CN105693136A - Kieselguhr wall material with Milan shadow style and construction method thereof - Google Patents
Kieselguhr wall material with Milan shadow style and construction method thereof Download PDFInfo
- Publication number
- CN105693136A CN105693136A CN201610146117.XA CN201610146117A CN105693136A CN 105693136 A CN105693136 A CN 105693136A CN 201610146117 A CN201610146117 A CN 201610146117A CN 105693136 A CN105693136 A CN 105693136A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- order
- wall material
- kieselguhr
- milan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kieselguhr wall material with the Milan shadow style and a construction method thereof, and belongs to the field of building materials. The kieselguhr wall material with the Milan shadow style is prepared from, by weight, 10-38 parts of 200-700-mesh kieselguhr, 10-40 parts of 700-1400-mesh shell powder, 8-50 parts of 80-1000-mesh natural marble dust, 5-35 parts of 600-1600-mesh rutile powder, 15-65 parts of 500-1200-mesh silica flour, 5-45 parts of 250-600-mesh malachite flour, 1-25 parts of 300-900-mesh attapulgite powder, 1-8 parts of nanometer titania, 0.1-2 parts of methylcellulose and 1-25 parts of redispersible emulsion powder. After construction is performed on the wall by means of the kieselguhr wall material and the construction method thereof, and the finished product effect is attractive.
Description
Technical field
The present invention relates to building material field, particularly relate to kieselguhr wall material and the construction method thereof with Milan shadow style。
Background technology
Kieselguhr is a kind of biogenic silicastone, it mainly by ancient times diatom remains formed, there is the characteristics such as exquisiteness, loose, light weight, porous, water absorption and permeability are strong。Along with people are more and more higher to the requirement of the living environment feature of environmental protection, kieselguhr is increasingly becoming a kind of very popular new indoor decoration material, with the addition of diatomaceous wall material and has and regulate the room temperature, eliminate the advantages such as abnormal flavour, absorption and decomposing harmful substances。At present, although utilizing kieselguhr wall material can produce certain texture on wall body surface, ornamental to increase it, but still have the space of improvement in this respect。
A large amount of valuable culture and arts legacy and famous historic site are contained in this city, Milan, centered by the seat of honour cathedral of trecento Italian Architecture elite, it is filled with century minor details sadly beautiful graceful and restrained and to the hope of new century and mist illusion, shows mankind's romance tenderness and the benz that future is yearned for。The fine and smooth building decoration style being rich in again artistic color receives generally liking of people。If but Milan architectural style traditionally is decorated, build the effect of shadow of great characteristic, long in time limit, costly, seriously limit its application。
If it is possible to provide a kind of kieselguhr wall material close with Milan building decoration style, then necessarily can meet people to a certain extent to the ornamental requirement of kieselguhr wall material。
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of kieselguhr wall material with Milan shadow style and construction method thereof。
For solving above-mentioned technical problem, the present invention provides technical scheme as follows:
A kind of kieselguhr wall material with Milan shadow style, containing, for example the component of lower weight portion:
200-700 order kieselguhr: 10-38 weight portion；
700-1400 order conch meal: 10-40 weight portion；
The natural marble dust of 80-1000 order: 8-50 weight portion；
600-1600 order golden red stone powder: 5-35 weight portion；
500-1200 order silica flour: 15-65 weight portion；
250-600 order peafowl stone powder: 5-45 weight portion；
300-900 order attapulgite powder: 1-25 weight portion；
Nano titanium oxide: 1-8 weight portion；
Methylcellulose: 0.1-2 weight portion；
Redispersible latex powder: 1-25 weight portion。
Further, there is described in the kieselguhr wall material component possibly together with following weight portion of Milan shadow style:
Inorganic pigment: 1-15 weight portion；
Preferably, described in there is the kieselguhr wall material of Milan shadow style, each constituent content is as follows:
300-600 order kieselguhr: 15-30 weight portion；
800-1200 order conch meal: 15-30 weight portion；
The natural marble dust of 120-800 order: 12-40 weight portion；
800-1500 order golden red stone powder: 10-25 weight portion；
600-1000 order silica flour: 20-50 weight portion；
325-500 order peafowl stone powder: 10-30 weight portion；
400-800 order attapulgite powder: 6-15 weight portion；
Nano titanium oxide: 2-5 weight portion；
Methylcellulose: 0.4-1.5 weight portion；
Redispersible latex powder: 4-18 weight portion。
Further, there is described in the kieselguhr wall material component possibly together with following weight portion of Milan shadow style:
Inorganic pigment: 1-15 weight portion；
It is highly preferred that described in there is the kieselguhr wall material of Milan shadow style, each constituent content is as follows:
300-600 order kieselguhr: 23 weight portions；
800-1200 order conch meal: 26 weight portions；
The natural marble dust of 120-800 order: 30 weight portions；
800-1500 order golden red stone powder: 18 weight portions；
600-1000 order silica flour: 38 weight portions；
325-500 order peafowl stone powder: 18 weight portions；
400-800 order attapulgite powder: 11 weight portions；
Nano titanium oxide: 3 weight portions；
Methylcellulose: 0.9 weight portion；
Redispersible latex powder: 10 weight portions。
Further, there is described in the kieselguhr wall material component possibly together with following weight portion of Milan shadow style:
Inorganic pigment: 8 weight portions。
Wherein, the above kieselguhr selects Primary Study of Choosing Diatomite。
The preparation method of the above-mentioned kieselguhr wall material with Milan shadow style is: is mixed according to corresponding parts by weight by mentioned component, stirs。
A kind of construction method of the above-mentioned kieselguhr wall material with Milan shadow style, including:
Step 1: wall body is carried out base treatment；
Step 2: by ratio mix homogeneously according to weight ratio 1:0.45-0.65 of kieselguhr wall material and water；
Step 3: batch scrape two times constructions, after wherein first pass is criticized and is scraped, THICKNESS CONTROL at 0.3-0.5mm, entirety metope non junction, after parching completely, smooth in wall material surface finish with the dry sand of 180-600 order, remove floating dust with hairbrush；Then criticize and scrape second time, THICKNESS CONTROL is at 0.3-0.5mm, criticize the most handy trowel when scraping to smear from different directions, Heavy Weight is stacked to wall material surface 3-5 when becoming dry, being closed flat press polish with special receipts light trowel, be preferably operated from different directions during press polish, effect is better, press polish number of times is preferably equivalent at least 2-3 time, and being closed flat press polish has reflecting effect to surface。
Wherein, wall body carried out base treatment be described in step 1: wall body entirety has been scraped water-proof putty brushing basement membrane, protect wall body corner with U.S. stricture of vagina paper；If wall body base material is different, also should stick binder in junction or grid cloth processes；Be disposed and require that wall body temperature is less than 10% afterwards, pH value less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing；
In step 2, construction temperature is not less than 5 DEG C；The described operational approach by kieselguhr wall material and water mix homogeneously is as follows: first add the water of water consumption 80% in container, add described kieselguhr wall material to stand 3-5 minute, then stir 8-12 minute with motor stirrer, the water of residue 20% it is slowly added into during stirring, stand 3-6 minute, then stir 7-10 minute with motor stirrer；
Preferably, stand again 20-40 minute after kieselguhr wall material and water mix homogeneously；
In step 3, described first pass is criticized the wall material thickness scraped and is: 0.3-0.5mm, and the second time batch of wall material thickness scraped is: 0.3-0.5mm and surface smear become irregular concave and convex plane；The described operative body rustless steel receiving light trowel makes, and thickness is: 0.03mm, and the plane set deformation volume of operative body is: 0.01mm。
The method have the advantages that
After utilizing the kieselguhr wall material of the present invention and construction method thereof to construct on wall body, finished product effect is attractive in appearance, and texture, close to Milan architectural style, can build the effect of shadow of characteristic, meets people to the ornamental requirement of kieselguhr wall material。
Detailed description of the invention
The invention provides a kind of kieselguhr wall material with Milan shadow style and construction method thereof, for making the purpose of the present invention, technical scheme and effect clearly, clearly, the present invention is described in more detail below。Should be appreciated that specific embodiment described herein is only in order to explain the present invention, is not intended to limit the present invention。Unreceipted actual conditions person in embodiment, conventionally the condition of condition or manufacturer's suggestion carries out。Agents useful for same or the unreceipted production firm person of instrument, be and can pass through the commercially available conventional products bought and obtain。
Embodiment 1
There is the kieselguhr wall material component containing, for example lower weight portion of Milan shadow style:
200-700 order Primary Study of Choosing Diatomite 10 weight portion；700-1400 order conch meal 10 weight portion；80-1000 order natural marble dust 8 weight portion；600-1600 order golden red stone powder 5 weight portion；500-1200 order silica flour 15 weight portion；250-600 order peafowl stone powder 5 weight portion；300-900 order attapulgite powder 1 weight portion；Nano titanium oxide 1 weight portion；Methylcellulose 0.1 weight portion；Redispersible latex powder 1 weight portion。
Embodiment 2
There is the kieselguhr wall material component containing, for example lower weight portion of Milan shadow style:
200-700 order Primary Study of Choosing Diatomite 38 weight portion；700-1400 order conch meal 40 weight portion；80-1000 order natural marble dust 50 weight portion；600-1600 order golden red stone powder 35 weight portion；500-1200 order silica flour 65 weight portion；250-600 order peafowl stone powder 45 weight portion；300-900 order attapulgite powder 25 weight portion；Nano titanium oxide 8 weight portion；Methylcellulose 2 weight portion；Redispersible latex powder 25 weight portion。
Embodiment 3
There is the kieselguhr wall material component containing, for example lower weight portion of Milan shadow style:
200-700 order Primary Study of Choosing Diatomite 35 weight portion；700-1400 order conch meal 35 weight portion；80-1000 order natural marble dust 45 weight portion；600-1600 order golden red stone powder 30 weight portion；500-1200 order silica flour 59 weight portion；250-600 order peafowl stone powder 36 weight portion；300-900 order attapulgite powder 20 weight portion；Nano titanium oxide 6 weight portion；Methylcellulose 1.8 weight portion；Redispersible latex powder 22 weight portion。
Embodiment 4
On the basis of embodiment 1, add inorganic pigment: 1 weight portion。
Embodiment 5
On the basis of embodiment 2, add inorganic pigment: 15 weight portions。
Embodiment 6
On the basis of embodiment 3, add inorganic pigment: 12 weight portions。
Embodiment 7
There is the kieselguhr wall material component containing, for example lower weight portion of Milan shadow style:
300-600 order Primary Study of Choosing Diatomite 15 weight portion；800-1200 order conch meal 15 weight portion；120-800 order natural marble dust 12 weight portion；800-1500 order golden red stone powder 10 weight portion；600-1000 order silica flour 20 weight portion；325-500 order peafowl stone powder 10 weight portion；400-800 order attapulgite powder 6 weight portion；Nano titanium oxide 2 weight portion；Methylcellulose 0.4 weight portion；Redispersible latex powder 4 weight portion。
Embodiment 8
There is the kieselguhr wall material component containing, for example lower weight portion of Milan shadow style:
300-600 order Primary Study of Choosing Diatomite 30 weight portion；800-1200 order conch meal 30 weight portion；120-800 order natural marble dust 40 weight portion；800-1500 order golden red stone powder 25 weight portion；600-1000 order silica flour 50 weight portion；325-500 order peafowl stone powder 30 weight portion；400-800 order attapulgite powder 15 weight portion；Nano titanium oxide 5 weight portion；Methylcellulose 1.5 weight portion；Redispersible latex powder 18 weight portion。
Embodiment 9
There is the kieselguhr wall material component containing, for example lower weight portion of Milan shadow style:
300-600 order Primary Study of Choosing Diatomite 26 weight portion；800-1200 order conch meal 28 weight portion；120-800 order natural marble dust 35 weight portion；800-1500 order golden red stone powder 22 weight portion；600-1000 order silica flour 46 weight portion；325-500 order peafowl stone powder 25 weight portion；400-800 order attapulgite powder 13 weight portion；Nano titanium oxide 4 weight portion；Methylcellulose 1.2 weight portion；Redispersible latex powder 15 weight portion。
Embodiment 10
On the basis of embodiment 7, add inorganic pigment: 1 weight portion。
Embodiment 11
On the basis of embodiment 8, add inorganic pigment: 15 weight portions。
Embodiment 12
On the basis of embodiment 9, add inorganic pigment: 12 weight portions。
Embodiment 13
There is the kieselguhr wall material component containing, for example lower weight portion of Milan shadow style:
300-600 order Primary Study of Choosing Diatomite 23 weight portion；800-1200 order conch meal 26 weight portion；120-800 order natural marble dust 30 weight portion；800-1500 order golden red stone powder 18 weight portion；600-1000 order silica flour 38 weight portion；325-500 order peafowl stone powder 18 weight portion；400-800 order attapulgite powder 11 weight portion；Nano titanium oxide 3 weight portion；Methylcellulose 0.9 weight portion；Redispersible latex powder 10 weight portion。
Embodiment 14
On the basis of embodiment 13, add inorganic pigment: 8 weight portions。
The present invention utilizes natural inorganic mineral raw material meticulously to allocate a kind of novel environment friendly wall body ornament materials being prepared from。Through actual verification, the above-mentioned kieselguhr wall material with Milan shadow style provided by the invention making the wall body decorative pattern obtained, effect is attractive in appearance, meets people to the ornamental requirement of kieselguhr wall material。The effect that the kieselguhr wall material that embodiment 7 to 12 provides obtains wherein is used to be better than embodiment 1 to 6, the effect that the kieselguhr wall material that embodiment 13 to 14 provides obtains is better than EXAMPLE Example 7 to 12, simultaneously in above-described embodiment, with the addition of the kieselguhr wall material of inorganic pigment relative to the kieselguhr wall material being not added with inorganic pigment, the finished product effect smoothness more attractive in appearance obtained。
Embodiment 15
The construction method of a kind of above-mentioned kieselguhr wall material with Milan shadow style provided by the invention, specific as follows:
Step 1: wall body is carried out base treatment；
According to this area common practice, wall body is processed so that it is be suitable to the construction of follow-up kieselguhr wall material。Wanting to obtain the kieselguhr wall material decorative effect better with Milan shadow style, wall body entirety should scrape water-proof putty brushing basement membrane, protects wall body corner with U.S. stricture of vagina paper；If wall body base material is different, also should stick binder in junction or grid cloth processes；Be disposed and require that wall body temperature is less than 10% afterwards, pH value less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing；
Step 2: by ratio mix homogeneously according to weight ratio 1:0.45-0.65 of kieselguhr wall material and water；
In this step, construction temperature is not less than 5 DEG C；The described operational approach by kieselguhr wall material and water mix homogeneously is as follows: first add the water of water consumption 80% in container, add described kieselguhr wall material to stand 3-5 minute, then stir 8-12 minute with motor stirrer, the water of residue 20% it is slowly added into during stirring, stand 3-6 minute, then stir 7-10 minute with motor stirrer；20-40 minute better effects if is stood again after kieselguhr wall material and water mix homogeneously。
Step 3: batch scrape two times constructions, after wherein first pass is criticized and is scraped, THICKNESS CONTROL at 0.3-0.5mm, entirety metope non junction, after parching completely, smooth in wall material surface finish with the dry sand of 180-600 order, remove floating dust with hairbrush；Then criticize and scrape second time, THICKNESS CONTROL is at 0.3-0.5mm, criticize the most handy trowel when scraping to smear from different directions, Heavy Weight is stacked to wall material surface 3-5 when becoming dry, being closed flat press polish with special receipts light trowel, be preferably operated from different directions during press polish, effect is better, press polish number of times is no less than 2-3 time, and being closed flat press polish has reflecting effect to surface。
In order to obtain better finished product effect in this step, first pass is criticized the wall material thickness scraped and is: 0.3-0.5mm, and the second time batch of wall material thickness scraped is: 0.3-0.5mm and surface smear become irregular concave and convex plane；The described operative body rustless steel receiving light trowel makes, and thickness is: 0.03mm, and the plane set deformation volume of operative body is: 0.01mm。
In embodiment 1-15, one or more in inorganic pigment preferential oxidation iron oxide red, cobalt violet, cobalt green, bismuth Huang, zinc-iron Huang, titanium yellow, titanium chromium palm fibre。
Inventor is through concentrating on studies discovery, and in order to use the wall material of containing diatomite to present, effect is attractive in appearance, texture close to Milan architectural style, and first key point is the formula of kieselguhr wall material；Second key point is then construction method, every opportunity etc. all over construction during including kieselguhr wall material and the ratio of water, stirring means, two times constructions；3rd key point is to use what type of construction tool, and these factors all can have influence on the texture effect of the finished product after kieselguhr wall material construction。
Study through for many years, inventor have developed the kieselguhr wall material with Milan shadow style and the construction method thereof of the present invention, obtain the texture wall body decorative pattern close to Milan architectural style it is thus possible to make, meet people to the ornamental requirement of kieselguhr wall material。
To sum up, after utilizing the kieselguhr wall material of the present invention and construction method thereof to construct on wall body, finished product effect is attractive in appearance, and texture, close to Milan architectural style, can build the effect of shadow of characteristic, meets people to the ornamental requirement of kieselguhr wall material。And, kieselguhr wall material provided by the invention does not contain any harmful material, not only will not the harmful gas such as emitting formaldehyde, benzene, ammonia, but also there is absorption, the function of resolving harmful gas, and there is certain equilibrium temperature function, it is provided simultaneously with transport, simple feature of constructing。
The present invention improves kieselguhr utilization in ornament materials, brings selection more healthy, environmental protection for life at home。
The above is the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from principle of the present invention; can also making some improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention。
Claims (9)
1. a kieselguhr wall material with Milan shadow style, it is characterised in that containing, for example the component of lower weight portion:
200-700 order kieselguhr: 10-38 weight portion；
700-1400 order conch meal: 10-40 weight portion；
The natural marble dust of 80-1000 order: 8-50 weight portion；
600-1600 order golden red stone powder: 5-35 weight portion；
500-1200 order silica flour: 15-65 weight portion；
250-600 order peafowl stone powder: 5-45 weight portion；
300-900 order attapulgite powder: 1-25 weight portion；
Nano titanium oxide: 1-8 weight portion；
Methylcellulose: 0.1-2 weight portion；
Redispersible latex powder: 1-25 weight portion。
2. the kieselguhr wall material with Milan shadow style according to claim 1, it is characterised in that containing, for example the component of lower weight portion:
300-600 order kieselguhr: 15-30 weight portion；
800-1200 order conch meal: 15-30 weight portion；
The natural marble dust of 120-800 order: 12-40 weight portion；
800-1500 order golden red stone powder: 10-25 weight portion；
600-1000 order silica flour: 20-50 weight portion；
325-500 order peafowl stone powder: 10-30 weight portion；
400-800 order attapulgite powder: 6-15 weight portion；
Nano titanium oxide: 2-5 weight portion；
Methylcellulose: 0.4-1.5 weight portion；
Redispersible latex powder: 4-18 weight portion。
3. the kieselguhr wall material with Milan shadow style according to claim 1, it is characterised in that containing, for example the component of lower weight portion:
300-600 order kieselguhr: 23 weight portions；
800-1200 order conch meal: 26 weight portions；
The natural marble dust of 120-800 order: 30 weight portions；
800-1500 order golden red stone powder: 18 weight portions；
600-1000 order silica flour: 38 weight portions；
325-500 order peafowl stone powder: 18 weight portions；
400-800 order attapulgite powder: 11 weight portions；
Nano titanium oxide: 3 weight portions；
Methylcellulose: 0.9 weight portion；
Redispersible latex powder: 10 weight portions。
4. according to the described kieselguhr wall material with Milan shadow style arbitrary in claims 1 to 3, it is characterised in that possibly together with inorganic pigment 1-15 weight portion。
5. the construction method of arbitrary described kieselguhr wall material with Milan shadow style in Claims 1-4, it is characterised in that comprise the steps:
Step 1: wall body is carried out base treatment；
Step 2: by ratio mix homogeneously according to weight ratio 1:0.45-0.65 of kieselguhr wall material and water；
Step 3: batch scrape two times constructions, after wherein first pass is criticized and is scraped, THICKNESS CONTROL at 0.3-0.5mm, entirety metope non junction, after parching completely, smooth in wall material surface finish with the dry sand of 180-600 order, remove floating dust；Then criticizing and scrape second time, THICKNESS CONTROL, at 0.3-0.5mm, is smeared from different directions, treats that wall material surface 3-5 becomes dry, and being closed flat press polish from different directions has reflecting effect to surface。
6. the construction method of the kieselguhr wall material with Milan shadow style according to claim 5; it is characterized in that; in step 1, described wall body is carried out base treatment it be: wall body entirety has been scraped water-proof putty brushing basement membrane, has protected wall body corner with U.S. stricture of vagina paper；If wall body base material is different, also should stick binder in junction or grid cloth processes；Be disposed and require that wall body humidity is less than 10% afterwards, pH value less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing。
7. the construction method of the kieselguhr wall material with Milan shadow style according to claim 5, it is characterised in that in step 2, described construction temperature is not less than 5 DEG C；The described operational approach by kieselguhr wall material and water mix homogeneously is as follows: the weight ratio of kieselguhr wall material and water is 1:0.55；In container, first add the water of water consumption 80%, add described kieselguhr wall material and stand 3-5 minute, then stir 8-12 minute with motor stirrer, be slowly added into the water of residue 20% during stirring, stand 3-6 minute, then stir 7-10 minute with motor stirrer；Stand again 20-40 minute after kieselguhr wall material and water mix homogeneously。
8. the construction method of the kieselguhr wall material with Milan shadow style according to claim 5, it is characterized in that, in step 3, described first pass criticizes the wall material thickness scraped: 0.3-0.5mm, and the second time batch of wall material thickness scraped is: 0.3-0.5mm and surface smear become irregular concave and convex plane。
9. the construction method of the kieselguhr wall material with Milan shadow style according to claim 5, it is characterized in that, in step 3, the described operative body rustless steel receiving light trowel makes, thickness is: 0.03mm, and the plane set deformation volume of operative body is: 0.01mm。