 11 parts, 3 ~ 5mm specification white sliver 10 parts, 1 ~ 3mm specification white sliver 15 parts, 5 ~ 10mm specification grey sliver 30 parts, 3 ~ 5mm specification grey sliver 20 parts, 1 ~ 3mm specification grey sliver 16 parts, 3 ~ 5mm specification black sliver 20 parts, 1 ~ 3mm specification black sliver 11 parts.
4. water-based fired slab marble paint as claimed in claim 1 or 2, it is characterized in that color sand is mixed by the one in Snow Flower White, China Dark, cream colour, yellow fraction or its several arbitrary proportion to form, its specification is 10 ~ 200 orders.
5. prepare water-based fired slab marble paint according to claim 1, its operation steps is as follows:
The preparation of dispersion liquid: add emulsion, film coalescence aid, wetting agent, defoamer, propylene glycol and sanitas successively and disperse 5 minutes in water, then add multifunctional assistant adjustment mixed solution pH value to 8.5 ~ 9, i.e. obtained dispersion liquid;
The preparation of base paint: add aqueous thickener solution in the dispersion liquid obtained by a step, obtained base paint;
The preparation of water-based fired slab marble paint: add sliver and color sand in the base paint obtained by b step, after stirring, i.e. obtained finished product.
6. application rights requires the method for the obtained imitative reason stone of the water-based fired slab marble paint spraying described in 1, comprises the following steps:
A, base treatment: remove basal plane top layer dirt settling, make it smooth with putty or Jiao Pigua basic unit of wiping one's face, maintain 18 ~ 48 hours, namely complete base treatment; Wherein the glue spread of putty is the glue spread of 0.5 ~ 2.5kg/ ㎡ or glue of wiping one's face is 1 ~ 5kg/ ㎡;
B, prime: in the process basic unit through a step, from top to bottom spraying or roller coating priming paint, dry 3 ~ 5 hours, namely complete prime, wherein the glue spread of priming paint was 0.05 ~ 0.3kg/ ㎡;
C, floating coat spray: in the coating through b step process, spray texture coating from top to bottom, then seasoning is after 18 ~ 26 hours, then spray from top to bottom or roller coating Color paint, and then seasoning 8 ~ 16 hours, namely completes floating coat brushing; Wherein, the glue spread of texture coating is 1 ~ 1.5kg/ ㎡, and the glue spread of Color paint is 0.2 ~ 0.3kg/ ㎡;
D, water-based fired slab marble paint spray: in the coating through step c process, spray the water-based fired slab marble paint of more than a time from top to bottom, each sprays in right-angled intersection all over upper one time, spray distance is 30 ~ 40cm, then seasoning 18 ~ 30 hours, namely complete the spraying of water-based fired slab marble paint, wherein the glue spread of water-based fired slab marble paint is 1 ~ 2kg/ ㎡;
E, finishing paint brushing: in the coating through Step d process, from top to bottom spraying or roller coating finishing paint, then seasoning 8 ~ 24 hours, namely complete the imitative reason stone construction of fired slab marble paint, wherein the glue spread of finishing paint is 0.05 ~ 0.2kg/ ㎡.