CN104100064B - Illusion-colour metal face overlay stone - Google Patents
Illusion-colour metal face overlay stone Download PDFInfo
- Publication number
- CN104100064B CN104100064B CN201410328496.5A CN201410328496A CN104100064B CN 104100064 B CN104100064 B CN 104100064B CN 201410328496 A CN201410328496 A CN 201410328496A CN 104100064 B CN104100064 B CN 104100064B
- Authority
- CN
- China
- Prior art keywords
- illusion
- colour
- disponer
- metallic paint
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
nullThe invention discloses a kind of illusion-colour metal face overlay stone，Including base material，The elastic coating being coated on base material，The roller coat coloured middle level on elastic coating，Illusion-colour metallic paint is sprayed on coloured middle level the effect layer formed，And the protective layer being coated on effect layer，Described protective layer is nano-fluorine carbon paint，Described illusion-colour metallic paint is by slurry、Mass fraction is 10% ~ 15% illusion-colour metal powder and 45% ~ 59% fluorine carbon-nano resin composition，Wherein slurry is the dimethylbenzene of 20% ~ 28% by mass fraction，The acetate butyl of 8% ~ 15%，8% concentration is the CAB of 20%，The Levaslip 432 of 0.7%，The Disponer 904s of 0.4% ~ 1%，The Disponer 912 of 0.6% ~ 0.8%，The Defom 6500 of 0.6% ~ 1%，The 201p composition of 2%，The present invention has transport、Easy construction，Style is stable，Feel is smooth、Moist feature.
Description
Technical field
The present invention relates to a kind of artificial stone field, more specifically, it relates to a kind of illusion-colour metal face overlay stone.
Background technology
At present, building wall is carrying out metal finishing when, or uses metal material to be affixed directly to building wall
Surface, face, or use metallic paint to be sprayed on composite sheet material, then composite sheet material is covered in the surface of building.
Use metal when decorating, owing to metal is heavier so that transport and construct and be extremely difficult to, relatively costly, and
And metal material easily corrodes；When using metallic paint to be sprayed on composite sheet material, such facing stone style is unstable, feel
Difference, and owing to coating is exposed in external environment condition, through wet by the rain and burnt by the sun, easily cause coating to fade, color duration mistake
Short.
Summary of the invention
The deficiency existed for prior art, it is an object of the invention to provide illusion-colour metal face overlay stone, this metal face overlay
It is light that stone has material, and transport, easy construction, style is stable, the feature that feel is smooth, moist.
For achieving the above object, the technical scheme is that a kind of illusion-colour metal face overlay stone, including base material,
The elastic coating being coated on base material, the roller coat coloured middle level on elastic coating, illusion-colour metallic paint is sprayed on coloured in
The effect layer formed on layer, and the protective layer being coated on effect layer, described protective layer is nano-fluorine carbon paint, described illusion-colour gold
Belonging to coating to be made up of slurry, illusion-colour metal powder and fluorine carbon-nano resin, the mass fraction of illusion-colour metal powder is 10% ~ 15%, fluorine
The mass fraction of carbon nano-resin is 45% ~ 59%.
Slurry is the dimethylbenzene of 20% ~ 28% by metal quality mark, the acetate butyl of 8% ~ 15%, and 8% concentration is 20%
CAB, the Levaslip 432 of 0.7%, the Disponer 904s of 0.4% ~ 1%, the Disponer 912 of 0.6% ~ 0.8%, 0.6%
The Defom 6500 of ~ 1%, the 201p composition of 2%.
The present invention is further arranged to: described illusion-colour metallic paint is by slurry, the illusion-colour metal powder of 10% and 46%
Fluorine carbon-nano resin forms；Slurry includes the dimethylbenzene that mass fraction is 21%, the acetate butyl of 10%, and 8% concentration is 20%
CAB, the Levaslip 432 of 0.7%, the Disponer 904s of 0.7%, the Disponer 912 of 0.7%, the Defom of 0.9%
6500, the 201p composition of 2%.
By using technique scheme, inorganic mineral gel, kaolin, rutile titanium white powder are imitative metal inorganic master
Body, made metal face overlay stone effect is true to nature, organosilicon-modified acrylic elastic emulsion be main filmogen, add
It is fine and smooth, smooth that the effect layer that the illusion-colour metallic paint that other auxiliary agents are made is formed has feel, the feature that hot strength is big, and
The same base material of this effect layer, elastic coating, coloured middle level and protective layer are the same, are all made up of the organic and inorganic material of lightweight, phase
Having the feature of light weight than metal material, thus easily transport, construct, on effect layer, coating one layer is made up of nano-fluorine carbon paint
Protective layer, can be effectively protected effect layer not by external interference so that its color is sufficiently stable.
Preparation method, preparation as described in one of claim 1 or 2 illusion-colour metal face overlay stone, it is characterized in that: include with
Lower step:
(1) base material with polyester fiber as main material is carried out smooth, dry process, use high-quality cracking resistance seal coat
The most uniformly brushing is in the one side of base material, and standing and drying；
(2) after high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, this elasticity
Coating is made with polymeric acrylic acid elastic emulsion for film forming matter；
(3) after described in (2), elastic coating is completely dried, on its surface, the most uniformly roller coat coloured silk joins priming paint, is formed
Look middle level；
(4) after middle level coloured described in (3) is completely dried, in its surface continuous uniform spraying illusion-colour metallic paint, shape
Become effect layer；
(5) after effect layer is completely dried described in (4), at its surface spraying nano-fluorine carbon paint, protective layer is formed.
By using technique scheme, polyester fiber can be strengthened as base material the hot strength of metal face overlay stone,
Coat high-quality cracking resistance seal coat in base material one side and play water-fast, the effect of acid and alkali-resistance, mildew resistant moistureproof；Elastic with polymeric acrylic acid
Emulsion is that the elastic coating that film forming matter is made can play enhancing feel, metal face overlay stone generation is answered by compensation temperature change
The effect of power；On elastic coating, roller coat is just joined priming paint and can be strengthened the color effect of metal face overlay stone；At illusion-colour metallic paint
The effect layer surface spraying nano-fluorine carbon paint formed, as protective layer, can be effectively protected effect layer not by external interference, make
Obtain its color sufficiently stable.
The utility model is further arranged to: described illusion-colour metallic paint sprays and complete at surface, coloured middle level first pass
After white drying, spraying second time again.
The present invention is further arranged to: the consumption of described high-quality cracking resistance seal coat is 0.1～0.15kg/m2；Described bullet
The thickness of property coating is 1.2mm；The thickness in described coloured middle level is 0.15mm；The thickness of described effect layer is 0.2mm
By using technique scheme, the spraying illusion-colour metallic paint of twice can ensure that effect layer feel is fine and smooth, outward
See true to nature, produced illusion-colour metal face overlay stone not only effect be set by above-mentioned thickness true to nature, and thickness is the thinnest,
While protected effect layer, the most not the representing of impact effect layer outward appearance.
The preparation method of illusion-colour metallic paint comprises the following steps: be sequentially added into dimethylbenzene, acetate butyl, 20% concentration
CAB disperses in dispersion tank, and jitter time is 5-10min, until fully transparent without graininess；Add Levaslip again
432, Disponer 904s, Disponer 912, Defom 6500,201p prepare to carrying out high speed dispersion in dispersion tank
Slurry；Being slowly added in slurry by illusion-colour metal powder, its medium speed is not above 900r/min, and jitter time is 10-
15min；After all raw materials are completely dispersed, add fluorine carbon-nano resin agitating uniform, obtain illusion-colour metallic paint.
By using technique scheme, it is sequentially added into dimethylbenzene, acetate butyl, the CAB of 20% concentration enter in dispersion tank
Row dispersion, jitter time is 5-10min, until fully transparent without graininess；Add Levaslip 432, Disponer again
904s, Disponer 912, Defom 6500,201p prepare slurry to carrying out high speed dispersion in dispersion tank；By illusion-colour metal
Powder is slowly added in slurry, and its medium speed is not above 900r/min, and jitter time is 10-15min；When all raw materials are complete
Add fluorine carbon-nano resin agitating after scattering uniform, obtain illusion-colour metallic paint；Wherein the CAB of 20% concentration is first pre-dissolved, illusion-colour
Metal powder is the most brewed, and with assorted high-grade illusion-colour metal powder modulation, without mill base, finished product has the illusion-colour of more than 3 kinds substantially
Metal powder, constructs on the synthesis polyester fiber of my door through high-temperature baking, then protects with fluorine carbon-nano finish, institute's lacquering
Film has impayable guarantor's chromatic effect, and other auxiliary agents so that the illusion-colour metallic paint of formation is provided that pole after shaping
High intensity and toughness, the ability of the strongest imitative metal, and also light weight, intensity are high；After obtaining the illusion-colour metallic paint of mobility,
By spray gun special, illusion-colour metallic paint is sprayed on surface, coloured middle level.
The present invention is further arranged to: in the preparation process of illusion-colour metallic paint, and temperature is 25 DEG C, and relative humidity is
40%-60%。
The present invention is further arranged to: by adding thickener, the viscosity of described illusion-colour metallic paint can be controlled in 100-
120KU。
By using technique scheme, by temperature control bit 25 DEG C, relative humidity in the preparation of illusion-colour metallic paint
For 40%-60%, its viscosity of illusion-colour metallic paint so produced is 90KU, meets the demand in major part market on the market and expires
The demand of foot particular client；In the step of illusion-colour metallic paint finished product, temperature is 25 DEG C, and relative humidity is 40%-60%, mixing
Time is within 1-5h, thus the illusion-colour metallic paint viscosity produced is 4000-9000mpa.s, is also modal on market
Use viscosity scope.
Detailed description of the invention
For the ease of the understanding of those skilled in the art, below in conjunction with specific embodiment, the present invention is made the most in detail
Describe.
A kind of illusion-colour metal face overlay stone, including base material, the elastic coating being coated on base material, roller coat is on elastic coating
Coloured middle level, is sprayed on coloured middle level the effect layer formed, and the protection being coated on effect layer by illusion-colour metallic paint
Layer, described protective layer is nano-fluorine carbon paint, and described illusion-colour metallic paint is by slurry, illusion-colour metal powder and fluorine carbon-nano resin structure
Becoming, the mass fraction of illusion-colour metal powder is 10% ~ 15%, and the mass fraction of fluorine carbon-nano resin is 45% ~ 59%.
Slurry is the dimethylbenzene of 20% ~ 28% by metal quality mark, the acetate butyl of 8% ~ 15%, and 8% concentration is 20%
CAB, the Levaslip 432 of 0.7%, the Disponer 904s of 0.4% ~ 1%, the Disponer 912 of 0.6% ~ 0.8%, 0.6%
The Defom 6500 of ~ 1%, the 201p of 2%.
The detailed proportioning of the classes of agents, raw material and the consumption that are used:
1. illusion-colour metallic paint proportioning:
Dimethylbenzene 20% ~ 28%；
Acetate butyl 8% ~ 15%；
20%CAB 8%；
Levaslip 432 0.7%；
Disponer 912 0.6%~0.8%；
Defom 6500 0.6%~1% ；
201p 2%；
Disponer 904 0.4%~1%；
Illusion-colour metal powder 10% ~ 15%；
Fluorine carbon-nano resin 45% ~ 59%.
Nano-fluorine carbon paint proportioning:
Dimethylbenzene 35～40%
Butyl acetate 10～15%
Disponer 904s(Ricinate) 0.3～0.5%
Levaslip 432(silicone levelling agent) 0.3～0.5%
Defoamer 635 0.4～0.7%
The nano combined fluorocarbon resin of solvent-borne type 50～55%.
Embodiment 1: the preparation process of illusion-colour metallic paint:
The preparation process of illusion-colour metallic paint: be sequentially added into dimethylbenzene, acetate butyl, 20% concentration CAB in dispersion tank
Disperseing, jitter time is 5-10min, until fully transparent without graininess；Add Levaslip 432, Disponer again
904s, Disponer 912, Defom 6500,201p prepare slurry to carrying out high speed dispersion in dispersion tank；By illusion-colour metal
Powder is slowly added in the slurry prepared, and its medium speed is not above 900r/min, and jitter time is 10-15min；When all raw materials
Add fluorine carbon-nano resin agitating after being completely dispersed uniform, obtain illusion-colour metallic paint.
3. the preparation process of metal face overlay stone:
(1) base material with polyester fiber as main material is fully cleaned, smooth, be dried process, during cleaning use
The cleaning agent of PH=8, keeps environment temperature: T=5 DEG C, then use high-quality cracking resistance seal coat the most uniformly to brush at base material
Simultaneously, and standing and drying, the consumption of high-quality cracking resistance seal coat is 0.1kg/m2；
(2) after high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, this elasticity
Coating is made with polymeric acrylic acid elastic emulsion for film forming matter, and this elastic coating thickness is 1.2mm；
(3) after described in (2), elastic coating is completely dried, on its surface, the most uniformly roller coat coloured silk joins priming paint, is formed
Look middle level, the thickness in coloured middle level is 0.15mm；
(4) after middle level coloured described in (3) is completely dried, in its surface continuous uniform spraying illusion-colour metallic paint, spray
After being coated with first pass, standing and drying, then spraying second time, form effect layer, the thickness of this effect layer is 0.2mm；
(5) after described in (4), effect layer is completely dried, at its surface spraying nano-fluorine carbon paint, its proportioning is: 35%
Dimethylbenzene, the butyl acetate of 10%, the Disponer 904s(Ricinate of 0.3%), the Levaslip 432(silicone of 0.3%
Levelling agent), the defoamer 635 of 0.4%, and the nano combined fluorocarbon resin of solvent-borne type of 54%, form protective layer, this protective layer
Thickness is 0.1mm.
Here, metal face overlay made of stones standby during, the high-quality cracking resistance seal coat that step (1) is used uses autonomous raw
The seal coat produced, has acid and alkali-resistance, water-fast, moisture resistance feature.
Embodiment 1.
The proportioning of illusion-colour metallic paint:
Dimethylbenzene 21%；
Acetate butyl 10%；
20%CAB 8%；
Levaslip 432 0.7% ；
Disponer 904 0.7%；
Disponer 912 0.7%；
Defom 6500 0.9% ；
201p 2%；
Illusion-colour metal powder 10%；
Fluorine carbon-nano resin 46%.
Operating process and condition:
1. it is sequentially added into dimethylbenzene, acetate butyl, the CAB dispersion 5-10min of 20%, to the most fully transparent without graininess, then adds
Add 4.5.6.7.8 high speed dispersion；
Add Levaslip 432, Disponer 904s, Disponer 912, Defom 6500,201p the most again
In dispersion tank, carry out high speed dispersion prepare slurry；Being slowly added in the slurry prepared by illusion-colour metal powder, its medium speed can not
Higher than 900r/min, jitter time is 10-15min；
3. being slowly added to by prefabricated metal paste, rotating speed, not above 900r/min, disperses 10-15 minute.
The preparation process of metal face overlay stone and condition in embodiment 2:
(1) base material with polyester fiber as main material is fully cleaned, smooth, be dried process, during cleaning use
The cleaning agent of PH=8, keeps environment temperature: T=5 DEG C, then use high-quality cracking resistance seal coat the most uniformly to brush at base material
Simultaneously, and standing and drying, the consumption of high-quality cracking resistance seal coat is 0.1kg/m2；
(2) after high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, this elasticity
Coating is made with polymeric acrylic acid elastic emulsion for film forming matter, and this elastic coating thickness is 1.2mm；
(3) after described in (2), elastic coating is completely dried, on its surface, the most uniformly roller coat coloured silk joins priming paint, is formed
Look middle level, the thickness in coloured middle level is 0.15mm；
(4) after middle level coloured described in (3) is completely dried, in its surface continuous uniform spraying illusion-colour metallic paint, spray
After being coated with first pass, standing and drying, then spraying second time, form effect layer, the thickness of this effect layer is 0.2mm；
(5) after described in (4), effect layer is completely dried, at its surface spraying nano-fluorine carbon paint, its proportioning is: 35%
Dimethylbenzene, the butyl acetate of 10%, the Disponer 904s(Ricinate of 0.3%), the Levaslip 432(silicone of 0.3%
Levelling agent), the defoamer 635 of 0.4%, and the nano combined fluorocarbon resin of solvent-borne type of 54%, form protective layer, this protective layer
Thickness is 0.1mm.
Embodiment 2.
The proportioning of illusion-colour metallic paint
Dimethylbenzene 23%；
Acetate butyl 8%；
20%CAB 8%；
Levaslip 432 0.7% ；
Disponer 904 0.5 %；
Disponer 912 0.8%；
Defom 6500 1% ；
201p 2%；
Illusion-colour metal powder 11%；
Fluorine carbon-nano resin 45%.
Operating process and condition:
1. it is sequentially added into dimethylbenzene, acetate butyl, the CAB dispersion 5-10min of 20%, to the most fully transparent without graininess, then adds
Add 4.5.6.7.8 high speed dispersion；
Add Levaslip 432, Disponer 904s, Disponer 912, Defom 6500,201p the most again
In dispersion tank, carry out high speed dispersion prepare slurry；Being slowly added in the slurry prepared by illusion-colour metal powder, its medium speed can not
Higher than 900r/min, jitter time is 10-15min；
3. being slowly added to by prefabricated metal paste, rotating speed, not above 900r/min, disperses 10-15 minute.
The preparation process of metal face overlay stone and condition in embodiment 2:
(1) base material with polyester fiber as main material is fully cleaned, smooth, be dried process, during cleaning use
The cleaning agent of PH=8, keeps environment temperature: T=5 DEG C, then use high-quality cracking resistance seal coat the most uniformly to brush at base material
Simultaneously, and standing and drying, the consumption of high-quality cracking resistance seal coat is 0.1kg/m2；
(2) after high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, this elasticity
Coating is made with polymeric acrylic acid elastic emulsion for film forming matter, and this elastic coating thickness is 1.2mm；
(3) after described in (2), elastic coating is completely dried, on its surface, the most uniformly roller coat coloured silk joins priming paint, is formed
Look middle level, the thickness in coloured middle level is 0.15mm；
(4) after middle level coloured described in (3) is completely dried, in its surface continuous uniform spraying illusion-colour metallic paint, spray
After being coated with first pass, standing and drying, then spraying second time, form effect layer, the thickness of this effect layer is 0.2mm；
(5) after described in (4), effect layer is completely dried, at its surface spraying nano-fluorine carbon paint, its proportioning is: 35%
Dimethylbenzene, the butyl acetate of 10%, the Disponer 904s(Ricinate of 0.3%), the Levaslip 432(silicone of 0.3%
Levelling agent), the defoamer 635 of 0.4%, and the nano combined fluorocarbon resin of solvent-borne type of 54%, form protective layer, this protective layer
Thickness is 0.1mm.
Embodiment 3.
The proportioning of illusion-colour metallic paint:
Dimethylbenzene 21%；
Acetate butyl 9%；
20%CAB 8%；
Levaslip 432 0.7% ；
Disponer 904 0.5 %；
Disponer 912 0.8%；
Defom 6500 1%
201p 2%；
Illusion-colour metal powder 10%；
Fluorine carbon-nano resin 47%.
Operating process and condition:
1. it is sequentially added into dimethylbenzene, acetate butyl, the CAB dispersion 5-10min of 20%, to the most fully transparent without graininess, then adds
Add 4.5.6.7.8 high speed dispersion；
Add Levaslip 432, Disponer 904s, Disponer 912, Defom 6500,201p the most again
In dispersion tank, carry out high speed dispersion prepare slurry；Being slowly added in the slurry prepared by illusion-colour metal powder, its medium speed can not
Higher than 900r/min, jitter time is 10-15min；
3. being slowly added to by prefabricated metal paste, rotating speed, not above 900r/min, disperses 10-15 minute.
The preparation process of the metal face overlay stone in embodiment 3 and condition:
(1) base material with polyester fiber as main material is fully cleaned, smooth, be dried process, during cleaning use
The cleaning agent of PH=8, keeps environment temperature: T=5 DEG C, then use high-quality cracking resistance seal coat the most uniformly to brush at base material
Simultaneously, and standing and drying, the consumption of high-quality cracking resistance seal coat is 0.1kg/m2；
(2) after high-quality cracking resistance seal coat described in (1) is completely dried, in its surface roller coating elastic coating, this elasticity
Coating is made with polymeric acrylic acid elastic emulsion for film forming matter, and this elastic coating thickness is 1.2mm；
(3) after described in (2), elastic coating is completely dried, on its surface, the most uniformly roller coat coloured silk joins priming paint, is formed
Look middle level, the thickness in coloured middle level is 0.15mm；
(4) after middle level coloured described in (3) is completely dried, in its surface continuous uniform spraying illusion-colour metallic paint, spray
After being coated with first pass, standing and drying, then spraying second time, form effect layer, the thickness of this effect layer is 0.2mm；
(5) after described in (4), effect layer is completely dried, at its surface spraying nano-fluorine carbon paint, its proportioning is: 35%
Dimethylbenzene, the butyl acetate of 10%, the Disponer 904s(Ricinate of 0.3%), the Levaslip 432(silicone of 0.3%
Levelling agent), the defoamer 635 of 0.4%, and the nano combined fluorocarbon resin of solvent-borne type of 54%, form protective layer, this protective layer
Thickness is 0.1mm.
The above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned enforcement
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that, for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications are also
Should be regarded as protection scope of the present invention.
Claims (7)
1. an illusion-colour metal face overlay stone, including base material, the elastic coating being coated on base material, roller coat having on elastic coating
Look middle level, is sprayed on coloured middle level the effect layer formed, and the protective layer being coated on effect layer by illusion-colour metallic paint,
It is characterized in that: described protective layer is nano-fluorine carbon paint, described illusion-colour metallic paint is by slurry, illusion-colour metal powder and fluorine carbon-nano
Resin is constituted；The mass fraction of illusion-colour metal powder is 10% ~ 15%, and the mass fraction of fluorine carbon-nano resin is 45% ~ 59%；
Described slurry is the dimethylbenzene of 20% ~ 28% by metal quality mark, the acetate butyl of 8% ~ 15%, and 8% concentration is 20%
CAB, the Levaslip 432 of 0.7%, the Disponer 904s of 0.4% ~ 1%, the Disponer 912 of 0.6% ~ 0.8%, 0.6%
The Defom 6500 of ~ 1%, the 201p composition of 2%；
The preparation method of illusion-colour metal face overlay stone comprises the following steps:
(1) base material with polyester fiber as main material is carried out smooth, dry process, use high-quality cracking resistance seal coat comprehensive
Uniformly brushing is in the one side of base material, and standing and drying；
(2) after high-quality cracking resistance seal coat described in (1) is completely dried, at its surface roller coating elastic coating, this elastic coating
Make with polymeric acrylic acid elastic emulsion for film forming matter；
(3) after described in (2), elastic coating is completely dried, on its surface, together uniformly roller coat coloured silk joins priming paint, formed coloured in
Layer；
(4) after middle level coloured described in (3) is completely dried, at its surface continuous uniform spraying illusion-colour metallic paint, effect is formed
Really layer；
(5) after effect layer is completely dried described in (4), at its surface spraying nano-fluorine carbon paint, protective layer is formed.
Illusion-colour metal face overlay stone the most according to claim 1, is characterized in that: described illusion-colour metallic paint by slurry, 10%
Illusion-colour metal powder and 46% fluorine carbon-nano resin composition；Slurry includes the dimethylbenzene that mass fraction is 21%, the acetic acid of 10%
Fourth fat, 8% concentration is the CAB of 20%, the Levaslip 432 of 0.7%, the Disponer 904s of 0.7%, 0.7%
The 201p composition of Disponer 912, the Defom 6500 of 0.9%, 2%.
Illusion-colour metal face overlay stone the most according to claim 1, is characterized in that: described illusion-colour metallic paint is at coloured middle level table
After face first pass sprays and is completely dried, spraying second time again.
Illusion-colour metal face overlay stone the most according to claim 1, is characterized in that: the consumption of described high-quality cracking resistance seal coat is
0.1～0.15kg/m2；The thickness of described elastic coating is 1.2mm；The thickness in described coloured middle level is 0.15mm；Described effect
The thickness of layer is 0.2mm.
Illusion-colour metal face overlay stone the most according to claim 1, is characterized in that: described illusion-colour metallic paint includes following step
Rapid:
Prepared by slurry: be sequentially added into dimethylbenzene, acetate butyl, the CAB of 20% concentration disperse in dispersion tank, jitter time
For 5-10min, until fully transparent without graininess；Add Levaslip 432, Disponer 904s, Disponer again
912, Defom 6500,201p prepare slurry to carrying out high speed dispersion in dispersion tank；Illusion-colour metal powder is slowly added into slurry
In material, its medium speed is not above 900r/min, and jitter time is 10-15min；Fluorine is added after all raw materials are completely dispersed
Carbon nano-resin stirs, and obtains illusion-colour metallic paint.
Illusion-colour metal face overlay stone the most according to claim 5, it is characterised in that in the preparation process of illusion-colour metallic paint
In, temperature is 25 DEG C, and relative humidity is 40%-60%.
Illusion-colour metal face overlay stone the most according to claim 6, it is characterised in that by adding thickener, described illusion-colour gold
The viscosity belonging to coating can be controlled in 100-120KU.