CN104591598A - Real stone paint, and preparation method and construction method thereof - Google Patents

Real stone paint, and preparation method and construction method thereof Download PDF

Info

Publication number
CN104591598A
CN104591598A CN201310529469.XA CN201310529469A CN104591598A CN 104591598 A CN104591598 A CN 104591598A CN 201310529469 A CN201310529469 A CN 201310529469A CN 104591598 A CN104591598 A CN 104591598A
Authority
CN
China
Prior art keywords
weight
mineral varnish
true mineral
color
natural stone
Prior art date
Application number
CN201310529469.XA
Other languages
Chinese (zh)
Other versions
CN104591598B (en
Inventor
王臻
魏红岩
秦东杰
邢净
郝志荣
阎佳林
Original Assignee
北新集团建材股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 北新集团建材股份有限公司 filed Critical 北新集团建材股份有限公司
Priority to CN201310529469.XA priority Critical patent/CN104591598B/en
Publication of CN104591598A publication Critical patent/CN104591598A/en
Application granted granted Critical
Publication of CN104591598B publication Critical patent/CN104591598B/en

Abstract

The invention provides a real stone paint. The real stone paint comprises, by weight, 90-130 parts of water, 2-5 parts of hydroxyethyl cellulose, 2-5 parts of a dispersant, 1-3 parts of a wetting agent, 4-8 parts of an antifoaming agent, 2-3 parts of an antiseptic, 100-150 parts of an emulsion, 5-12 parts of a film forming assistant, 1-3 parts of a pH adjusting agent, 5-20 parts of an antifreeze agent and 400-900 parts of a color sand component, wherein the color sand component comprises two or more than two natural stone flours with similar color. The invention further provides a preparation method of the real stone paint. The natural stone flowers with similar color in raw materials are blended in the embodiment of the invention to balance the color difference of all the natural stone flours, so even the color of one of the natural stone flours changes, the color difference of real stone paint products in batches is very small under the contrast of other natural stone flours with similar color, thereby the color difference change of the real stone paint is well controlled.

Description

A kind of true mineral varnish and preparation method thereof, constructional method
Technical field
The present invention relates to a kind of building coating, particularly a kind of true mineral varnish and preparation method thereof, constructional method.
Background technology
True mineral varnish is made primarily of high molecular polymer, natural color stone sand and related auxiliaries, and as hard as flint after dry and hard solidification, looks like natural real stone the same.Widely, and it is high to have hardness, good weathering resistance in the application of true mineral varnish, also has fire prevention, acid and alkali-resistance, anti-pollution, the feature such as nontoxic, tasteless.Compared with lithotome, there is the low and advantage such as simple of constructing of good decorating effect, construction costs, the position that true mineral varnish can not can also be constructed at a lot of stone material is simultaneously carried out construct (as building cylinder, position, turning etc.), can not stay and connect stubble seam, make whole building have more stylishness, beautiful feeling.
In the prior art, true mineral varnish is a kind of by the natural colour sand of shades of colour, grain composition, is base-material with emulsion, and is aided with the obtained high simulative stone substrate coating of various auxiliary agent.But often there is following defect in existing true mineral varnish:
First, natural colour sand is derived from lithotome, obtain through pulverizing, grinding, screen, be difficult to the color controlling starting material (natural colour sand), every batch of color sand consistency of colour can not be ensured, more or less all can there are differences between starting material batch, if do not adjust formula between producing at every batch, to there is very large aberration in true mineral varnish product, and then in construction process, very large aberration appears in true mineral varnish metope, causes accident resulting from poor quality of projects between different batches.
Secondly, under normal construction environment, existing true mineral varnish drying is too fast, be generally 2 hours time of drying, body of wall is constructed up and down and be there is certain time interval, especially higher Highrise buildings, the construction interval of high-rise body of wall and low layer body of wall, was more than two hours, body of wall is easy to occur upper and lower color disunity or there is larger aberration, and once occur that aberration is just difficult to repair, causes accident resulting from poor quality of projects and huge financial loss.
Existing true mineral varnish stain resistant is poor, after true mineral varnish spraying, and coating surface concave-convex surface, very easily covered with dust, accumulation spot, and not easy to clean.
In addition, because true mineral varnish drying is too fast, when the true mineral varnish wall construction of brick, easily occur that difficulty tears U.S. line paper, even tear situation about not coming; When constructing under the mal-condition of drying, high temperature, strong wind, true mineral varnish drying quickly, is easy to occur to ftracture, the situation such as comes off, and therefore existing true mineral varnish is unsuitable for the construction of severe environment of drying, high temperature, strong wind.
Summary of the invention
Technical problem to be solved by this invention is that the natural colour sand of every batch of the prior art is difficult to ensure colour consistency, and then cause true mineral varnish product to occur very large aberration between not batch, and due to body of wall interval of constructing up and down long, cause body of wall to be easy to the defect occurring upper and lower color disunity or there is larger aberration.
Second technical problem to be solved by this invention be true mineral varnish of the prior art not stain resistant and under severe conditions construction time easily there is the defect of situations such as ftractureing, come off.
In order to solve the problems of the technologies described above, the object of the invention is to provide a kind of true mineral varnish, it comprises the feed composition of following parts by weight: water 90-130 weight part, Natvosol 2-5 weight part, dispersion agent 2-5 weight part, wetting agent 1-3 weight part, defoamer 4-8 weight part, sanitas 2-3 weight part, emulsion 100-150 weight part, film coalescence aid 5-12 weight part, pH adjusting agent 1-3 weight part, frostproofer 5-20 weight part, color sand component 400-900 weight part, described color sand component comprises the close natural stone-powder of two or more color.
Preferably, described color sand component comprises the close natural stone-powder of 2-6 kind color.
Preferably, the granularity of described natural stone-powder comprises 20-40 order, 40-80 order and/or 80-120 order.
Preferably, the water-ground limestone of 0-100 weight part and/or the titanium dioxide of 0-1 weight part is also comprised.
Preferably, described emulsion is one or more in pure third, phenylpropyl alcohol, silicon third, and the second-order transition temperature of described emulsion is more than 30 DEG C.
Preferably, described emulsion is pure-acrylic emulsion, benzene emulsion or organosilicon crylic acid latex.
Preferably, 0-10 parts by weight of thickening agent is also comprised.
Preferably, described thickening material is Natvosol, hydroxyethylmethyl-cellulose or Type 3U.
Preferably, described wetting agent is non-ionic wetting agent.
Preferably, described dispersion agent is vinylformic acid sodium salt or vinylformic acid ammonium salt; Described defoamer is mineral oils or silicone based; Described sanitas is BIT (BIT) or CMIT/MIT (CMIT/MIT); Described film coalescence aid is 2,2,4-trimethylammonium-1,3-pentanediol mono isobutyrate or lauryl alcohol ester; Described pH adjusting agent is organic amine or sodium hydroxide.
Present invention also provides a kind of preparation method of above-mentioned true mineral varnish, it is characterized in that, comprise the following steps:
(1) take water 90-130 weight part, Natvosol 2-5 weight part, dispersion agent 2-5 weight part, wetting agent 1-3 weight part, defoamer 3-5 weight part, sanitas 2-3 weight part, obtains mixture after stirring;
(2) emulsion 100-150 part is taken, film coalescence aid 5-12 weight part, pH adjusting agent 1-3 weight part, frostproofer 5-20 weight part, the natural stone-powder 400-900 weight part that two or more color is close, defoamer 1-3 part, and join in the mixture that described step (1) obtains, stir and obtain true mineral varnish.
Preferably, described step (2) also comprises: before described emulsion, film coalescence aid, pH adjusting agent, frostproofer, natural stone-powder and defoamer being joined the mixture that described step (1) obtains, in the mixture that described step (1) obtains, add the water-ground limestone of 0-100 weight part and/or the titanium dioxide of 0-1 weight part, and high-speed stirring dispersion makes the fineness of described water-ground limestone and/or titanium dioxide reach less than 100 microns.
Preferably, described step (2) is also included in the thickening material adding 0-10 weight part in the mixture obtained to described step (1) under stirring at low speed.
Present invention also provides a kind of constructional method of true mineral varnish described above, it is characterized in that, comprise the following steps:
1) base treatment
First remove the surface attachments on metope, large concavo-convex position grout is filled and led up, and then polishes flat, and tiny crack, cavity polyalcohol cement basis putty are repaired;
2) roller coat priming paint
On metope, roller coat is primed 1-2 time, waits drying;
3) true mineral varnish is sprayed
After described priming paint drying, primed surface draws the line of ink marker, T-me line paper; Spray true mineral varnish 1-2 time again, often 24 hours, time interval, after spraying, tears U.S. line paper, cleaning jointing; For the true mineral varnish of described spraying, the pressure of spray gun is 0.4Kg/cm 2-0.6Kg/cm 2, nozzle diameter is 3cm – 10cm, and the vertical range between nozzle and metope is 40-50cm; The speed that spray gun runs is 1-3m/s;
4) spraying or roller coat overlay coating
Spraying or roller coat overlay coating 1-2 time, for described coating hood coating materials, the pressure of spray gun is 4Kg/cm 2-6Kg/cm 2, nozzle diameter is 2cm-3cm, and spray is apart from being 50cm-60cm, and the speed that spray gun runs is 1-5m/s; For described roller coat overlay coating, glue spread is 0.15Kg/m 2-0.20Kg/m 2/ time.
Technical scheme of the present invention compares in prior art, has the following advantages:
(1) true mineral varnish of the present invention comprises the feed composition of following parts by weight: water 90-130 part, Natvosol 2-5 part, dispersion agent 2-5 part, wetting agent 1-3 part, defoamer 4-8 part, sanitas 2-3 part, emulsion 100-150 part, film coalescence aid 5-12 part, pH adjusting agent 1-3 part, frostproofer 5-20 part, color sand component 400-900 part, described color sand component comprises the close natural stone-powder of two or more color.Owing to adopting above technical scheme, the embodiment of the present invention passes through the natural stone-powder that mixture color is close in the feed, the aberration of various natural stone-powder can be balanced, even if there is a kind of color of natural stone-powder that the change of some occurs, under the natural stone-powder phase contrast that other color is close, the aberration of the true mineral varnish product between each batch is very little, controls the chromatic aberration of true mineral varnish product well.
Adopt the content proportioning of various auxiliary agent in above-mentioned formula, especially Natvosol 2-5 part, extend the open hour of paint film, make true mineral varnish film have longer surface drying time, under normal construction environment, surface drying time is 4-6 hour, so not only be easy to construction, save material, and can ensure that metope color ensures consistence well, body of wall is not easy to occur aberration problem up and down, is particularly useful for the large hoarding construction of Highrise buildings.
Owing to extending the time of drying of true mineral varnish, difficulty is there will not be to tear the situation of U.S. line paper in construction period, also broken restricted that existing true mineral varnish should not be constructed under the adverse weather condition of drying, high temperature, strong wind simultaneously, be also not easy to occur the situations such as true mineral varnish ftractures, come off even if construct under severe conditions.
Meanwhile, owing to adding wetting agent in above-mentioned formula, reduce surface tension or the interfacial tension of solid materials, solid materials can be made more easily to be soaked in water, and it is better that solid materials disperses in water.
In addition, discharge pollutants in true mineral varnish one side production process of the present invention almost nil, on the other hand, decrease the consumption to stone material, stone material consumption is only about 10% of sheet material, significantly reduces environmental stress.
(2) true mineral varnish of the present invention, adopt the natural stone-powder of not identical granularity and proportioning, not only can improve the true mineral varnish layer hardness after construction, but also the aberration between various natural stone-powder can be balanced further, the aberration of true mineral varnish product between each batch is reduced further.
(3) true mineral varnish of the present invention, also comprise the titanium dioxide of 0-1 weight part and/or the water-ground limestone of 0-100 weight part, because titanium dioxide has extraordinary opacifying power, water-ground limestone has the stronger transparency, therefore, can by regulating the consumption of titanium dioxide and water-ground limestone neatly, true mineral varnish film is made to reach required opacifying power or transparency, thus contribute to the thickness reducing true mineral varnish film in construction, thickness can be reduced to 2-3mm by 5mm, thus reduce the materials of true mineral varnish, reduce construction costs significantly.
(4) true mineral varnish of the present invention, owing to adopting emulsion (as DOW Chemical DC-420, Bao Lijia BLJ-996HD, the rich RS-992 of Ahmedabad etc.) 10-15 part that second-order transition temperature is higher, strengthen paint film strength and the white property of water resistant, dust and spot difficulty is made to be attached at coating surface, even if there is attachment, under rainwash, also can keep clean, thus enhance the stain resistant of true mineral varnish.
In addition; true mineral varnish of the present invention can adopt the technical scheme of spraying or roller coat overlay coating on true mineral varnish layer when constructing; its overlay coating can play the effect of facing protective layer; enhance the water-repellancy of true mineral varnish, the white property of water resistant, weathering resistance, stain resistant, also improve hardness and the slipperiness on surface.Preferably, described overlay coating adopts high glass transition temperature, high-weatherability emulsion, not only can strengthen paint film strength; also cover enamelled coating surface unusual light can be made; be difficult to pile up dust, and easy cleaning, more can play a protective role to true mineral varnish layer in the white property of water resistant and weathering resistance.
Embodiment
Below will make further instructions the present invention by way of example, but following examples are only example, and are not used to limit the present invention.
Embodiment 1
(1) water 100 weight part is first taken, Natvosol (model: HBR-250, manufacturer is sub-to dragon, viscosity is 30000CP, lower same) 4 weight parts, dispersion agent (vinylformic acid sodium salt, model: easy soon, manufacturer: DOW Chemical) 3 weight parts, wetting agent (non-ionic type, model: X-405, manufacturer: DOW Chemical) 3 weight parts, defoamer (model: NXZ, manufacturer: Nuo Puke company) 4 weight parts, sanitas (1, 2-benzisothiazole-3-ketone (BIT), model: EG-CT, manufacturer: gram Lay benefactor department) 2 weight parts, then by Natvosol, dispersion agent, wetting agent, defoamer and sanitas are slowly added to the water under stirring at low speed, mixture is obtained after stirring.
(2) selected a kind of yellow standard specimen, then the close yellow natural stone-powder of two kinds of colors is chosen according to standard specimen color, a kind of natural stone-powder yellow fraction 40-80 order, 200 weight parts, the another kind of natural stone-powder Chrysan Yellow 80-120 order close with it, 450 weight parts, and then take pure-acrylic emulsion (model: RS-706, manufacturer: the rich company of Ahmedabad, second-order transition temperature is 30 DEG C) 120 weight parts, film coalescence aid (model: Texanol, manufacturer: Yi Shi Man) 12 weight parts, pH adjusting agent (model: AMP-95, manufacturer: DOW Chemical) 2 weight parts, frostproofer (model: ethylene glycol, manufacturer: Yanshan Petrochemical) 10 weight parts, defoamer 1 weight part, and by emulsion, film coalescence aid, pH adjusting agent, frostproofer, natural stone-powder and defoamer join in the mixture that step (1) obtains, stir and obtain true mineral varnish A.
(3) the yellow natural stone-powder that above-mentioned two kinds of colors are close is adopted, the true mineral varnish of different batches is repeatedly prepared according to the step of step (1) and step (2), aberration between its true mineral varnish and true mineral varnish A and between the true mineral varnish of different batches is very little, and the color that detects by an unaided eye is completely the same.
Embodiment 2
(1) water 90 weight part is first taken, Natvosol (model: HBR-250, manufacturer is sub-to dragon, viscosity is 30000cp) 2 weight parts, dispersion agent (vinylformic acid ammonium salt, model: easy soon, manufacturer: DOW Chemical) 5 weight parts, wetting agent (non-ionic type, model: PE-100, manufacturer: extra large river science and technology) 2 weight parts, defoamer (model: NXZ, manufacturer: Nuo Puke company) 3 weight parts, sanitas (1, 2-benzisothiazole-3-ketone (BIT), model: EG-CT, manufacturer: gram Lay benefactor department) 3 weight parts, then by Natvosol, dispersion agent, wetting agent, defoamer and sanitas are slowly added to the water under stirring at low speed, mixture is obtained after stirring.
(2) under high velocity agitation by 1 weight part titanium dioxide (model: rutile-type, commercially available) add in the mixture that step (1) obtains, because the fineness of titanium dioxide is smaller, surface energy is higher, be not easy to scatter, therefore necessary high-speed stirring 10 minutes, surveys the fineness of titanium dioxide, stop stirring when fineness is less than 100 microns, obtain the mixture containing titanium dioxide.
(3) selected a kind of white standard specimen, then three kinds of natural stone-powders are chosen according to standard specimen color, concrete data are in table 1, and then take pure-acrylic emulsion (model: RS-706, manufacturer: the rich company of Ahmedabad, second-order transition temperature is 30 DEG C) 150 weight parts, film coalescence aid (lauryl alcohol ester, neat large chemistry) 10 weight parts, pH adjusting agent (AMP-95, Mykrolis Corp) 1 weight part, frostproofer (ethylene glycol, Yanshan Petrochemical) 20 weight parts, defoamer (NXZ, Nuo Puke company) 3 weight parts, then by pure-acrylic emulsion, film coalescence aid, pH adjusting agent, frostproofer, natural stone-powder and defoamer join in the mixture that step (2) obtains, stir and obtain true mineral varnish B.
(4) the natural stone-powder raw material that the shown three kinds of colors of table 1 are close is adopted, the true mineral varnish of different batches is repeatedly prepared according to step (1)-(3), aberration between its true mineral varnish and true mineral varnish B and between the true mineral varnish of different batches is very little, and the color that detects by an unaided eye is completely the same.
Table 1
Natural stone-powder 1 2 3
Weight part 200 350-400 40-60
Granularity (order) 40-80 80-120 20-40
Model, source Snow Flower White Snow Flower White Snow Flower White
Embodiment 3
(1) water 130 weight part is first taken, Natvosol (model: HBR-250, manufacturer is sub-to dragon, viscosity is 30000cp) 5 weight parts, dispersion agent (vinylformic acid ammonium salt, model: easy soon, manufacturer: DOW Chemical) 2 weight parts, wetting agent (non-ionic type, model: X-405, manufacturer: DOW Chemical) 1 weight part, defoamer (model: NXZ, manufacturer: Nuo Puke company) 3 weight parts, sanitas (1, 2-benzisothiazole-3-ketone (BIT), model: EG-CT, manufacturer: gram Lay benefactor department) 2 weight parts, then by Natvosol, dispersion agent, wetting agent, defoamer and sanitas are slowly added to the water under stirring at low speed, mixture is obtained after stirring.
(2) under high velocity agitation 10 weight part water-ground limestones are added in the mixture that step (1) obtains, because the fineness of water-ground limestone is smaller, surface energy is higher, be not easy to scatter, therefore necessary high-speed stirring 10 minutes, survey the fineness of water-ground limestone, stop stirring when fineness is less than 100 microns, obtain the mixture containing water-ground limestone.
(3) selected a kind of grey standard specimen, then four kinds of natural stone-powders are chosen according to standard specimen color, concrete data are in table 2, and then (second-order transition temperature is 30 DEG C to take benzene emulsion, model: RS-992, manufacturer: the rich company of Ahmedabad) 100 weight parts, film coalescence aid (lauryl alcohol ester, neat large chemistry) 5 weight parts, pH adjusting agent (AMP-95, Mykrolis Corp) 3 weight parts, frostproofer (ethylene glycol, Yanshan Petrochemical) 5 weight parts, defoamer (NXZ, Nuo Puke company) 1 weight part, thickening material (SCT-275, DOW Chemical) 1 weight part.Then benzene emulsion, film coalescence aid, pH adjusting agent, frostproofer, natural stone-powder, defoamer and thickening material are joined in the mixture that step (2) obtains, stir and obtain true mineral varnish C.
(4) the natural stone-powder raw material that four kinds of colors of the different batches shown in table 2 are close is adopted, the true mineral varnish of different batches is repeatedly prepared according to step (1)-(3), aberration between its true mineral varnish and true mineral varnish C and between the true mineral varnish of different batches is very little, and the color that detects by an unaided eye is completely the same.
Table 2
Natural stone-powder 1 2 3 4
Weight part 50-100 100-200 200-300 50-80
Granularity (order) 20-40 80-120 80-120 20-40
Model, source Gray jade Gray jade Steel gray Steel gray
Embodiment 4
(1) water 120 weight part is first taken, Natvosol (model: HBR-250, manufacturer is sub-to dragon, viscosity is 30000cp) 4 weight parts, dispersion agent (vinylformic acid ammonium salt, model: easy soon, manufacturer: DOW Chemical) 3 weight parts, wetting agent (non-ionic type, model: X-405, manufacturer: DOW Chemical) 2 weight parts, defoamer (model: NXZ, manufacturer: Nuo Puke company) 4 weight parts, sanitas (1, 2-benzisothiazole-3-ketone (BIT), model: EG-CT, manufacturer: gram Lay benefactor department) 2 weight parts, then by Natvosol, dispersion agent, wetting agent, defoamer and sanitas are slowly added to the water under stirring at low speed, mixture is obtained after stirring.
(2) under high velocity agitation 50 weight part water-ground limestones are added in the mixture that step (1) obtains, high-speed stirring 10 minutes, survey the fineness of water-ground limestone, stop stirring when fineness is less than 100 microns, obtain the mixture containing water-ground limestone.
(3) selected a kind of light yellow standard specimen, then choose the close natural stone-powder of six kinds of colors according to standard specimen color, concrete data are in table 3; Take organosilicon crylic acid latex (second-order transition temperature is 30 DEG C, model: BLJ-996HD, manufacturer: Bao Lijia company) 150 weight parts again, film coalescence aid (lauryl alcohol ester, neat large chemistry) 10 weight parts, pH adjusting agent (AMP-95, Mykrolis Corp) 2 weight parts, frostproofer (ethylene glycol, Yanshan Petrochemical) 10 weight parts, defoamer (NXZ, Nuo Puke company) 1-3 part, thickening material (SCT-275, DOW Chemical) 5 weight parts.Then organosilicon crylic acid latex, film coalescence aid, pH adjusting agent, frostproofer, natural stone-powder, defoamer and thickening material are joined in the mixture that step (2) obtains, stir and obtain true mineral varnish D.
(4) the natural stone-powder raw material that six kinds of colors of the different batches shown in table 3 are close is adopted, the true mineral varnish of different batches is repeatedly prepared according to step (1)-(3), aberration between its true mineral varnish and true mineral varnish D and between the true mineral varnish of different batches is very little, and the color that detects by an unaided eye is completely the same.
Table 3
Natural stone-powder 1 2 3 4 5 6
Weight part 50-100 150-200 100-150 20-30 80-100 80-100
Granularity (order) 80-120 80-120 80-120 40-80 40-80 40-80
Model, source Snow Flower White Chrysan Yellow Yellow fraction Snow Flower White Chrysan Yellow Yellow fraction
Embodiment 5
(1) water 90 weight part is first taken, Natvosol (model: HBR-250, manufacturer is sub-to dragon, viscosity is 30000cp) 2 weight parts, dispersion agent (vinylformic acid ammonium salt, model: easy soon, manufacturer: DOW Chemical) 5 weight parts, wetting agent (non-ionic type, model: X-405, manufacturer: DOW Chemical) 3 weight parts, defoamer (model: NXZ, manufacturer: Nuo Puke company) 3 weight parts, sanitas (1, 2-benzisothiazole-3-ketone (BIT), model: EG-CT, manufacturer: gram Lay benefactor department) 2 weight parts, then by Natvosol, dispersion agent, wetting agent, defoamer and sanitas are slowly added to the water under stirring at low speed, mixture is obtained after stirring.
(2) selected a kind of sorrel standard specimen, then choose the close natural stone-powder of 5 kinds of colors according to standard specimen color, concrete data are in table 4; Take benzene emulsion (second-order transition temperature is 30 DEG C, model: RS-992, manufacturer: the rich company of Ahmedabad) 120 weight parts again, film coalescence aid (lauryl alcohol ester, neat large chemistry) 6 weight parts, pH adjusting agent (AMP-95, Mykrolis Corp) 2 weight parts, frostproofer (ethylene glycol, Yanshan Petrochemical) 10 weight parts, defoamer (NXZ, Nuo Puke company) 5 parts, thickening material (SCT-275, DOW Chemical) 5-10 weight part.Benzene emulsion, film coalescence aid, pH adjusting agent, frostproofer, natural stone-powder, defoamer and thickening material are joined in the mixture that step (1) obtains, stir and obtain true mineral varnish E.
(3) the natural stone-powder raw material that six kinds of colors of the different batches shown in table 4 are close is adopted, the true mineral varnish of different batches is repeatedly prepared according to step (1) and step (2), aberration between its true mineral varnish and true mineral varnish E and between the true mineral varnish of different batches is very little, and the color that detects by an unaided eye is completely the same.
Table 4
Natural stone-powder 1 2 3 4 5 6
Weight part 200-300 200-300 20-50 130-150 20-30 20-70
Granularity (order) 40-80 80-120 180-200 80-120 40-80 20-40
Model, source Coffee is red Chicken is blood red Chrysan Yellow Coffee is red China Dark Coffee is red
Embodiment 6
The execution conditions of the present embodiment: indoor, envrionment temperature is 20 DEG C.
1) base treatment
Removed by surface attachments (as dust, releasing agent, greasy dirt) on metope clean, and then fill and lead up large concavo-convex position sand-cement slurry, polish, if having tiny crack and cavity etc., usable polymers cement based putty is repaired.The coating if substrate surface is had been friends in the past, first root out loose, flake, crisp strong old coating, and then by smooth for the old coating sand papering of adhere well; If substrate surface has not water-fast coating, can be rooted out.
2) roller coat priming paint
To prime (alkali-resistant primer) 1-2 time at metope top roll, wait drying;
3) spraying or the true mineral varnish of blade coating
After priming paint drying, then spray the true mineral varnish A of embodiment 1, wait drying; For the true mineral varnish of spraying, the pressure of spray gun is 0.4-0.6Kg/cm 2, nozzle diameter is 3cm-10cm, and spray is apart from being 40-50cm, and the speed that spray gun runs is 1-3m/s; For the true mineral varnish of described spraying, glue spread is 3-5Kg/m 2/ time.
In construction process, true mineral varnish A extends time of drying, reduces largely or eliminates the aberration of constructing and causing, detecting by an unaided eye, the very unification of the upper and lower color of body of wall; And U.S. line paper can be easy to tear it down, do not occur the situation that U.S. line paper difficulty is torn, the time of drying of true mineral varnish is 2-4 hour.
4) spraying or roller coat overlay coating
After true mineral varnish drying, then spray or roller coat overlay coating (high-weatherability overlay coating) 1-2 time, for coating hood coating materials, the pressure of spray gun is 4Kg/cm2, and spray is apart from being 50-60cm, and the speed that spray gun runs is 1-5mm/s; For roller coat overlay coating, glue spread is 0.15-0.20Kg/m2/ time.
The true mineral varnish of the present embodiment contains the higher pure-acrylic emulsion of second-order transition temperature, and make true mineral varnish metope have stain resistant, dust and spot difficulty are attached at coating surface, even if be attached with dust, rush also can keep clean with water one.
Embodiment 7
The execution conditions of the present embodiment: envrionment temperature is about 35 DEG C, dry weather, and has strong wind.
1) base treatment
Removed by surface attachments (as dust, releasing agent, greasy dirt) on metope clean, and then fill and lead up large concavo-convex position sand-cement slurry, polish, if having tiny crack and cavity etc., usable polymers cement based putty is repaired.The coating if substrate surface is had been friends in the past, first root out loose, flake, crisp strong old coating, and then by smooth for the old coating sand papering of adhere well; If substrate surface has not water-fast coating, can be rooted out.
2) roller coat priming paint
Prime (alkali-resistant primer) 2 times at metope top roll, the thickness of paint film wants consistent.Wait drying; For the construction of partition seam style, according to the requirement of Pattern Design, primed surface applies infiltration black backing varnish or black sand wall priming paint, thus the line of ink marker required for being formed, and then the U.S. line paper of sealing label.
3) true mineral varnish is sprayed
After priming paint drying, the true mineral varnish A choosing embodiment 1 sprays, and can spray 1-2 time as required, wait drying; For the true mineral varnish of spraying, the pressure of spray gun is 0.4-0.6Kg/cm 2, spray is apart from being 40-50cm, and the speed that spray gun runs is 1-3mm/s; Consumption is 3-4Kg/m 2/ time.After completing the true mineral varnish of spraying, U.S. line paper is torn, then clears up jointing, if there is dipping phenomenon at side seam place, then describe with the colored paint of priming paint same color.
In construction process, true mineral varnish A, owing to extending time of drying, reduces largely or eliminates the aberration of constructing and causing, detecting by an unaided eye, the very unification of the upper and lower color of body of wall; And when constructing under the mal-condition of drying, high temperature, strong wind, the situation ftractureing, come off does not appear in true mineral varnish yet, and U.S. line paper can be easy to tear it down, do not occur the situation that U.S. line paper difficulty is torn, the time of drying of true mineral varnish is 2-3 hour.
4) spraying or roller coat overlay coating
After true mineral varnish drying, then spray or roller coat overlay coating (high-weatherability overlay coating) 1-2 time, for coating hood coating materials, the pressure of spray gun is 4Kg/cm 2, spray is apart from being 50-60cm, and the speed that spray gun runs is 1-5mm/s; For roller coat overlay coating, glue spread is 0.20Kg/m 2/ time.
The true mineral varnish of the present embodiment contains the higher pure-acrylic emulsion of second-order transition temperature, and overlay coating adopts the emulsion of high glass transition temperature, high-weatherability, further enhancing the stain resistant of true mineral varnish metope, dust and spot difficulty are attached at coating surface, even if be attached with dust, rush with water one and also can keep clean.
Embodiment 8
The method of this enforcement is identical with the method for embodiment 7, and difference is: true mineral varnish B, C, D, E replace true mineral varnish A as construction materials respectively, thus obtained four kinds of untrue mineral varnish metopes.
In construction process, true mineral varnish film B, C, D, E extend time of drying, reduce or eliminate the aberration of the true mineral varnish film in construction process largely, detect by an unaided eye, the very unification of the upper and lower color of body of wall; When constructing under the mal-condition of drying, high temperature, strong wind, there is not the situation ftractureing, come off in true mineral varnish, and U.S. line paper can be easy to tear it down, there is not the situation that U.S. line paper difficulty is torn, 2,4,3, the 4 hours respectively time of drying of true mineral varnish film.
Because true mineral varnish B contains titanium dioxide, improve the opacifying power of true mineral varnish, only need the true mineral varnish film of spraying 2mm, just can hide priming paint completely, reach extraordinary covering effect.
Because true mineral varnish C and D contains water-ground limestone, improve the transparent effect of true mineral varnish, only need the true mineral varnish film of spraying 3mm, just can reach required extraordinary transparent effect.
Comparative example 1
This comparative example is identical with the method for embodiment 1, and difference is: just replace two kinds of natural stone-powders in embodiment 1 with the natural stone-powder of solid color.
Adopt the natural stone-powder of solid color repeatedly to prepare the true mineral varnish of different batches, its true mineral varnish prepared has very large aberration between different batches, and detect by an unaided eye, the color of true mineral varnish exists notable difference.
Comparative example 2
This comparative example is identical with the method for embodiment 2, and difference is: just replace three kinds of natural stone-powders in embodiment 2 with the natural stone-powder of solid color.
Adopt the natural stone-powder of solid color repeatedly to prepare the true mineral varnish of different batches, its true mineral varnish prepared has very large aberration between different batches, and detect by an unaided eye, the color of true mineral varnish exists notable difference.
Comparative example 3
This comparative example is identical with the method for embodiment 5, and difference is: just replace six kinds of natural stone-powders in embodiment 5 with the natural stone-powder of solid color.
Adopt the natural stone-powder of solid color repeatedly to prepare the true mineral varnish of different batches, its true mineral varnish prepared has very large aberration between different batches, and detect by an unaided eye, the color of true mineral varnish exists notable difference.
In sum; these are only preferred embodiment of the present invention, be not intended to limit protection scope of the present invention, therefore; all any amendments done within the spirit and principles in the present invention, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.

Claims (13)

1. a true mineral varnish, is characterized in that, it comprises the feed composition of following parts by weight: water 90-130 weight part, Natvosol 2-5 weight part, dispersion agent 2-5 weight part, wetting agent 1-3 weight part, defoamer 4-8 weight part, sanitas 2-3 weight part, emulsion 100-150 weight part, film coalescence aid 5-12 weight part, pH adjusting agent 1-3 weight part, frostproofer 5-20 weight part, color sand component 400-900 weight part, described color sand component comprises the close natural stone-powder of two or more color.
2. true mineral varnish according to claim 1, is characterized in that, described color sand component comprises the close natural stone-powder of 2-6 kind color.
3. true mineral varnish according to claim 1 and 2, is characterized in that, the granularity of described natural stone-powder comprises 20-40 order, 40-80 order and/or 80-120 order.
4. true mineral varnish according to claim 1 and 2, is characterized in that, also comprises the water-ground limestone of 0-100 weight part and/or the titanium dioxide of 0-1 weight part.
5. true mineral varnish according to claim 1 and 2, is characterized in that, described emulsion is one or more in pure-acrylic emulsion, benzene emulsion and organosilicon crylic acid latex, and the second-order transition temperature of described emulsion is more than 30 DEG C.
6. true mineral varnish according to claim 1 and 2, is characterized in that, also comprises 0-10 parts by weight of thickening agent.
7. true mineral varnish according to claim 6, is characterized in that, described thickening material is Natvosol, hydroxyethylmethyl-cellulose or Type 3U.
8. true mineral varnish according to claim 1 and 2, is characterized in that, described wetting agent is non-ionic wetting agent.
9. true mineral varnish according to claim 1 and 2, is characterized in that, described dispersion agent is vinylformic acid sodium salt or vinylformic acid ammonium salt; Described defoamer is mineral oils or silicone based; Described sanitas is BIT (BIT) or CMIT/MIT (CMIT/MIT); Described film coalescence aid is 2,2,4-trimethylammonium-1,3-pentanediol mono isobutyrate or lauryl alcohol ester; Described pH adjusting agent is organic amine or sodium hydroxide.
10., according to a preparation method for the true mineral varnish in claim 1-9 described in any one, it is characterized in that, comprise the following steps:
(1) take water 90-130 weight part, Natvosol 2-5 weight part, dispersion agent 2-5 weight part, wetting agent 1-3 weight part, defoamer 3-5 weight part, sanitas 2-3 weight part, obtains mixture after stirring;
(2) emulsion 100-150 part is taken, film coalescence aid 5-12 weight part, pH adjusting agent 1-3 weight part, frostproofer 5-20 weight part, the natural stone-powder 400-900 weight part that two or more color is close, defoamer 1-3 part, and join in the mixture that described step (1) obtains, stir and obtain true mineral varnish.
11. preparation methods according to claim 10, it is characterized in that, described step (2) also comprises: before described emulsion, film coalescence aid, pH adjusting agent, frostproofer, natural stone-powder and defoamer being joined the mixture that described step (1) obtains, in the mixture that described step (1) obtains, add the water-ground limestone of 0-100 weight part and/or the titanium dioxide of 0-1 weight part, and high-speed stirring dispersion makes the fineness of described water-ground limestone and/or titanium dioxide reach less than 100 microns.
12. preparation methods according to claim 10 or 11, is characterized in that, described step (2) is also included in the thickening material adding 0-10 weight part in the mixture obtained to described step (1) under stirring at low speed.
The constructional method of 13. 1 kinds of true mineral varnish according to any one of claim 1-9, is characterized in that, comprise the following steps:
1) base treatment
First remove the surface attachments on metope, large concavo-convex position grout is filled and led up, and then polishes flat, and tiny crack, cavity polyalcohol cement basis putty are repaired;
2) roller coat priming paint
On metope, roller coat is primed 1-2 time, waits drying;
3) true mineral varnish is sprayed
After described priming paint drying, primed surface draws the line of ink marker, T-me line paper; Spray true mineral varnish 1-2 time again, often 24 hours, time interval, after spraying, tears U.S. line paper, cleaning jointing; For the true mineral varnish of described spraying, the pressure of spray gun is 0.4Kg/cm 2-0.6Kg/cm 2, nozzle diameter is 3cm – 10cm, and the vertical range between nozzle and metope is 40-50cm; The speed that spray gun runs is 1-3m/s;
4) spraying or roller coat overlay coating
Spraying or roller coat overlay coating 1-2 time, for described coating hood coating materials, the pressure of spray gun is 4Kg/cm 2-6Kg/cm 2, nozzle diameter is 2cm-3cm, and spray is apart from being 50cm-60cm, and the speed that spray gun runs is 1-5m/s; For described roller coat overlay coating, glue spread is 0.15Kg/m 2-0.20Kg/m 2/ time.
CN201310529469.XA 2013-10-31 2013-10-31 A kind of true mineral varnish and preparation method thereof, construction method CN104591598B (en)