CN105753376A - Imitation leather diatomite wall material and construction method thereof - Google Patents
Imitation leather diatomite wall material and construction method thereof Download PDFInfo
- Publication number
- CN105753376A CN105753376A CN201610146108.0A CN201610146108A CN105753376A CN 105753376 A CN105753376 A CN 105753376A CN 201610146108 A CN201610146108 A CN 201610146108A CN 105753376 A CN105753376 A CN 105753376A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- mesh
- wall material
- powder
- kieselguhr
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an imitation leather diatomite wall material and a construction method thereof.The diatomite wall material comprises the following components according to parts by weight: 10-50 parts of 300- to 800-mesh featured diatomite, 5-30 parts of 400- to 900-mesh malachite powder, 10-60 parts of 400- to 1200-mesh attapulgite, 10-50 parts of 300- to 800-mesh spinel powder, 10-40 parts of 300- to 1200-mesh quartz powder, 10-50 parts of 300- to 800-mesh dolomite powder, 5-28 parts of 300- to 800-mesh celestite powder, 5-35 parts of 400- to 1200-mesh light alumina powder, 2-15 parts of nano titanium dioxide, 0.2-2 parts of methylcellulose, and 5-35 parts of redispersible emulsion powder.The imitation leather diatomite wall material and the construction method thereof provided herein have the advantage that the finished product has fine and smooth handle after construction on a wall.
Description
Technical field
The present invention relates to building material field, particularly relate to kieselguhr wall material and the construction party thereof of leather texture imitation
Method.
Background technology
Kieselguhr is a kind of biogenic silicastone, and it is mainly by the remains institute group of diatom in ancient times
Become, there is the characteristics such as exquisiteness, loose, light weight, porous, water absorption and permeability are strong.Along with people
Requirement to the living environment feature of environmental protection is more and more higher, and kieselguhr is increasingly becoming a kind of very popular new
Type interior decoration ornament materials, with the addition of diatomaceous wall material and has and regulate the room temperature, eliminate abnormal flavour, suction
The advantages such as receipts and decomposing harmful substances.At present, although utilizing the kieselguhr wall material can be on wall body surface
Produce certain texture, ornamental to increase it, but the most still have the space of improvement.
The texture of dermatoglyph concave-convex surface, soft texture is the symbol of a kind of fashion and trend, its
Naturally color and luster and fine and smooth sense of touch have the strongest dicoration, apply in house wall material is fitted up permissible
Coordinate with leather furniture collocation, build the overall household atmosphere of harmony, it is achieved warm, comfortable,
Soft sensation.If but using corium material, the most not environmentally practicality but also cost dearly in wall material.
If it is possible to provide a kind of to take into account environmental protection and attractive in appearance, the fine and smooth smooth leather texture imitation silicon of sense of touch
Diatomaceous earth wall material, the most necessarily can meet people to a certain extent and want kieselguhr wall material is ornamental
Ask.
Summary of the invention
It is attractive in appearance that the technical problem to be solved in the present invention is to provide a kind of finished product effect, and sense of touch is fine and smooth smooth
The kieselguhr wall material of the leather texture imitation of special-effect and construction method thereof.
For solving above-mentioned technical problem, the present invention provides technical scheme as follows:
A kind of kieselguhr wall material of leather texture imitation, containing the component of following weight portion:
300-800 mesh kieselguhr: 10-50 weight portion；
400-900 mesh peafowl stone powder: 5-30 weight portion；
400-1200 mesh attapulgite: 10-60 weight portion；
300-800 mesh spinel powder: 10-50 weight portion；
300-1200 mesh silica flour: 10-40 weight portion；
300-800 whitish eye marble dust: 10-50 weight portion；
300-800 mesh celestite powder: 5-28 weight portion；
400-1200 mesh light aluminum oxide powder: 5-35 weight portion；
Nano titanium oxide: 2-15 weight portion；
Methylcellulose: 0.2-2 weight portion；
Redispersable latex powder: 5-35 weight portion.
Further, the kieselguhr wall material of described leather texture imitation is possibly together with the component of following weight portion:
Inorganic pigment: 1-15 weight portion；
Preferably, the kieselguhr wall material of described leather texture imitation, each constituent content is as follows:
400-600 mesh Primary Study of Choosing Diatomite: 18-30 weight portion；
600-800 mesh peafowl stone powder: 10-26 weight portion；
500-1000 mesh attapulgite: 20-40 weight portion；
400-600 mesh spinel powder: 15-30 weight portion；
600-1000 mesh silica flour: 15-35 weight portion；
400-600 whitish eye marble dust: 18-30 weight portion；
400-600 mesh celestite powder: 10-18 weight portion；
600-1000 mesh light aluminum oxide powder: 10-28 weight portion；
Nano titanium oxide: 5-10 weight portion；
Methylcellulose: 0.5-1.5 weight portion；
Redispersable latex powder: 10-25 weight portion.
Further, the kieselguhr wall material of described leather texture imitation is possibly together with the component of following weight portion:
Inorganic pigment: 1-15 weight portion；
It is highly preferred that the kieselguhr wall material of described leather texture imitation, each constituent content is as follows:
450-550 mesh Primary Study of Choosing Diatomite: 25 weight portions；
650-750 mesh peafowl stone powder: 18 weight portions；
600-800 mesh attapulgite: 30 weight portions；
450-550 mesh spinel powder: 20 weight portions；
700-900 mesh silica flour: 25 weight portions；
450-550 whitish eye marble dust: 25 weight portions；
450-550 mesh celestite powder: 14 weight portions；
700-900 mesh light aluminum oxide powder: 20 weight portions；
Nano titanium oxide: 7 weight portions；
Methylcellulose: 1 weight portion；
Redispersable latex powder: 18 weight portions.
Further, the kieselguhr wall material of described leather texture imitation is possibly together with the component of following weight portion:
Inorganic pigment: 8 weight portions；
The preparation method of the kieselguhr wall material of above-mentioned leather texture imitation is: by mentioned component according to corresponding weight
Number mixes, and stirs.
A kind of construction method of the kieselguhr wall material of above-mentioned leather texture imitation, including:
Step 1: wall body is carried out base treatment；
Step 2: by kieselguhr wall material and water according to the ratio mix homogeneously of weight ratio 1:0.4-0.6；
Step 3: batch scrape three times constructions, wherein, first pass is criticized after scraping, THICKNESS CONTROL at 0.5-0.8mm,
Texture size requirements is uniform；Criticizing when wall material to 5-6 becomes dry and scrape second time, noting when batch scraping can not be
The decorative pattern that bottom pulls out is floating, carry out filling up according to the thickness of plucking decorative pattern and batch scrape, at the bottom of preventing
The decorative pattern that pulls out of layer is floating, batch scrapes smooth, maneuver weight such as；Then treat that second time batch is scraped rear wall
When material 3-6 becomes dry, adding wall material with trowel again and pull on one time, thickness is preferably controlled in about 0.2mm,
It is closed flat press polish with receiving light trowel, receives light number of times at least 2 times；After wall material parches, surface self is received
The irregular splitting that contracting is formed carries out filling up criticizing to be scraped, it should be noted that gently scrapes and gently fills out, overall uniform, crackle
Filling full, the most handy plastic scrapers carries out criticizing to be scraped, and its material is soft and contact surface is little, it is not easy to destroy
Crackle, prevents wall material undue force from coming off；Finally with towel cleaning surface defective material, stamp a wood cured
Oil.
Wherein, wall body carried out base treatment be described in step 1: wall body entirety has been scraped waterproof
Putty brushing basement membrane, protect wall body corner with U.S. stricture of vagina paper；If wall body base material is different, also
Binder should be sticked in junction or grid cloth processes；It is disposed and requires that wall body temperature is less than afterwards
10%, pH value be less than 10, wall body overall leveling, closely knit, clean without floating dust, without ftracture hollowing；
In step 2, construction temperature is not less than 5 DEG C；Described by kieselguhr wall material and water mix homogeneously
Operational approach as follows: in container, first add the water of water consumption 80%, add described kieselguhr
Wall material stands 3-5 minute, then stirs 8-12 minute with motor stirrer, is slowly added into surplus during stirring
Yu 20% water, stand 3-6 minute, then with motor stirrer stir 7-10 minute；
Preferably, after kieselguhr wall material and water mix homogeneously, 20-40 minute is stood again；
In step 3, the wall material thickness that described second time batch is scraped is: 1-1.5mm, scrapes for the 3rd time batch
Wall material thickness be: 0.5-1.0mm and surface smear become irregular concave and convex plane；Described receipts light
The operative body of trowel rustless steel makes, and thickness is: 0.03mm, and the plane of operative body is permanent
Deflection is: 0.01mm；Described irregular crackle is filled up that batch to scrape use instrument be plastics
Scraper plate.
The method have the advantages that
After utilizing the kieselguhr wall material of the present invention and construction method thereof to construct on wall body, finished product is imitated
The most attractive in appearance, sense of touch exquisiteness is smooth, meets people's requirement ornamental to kieselguhr wall material.
Detailed description of the invention
The invention provides kieselguhr wall material and the construction method thereof of a kind of leather texture imitation, for making the present invention's
Purpose, technical scheme and effect are clearer, clear and definite, and the present invention is described in more detail below.
Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not used to limit
The present invention.Unreceipted actual conditions person in embodiment, the condition advised according to normal condition or manufacturer
Carry out.Agents useful for same or instrument unreceipted production firm person, being can be by commercially available purchase acquisition
Conventional products.
Embodiment 1
The kieselguhr wall material of leather texture imitation contains the component of following weight portion:
300-800 mesh kieselguhr 10 weight portion；400-900 mesh peafowl stone powder 5 weight portion；400-1200
Mesh attapulgite 10 weight portion；300-800 mesh spinel powder 10 weight portion；300-1200 mesh quartz
Powder 10 weight portion；300-800 whitish eye marble dust 10 weight portion；300-800 mesh celestite powder 5 weight
Part；400-1200 mesh light aluminum oxide powder 5 weight portion；Nano titanium oxide 2 weight portion；Methyl is fine
Tie up plain 0.2 weight portion；Redispersable latex powder 5 weight portion.
Embodiment 2
The kieselguhr wall material of leather texture imitation contains the component of following weight portion:
300-800 mesh kieselguhr 50 weight portion；400-900 mesh peafowl stone powder 30 weight portion；400-1200
Mesh attapulgite 60 weight portion；300-800 mesh spinel powder 50 weight portion；300-1200 mesh quartz
Powder 40 weight portion；300-800 whitish eye marble dust 50 weight portion；300-800 mesh celestite powder 28 weight
Amount part；400-1200 mesh light aluminum oxide powder 35 weight portion；Nano titanium oxide 15 weight portion；First
Base cellulose 2 weight portion；Redispersable latex powder 35 weight portion.
Embodiment 3
The kieselguhr wall material of leather texture imitation contains the component of following weight portion:
300-800 mesh kieselguhr 38 weight portion；400-900 mesh peafowl stone powder 28 weight portion；400-1200
Mesh attapulgite 50 weight portion；300-800 mesh spinel powder 40 weight portion；300-1200 mesh quartz
Powder 38 weight portion；300-800 whitish eye marble dust 40 weight portion；300-800 mesh celestite powder 23 weight
Amount part；400-1200 mesh light aluminum oxide powder 32 weight portion；Nano titanium oxide 12 weight portion；First
Base cellulose 1.8 weight portion；Redispersable latex powder 30 weight portion.
Embodiment 4
On the basis of embodiment 1, interpolation inorganic pigment: 1 weight portion.
Embodiment 5
On the basis of embodiment 2, interpolation inorganic pigment: 15 weight portions.
Embodiment 6
On the basis of embodiment 3, interpolation inorganic pigment: 12 weight portions.
Embodiment 7
The kieselguhr wall material of leather texture imitation contains the component of following weight portion:
400-600 mesh Primary Study of Choosing Diatomite 18 weight portion；600-800 mesh peafowl stone powder 10 weight portion；
500-1000 mesh attapulgite 20 weight portion；400-600 mesh spinel powder 15 weight portion；600-1000
Mesh silica flour 15 weight portion；400-600 whitish eye marble dust 18 weight portion；400-600 mesh celestite powder
10 weight portions；600-1000 mesh light aluminum oxide powder 10 weight portion；Nano titanium oxide 5 weight portion；
Methylcellulose 0.5 weight portion；Redispersable latex powder 10 weight portion.
Embodiment 8
The kieselguhr wall material of leather texture imitation contains the component of following weight portion:
400-600 mesh Primary Study of Choosing Diatomite 30 weight portion；600-800 mesh peafowl stone powder 26 weight portion；
500-1000 mesh attapulgite 40 weight portion；400-600 mesh spinel powder 30 weight portion；600-1000
Mesh silica flour 35 weight portion；400-600 whitish eye marble dust 30 weight portion；400-600 mesh celestite powder
18 weight portions；600-1000 mesh light aluminum oxide powder 28 weight portion；Nano titanium oxide 10 weight
Part；Methylcellulose 1.5 weight portion；Redispersable latex powder 25 weight portion.
Embodiment 9
The kieselguhr wall material of leather texture imitation contains the component of following weight portion:
400-600 mesh Primary Study of Choosing Diatomite 20 weight portion；600-800 mesh peafowl stone powder 15 weight portion；
500-1000 mesh attapulgite 25 weight portion；400-600 mesh spinel powder 18 weight portion；600-1000
Mesh silica flour 20 weight portion；400-600 whitish eye marble dust 22 weight portion；400-600 mesh celestite powder
12 weight portions；600-1000 mesh light aluminum oxide powder 15 weight portion；Nano titanium oxide 6 weight portion；
Methylcellulose 0.8 weight portion；Redispersable latex powder 15 weight portion.
Embodiment 10
On the basis of embodiment 7, interpolation inorganic pigment: 1 weight portion.
Embodiment 11
On the basis of embodiment 8, interpolation inorganic pigment: 15 weight portions.
Embodiment 12
On the basis of embodiment 9, interpolation inorganic pigment: 12 weight portions.
Embodiment 13
The kieselguhr wall material of leather texture imitation contains the component of following weight portion:
500 mesh Primary Study of Choosing Diatomite 25 weight portions；700 mesh peafowl stone powder 18 weight portions；700 mesh are concavo-convex
Native 30 weight portions of rod；500 mesh spinel powder 20 weight portions；800 mesh silica flour 25 weight portions；500
Whitish eye marble dust 25 weight portion；500 mesh celestite powder 14 weight portions；800 mesh light aluminum oxide powder
20 weight portions；Nano titanium oxide 7 weight portion；Methylcellulose 1 weight portion；Redispersable latex
Powder 18 weight portion.
Embodiment 14
On the basis of embodiment 13, interpolation inorganic pigment: 8 weight portions.
The present invention is to utilize natural inorganic mineral raw material meticulously to allocate a kind of novel environment friendly being prepared from
Wall body ornament materials.Through actual verification, the kieselguhr wall material system of above-mentioned leather texture imitation provided by the present invention
Making the wall body decorative pattern obtained, effect is attractive in appearance, natural in color is smooth, meets people to kieselguhr
The ornamental requirement of wall material.The effect that the kieselguhr wall material wherein using embodiment 7 to 12 to provide obtains
Fruit is better than embodiment 1 to 6, and the effect that the kieselguhr wall material that embodiment 13 to 14 provides obtains is wanted
It is better than EXAMPLE Example 7 to 12, simultaneously in above-described embodiment, with the addition of the kieselguhr of inorganic pigment
Wall material is relative to being not added with the kieselguhr wall material of inorganic pigment, and the dermatoglyph texture effect obtained is more attractive in appearance
Smooth.
Embodiment 15
The construction method of the kieselguhr wall material of a kind of above-mentioned leather texture imitation that the present invention provides, specific as follows:
Step 1: wall body is carried out base treatment；
According to this area common practice, wall body is processed so that it is be suitable to follow-up kieselguhr wall material
Construct.Wanting to obtain the decorative effect of more preferable leather texture imitation, wall body should entirety have been scraped waterproof greasy
Son brushing basement membrane, protect wall body corner with U.S. stricture of vagina paper；If wall body base material is different, also should
When sticking binder or grid cloth process in junction；It is disposed and requires that wall body temperature is less than afterwards
10%, pH value be less than 10, wall body overall leveling, closely knit, clean without floating dust, without ftracture hollowing；
Step 2: by kieselguhr wall material and water according to the ratio mix homogeneously of weight ratio 1:0.4-0.6；
In this step, construction temperature is not less than 5 DEG C；Described by kieselguhr wall material and water mix homogeneously
Operational approach as follows: in container, first add the water of water consumption 80%, add described kieselguhr
Wall material stands 3-5 minute, then stirs 8-12 minute with motor stirrer, is slowly added into surplus during stirring
Yu 20% water, stand 3-6 minute, then with motor stirrer stir 7-10 minute；By kieselguhr wall
20-40 minute effect is stood again more preferable after material and water mix homogeneously.
Step 3: batch scrape three times constructions, wherein, first pass is criticized after scraping, THICKNESS CONTROL at 0.5-0.8mm,
Texture size requirements is uniform；Criticizing when wall material to 5-6 becomes dry and scrape second time, noting when batch scraping can not be
The decorative pattern that bottom pulls out is floating, carry out filling up according to the thickness of plucking decorative pattern and batch scrape, at the bottom of preventing
The decorative pattern that pulls out of layer is floating, batch scrapes smooth, maneuver weight such as；Then treat that second time batch is scraped rear wall
When material 3-6 becomes dry, adding wall material with trowel again and pull on one time, thickness is preferably controlled in about 0.2mm,
It is closed flat press polish with receiving light trowel, receives light number of times at least 2 times；After wall material parches, surface self is received
The irregular splitting that contracting is formed carries out filling up criticizing to be scraped, it should be noted that gently scrapes and gently fills out, overall uniform, crackle
Filling full, the most handy plastic scrapers carries out criticizing to be scraped, and its material is soft and contact surface is little, it is not easy to destroy
Crackle, prevents wall material undue force from coming off；Finally with towel cleaning surface defective material, stamp a wood cured
Oil.
In order to obtain the leather texture imitation decoration effect of more preferable finished product effect and natural in color smoothness in this step
Really, the second time batch of wall material thickness scraped is: 1-1.5mm, and the 3rd time batch of wall material thickness scraped is:
0.5-1.0mm and surface smear become irregular concave and convex plane；The described operative body receiving light trowel
Making of rustless steel, thickness is: 0.03mm, and the plane set deformation volume of operative body is: 0.01mm.
In embodiment 1-15, inorganic pigment preferential oxidation iron oxide red, cobalt violet, cobalt green, bismuth are yellow, zinc-iron
One or more in Huang, titanium yellow, titanium chromium palm fibre.
Inventor is through concentrating on studies discovery, beautiful in order to use the wall material of containing diatomite to present effect
Sight, the fine and smooth smooth dermatoglyph texture of sense of touch, first key point is the formula of kieselguhr wall material；Second
Individual key point is then construction method, including kieselguhr wall material and the ratio of water, stirring means, executes for two times
Every opportunity etc. all over construction in man-hour；3rd key point is to use what type of construction tool, these
Factor all can have influence on the texture effect of the finished product after kieselguhr wall material construction.
Studying through for many years, the invention talent, according to the texture feature of dermatoglyph, have developed the imitative of the present invention
The kieselguhr wall material of dermatoglyph and construction method thereof such that it is able to make and obtain the texture wall body close to dermatoglyph
Decorative pattern, meets people's requirement ornamental to kieselguhr wall material.
To sum up, after utilizing the kieselguhr wall material of the present invention and construction method thereof to construct on wall body,
Finished product effect is attractive in appearance, and sense of touch exquisiteness is smooth, meets people's requirement ornamental to kieselguhr wall material.
Further, the kieselguhr wall material that the present invention provides does not contains any harmful material, the most not
The harmful gass such as meeting emitting formaldehyde, benzene, ammonia, but also there is absorption, the merit of resolving harmful gas
Can, and there is certain equilibrium temperature function, it is provided simultaneously with transport, simple feature of constructing.
The present invention improves kieselguhr utilization in ornament materials, brings more strong for life at home
Health, the selection of environmental protection.
The above is the preferred embodiment of the present invention, it is noted that general for the art
For logical technical staff, on the premise of without departing from principle of the present invention, it is also possible to make some changing
Entering and retouch, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (9)
1. the kieselguhr wall material of a leather texture imitation, it is characterised in that containing the component of following weight portion:
300-800 mesh kieselguhr: 10-50 weight portion；
400-900 mesh peafowl stone powder: 5-30 weight portion；
400-1200 mesh attapulgite: 10-60 weight portion；
300-800 mesh spinel powder: 10-50 weight portion；
300-1200 mesh silica flour: 10-40 weight portion；
300-800 whitish eye marble dust: 10-50 weight portion；
300-800 mesh celestite powder: 5-28 weight portion；
400-1200 mesh light aluminum oxide powder: 5-35 weight portion；
Nano titanium oxide: 2-15 weight portion；
Methylcellulose: 0.2-2 weight portion；
Redispersable latex powder: 5-35 weight portion.
The kieselguhr wall material of leather texture imitation the most according to claim 1, it is characterised in that containing the component of following weight portion:
400-600 mesh kieselguhr: 18-30 weight portion；
600-800 mesh peafowl stone powder: 10-26 weight portion；
500-1000 mesh attapulgite: 20-40 weight portion；
400-600 mesh spinel powder: 15-30 weight portion；
600-1000 mesh silica flour: 15-35 weight portion；
400-600 whitish eye marble dust: 18-30 weight portion；
400-600 mesh celestite powder: 10-18 weight portion；
600-1000 mesh light aluminum oxide powder: 10-28 weight portion；
Nano titanium oxide: 5-10 weight portion；
Methylcellulose: 0.5-1.5 weight portion；
Redispersable latex powder: 10-25 weight portion.
The kieselguhr wall material of leather texture imitation the most according to claim 1, it is characterised in that containing the component of following weight portion:
400-600 mesh kieselguhr: 25 weight portions；
600-800 peafowl stone powder: 20 weight portions；
500-1000 mesh attapulgite: 30 weight portions；
400-600 mesh spinel powder: 20 weight portions；
600-1000 mesh silica flour: 25 weight portions；
400-600 whitish eye marble dust: 25 weight portions；
400-600 mesh celestite powder: 14 weight portions；
600-1000 mesh light aluminum oxide powder: 18 weight portions；
Nano titanium oxide: 8 weight portions；
Methylcellulose: 1 weight portion；
Redispersable latex powder: 18 weight portions.
4. according to the kieselguhr wall material of described leather texture imitation arbitrary in claims 1 to 3, it is characterised in that possibly together with inorganic pigment 1-15 weight portion.
5. the construction method of the kieselguhr wall material of arbitrary described leather texture imitation in Claims 1-4, it is characterised in that comprise the steps:
Step 1: wall body is carried out base treatment；
Step 2: by kieselguhr wall material and water according to the ratio mix homogeneously of weight ratio 1:0.4-0.6；
Step 3: criticizing and scrape three times constructions, after wherein first pass is criticized and scraped, THICKNESS CONTROL, at 0.5-0.8mm, carries out plucking with plucking cylinder, and the texture size requirements pulled up is uniform；Criticize when wall material to 5-6 becomes dry and scrape second time, criticize and notice that the decorative pattern that bottom can not be pulled out is floating when scraping, carry out filling up criticizing according to the thickness of plucking decorative pattern and scrape；Then, in time batch scraping rear wall material 3-6 for second time and become dry, add wall material with trowel again and pull on one time, be closed flat press polish with receiving light trowel；After wall material parches, the irregular splitting forming surface autogenous shrinkage is filled up to criticize and is scraped；Finally with towel cleaning surface defective material, stamp a wooden wax oil.
The construction method of the kieselguhr wall material of leather texture imitation the most according to claim 5, it is characterised in that in step 1, described carry out base treatment to wall body and is: wall body entirety has been scraped water-proof putty brushing basement membrane, has protected wall body corner with U.S. stricture of vagina paper；If wall body base material is different, also should stick binder in junction or grid cloth processes；Being disposed and require wall body humidity less than 10% afterwards, pH value is less than 10, wall body overall leveling, closely knit, clean without floating dust, without the hollowing that ftractures.
The construction method of the kieselguhr wall material of leather texture imitation the most according to claim 5, it is characterised in that in step 2, described construction temperature is not less than 5 DEG C；The described operational approach by kieselguhr wall material and water mix homogeneously is as follows: the weight ratio of kieselguhr wall material and water is 1:0.55；In container, first add the water of water consumption 80%, add described kieselguhr wall material and stand 3-5 minute, then stir 8-12 minute with motor stirrer, be slowly added into the water of residue 20% during stirring, stand 3-6 minute, then stir 7-10 minute with motor stirrer；20-40 minute is stood again after kieselguhr wall material and water mix homogeneously.
The construction method of the kieselguhr wall material of leather texture imitation the most according to claim 5, it is characterized in that, in step 3, the wall material thickness that described second time batch is scraped is: 1-1.5mm, and the 3rd time batch of wall material thickness scraped is: 0.5-1.0mm and surface smear become irregular concave and convex plane；Described add wall material with trowel again and pull on the thickness of one time be: 0-0.2mm.
The construction method of the kieselguhr wall material of leather texture imitation the most according to claim 5, it is characterised in that in step 3, the described operative body rustless steel receiving light trowel makes, and thickness is: 0.03mm, and the plane set deformation volume of operative body is: 0.01mm；Described irregular crackle is filled up that batch to scrape use instrument be plastic scrapers.