CN109021654A - A kind of lacquer and preparation method thereof - Google Patents
A kind of lacquer and preparation method thereof Download PDFInfo
- Publication number
- CN109021654A CN109021654A CN201810860798.5A CN201810860798A CN109021654A CN 109021654 A CN109021654 A CN 109021654A CN 201810860798 A CN201810860798 A CN 201810860798A CN 109021654 A CN109021654 A CN 109021654A
- Authority
- CN
- China
- Prior art keywords
- parts
- lacquer
- mixing
- mud
- mesh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of lacquers and preparation method thereof, lacquer includes following raw material by weight: 60-80 parts of water, 1-3 parts of cellulose, 1-3 parts of modified alta-mud, 120-150 parts of lacquer lotion, 6-8 parts of coalescing agent, 0.6-1.6 parts of defoaming agent, 1-2 parts of fungicide, neutralize 0.5-1.6 parts of tone pitch agent, 4-8 parts of ethylene glycol, 600-800 parts of color sand.It is added to modified alta-mud in this product, the application property of product can be changed, improve caking ability, prevent drop, increase suspension, prevent color sand from sinking.Modified alta-mud and other raw materials are used in mixed way, and color of light distinctness is bright after lacquer decoration obtained, fire prevention, waterproof, acid and alkali-resistance, anti-pollution, while non-toxic and tasteless colour-fast not being cracked.
Description
Technical field
The present invention relates to exterior wall decorating coating technical fields, and in particular to a kind of lacquer and preparation method thereof.
Background technique
Lacquer is that a kind of decorative effect exactly likes marble, granite, and lacquer is also referred to as liquid stone multicolor finish.Mainly adopt
It is formulated with the natural stone-powder of various colors, the building after lacquer finishing has natural true natural colour, gives people
With elegance, harmonious, serious aesthetic feeling is suitable for the indoor and outdoor decoration of all kinds of buildings.Especially decorated on curved-surface building object,
Can receive it is vivid, the effect of back to nature.Lacquer has fire prevention, waterproof, acid and alkali-resistance, anti-pollution.Nontoxic, tasteless,
The features such as bonding force is strong, will never fade can effectively stop extraneous adverse circumstances and corrode building, extend the longevity of building
Life, since lacquer has good adhesive force and freeze-thaw resistance property；Therefore it is particularly suitable for using in cold district.Lacquer tool
There is the advantages that various shapes, easy for construction.
However, existing lacquer often has the disadvantage that
1, after common lacquer decoration permanent color can thin out and color that is newly decorating become two kinds of face in contrast
Color；
2, common lacquer can crack fried skin phenomenon over time, and there are also hollow phenomenons；
3, common lacquer will appear to fall husky phenomenon over time；
4, common lacquer will appear drop serious phenomenon in construction；
5, common lacquer will appear whiting metachromatism over time.
Summary of the invention
Easily occur cracking technical problem to be solved by the present invention lies in existing lacquer caking ability is inadequate, after decoration, fall
The problem of sand and phenomena such as fading.
The present invention solves above-mentioned technical problem by the following technical programs:
A kind of lacquer, including following raw material by weight:
60-80 parts of water, 1-3 parts of cellulose, 1-3 parts of modified alta-mud, 120-150 parts of lacquer lotion, coalescing agent 6-8
Part, 0.6-1.6 parts of defoaming agent, 1-2 parts of fungicide, neutralize 0.5-1.6 parts of tone pitch agent, 4-8 parts of ethylene glycol, 600-800 parts of color sand.
Further, the lacquer includes following raw material by weight:
72 parts of water, 1.5 parts of cellulose, 1 part of modified alta-mud, 135 parts of lacquer lotion, 7 parts of coalescing agent, defoaming agent 1
Part, 1 part of fungicide, neutralize 1 part of tone pitch agent, 5 parts of ethylene glycol, 750 parts of color sand.
Further, the granularity of the color sand is divided into 20-40 mesh, 40-80 mesh and three kinds of 80-120 mesh, and granularity is 20-
The mass ratio of the color sand of 40 mesh, 40-80 mesh and 80-120 mesh is 1:8:6.
Further, the modified alta-mud includes 10-20 parts of bentonite, and 2-5 parts of polyacrylamide, 2-5 parts of ethylene glycol,
3-5 parts of zirconium English powder, 4-6 parts of pentaerythrite, 2-4 parts of ethyl acrylate, 10-20 parts of water.
Further, the method for preparing modified bentonite are as follows: (1) it is ethylene glycol is soluble in water, add polypropylene
Amide, bentonite, ethyl acrylate, polyethylene alcohol and water stir evenly, and obtain mixing suspension；
(2) bentonite, pentaerythrite are mixed evenly, zirconium English powder is then added, continuation is dried after mixing evenly, powder
Mixed-powder is obtained after broken；
(3) suspension in step (1) and the mixed-powder in step (2) are mixed and stirred for uniformly, drying, crushing
After processing, it is sieved and modified alta-mud is made.
Further, in the step (2), mixing time is 35-45 minutes, and mixing speed is 1000-1200 revs/min,
It is dried at 50-60 DEG C.
Further, in the step (1), prepared mixing suspension is stood 25-30 hours.
The preparation method of the lacquer includes:
(1) it adds water in a mixing bowl, lacquer lotion, fungicide and ethylene glycol is added under stirring, is mixed
Solution；
(2) cellulose and modified alta-mud are added into mixed solution, after mixing evenly, adds coalescing agent, defoaming
Agent and neutralization tone pitch agent, continuation obtain lacquer base paste after mixing evenly；
(3) the lacquer base paste prepared in step (2) is mixed with color sand, after mixing blowing, barrelling.
Further, in the step (1), speed of agitator is 250-280 revs/min, and mixing time is 25-40 minutes.
Compared with prior art, the present invention have it is following the utility model has the advantages that
It is added to modified alta-mud in this product, the application property of product can be changed, improve caking ability, prevents drop, increases
Add suspension, prevents color sand from sinking.Modified alta-mud and other raw materials are used in mixed way, color of light after lacquer decoration obtained
Distinct bright, fire prevention, waterproof, acid and alkali-resistance, anti-pollution, while non-toxic and tasteless colour-fast not cracking.
Bentonite is modified by using zirconium English powder, pentaerythrite and ethyl acrylate, improves bentonitic point
Effect is dissipated, increases suspension, prevents color sand from sinking.By that will have the mixing suspension of ethylene glycol, polyacrylamide to swollen
The mixed-powder of profit soil is wrapped up, and is modified to bentonite surface, is changed strand frame of the plurality of raw materials in mortar,
It is added in lacquer raw material, is remarkably improved the adhesion strength of lacquer, prevents drop.
Specific embodiment
Below with reference to embodiment, the invention will be further described.
Embodiment 1
A kind of lacquer, including following raw material by weight:
60 parts of water, 1 part of cellulose, 1 part of modified alta-mud, 120 parts of lacquer lotion, 6 parts of coalescing agent, defoaming agent 0.6
Part, 1 part of fungicide, neutralize 0.5 part of tone pitch agent, 4 parts of ethylene glycol, 600 parts of color sand.
Wherein, the granularity of the color sand is divided into three kinds of 20 mesh, 40 mesh and 80 mesh, and granularity is 20 mesh, 40 mesh and 80 purposes
The mass ratio of color sand is 1:8:6.
The modified alta-mud includes 10 parts of bentonite, and 2 parts of polyacrylamide, 2 parts of ethylene glycol, 3 parts of zirconium English powder, Ji Wusi
4 parts of alcohol, 2 parts of ethyl acrylate, 10 parts of water.
The method for preparing modified bentonite are as follows:
(1) ethylene glycol is soluble in water, it adds polyacrylamide, bentonite, ethyl acrylate, polyethylene alcohol and water and stirs
It mixes uniformly, obtains mixing suspension；Prepared mixing suspension is stood 25 hours.
(2) bentonite, pentaerythrite are mixed evenly, zirconium English powder is then added, continuation is dried after mixing evenly, powder
Mixed-powder is obtained after broken；Mixing time is 35 minutes, and mixing speed is 1000 revs/min, is dried at 50 DEG C.
(3) suspension in step (1) and the mixed-powder in step (2) are mixed and stirred for uniformly, drying, crushing
After processing, it is sieved and modified alta-mud is made.
The preparation method of the lacquer includes:
(1) it adds water in a mixing bowl, lacquer lotion, fungicide and ethylene glycol is added under stirring, is mixed
Solution；Speed of agitator is 250 revs/min, and mixing time is 25 minutes.
(2) cellulose and modified alta-mud are added into mixed solution, after mixing evenly, adds coalescing agent, defoaming
Agent and neutralization tone pitch agent, continuation obtain lacquer base paste after mixing evenly；
(3) the lacquer base paste prepared in step (2) is mixed with color sand, after mixing blowing, barrelling.
Embodiment 2
A kind of lacquer, including following raw material by weight:
80 parts of water, 3 parts of cellulose, 3 parts of modified alta-mud, 150 parts of lacquer lotion, 8 parts of coalescing agent, defoaming agent 1.6
Part, 2 parts of fungicide, neutralize 1.6 parts of tone pitch agent, 8 parts of ethylene glycol, 800 parts of color sand.
Wherein, the granularity of the color sand is divided into three kinds of 40 mesh, 80 mesh and 120 mesh, and granularity is 40 mesh, 80 mesh and 120 mesh
Color sand mass ratio be 1:8:6.
The modified alta-mud includes 20 parts of bentonite, and 5 parts of polyacrylamide, 5 parts of ethylene glycol, 5 parts of zirconium English powder, Ji Wusi
6 parts of alcohol, 4 parts of ethyl acrylate, 20 parts of water.
The method for preparing modified bentonite are as follows:
(1) ethylene glycol is soluble in water, it adds polyacrylamide, bentonite, ethyl acrylate, polyethylene alcohol and water and stirs
It mixes uniformly, obtains mixing suspension；Prepared mixing suspension is stood 30 hours.
(2) bentonite, pentaerythrite are mixed evenly, zirconium English powder is then added, continuation is dried after mixing evenly, powder
Mixed-powder is obtained after broken；Mixing time is 45 minutes, and mixing speed is 1200 revs/min, is dried at 60 DEG C.
(3) suspension in step (1) and the mixed-powder in step (2) are mixed and stirred for uniformly, drying, crushing
After processing, it is sieved and modified alta-mud is made.
The preparation method of the lacquer includes:
(1) it adds water in a mixing bowl, lacquer lotion, fungicide and ethylene glycol is added under stirring, is mixed
Solution；Speed of agitator is 280 revs/min, and mixing time is 40 minutes.
(2) cellulose and modified alta-mud are added into mixed solution, after mixing evenly, adds coalescing agent, defoaming
Agent and neutralization tone pitch agent, continuation obtain lacquer base paste after mixing evenly；
(3) the lacquer base paste prepared in step (2) is mixed with color sand, after mixing blowing, barrelling.
Embodiment 3
A kind of lacquer, including following raw material by weight:
72 parts of water, 1.5 parts of cellulose, 1 part of modified alta-mud, 135 parts of lacquer lotion, 7 parts of coalescing agent, defoaming agent 1
Part, 1 part of fungicide, neutralize 1 part of tone pitch agent, 5 parts of ethylene glycol, 750 parts of color sand.
Wherein, the granularity of the color sand is divided into three kinds of 30 mesh, 60 mesh and 100 mesh, and granularity is 30 mesh, 60 mesh and 100 mesh
Color sand mass ratio be 1:8:6.
The modified alta-mud includes 15 parts of bentonite, and 3 parts of polyacrylamide, 4 parts of ethylene glycol, 4 parts of zirconium English powder, Ji Wusi
5 parts of alcohol, 3 parts of ethyl acrylate, 15 parts of water.
The method for preparing modified bentonite are as follows:
(1) ethylene glycol is soluble in water, it adds polyacrylamide, bentonite, ethyl acrylate, polyethylene alcohol and water and stirs
It mixes uniformly, obtains mixing suspension；Prepared mixing suspension is stood 28 hours.
(2) bentonite, pentaerythrite are mixed evenly, zirconium English powder is then added, continuation is dried after mixing evenly, powder
Mixed-powder is obtained after broken；Mixing time is 40 minutes, and mixing speed is 1100 revs/min, is dried at 55 DEG C.
(3) suspension in step (1) and the mixed-powder in step (2) are mixed and stirred for uniformly, drying, crushing
After processing, it is sieved and modified alta-mud is made.
The preparation method of the lacquer includes:
(1) it adds water in a mixing bowl, lacquer lotion, fungicide and ethylene glycol is added under stirring, is mixed
Solution；Speed of agitator is 260 revs/min, and mixing time is 35 minutes.
(2) cellulose and modified alta-mud are added into mixed solution, after mixing evenly, adds coalescing agent, defoaming
Agent and neutralization tone pitch agent, continuation obtain lacquer base paste after mixing evenly；
(3) the lacquer base paste prepared in step (2) is mixed with color sand, after mixing blowing, barrelling.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although referring to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features.It is all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of lacquer, which is characterized in that including following raw material by weight:
60-80 parts of water, 1-3 parts of cellulose, 1-3 parts of modified alta-mud, 120-150 parts of lacquer lotion, 6-8 parts of coalescing agent,
0.6-1.6 parts of defoaming agent, 1-2 parts of fungicide, neutralize 0.5-1.6 parts of tone pitch agent, 4-8 parts of ethylene glycol, 600-800 parts of color sand.
2. a kind of lacquer according to claim 1, which is characterized in that including following raw material by weight:
It 72 parts of water, 1.5 parts of cellulose, 1 part of modified alta-mud, 135 parts of lacquer lotion, 7 parts of coalescing agent, 1 part of defoaming agent, kills
1 part of microbial inoculum, neutralize 1 part of tone pitch agent, 5 parts of ethylene glycol, 750 parts of color sand.
3. a kind of lacquer according to claim 1, which is characterized in that the granularity of the color sand is divided into 20-40 mesh, 40-
80 mesh and three kinds of 80-120 mesh, and it is 1:8:6 that granularity, which is the mass ratio of the color sand of 20-40 mesh, 40-80 mesh and 80-120 mesh,.
4. a kind of lacquer according to claim 1, which is characterized in that the modified alta-mud includes bentonite 10-20
Part, 2-5 parts of polyacrylamide, 2-5 parts of ethylene glycol, 3-5 parts of zirconium English powder, 4-6 parts of pentaerythrite, 2-4 parts of ethyl acrylate, water
10-20 parts.
5. a kind of lacquer according to claim 4, which is characterized in that the method for preparing modified bentonite are as follows: (1)
Ethylene glycol is soluble in water, it adds polyacrylamide, bentonite, ethyl acrylate, polyethylene alcohol and water and stirs evenly, obtain
Mixing suspension；
(2) bentonite, pentaerythrite are mixed evenly, zirconium English powder are then added, continuation is dried after mixing evenly, after crushing
Obtain mixed-powder；
(3) suspension in step (1) and the mixed-powder in step (2) are mixed and stirred for uniformly, drying, pulverization process
Afterwards, it is sieved and modified alta-mud is made.
6. a kind of lacquer according to claim 5, which is characterized in that in the step (2), mixing time 35-45
Minute, mixing speed is 1000-1200 revs/min, is dried at 50-60 DEG C.
7. a kind of lacquer according to claim 5, which is characterized in that in the step (1), prepared mixing is outstanding
Supernatant liquid stands 25-30 hours.
8. a kind of preparation method of the lacquer as described in claim 1-7 any one characterized by comprising
(1) it adds water in a mixing bowl, lacquer lotion, fungicide and ethylene glycol is added under stirring, obtains mixed solution；
(2) cellulose and modified alta-mud are added into mixed solution, after mixing evenly, add coalescing agent, defoaming agent and
Tone pitch agent is neutralized, continuation obtains lacquer base paste after mixing evenly；
(3) the lacquer base paste prepared in step (2) is mixed with color sand, after mixing blowing, barrelling.
9. the preparation method of lacquer according to claim 8, which is characterized in that in the step (1), speed of agitator is
250-280 revs/min, mixing time is 25-40 minutes.