CN102786260B - Environment-friendly diatom emulsion interior wall decorative material and preparation method thereof - Google Patents
Environment-friendly diatom emulsion interior wall decorative material and preparation method thereof Download PDFInfo
- Publication number
- CN102786260B CN102786260B CN201210311965.3A CN201210311965A CN102786260B CN 102786260 B CN102786260 B CN 102786260B CN 201210311965 A CN201210311965 A CN 201210311965A CN 102786260 B CN102786260 B CN 102786260B
- Authority
- CN
- China
- Prior art keywords
- environment
- decorative material
- internal wall
- friendly type
- breast
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses environment-friendly diatom emulsion interior wall decorative material. The environment-friendly diatom emulsion interior wall decorative material comprises, by mass ratio, 9%-15% of diatomite, 6%-10% of attapulgite powder, 7%-10% of calcined kaolin, 1.7%-3% of titanium dioxide, 0.2%-0.4% of nano-titania, 5%-9% of calcite powder, 0.3%-0.4% of carboxy methyl cellulose, 0.3% of flatting agent, 0.3% of dispersant, 0.3% of preservative, 0.6%-1.2% of mildew preventive, 8%-12% of re-dispersible emulsion powder, and the balance of distilled water. The invention also discloses a preparation method of the environment-friendly diatom emulsion interior wall decorative material. The preparation method includes proportionally adding the ingredients into a dispersing barrel, using a high-speed disperser to evenly disperse, and filtering to obtain the finished product. The preparation method of the environment-friendly diatom emulsion interior wall decorative material is simple, construction is simple and convenient, materials are saved, and the environment-friendly diatom emulsion interior wall decorative material is higher in efficiency of absorbing harmful matters in air.
Description
Technical field
The present invention relates to a kind of decorative material for internal wall and preparation method thereof, particularly a kind of environment-friendly type diatom breast decorative material for internal wall and preparation method thereof.
Background technology
Current diatom ooze decorative material for internal wall is on the market mainly blade coating type powder coating, is again diatom ooze, and China recent years starts development and production, develops gradually so far market.But above-described diatom ooze has a very great shortcoming, be exactly that working procedure is loaded down with trivial details, must just can obtain needed decorative effect by professional construction crew's operation.
Summary of the invention
The object of the invention is to, provide a kind of construction simple and convenient, save material, to environment-friendly type diatom breast decorative material for internal wall that in air, objectionable impurities adsorption rate is high and preparation method thereof.
For achieving the above object, technical scheme provided by the invention is: a kind of environment-friendly type diatom breast decorative material for internal wall, the composition with following mass ratio: diatomite 9% ~ 15%, attapulgite 6% ~ 10%, calcined kaolin 7% ~ 10%, titanium dioxide 1.7% ~ 3%, nano titanium oxide 0.2% ~ 0.4%, coarse whiting 5% ~ 9%, Walocel MT 20.000PV 0.3% ~ 0.4%, flow agent 0.3%, dispersion agent 0.3%, sanitas 0.3%, mould inhibitor 0.6% ~ 1.2%, redispersible latex powder 8% ~ 12%, all the other are distilled water.
In the present invention, the preferred mass of the various compositions of described diatom breast ratio is: diatomite 10.8%, attapulgite 8%, calcined kaolin 7.5%, titanium dioxide 1.8%, nano titanium oxide 0.3%, coarse whiting 7.3%, Walocel MT 20.000PV 0.4%, flow agent 0.3%, dispersion agent 0.3%, sanitas 0.3%, mould inhibitor 1%, redispersible latex powder 11%, distilled water 51%.
In the present invention, described diatomite is preferably 325 orders.
In the present invention, described attapulgite and the preferred whiteness of described calcined kaolin are greater than 90, and calcined kaolin is 800 orders preferably; Described coarse whiting whiteness is greater than 80, preferably 1500 orders.
In the present invention, described titanium dioxide is preferably anatase titanium dioxide, and content of titanium dioxide is greater than 95%.
In the present invention, described nano titanium oxide preferably 10 nm to 50nm.
In the present invention, described Walocel MT 20.000PV is white, and molecular weight is 20000.
A preparation method for environment-friendly type diatom breast decorative material for internal wall, according to above-described environment-friendly type diatom breast decorative material for internal wall, adds various components in proportion and disperses in bucket, uses high speed dispersor to be uniformly dispersed, and is packaged to be finished product after filtration.
The invention has the beneficial effects as follows: preparation method is simple, constructional method is identical with conventional wall paint, simpler than diatom ooze construction, do not need professional training workmen, the thickness of roller coat can be thinner, saves material, high to objectionable impurities adsorption rate in air, can also releasing negative oxygen ion.
Embodiment
Embodiment 1:
Take that to prepare double centner diatom breast be example, according to the quality sampling of following various components, 325 10.8 kilograms, order diatomite, whiteness is greater than 8 kilograms of 90 attapulgites, whiteness is greater than 7.5 kilograms of 90 800 order calcined kaolins, 1.8 kilograms of anatase titanium dioxides, 0.3 kilogram of nano titanium oxide, whiteness is greater than 7.3 kilograms of 80 1500 order coarse whitings, molecular weight is 0.4 kilogram of 20000 Walocel MT 20.000PV, 0.3 kilogram of flow agent, 0.3 kilogram of dispersion agent, 0.3 kilogram of sanitas, 1 kilogram of mould inhibitor, 11 kilograms of redispersible latex powders, 51 kilograms of distilled water, above various components are mixed.If the coloured requirement of client, adds mineral dye in right amount according to required color, then join and disperse in bucket, use high speed dispersor to be uniformly dispersed, after filtration, be packaged to be finished product.Finished product directly roller coat is on interior wall, identical with common wall paint using method.
Embodiment 2:
Take that to prepare double centner diatom breast be example, according to the quality sampling of following various components, 325 9 kilograms, order diatomite, whiteness is greater than 10 kilograms of 90 attapulgites, whiteness is greater than 8 kilograms of 90 800 order calcined kaolins, 3 kilograms of anatase titanium dioxides, 0.3 kilogram of nano titanium oxide, whiteness is greater than 7 kilograms of 80 1500 order coarse whitings, molecular weight is 0.3 kilogram of 20000 Walocel MT 20.000PV, 0.3 kilogram of flow agent, 0.3 kilogram of dispersion agent, 0.3 kilogram of sanitas, 1 kilogram of mould inhibitor, 8.5 kilograms of redispersible latex powders, 52 kilograms of distilled water, above various components are mixed.If the coloured requirement of client, adds mineral dye in right amount according to required color, then join and disperse in bucket, use high speed dispersor to be uniformly dispersed, after filtration, be packaged to be finished product.Finished product directly roller coat is on interior wall, identical with common wall paint using method.
Embodiment 3:
Take that to prepare double centner diatom breast be example, according to the quality sampling of following various components, 325 15 kilograms, order diatomite, whiteness is greater than 7 kilograms of 90 attapulgites, whiteness is greater than 7.3 kilograms of 90 800 order calcined kaolins, 2 kilograms of anatase titanium dioxides, 0.2 kilogram of nano titanium oxide, whiteness is greater than 9 kilograms of 80 1500 order coarse whitings, molecular weight is 0.4 kilogram of 20000 Walocel MT 20.000PV, 0.3 kilogram of flow agent, 0.3 kilogram of dispersion agent, 0.3 kilogram of sanitas, 1.2 kilograms of mould inhibitors, 8 kilograms of redispersible latex powders, 49 kilograms of distilled water, above various components are mixed.If the coloured requirement of client, adds mineral dye in right amount according to required color, then join and disperse in bucket, use high speed dispersor to be uniformly dispersed, after filtration, be packaged to be finished product.Finished product directly roller coat is on interior wall, identical with common wall paint using method.
Above embodiment is the object for giving an example and illustrating just, rather than the present invention is limited to described embodiment, and more kinds of variants and modifications of making according to the present invention, all drops in protection scope of the present invention.
Claims (8)
1. environment-friendly type diatom breast decorative material for internal wall, it is characterized in that, the composition with following mass ratio: diatomite 9% ~ 15%, attapulgite 6% ~ 10%, calcined kaolin 7% ~ 10%, titanium dioxide 1.7% ~ 3%, nano titanium oxide 0.2% ~ 0.4%, coarse whiting 5% ~ 9%, Walocel MT 20.000PV 0.3% ~ 0.4%, flow agent 0.3%, dispersion agent 0.3%, sanitas 0.3%, mould inhibitor 0.6% ~ 1.2%, redispersible latex powder 8% ~ 12%, all the other are distilled water.
2. a kind of environment-friendly type diatom breast decorative material for internal wall according to claim 1, it is characterized in that, the preferred mass ratio of the various compositions of described diatom breast is: diatomite 10.8%, attapulgite 8%, calcined kaolin 7.5%, titanium dioxide 1.8%, nano titanium oxide 0.3%, coarse whiting 7.3%, Walocel MT 20.000PV 0.4%, flow agent 0.3%, dispersion agent 0.3%, sanitas 0.3%, mould inhibitor 1%, redispersible latex powder 11%, distilled water 51%.
3. a kind of environment-friendly type diatom breast decorative material for internal wall according to claim 1, is characterized in that: described diatomite is preferably 325 orders.
4. a kind of environment-friendly type diatom breast decorative material for internal wall according to claim 1, is characterized in that: described attapulgite and the preferred whiteness of described calcined kaolin are greater than 90, and calcined kaolin is 800 orders preferably; Described coarse whiting whiteness is greater than 80, preferably 1500 orders.
5. a kind of environment-friendly type diatom breast decorative material for internal wall according to claim 1, is characterized in that: described titanium dioxide is preferably anatase titanium dioxide, and content of titanium dioxide is greater than 95%.
6. a kind of environment-friendly type diatom breast decorative material for internal wall according to claim 1, is characterized in that: described nano titanium oxide preferably 10 nm to 50nm.
7. a kind of environment-friendly type diatom breast decorative material for internal wall according to claim 1, is characterized in that: described Walocel MT 20.000PV is white, and molecular weight is 20000.
8. the preparation method of environment-friendly type diatom breast decorative material for internal wall, it is characterized in that: according to the environment-friendly type diatom breast decorative material for internal wall described in any one in claim 1-7, various components are added in proportion and disperseed in bucket, use high speed dispersor to be uniformly dispersed, after filtration, be packaged to be finished product.