CN109370334A - A kind of insulating moulding coating and preparation method thereof for aqueous acrylamide acid type finishing coat - Google Patents
A kind of insulating moulding coating and preparation method thereof for aqueous acrylamide acid type finishing coat Download PDFInfo
- Publication number
- CN109370334A CN109370334A CN201811089880.9A CN201811089880A CN109370334A CN 109370334 A CN109370334 A CN 109370334A CN 201811089880 A CN201811089880 A CN 201811089880A CN 109370334 A CN109370334 A CN 109370334A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- insulating moulding
- moulding coating
- finishing coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat, by weight, including following raw material: 20-60 parts of acrylic emulsion resin, 10-15 parts of hollow glass micropearl, 10-15 parts of pigment, 10-30 parts of filler, 0.1-2 parts of wetting agent, 0.1-2 parts of antifreezing agent, 0.1-2 parts of thickener, 0.1-2 parts of dispersing agent, 0.1-2 parts of neutralizer, 0.1-2 parts of defoaming agent, 0.1-2 parts of levelling agent, 0.1-5 parts of coalescing agent, 10-30 parts of water.Acrylic type finishing coat insulating moulding coating flat appearance of the invention, it is interior that there is bead micropore, isolation heat conductivity, the flexibility having had, the adhesion strength that weatherability, water resistance, easy act, stain resistance and exterior wall are possessed.
Description
Technical field
The present invention relates to a kind of insulating moulding coatings and preparation method thereof for aqueous acrylamide acid type finishing coat.
Background technique
The one-component quick-drying finishing coat that acrylic acid top-coat is made of thermoplastic acrylic resin, pigment, auxiliary agent, solvent etc..
The paint has good colour retention and workability.Protection and dress are provided for outdoor wall, steel construction, mechanical equipment, motor etc.
The effect of decorations also can be used as the finishing coat of embossment figure layer system.
Suitable for building the acrylic acid top-coat of painting or metal surface, pass through isolation heat transfer in substrate surface with insulating moulding coating
Mode block contact and conduction of the ultraviolet light heat with substrate, can be applied to common external wall and metal storage
The industries such as tank, metal container, for insulating moulding coating due to technical restriction, the country is very few for the exploitation of insulating moulding coating at present, has
Relatively good market prospects.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides a kind of heat-insulated paintings for aqueous acrylamide acid type finishing coat
Material, suitable for building painting or metal surface, good heat-insulation effect has preferable market prospects.
Invention also provides the preparation methods of above-mentioned insulating moulding coating.
To achieve the goals above, a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat that the present invention uses, by weight
It measures part to count, including following raw material: 20-60 parts of acrylic emulsion resin, 10-15 parts of hollow glass micropearl, 10-15 parts of pigment,
10-30 parts of filler, 0.1-2 parts of wetting agent, 0.1-2 parts of antifreezing agent, 0.1-2 parts of thickener, 0.1-2 parts of dispersing agent, neutralizer
0.1-2 parts, 0.1-2 parts of defoaming agent, 0.1-2 parts of levelling agent, 0.1-5 parts of coalescing agent, 10-30 parts of water.
As an improvement, the solid content of the acrylic emulsion resin is 20-50%.
As an improvement, the average particle size of the hollow glass micropearl is 200-800nm；The pigment using titanium dioxide,
The mixing of one or more of powdered whiting and precipitated calcium carbonate, the average mesh number of pigment are 300-1000 mesh；Described
Filler uses the mixing of one or more of calcined kaolin, mica powder, talcum powder, and the average mesh number of filler is 300-1000
Mesh.
As an improvement, one or more of mixing that the wetting agent is produced using DOW Chemical.
As an improvement, the antifreezing agent is higher than 250 DEG C of novel alcohols antifreezing agent using boiling point.
As an improvement, the thickener uses cellulose type and acrylic type thickener.
As an improvement, the dispersing agent uses polycarboxylic acids ammonium salt class dispersing agent.
As an improvement, the neutralizer uses the ammonium hydroxide of 30% concentration.
As an improvement, the defoaming agent uses the defoaming agent of mineral oil type；The levelling agent uses DOW Chemical
The mixing of one or more of product；The coalescing agent uses Yi Shiman alcohol ester 12.
In addition, the present invention also provides the preparation method for the insulating moulding coating for being used for aqueous acrylamide acid type finishing coat described in one kind,
Water, wetting agent, antifreezing agent, thickener and dispersing agent are sequentially added into dispersion machine in the case where stirring at low speed, low speed adds after being uniformly dispersed
Enter hollow glass micropearl, be added pigment, filler afterwards, dispersion machine is added acrylic emulsion resin after stirring at low speed, it is rear be added at
Film auxiliary agent and neutralizer, defoaming agent, levelling agent, after then dispersing 15min, control viscosity can be prepared by required insulating moulding coating.
Compared with prior art, acrylic type finishing coat insulating moulding coating flat appearance of the invention, it is interior to have bead micro-
Hole, isolation heat conductivity, the flexibility having had, weatherability, water resistance, easy act, stain resistance and exterior wall are possessed
Adhesion strength.
Specific embodiment
In order to make the objectives, technical solutions and advantages of the present invention clearer, the present invention is carried out below further detailed
It describes in detail bright.However, it should be understood that the specific embodiments described herein are merely illustrative of the present invention, it is not limited to this hair
Bright range.
Unless otherwise defined, all technical terms and scientific terms used herein are led with technology of the invention is belonged to
The normally understood meaning of the technical staff in domain is identical, and term as used herein in the specification of the present invention is intended merely to retouch
State the purpose of specific embodiment, it is not intended that in the limitation present invention.
A kind of insulating moulding coating for aqueous acrylamide acid type finishing coat, by weight, including following raw material: acrylic type cream
It is 20-60 parts of liquid resin, 10-15 parts of hollow glass micropearl, 10-15 parts of pigment, 10-30 parts of filler, 0.1-2 parts of wetting agent, antifreeze
0.1-2 parts of agent, 0.1-2 parts of thickener, 0.1-2 parts of dispersing agent, 0.1-2 parts of neutralizer, 0.1-2 parts of defoaming agent, levelling agent 0.1-2
Part, 0.1-5 parts of coalescing agent, 10-30 parts of water.
The solid content of the acrylic emulsion resin is 20-50%.
The average particle size of the hollow glass micropearl is 200-800nm；The pigment is using titanium dioxide, calcining kaolinite
The mixing of one or more of soil, powdered whiting and precipitated calcium carbonate, the average mesh number of pigment are 300-1000 mesh；It is described
Filler use the mixing of one or more of mica powder, talcum powder, the average mesh number of filler is 300-1000 mesh.
One or more of mixing that the wetting agent is produced using DOW Chemical.
The antifreezing agent is higher than 250 DEG C of novel alcohols antifreezing agent using boiling point.
The thickener uses cellulose type and acrylic type thickener.
The dispersing agent uses polycarboxylic acids ammonium salt class dispersing agent.
The neutralizer uses the ammonium hydroxide of 30% concentration.
The defoaming agent uses the defoaming agent of mineral oil type；The levelling agent is using one in DOW Chemical product
Kind or several mixing；The coalescing agent uses Yi Shiman alcohol ester 12.
In addition, the present invention also provides the preparation method for the insulating moulding coating for being used for aqueous acrylamide acid type finishing coat described in one kind,
Water, wetting agent, antifreezing agent, thickener and dispersing agent are sequentially added into dispersion machine, one component low speed of every addition in the case where stirring at low speed
After stirring 3~5min, next component is added；Hollow glass micropearl is added after low speed is uniformly dispersed；Pigment is added afterwards, fills out
Expect, acrylic emulsion resin is added after stirring at low speed under dispersion machine, it is rear that coalescing agent and neutralizer, defoaming agent, stream is added
Flat agent, after then dispersing 15min, control viscosity can be prepared by required insulating moulding coating.
The present invention need to handle material surface, build painting when building or metal surface carry out surface construction
BGD cement board surface can carry out after need to being polished, being soaked, and metal surface need to carry out polishing derusting, and decontamination, oil removing can carry out
Spraying.
The spraying method of aqueous acrylamide acid type finishing coat insulating moulding coating of the invention is realized in that:
1) insulating moulding coating of the invention after mixing evenly, carries out spraying operation, spray gun is away from workpiece surface under high-pressure spray gun
Not less than 20cm, coating is sprayed on processed workpiece by angle of gun and workpiece surface at 70-90 ° of angle；
2) after the workpiece sprayed being placed 3d at room temperature.
Embodiment 1
A kind of insulating moulding coating for aqueous acrylamide acid type finishing coat, by weight, including following raw material: acrylic type cream
20 parts of liquid resin, 10 parts of hollow glass micropearl, 10 parts of pigment, 10 parts of filler, 0.1 part of wetting agent, 0.1 part of antifreezing agent, thickener
0.1 part, 0.1 part of dispersing agent, 0.1 part of neutralizer, 0.1 part of defoaming agent, 0.1 part of levelling agent, 0.1 part of coalescing agent, 10 parts of water.
The insulating moulding coating for aqueous acrylamide acid type finishing coat, by water, wetting agent, antifreezing agent, thickener and dispersing agent
Dispersion machine is sequentially added in the case where stirring at low speed, hollow glass micropearl is added in low speed after being uniformly dispersed, pigment, filler are added afterwards, point
Acrylic emulsion resin is added in scattered machine after stirring at low speed, rear that coalescing agent and neutralizer, defoaming agent, levelling agent is added, so
After dispersing 15min afterwards, control viscosity can be prepared by required insulating moulding coating.
Embodiment 2
A kind of insulating moulding coating for aqueous acrylamide acid type finishing coat, by weight, including following raw material: acrylic type cream
40 parts of liquid resin, 12 parts of hollow glass micropearl, 13 parts of pigment, 20 parts of filler, 1 part of wetting agent, 1 part of antifreezing agent, 1 part of thickener,
1 part of dispersing agent, 1 part of neutralizer, 1 part of defoaming agent, 1 part of levelling agent, 3 parts of coalescing agent, 20 parts of water.
The insulating moulding coating for aqueous acrylamide acid type finishing coat, by water, wetting agent, antifreezing agent, thickener and dispersing agent
Dispersion machine is sequentially added in the case where stirring at low speed, hollow glass micropearl is added in low speed after being uniformly dispersed, pigment, filler are added afterwards, point
Acrylic emulsion resin is added in scattered machine after stirring at low speed, rear that coalescing agent and neutralizer, defoaming agent, levelling agent is added, so
After dispersing 15min afterwards, control viscosity can be prepared by required insulating moulding coating.
Embodiment 3
A kind of insulating moulding coating for aqueous acrylamide acid type finishing coat, by weight, including following raw material: acrylic type cream
60 parts of liquid resin, 15 parts of hollow glass micropearl, 15 parts of pigment, 30 parts of filler, 2 parts of wetting agent, 2 parts of antifreezing agent, 2 parts of thickener,
2 parts of dispersing agent, 2 parts of neutralizer, 2 parts of defoaming agent, 2 parts of levelling agent, 5 parts of coalescing agent, 30 parts of water.
The insulating moulding coating for aqueous acrylamide acid type finishing coat, by water, wetting agent, antifreezing agent, thickener and dispersing agent
Dispersion machine is sequentially added in the case where stirring at low speed, hollow glass micropearl is added in low speed after being uniformly dispersed, pigment, filler are added afterwards, point
Acrylic emulsion resin is added in scattered machine after stirring at low speed, rear that coalescing agent and neutralizer, defoaming agent, levelling agent is added, so
After dispersing 15min afterwards, control viscosity can be prepared by required insulating moulding coating.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modification, equivalent replacement or improvement etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (10)
1. a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat, which is characterized in that by weight, including following raw material:
20-60 parts of acrylic emulsion resin, 10-15 parts of hollow glass micropearl, 10-15 parts of pigment, 10-30 parts of filler, wetting agent
0.1-2 parts, 0.1-2 parts of antifreezing agent, 0.1-2 parts of thickener, 0.1-2 parts of dispersing agent, 0.1-2 parts of neutralizer, defoaming agent 0.1-2
Part, 0.1-2 parts of levelling agent, 0.1-5 parts of coalescing agent, 10-30 parts of water.
2. a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat according to claim 1, which is characterized in that described third
The solid content of olefin(e) acid type emulsion resin is 20-50%.
3. a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat according to claim 1, which is characterized in that described
The average particle size of hollow glass micropearl is 200-800nm；The pigment is using in titanium dioxide, powdered whiting and precipitated calcium carbonate
One or more of mixing, the average mesh number of pigment is 300-1000 mesh；The filler uses calcined kaolin, mica
The mixing of one or more of powder, talcum powder, the average mesh number of filler are 300-1000 mesh.
4. a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat according to claim 1, which is characterized in that described
One or more of mixing that wetting agent is produced using DOW Chemical.
5. a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat according to claim 1, which is characterized in that described
Antifreezing agent is higher than 250 DEG C of novel alcohols antifreezing agent using boiling point.
6. a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat according to claim 1, which is characterized in that described
Thickener uses cellulose type and acrylic type thickener.
7. a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat according to claim 1, which is characterized in that described
Dispersing agent uses polycarboxylic acids ammonium salt class dispersing agent.
8. a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat according to claim 1, which is characterized in that described
Neutralizer uses the ammonium hydroxide of 30% concentration.
9. a kind of insulating moulding coating for aqueous acrylamide acid type finishing coat according to claim 1, which is characterized in that described
Defoaming agent uses the defoaming agent of mineral oil type；The levelling agent is mixed using one or more of DOW Chemical product
It closes；The coalescing agent uses Yi Shiman alcohol ester 12.
10. being used for the insulating moulding coating of aqueous acrylamide acid type finishing coat described in a kind of any one of claim 1-9, which is characterized in that will
Water, wetting agent, antifreezing agent, thickener and dispersing agent sequentially add dispersion machine in the case where stirring at low speed, and low speed is added after being uniformly dispersed
Pigment, filler is added in hollow glass micropearl afterwards, and acrylic emulsion resin is added in dispersion machine after stirring at low speed, rear that film forming is added
Auxiliary agent and neutralizer, defoaming agent, levelling agent, after then dispersing 15min, control viscosity can be prepared by required insulating moulding coating.