CN104371464A - Sand-in-water paint and manufacturing method thereof - Google Patents
Sand-in-water paint and manufacturing method thereof Download PDFInfo
- Publication number
- CN104371464A CN104371464A CN201410558429.2A CN201410558429A CN104371464A CN 104371464 A CN104371464 A CN 104371464A CN 201410558429 A CN201410558429 A CN 201410558429A CN 104371464 A CN104371464 A CN 104371464A
- Authority
- CN
- China
- Prior art keywords
- water
- sand
- deionized water
- burnt
- complex thickener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a sand-in-water paint and a manufacturing method thereof. The invention aims to provide a paint with uneven use effect like a fire board and also provide a manufacturing method with the characteristics of simple technique and lower cost. The technical scheme is as follows: the sand-in-water paint comprises the following components: 1) material A: water-based resin, deionized water, assistant, pigment, kaolin, composite thickener and quartz sand; 2) material B: deionized water and protective adhesive; and 3) material C: water-based resin and composite thickener. The manufacturing method of the sand-in-water paint comprises the following steps: 1) uniformly mixing the deionized water, pigment, kaolin and composite thickener in the material A, adding the quartz sand and emulsion, and carrying out color matching; 2) uniformly mixing the material B; 3) mixing the material A and material B prepared in the steps 1) and 2), and granulating; 4) uniformly mixing the material C; and 5) carrying out shear mixing on the materials prepared in the steps 3) and 4).
Description
Technical field
The present invention relates to the making method of a kind of exterior coating and this coating.
Background technology
Grouan is the dalle that people like; Especially through the grouan (being called fired slab) of high temperature process, because surface is heated differential expansion difference, and produce texture and the visual effect of a little concavo-convex similar bush-hammered face, there is decoration and anti-skidding effect, be subject to the favor of many human consumers, but price is also more expensive.For this reason, someone attempts to study imitation products, adopts traditional water-water coating to produce the visual effect of similar fired slab; But because being a granulated into of water-water coating be divided into water and superfine paint filler, the color thus produced and texture effect not strong.
Summary of the invention
The object of the invention is to overcome the deficiency in above-mentioned background technology, a kind of water burnt-in sand coating and preparation method thereof is provided, the coating provided should have the rough result of use of similar fired slab, and the making method provided should have simple, the lower-cost feature of technique.
Technical scheme provided by the invention is:
A kind of water burnt-in sand coating, the composition comprised and weight part are:
1) A material:
Water-base resin 30-40, deionized water 10 ~ 30, auxiliary agent 3 ~ 5, pigment 5 ~ 10, kaolin 10 ~ 20, complex thickener 3 ~ 5, quartz sand 30 ~ 40;
2) B material:
Deionized water 94 ~ 98, protecting glue 2 ~ 6;
3) C material
Water-base resin 95-100, complex thickener 3 ~ 5;
Described complex thickener is mixed in 1:1 ratio by Natvosol and special gelatin; Described special gelatin is the one in hydroxypropylguar gum, gelatin, sodium alginate and carrageenin;
Described protecting glue is mixed in 8:2 ratio by lithium bentonite and neusilin;
Described water-base resin is pure-acrylic emulsion or fluorocarbon resin emulsion or organosilicon acrylic resin emulsion or fluorine silicon resin emulsion.
Described pigment is titanium dioxide, preferred rutile titanium white powder R975.
Kaolin fineness is not more than 1250 orders, and the fineness of quartz sand is not more than 120 orders;
Composition and the weight part of described water burnt-in sand coating are:
1) A material:
Water-base resin 30-40, deionized water 10 ~ 25, auxiliary agent 3 ~ 4, pigment 6 ~ 8, kaolin 10 ~ 15, complex thickener 3 ~ 4, quartz sand 30 ~ 40;
2) B material:
Deionized water 95 ~ 97, protecting glue 3 ~ 5;
3) C material
Water-base resin 95-97, complex thickener 3 ~ 5.
Composition and the weight part of described water burnt-in sand coating are:
1) A material:
Water-base resin 30.0, deionized water 10.0, auxiliary agent 3.0, pigment 7.0, kaolin 10.0, complex thickener 3.0, quartz sand 37.0;
2) B material:
Deionized water 95.0, protecting glue 5.0;
3) C material
Water-base resin 97.0, complex thickener 3.0.
Described auxiliary agent comprises cation dispersing agent, cationic wetting agents, film coalescence aid, sterilant, defoamer and frostproofer.
The making method of above-mentioned water burnt-in sand coating, carry out according to following steps:
1) deionized water in A being expected, pigment, kaolin, adds quartz sand and emulsion, then mixes colours as requested after complex thickener mixes;
2) B material is mixed;
3) by above-mentioned steps 1), 2) obtained A material, made into particulate form after the mixing of B material;
4) C is expected mixing and stirring;
5) by step 3) with step 4) obtained material shear-mixed, namely form the water burnt-in sand coating of different colours uniform particles distribution.
Described step 3) in grain diameter be 1-5mm.
The invention has the beneficial effects as follows: after the drying of water burnt-in sand paint spay-coating, present be not of uniform size, height not etc. and the small sand heap of irregular distribution, embody texture and the color of natural rock (especially fired slab) completely, there is extremely strong relief emulation visual effect, solving conventional water-water coating uses rear stereoscopic sensation strong, lacks the defect of texture.And complete processing is simple, employing be again the conventional raw materials had a large capacity and a wide range, therefore cost of manufacture is not high, is applicable to promoting the use of in the industry.
Embodiment
Thinking of the present invention is; If change the granulation composition in coating into quartz sand, the natural rock texture effect needed just can be obtained; Form the present invention at this point.
Embodiment 1
A kind of water burnt-in sand coating, the composition comprised and weight part are:
1) A material:
The complex thickener 3.0 that pure-acrylic emulsion 30.0, deionized water 10.0, auxiliary agent 3.0, titanium dioxide 7.0, kaolin 10.0, Natvosol and hydroxypropylguar gum mix in 1:1 ratio, quartz sand 37.0;
2) B material:
Deionized water 94, the protecting glue 6 that lithium bentonite and neusilin mix in 8:2 ratio;
3) C material
Pure-acrylic emulsion 95, the complex thickener 5.0 that Natvosol and hydroxypropylguar gum mix in 1:1 ratio;
The making method of this water burnt-in sand coating, carry out according to following steps:
1) deionized water in A being expected, titanium dioxide, kaolin, auxiliary agent, complex thickener mixes, and adds quartz sand and pure-acrylic emulsion after high speed dispersion is even, then toning as requested (will be as requested during recommendation shading process: A material toning, A material is divided into several parts, the no color of furnishing);
2) B material is mixed
3) by above-mentioned steps 1), 2) obtained A, B material mixing, then stir and make particle shape one by one; Grain diameter controls as 3mm;
4) C is expected mixing and stirring;
5) by step 3) obtained material and step 4) obtained material mix, i.e. the water burnt-in sand coating that distributes of formation different colours uniform particles.
Embodiment 2
A kind of water burnt-in sand coating, the composition comprised and weight part are:
1) A material:
Fluorine carbon emulsion 30.0, deionized water 10.0, titanium dioxide 6.0, kaolin 12.0, the complex thickener 4.0 that auxiliary agent 3.0, Natvosol and gelatin mix in 1:1 ratio, quartz sand 35;
2) B material:
Deionized water 96, the protecting glue 4 that lithium bentonite and neusilin mix in 8:2 ratio;
3) C material
Fluorocarbon resin emulsion 96, the complex thickener 4.0 that Natvosol and gelatin mix in 1:1 ratio;
The making method of this water burnt-in sand coating, carry out according to following steps:
1) deionized water in A being expected, titanium dioxide, kaolin, auxiliary agent, complex thickener mixes, and adds quartz sand and fluorine carbon emulsion, then mix colours as requested after high speed dispersion is even;
2) B material is mixed
3) by above-mentioned steps 1), 2) obtained A, B material mixing, then stir and make particle shape one by one; Grain diameter controls as 1mm;
4) C is expected mixing and stirring;
5) by step 3) obtained material and step 4) obtained material mix, i.e. the water burnt-in sand coating that distributes of formation different colours uniform particles.
Embodiment 3
A kind of water burnt-in sand coating, the composition comprised and weight part are:
1) A material:
Organosilicon acrylic resin emulsion 35.0, deionized water 10.0, titanium dioxide 6.0, auxiliary agent 3.5, kaolin 15.0, complex thickener 3.0, quartz sand 31.0 that Natvosol and carrageenin mix in 1:1 ratio;
2) B material:
Deionized water 96.0, the protecting glue 4 that lithium bentonite and neusilin mix in 8:2 ratio;
3) C material
Organosilicon acrylic resin emulsion 95, the complex thickener 5.0 that Natvosol and carrageenin mix in 1:1 ratio;
The making method of this water burnt-in sand coating, carry out according to following steps:
1) deionized water in A being expected, titanium dioxide, kaolin, auxiliary agent, complex thickener mixes, and adds quartz sand and organosilicon acrylic resin emulsion, then mix colours as requested after high speed dispersion is even;
2) B material is mixed
3) by above-mentioned steps 1), 2) obtained A, B material mixing, then stir and make particle shape one by one; Grain diameter controls as 5mm;
4) C is expected mixing and stirring;
5) by step 3) obtained material and step 4) obtained material mix, i.e. the water burnt-in sand coating that distributes of formation different colours uniform particles.
The auxiliary agent that above-described embodiment adopts comprises cation dispersing agent, cationic wetting agents, film coalescence aid, sterilant, defoamer and frostproofer successively; Recommendation ratio between each composition is 3: 2: 6: 1: 10.Each composition of described auxiliary agent is the conventional variety for coating.
In embodiment 3, cation dispersing agent is SUA-110; Cationic wetting agents is SUA-030; Film coalescence aid is W825; Sterilant is QK20; Defoamer is NXZ; Frostproofer is propylene glycol.
Claims (5)
1. a water burnt-in sand coating, the composition comprised and weight part are:
1) A material:
Water-base resin 30-40, deionized water 10 ~ 30, auxiliary agent 3 ~ 5, pigment 5 ~ 10, kaolin 10 ~ 20, complex thickener 3 ~ 5, quartz sand 30 ~ 40;
2) B material:
Deionized water 94 ~ 98, protecting glue 2 ~ 6;
3) C material
Water-base resin 95-97, complex thickener 3 ~ 5;
Described complex thickener is mixed in 1:1 ratio by Natvosol and special gelatin; Described special gelatin is the one in hydroxypropylguar gum, gelatin, sodium alginate and carrageenin;
Described protecting glue is mixed in 8:2 ratio by lithium bentonite and neusilin;
Described water-base resin is pure-acrylic emulsion or fluorocarbon resin emulsion or organosilicon acrylic resin emulsion or fluorine silicon resin emulsion;
Described auxiliary agent comprises cation dispersing agent, cationic wetting agents, film coalescence aid, sterilant, defoamer and frostproofer;
Described pigment is titanium dioxide.
2. water burnt-in sand coating according to claim 1, is characterized in that the composition of this water burnt-in sand coating and weight part are:
1) A material:
Water-base resin 30-40, deionized water 10 ~ 25, auxiliary agent 3 ~ 4, pigment 6 ~ 8, kaolin 10 ~ 15, complex thickener 3 ~ 4, quartz sand 30 ~ 40;
2) B material:
Deionized water 95 ~ 97, protecting glue 3 ~ 5;
3) C material
Water-base resin 95-97, complex thickener 3 ~ 5.
3. water burnt-in sand coating according to claim 2, is characterized in that the composition that this water burnt-in sand coating comprises and weight part are:
1) A material:
Water-base resin 30.0, deionized water 10.0, auxiliary agent 3.0, pigment 7.0, kaolin 10.0, complex thickener 3.0, quartz sand 37.0;
2) B material:
Deionized water 95.0, protecting glue 5.0;
3) C material
Water-base resin 97.0, complex thickener 3.0.
4. the making method of water burnt-in sand coating according to claim 1, carry out according to following steps:
1) deionized water in A being expected, pigment, kaolin, adds quartz sand after complex thickener mixes, then mixes colours as requested;
2) B material is uniformly dispersed
3) by above-mentioned steps 1), 2) obtained A material, B material be uniformly mixed made into particulate form according to 1:1;
4) C is expected mixing and stirring;
5) by step 3) with step 4) obtained material shear-mixed, namely form the water burnt-in sand coating of different colours uniform particles distribution.
5. the making method of water burnt-in sand coating according to claim 4, is characterized in that described step 3) in grain diameter be 1-5mm.