CN101798474A - Multi-angle reflect type coating and preparation method thereof - Google Patents
Multi-angle reflect type coating and preparation method thereof Download PDFInfo
- Publication number
- CN101798474A CN101798474A CN200910021056A CN200910021056A CN101798474A CN 101798474 A CN101798474 A CN 101798474A CN 200910021056 A CN200910021056 A CN 200910021056A CN 200910021056 A CN200910021056 A CN 200910021056A CN 101798474 A CN101798474 A CN 101798474A
- Authority
- CN
- China
- Prior art keywords
- parts
- type coating
- boraxs
- angle reflect
- reflect type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a multi-angle reflect type coating. The coating comprises the following components in parts by weight: 100 parts of quartz sand, 25-57.3 parts of carbonate and 22.3-80 parts of filler composite, wherein the carbonate comprises one or any combination of sodium carbonate, potassium carbonate and calcium carbonate; and the filler composite comprises the following components in parts by weight: 11 parts of miniumite, 3 parts of borax, 1.3 parts of copper cuttings, 3.7 parts of cuprous oxide, 1.3 parts of iron cuttings and 2.0 parts of tin powder, or 4 parts of miniumite, 4 parts of borax, 7 parts of copper cuttings, 11 parts of cuprous oxide and 4.0 parts of stannous oxide. The invention solves the technical problems that the background art has monotonous decorative effect, poor texture and lower durability. The coating of the invention has the advantages that various flash colors can be generated under illumination, the visual effect is obvious; the production process is simple, the construction cost is appropriate, the application range is wide; and the Environmental friend and chemical stability are good, etc.
Description
Technical field
The present invention relates to a kind of architectural decoration coating material and preparation method thereof, be specifically related to a kind of multi-angle reflect type coating and preparation method thereof.
Background technology
Along with human living standard's raising, people have had higher requirement to building decoration visual effect and life-span.Decorative paint is a kind of important material of construction in building decoration, it all has importantly influence to building decoration visual effect and life-span, and the colo(u)r coating that existing coating is generally whitewash or has single color, these coating all exist decorative effect single, texture is poor, problems such as poor durability are difficult to satisfy the demand of high-grade decorative engineering.Though the metal curtain wall decorative effect of Chu Xianing was better in recent years, good endurance, it involves great expense, and has only in the minority engineering and is just used, and is difficult to promote.
Summary of the invention
The object of the present invention is to provide a kind of multi-angle reflect type coating and preparation method thereof, it is single that it has solved in the background technology decorative effect, the technical problem of the relatively poor and poor durability of texture.
Technical scheme of the present invention is:
A kind of multi-angle reflect type coating with the weight part metering, comprises 100 parts of quartz sands, 25～57.3 parts of carbonate and 22.3～80 parts of fill compositions.
Above-mentioned carbonate comprises the arbitrary of soda ash, salt of wormwood, lime carbonate and combination thereof.
Above-mentioned fill composition comprises 11 parts of red leads, 3 parts of boraxs, 1.3 parts of copper scales, 3.7 parts of Red copper oxide, 1.3 parts of iron filings and 2.0 parts of glass puttys or 4 parts of red leads, 4 parts of boraxs, 7 parts of copper scales, 11 parts of Red copper oxide and 4.0 parts of tin protoxides with weight part metering.
Above-mentioned fill composition comprises 15 parts of feldspars, 8 parts of fluorites, 14 parts of potassiumchromates and 12 parts of barium sulfate or 22 parts of feldspars, 10 parts of fluorites, 12 parts of tin protoxides, 6 parts of potassiumchromates, 12 parts of Manganse Dioxide and 18 parts of sodium sulfate with weight part metering.
Above-mentioned fill composition comprises 6 parts of red leads, 4 parts of boraxs, 8 parts of fluorites, 4 parts of nitre, 4 parts of ferric oxide, 2 parts of tin protoxides, 4 parts of barium sulfate, 8 parts of bone ashes, 0.00025 part of cobalt oxide and 1.0 parts of white arsenics or 6 parts of red leads, 4 parts of boraxs, 8 parts of fluorites, 4 parts of nitre, 4 parts of ferric oxide, 4 parts of Manganse Dioxide, 4 parts of barium sulfate, 8 parts of bone ashes, 0.00025 part of cobalt oxide, 0.25 part of sulphur and 1.0 parts of white arsenics with weight part metering.
Above-mentioned fill composition comprises 0.45 part of borax, 9.1 parts of feldspars, 0.63 part of Manganse Dioxide, 4.6 parts of sodium sulfate and 0.45 part of barium sulfate or 2.0 parts of boraxs, 3.0 parts of feldspars, 12.5 parts of sodium aluminum fluorides, 6.0 parts of grey feldspars and 0.28 part of copper sulfate with weight part metering.
Above-mentioned fill composition comprises 2.0 parts of red leads, 2.0 parts of boraxs, 5.0 parts of nitre, 4.5 parts of Manganse Dioxide oxygen, 8 parts of bone ashes and 7 parts of sodium aluminum fluorides or 50 parts of red leads, 14 parts of boraxs, 10 parts of nitre, 2.6 parts of Manganse Dioxide oxygen and 0.006 part of gold trichloride with weight part metering.
Above-mentioned tackiness agent is construction cement, polyvinyl acetate emulsion, true mineral varnish tackiness agent, vinylformic acid, silicon third and styrene-acrylate emulsion type coating glue stick.
A kind of preparation method of multi-angle reflect type coating, its special character is that this method may further comprise the steps:
1] selects the material of preparation coating and the proportioning of definite each component for use;
2] to above-mentioned steps 1] in material mixing, and pulverize evenly to particle diameter below 5 millimeters; And cool shine or artificial seasoning to the seasoning state.
3] be heated to 1150～1600 ℃ in the dry back placement container and make its fusion;
4] material after the fusion is cooled to normal temperature;
5] crush and screen to particle diameter 0.5～5mm standby to cooled material.
6] material after crushing and screening adds adhesive in the described ratio of claim 1, and mixing promptly gets this multi-angle reflect type coating.
Advantage of the present invention is as follows:
1, this coating can produce multiple flash of light color under illumination, and visual effect is obvious;
2, the decoration defencive function is complete: have decoration, waterproof, fire prevention, sun-proof comprehensive function;
3, production technique is simple, and it is suitable to build construction cost, has wide range of applications;
4, since this coating by SiO
2Form Deng materials processing, raw material is easy to get and has excellent weather resistance;
5, the feature of environmental protection, chemical stability are good: this coating is nontoxic, tasteless, non-stimulated, pollution-free.
Embodiment
A kind of multi-angle reflect type coating with the weight part metering, comprises 100 parts of quartz sands, 25～57.3 parts of carbonate and 22.3～80 parts of fill compositions.Carbonate comprises the arbitrary of soda ash, salt of wormwood, lime carbonate and combination thereof.Fill composition comprises 11 parts of red leads, 3 parts of boraxs, 1.3 parts of copper scales, 3.7 parts of Red copper oxide, 1.3 parts of iron filings and 2.0 parts of glass puttys or 4 parts of red leads, 4 parts of boraxs, 7 parts of copper scales, 11 parts of Red copper oxide and 4.0 parts of tin protoxides with weight part metering.Fill composition comprises 15 parts of feldspars, 8 parts of fluorites, 14 parts of potassiumchromates and 12 parts of barium sulfate or 22 parts of feldspars, 10 parts of fluorites, 12 parts of tin protoxides, 6 parts of potassiumchromates, 12 parts of Manganse Dioxide and 18 parts of sodium sulfate with weight part metering.Fill composition comprises 6 parts of red leads, 4 parts of boraxs, 8 parts of fluorites, 4 parts of nitre, 4 parts of ferric oxide, 2 parts of tin protoxides, 4 parts of barium sulfate, 8 parts of bone ashes, 0.00025 part of cobalt oxide and 1.0 parts of white arsenics or 6 parts of red leads, 4 parts of boraxs, 8 parts of fluorites, 4 parts of nitre, 4 parts of ferric oxide, 4 parts of Manganse Dioxide, 4 parts of barium sulfate, 8 parts of bone ashes, 0.00025 part of cobalt oxide, 0.25 part of sulphur and 1.0 parts of white arsenics with weight part metering.Fill composition comprises 0.45 part of borax, 9.1 parts of feldspars, 0.63 part of Manganse Dioxide, 4.6 parts of sodium sulfate and 0.45 part of barium sulfate or 2.0 parts of boraxs, 3.0 parts of feldspars, 12.5 parts of sodium aluminum fluorides, 6.0 parts of grey feldspars and 0.28 part of copper sulfate with weight part metering.Fill composition comprises 2.0 parts of red leads, 2.0 parts of boraxs, 5.0 parts of nitre, 4.5 parts of Manganse Dioxide oxygen, 8 parts of bone ashes and 7 parts of sodium aluminum fluorides or 50 parts of red leads, 14 parts of boraxs, 10 parts of nitre, 2.6 parts of Manganse Dioxide oxygen and 0.006 part of gold trichloride with weight part metering.Tackiness agent is construction cement, polyvinyl acetate emulsion, true mineral varnish tackiness agent, vinylformic acid, silicon third and styrene-acrylate emulsion type coating glue stick.
A kind of preparation method of multi-angle reflect type coating, its special character is that this method may further comprise the steps:
1] selects the material of preparation coating and the proportioning of definite each component for use;
2] to above-mentioned steps 1] in material mixing, and pulverize evenly to particle diameter below 5 millimeters; And cool shine or artificial seasoning to the seasoning state.
3] be heated to 1150～1600 ℃ in the dry back placement container and make its fusion;
4] material after the fusion is cooled to normal temperature;
5] crush and screen to particle diameter 0.5～5mm standby to cooled material.
6] material after crushing and screening adds adhesive in the described ratio of claim 1, and mixing promptly gets this multi-angle reflect type coating.
The present invention is as follows with the basic recipe table of weight part metering:
Use several construction technology of the present invention:
Example 1: the diamond coating spray bullet for the indoor and outdoor metope of having plastered and ceiling or ground is coated with way:
(1) bullet is coated with or sprays polymer cement mortar monochrome or the flat slurry of polychrome point.
(2) spray diamond coating one～two road.
(3) with oil gun spray or brush one of agent of cover (waterproofing agent of organosilicon or the agent of commercially available true lacquer cover)
The spraying of appendix one polymer cement mortar, bullet are coated with proportioning commonly used (weight ratio)
Spraying mortar mix ratio subordinate list 1.1
| The facing way | Cement | Pigment | Fine aggregate | Xylogen lime carbonate | Polyvinyl acetate emulsion | Lime putty | Slurry consistency (cm) |
| The corrugated, corrugated is granular | ??100??100??100??100 | An amount of | ??200??400??200??400 | ??0.3??0.3??0.3??0.3 | ??8-15??8-15??8-15??8-15 | ??-??100??-??100 | ??13-14??13-14??10-11??10-11 |
Play buttering proportioning subordinate list 1.2
| Project | Cement | Pigment | Water | Polyvinyl acetate emulsion |
| Brush background color slurry brush background color slurry is fluffed cotton and is a little fluffed cotton a little | Ordinary Portland cement 100 white cements 100 ordinary Portland cements 100 white cements 100 | An amount of | ??90??80??55??45 | ??8～15??8～15??8～15??8～15 |
Annotate: according to the temperature situation, amount of water can suitably be adjusted.
Example 2: the true mineral varnish for interior exterior wall of having plastered and ceiling adds diamond coating way:
(1) spray one of agent of (brush) back cover (true mineral varnish auxiliary products)
(2) topcoating one～two road (true mineral varnish auxiliary products)
(3) spray diamond coating one～two road
(4) spray one facing of (brush) overlay coating (true mineral varnish auxiliary products).
Illustrate:
1) diamond coating also can add a spray mo(u)lding in the true stone finish paint by suitable proportion.
2) true mineral varnish master operation and constructional method see the stone paint description of product for details.
Claims (9)
1. a multi-angle reflect type coating with the weight part metering, comprises 100 parts of quartz sands, 25～57.3 parts of carbonate and 22.3～80 parts of fill compositions.
2. according to the described multi-angle reflect type coating of claim 1, it is characterized in that: described carbonate comprises the arbitrary of soda ash, salt of wormwood, lime carbonate and combination thereof.
3. according to the described multi-angle reflect type coating of claim 1, it is characterized in that: described fill composition comprises 11 parts of red leads, 3 parts of boraxs, 1.3 parts of copper scales, 3.7 parts of Red copper oxide, 1.3 parts of iron filings and 2.0 parts of glass puttys or 4 parts of red leads, 4 parts of boraxs, 7 parts of copper scales, 11 parts of Red copper oxide and 4.0 parts of tin protoxides with weight part metering.
4. according to the described multi-angle reflect type coating of claim 1, it is characterized in that: described fill composition comprises 15 parts of feldspars, 8 parts of fluorites, 14 parts of potassiumchromates and 12 parts of barium sulfate or 22 parts of feldspars, 10 parts of fluorites, 12 parts of tin protoxides, 6 parts of potassiumchromates, 12 parts of Manganse Dioxide and 18 parts of sodium sulfate with weight part metering.
5. according to the described multi-angle reflect type coating of claim 1, it is characterized in that: described fill composition comprises 6 parts of red leads, 4 parts of boraxs, 8 parts of fluorites, 4 parts of nitre, 4 parts of ferric oxide, 2 parts of tin protoxides, 4 parts of barium sulfate, 8 parts of bone ashes, 0.00025 part of cobalt oxide and 1.0 parts of white arsenics or 6 parts of red leads, 4 parts of boraxs, 8 parts of fluorites, 4 parts of nitre, 4 parts of ferric oxide, 4 parts of Manganse Dioxide, 4 parts of barium sulfate, 8 parts of bone ashes, 0.00025 part of cobalt oxide, 0.25 part of sulphur and 1.0 parts of white arsenics with weight part metering.
6. according to the described multi-angle reflect type coating of claim 1, it is characterized in that: described fill composition comprises 0.45 part of borax, 9.1 parts of feldspars, 0.63 part of Manganse Dioxide, 4.6 parts of sodium sulfate and 0.45 part of barium sulfate or 2.0 parts of boraxs, 3.0 parts of feldspars, 12.5 parts of sodium aluminum fluorides, 6.0 parts of grey feldspars and 0.28 part of copper sulfate with weight part metering.
7. according to the described multi-angle reflect type coating of claim 1, it is characterized in that: described fill composition comprises 2.0 parts of red leads, 2.0 parts of boraxs, 5.0 parts of nitre, 4.5 parts of Manganse Dioxide oxygen, 8 parts of bone ashes and 7 parts of sodium aluminum fluorides or 50 parts of red leads, 14 parts of boraxs, 10 parts of nitre, 2.6 parts of Manganse Dioxide oxygen and 0.006 part of gold trichloride with weight part metering.
8. according to the arbitrary described multi-angle reflect type coating of claim 1～7, it is characterized in that: described tackiness agent is construction cement, polyvinyl acetate emulsion, true mineral varnish tackiness agent, vinylformic acid, silicon third and styrene-acrylate emulsion type coating glue stick.
9. the preparation method of the described multi-angle reflect type coating of claim 1 is characterized in that, this method may further comprise the steps:
1] selects the material of preparation coating and the proportioning of definite each component for use;
2] to above-mentioned steps 1] in material mixing, and pulverize evenly to particle diameter below 5 millimeters; And cool shine or artificial seasoning to the seasoning state;
3] be heated to 1150～1600 ℃ in the dry back placement container and make its fusion;
4] material after the fusion is cooled to normal temperature;
5] crush and screen to particle diameter 0.5～5mm standby to cooled material;
6] material after crushing and screening adds adhesive in the described ratio of claim 1, and mixing promptly gets this multi-angle reflect type coating.