CN102533039A - Paint with elastic texture - Google Patents

Paint with elastic texture Download PDF

Info

Publication number
CN102533039A
CN102533039A CN2011104257800A CN201110425780A CN102533039A CN 102533039 A CN102533039 A CN 102533039A CN 2011104257800 A CN2011104257800 A CN 2011104257800A CN 201110425780 A CN201110425780 A CN 201110425780A CN 102533039 A CN102533039 A CN 102533039A
Authority
CN
China
Prior art keywords
component
paint
elastic
texture coating
flexible texture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011104257800A
Other languages
Chinese (zh)
Other versions
CN102533039B (en
Inventor
李明献
任志军
李浩民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HENAN DEJIALI TECHNOLOGY DEVELOPMENT Co Ltd
Original Assignee
HENAN DEJIALI TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HENAN DEJIALI TECHNOLOGY DEVELOPMENT Co Ltd filed Critical HENAN DEJIALI TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN 201110425780 priority Critical patent/CN102533039B/en
Publication of CN102533039A publication Critical patent/CN102533039A/en
Application granted granted Critical
Publication of CN102533039B publication Critical patent/CN102533039B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to paint with elastic texture, which comprises an A component and a B component, wherein the A component comprises water, hydroxypropyl methylcellulose, quartz sand, and some other additives; the B component comprises 1250-mesh barium sulfate, rutile titanium dioxide, calcined kaolinite, elastic emulsion, styrene-acrylic emulsion, and some other additives, and the B component is obtained by mixing the above components with a proper amount of color paste; the paint with elastic texture is obtained by uniformly stirring the A component and the B component according to weight percents. The paint with elastic texture of the invention is waterborne thick-paste paint with specially-produced pure styrene-acrylic emulsion as a base material and natural granite stone powder as main fillers, and has better wear resistance and cracking resistance than common flat paint or elastic paint; cracks of walls can be bridged effectively because of the flexibility property; and the excellent ultraviolet radiation resistance is especially suitable for areas with strong sunlight.

Description

Flexible texture coating
Technical field
The present invention relates to a kind of chemical materials, relate in particular to a kind of flexible texture coating.
Background technology
Flexible texture coating-artistic coating series is artistic type coating; Compare with traditional smooth type coating; The design of its abundant cubic texture effect, self-help type can be immersed among the tempting artistic atmosphere your household moment fully; Really deserve to be called the metope art coating that everybody can enjoy, decorate and protective coating in construction wall all the fashion both at home and abroad in recent years, currently also be able to fast development and comprehensively apply in China.Flexible texture coating-artistic coating has been inherited the tradition of metope paint; And the utilization modern science and technology, producing can be through one little scraper, just can make like three-dimensional oil painting; Three-dimensional wallpaper; The metope statue, incredible artistic effects such as sandstone, marble, fossil, pearl face, metal fluorescence, facing modelled after an antique, illusion-colour can be brought into play unlimited intention.For a long time Chang Xin is applicable to that hotel, dining room, night club, office building and household increase modern elegance and romance.Be coated with the membrane pores people but also exist, easy absorption dust, laying dust are bought dirt, big, the insufficient inferior position of compactness of feed consumption.
Summary of the invention
The present invention has overcome rubber-emulsion paint and has not had splitting resistance, and the construction of true mineral varnish such as is difficult at defective, and constructional method can adopt roller coating, spray, smear multiple constructional method such as pressure, substitutes true mineral varnish and stone material, and construction is simple, and little to the body of wall load, resistance to cleavage is excellent.
The present invention adopts technical scheme to be:
A kind of flexible texture coating is made up of A component and B component, wherein said A component; According to weight percent meter; Comprise following moity, water 12%, HPMC 0.4%, elastic emulsion 8%, NXZ skimmer 0.2%, AMP-95 multifunctional assistant 0.3% are transferred pH value 8-9; Film coalescence aid 0.8%, LXE fungicidal preservative 0.1%, (40 ~ 120) order silica sand 78%, XG-60 thickening material 0.2%;
Wherein said B component is according to weight percent meter; Comprise following moity; SN-5040 dispersion agent 0.4%, F111 skimmer 0.4%, X-405 wetting agent 0.1%, film coalescence aid 0.5%, terepthaloyl moietie 1%, Natvosol 0.2%, multifunctional assistant 0.3%, fungicidal preservative 0.1%, 1250 order permanent white 5%, rutile titanium white powder 25%, calcined kaolin 1.9%, elastic emulsion 35%, benzene emulsion 10%, XG-60 thickening material 0.7%, R-2020 flow agent 0.3%; Said components and an amount of mill base are mixed, both got the B component;
According to weight percent meter, get 80% A component and 20% B component and stir, both flexible texture coating.
Further, described HPMC is 100000mPas.
Further, described film coalescence aid is an alcohol ester 12.
Further, described silica sand is made up of (40 ~ 80) order silica sand of 50% and (80-120) order silica sand of 28%.
Further, the globule size of described permanent white is 1250 orders.
Beneficial effect of the present invention:
Flexible texture coating of the present invention is to be base-material with special pure-acrylic emulsion, is the water-based high build paint of main stuffing with the natural granite stone flour.It is than common flat be coated with or elastic coating has more wear-resistant and cracking resistance advantage, and pliable and tough speciality is the be full of cracks of bridging body of wall effectively, and it is regional strongly that its excellent ultra-violet radiation resisting function is particularly useful for sunshine.See through the texture of stereo natural, show the aestheticism artistic style of building especially.Pliable and tough thick and heavy material is selected different instruments and construction gimmick for use, can create the grain effect of different style, makes architectural appearance have uniqueness, activity and individual character.
The present invention mainly adopts true stone starting material and other auxiliary agent, elastic emulsion etc., the Product Green environmental protection of producing; Easy construction, sprays, smears pressure and get final product at roller coating, replaces true mineral varnish and stone material; Be the fabulous finishing material of external wall of building, interior wall also can be used to decorate cultural wall etc.
Embodiment
are done further explanation below in conjunction with concrete embodiment to the present invention.
A kind of flexible texture coating; Form by A component and B component; Wherein said A component according to weight percent meter, comprises following moity; The HPMC 0.4% of water 12%, 100,000 viscosity, elastic emulsion 8%, NXZ skimmer 0.2%, AMP-95 multifunctional assistant 0.3% are transferred pH value 8-9; Alcohol ester 12 film coalescence aid 0.8%, LXE fungicidal preservative 0.1%, (40 ~ 80) order silica sand 50%, (80 ~ 120) order silica sand 28%, XG-60 thickening material 0.2%;
Wherein said B component is according to weight percent meter; Comprise following moity; SN-5040 dispersion agent 0.4%, F111 skimmer 0.4%, X-405 wetting agent 0.1%, alcohol ester 12 film coalescence aid 0.5%, terepthaloyl moietie 1%, Natvosol 0.2%, multifunctional assistant 0.3%, fungicidal preservative 0.1%, 1250 order permanent white 5%, rutile titanium white powder 25%, calcined kaolin 1.9%, elastic emulsion 35%, benzene emulsion 10%, XG-60 thickening material 0.7%, R-2020 flow agent 0.3%; Said components and an amount of mill base are mixed, both got the B component;
According to weight percent meter, get 80% A component and 20% B component and stir, both flexible texture coating.
Color can be added different mill bases and adjust according to different needs.

Claims (5)

1. flexible texture coating; It is characterized in that: form by A component and B component; Wherein said A component according to weight percent meter, comprises following moity; Water 12%, HPMC 0.4%, elastic emulsion 8%, NXZ skimmer 0.2%, AMP-95 multifunctional assistant 0.3% are transferred pH value 8-9; Film coalescence aid 0.8%, LXE fungicidal preservative 0.1%, (40 ~ 120) order silica sand 78%, XG-60 thickening material 0.2%;
Wherein said B component is according to weight percent meter; Comprise following moity; SN-5040 dispersion agent 0.4%, F111 skimmer 0.4%, X-405 wetting agent 0.1%, film coalescence aid 0.5%, terepthaloyl moietie 1%, Natvosol 0.2%, multifunctional assistant 0.3%, fungicidal preservative 0.1%, 1250 order permanent white 5%, rutile titanium white powder 25%, calcined kaolin 1.9%, elastic emulsion 35%, benzene emulsion 10%, XG-60 thickening material 0.7%, R-2020 flow agent 0.3%; Said components and an amount of mill base are mixed, both got the B component;
According to weight percent meter, get 80% A component and 20% B component and stir, both flexible texture coating.
2. flexible texture coating according to claim 1 is characterized in that: described HPMC is 100000mPas.
3. flexible texture coating according to claim 1 is characterized in that: described film coalescence aid is an alcohol ester 12.
4. flexible texture coating according to claim 1 is characterized in that: described silica sand is made up of (40 ~ 80) order silica sand of 50% and (80-120) order silica sand of 28%.
5. flexible texture coating according to claim 1 is characterized in that: the globule size of described permanent white is 1250 orders.
CN 201110425780 2011-12-19 2011-12-19 Paint with elastic texture Active CN102533039B (en)