CN105001731A - Creative environment-friendly dry powder paint for wall decoration - Google Patents
Creative environment-friendly dry powder paint for wall decoration Download PDFInfo
- Publication number
- CN105001731A CN105001731A CN201510481055.3A CN201510481055A CN105001731A CN 105001731 A CN105001731 A CN 105001731A CN 201510481055 A CN201510481055 A CN 201510481055A CN 105001731 A CN105001731 A CN 105001731A
- Authority
- CN
- China
- Prior art keywords
- dry powder
- powder paint
- parts
- paint
- described dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides creative environment-friendly dry powder paint for wall decoration. The creative environment-friendly dry powder paint comprises, by weight, 3-30 parts of titanium dioxide, 3-30 parts of white cement, 20-60 parts of acrylic acid rubber powder, 5-40 parts of lime and/or wollastonite, 0.02-0.8 part of cellulose, 0.5-12 parts of citric acid and 0.1-3 parts of defoamer. The creative environment-friendly dry powder paint for wall decoration is inorganic active dry powder wall paint which is resistant to water, crack and weather, free of VOC and formaidehyde, free of the saltpetering phenomenon and quite good in workability, the later-period strength of a coating is high, and the creative environment-friendly dry powder paint can be widely applied to painting and decorating of inner walls and outer walls.
Description
Technical field
The present invention relates to a kind of metope dry powder paint, especially a kind of environmental protection innovation and the decorated wall surface dry powder paint of practicality.
Background technology
Easily there is the problem of weathering resistance difference or environmental protection not in existing wall decoration material (as coating or paint).Such as emulsion coatings is adopt pure organism to prepare substantially, therefore exterior coating anti-uv-ray is poor, and weathering resistance is poor, its easily be full of cracks, fugitive color, Yi Huahua after uviolizing.In addition, because various filler (concrete wall surface, sand mix metope, putty powder metope) of inner-outer wall are inorganic coagulation material or are added with the inorganic coagulation material of a small amount of organic materials, and the coating of apposition on it is organic materials, the two different in kind, situation of expanding with heat and contract with cold is not identical, when temperature variation degree is identical, the two amplitude of expanding with heat and contract with cold is different, thus causes being coated with charge level or lacquer painting ftractures, the phenomenon such as come off.Have again, various emulsion coatings is all containing chemical substances such as ethylene glycol (frostproofer), ammoniacal liquor (pH value regulator), these materials can produce the obnoxious flavoures such as volatile organic compounds (VOC) and formaldehyde in construction process, and environmental-protecting performance is poor; It brings detrimentally affect for giving the physical and mental health of people during upholstery.
Therefore, this area needs to adopt the coating of new form to carry out alternative existing emulsion coatings.
A kind of green powdered paint and preparation method thereof is disclosed in patent of invention CN200610036625.9, this green powdered paint is made up of the material of following weight percent: Redispersible Polymeric Emulsion Powder 5 ~ 20%, white cement 20 ~ 40%, calcium carbonate 20 ~ 45%, titanium dioxide 5 ~ 25%, diatomite 2 ~ 8%, wilkinite 1 ~ 2%, ether of cellulose 0.2 ~ 0.5%, defoamer 0.2 ~ 0.5%, tinting pigment 0 ~ 4%.Each component is dropped into stirrer by weight percentage, and after mixing, packaging can obtain finished product green powdered paint.At the construction field (site), adjust with water one, can use.Once-forming from the end to face, save time, economize operation, without any volatilization pungent, real Diamond Search, water-proof, paint film is smooth, and hardness is high, intensity is large, ageing-resistant, cracking resistance, is the decorative product replacing traditional glue putty, emulsion paint Novel two-in-one metope, is widely used in the decoration of buildings inner-outer wall.
Separately there is in patent application CN201310721041.5 the dry powder emulsion paint coating disclosing a kind of efficient-decomposition formaldehyde, this dry powder emulsion paint coating comprises the component of following parts by weight: nano zine oxide 1 part ~ 26 parts, silicon-dioxide and zinc oxide composite 1 part ~ 30 parts, Paris white 20 parts ~ 70 parts, sierozem power 0 part ~ 40 parts, white cement 0 part ~ 20 parts, talcum powder 3 parts ~ 10 parts, light calcium carbonate 2 parts ~ 10 parts, kaolin 0 part ~ 30 parts, titanium dioxide 0 part ~ 25 parts, organic polymer 0.5 part ~ 50 parts and Mierocrystalline cellulose 0.1 part ~ 1 part; Said components is mixed in proportion, stirs, namely obtain dry powder emulsion paint coating.Dry powder emulsion paint coating of the present invention not only for shelf-stable, ventilative, protection against the tide, mildew-resistant, acid and alkali-resistance, cohesive strength is high, splitting resistance is excellent, and can long-acting bacteriostatic be played used as during indoor wall coating, decomposing the effect of indoor formaldehyde and toluene gas and elimination air peculiar smell, is a kind of nontoxic, tasteless safe environment protection type coating.
But above-mentioned dry powder paint always has part not fully up to expectations in the later strength etc. of weathering resistance, accumulation of salt in the surface soil phenomenon, coating application performance (setting time of liquid coating after the mixing that adds water and hydration time enough long) and coating, makes such dry powder paint to adapt to standard and to be applied on a large scale.
Summary of the invention
Therefore, the invention provides a kind of waterproof, cracking resistance, weather-proof, Diamond Search, zero formaldehyde, there will not be accumulation of salt in the surface soil phenomenon, coating application performance fabulous and the inorganic active metope dry powder paint that coating later strength is high.
The present invention with the pure acrylic acid rubber powder of white cement and excellent in weather for inorganic substrate and organic substrate, science through other batching is composite, under the effect of water, organic materials and inorganic materials are produced and hands over chain-like structure, make the physical and chemical performances such as its waterproof, cracking resistance, cohesive force, intensity reach good effect.The composite inorganic materials that solves of these two kinds of base materials only has rigidity not have flexibility, and organic materials only has flexibility not have a congenital difficult problem for toughness.
Therefore, the invention provides a kind of Innovation & environment type decorated wall surface dry powder paint, described dry powder paint comprises the component of following weight part: titanium dioxide 3 ~ 30 parts, white cement 3 ~ 30 parts, vinylformic acid rubber powder 20 ~ 60 parts, lime and/or wollastonite 5 ~ 40 parts, Mierocrystalline cellulose 0.02 ~ 0.8 part, citric acid 0.5 ~ 12 part and defoamer 0.1 ~ 3 part.
In a kind of concrete embodiment, limy 3 ~ 30 parts and wollastonite 2 ~ 10 parts in described dry powder paint.
In a kind of concrete embodiment, in described dry powder paint, also also contain Shuanghui powder 5 ~ 30 parts containing in talcum powder 3 ~ 10 parts and/or described dry powder paint.
In a kind of concrete embodiment, also containing 0.1 ~ 1 part, chlorinated lime in described dry powder paint.
In a kind of concrete embodiment, in described dry powder paint, also contain the high molecular polymer 0.01 ~ 0.05 part of thickening, viscosifying action.
In a kind of concrete embodiment, also containing neusilin 0.1 ~ 1 part in described dry powder paint.
In a kind of concrete embodiment, also containing cement dispersion agent 0.01 ~ 0.05 part in described dry powder paint.
In a kind of concrete embodiment, also containing mineral dye and/or the color sand of 80 ~ 120 objects in described dry powder paint.
In a kind of concrete embodiment, it is titanium dioxide 3 ~ 30%, white cement 3 ~ 30%, vinylformic acid rubber powder 20 ~ 60%, lime and/or wollastonite 5 ~ 40%, Mierocrystalline cellulose 0.02 ~ 0.8%, citric acid 0.5 ~ 12% and defoamer 0.1 ~ 3% that described dry powder paint comprises weight percentage.
In a kind of concrete embodiment, it is titanium dioxide 3 ~ 30%, white cement 3 ~ 30%, vinylformic acid rubber powder 20 ~ 60%, lime 3 ~ 30%, wollastonite 2 ~ 10%, Mierocrystalline cellulose 0.02 ~ 0.8%, citric acid 0.5 ~ 12%, defoamer 0.1 ~ 3%, talcum powder 3 ~ 10%, Shuanghui powder 5 ~ 30%, chlorinated lime 0.1 ~ 1%, high molecular polymer 0.01 ~ 0.05%, neusilin 0.1 ~ 1% and cement dispersion agent 0.01 ~ 0.05% that described dry powder paint comprises weight percentage.
The chemical property of dry powder paint provided by the invention and the chemical property of body of wall close, thus its brushing postadhesion power is high, weathering resistance is strong; Described dry powder paint Diamond Search and formaldehyde, safety and environmental protection; The workability of described dry powder paint is splendid, its aquation and set time long, to the engineering time of operator's abundance, and the usage ratio of itself and water can change arbitrarily within the specific limits, can thick also can be rare, thus can adapt to the operating habit of various different metope and different workman.After dry powder paint provided by the invention smears to metope, its long service life, has the identical life-span with body of wall itself.
Embodiment
The invention provides a kind of Innovation & environment type decorated wall surface dry powder paint, described dry powder paint comprises the component of following weight part: titanium dioxide 3 ~ 30 parts, white cement 3 ~ 30 parts, vinylformic acid rubber powder 20 ~ 60 parts, lime and/or wollastonite 5 ~ 40 parts, Mierocrystalline cellulose 0.02 ~ 0.8 part, citric acid 0.5 ~ 12 part and defoamer 0.1 ~ 3 part.
Those skilled in the art know, and the major ingredient of titanium dioxide is titanium dioxide.Mainly use rutile-type during composition in the present invention as exterior coating, during composition as interior wall coating, mainly use Detitanium-ore-type.In this area, the granularity of titanium dioxide commercially, mostly at 2000 ~ 3000 orders, even reaches nano level, and it is for mainly playing the effect brightening and increase hiding rare in dry powder paint of the present invention.
In the present invention, use white portland cement (white cement) as one of base-material of dry powder paint, the chemical property of various filler (concrete wall surface, sand mix metope, putty powder metope) of its chemical property and inner-outer wall is close, good with the consistency of fillering after making coating products provided by the invention smear metope, the water-proofing anticracking of coating and excellent in weather.
In the present invention, described vinylformic acid rubber powder is the vinylformic acid rubber powder be purchased, the 6021-A vinylformic acid rubber powder such as provided for precious occasion are chemical.The vinylformic acid rubber powder be purchased is through SUMITOMO CHEMICAL chemical analysis center certification, and it is zero that its VOC pollutes.It, in dry powder paint of the present invention, mainly plays the pore of closed white cement, extends the hydration time of cement, allows the effect of the abundant aquation of cement; Meanwhile, it also plays the effect increasing coating flexibility.Generally speaking, water-fast, weather-proof and film forming after it is put on metope after dry powder paint provided by the invention being coated in add water to mix well.
The air-setting inorganic coagulation material of lime to be a kind of with calcium oxide be major ingredient.Be used alone lime when smearing material as metope, it does not have a water tolerance.But in the present invention, lime is used in dry powder paint in conjunction with white cement and other composition, and its not water-fast character just can not show again, also can contain a certain amount of lime completely in the exterior wall dry powder paint thus in the present invention.Lime is as a kind of air-setting inorganic coagulation material, and its Main Function in dry powder paint provided by the invention is the later strength strengthening coating.
The composition of wollastonite is Ca
3(Si
3o
9), it is used in coating of the present invention the effect mainly played and increase denseness and increase later strength.Effect in lime and wollastonite dry powder paint in the present invention has same or similar part, thus can use wherein a kind ofly partly or entirely to replace another kind of component, but more preferably both all has certain content in dry powder paint.
Mierocrystalline cellulose in the present invention is for being purchased cellulose powder, and its molecular-weight average is 50,000 ~ 2,500,000, such as, be 200,000.Described celluloses is as being Vltra tears.Mierocrystalline cellulose effect is in the present invention the workability ensureing described dry powder paint, plays the effect of water conservation and thickening in construction.
The citric acid used in the present invention is crystal or Powdered.Contriver finds to add in the present invention the composite dry powder paint that can to make with alkaline white cement be one of main ingredient of the component such as a certain amount of citric acid and vinylformic acid rubber powder during the life-time service after completing of constructing, all there will not be accumulation of salt in the surface soil phenomenon (comprise whiten, peeling, to come off).In addition, adding of citric acid can also play slow hard effect to white cement, thus reserves enough engineering times to workmen.
The defoamer used in the present invention can be the water-borne coatings defoamer be purchased, and adds water to mix well play froth breaking effect afterwards for the dry powder paint in the present invention.Described defoamer is such as the model of German import is the defoamer of P803.The effect of defoamer is that the workability after dry powder paint of the present invention and water are mixed well is protected, and makes this coating to be applied in metope equably and can not to bubble or pile up.
In a kind of concrete embodiment, limy 3 ~ 30 parts and wollastonite 2 ~ 10 parts in described dry powder paint.
In a kind of concrete embodiment, in described dry powder paint, also also contain Shuanghui powder 5 ~ 30 parts containing in talcum powder 3 ~ 10 parts and/or described dry powder paint.
Also optionally add the talcum powder of certain content in the present invention, it is used in coating of the present invention the effect can played and increase denseness, brighten, increase slickness and increase material suspension property in water.
The Shuanghui powder of certain content is also optionally added in the present invention.Shuanghui powder is also named " calcium-magnesium powder ", and main component is the carbonate of calcium and magnesium, is typically used as filler.Its Main Function being used in dry powder paint of the present invention as filler, the cost of dry powder paint product is reduced, and in addition, it also has the effect strengthening hiding rare and increase coating denseness.
In a kind of concrete embodiment, also containing 0.1 ~ 1 part, chlorinated lime in described dry powder paint.Also optionally add the chlorinated lime of certain content in the present invention, its effect mainly increases the outward appearance whiteness after coating material.
In a kind of concrete embodiment, in described dry powder paint, also contain the high molecular polymer 0.01 ~ 0.05 part of thickening, viscosifying action.Also optionally add the high molecular polymer of certain content in the present invention, described high molecular polymer plays thickening, viscosifying action.
In a kind of concrete embodiment, also containing neusilin 0.1 ~ 1 part in described dry powder paint.Also optionally add the neusilin of certain content in the present invention, described neusilin plays the effect of auxiliary fiber element water conservation.
In a kind of concrete embodiment, also containing cement dispersion agent 0.01 ~ 0.05 part in described dry powder paint.Also optionally add the cement dispersion agent of certain content in the present invention, described dispersion agent is used for preventing cement from luming in construction process or piling up, and such as uses the dispersion agent of model for P88 of German import in the present invention.
In a kind of concrete embodiment, also containing mineral dye and/or the color sand of 80 ~ 120 objects in described dry powder paint.Mineral dye and/or the color sand of 80 ~ 120 objects of certain content is also optionally added in the present invention, those skilled in the art can understand ground, the purposes of described color sand or mineral dye is the decorative colors changing described coating, the consumption of pigment used or color sand is not limit, and considers add according to the demand of user.In the preferred mode of one, described color sand is natural colour sand.
Under existing market situation, in the present invention, the price of titanium dioxide used is approximately 10,000 yuan/ton, the price of white cement about 0.1 ten thousand yuan/ton, the price of vinylformic acid rubber powder roughly at 2.6 ten thousand yuan/ton, lime and wollastonite about 0.03 ~ 0.1 ten thousand yuan/ton.It can thus be appreciated that dry powder paint provided by the invention is moderate, though higher than the most cheap emulsion coatings unit price, more much lower than the unit price of domestic your emulsion coatings.Even and if dry powder paint provided by the invention is compared with the most expensive domestic emulsion coatings, its environmental-protecting performance is also well a lot, and dry powder paint provided by the invention can reach the effect of Diamond Search and zero formaldehyde emissions like a cork.And inevitably containing antifreeze glycol and pH value regulator ammoniacal liquor in existing emulsion coatings, even if this makes the VOC in the emulsion coatings that quality is good again and formaldehyde content also can not be zero.
Dry powder paint provided by the invention is used in exterior wall and interior wall all has extraordinary effect.For during exterior wall compared with emulsion coatings, its superiority in uvioresistant is more remarkable; And for during interior wall compared with emulsion coatings, its advantage in the environmental-protecting performance such as VOC and formaldehyde emissions is more remarkable.
The using method of dry powder paint in the present invention: add after a certain amount of water (weight of such as water is 0.5 times of dry powder paint weight to 2 times) is mixed well and be applied in the inner wall surface or wall face filled and led up, generally smearing pass is can realize good covering effect and visual effect 2 ~ 3 times, the visual effect after this coating is applied smear with emulsion coatings after visual effect consistent.The situation of the construction of dry powder paint in the present invention is substantially identical with existing emulsion coatings.The brushing quality guaranteed period of the dry powder paint provided in the present invention after enough adding water is 2 ~ 3 days, needs to be finished as early as possible in 3 days under the water-borne coatings normal temperature that obtains after mixing well of that is adding water.And this dry powder paint can be preserved and never degenerates at least 1 year under the state of sealed damp-proof.
Embodiment 1 ~ 6
Provide six kinds of formula examples in dry powder paint feasible in the present invention in embodiment 1 ~ 6, wherein the consumption of each component refers to table 1.Tested according to national standard by dry powder paint in embodiment 1 ~ 6, specifically the usage ratio of dry powder paint and water is 1:1.4, and mixing well the assay after smearing is the requirement that these the 6 kinds different dry powder paints of formula all can meet national standard.Its application property is: be uniformly dispersed, and roller coating is accessible; Its operable time is: 2h liquid is coated with accessible; Its appearance of film is normal; Its time of drying (surface drying)≤2h; Its snappiness is: diameter 100mm flawless; Its abrasion resistance all >=500 times; Its content of volatile organic compound (VOC)≤1g/Kg; Its benzene, toluene, ethylbenzene and xylene content summation≤50mg/Kg; Its free formaldehyde content≤5mg/Kg; Its soluble heavy metal content (lead, cadmium, chromium, mercury) all can meet the regulation of GB18582.
Table 1
In sum, the invention provides a kind of therefore anti-aging, weather-proof, have intensity, high-density, have flexibility, impervious water, cracking resistance and the high dry powder paint of practicality.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (10)
1. an Innovation & environment type decorated wall surface dry powder paint, described dry powder paint comprises the component of following weight part: titanium dioxide 3 ~ 30 parts, white cement 3 ~ 30 parts, vinylformic acid rubber powder 20 ~ 60 parts, lime and/or wollastonite 5 ~ 40 parts, Mierocrystalline cellulose 0.02 ~ 0.8 part, citric acid 0.5 ~ 12 part and defoamer 0.1 ~ 3 part.
2. dry powder paint according to claim 1, is characterized in that, limy 3 ~ 30 parts and wollastonite 2 ~ 10 parts in described dry powder paint.
3. dry powder paint according to claim 1, is characterized in that, also also contains Shuanghui powder 5 ~ 30 parts containing in talcum powder 3 ~ 10 parts and/or described dry powder paint in described dry powder paint.
4. dry powder paint according to claim 1, is characterized in that, also containing 0.1 ~ 1 part, chlorinated lime in described dry powder paint.
5. dry powder paint according to claim 1, is characterized in that, has also contained the high molecular polymer 0.01 ~ 0.05 part of thickening, viscosifying action in described dry powder paint.
6. dry powder paint according to claim 1, is characterized in that, also containing neusilin 0.1 ~ 1 part in described dry powder paint.
7. according to the dry powder paint in claim 1 ~ 6 described in any one, it is characterized in that, also containing cement dispersion agent 0.01 ~ 0.05 part in described dry powder paint.
8. according to the dry powder paint in claim 1 ~ 6 described in any one, it is characterized in that, also containing mineral dye and/or the color sand of 80 ~ 120 objects in described dry powder paint.
9. according to the dry powder paint in claim 1 ~ 6 described in any one, it is characterized in that, it is titanium dioxide 3 ~ 30%, white cement 3 ~ 30%, vinylformic acid rubber powder 20 ~ 60%, lime and/or wollastonite 5 ~ 40%, Mierocrystalline cellulose 0.02 ~ 0.8%, citric acid 0.5 ~ 12% and defoamer 0.1 ~ 3% that described dry powder paint comprises weight percentage.
10. dry powder paint according to claim 9, it is characterized in that, it is titanium dioxide 3 ~ 30%, white cement 3 ~ 30%, vinylformic acid rubber powder 20 ~ 60%, lime 3 ~ 30%, wollastonite 2 ~ 10%, Mierocrystalline cellulose 0.02 ~ 0.8%, citric acid 0.5 ~ 12%, defoamer 0.1 ~ 3%, talcum powder 3 ~ 10%, Shuanghui powder 5 ~ 30%, chlorinated lime 0.1 ~ 1%, high molecular polymer 0.01 ~ 0.05%, neusilin 0.1 ~ 1% and cement dispersion agent 0.01 ~ 0.05% that described dry powder paint comprises weight percentage.