CN108997866A - A kind of quick-dry type lacquer - Google Patents
A kind of quick-dry type lacquer Download PDFInfo
- Publication number
- CN108997866A CN108997866A CN201811038999.3A CN201811038999A CN108997866A CN 108997866 A CN108997866 A CN 108997866A CN 201811038999 A CN201811038999 A CN 201811038999A CN 108997866 A CN108997866 A CN 108997866A
- Authority
- CN
- China
- Prior art keywords
- parts
- lacquer
- agent
- defoaming agent
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to exterior wall surface decorative field of material technology, especially a kind of quick-dry type lacquer；Its mass parts composition is as follows: 10-30 parts of 15-20 parts of quartz sand, 15-20 parts of Hydroxylated acrylic resin, 5-15 parts of potassium base waterglass, 0.2-1.2 parts of thickener BS-888,0.1-0.2 parts of defoaming agent, butyl glycol ether or benzyl alcohol, 0.06-0.08 parts of auxiliary rheological agents, 2.4-2.8 parts of organosilicon moisture repellent, 0.15-0.45 parts of silane coupling agent, 0.2-0.8 parts of wetting agent, 30-50 parts of water；The shortcomings that dedicated thickener BS-888 of lacquer in the present invention is for spraying lacquer, complete substituted cellulose, overcomes cellulose degradable mildew, greatly improve that lacquer initial stage is water-fast, hardness, improve lacquer point water plate knot phenomenon, accelerates lacquer and do solid work speed, construction is smooth.
Description
Technical field
The present invention relates to exterior wall surface decorative field of material technology, especially a kind of quick-dry type lacquer.
Background technique
Lacquer is the coating that a kind of decorative effect exactly likes marble, granite.The main natural stone for using various colors
Powder is formulated, applied to the imitation stone effect of external wall, therefore also known as liquid stone.
Building after lacquer finishing has natural true natural colour, gives graceful, harmonious, serious beauty
Sense, is suitable for the indoor and outdoor decoration of all kinds of buildings.Especially decorated on curved-surface building object, it is vivid, there is a kind of recurrence
Natural effect.Lacquer has fire prevention, waterproof, acid and alkali-resistance, anti-pollution.It is nontoxic, tasteless, bonding force is strong, will never fade equal spies
Point, can effectively stop extraneous adverse circumstances to building corrode, extend the service life of building, due to lacquer have it is good
Adhesive force and freeze-thaw resistance property, therefore be suitble to use in cold district.
Majority lacquer at present, drying time is too slow, is influenced by temperature, influences to construct.Summary of the invention
The object of the present invention is to provide a kind of drying time it is short, small quick-dry type lacquer is influenced by temperature.
In order to solve the above technical problems, The technical solution adopted by the invention is as follows:
A kind of quick-dry type lacquer, mass parts composition are as follows: 15-20 parts of quartz sand, 15-20 parts of Hydroxylated acrylic resin, potassium
5-15 parts of base waterglass, 0.2-1.2 parts of thickener BS-888,0.1-0.2 parts of defoaming agent, butyl glycol ether or benzyl alcohol 10-30
Part, 0.06-0.08 parts of auxiliary rheological agents, 2.4-2.8 parts of organosilicon moisture repellent, 0.15-0.45 parts of silane coupling agent, wetting agent 0.2-
0.8 part, 30-50 parts of water.
Further, the hydroxy radical content in the Hydroxylated acrylic resin is 2%-4%, in the Hydroxylated acrylic resin
At least two hydroxyl values on every strand.
Further, the mass parts composition of the defoaming agent is as follows: 10-15 parts of methyl silicone oil, sodium tripolyphosphate 10-
12 parts, 72-76 parts of salt, 6-8 parts of mannitol, 3-5 parts of silica, the defoaming agent the preparation method is as follows: (1) in room temperature
It is lower to mix methyl silicone oil and silica, mixture is obtained, (2) are by the sodium tripolyphosphate, mannitol, salt etc. of crushing
Then mixing stirs evenly in the mixture in step (1) points, obtains defoaming agent.
Further, the wetting agent is total to modified polyorganosiloxanes, polyoxyethylene alkylphenol using organic fluoro- polyethers
Ether, polyoxyethylene aliphatic alcohol ether, one of polyoxyethylene polyoxypropylene block copolymer.
Further, the auxiliary rheological agents select polyamide wax powder auxiliary rheological agents, active castor oil organic derivative, castor
One of sesame oil organic derivative.
Further, the modulus of the potassium base waterglass is 2.0-4.0.
Further, mass parts composition is as follows: 16-18 parts of quartz sand, 16-18 parts of Hydroxylated acrylic resin, potassium Ji Shui
6-12 parts of glass, 0.5-1.0 parts of thickener BS-888,0.12-0.18 parts of defoaming agent, butyl glycol ether or benzyl alcohol 12-28
Part, 0.06-0.08 parts of auxiliary rheological agents, 2.5-2.7 parts of organosilicon moisture repellent, 0.2-0.4 parts of silane coupling agent, wetting agent 0.3-
0.5 part, 35-45 parts of water.
Further, mass parts composition is as follows: 18 parts of quartz sand, 18 parts of Hydroxylated acrylic resin, potassium base waterglass 10
It is part, 0.7 part of thickener BS-888,0.15 part of defoaming agent, butyl glycol ether or 20 parts of benzyl alcohol, 0.07 part of auxiliary rheological agents, organic
2.5 parts of silicon hydrophober, 0.3 part of silane coupling agent, 0.5 part of wetting agent, 40 parts of water.
It is using the beneficial effect of technical solution of the present invention:
1, for the dedicated thickener BS-888 of lacquer in the present invention for spraying lacquer, complete substituted cellulose overcomes fibre
The shortcomings that tieing up plain degradable mildew, greatly improves that lacquer initial stage is water-fast, hardness, improves lacquer point water plate knot phenomenon, accelerates
Lacquer does solid work speed, and construction is smooth.
2, the general OH content of Hydroxylated acrylic resin in the present invention is between 2%~4%, and then curing agent cost increases too much
Add.Due to containing largely with the hydroxyl of stronger reactivity, at normal temperature the potassium silicate meeting in potassium base waterglass in the present invention
Slow reaction occurs therewith, in 70 °C or more high temperature fast reactions, improves rate of drying quickly, forms continuous paint film；?
When stone patch true with lacquer production finished product porcelain tendre, as long as production temperature is transferred to 70 to 100 °C, 3-10min is close to real
It is dry, it can quickly improve production efficiency.
Specific embodiment
The following examples can make those skilled in the art that the present invention be more fully understood, but these embodiments are not
Limiting the scope of the invention." one embodiment " or " embodiment " referred to herein, which refers to, may be included in the present invention at least
A particular feature, structure, or characteristic in one implementation.In the present specification different places occur " in one embodiment
In " the same embodiment not is referred both to, nor the individual or selective embodiment mutually exclusive with other embodiments.
Embodiment 1
A kind of quick-dry type lacquer, mass parts composition are as follows: 15 parts of quartz sand, 15 parts of Hydroxylated acrylic resin, potassium base water glass
10 parts of 5 parts of glass, 0.2 part of thickener BS-888,0.1 part of defoaming agent, butyl glycol ether or benzyl alcohol, have 0.06 part of auxiliary rheological agents
2.4 parts of machine silicon hydrophober, 0.15 part of silane coupling agent, 0.2 part of wetting agent, 30 parts of water.
Wherein, the hydroxy radical content in Hydroxylated acrylic resin is 2%, every strand in Hydroxylated acrylic resin up to
It is few that there are two hydroxyl values.
Wherein, defoaming agent mass parts composition it is as follows: 10 parts of methyl silicone oil, 10 parts of sodium tripolyphosphate, 72 parts of salt,
6 parts of mannitol, 3 parts of silica, the defoaming agent the preparation method is as follows: (1) at room temperature by methyl silicone oil and two
Silica mixes, and obtains mixture, and (2) mix sodium tripolyphosphate, mannitol, salt of crushing etc., then and in step (1)
Mixture in point stir evenly, obtain defoaming agent.
Wherein, wetting agent is total to modified polyorganosiloxanes using organic fluoro- polyethers.
Wherein, auxiliary rheological agents select polyamide wax powder auxiliary rheological agents.
Wherein, the modulus of potassium base waterglass is 2.0.
Embodiment 2
A kind of quick-dry type lacquer, mass parts composition are as follows: 16 parts of quartz sand, 16 parts of Hydroxylated acrylic resin, potassium base water glass
12 parts of 6 parts of glass, 0.5 part of thickener BS-888,0.12 part of defoaming agent, butyl glycol ether or benzyl alcohol, 0.06 part of auxiliary rheological agents,
2.5 parts of organosilicon moisture repellent, 0.2 part of silane coupling agent, 0.3 part of wetting agent, 35 parts of water.
Wherein, the hydroxy radical content in Hydroxylated acrylic resin is 2%, every strand in the Hydroxylated acrylic resin
On at least two hydroxyl values.
Wherein, defoaming agent mass parts composition it is as follows: 10 parts of methyl silicone oil, 10 parts of sodium tripolyphosphate, 72 parts of salt,
6 parts of mannitol, 3 parts of silica, the defoaming agent the preparation method is as follows: (1) at room temperature by methyl silicone oil and two
Silica mixes, and obtains mixture, and (2) mix sodium tripolyphosphate, mannitol, salt of crushing etc., then and in step (1)
Mixture in point stir evenly, obtain defoaming agent.
Wherein, wetting agent is total to modified polyorganosiloxanes using organic fluoro- polyethers.
Wherein, auxiliary rheological agents select polyamide wax powder auxiliary rheological agents.
Wherein, the modulus of potassium base waterglass is 2.0.
Embodiment 3
A kind of quick-dry type lacquer, mass parts composition are as follows: 18 parts of quartz sand, 18 parts of Hydroxylated acrylic resin, potassium base water glass
20 parts of 10 parts of glass, 0.7 part of thickener BS-888,0.15 part of defoaming agent, butyl glycol ether or benzyl alcohol, 0.07 part of auxiliary rheological agents,
2.5 parts of organosilicon moisture repellent, 0.3 part of silane coupling agent, 0.5 part of wetting agent, 40 parts of water.
Wherein, the hydroxy radical content in Hydroxylated acrylic resin is 3%, every strand in the Hydroxylated acrylic resin
On at least two hydroxyl values.
Wherein, defoaming agent mass parts composition it is as follows: 12 parts of methyl silicone oil, 11 parts of sodium tripolyphosphate, 75 parts of salt,
7 parts of mannitol, 4 parts of silica, the defoaming agent the preparation method is as follows: (1) at room temperature by methyl silicone oil and two
Silica mixes, and obtains mixture, and (2) mix sodium tripolyphosphate, mannitol, salt of crushing etc., then and in step (1)
Mixture in point stir evenly, obtain defoaming agent.
Wherein, wetting agent is total to modified polyorganosiloxanes using organic fluoro- polyethers.
Wherein, auxiliary rheological agents select polyamide wax powder auxiliary rheological agents.
Wherein, the modulus of potassium base waterglass is 3.0.
Embodiment 4
A kind of quick-dry type lacquer, mass parts composition are as follows: 18 parts of quartz sand, 18 parts of Hydroxylated acrylic resin, potassium base water glass
28 parts of 12 parts of glass, 1.0 parts of thickener BS-888,0.18 part of defoaming agent, butyl glycol ether or benzyl alcohol, 0.08 part of auxiliary rheological agents,
2.7 parts of organosilicon moisture repellent, 0.4 part of silane coupling agent, 0.5 part of wetting agent, 45 parts of water.
Wherein, the hydroxy radical content in Hydroxylated acrylic resin is 4%, every strand in the Hydroxylated acrylic resin
On at least two hydroxyl values.
Wherein, defoaming agent mass parts composition it is as follows: 15 parts of methyl silicone oil, 12 parts of sodium tripolyphosphate, 76 parts of salt,
8 parts of mannitol, 5 parts of silica, the defoaming agent the preparation method is as follows: (1) at room temperature by methyl silicone oil and two
Silica mixes, and obtains mixture, and (2) mix sodium tripolyphosphate, mannitol, salt of crushing etc., then and in step (1)
Mixture in point stir evenly, obtain defoaming agent.
Wherein, wetting agent uses polyoxyethylated alkyl phenol, polyoxyethylene aliphatic alcohol ether.
Wherein, auxiliary rheological agents select active castor oil organic derivative.
Wherein, the modulus of potassium base waterglass is 4.0.
Embodiment 5
A kind of quick-dry type lacquer, mass parts composition are as follows: 20 parts of quartz sand, 20 parts of Hydroxylated acrylic resin, potassium base water glass
30 parts of 15 parts of glass, 1.2 parts of thickener BS-888,0.2 part of defoaming agent, butyl glycol ether or benzyl alcohol, 0.08 part of auxiliary rheological agents,
2.8 parts of organosilicon moisture repellent, 0.45 part of silane coupling agent, 0.8 part of wetting agent, 50 parts of water.
Wherein, the hydroxy radical content in Hydroxylated acrylic resin is 4%, every strand in the Hydroxylated acrylic resin
On at least two hydroxyl values.
Wherein, defoaming agent mass parts composition it is as follows: 15 parts of methyl silicone oil, 12 parts of sodium tripolyphosphate, 76 parts of salt,
8 parts of mannitol, 5 parts of silica, the defoaming agent the preparation method is as follows: (1) at room temperature by methyl silicone oil and two
Silica mixes, and obtains mixture, and (2) mix sodium tripolyphosphate, mannitol, salt of crushing etc., then and in step (1)
Mixture in point stir evenly, obtain defoaming agent.
Wherein, wetting agent uses polyoxyethylene polyoxypropylene block copolymer.
Wherein, auxiliary rheological agents select castor oil organic derivative.
Wherein, the modulus of potassium base waterglass is 4.0.
Embodiment 6
Embodiment 6 and the difference of embodiment 3 are: embodiment 6 uses common Commercial antifoam agent.
Embodiment 7
Embodiment 7 and the difference of embodiment 3 are: the thickener in embodiment 7 selects HY-305 polyurethane associative thickener.
Embodiment 8
Embodiment 8 and the difference of embodiment 3 are: thickener selects HY-305 polyurethane associative thickener in embodiment 8, and
And use common Commercial antifoam agent.
Embodiment 9
Embodiment 9 is common commercially available quick-dry type lacquer.
Quick-dry type lacquer in embodiment 1-7 is made using conventional method.
| Detection project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Embodiment 6 | Embodiment 7 | Embodiment 8 | Embodiment 9 |
| Low-temperature storage stability, 3 times | Without agglomeration | Without agglomeration | Without agglomeration | Without agglomeration | Without agglomeration | There is agglomeration | There is agglomeration | There is agglomeration | There is agglomeration |
| Drying time (surface drying) min | 42 | 45 | 38 | 43 | 45 | 60 | 65 | 100 | 66 |
| Weatherability (96h) | It is excellent | It is excellent | It is excellent | It is excellent | It is excellent | Generally | Generally | Generally | Generally |
| Alkali resistance (96h) | It is without exception | It is without exception | It is without exception | It is without exception | It is without exception | Generally | Generally | Generally | Generally |
| Water resistance (96h) | It is without exception | It is without exception | It is without exception | It is without exception | It is without exception | Generally | Generally | Generally | Generally |
| Standard state viscosity intensity (MPa) | 1.21 | 1.16 | 1.20 | 1.25 | 1.18 | 0.72 | 0.75 | 0.26 | 0.39 |
| Adhesion | It is excellent | It is excellent | It is excellent | It is excellent | It is excellent | Generally | Generally | Generally | Generally |
| Thermal storage stability | It is without exception | It is without exception | It is without exception | It is without exception | It is without exception | There is agglomeration | There is agglomeration | There is agglomeration | There is agglomeration |
It will be apparent to an ordinarily skilled person in the art that: the purpose of the present invention is: 1, the lacquer in the present invention is special
With thickener BS-888 for spraying lacquer, complete substituted cellulose, the shortcomings that overcoming cellulose degradable mildew, significantly
Raising lacquer initial stage is water-fast, hardness, improves lacquer point water plate knot phenomenon, accelerates lacquer and does solid work speed, construction is smooth.
2, the general OH content of Hydroxylated acrylic resin in the present invention is between 2%~4%, and then curing agent cost increases too much
Add.Due to containing largely with the hydroxyl of stronger reactivity, at normal temperature the potassium silicate meeting in potassium base waterglass in the present invention
Slow reaction occurs therewith, in 70 °C or more high temperature fast reactions, improves rate of drying quickly, forms continuous paint film；?
When stone patch true with lacquer production finished product porcelain tendre, as long as production temperature is transferred to 70 to 100 °C, 3-10min is close to real
It is dry, it can quickly improve production efficiency.
Taking the above-mentioned ideal embodiment according to the present invention as inspiration, through the above description, relevant staff is complete
Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention' entirely.It is all in essence of the invention
Within mind and principle, any modification, equivalent substitution, improvement and etc. done be should all be included in the protection scope of the present invention.This
The technical scope of item invention is not limited to the contents of the specification, it is necessary to its technology is determined according to scope of the claims
Property range.
Claims (8)
1. a kind of quick-dry type lacquer, it is characterised in that: its mass parts composition is as follows: 15-20 parts of quartz sand, hydroxy acrylic acid tree
15-20 parts of rouge, 5-15 parts of potassium base waterglass, 0.2-1.2 parts of thickener BS-888,0.1-0.2 parts of defoaming agent, butyl glycol ether
Or 10-30 parts of benzyl alcohol, 0.06-0.08 parts of auxiliary rheological agents, 2.4-2.8 parts of organosilicon moisture repellent, silane coupling agent 0.15-0.45
Part, 0.2-0.8 parts of wetting agent, 30-50 parts of water.
2. a kind of quick-dry type lacquer according to claim 1, it is characterised in that: the hydroxyl in the Hydroxylated acrylic resin
Base content is 2%-4%, at least two hydroxyl values on every strand in the Hydroxylated acrylic resin.
3. a kind of quick-dry type lacquer according to claim 1, it is characterised in that: the mass parts composition of the defoaming agent is such as
Under: 10-15 parts of methyl silicone oil, 10-12 parts of sodium tripolyphosphate, 72-76 parts of salt, 6-8 parts of mannitol, silica 3-5
Part, the defoaming agent the preparation method is as follows: (1) at room temperature mixes methyl silicone oil and silica, mixed
Object, (2) mix sodium tripolyphosphate, mannitol, salt of crushing etc., then stir evenly, obtain in the mixture in step (1) points
To defoaming agent.
4. a kind of flexible real stone paint according to claim 1, it is characterised in that: the wetting agent uses organic fluoro- polyethers
Modified polyorganosiloxanes, polyoxyethylated alkyl phenol altogether, polyoxyethylene aliphatic alcohol ether, polyoxyethylene polyoxypropylene block copolymerization
One of object.
5. a kind of flexible real stone paint according to claim 1, it is characterised in that: the auxiliary rheological agents select polyamide wax powder
One of body auxiliary rheological agents, active castor oil organic derivative, castor oil organic derivative.
6. a kind of flexible real stone paint according to claim 1, it is characterised in that: the modulus of the potassium base waterglass is 2.0-
4.0。
7. a kind of flexible real stone paint according to claim 1, it is characterised in that: its mass parts composition is as follows: quartz sand 16-
18 parts, 16-18 parts of Hydroxylated acrylic resin, 6-12 parts of potassium base waterglass, 0.5-1.0 parts of thickener BS-888, defoaming agent
12-28 parts of 0.12-0.18 parts, butyl glycol ether or benzyl alcohol, 0.06-0.08 parts of auxiliary rheological agents, organosilicon moisture repellent 2.5-2.7
Part, 0.2-0.4 parts of silane coupling agent, 0.3-0.5 parts of wetting agent, 35-45 parts of water.
8. a kind of flexible real stone paint according to claim 7, it is characterised in that: its mass parts composition is as follows: quartz sand 18
Part, 18 parts of Hydroxylated acrylic resin, 10 parts of potassium base waterglass, 0.7 part of thickener BS-888,0.15 part of defoaming agent, ethylene glycol fourth
20 parts of ether or benzyl alcohol, 0.07 part of auxiliary rheological agents, 2.5 parts of organosilicon moisture repellent, 0.3 part of silane coupling agent, 0.5 part of wetting agent,
40 parts of water.