CN108485427A - A kind of high texture imitates sandstone coating and preparation method thereof - Google Patents
A kind of high texture imitates sandstone coating and preparation method thereof Download PDFInfo
- Publication number
- CN108485427A CN108485427A CN201810229112.2A CN201810229112A CN108485427A CN 108485427 A CN108485427 A CN 108485427A CN 201810229112 A CN201810229112 A CN 201810229112A CN 108485427 A CN108485427 A CN 108485427A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- imitates
- high texture
- sandstone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high texture to imitate sandstone coating, including following components and parts by weight content:10 20 parts of silicone acrylic emulsion, 10 15 parts of natural colour sand, 24 parts of pigment of reflection, 35 parts of ceramic microsphere, 46 parts of reflective insulation powder, 12 parts of calcium formate, 1 1.5 parts of bentonite, 0.5 1 parts of lignocellulosic, 23 parts of rubber powder, 45 parts of coalescents, 57 parts of dispersant, 45 parts of antifoaming agent, 23 parts of thickener, 20 30 parts of deionized water.Compared with prior art, coating of the present invention mixes natural colour sand with ceramic microsphere progress grading, is dispersed in coating, enhances sandstone texture, the reflection pigment and reflective insulation powder of addition enhance the reflecting feel of coating.The addition of calcium formate, bentonite, lignocellulosic and rubber powder, improve the compatibility of the organic components such as silicone acrylic emulsion and inorganic component, the adhesion strength for improving coating ensures, in the case where adding a large amount of inorganic component, still to keep preferable impact resistance.
Description
Technical field
The present invention relates to a kind of stone-like coatings, and sandstone coating and preparation method thereof is imitated more particularly, to a kind of high texture.
Background technology
Stone-like coating is widely popularized on building materials industry exterior wall interior wall, and stone-like coating is also known as lacquer, is
It is equipped with the decorating inner and external walls coating that lithotome pulverized particles are main raw material(s) with synthetic resin emulsion.Lacquer China most
It early appears in the 1980s, the annual project for selecting lacquer can be more and more at present, although stone-like coating is with imitative natural
Based on stone material, its color is imitated, is also only limited to carry out construction usage at project scene, due to site environment (scaffold
Build, weather, basal plane) etc. reasons, live stone-like coating using when will appear floating phenomena such as.Present stone-like coating in toning and
True stone material color can only be imitated in work progress, but the smoothness of the natural texture and surface for some stone materials
It can not be imitated, some high-grade stone markets cannot be promoted due to this.
Chinese patent CN104974621A discloses a kind of environment-friendly water-soluble and imitates sandstone decorative paint and its application, by setting
Fat synthetic emulsion is mixed to form with natural colour sand;Imitative sandstone decorative paint is for manufacturing imitative sandstone decorative paint production board, method
It is as follows:Stone base paint special is imitated in roller coating first on cladding production board, forms prime coat;Trowelling or spraying are imitated sandstone decoration and are applied
Material forms first layer and imitates sandstone decorative coveringn;It carries out spraying again or trowelling imitates sandstone decorative paint, form making for setting
Type forms the second layer and imitates sandstone decorative coveringn;Sandstone decorative coveringn surface roller coating profession protective topcoat is imitated in the second layer, is formed and is protected
Sheath.But sandstone is laborious on building occupancy, and technique is cumbersome, and costly, the quality for imitating sandstone coating is not fully up to expectations for price.
Invention content
The purpose of the present invention is exactly to solve the above-mentioned problems and provides a kind of high texture and imitate sandstone coating and its preparation side
Method.
The purpose of the present invention is achieved through the following technical solutions:
A kind of imitative sandstone coating of high texture, including following components and parts by weight content:10-20 parts of silicone acrylic emulsion, natural color
10-15 parts of sand, 2-4 parts of pigment of reflection, 3-5 parts of ceramic microsphere, 4-6 parts of reflective insulation powder, 1-2 parts of calcium formate, bentonite 1-1.5
Part, 0.5-1 parts of lignocellulosic, 2-3 parts of rubber powder, 4-5 parts of coalescents, 5-7 parts of dispersant, 4-5 parts of antifoaming agent, thickener 2-
3 parts, 20-30 parts of deionized water.
The natural colour sand granularity is selected from 50-70 mesh.
The reflection pigment is titanium dioxide.
The reflective insulation powder is any one or more in aluminium oxide, iron oxide or copper oxide.
The grain size of the ceramic microsphere is 20-40 mesh.
The rubber powder is cinnamic acrylic ester or VAE rubber powders.
The coalescents be propandiol butyl ether, propylene glycol methyl ether acetate, butyl glycol ether or propylene glycol phenylate one
Kind is a variety of.
The dispersant is polycarboxylate sodium's anionic dispersing agents.
The thickener is polyurethanes thickener, and the antifoaming agent is metal soap antifoaming agent.
A kind of high texture imitates the preparation method of sandstone coating, includes the following steps:
(1) natural colour sand, reflection pigment, ceramic microsphere and reflective insulation powder are uniformly mixed;
(2) silicone acrylic emulsion, lignocellulosic and rubber powder are uniformly mixed;
(3) mixture that step (1) and step (2) obtain is mixed, and sequentially add calcium formate, bentonite, at
Film auxiliary agent, dispersant, antifoaming agent, thickener and deionized water are dispersed with stirring uniformly, obtain product.
Compared with prior art, it is 20- by natural colour sand and grain size that granularity is 50-70 mesh in formulation for coating material of the present invention
The ceramic microsphere of 40 mesh carries out grading mixing, and the ceramic microsphere of small particle contributes to natural colour sand point with after natural colour sand doping
It is dispersed in coating, enhances sandstone texture.The reflection pigment and reflective insulation powder of this formula addition, enhance the gloss of coating
Sense, reflection pigment titanium white main component are the white pigment of titanium dioxide, are a kind of polycrystalline compounds, and particle is arranged in rule
Row have grid system, are added into this coating together with reflective insulation powder, significantly improve the quality gloss of coating.And it is
Inorganic matter can be mixed well with ceramic microsphere and natural colour sand.Calcium formate, bentonite, lignocellulosic and rubber powder add
Add, improve the compatibility of the organic components such as silicone acrylic emulsion and inorganic component, improve the adhesion strength of coating, ensures adding
In the case of a large amount of inorganic component, coating still keeps preferable impact resistance, improves product quality.
Specific implementation mode
With reference to specific embodiment, the present invention is described in detail, but should be in no way restrictive.
Embodiment 1
A kind of imitative sandstone coating of high texture, including following components and content:It is silicone acrylic emulsion 10kg, natural colour sand 10kg, anti-
Penetrate pigment 2kg, ceramic microsphere 3kg, reflective insulation powder 4kg, calcium formate 1kg, bentonite 1kg, lignocellulosic 0.5kg, rubber powder
2kg, coalescents 4kg, dispersant 5kg, antifoaming agent 4kg, thickener 2kg, deionized water 20kg.
Wherein, natural colour sand granularity is in 50-70 mesh, and for the grain size of ceramic microsphere in 20-40 mesh, reflection pigment is titanium dioxide,
Reflective insulation powder is aluminium oxide, and rubber powder is cinnamic acrylic ester, and coalescents are propandiol butyl ether, and dispersant is polycarboxylic acids
Sodium salt anionic dispersing agents, thickener are polyurethanes thickener, and antifoaming agent is metal soap antifoaming agent.
When specific preparation, steps are as follows:
(1) natural colour sand, reflection pigment, ceramic microsphere and reflective insulation powder are uniformly mixed;
(2) silicone acrylic emulsion, lignocellulosic and rubber powder are uniformly mixed;
(3) mixture that step (1) and step (2) obtain is mixed, and sequentially add calcium formate, bentonite, at
Film auxiliary agent, dispersant, antifoaming agent, thickener and deionized water are dispersed with stirring uniformly, obtain product.
Embodiment 2
A kind of imitative sandstone coating of high texture, including following components and content:It is silicone acrylic emulsion 15kg, natural colour sand 15kg, anti-
Penetrate pigment 4kg, ceramic microsphere 5kg, reflective insulation powder 6kg, calcium formate 2kg, bentonite 1.5kg, lignocellulosic 1kg, rubber powder
3kg, coalescents 5kg, dispersant 7kg, antifoaming agent 5kg, thickener 3kg, deionized water 30kg.Wherein, natural colour sand granularity
In 50-70 mesh, for the grain size of ceramic microsphere in 20-40 mesh, reflection pigment is titanium dioxide, and reflective insulation powder is iron oxide, and rubber powder is
VAE rubber powders, coalescents are propandiol butyl ether, and dispersant is polycarboxylate sodium's anionic dispersing agents, and thickener is polyurethanes
Thickener, antifoaming agent are metal soap antifoaming agent.
The preparation method is the same as that of Example 1.
Embodiment 3
A kind of imitative sandstone coating of high texture, including following components and content:It is silicone acrylic emulsion 17kg, natural colour sand 13kg, anti-
Penetrate pigment 3kg, ceramic microsphere 4.2kg, reflective insulation powder 4.8kg, calcium formate 1.7kg, bentonite 1.3kg, lignocellulosic
0.9kg, rubber powder 2.5kg, coalescents 4.5kg, dispersant 6.3kg, antifoaming agent 4.7kg, thickener 2.5kg, deionized water
28kg.Wherein, natural colour sand granularity is in 50-70 mesh, and for the grain size of ceramic microsphere in 20-40 mesh, reflection pigment is titanium dioxide, reflection
Heat-insulating powder is iron oxide, and rubber powder is cinnamic acrylic ester, and coalescents are propandiol butyl ether, and dispersant is polycarboxylate sodium
Anionic dispersing agents, thickener are polyurethanes thickener, and antifoaming agent is metal soap antifoaming agent.
The preparation method is the same as that of Example 1.
Comparative example 1
Ceramic microsphere is not added, remaining is same as Example 1.
Comparative example 2
Reflection pigment and reflective insulation powder are not added, remaining is same as Example 1.
The product obtained by embodiment 1-3 and comparative example 1-3 is detected respectively by standard JG/T24-2000, part
The results are shown in Table 1.As shown in Table 1, this coating can be significantly improved using ceramic microsphere, reflection pigment and reflective insulation powder
Energy.
1 embodiment 1-3 of table and comparative example 1-3 testing results
☆ number indicates product fine at degree.
Claims (10)
1. a kind of high texture imitates sandstone coating, which is characterized in that including following components and parts by weight content:Silicone acrylic emulsion 10-20
It is part, 10-15 parts of natural colour sand, 2-4 parts of pigment of reflection, 3-5 parts of ceramic microsphere, 4-6 parts of reflective insulation powder, 1-2 parts of calcium formate, swollen
Moisten 1-1.5 parts of soil, 0.5-1 parts of lignocellulosic, 2-3 parts of rubber powder, 4-5 parts of coalescents, 5-7 parts of dispersant, antifoaming agent 4-5
Part, 2-3 parts of thickener, 20-30 parts of deionized water.
2. a kind of high texture according to claim 1 imitates sandstone coating, which is characterized in that the natural colour sand granularity is selected from
50-70 mesh.
3. a kind of high texture according to claim 1 imitates sandstone coating, which is characterized in that the reflection pigment is titanium white
Powder.
4. a kind of high texture according to claim 1 imitates sandstone coating, which is characterized in that the reflective insulation powder is oxidation
Any one or more in aluminium, iron oxide or copper oxide.
5. a kind of high texture according to claim 1 imitates sandstone coating, which is characterized in that the grain size of the ceramic microsphere is
20-40 mesh.
6. a kind of high texture according to claim 1 imitates sandstone coating, which is characterized in that the rubber powder is styrene-the third
Olefin(e) acid ester or VAE rubber powders.
7. a kind of high texture according to claim 1 imitates sandstone coating, which is characterized in that the coalescents are propylene glycol
Butyl ether, propylene glycol methyl ether acetate, butyl glycol ether or propylene glycol phenylate it is one or more.
8. a kind of high texture according to claim 1 imitates sandstone coating, which is characterized in that the dispersant is sodium polycarboxylate
Salt anionic dispersant.
9. a kind of high texture according to claim 1 imitates sandstone coating, which is characterized in that the thickener is polyurethanes
Thickener, the antifoaming agent are metal soap antifoaming agent.
10. a kind of a kind of high texture as described in claim 1 imitates the preparation method of sandstone coating, which is characterized in that including with
Lower step:
(1) natural colour sand, reflection pigment, ceramic microsphere and reflective insulation powder are uniformly mixed;
(2) silicone acrylic emulsion, lignocellulosic and rubber powder are uniformly mixed;
(3) mixture that step (1) and step (2) obtain is mixed, and sequentially adds calcium formate, bentonite, film forming and helps
Agent, dispersant, antifoaming agent, thickener and deionized water are dispersed with stirring uniformly, obtain product.